JPH02253094A - エレクトロフュージョン継手 - Google Patents

エレクトロフュージョン継手

Info

Publication number
JPH02253094A
JPH02253094A JP1072336A JP7233689A JPH02253094A JP H02253094 A JPH02253094 A JP H02253094A JP 1072336 A JP1072336 A JP 1072336A JP 7233689 A JP7233689 A JP 7233689A JP H02253094 A JPH02253094 A JP H02253094A
Authority
JP
Japan
Prior art keywords
thermoplastic resin
resin layer
crosslinked
joint
layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP1072336A
Other languages
English (en)
Other versions
JP2545973B2 (ja
Inventor
Hiroyuki Nishimura
寛之 西村
Akio Nakashiba
中芝　明雄
Fumio Hase
文夫 長谷
Kazunori Mito
水戸　和憲
Toshio Shibabuchi
利夫 柴渕
Mikio Nakaoka
幹夫 中岡
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shinwa Sangyo Co Ltd
Mitsui Petrochemical Industries Ltd
Osaka Gas Co Ltd
Original Assignee
Shinwa Sangyo Co Ltd
Mitsui Petrochemical Industries Ltd
Osaka Gas Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shinwa Sangyo Co Ltd, Mitsui Petrochemical Industries Ltd, Osaka Gas Co Ltd filed Critical Shinwa Sangyo Co Ltd
Priority to JP1072336A priority Critical patent/JP2545973B2/ja
Publication of JPH02253094A publication Critical patent/JPH02253094A/ja
Application granted granted Critical
Publication of JP2545973B2 publication Critical patent/JP2545973B2/ja
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】 〔産業上の利用分野〕 この発明はポリオレフィンパイプ等の被接合体、特に温
水用の導管を接合するためのエレクトロフュージョン継
手に関するものである。
〔従来の技術〕
温水用の導管として、シラン架橋ポリエチレン等の架橋
ポリオレフィンパイプが使用されている。
この架橋ポリオレフィンは耐熱性、高温クリープ特性な
どの高温性能に優れ、形状保持性能を有するが、非架橋
ポリオレフィンとは異なり、被接合体に融着を行うこと
ができない。従って非架橋のポリオレフィンパイプの継
手として使用されているエレクトロフュージョン継手を
、架橋ポリオレフィンパイプの継手として利用すること
はできない。また架橋ポリオレフィンを使用してエレク
トロフュージョン継手を形成することもできない。
従って架橋ポリオレフィンパイプに接合するための継手
、あるいは架橋ポリオレフィンを用いた継手としては、
機械的な接合を行う継手が使用されている。ところが温
水管の場合は使用圧力が高く、強度が要求されるため構
造的に複雑となり、配管の作業性が悪いとともに、圧縮
によるシールを行うため、管のクリープによるシール性
能の低下など、長期的な性能低下が起こるという問題点
がある。
〔発明が解決しようとする課題〕
本発明は上記問題点を解決するため、架橋ポリオレフィ
ン等の熱可塑性樹脂を使用して耐熱強度を高め、かつ接
合面全体で均一に融着を行うことによりシール性能およ
び耐圧強度を高め、作業性も良好なエレクトロフュージ
ョン継手を提供することである。
〔課題な解決するための手段〕
本発明は、継手本体を形成する架橋熱可塑性樹脂層と、
この架橋熱可塑性樹脂層の内側の被接合体に接する位置
に、架橋熱可塑性樹脂層と一体的に形成された非架橋熱
可塑性樹脂層と、この非架橋熱可塑性樹脂層の内部、外
表面、または内表面に設けられた電熱線とを備え、前記
非架橋熱可塑性樹脂層は、中央部が厚肉で、両端部が薄
肉になるように形成されていることを特徴とするエレク
トロフュージョン継手である。
本発明においては、架橋熱可塑性樹脂層と非架橋熱可塑
性樹脂層とは隣接して一体化している。
架橋熱可塑性樹脂は融着性を有しないため、架橋後の架
橋熱可塑性樹脂と非架橋熱可塑性樹脂を押出成形、射出
成形等により成形しても、それぞれの層は分離して一体
化しないが、未架橋の架橋性熱可塑性樹脂と非架橋熱可
塑性樹脂とを加熱成形して一体化し、その後架橋性熱可
塑性樹脂製架橋させると、架橋熱可塑性樹脂と非架橋熱
可塑性樹脂が一体化した積層体が得られる。本発明では
このように架橋熱可塑性樹脂層と非架橋熱可塑性樹脂層
が一体化した積層体を使用する。
架橋熱可塑性樹脂は、熱可塑性樹脂の分子間架橋により
立体構造となったものであり、シラン架橋熱可塑性樹脂
、ジビニルベンゼン架橋熱可塑性樹脂などの架橋剤によ
り架橋したもののほか、有機過酸化物、放射線等により
直接架橋したものでもよい。
非架橋熱可塑性樹脂は一般に熱可塑性樹脂として使用さ
れている架橋性を有しないポリオレフィン等の樹脂であ
る。非架橋熱可塑性樹脂層は中央部はど肉厚が厚く、両
端部はど薄肉になるように形成する。
本発明に係わる熱可塑性樹脂として具体的にはポリオレ
フィンを例示でき、ポリオレフィンとしては、炭素数２
〜２０．好ましくは２〜１２のα−オレフィンの単独ま
たは共重合体があげられる。好ましいα−オレフィンと
しては、エチレン、プロピレン、ブテン−１，４−メチ
ルペンテン−１などがあげられる。
〔作　用〕
本発明のエレクトロフュージョン継手は、中央部はど肉
厚が厚く、両端部はど薄肉になるように成形された非架
橋熱可塑性樹脂層の内部、外表面、または内表面に電熱
線を埋設し、あるいは未架橋熱可塑性樹脂層表面に巻き
付けた状態で、架橋性熱可塑性樹脂層と積層一体止した
後、架橋性熱可塑性樹脂層を架橋させて架橋熱可塑性樹
脂層を形成することにより製造される。
こうして製造されたエレクトロフュージョン継手は、熱
可塑性樹脂チューブ等の被接合体の接合部に、非架橋熱
可塑性樹脂層が被接合体と接するように取付け、電熱線
に通電すると、非架橋熱可塑性樹脂層が溶融して被接合
体に一体的に融着する。
このとき非架橋熱可塑性樹脂層の中央部はど熱が蓄積さ
れやすいが、非架橋熱可塑性樹脂層は、中央部が厚肉で
、両端部が薄肉になるように形成されているので、中央
部はど多量に溶融する。この結果、溶融した非架橋熱可
塑性樹脂層の中央部の溶融した樹脂は容易に流動できる
ので、均一な圧力上昇が生じる。
被接合体としては表層または全体が熱可塑性樹脂、特に
相溶性を有する樹脂からなるものが好ましく、非架橋の
熱可塑性樹脂からなるものは特に優れた融着性を示す。
〔実施例〕
以下、本発明の実施例を図面により説明する。
第１図、第２図、第３図は別の実施例のエレクトロフュ
ージョン継手の右半分を断面で示す正面図であり、左右
対称に構成されている。図において、１はエレン１ヘロ
フユージヨン継手で、継手本体を形成する管状の架橋ポ
リオレフィン層２と、この架橋ポリオレフィン層２の内
側の被接合体５、６に接する位置に、架橋ポリオレフィ
ン層２と一体的に形成された非架橋ポリオレフィン層３
と、この非架橋ポリオレフィン層３の内部、外表面また
は内表面にコイル状に設けられた電熱線４とを有する。
非架橋ポリオレフィン層３は中央部が厚内で、両端部が
薄肉になるように形成されている。
被接合体５．６はポリエチレン等の熱可塑性樹脂層を有
する管からなり、全体が融着性の熱可塑性樹脂からなる
ものでもよいが、架橋ポリオレフィン等の耐熱性材料を
用いる場合は、外表面を融着性の熱可塑性樹脂で被覆し
たものを用いる。架橋ポリオレフィン層２は被接合体５
．６の接合部（突合せ部）７付近を全周にわたって覆う
管状の構造であり、その長手方向の両側の各被接合体５
．６に対応する部分の内周に非架橋ポリオレフィン層３
が積層され、第１図ではその内部に電熱線４が埋設され
、第２図ではその外表面に、また第３図では内表面に埋
設されている。
」１記のエレン１−ロフユージヨン継手１は、中央部が
厚肉で、両端部が薄肉になるように形成された非架橋ポ
リオレフィン中３中に電熱線４を埋設または巻き付けた
状態で、ポリオレフィン中に架橋剤、架橋助剤、触媒等
を含む架橋性ポリオレフィン層と積層一体止した後、上
記架橋性ポリオレフィン層を架橋させて架橋ポリオレフ
ィン層２を形成することにより製造される。
こうして製造されたエレクトロフュージョン継手１は、
ポリオレフィンチューブ等の被接合体５．６の接合部７
付近に、非架橋ポリオレフィン層３が被接合体５．６と
接するように取付け、電熱線４に通電すると、非架橋ポ
リオレフィン層３が均一に溶融して被接合体５．６に融
着して一体化する。
この融着時には、非架橋ポリオレフィン層３は、中央部
が厚肉で両端部が薄肉になるように形成されているので
、中央部に蓄積される多量の熱量は厚肉の非架橋ポリオ
レフィンＮ３の溶融に消費され、両端部付近を溶融する
ために必要な熱量は少なくなる。そして溶融した中央部
の非架橋ポリオレフィンは容易に流動できるので均一な
圧力上昇が生じる。この結果非架橋ポリオレフィン層３
と被接合体５．６との融着はむらのない均一なものとな
る。
上記のエレクトロフュージョン継手１は、継手本体を形
成する管状の架橋ポリオレフィン層２が耐熱強度を負担
するので、給湯管等の接合に用いても形状保持性に優れ
る。−ｊ非架橋ポリオレフィンＭ３が架橋ポリオレフィ
ン層２と一体化した状態で、被接合体５．６に均一に融
着して一体化するため、シール性および耐圧性に優れ、
給湯管に用いても長期にわたってシール性を保持する。
なお、上記実施例では継手１は左右対称となるように、
両側に非架橋ポリオレフィン層３および電熱線４を設け
た例を示したが、片側例えば第１〜３図の右側を図のよ
うに構成し、反対側例えば左側にはねじ等の接続部を有
する接続部材を取付けて被接合体５．６と機械的に接合
するようにしてもよい。また電熱線４を非架橋ポリオレ
フィン層３の外表面または内表面に設ける場合には、非
架橋ポリオレフィン層３または被接合体５．６に巻き付
けてもよい。
〔発明の効果〕
本発明によれば、中央部が厚肉で、両端部が薄肉になる
ように形成された非架橋熱可塑性樹脂層に架橋熱可塑性
樹脂層を一体化し、その内部、外表面または内表面に電
熱線を設けたので、非架橋熱可塑性樹脂層の温度分布を
均一にして、全体を均一に融着させ、シール性、耐圧性
および耐熱強度等の高温性能に優れ、かつ取付作業等の
作業性にも優れたエレクトロフュージョン継手が得られ
る。
【図面の簡単な説明】
第１図ないし第３図は別の実施例の一部を断面で示す正
面図である。 各図中、同一符号は同一または相当部分を示し、２は架
橋ポリオレフィン層、３は非架橋ポリオレフィン層、４
は電熱線、５．６は被接合体である。 代理人　弁理士　柳　原　　　成

Claims (1)

    【特許請求の範囲】
  1. （１）継手本体を形成する架橋熱可塑性樹脂層と、この
    架橋熱可塑性樹脂層の内側の被接合体に接する位置に、
    架橋熱可塑性樹脂層と一体的に形成された非架橋熱可塑
    性樹脂層と、この非架橋熱可塑性樹脂層の内部、外表面
    、または内表面に設けられた電熱線とを備え、前記非架
    橋熱可塑性樹脂層は、中央部が厚肉で、両端部が薄肉に
    なるように形成されていることを特徴とするエレクトロ
    フュージョン継手。
JP1072336A 1989-03-24 1989-03-24 エレクトロフュージョン継手 Expired - Lifetime JP2545973B2 (ja)