JPH01100752A - 磁気記録、光再生用記録媒体 - Google Patents

磁気記録、光再生用記録媒体

Info

Publication number
JPH01100752A
JPH01100752A JP62256386A JP25638687A JPH01100752A JP H01100752 A JPH01100752 A JP H01100752A JP 62256386 A JP62256386 A JP 62256386A JP 25638687 A JP25638687 A JP 25638687A JP H01100752 A JPH01100752 A JP H01100752A
Authority
JP
Japan
Prior art keywords
film
medium
recording
magnetic field
magnetic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP62256386A
Other languages
English (en)
Inventor
Osamu Ishii
修 石井
Iwao Hatakeyama
畠山　巌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NTT Inc
Original Assignee
Nippon Telegraph and Telephone Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Telegraph and Telephone Corp filed Critical Nippon Telegraph and Telephone Corp
Priority to JP62256386A priority Critical patent/JPH01100752A/ja
Priority to US07/188,876 priority patent/US5051970A/en
Priority to DE8888304128T priority patent/DE3876133T2/de
Priority to KR1019880005262A priority patent/KR910003935B1/ko
Priority to EP88304128A priority patent/EP0291248B1/en
Publication of JPH01100752A publication Critical patent/JPH01100752A/ja
Pending legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】 ［産業上の利用分野］ 本発明は高速で重ね書きの可能な光磁気デイク媒体に関
するものである。
［従来の技術］ 従来、光磁気ディスクへの記録（情報の書き込み）は、
−様に磁化した光記録媒体（Ｔｂ−Ｆｅ薄膜等の垂直磁
化薄膜）に対し、異方性磁界以下のバイアス磁場を磁化
と逆向きに加えつつ、レーザービームを照射して照射領
域の温度をキュリー温度以上に上げた後、媒体が冷却す
る過程でバイアス磁場の方向に磁化が反転することを利
用しており、レーザービームをオン・オフする事で磁化
反転の列として情報を記録していた（通常の光変調記＃
３）。この方式では一旦記録された領域に再度新しい情
報を記録する場合には、記録時とは逆向きのバイアス磁
場中で連続レーザービームを照射して媒体を加熱し、磁
化を全て一方向に揃える事（これを消去過程という）が
必要であった。即ち、消去して後に再度記録を行う必要
があり、通常の磁気記録における情報の書き込みのよう
に、予め記録されていた領域の上に別の情報を記録する
ことで、前の情報は自動的に消える事はなく、アクセス
速度の高速化上の障害となっていた。
上記問題を解決するため、最近、重ね書きの出来る光磁
気ディスクが提案されている。以下に、その動作メカニ
ズムを述べる。第３図に光磁気デ゛　イスクの概略を示
す。１は光磁気ディスク用基板、２は記録媒体、３はレ
ーザー光、４は光ヘッド、５は信号磁界印加用コイルで
ある。ディスクが回転している時、この媒体は光ヘッド
の下に移動して光ビームで加熱される。加熱された領域
は、キュリー温度以上となるため非磁性になり、書き込
まれていたビットは消去される。媒体が移動してレーザ
ービームで照射された領域の温度が低下する時に、信号
磁界を印加すれば、記録媒体の磁化は信号磁界の方向に
揃う（磁界変調記録）。書き込まれた情報は、通常の光
変調記録の場合と同様に、レーザービームの反射光の偏
光面の回転角の差として読み出すことができる。
しかしながら、記録媒体としてＴｂ　−Ｆｅ　−Ｃｏ薄
膜を用いた例では、信号磁界として数百０ｅ以上の高磁
場が必要である（電気学会マグネティックス研究会二田
中富士雄、田中ｆ８介、今村修武「磁界変調記録法によ
るオーバーライド」講演番号ＭＡＧ−８６−９５）。光
磁気ディスクは一般にカセットに収納されており記録媒
体と信号磁界印加用コイルとの間隔が数ｎｏｎ以上であ
ることを考慮すると、このような高い磁場を得るために
は信号電流がなかつ大きくなるため、装置の発熱等の問
題を内在するといえる。また、大電流を流すコイルは必
然的に大型にならざるをえず、コイルのインダクタンス
が増大する。このため、高周波の信号電流をコイルに流
すことが困難になり、データ転送に高速化に支障をきた
す。上記の例では、数ＭＨｚが駆動周波数の上限となっ
ている。
次に重ね書き方式による記録動作メカニズムを述べる。
第４図は光磁気ディスクの例である。１は光磁気ディス
ク用基板、２はレーザー光、３は光ヘッド、６は第１の
媒体、７は第２の媒体、８は磁気記録用ヘッドである。
第４図において、ディスクが矢印方向へと回転している
時、先ず第１の媒体６に対して磁気ヘッド８から発生す
る磁場で情報を記録する。この過程は従来の磁気記録に
おける書き込みプロセスと同一であり、薄膜ヘッド等の
従来型磁気ヘッドを用いれば数十ＭＨｚの周波数まで駆
動できる。この時の記録磁界は第１の媒体６の保磁力よ
り高く、かつ、第２の媒体７の保磁力よりは低い値に設
定する。従って第１の媒体６のみが情報を書き込まれ第
２の媒体７には情報は記録されない。第２の媒体７への
情報の記録は次ぎの過程を経て完結する。媒体が記録ヘ
ッド４の下に移動して光ビーム３で加熱される。この時
に、光ビームのパワーは照射部分の最高温度が第２の媒
体７のキュリー温度以上、第１の媒体６のキュリー温度
以下となるように設定する。第２の媒体７が非磁性にな
るのに対し、第１の媒体６はキュリー温度が高いため、
磁化情報は破壊されずに残っておりそのビットからは溜
れ磁界が発生している。次ぎに、媒体が移動してレーザ
ービ−ムで照射された領域の温度が低下してきた場合に
は、第２の媒体７の磁化は第１の媒体６から発生する磁
場方向に揃うため、第１の媒体６に書き込まれた磁化情
報は第２の媒体７に転写される。即ち、光ビーム３の幅
のトラックで第２の媒体７上には磁気情報が記録される
。
書き込まれた情報の再生はレーザービームの反射光の偏
光面の傾きの差として読み出すとかできる。この時のレ
ーザーパワーは、媒体温度が第２の媒体７のキュリー温
度よりも充分低い温度になるように設定する必要がある
。このディスクへの重ね書きは、第１の媒体６上へ磁気
ヘッドで新しい情報を書き加えれば達成できる。第１の
媒体６への重ね書きは通常−４０ｄＢ程度の消し残り成
分を伴うが、この値は極めて小さいと言える。この時、
両媒体のＨｃは第２の媒体７〉〉第１の媒体６なので重
ね書きのための磁場は第１の媒体６のみを磁化し第２の
媒体７には影響を及ぼさない。
［発明が解決しようとする問題点１ 本方式の特徴は、光磁気ディスクにおいて磁気記録と同
等のアクセス速度を持ち、しかも消去過程を経ずに新し
い情報を加えられる事である。しかしながら、この方法
には以下のような欠点がある。すなわちＣｏ　−Ｃｒ／
　Ｔｂ　−Ｆｅ薄膜では薄膜の保磁力が大きいため、磁
化率が低く書き込み磁場は単調に発散する。従って、媒
体に加わる磁場の絶対値が低いだけでなくその分布もブ
ロードになる。
媒体の磁化反転は磁場の絶対値が大きいと同時にその分
布も急峻であることが必要であり、コイル電流を増す等
してヘッド磁場を強めるだけでは磁場を強めてもその分
布をシャープにはできなかった。
本発明は上述した従来の欠点を解決し、媒体に加わる磁
場の分布を急峻にし、小さな書き込み電流で大きな再生
出力を得ることのできる記録媒体を提供することを目的
とする。
［問題点を解決するための手段］ このような目的を達成するために、本発明は軟磁性体と
、軟磁性体上に形成された第１の垂直磁化膜と、第１の
垂直磁化膜上に形成された異方性磁場が第１の垂直磁化
膜の異方性磁場より太き（かつキュリー温度が第１の垂
直磁化膜のキュリー温度より低い第２の垂直磁化膜とを
有することを特徴とする。
［作　用］ 磁気ヘッドで媒体１に対し情報を記録する場合には磁気
記録媒体１の磁化反転が完全に行われることが望ましい
。このためには、磁気ヘッドから発生する記録磁場の垂
直成分が大きくかつその分布が急峻であることが重要で
ある。このような目的を達成するために第１の媒体６の
裏側にパーマロイ等の軟磁性体薄膜を設ける事は極めて
有効である。すなわち第１の媒体を挟んで磁気ヘッドと
軟磁性体薄膜が存在するため、軟磁性体薄膜は磁束の通
り道を形成する事となる。もし、軟磁性体薄膜の透磁率
が無限大であれば、鏡像効果によって第１の媒体に加わ
る垂直磁場は２倍に強められると同時に、垂直磁場の分
布も急峻になる。
［実施例］ 第１図に、本発明による光磁気ディスクの実施例の概略
を示す。光磁気ディスク用基板上に７８ａｔ％Ｎｉ　−
２２ａｔ％Ｆｅからなる初透磁率約４，０００　。
キュリー温度的５８０℃のパーマロイ薄＠９を０．５μ
ｍ形成後、第１の媒体として７８．５％Ｃｏ　−２１，
５％Ｃｒ薄膜６（異方性磁場４５０００ｅ、キュリー温
度的６００℃）を１０００人厚形成し、引き続きその上
に第２の媒体として７９％Ｆｅ−２１％Ｔｂ薄膜７（異
方゛性磁場１５０００ｅ、キュリー温度約１２５℃）を
ａＯＯ人厚形厚形成。比較のためにパーマロイ薄膜９を
省略した構造の媒体も形成した。基板としてガラス円板
上に２２剤を塗布後ホトリソグラフ技術を用いて同心円
状のトラック溝を形成したものである。本実施例では磁
気記録用ヘッドは、垂直磁化記録を目的としているので
主磁極励磁型の構造となっているが、原理的にはリング
型でもあるいは補助磁極励磁型でも垂直磁化記録は可能
である。
ディスクが矢印方向へと回転している時、先ず、Ｃｏ−
［：ｒ媒体に対して主磁極から発生する磁場で情報を記
録する。この過程は従来のｌｉｌ気記録における書き込
みプロセスと同一である。この時の記録電流値と記録用
磁気ヘッドで再生した出力の関係を第２図に示す。記録
電流値はヘッド磁極先端が磁気的に飽和しない範囲内で
は書き込み磁場の強度に比例すると考λられる。即ち、
パーマロイ薄膜を形成した場合の方が同一再生出力を得
るための書き込み電流値が数十分の−の低下する事が判
る。
なお、本実施例における第１および第２の媒体は各々高
キュリー温度、及び低キユリー温度高異方性磁場の垂直
膜の例であり、この他にも第１の媒体としては垂直磁気
記録用媒体として検討されているバリウムフェライト膜
、Ｃｏ−Ｃｒ合金の種々の添加元素を加えた膜等が、第
２の媒体としては光磁気記録用媒体であるＭｎ−Ｂｉ合
金膜、　ＹＩＧ　＠。
ＣＯフェライト膜等が適用出来る。
［発明の効果］ 以上述べたように、軟磁性体薄膜、高キュリー温度の垂
直異方性磁化薄膜、低キユリー温度の垂直異方性磁化薄
膜の３層構造薄膜とすることで、磁気的に情報を記録す
る場合の磁場が著しく低減でき、磁気ヘッド媒体間隔を
広く設定することや、高周波駆動時の発熱量を少なく抑
えることができる。
【図面の簡単な説明】
第１図本発明による磁気記録、光再生方式の記録媒体の
実施例を示す図、 第２図は軟磁性膜がある場合および、無い場合の再生出
力の書き込み電流依存性を示す図、第３図および第４図
は従来の光磁気ディスクの概要図である。 １・・・光磁気ディスク用基板、 ２・・・記録媒体、 ３・・・レーザー光、 ４・・・光ヘッド、 ５・・・信号磁界印加用コイル、 ６・・・第１の媒体、 ７・・・第２の媒体、 ８・・・磁気記録用ヘッド、 ９・・・軟磁性膜。

Claims (1)

  1. 【特許請求の範囲】 １）軟磁性体と、該軟磁性体上に形成された第１の垂直
    磁化膜と、該第１の垂直磁化膜上に形成された異方性磁
    場が第１の垂直磁化膜の異方性磁場より大きくかつキュ
    リー温度が第１の垂直磁化膜のキュリー温度より低い第
    ２の垂直磁化膜とを有することを特徴とする磁気記録、
    光再生用記録媒体。 ２）前記軟磁性体がパーマロイ、センダスト、Ｃｏ−Ｚ
    ｒ合金またはフェライトのいずれかからなる薄膜または
    基板であり、前記第１の垂直磁化膜がＣｏ−Ｃｒ合金膜
    、Ｃｏ−Ｃｒを主成分とする合金膜またはバリウムフェ
    ライト膜のいずれかであり、かつ前記第２の垂直磁化膜
    が希土類・遷移金属合金薄膜（希土類元素はＴｂ、Ｇｄ
    、Ｎｄ、Ｄｙののうち少なくとも１種類以上、遷移金属
    としてはＦｅ、Ｃｏ、Ｎｉのうち少なくとも１種類以上
    を含む）、Ｍｎ−Ｂｉ合金膜、ＹＩＧ膜、Ｃｏフェライ
    ト薄膜のいずれかであることを特徴とする特許請求の範
    囲第１項記載の磁気記録、光再生用記録媒体。
JP62256386A 1987-05-08 1987-10-13 磁気記録、光再生用記録媒体 Pending JPH01100752A (ja)