JPH0251960B2 - - Google Patents

Info

Publication number
JPH0251960B2
JPH0251960B2 JP59502611A JP50261184A JPH0251960B2 JP H0251960 B2 JPH0251960 B2 JP H0251960B2 JP 59502611 A JP59502611 A JP 59502611A JP 50261184 A JP50261184 A JP 50261184A JP H0251960 B2 JPH0251960 B2 JP H0251960B2
Authority
JP
Japan
Prior art keywords
lubricant
vehicle
composition
wax
weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
JP59502611A
Other languages
English (en)
Other versions
JPS60501814A (ja
Inventor
Deiiserumu Hesu
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Publication of JPS60501814A publication Critical patent/JPS60501814A/ja
Publication of JPH0251960B2 publication Critical patent/JPH0251960B2/ja
Granted legal-status Critical Current

Description

【図面の簡単な説明】
図は、この発明に係る潤滑剤の一実施例を示す
断面図である。

Claims (1)

  1. 【特許請求の範囲】 １ 織物に接続された取付具、特に衣服に縫い付
    けたジツパーに用いる組成物において、 水溶性ビヒクルと該ビヒクルに含まれた少なく
    とも一つの潤滑物質より成る潤滑性の物質の組成
    物であつて、 該水溶性ビヒクルが該物質の組成物の75〜95重
    量％を占め、残部は少なくとも一つの潤滑物質で
    あり、 該ビヒクルが大体、一価アルコール、多価アル
    コール、そのようなアルコールから誘導されたエ
    ーテル、そのようなアルコールのエステルより成
    る群から選ばれるビヒクルであり、 少なくとも一つの潤滑物質がワツクスであるこ
    とを特徴とする組成物。 ２ 潤滑物質を一つ以上含む請求の範囲第１項に
    記載の物質の組成物において、そのような複数の
    潤滑物質が、該組成物中の一つの潤滑物質の粒子
    が該組成物中のもう一つのそのような物質のもの
    と粒子の大きさの点で異なるような粒子の形で存
    在している組成物。 ３ 該ビヒクルがポリエチレン・グリコールであ
    る前記請求の範囲のいずれかに記載の物質の組成
    物。 ４ 該ビヒクルが分子量500のポリエチレン・グ
    リコールである請求の範囲第３項に記載の物質の
    組成物。 ５ 少なくとも一つの潤滑物質がポリエチレン・
    ワツクスの形である請求の範囲第４項に記載の物
    質の組成物。 ６ 大体、脂肪酸、脂肪酸のエステル、脂肪酸の
    アミドより成る群から選ばれた少なくとも一つの
    潤滑物質を含む前記請求の範囲のいずれかに記載
    の物質の組成物。 ７ 少なくとも一つの潤滑物質がエルカミドの形
    である請求の範囲第６項に記載の物質の組成物。 ８ 少なくとも一つの潤滑物質がポリシロキサン
    の形である前記請求の範囲のいずれかに記載の物
    質の組成物。 ９ 少なくとも一つの潤滑物質がシリコン・オイ
    ルの形である請求の範囲第８項に記載の物質の組
    成物。 １０ 大体、分子量500のポリエチレン・グリコ
    ール80重量部と、ポリエチレン・ワツクスとエル
    カミド各々10重量部より成る前記請求の範囲のい
    ずれかに記載の物質の組成物。 １１ 大体、分子量500のポリエチレン・グリコ
    ール90重量部、ポリエチレン・ワツクス9.8重量
    部、シリコン・オイル0.2重量部より成る前記請
    求の範囲第１項ないし第９項のいずれかに記載の
    物質の組成物。 １２ 少なくとも一つの潤滑物質がケイ酸の形で
    ある前記請求の範囲のいずれかに記載の物質の組
    成物。 １３ ケイ酸が２〜３重量％で、ワツクスの量が
    それに相応して減少している請求の範囲第１２項
    に記載の物質の組成物。 〔産業上の利用分野〕 本発明は、織物に接続された取付具、特に衣服
    に縫い付けたジツパー等に用いる多成分潤滑剤組
    成物に係るものである。 〔従来の技術〕 既知の潤滑剤は、一般に異なつた等級の鉱油の
    配合物より成るものである。この種の材料は水に
    溶けないが、例えばグリースのついたトレーラー
    の連結器や自動車のドアロツク等を扱つている時
    に、潤滑剤が織物に触れてそれを汚すことがよく
    ある。全く潤滑されない器具があるのは、多くの
    場合潤滑剤の汚す効果が原因であつた。なぜな
    ら、例えば衣服に縫い付けたジツパーは、長時間
    経つうちには堅くなりがちであることは経験して
    いることであるからであり、そうならなければこ
    のような潤滑は望ましいものである。既知の潤滑
    剤による汚れを落とすには、通常潤滑剤のついた
    織物を溶剤その他の組成物で処理しなければなら
    ない。これは面倒かつ高価であるので、不利と考
    えられる。 〔発明が解決しようとする課題〕 この点を考慮して、本発明の目的は、水で織物
    から洗い落とすことのできる潤滑剤を創り出すこ
    とにある。 〔課題を解決するための手段〕 本発明によれば、この目的は、水溶性ビヒクル
    物質より成り、かつそれに少なくとも一つの潤滑
    物質を細かく分散した状態で混入した潤滑剤組成
    物を用いて驚くほど簡単に達成される。 この水溶性ビヒクル物質は潤滑剤の重量の75〜
    95％で、その重量の残部は混入した潤滑物質より
    成つている。 このビヒクルは、モノヒドロキシ・アルコール
    またはポリヒドロキシ・アルコールおよび／また
    はそれに相応するエーテルおよび／またはそれに
    相応するエステルとするものである。 また、この潤滑剤はポリエチレン・ワツクス、
    エステル・ワツクスあるいはアミド・ワツクスの
    ようなワツクスの形の潤滑物質を少なくとも一つ
    含むものである。 ここで、粒子（particle）または球体の大きさ
    の異なる一つ以上の潤滑物質をビヒクルに混入し
    てもよい。 ビヒクルとして、ポリエチレン・グリコールを
    用いてもよい。このポリエチレン・グリコール
    は、分子量500程度とすると更に好ましい。 少なくとも一つの潤滑物質を脂肪酸および／ま
    たはそれのエステルおよび／またはそれのアミド
    の形としてもよい。 また、少なくとも一つの潤滑物質がポリシロキ
    サンの形であることとしてもよい。 ワツクスの若干またはすべてをケイ酸
    SiO2nH2Oに置き換えてもよい。 〔作 用〕 以上の構成とした結果、潤滑剤の重量割合の大
    部分を占めるビヒクルが水に可溶であることによ
    り、存在する割合が少量にすぎない潤滑物質を水
    を使つて織物から洗い落とすことができる。潤滑
    物質は、それらの重量割合が少ないので、痕跡や
    しみを残さないでほぼ洗い流される。このため、
    織物を溶剤等の清浄用組成物で処理しなくてもよ
    いという利点がある。試験でわかつたように、一
    般的に通常織物を水で洗えば充分である。 本発明による潤滑剤組成物の更に有用な効果
    は、織物及び一般に樹脂製であるジツパーのよう
    なそれに取り付けたフアスナーが、概して潤滑剤
    によつて侵されないことである。それが、更に有
    用な効果として、衣服に取り付けたジツパーや他
    の器具のフアスナーを潤滑するため、それらが長
    時間の間に堅くならず実際常に使いやすく、また
    寿命を長くすることができるようになる理由であ
    る。以前はこれができなかつた。本発明の潤滑剤
    の更に一つの用途は、カーテン用のランナーある
    いはそれに用いられるくぼんだレールである。し
    かし、この潤滑剤は更に、例えば自動車のロツク
    やトレーラーの連結器のような織物とよく接触し
    がちな機械部品に用いると有益であり、従来の潤
    滑剤を用いていた今までの場合よりも汚れによる
    不都合がずつと少なくなる。本発明によつて得ら
    れる有用な効果は、特に著しい節約がなされる点
    に見られるであろう。 また、ビヒクルは、モノヒドロキシ・アルコー
    ルまたはポリヒドロキシ・アルコールおよび／ま
    たはそれに相応するエーテルおよび／またはそれ
    に相応するエステルとするものである。 試験によつて、ポリエチレン・グリコールがビ
    ヒクルとして一層好ましいことが明らかになつ
    た。このようなビヒクルは、広範囲の温度に耐え
    るとともに潤滑物質を混入することのできる安定
    な構造を提供するという有利な効果がある。さら
    に粘度は、分子量だけが異なる多数の異なつた形
    状の同じビヒクルの一つを選択することによつ
    て、容易に調整することができる。試験の結果、
    平均分子量500のものが物性すなわちコンシステ
    ンス（consistence）が軟膏と似ており、特に便
    利であることが明らかになつた。分子量と融点が
    異なる多数の異なつた等級の同じ成分を配合する
    ことによつて、軟化点や溶解点の範囲を広くする
    ことができる。これは、同時に小さい温度変化に
    よつてビヒクルがその性質を急激に失わないよう
    に保証を与えるものであり、従つて本発明による
    潤滑剤には広い分野の応用が開かれている。 また、本発明の潤滑剤はポリエチレン・ワツク
    ス、エステル・ワツクスあるいはアミド・ワツク
    スのようなワツクスの形の潤滑物質を少なくとも
    一つ含むものである。 この種の材料は、それらの粒子の形状と大きさ
    のために、水をさつとかけることによつて容易に
    織物から洗い落としたり取り去ることができる。
    同時に、約150℃までの温度で安定という有用な
    効果があるため、広い異なつた温度範囲にわたつ
    て潤滑剤を用いることができる。潤滑剤を高温で
    用いる場合にはワツクスの若干またはすべてをケ
    イ酸SiO2nH2Oに置き換えて、ビヒクルの温度安
    定性によりいつそう有益な効果が得られるように
    することができる。 本発明の主な考えの発展の一部として、少なく
    とも一つの潤滑物質を脂肪酸および／またはそれ
    のエステルおよび／またはそれのアミドの形とす
    ることができる。この種の物質は、それらの粒子
    の形と大きさのために、ワツクスと共に使用する
    補助剤として非常に有用と考えられている。 本発明の更に可能な特徴は、少なくとも一つの
    潤滑物質がポリシロキサンの形であることであ
    る。このような潤滑物質を用いれば、必要な潤滑
    物質の総量はほんの少しでよいため、容易に洗い
    流せるビヒクルの割合が大きくなり、潤滑剤を洗
    い流すのがより容易になる。 本発明の更に発展の一部として、粒子
    （particle）または球体の大きさの異なる一つ以
    上の潤滑物質をビヒクルに混入したものがある。
    粒子の大きさが違うので、極めて満足な潤滑性が
    得られる。 〔実施例〕 本発明の更に有用な発展と派生は、請求の範囲
    と以下に述べる本発明の実施例についての説明に
    よつて明らかにされる。 例 長時間の間にジツパーが堅くなるため、使いに
    くくまた速く磨耗することは、一般に知られてい
    る。これは、適切な潤滑剤で潤滑することによつ
    てそうならないようにすることができる。この目
    的のための試験に用いた潤滑剤は、ポリエチレ
    ン・グリコール80重量％、ポリエチレン・ワツク
    ス10重量％、エルカミド（erucamid）10重量％
    より成るものである。この場合、ポリエチレン・
    グリコールはビヒクルを形成し、その中にポリエ
    チレン・ワツクスとエルカミドが細かく分散した
    状態で混入されるが、これは標準的な圧力と標準
    的な温度の下で撹拌によつて行われる。 ポリエチレン・グリコールの平均分子量は500
    である。それのコンシステンシイ（consistency）
    すなわち物理的性状は、軟膏に似ているため、ブ
    ラシや小さい刃を使つて全く均等に塗ることがで
    きる。その平均分子量は、異なつた等級の200〜
    10000の範囲の異なつた分子量をもつポリエチレ
    ン・グリコールを配合して得たものである。その
    溶融範囲は高かつた。150゜のオーダーの温度にお
    いても、ビヒクルとして用いたポリエチレン・グ
    リコールはその性質を失わなかつた。この例で
    は、温度の上限はポリエチレン・ワツクスによつ
    て可能になつた。すなわち、それが熱の影響に最
    もよく耐えたのである。耐熱性を増すために、そ
    のワツクスの全部又は一部をケイ酸SiO2nH2Oに
    置き換えるとよいかもしれない。 長時間にわたつて本発明の潤滑剤について試験
    を行つた結果、合成樹脂製のジツパーもそれに隣
    接した人造及び天然繊維製の織物も、どちらもこ
    れによつて侵されないことがわかつた。故意に織
    物の材料につけた潤滑剤の斑点は、水道栓の水を
    使つて痕跡を残さずに完全に洗い流すことができ
    た。水は約45℃に加熱すると特に効果的である。 この新規な潤滑剤で潤滑したジツパーは、非常
    に滑りが自由であつた。詰まつたあるいは堅いジ
    ツパーも、この潤滑剤で潤滑すれば、極めて短時
    間に非常に自由に滑るようになつた。この効果
    は、ポリエチレン・ワツクスとエルカミドの場合
    は、好適な粒子の大きさと形状に起因する。分散
    の状態または粒子の大きさがポリエチレン・ワツ
    クスとエルカミドとの中間の程度であるケイ酸を
    加えることによつて、この点に関してなお更に向
    上が見られた。形状が適当であるとわかつたケイ
    酸は、エアロシル（Aerosil、登録商標）（極微小
    発熱性シリカ）という商品名でデグツサ インコ
    ーポレーテツド（Degussa Inc.）が販売してい
    るものであつた。 ケイ酸の添加量は約２〜３重量％であり、同量
    のポリエチレン・ワツクスが置き換えられた。 例 ポリエチレン・グリコール90重量％、ポリエチ
    レン・ワツクス9.8重量％、シリコン・オイル0.2
    重量％より成る潤滑剤の平行した長期試験で、例
    と同じ有用な機能的効果が見られたが、例の
    場合よりも潤滑剤を洗い落とすのが一層簡単であ
    つた。これは、ビヒクルの割合がより高いことに
    起因するが、これはシリコン・オイルを使うこと
    によつて可能になつたのである。例の配合の場
    合にも、ワツクスの１部又は全部をケイ酸と置き
    換えることは可能である。 さて、図に示すようなジツパーのような帯状ま
    たはレール様の構造物の潤滑についての本発明の
    好ましい実施例について説明する。 図に見られる潤滑装置は、穴２をあけた壁３に
    よつて塗布ローラ５を収容する作業スペース４か
    ら分離されており、かつ塗布ローラの回転軸に垂
    直に延びる入口スロツト６を有する潤滑剤用収容
    スペース１を有するものである。材料９の帯片に
    固定されたジツパー（スライド・フアスナー）７
    を動かすのは、このスロツトを通してである。塗
    布ローラー５は、ブラシの形で造られれば最良で
    あるが、それが穴２をあけた壁をこすりあるいは
    ブラシがけをするとともに、穴から出てくる潤滑
    剤を取り出すような大きさと位置にし、従つてス
    ロツト６に置かれたあらゆる物、この場合はジツ
    パー７に潤滑剤を押し付けあるいは拭つて、それ
    が潤滑されるようにする。塗布ローラー５は、そ
    れに接線方向に触れるジツパー７によつて回転さ
    れる。 塗布ローラー５を回転できるようにその中に置
    きかつ支持した作業スペース４は、穴をあけた壁
    ３のある頑丈なハウジング１１中に設けられ、さ
    らにそこに収容スペース１のあるハウジング１４
    は、ハウジング１１の上に嵌合あるいは螺合され
    る。ハウジング１４は、単にゴム様の壁の屈曲可
    能な管あるいはガラスびんの形とし、その中の潤
    滑剤が容易にしぼり出されるようにする。しか
    し、なおバネやネジで作動するピストンを設ける
    ことも可能である。この場合は、望まれる時に潤
    滑剤の穴を通る流れを止めるために、スライド等
    の形の弁を設けることが最良である。穴は、ビヒ
    クル中の物質の分子によつて詰ることのないよう
    な横断面とする。
JP59502611A 1983-07-07 1984-07-03 潤滑剤 Granted JPS60501814A (ja)