JPH01201025A - 酸化物超伝導材料 - Google Patents
酸化物超伝導材料Info
- Publication number
- JPH01201025A JPH01201025A JP63026128A JP2612888A JPH01201025A JP H01201025 A JPH01201025 A JP H01201025A JP 63026128 A JP63026128 A JP 63026128A JP 2612888 A JP2612888 A JP 2612888A JP H01201025 A JPH01201025 A JP H01201025A
- Authority
- JP
- Japan
- Prior art keywords
- alkaline earth
- elements
- crystal phase
- superconducting material
- approximately
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
産業上の利用分野
本発明は酸化物超伝導材料に関する。
従来の技術
近年超伝導材としてYBaCuO系の材料か報告され、
色々な試験研究が行われている。その結果、この材料は
非常に不安定であり、又超伝導状態の開始温度と完了温
度との差が大きいといった大きな欠点がある事が知られ
てきた。さらに希土類元素を多量に使用する為に価格も
たかく市況変動に左右されやすいといった経済的にも不
安定な要素を抱えている。これらすべてについての改良
がのぞまれている。
色々な試験研究が行われている。その結果、この材料は
非常に不安定であり、又超伝導状態の開始温度と完了温
度との差が大きいといった大きな欠点がある事が知られ
てきた。さらに希土類元素を多量に使用する為に価格も
たかく市況変動に左右されやすいといった経済的にも不
安定な要素を抱えている。これらすべてについての改良
がのぞまれている。
さらに極く最近、5rBiCuO系の新材料が報告され
ている。しかし、これらについては詳しいことは現在の
所不明である。
ている。しかし、これらについては詳しいことは現在の
所不明である。
発明が解決しようとする課題
本発明はE述のような温度差、安定性、さらには経済性
に問題のない材料を提供することを目的とする。
に問題のない材料を提供することを目的とする。
課題を解決するための手段
AB i CuO(Aはアルカリ王族より成る元素の少
なくとも一種以上を含む)を主とした構成元素よりなり
、さらにA / B i / Cuの原子比がCUを2
としたときにAが1.9〜2.5、Biが1.1〜1.
7にあり、ほぼ5/315ないしは3/2/3と記載さ
れうる結晶相を少なくとも含有せしめる。さらに高特性
を得るために、Aのイオン半径が1オングストローム以
上の元素とそれ以下の元素が混在せしめる。
なくとも一種以上を含む)を主とした構成元素よりなり
、さらにA / B i / Cuの原子比がCUを2
としたときにAが1.9〜2.5、Biが1.1〜1.
7にあり、ほぼ5/315ないしは3/2/3と記載さ
れうる結晶相を少なくとも含有せしめる。さらに高特性
を得るために、Aのイオン半径が1オングストローム以
上の元素とそれ以下の元素が混在せしめる。
作 用
不安定性の原因となる希土類元素やアルカリ土族元素を
不安定な形で多量に含まない為に水による浸食等が生じ
ない。また固溶範囲が広いと推定され、その為と思われ
るが不純物相を余り含有せずこれも安定性に役立ってい
ると思われる。さらにこの事が上述の温度差を小さ(す
るのに役立っていると思われる。アルカリ土族元素を先
ずイオン半径1オンゴストローム以上と以下を混在させ
る事により適切なる元素間距離を実現している為に優れ
た特性が得られていると推定される。
不安定な形で多量に含まない為に水による浸食等が生じ
ない。また固溶範囲が広いと推定され、その為と思われ
るが不純物相を余り含有せずこれも安定性に役立ってい
ると思われる。さらにこの事が上述の温度差を小さ(す
るのに役立っていると思われる。アルカリ土族元素を先
ずイオン半径1オンゴストローム以上と以下を混在させ
る事により適切なる元素間距離を実現している為に優れ
た特性が得られていると推定される。
さらに明白なように高価な供給の不安定な希土類元素を
全(含まない事からも分かるように経済性にも優れてい
る。
全(含まない事からも分かるように経済性にも優れてい
る。
実施例
一般的な最近のYBaCuO系の材料について追試を行
った所、所謂123 (Y/Ba/Cuの比〉の最適な
組成でも本発明者らの検討によれば、転移温度は約90
度にであったが、上述の温度差は杓10度近く有り非常
に大きい事が示され、又少し組成を変動させれば不純物
相が生成し特性が変動する事が示された。
った所、所謂123 (Y/Ba/Cuの比〉の最適な
組成でも本発明者らの検討によれば、転移温度は約90
度にであったが、上述の温度差は杓10度近く有り非常
に大きい事が示され、又少し組成を変動させれば不純物
相が生成し特性が変動する事が示された。
これに対して本発明者らの検討によれば新材料は以下に
示したように安定した優れた特性を有している。
示したように安定した優れた特性を有している。
イオン半径1オンゴストローム以下のMgCaの一群と
Sr、Baの一群の各々から少なくとも一種以上と、B
i、Cuを含む酸化物を王者の比A / B i /
Cuがほぼ5/315.3/2/3ないしはその近傍に
なるように秤量し、次に均一に混合した後に800から
850度で仮焼、さらに粉砕、成型した後に焼成を83
0から870度で行った。得られた結果を第−表に示す
。
Sr、Baの一群の各々から少なくとも一種以上と、B
i、Cuを含む酸化物を王者の比A / B i /
Cuがほぼ5/315.3/2/3ないしはその近傍に
なるように秤量し、次に均一に混合した後に800から
850度で仮焼、さらに粉砕、成型した後に焼成を83
0から870度で行った。得られた結果を第−表に示す
。
第 1 表
同表より明らかな様に上述の温度差は全て5度以下と小
さ(、転移温度も約100度に以上と安定している事が
示された。さらに上記二群の元素を混在せしめる事によ
って、単独の場合には転移温度が20から30度にのも
のが100度に以上と成っている事が示されている。さ
らに高温高湿下(60度60%)に1ケ月放置する耐湿
テストでは所謂YBaCu系材料では全体が白色に変化
しかなり崩壊したのに対して、本材料は表面が僅かに白
色化したのみであり非常に安定している事が示された。
さ(、転移温度も約100度に以上と安定している事が
示された。さらに上記二群の元素を混在せしめる事によ
って、単独の場合には転移温度が20から30度にのも
のが100度に以上と成っている事が示されている。さ
らに高温高湿下(60度60%)に1ケ月放置する耐湿
テストでは所謂YBaCu系材料では全体が白色に変化
しかなり崩壊したのに対して、本材料は表面が僅かに白
色化したのみであり非常に安定している事が示された。
第1表からも分かる様に基本的には組成2.3.4.5
(その中の15)でほぼ囲まれた範囲で特に優れている
事が示されている。
(その中の15)でほぼ囲まれた範囲で特に優れている
事が示されている。
又、11.12.13の様にアルカリ土族元素の置き換
わった物でも良い特性を示している。
わった物でも良い特性を示している。
又、X線による解析の結果ではかなり広い範囲で単一の
3/2/3ないしは5/315の組成比からなる結晶相
(現在検討中であるが格子定数がa=5.4オンゴスト
ローム、b=27.0オンゴストローム、c=15.3
オンゴストロームの斜方晶と表面上記述され、透過電子
顕微鏡の結果と合わせれば単位胞5.4オンゴストロー
ムの疑似正方品の超格子より成ると推定される。)を形
成しており、0面で非常に壁間し易い事が確認された。
3/2/3ないしは5/315の組成比からなる結晶相
(現在検討中であるが格子定数がa=5.4オンゴスト
ローム、b=27.0オンゴストローム、c=15.3
オンゴストロームの斜方晶と表面上記述され、透過電子
顕微鏡の結果と合わせれば単位胞5.4オンゴストロー
ムの疑似正方品の超格子より成ると推定される。)を形
成しており、0面で非常に壁間し易い事が確認された。
発明の効果
本発明によれば、耐湿性に優れた、且つ、固溶範囲の広
(上述の温度差の小さな安定性再現性の優れた材料を提
供することができ、広く超伝導機器に適用され得る。
(上述の温度差の小さな安定性再現性の優れた材料を提
供することができ、広く超伝導機器に適用され得る。
Claims (3)
- (1)ABiCuO(Aはアルカリ土族より成る元素の
少なくとも一種以上を含む)を主とした構成元素よりな
り、さらにA/Bi/Cuの原子比が、Cuを2とした
ときにAが1.9〜2.5、Biが1.1〜1.7にあ
り、ほぼ5/3/5と記載されうる結晶相を少なくとも
含有する事を特徴とする酸化物超伝導材料。 - (2)ABiCuO(Aはアルカリ土族より成る元素の
少なくとも一種以上を含む)を主とした構成元素よりな
り、さらにA/Bi/Cuの原子比が、Cuを2とした
ときにAが1.9〜2.5、Biが1.1〜1.7にあ
り、ほぼ3/2/3と記載されうる結晶相を少なくとも
含有する事を特徴とした酸化物超伝導材料。 - (3)Aのイオン半径が1オングストローム以上の元素
とそれ以下の元素が混在している事を特徴とする特許請
求の範囲第1項または第2項記載の酸化物超伝導材料。