JPH0228901Y2 - - Google Patents
Info
- Publication number
- JPH0228901Y2 JPH0228901Y2 JP1986015451U JP1545186U JPH0228901Y2 JP H0228901 Y2 JPH0228901 Y2 JP H0228901Y2 JP 1986015451 U JP1986015451 U JP 1986015451U JP 1545186 U JP1545186 U JP 1545186U JP H0228901 Y2 JPH0228901 Y2 JP H0228901Y2
- Authority
- JP
- Japan
- Prior art keywords
- weight
- resin component
- vinyl acetate
- sanitary
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【考案の詳細な説明】 （産業上の利用分野） 本考案は生理用シヨーツに関するものである。[Detailed explanation of the idea] (Industrial application field) The present invention relates to menstrual shorts.
（従来の技術及び問題点）
従来、生理用シヨーツとして販売されているも
のは、生理用品のずれ止め効果、反復しての洗濯
性、柔軟性等の点において問題があつた。(Prior Art and Problems) Conventionally, sanitary shorts sold as sanitary shorts have had problems in terms of the anti-slip effect of sanitary products, ease of repeated washing, flexibility, etc.
また、実開昭58−188017号公報に示されるもの
が提案されている。この公報に示されるものは、
シヨーツ主体の股部内面に発泡性インクを印刷
し、更にその上面に発泡性インクからなる多数の
穿条を設けたものがしめされているが、該公報に
示されたものでは、具体的に実施することができ
ず、商品化されていない。 Furthermore, the method shown in Japanese Utility Model Application Publication No. 58-188017 has been proposed. What is shown in this bulletin is
The publication shows a shorts with foaming ink printed on the inner surface of the crotch area and a large number of perforations made of foaming ink on the top surface, but the publication does not specifically explain It cannot be implemented and has not been commercialized.
（問題点を解決する手段）
本考案は、生理用品当接部に、発泡体により形
成されたずれ止めが設けられてなる生理用シヨー
ツであつて、発泡体がアクリル樹脂、酢酸ビニー
ル樹脂、エチルセルロース、発泡剤及び水性ウレ
タンからなり、しかも、アクリル樹脂成分を総量
40〜50重量％含み、アクリル樹脂成分100重量部
に対して酢酸ビニール樹脂成分が５〜10重量部の
割合としたことを特徴とする生理用シヨーツであ
る。(Means for Solving the Problems) The present invention is a sanitary short in which a slip stopper made of a foam is provided in the sanitary product contacting part, and the foam is made of acrylic resin, vinyl acetate resin, ethyl cellulose, etc. , consists of a foaming agent and water-based urethane, and also contains a total amount of acrylic resin component.
These sanitary shorts are characterized in that the vinyl acetate resin component is contained in an amount of 40 to 50% by weight, and the ratio of the vinyl acetate resin component to 100 parts by weight of the acrylic resin component is 5 to 10 parts by weight.
アクリル樹脂としては、アクリル酸およびその
誘導体を重合したものをいい、アクリル酸および
そのエステル、アクリルアミド、アクリロニトリ
ル、メタクリル酸およびそのエステルなどの重合
体および共重合体を包含する。 The acrylic resin refers to one obtained by polymerizing acrylic acid and its derivatives, and includes polymers and copolymers of acrylic acid and its esters, acrylamide, acrylonitrile, methacrylic acid and its esters.
発泡剤としてはたとえば炭酸水素ナトリウム、
炭酸アンモニウム、酢酸アミル、酢酸ブチル、ジ
アゾアミノベンゼン、アゾビスイソブチロニトリ
ル、ベンゾイルパーオキシド、硝酸アンモニウ
ム、炭酸カルシウム、硫酸アルミニウムと炭酸水
素ナトリウムの混合物などがある。 Examples of blowing agents include sodium hydrogen carbonate,
Examples include ammonium carbonate, amyl acetate, butyl acetate, diazoaminobenzene, azobisisobutyronitrile, benzoyl peroxide, ammonium nitrate, calcium carbonate, and a mixture of aluminum sulfate and sodium bicarbonate.
（作用）
アルリル樹脂成分および酢酸ビニール樹脂成分
を総量40〜50重量％含むものであることにより、
強靭性の点ですぐれ、また、アクリル樹脂成分
100重量部に対して酢酸ビニール樹脂成分が５〜
10重量部の割合であることにより、ずれ止めの柔
軟性の点で優れる。(Function) By containing 40 to 50% by weight of allyl resin component and vinyl acetate resin component,
It has excellent toughness and also contains acrylic resin components.
Vinyl acetate resin component is 5 to 100 parts by weight
By having a proportion of 10 parts by weight, the flexibility of preventing slippage is excellent.
そして、アクリル樹脂、酢酸ビニール、エチル
セルロース、溌泡剤及び水性ウレタンからなり、
しかも、アクリル樹脂成分酢酸ビニール樹脂成分
を総量40〜50重量％含み、アクリル樹脂成分100
重量部に対して酢酸ビニール樹脂成分が５〜10重
量部の割合とした発泡体を生理用品当接部に形成
したことにより、生理用品のずれ止め効果におい
て優れた効果が得られた。 It is made of acrylic resin, vinyl acetate, ethyl cellulose, foaming agent, and water-based urethane.
Moreover, the total amount of acrylic resin component vinyl acetate resin component is 40 to 50% by weight, and the acrylic resin component is 100% by weight.
By forming a foam containing 5 to 10 parts by weight of the vinyl acetate resin component in the contacting part of the sanitary product, an excellent effect of preventing the sanitary product from slipping was obtained.
（実施例）
以下図面を参照しながら、実施例につき説明す
る。(Example) An example will be described below with reference to the drawings.
１は生理用シヨーツであり、シヨーツの股部２
内面の生理用品当接部３に布部材４が縫着されて
おり、この布部材４にずれ止め５が形成されてい
る。ずれ止め５は、アクリル樹脂40重量％、酢酸
ビニール樹脂２重量％、エチルセルロース0.2重
量％、発泡剤9.0％、水48.8重量％からなる水性
エマルジヨン100重量部に対して水性ウレタン15
重量部を混合し、これを防水性能を有する布地上
に規則的または不規則的に多数点在させた後、常
温で約６時間乾燥させ、110〜120℃の乾燥器中で
水蒸気を約５秒間噴射させて発泡させてなる。な
お、発泡は赤外線の照射により行つてもよい。 1 is menstrual shorts, and the crotch part 2 of the shorts
A cloth member 4 is sewn to the sanitary product abutting portion 3 on the inner surface, and a slip stopper 5 is formed on this cloth member 4. The anti-slip material 5 contains 15 parts by weight of water-based urethane based on 100 parts by weight of an aqueous emulsion consisting of 40% by weight of acrylic resin, 2% by weight of vinyl acetate resin, 0.2% by weight of ethyl cellulose, 9.0% of a foaming agent, and 48.8% by weight of water.
After mixing the parts by weight and dotting the mixture regularly or irregularly on a waterproof fabric, the mixture is dried at room temperature for about 6 hours, and water vapor is removed by about 5% in a dryer at 110-120℃. Spray for seconds to foam. Note that foaming may be performed by irradiation with infrared rays.
（考案の効果）
このようになるシヨーツを着用して生理用品の
ずれ状態をみたところ、水分の多い状態において
12時間経過しても、ほとんどずれは生じず、ずれ
止めに爪をたてても剥離がみられなかつた。また
通常の洗濯を10分として、洗濯機により100回洗
濯を行つたが剥離はなかつた。(Effects of the invention) When we looked at the slippage of sanitary products while wearing shorts like this, we found that when there is a lot of moisture,
Even after 12 hours had passed, almost no shearing occurred, and no peeling was observed even when I used my nails to prevent it from slipping. In addition, the film was washed 100 times in a washing machine with a normal washing time of 10 minutes, but no peeling occurred.
すなわち、ずれ止め効果において優れた効果を
有するとともに、洗濯機による洗濯によつても剥
離がなかつた。 That is, it had an excellent anti-slip effect and did not peel off even when washed in a washing machine.
また、実開昭58−188017号公報に示されるもの
により作成したもの（従来品という）と比較した
ところつぎの結果を得た。 In addition, the following results were obtained when compared with a product prepared by the method disclosed in Japanese Utility Model Application Publication No. 58-188017 (referred to as a conventional product).
試験１
はぶらしによる摩擦
従来品
50回目で一部欠け落ち、100回目で殆ど全
部剥離した。 Test 1 Friction due to hanging Conventional product Partially chipped off after the 50th test, and almost completely peeled off after the 100th test.
本考案品
300回こすつたけれども剥離はみられなか
つた。 Although this product was rubbed 300 times, no peeling was observed.
試験２
デニム生地により摩擦
従来品
５〜６回目より欠け落ちが始まり、20回目
で殆ど全部剥離した。 Test 2 Friction due to denim fabric Conventional product It started chipping off after the 5th or 6th time, and almost completely peeled off at the 20th time.
本考案品
100回こすつたけれども剥離はみられなか
つた。 Although the product of this invention was rubbed 100 times, no peeling was observed.
試験３
牛皮裏面による摩擦
従来品
８回目で一部欠け落ち25回目で殆ど全部剥
離した。 Test 3 Friction with the back side of cowhide Conventional product Partially chipped off after the 8th test, and almost completely peeled off after the 25th test.
本考案品
100回こすつたけれども剥離はみられなか
つた。 Although this product was rubbed 100 times, no peeling was observed.
試験４
爪によるひつかき摩擦
従来品
３〜４回目より剥離し始め８回目で殆ど全
部剥離した。 Test 4 Scratching with fingernails Conventional product Peeling started after the 3rd or 4th try, and almost completely peeled off after the 8th try.
本考案品
50回引つ掻き摩擦をしたけれども殆ど剥離
しなかつた。 Although the product of this invention was scratched and rubbed 50 times, it hardly peeled off.
以上のとおり、本考案は、ずれ止め効果におい
て優れていることにあわせて、発泡体であるので
柔軟で肌ざわりも柔らかく、しかもずれ止めを構
成する発泡体の剥離がほとんどないものである。 As described above, the present invention not only has an excellent anti-slip effect, but is also flexible and soft to the touch because it is made of foam, and there is almost no peeling of the foam that constitutes the anti-slip material.
第１図は本考案の実施例を示す断面図、第２図
はずれ止めの断面図である。
１……生理用シヨーツ、２……股部、３……生
理用品当接部、４……布部材、５……ずれ止め。
FIG. 1 is a sectional view showing an embodiment of the present invention, and FIG. 2 is a sectional view of a stopper. 1... Sanitary shorts, 2... Crotch part, 3... Sanitary product contact part, 4... Cloth member, 5... Slip prevention.
Claims (1)
れ止めが設けられてなる生理用シヨーツであつ
て、 発泡体がアクリル樹脂、酢酸ビニール、エチル
セルロース、発泡剤及び水性ウレタンからなり、 しかも、アクリル樹脂成分と酢酸ビニール樹脂
成分を総量40〜50重量％含み、アクリル樹脂成分
100重量部に対して酢酸ビニール樹脂成分が５〜
10重量部の割合としたことを特徴とする生理用シ
ヨーツ。[Scope of Claim for Utility Model Registration] Sanitary shorts comprising a slip stopper formed of foam in the sanitary product contacting part, where the foam is made of acrylic resin, vinyl acetate, ethyl cellulose, a foaming agent, and an aqueous material. It is made of urethane, and contains a total of 40 to 50% by weight of acrylic resin component and vinyl acetate resin component.
Vinyl acetate resin component is 5 to 100 parts by weight
Sanitary shorts characterized by having a proportion of 10 parts by weight.