JPH01201089A - 多孔質セラミック体の表面の一部分を被覆する方法 - Google Patents

多孔質セラミック体の表面の一部分を被覆する方法

Info

Publication number
JPH01201089A
JPH01201089A JP63311794A JP31179488A JPH01201089A JP H01201089 A JPH01201089 A JP H01201089A JP 63311794 A JP63311794 A JP 63311794A JP 31179488 A JP31179488 A JP 31179488A JP H01201089 A JPH01201089 A JP H01201089A
Authority
JP
Japan
Prior art keywords
ceramic
ceramic body
slurry
porous ceramic
coated
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP63311794A
Other languages
English (en)
Inventor
Albert Maurer
アルベルト・マウレル
Tiberiu Mizrah
ティベリュー・ミツラー
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SCHWEIZ ALUM AG <ALUSUISSE>
Rio Tinto Switzerland AG
Original Assignee
SCHWEIZ ALUM AG <ALUSUISSE>
Alusuisse Holdings AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SCHWEIZ ALUM AG <ALUSUISSE>, Alusuisse Holdings AG filed Critical SCHWEIZ ALUM AG <ALUSUISSE>
Publication of JPH01201089A publication Critical patent/JPH01201089A/ja
Pending legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】 （産業上の利用分野） 本発明は、相互に連結し合った開口小房（ｏｐｅｎ　ｃ
ａｌｌｓ）より成る３次元的網目状構造を有する多孔質
セラミック体の表面部分にセラミック層を塗布し、被覆
する方法に関するものである。
（従来の技術） この種の多孔質セラミック体の製造についてはＵＳ特許
３，０９０．０９４に述べられている。そのようなセラ
ミック体をフィルタ一部品（エレメント）、たとえば内
燃機関、特にぜジーゼルエンジンの排気ガスの浄化用に
、或は溶融金属の濾過用に効率よく用いるには、フィル
ター組立体にセラミック体の支持物を適宜固定する必要
がある。セラミック体は直接的な集中応力に対して常に
非常に脆弱で、きわめてこわれやすい。繊細なセラミッ
クの薄板（ウェブ）の損傷を防ぐには、したがって、セ
ラミック体の角部に応力がかからないようにするのが望
ましい。このような問題は、オツトーサイクルエンジン
用排気用触媒において見られるようにフィルタ一体が金
属容器にいわば「罐詰め」されているような場合には、
フィルタ一体を機械的応力の原因となるような振動、す
れなど有害な影響から保護すべく、それを針金を織った
もの及び／又はセラミック製むしろ状物で保設してやれ
ばよい。
（発明が解決しようとする課題） このような方法でセラミック体を保護する際の問題はＵ
Ｓ特許４，５４０，５３５に述べられている。
この特許では問題点を該セラミック体と同一組成を有す
るセラミック泥漿Ｃｓ１ｉｐ）’を繰り返して吹き付け
て乾燥し、セラミック体の外部の細孔を閉じろことで解
決している。この方法はしかし、作業が複雑なのと、多
量の泥しようの塗布で開口細孔が閉じられてしまうので
、セラミック体のかなりの部分がもはやその機能を実際
に発揮しなくなるという欠点がある。
（課題を解決するための手段） 本発明者らはそこで、相互に連なる開口小房を有する３
次元的網目状構造を有する多孔質セラミック体の表面部
分に、上記欠点を改善した、封止（５ｅａｌｉ％ｇ）や
補強に役立つセラミック層を塗布し、被覆する方法をま
ず得ようと意図した。
さらに、この種のセラミック体の再生法についても考え
てみることにした。このセラミック体というのは、内燃
機関、特にジーゼルエンジンの排気ガスの浄化に用いら
れるフィルター用に付されるものである。なお、電気抵
抗加熱及び／又は灼熱によってフィルターを再生する場
合には、上記被覆には電気的接触部としての機能も与え
られる。
本発明における最初のねらいは、互いに連なる開口小房
を有する３次元的網目状構造を有する多孔質セラミック
体の表面部分にセラミック層を塗布し、被覆することに
より達成される。ただしこの方法では、吸収性の［平薄
な材料Ｊ　（ｐｌａｎｅｍａｔｅｒｉａｌ）の少なくと
も一面にセラミック泥しようの薄い層が被覆され、この
平温材料のセラミック泥しようを有する側は未焼成セラ
ミツク体の補強されセして／又は封止される側の面の上
におかれ、乾燥され、そしてセラミック体とともに焼成
される。
本発明の改良点には、平薄材料上の乾燥セラミック泥し
ようとセラミック体とが共に焼結されろような温度で灼
熱されることが含捷れる。平温材料としては紙、むしろ
状物或は他の博識状物のセラミック裂織物又は繊維が用
いられる。平薄材料には、灼熱によりセラミック体の上
に多孔質セラミック層が形成されるよう多孔質のセラミ
ック泥しようを被覆するのが良かろう。なお、平薄材料
には、灼熱によりセラミック体上に封止セラミック層が
形成されるように、非多孔質のセラミック泥しよう暑被
覆するのがよかろう。
提案された方法は、内燃機関、特にジーゼルエンジンの
排気浄化用フィルターの製造に向いている。
溶融金属の溶過に上記のようなフィルターを用（・るユ
ーザーにおいては、時々、機械的に補強された周縁（、
ｉ−）を有する上記のようなフィルター組立体とする。
特にこの目的のためには、本発明の方法は封止や補強を
意図したフィルターの周縁を形成するのに適している。
なぜなら、得られたフィルター周縁の表面は滑らかでき
ざぎざなどがなく、フィルター組立体の座にぴったりと
おさまり、耐熱性セラミックをあてがったりしな（ても
よいためである。
本発明の方法、特にジーゼルエンジンのすす用フィルタ
ーの製造法は有益な効果を提供する。本発明の方法によ
り、フィルターの形式に応じた表面、即ち、補強用のみ
の、封止用のみの、或は両方の目的のための表面ビつく
ることができる。平薄相料に塗布される泥しようを選ぶ
ことにより及び／又は望ましい性質の泥しよう材を選ぶ
ことにより色々な可能性が生じてくる。目の粗い繊維は
セラミック体を封することな（その表面を補強する。一
方、灼熱後にお（・ても封止性を保持するセラミック泥
しようを連続薄層状に塗った紙はセラミック体に封止と
補強のなされた表面を形成する。
（実施例） 発明の特徴と詳細は以下の例から明らかになる。
まず、吸収性が若干ある紙、むしろ状物或は他の薄截物
ビ補強すべきセラミック体の縁のサイズに切断する。そ
して使用材料にはけや他の過当なもの暑用いてセラミッ
ク泥しようを薄い層状に塗布する。セラミック泥しよう
は基本的にはコージェライト、酸化アルミニウム或はム
ライトなど乞含むようなものとすれはよい；ただセラミ
ック体に付着しさえすればよいのである。しかし、多孔
質セラミック体の製造に用いたのと同じ泥しようを用い
るのが望ましい。下地の紙、むしろ状物或は他の博識物
は若干の吸収性馨有しているので、泥しようの薄層が付
着しやすい。泥しようを塗布された下地はそこで補強す
べき多孔質フィルターへ、泥しようののりを用い、のり
が乾かないうちにはりつけられる。８０〜１００℃で行
うのが望ましい乾燥の間、のりは未灼熱多孔質セラミッ
ク体の被包された縁部とその上で乾燥されるセラミック
泥しようとの間を保持する。特に紙の下地が用いられた
ときには、それは焼結灼熱が十分に行われる前にたやす
く除かれる。このような手段はしかし、焼結法により多
孔質セラミック体をつくる際にポリウレタン多孔質体が
焼き尽（されるのと同様、下地が焼き尽（されるときに
は必要としない。
灼熱工程後、通常必要な温度で焼結される。そしてセラ
ミック壱の付着により表面部は封止されセして／或は補
強されるが、その際、用いられるセラミック泥しようと
下地相料とをうま（選択することが必要である。この種
のセラミック体の周縁部の機械的強度は望ましいもので
ある。
もし上記のようなディーゼルエンジンのすす用フィルタ
ービ電気抵抗加熱及び／或は灼熱により再生するのなら
、加熱後電気接触部として寄与する電気伝導性のセラミ
ックＮを生じるような泥しよう？用いる必要がある。特
に、泥しよう中の固形物としては炭化珪素又は望むらく
は二硼化チタン或はそれらの混合物がこの目的のために
用いられる。たとえこれら組成物のどれを用いても、セ
ラミック体に密着し、そして耐久性のある電気的接触部
を形成することができる。
（外４名）

Claims (1)

  1. 【特許請求の範囲】 １、３次元的網目状構造を有するセラミック体の表面部
    分を被覆する方法であつて、多孔質セラミック体を用意
    し、吸収性の平薄材料の少なくとも一面をセラミック泥
    漿の層で被覆し、この被覆面を上記多孔質セラミック体
    の上に置いて一つの組立体となし、そしてこの組立体を
    灼熱して有被覆セラミック体とすることより成る方法。 ２、平薄な材料上のセラミック泥漿とセラミック体とが
    焼結し合うような温度で灼熱する、請求項１に記載の方
    法。 ３、平薄材料が紙、むしろ状物、織物及びセラミック繊
    維よりなる群から選ばれる、請求項１に記載の方法。 ４、灼熱によりセラミック体の上に多孔質セラミック層
    が形成されるよう、多孔質のセラミック泥漿が平薄材料
    に被覆される、請求項１に記載の方法。 ５、灼熱によりセラミック体の上に封止セラミック層が
    形成されるよう、非多孔質のセラミック泥漿が平薄材料
    に被覆される、請求項１に記載の方法。 ６、セラミック泥漿がコージェライト、酸化アルミニウ
    ム、ムライト及びそれらの混合物より成る群から選ばれ
    る材料を含んでいる、請求項１に記載の方法。 ７、セラミック体とセラミック泥漿には同じセラミック
    材料が用いられる、請求項１に記載の方法。 ８、組立体が灼熱の前に乾燥される、請求項１に記載の
    方法。 ９、組立体が灼熱の前に８０〜１００℃の温度で乾燥さ
    れる、請求項８に記載の方法。 １０、吸収性の平薄材料が灼熱の前に除かれる、請求項
    １に記載の方法。 １１、溶融金属濾過用フィルターの製造に供される、請
    求項１に記載の方法。 １２、内燃機関の排気浄化用フィルターの製造に供され
    る、請求項１に記載の方法。 １３、セラミック泥漿を加熱することにより、それがフ
    ィルターの再生において電気伝導接触部として役立つ電
    気伝導性のセラミック層となる、請求項１に記載の方法
    。 １４、多孔質セラミック体が電気伝導性の材料より形成
    されている、請求項１に記載の方法。 １５、セラミック泥漿が炭化珪素、二硼化チタン及びそ
    れらの混合物より成る群より選ばれる材料を含んでいる
    、請求項１に記載の方法。 １６、セラミック体が炭化珪素、二硼化チタン及びそれ
    らの混合物より成る群より選ばれる材料を含んでいる、
    請求項１に記載の方法。
JP63311794A 1987-12-09 1988-12-09 多孔質セラミック体の表面の一部分を被覆する方法 Pending JPH01201089A (ja)