JP3144823B2 - 無アルカリガラス - Google Patents

無アルカリガラス

Info

Publication number
JP3144823B2
JP3144823B2 JP12494691A JP12494691A JP3144823B2 JP 3144823 B2 JP3144823 B2 JP 3144823B2 JP 12494691 A JP12494691 A JP 12494691A JP 12494691 A JP12494691 A JP 12494691A JP 3144823 B2 JP3144823 B2 JP 3144823B2
Authority
JP
Japan
Prior art keywords
glass
alkali
hydrofluoric
resistance
nitric acid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
JP12494691A
Other languages
English (en)
Other versions
JPH04325434A (ja
Inventor
英樹 櫛谷
学 西沢
泰昌 中尾
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
AGC Inc
Original Assignee
Asahi Glass Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Asahi Glass Co Ltd filed Critical Asahi Glass Co Ltd
Priority to JP12494691A priority Critical patent/JP3144823B2/ja
Priority to EP92106679A priority patent/EP0510543B1/en
Priority to DE69212052T priority patent/DE69212052T2/de
Priority to KR1019920007032A priority patent/KR100259993B1/ko
Publication of JPH04325434A publication Critical patent/JPH04325434A/ja
Priority to US08/152,927 priority patent/US5348916A/en
Application granted granted Critical
Publication of JP3144823B2 publication Critical patent/JP3144823B2/ja
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Description

【発明の詳細な説明】
【０００１】
【産業上の利用分野】本発明は、各種ディスプレイやフ
ォトマスク用基板ガラスとして好適な、アルカリ金属酸
化物を実質上含有せずフロート成形の可能な、無アルカ
リガラスに関するものである。
【０００２】
【従来の技術】従来、各種ディスプレイ用ガラス、特に
表面に金属薄膜等を形成させるものについては、以下に
示す高度な特性が要求されている。
【０００３】（１）薄膜形成工程において高温で熱処理
されるため、６００℃以上の高い歪点を有しているこ
と。 （２）アルカリ金属酸化物を含有していると、アルカリ
金属イオンが薄膜中に拡散して、膜特性を劣化させてし
まうため、実質的にアルカリイオンを含まないこと。 （３）内部及び表面に欠点（泡、脈理、インクルージョ
ン、ピット、キズなど）をもたないこと。 （４）洗浄工程などに耐えるように優れた化学耐久性を
有すること。
【０００４】しかしながら、近年、ガラス基板上にＴＦ
Ｔ(Thin Film Transistor)と呼ばれる、非晶質シリコン
や多結晶シリコンを用いた薄膜トランジスタを形成させ
た液晶ディスプレイが増えてきている。これらに用いら
れるディスプレイ基板は、半導体形成工程において、Ｓ
ｉ、ＳｉＯ2 やＳｉ3 Ｎ4 などのエッチングのためフッ
酸を含有したエッチャントにさらされることが多い。代
表的なエッチャントとしては、フッ酸に緩衝剤としてフ
ッ化アンモニウムを加えたバッファードフッ酸と、硝酸
とフッ酸の混液であるフッ硝酸が挙げられる。
【０００５】従来の無アルカリガラスでは、バッファー
ドフッ酸にさらされると表面に反応生成物が生成し、こ
れが容易に除去できないため使用に耐えなくなるものが
多かった。
【０００６】フッ硝酸にさらされた場合には、ガラス中
のアルカリ土類イオンと溶液中のフッ素イオン（Ｆ
- ）、硝酸イオン（ＮＯ3 -）が反応し、表面に反応生成
物が付着する。ガラス中のアルカリ土類酸化物の内、Ｂ
ａＯとＭｇＯを多く含むガラスは、フッ硝酸に浸漬され
ると表面に微細な結晶性物質を生成するのに対し、Ｃａ
ＯやＳｒＯを多く含むガラスの場合はゲル状の非晶質物
質を表面に生成する。このゲル状の反応生成物がマスク
剤として働くため、エッチングむらを生じ、ガラス表面
に数μｍの凹凸が形成される。そのため、高平坦性を要
求されるディスプレイ用ガラスとしては使用できないと
いう課題があった。
【０００７】これらに耐えるものとしては、石英ガラス
やアルカリ土類酸化物としてＢａＯだけを含むコーニン
グ社の＃７０５９ガラスなどが挙げられるが、石英ガラ
スに関しては、非常に高粘性で熔解が困難であり、製造
コストが高い。＃７０５９ガラスに関しては、Ｂ2 Ｏ3
含有量が多く、熔解時にＢ2 Ｏ3 が揮散するため熔解が
困難であり、歪点が低いため半導体形成工程においてガ
ラスが収縮するという課題があった。
【０００８】特開昭６３−７４９３５号公報には、Ｍｇ
Ｏを実質的に含有しないものが示されている。このガラ
スはバッファードフッ酸に対しては耐久性を示すが、Ｍ
ｇＯを含有しないため、フッ硝酸に浸漬した場合表面に
凹凸が形成されるという課題があった。
【０００９】特開平２−１３３３３４号公報には、Ｃａ
Ｏを８〜１５重量％含有する無アルカリガラスが示され
ている。このガラスはＣａＯを過剰に含有するため、耐
フッ硝酸性が充分ではないという課題があった。
【００１０】
【発明が解決しようとする課題】本発明の目的は、上記
欠点を解決し、バッファードフッ酸により白濁をおこさ
ず、フッ硝酸により表面に凹凸を形成せず、他の化学耐
久性もすぐれ、熔解・成形が容易で、高い歪点を有し、
フロート成形が可能で、低膨脹な無アルカリガラスを提
供することにある。
【００１１】
【課題を解決するための手段】本発明は、重量％表示で
実質的に、ＳｉＯ2 ：５４〜５８％、Ａｌ2 Ｏ3 ：１０
〜１４％、Ｂ2 Ｏ3 ：４〜１０％、ＭｇＯ：１．５〜５
％、ＣａＯ：０〜７％、ＳｒＯ：０〜１０％、ＢａＯ：
１０〜２０％、ＺｎＯ：０〜３％からなり、アルカリ金
属酸化物を実質的に含有せず、６２０℃以上の歪点を有
し、フロート成形可能な無アルカリガラスを提供するも
のである。
【００１２】次に上記の通り各成分の組成範囲を限定し
た理由について述べる。ＳｉＯ2 は５４重量％（以下、
単に％と記載）未満では、ガラスの化学耐久性が悪化す
ると共に、熱膨脹係数が大きくなる。他方、５８％をこ
えると熔解性が低下し、失透温度が上昇する。
【００１３】Ａｌ2 Ｏ3 はガラスの分相性を抑制し、熱
膨脹係数を下げ、歪点を上げる働きがあるが１０％未満
ではこの効果があらわれず、１４％をこえるとガラスの
熔解性が悪くなる。
【００１４】Ｂ2 Ｏ3 はバッファードフッ酸による白濁
発生を防止し、低膨脹性、熔解性に関して有効な成分で
あるが４％未満ではその効果はあらわれず、１０％をこ
えると歪点が低くなり耐フッ硝酸性が悪化する。Ｂ2 Ｏ
3 は、上記範囲中５．５〜８．５％の範囲がより好まし
い。
【００１５】ＭｇＯは耐フッ硝酸性を向上させ、しかも
歪点が低下しないという特徴を有するので、少なくとも
１．５％含有させる。５％をこえると、バッファードフ
ッ酸による白濁やガラスの分相が生じやすくなる。Ｍｇ
Ｏは、上記範囲中２〜４．５％の範囲がより好ましい。
【００１６】ＣａＯは必須ではないが、含有させること
ができる。７％をこえると、ガラスの耐フッ硝酸性が低
下する。ＣａＯは２〜５％の範囲がより好ましい。
【００１７】ＳｒＯは必須ではないが、ガラスの分相を
抑制し、バッファードフッ酸による白濁に対し比較的有
用な成分である。１０％をこえると熱膨脹係数が増大
し、耐フッ硝酸性が低下する。ＳｒＯは２〜８％の範囲
がより好ましい。
【００１８】ＢａＯはガラスの分相を抑制し、熔解性を
向上させ、失透温度を低下させる効果がある。１０％未
満ではその効果は少なく、２０％をこえると熱膨脹係数
が増大し、耐水性等の化学耐久性が劣化する。ＢａＯは
１２〜１８％の範囲がより好ましい。
【００１９】ＺｎＯは必須ではないが、ガラスの熱膨脹
係数を低下させる効果がある。３％をこえるとフッ酸に
よる白濁が生じやすくなり、製造時においてもフロート
バス中で還元され蒸発し表層部に異質層を形成し、フロ
ート成形が難しくなる。ＺｎＯは０〜２％の範囲がより
好ましい。
【００２０】本発明によるガラスは上記成分以外にガラ
スの熔解性、清澄性、成形性を改善するため、ＺｒＯ
2 、Ｐ2 Ｏ5 、ＴｉＯ2 、ＳＯ3 、Ａｓ2 Ｏ3 、Ｓｂ2
Ｏ3 、Ｆ、Ｃｌを総量で５％以下添加することができ
る。
【００２１】本発明のガラスは、例えば次のような方法
で製造できる。通常使用される各成分の原料を目標成分
になるように調合し、これを熔解炉に連続的に投入し、
１５００〜１６００℃に加熱して熔融する。この熔融ガ
ラスをフロート法により所定の板厚に成形し、徐冷後切
断する。
【００２２】
【実施例】各成分の原料を目標組成になるように調合
し、白金坩堝を用いて、１５００〜１６００℃の温度で
４時間加熱し熔解した。熔解にあたっては、白金スター
ラーを挿入し２時間撹拌しガラスの均質化を行った。次
いで熔融ガラスを流し出し、板状に成形後徐冷した。
【００２３】表１にガラス組成（単位：重量％）を示
し、表２に熱膨脹係数、ｌｏｇη＝２．５、４．０（η
はポイズで示した粘度）となる温度、失透温度、歪点、
耐水性、耐酸性、耐バッファードフッ酸性及び耐フッ硝
酸性を示した。
【００２４】耐水性は、９５℃のイオン交換水中に４０
時間浸漬した後、重量減を測定し、それをガラスの単位
表面積あたりに換算して示した。耐酸性は、９５℃の１
／１００規定のＨＮＯ3 中に２０時間浸漬した後、重量
減を測定し、それをガラスの単位表面積あたりに換算し
て示した。
【００２５】耐バッファードフッ酸性は、ＮＨ4 ＦとＨ
Ｆの混液（４０重量％ＮＨ4 Ｆ水溶液と５１重量％ＨＦ
水溶液とを重量で９：１に混合した液）中に２５℃で２
０分浸漬した後、目視観察し外観の良好なものを○印、
不良なものを×印として示した。耐フッ硝酸性は、ＨＦ
とＨＮＯ3 の混液（５１重量％ＨＦ水溶液と６１重量％
ＨＮＯ3 水溶液とを体積で１：２に混合した液）中に２
５℃で５分浸漬した後、表面粗さを測定し、表面性状の
良好なものを○印、不良なものを×印として示した。
【００２６】表２からも明らかなように、実施例のいず
れのガラスも、熱膨脹係数は４０×１０ -7 ／℃〜５０×
１０-7／℃で低い値を示し、熔解の目安であるｌｏｇη
＝２．５となる温度も比較的低く熔解が容易であること
がわかる。また成形性も目安であるｌｏｇη＝４．０と
なる温度と失透温度の関係も良好で、成形時に失透が生
成するなどのトラブルがないと考えられる。歪点も６２
０℃以上と高い値を示しており、高温での熱処理に充分
耐えられるものであることがわかる。
【００２７】化学的特性に関しても耐水性、耐酸性にす
ぐれ、バッファードフッ酸により白濁を生じにくく、フ
ッ硝酸により表面に凹凸が形成されることはない。一
方、Ｎｏ．３、７、８には比較例を示した。Ｎｏ．７
は、ｌｏｇη＝２．５となる温度が比較的低く熔解性は
よいと思われるが、耐フッ硝酸性は劣っている。また、
Ｎｏ．８は、耐バッファードフッ酸性、耐フッ硝酸性は
よいが、ｌｏｇη＝２．５、４．０となる温度が高過
ぎ、熔解・成形が困難なことが予想される。
【００２８】
【表１】
【００２９】
【表２】
【００３０】
【発明の効果】本発明によるガラスは、フロート法によ
る成形が可能である。また、バッファードフッ酸による
白濁が生じにくく、耐フッ硝酸性に優れ、耐熱性が高
く、かつ低い熱膨脹係数を有しているのでディスプレイ
用基板、フォトマスク基板、ＴＦＴタイプのディスプレ
イ基板等かかる特性を要求する用途に好適である。
───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 平１−201041（ＪＰ，Ａ) 特開 昭63−74935（ＪＰ，Ａ) 特開 平３−174336（ＪＰ，Ａ) (58)調査した分野(Int.Cl.7，ＤＢ名) C03C 3/091 C03C 3/093

Claims (2)

    (57)【特許請求の範囲】
  1. 【請求項１】重量％表示で実質的に、ＳｉＯ2 ：５４〜
    ５８％、Ａｌ2 Ｏ3 ：１０〜１４％、Ｂ2 Ｏ3 ：４〜１
    ０％、ＭｇＯ：１．５〜５％、ＣａＯ：０〜７％、Ｓｒ
    Ｏ：０〜１０％、ＢａＯ：１０〜２０％、ＺｎＯ：０〜
    ３％からなり、アルカリ金属酸化物を実質的に含有せ
    ず、６２０℃以上の歪点を有し、フロート成形可能な無
    アルカリガラス。
  2. 【請求項２】重量％表示で実質的に、ＳｉＯ2 ：５４〜
    ５８％、Ａｌ2 Ｏ3 ：１０〜１４％、Ｂ2 Ｏ3 ：５．５
    〜８．５％、ＭｇＯ：２〜４．５％、ＣａＯ：２〜５
    ％、ＳｒＯ：２〜８％、ＢａＯ：１２〜１８％、Ｚｎ
    Ｏ：０〜２％からなる請求項１に記載の無アルカリガラ
    ス。
JP12494691A 1991-04-26 1991-04-26 無アルカリガラス Expired - Lifetime JP3144823B2 (ja)