JPH0219223B2 - - Google Patents

Info

Publication number
JPH0219223B2
JPH0219223B2 JP1712682A JP1712682A JPH0219223B2 JP H0219223 B2 JPH0219223 B2 JP H0219223B2 JP 1712682 A JP1712682 A JP 1712682A JP 1712682 A JP1712682 A JP 1712682A JP H0219223 B2 JPH0219223 B2 JP H0219223B2
Authority
JP
Japan
Prior art keywords
component
fibers
composite
melting point
fiber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
JP1712682A
Other languages
English (en)
Other versions
JPS58136867A (ja
Inventor
Susumu Tomioka
Masahiko Taniguchi
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JNC Corp
Original Assignee
Chisso Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=11935335&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=JPH0219223(B2) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by Chisso Corp filed Critical Chisso Corp
Priority to JP57017126A priority Critical patent/JPS58136867A/ja
Priority to US06/463,074 priority patent/US4500384A/en
Priority to FI830355A priority patent/FI830355A7/fi
Priority to DK46283A priority patent/DK160326C/da
Priority to KR1019830000432A priority patent/KR880000386B1/ko
Priority to DE8383300608T priority patent/DE3374426D1/de
Priority to EP19830300608 priority patent/EP0086103B2/en
Publication of JPS58136867A publication Critical patent/JPS58136867A/ja
Publication of JPH0219223B2 publication Critical patent/JPH0219223B2/ja
Granted legal-status Critical Current

Description

【発明の詳細な説明】
本発明は不織布の製造方法に関するものであ
る。更に詳しくは熱接着不織布の製造方法に関す
るものである。 融点を異にする繊維形成性重合体を複合成分と
する複合繊維を用いて得られる不織布は特公昭42
―21318、同44―22547、同52―12830等において
公知である。近年不織布の用途の多様化に伴い、
不織布に要求される性能も高度化し出来るだけ少
い不織布重量で高い不織布強力を維持し、かつ、
出来るだけソフトな風合が基本的に要求されて来
ており、単に融点差を有する複合成分から構成さ
れた複合繊維を用いる上記公知の方法によつては
これを満足させることが出来なかつた。 本発明者等は出来るだけ少い不織布重量で出来
るだけ高い不織布強力を維持し、かつ、出来るだ
けソフトな風合を有する不織布の製造方法につき
鋭意研究の結果本発明に到達したものである。 すなわち本発明は、繊維形成性重合体から成る
第１成分を芯成分とし、融点が該第１成分のそれ
より30℃以上低い１種又は２種以上の重合体から
成る第２成分をその平均厚みが1.0〜4.0ミクロン
となる様に鞘成分とした鞘芯型複合繊維（以下単
に複合繊維という事がある）単独から成るまたは
該複合繊維を混合繊維全量に基いて少くとも20重
量％含有する他の繊維との混合繊維から成る繊維
集合体を形成し、該複合繊維の第１成分の融点未
満、第２成分の融点以上で、かつ、10〜100sec-1
の剪断速度で測定した第２成分の見かけ粘度が１
×103〜５×104ポアズとなる様な温度で熱処理す
ることにより第２成分の熱融着により形態を安定
化する事を特徴とする熱接着不織布の製造方法で
ある。 本発明を更に詳しく説明する。 本発明において複合両成分の融点差を30℃以上
と限定する理由は、後述の如く不織布製造におい
て10〜100sec-1の剪断速度で測定した第２成分の
見かけ粘度が１×103〜５×104ポアズとなる様な
温度で熱処理を行うが、このような粘度には第２
成分の融点より少くとも10℃以上高温でないと達
することができず、熱処理時の温度と第１成分の
融点との差が20℃以下であると該熱処理時に複合
繊維に熱収縮等の変形が発生したりして不織布の
寸法安定性を阻害して好ましくない為である。 第２成分を複合繊維の鞘部に配するに際しその
平均厚みを1.0〜4.0ミクロンの範囲と限定する理
由は以下に述べる通りである。 第２成分の平均厚みが1.0ミクロンに達しない
と、第２成分が適正な溶融粘度を示すような熱処
理条件下で複合繊維を熱融着させても融着形成部
の面積が小さくて不織布強力が強い、更に、該熱
処理の前工程で行われる繊維集合体の形成時に複
合繊維が受ける機械的衝撃や摩擦等によつて第２
成分が複合繊維表面より剥離し易くなり、剥離が
発生すると不織布強力は極度に低下する等の欠点
が生ずる。第２成分の平均厚みが4.0ミクロンを
超すと、熱処理の為の昇温過程において第２成分
の軟化点ないし融点附近で第２成分に急激に収縮
力が働き複合繊維表面に凹凸を形成し、その後に
適正な温度にまで昇温し第２成分の見かけ粘度が
低下してもこの凹凸が緩和しきれず第２成分が第
１成分の表面に滴状または球状に存在することと
なり、接着力が低下したり、不織布の風合が硬く
なる等の欠点が生ずる。 第２成分の平均厚みは、公知の鞘芯型複合紡糸
機を用いて紡糸する際の第１成分と第２成分との
複合比及び複合繊維の繊度（デニール）から容易
に算出することができる。 次に、不織布製造のための熱処理温度を第１成
分の融点未満、第２成分の融点以上で、かつ、10
〜100sec-1の剪断速度で測定した第２成分の見か
け粘度が１×103〜５×104ポアズとなる様な温度
と規定する理由を以下に述べる。見かけ粘度が５
×104を超して高い（温度が低い）場合には複合
繊維間の接触部分における第２成分の融着面積が
小さい為に不織布強力が低くなる。このような熱
処理温度で、繊維集合体を機械的に圧縮すること
により融着部分の面積を増した場合には不織布の
風合は硬くなり好ましくない。又、見かけ粘度が
１×103に達せず低い（温度が高い）場合には複
合繊維間の接触部分における第２成分の融着が容
易になりすぎ、融着面積が大きくなりすぎて不織
布はペーパーライトで柔軟性に欠け、硬い風合の
ものになり好ましくない。更に、このような熱処
理温度では、第２成分の平均厚みが１〜４ミクロ
ンの範囲内であつても、第２成分は第１成分上に
滴状又は球状となつて存在し易くなり好ましくな
い。 本発明に用いる複合繊維は、その第２成分が10
〜100sec-1の剪断速度で測定した見かけ粘度が１
×103〜５×104ポアズとなる温度範囲を有し、か
つ、第１成分が前記温度範囲より高いの融点を有
するような複合成分を配したものでなければなら
ない。ここで第２成分の見かけ粘度とは紡糸工程
を経た後の第２成分の見かけ粘度を指すものであ
り、そのような粘度は複合紡糸時の第２成分側と
同一の条件で第２成分のみを単独で紡糸して得ら
れる試料を公知の方法（例えばJIS K7210：高化
式フローテスターを用いる方法）によつて測定す
ることが出来る。 本発明において熱処理して不織布とする繊維集
合体としては、上記の特性を有する複合繊維のみ
から成るもの許りでなく、該複合繊維を混合物中
に少くとも20重量％含有する他の繊維との混合物
から成る繊維集合体も好ましく用いることが出来
る。他の繊維としては不織布製造のための熱処理
時に溶融や大きな熱収縮を起さない繊維であれば
いずれも用いることが出来るが、例えば、木綿、
洋毛等の天然繊維、ビスコースレーヨン、酢酸繊
維素繊維等の半合成繊維、ポリオレフイン繊維、
ポリアミド繊維、ポリエステル繊維、アクリル繊
維等の合成繊維、更にはガラス繊維、アスベスト
等の無機物繊維等の一種又は２種以上の繊維が適
宜選択して用いられ、その使用量は複合繊維との
総量に基いて80重量％以下の割合である。繊維集
合体中の複合繊維の割合が20重量％以下になると
不織布強力が低下して好ましくない。 複合繊維単独又は複合繊維と他の繊維との混合
物を繊維集合体に形成する方法としては、一般に
不織布製造に用いられる公知の方法、例えばカー
ド法、エアーレイ法、乾式パルプ法、湿式抄紙法
等がいずれも使用できる。 上記繊維集合体を複合繊維の低融点成分の熱融
着により不織布化するために施す熱処理方法とし
ては、熱風ドライヤー、サクシヨンドラムドライ
ヤー、ヤンキードライヤー等のドライヤーやフラ
ツトカレダーロール、エンボスロール等のヒート
ロール等のいずれの方式も使用できる。 本発明を実施例によつて更に説明する。なお実
施例中に示された物性値の測定法又は定義をまと
めて示しておく。 不織布強力：JIS L1096に準じ巾５cmの試料片を
つかみ間隔10cm、伸長速度１分間当り100％
で測定した。 不織布風合：５人のパネラーによる官能試験を行
い、全員がソフトであると判定した場合を
○、３名以上がソフトであると判定した場合
を△、３名以上がソフト感に欠けると判定し
た場合を×と評価した。 見かけ粘度：JIS K7210流れ試験方法（参考試
験）に準じ高化式フローテスターを用いて測
定したＱ値より下記の換算式によつて算出し
た。 剪断速度；D′m＝4Q／πr3 ―(1) 剪断応力；tm＝Pr／2l ―(2) 見かけ粘度；η＝4tm／D′m. （３＋dlogD′m／ｄ log tm）
(3) ここで、Ｑは流出量（cm3／sec）、ｒはノズ
ルの半径（＝0.05cm）、ｌはノズルの長さ
（＝1.00cm）であり、測定圧力Ｐとしては
（10，15，25，50，100Kg／cm2）の各値を用い
た。 実施例 １ メルトフローレート15のポリプロピレン（融点
165℃）を第１成分（芯成分）とし、メルトイン
デツクス20のエチレン酢ビコポリマー（酢ビ含量
15％、融点96℃）を第２成分（鞘成分）とし孔径
0.5mm、50孔の紡糸口金を用い265℃で溶融紡糸し
て第１表に示される各種の複合比の未延伸糸を得
た。又、第一成分側のギヤポンプを停止して、第
２成分のみを捲き取り見かけ粘度測定用の試料と
した。これらの未延伸糸をいずれも50℃で4.0倍
に延伸し、スタフアーボツクスで捲縮を与えた後
繊維長51mmにカツトすることにより第１表に示し
た鞘部平均厚みを有する３デニールの複合繊維を
得た。 これらの複合繊維をエアーレイ法により約100
ｇ／m2のウエツブとした後エアーサクシヨンタイ
プのドライヤーにより所定温度でいずれも30秒間
熱処理して不織布を得た。得られた不織布の強力
並びに風合の評価を第１表に示した。
【表】 実施例 ２ 固有粘度0.65のポリエチレンテレフタレート
（融点258℃）を第１成分とし、メルトインデツク
ス23の高密度ポリエチレン（融点130℃）を第２
成分とし、実施例１と同様にして295℃で溶融紡
糸した。得られた未延伸糸を110℃で2.5倍に延伸
し、スタフアーボツクスで捲縮を与えた後繊維長
64mmにカツトすることにより第２表に示した鞘部
平均厚みを有する３デニールの複合繊維を得た。 これらの複合繊維をカード法により約20ｇ／m2
のウエツブとした後、金属フラツトロールとコツ
トンロールを組み合せたカレンダーロールにおい
て金属フラツトロールを所定の温度とし、５Kg／
cmの圧力で加熱処理して不織布を得た。得られた
不織布の強力と風合を評価した製造条件と対比し
て第２表に示した。
【表】 実施例１及び２の検討結果より、第２成分（鞘
部分）の平均厚みが１〜４ミクロンの複合繊維か
ら成る繊維集合体を、第１成分の融点以下、第２
成分の融点以上で、かつ、10〜100sec-1の剪断速
度で測定した第２成分の見かけ粘度が１×103〜
５×104ポアズとなる様な温度で熱処理すること
によつて高い不織布強力と同時に良好な風合の不
織布が得られる事がわかる。 実施例 ３ 実施例１（試験番号１―３）で用いた複合繊維
20重量％と、ポリエステル繊維（6d×64mm、融
点258℃）80重量％とから成る混合物を用いカー
ド法により約200ｇ／m2のウエツブとした後エア
ーサクシヨンタイプのドライヤーにより135℃で
30秒間熱処理して不織布を得た。この不織布はキ
ルト製品として充分な強力（7.4Kg）を有し、か
つ、表面の毛羽立ちの少いソフトな風合のもので
あつた。

Claims (1)

    【特許請求の範囲】
  1. １ 繊維形成性重合体から成る第１成分を芯成分
    とし、融点が該第１成分のそれより30℃以上低い
    １種又は２種以上の重合体から成る第２成分をそ
    の平均厚みが1.0〜4.0ミクロンとなる様に鞘成分
    とした鞘芯型複合繊維（以下単に複合繊維という
    事がある）単独から成るまたは該複合繊維を混合
    繊維全量に基いて少くとも20重量％含有する他の
    繊維との混合繊維から成る繊維集合体を形成し、
    該複合繊維の第１成分の融点未満、第２成分の融
    点以上で、かつ、10〜100sec-1の剪断速度で測定
    した第２成分の見かけ粘度が１×103〜５×104ボ
    アズとなる様な温度で熱処理することにより第２
    成分の熱融着により形態を安定化する事を特徴と
    する熱接着不織布の製造方法。
JP57017126A 1982-02-04 1982-02-05 熱接着不織布の製造方法 Granted JPS58136867A (ja)