JPH0244902B2 - Nanjiseiseimitsubuhinnohyomenkokashorihoho - Google Patents
NanjiseiseimitsubuhinnohyomenkokashorihohoInfo
- Publication number
- JPH0244902B2 JPH0244902B2 JP27199085A JP27199085A JPH0244902B2 JP H0244902 B2 JPH0244902 B2 JP H0244902B2 JP 27199085 A JP27199085 A JP 27199085A JP 27199085 A JP27199085 A JP 27199085A JP H0244902 B2 JPH0244902 B2 JP H0244902B2
- Authority
- JP
- Japan
- Prior art keywords
- plating
- degreasing
- soft magnetic
- precision parts
- treatment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】
［産業上の利用分野］
この発明は、プリンターの印字駆動部に使用さ
れるアーマチアやヨークのように、磁気回路を構
成するとともに耐摩耗性が要求される精密部品の
表面硬化処理方法に関するものである。
れるアーマチアやヨークのように、磁気回路を構
成するとともに耐摩耗性が要求される精密部品の
表面硬化処理方法に関するものである。
［従来の技術］
従来において、軟磁特性が要求される精密部
品、たとえばプリンターの印字駆動部のアーマチ
ア、ヨーク等には、電磁軟鉄、ケイ素鋼等の表面
に防錆および耐摩耗性を付与する目的でNiメツ
キ、Znメツキ、Crメツキ、Ni−Ｐ無電解メツキ
などがほどこされている。
品、たとえばプリンターの印字駆動部のアーマチ
ア、ヨーク等には、電磁軟鉄、ケイ素鋼等の表面
に防錆および耐摩耗性を付与する目的でNiメツ
キ、Znメツキ、Crメツキ、Ni−Ｐ無電解メツキ
などがほどこされている。
［発明が解決しようとする問題点］
上記従来例において、Niメツキ、Znメツキは
表面硬度がHV400程度であり耐摩耗性で問題が
ある。CrメツキはHV800程度であり耐久性は有
利であるが電気メツキのため部品へのメツキの付
き回りにムラがあり、量産上不適当である。Ni
−Ｐメツキでも耐摩耗性がHV400以下と低いの
で問題である。なおNi−Ｐメツキ後400℃前後で
熱処理を行なうとHV800程度に向上するが、そ
の場合材料本来の磁気特性に劣化が生じるため使
用することができない。
表面硬度がHV400程度であり耐摩耗性で問題が
ある。CrメツキはHV800程度であり耐久性は有
利であるが電気メツキのため部品へのメツキの付
き回りにムラがあり、量産上不適当である。Ni
−Ｐメツキでも耐摩耗性がHV400以下と低いの
で問題である。なおNi−Ｐメツキ後400℃前後で
熱処理を行なうとHV800程度に向上するが、そ
の場合材料本来の磁気特性に劣化が生じるため使
用することができない。
［問題点を解決するための手段］
この発明はこうした従来例における問題点を解
決するためのものであり、ケイ素鋼部材に対し、
まず、磁気特性を得る目的、および表面の酸化膜
の形成防止を兼ねて真空中において焼鈍し、つい
でメツキのための前処理として、有機溶剤による
脱脂処理、アルカリによる脱脂処理、酸洗に処
理、さらに酸とインヒビターの混合液によるシリ
コン酸化物除去処理を施した後、コバルト・リン
系無電解化学メツキを施すことにより、被処理材
の磁性特性を損なうことなく、耐摩耗性の向上し
た表面硬化処理をするものである。
決するためのものであり、ケイ素鋼部材に対し、
まず、磁気特性を得る目的、および表面の酸化膜
の形成防止を兼ねて真空中において焼鈍し、つい
でメツキのための前処理として、有機溶剤による
脱脂処理、アルカリによる脱脂処理、酸洗に処
理、さらに酸とインヒビターの混合液によるシリ
コン酸化物除去処理を施した後、コバルト・リン
系無電解化学メツキを施すことにより、被処理材
の磁性特性を損なうことなく、耐摩耗性の向上し
た表面硬化処理をするものである。
［実施例］
まず素材として３％ケイ素鋼を用い、所定の部
品形状に加工しておく。このケイ素鋼は磁気特性
はすぐれているが、表面が活性のため酸化膜
（SiO2）を形成しやすい材料である。
品形状に加工しておく。このケイ素鋼は磁気特性
はすぐれているが、表面が活性のため酸化膜
（SiO2）を形成しやすい材料である。
本発明による処理法は、第一ステツプとして、
ケイ素鋼本来の磁気特性を得る目的とともにケイ
素鋼表面に酸化膜の形成防止を兼ねて、真空中に
おいて850℃、１時間の焼鈍をおこなう。この場
合、真空雰囲気以外のN2、Ar等の無酸化雰囲気
では表面見かけ上光輝に仕上がるが、最終的なメ
ツキ仕上り後の密着性が不十分であり、真空雰囲
気による熱処理が必要とされる。
ケイ素鋼本来の磁気特性を得る目的とともにケイ
素鋼表面に酸化膜の形成防止を兼ねて、真空中に
おいて850℃、１時間の焼鈍をおこなう。この場
合、真空雰囲気以外のN2、Ar等の無酸化雰囲気
では表面見かけ上光輝に仕上がるが、最終的なメ
ツキ仕上り後の密着性が不十分であり、真空雰囲
気による熱処理が必要とされる。
第二のステツプとして、無電解Coメツキの前
処理として次の工程の処理をする。
処理として次の工程の処理をする。
(1) 脱脂処理として、主に鉱物油の除去を目的と
して有機溶剤による処理をする。有機溶剤とし
て、例えば１−１−１トリクロルエタンの液中
に超音波をかけて約３分間浸漬する。
して有機溶剤による処理をする。有機溶剤とし
て、例えば１−１−１トリクロルエタンの液中
に超音波をかけて約３分間浸漬する。
(2) ついで第二の脱脂処理として、主に動、植物
油の除去を目的として、アルカリと表面活性剤
の混合液、たとえばオルソケイ酸ソーダのよう
な市販のアルカリ脱脂剤で、被処理材を揺動し
ながら約３分間液中に浸漬する。
油の除去を目的として、アルカリと表面活性剤
の混合液、たとえばオルソケイ酸ソーダのよう
な市販のアルカリ脱脂剤で、被処理材を揺動し
ながら約３分間液中に浸漬する。
(3) つぎに主に鉄の酸化物の除去を目的として、
７％の塩酸水溶液中で約10〜30秒被処理材を揺
動しながら浸漬する。
７％の塩酸水溶液中で約10〜30秒被処理材を揺
動しながら浸漬する。
(4) さらに主にシリコンの酸化物の除去を目的と
して、フツ素化合物を主成分とした、酸とイン
ヒビターの混合液の希釈液中に被処理物を揺動
しながら10〜30秒間浸漬する。
して、フツ素化合物を主成分とした、酸とイン
ヒビターの混合液の希釈液中に被処理物を揺動
しながら10〜30秒間浸漬する。
上記(1)〜(4)の前処理を施した後、最後に被処理
物の耐久性を上げる目的で、ジ亜リン酸ソーダを
還元剤としたコバルト無電解メツキ液中に浸漬し
て、コバルトに４〜６％程度のリンを添加した無
電解化学Coメツキを10〜20μｍ程度付着させる。
10μｍ未満では十分な耐久性を得ることはでき
ず、20μｍを超えると量産性の点から問題があ
る。
物の耐久性を上げる目的で、ジ亜リン酸ソーダを
還元剤としたコバルト無電解メツキ液中に浸漬し
て、コバルトに４〜６％程度のリンを添加した無
電解化学Coメツキを10〜20μｍ程度付着させる。
10μｍ未満では十分な耐久性を得ることはでき
ず、20μｍを超えると量産性の点から問題があ
る。
以上の工程を経て得られた被処理材はCo−Ｐ
系の化学メツキの表面硬度はHV400〜500であ
り、従来のNiメツキに近いものであるが、潤滑
性が保持されているため、耐摩耗性が必要とされ
る精密部品に適したものである。
系の化学メツキの表面硬度はHV400〜500であ
り、従来のNiメツキに近いものであるが、潤滑
性が保持されているため、耐摩耗性が必要とされ
る精密部品に適したものである。
インバクト型ドツドプリンタの印字機構のヨー
クに本発明の処理を施したものを用いて、従来の
Niメツキのものを使つたプリンタと印字回数を
比較すると、従来のものでは3000万字程度の耐久
性であつたのに対し、本発明のものでは約２億字
と耐久性が飛躍的に向上した。
クに本発明の処理を施したものを用いて、従来の
Niメツキのものを使つたプリンタと印字回数を
比較すると、従来のものでは3000万字程度の耐久
性であつたのに対し、本発明のものでは約２億字
と耐久性が飛躍的に向上した。
［発明の効果］
この発明によれば、軟磁性精密部品に対し、磁
性特性を保ちながら、表面硬度とともに潤滑性を
も付与することができ、耐久性を向上させること
ができる。
性特性を保ちながら、表面硬度とともに潤滑性を
も付与することができ、耐久性を向上させること
ができる。
Claims (1)
- 【特許請求の範囲】 １ 軟磁性ケイ素鋼よりなる精密部品に対し、 真空中で焼鈍する工程と、 メツキの前処理として、有機溶剤による脱脂処
理、アルカリによる脱脂処理、酸洗に処理、さら
に酸とインヒビターの混合液によるシリコン酸化
物除去処理を順次施す工程と、 コバルト・リン系無電解化学メツキを施す工程
とを含む軟磁性精密部品の表面硬化処理方法。