JPH0319059B2 - - Google Patents
Info
- Publication number
- JPH0319059B2 JPH0319059B2 JP15002683A JP15002683A JPH0319059B2 JP H0319059 B2 JPH0319059 B2 JP H0319059B2 JP 15002683 A JP15002683 A JP 15002683A JP 15002683 A JP15002683 A JP 15002683A JP H0319059 B2 JPH0319059 B2 JP H0319059B2
- Authority
- JP
- Japan
- Prior art keywords
- silicone
- silicone elastomer
- sensitive adhesive
- resin layer
- pressure
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【発明の詳細な説明】
本発明は、シリコーンエラストマー積層体に関
する。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to silicone elastomer laminates.
シリコーンエラストマー成形体は、建築用シー
ル材、医療用部材、各種工業用部品、火花遮断
膜、放熱シートなどとして広く使用されている。 Silicone elastomer molded bodies are widely used as architectural sealants, medical components, various industrial parts, spark blocking films, heat dissipation sheets, and the like.
しかしながら、シリコーンエラストマー成形体
は一般に柔かく、表面の粘着感が強いため塵埃に
より汚れやすいという欠点がある。これを解消す
る手段としてシリコーンエラストマー成形体の表
面をシリコーンレジン層により被覆することが提
案されている。 However, silicone elastomer molded bodies are generally soft and have a strong surface tackiness, so they have the disadvantage of being easily stained by dust. As a means to solve this problem, it has been proposed to cover the surface of the silicone elastomer molded article with a silicone resin layer.
しかしながら、シリコーンレジンは一般にシリ
コーンエラストマー成形体に接着しにくく、たと
え接着したとしても接着耐久性が乏しく、そのた
め、シリコーンレジン層がシリコーンエラストマ
ー成形体からはがれやすいという問題がある。 However, silicone resins generally have difficulty adhering to silicone elastomer molded bodies, and even if they do, they have poor adhesion durability, resulting in the problem that the silicone resin layer easily peels off from the silicone elastomer molded body.
そこで、本発明者はシリコーンレジン層がシリ
コーンエラストマー成形体によく接着し、接着耐
久性のすぐれているシリコーンレジン被膜のシリ
コーンエラストマー成形体および異種固体材料で
補強されたシリコーンエラストマー成形体を開発
すべく鋭意研究した結果、本発明に到達した。 Therefore, the present inventor set out to develop a silicone elastomer molded body with a silicone resin coating and a silicone elastomer molded body reinforced with a different solid material, in which the silicone resin layer adheres well to the silicone elastomer molded body and has excellent adhesion durability. As a result of intensive research, we have arrived at the present invention.
すなわち、本発明は、シリコーンエラストマー
積層体において、シリコーンエラストマー成形体
の表面がシリコーン感圧接着剤の薄層により被覆
され、該シリコーン感圧接着剤薄層の表面がシリ
コーンレジン層により被覆されていることを特徴
とするシリコーンエラストマー積層体、および、
異種固体材料で補強されたシリコーンエラストマ
ー積層体において、シリコーンエラストマー成形
体の表面がシリコーン感圧接着剤の薄層により被
覆され、該シリコーン感圧接着剤薄層の表面がシ
リコーンレジン層により被覆されていることを特
徴とするシリコーンエラストマー積層体に関す
る。 That is, the present invention provides a silicone elastomer laminate in which the surface of the silicone elastomer molded body is covered with a thin layer of silicone pressure-sensitive adhesive, and the surface of the thin silicone pressure-sensitive adhesive layer is covered with a silicone resin layer. A silicone elastomer laminate characterized by:
In a silicone elastomer laminate reinforced with different solid materials, the surface of the silicone elastomer molded body is coated with a thin layer of silicone pressure-sensitive adhesive, and the surface of the thin layer of silicone pressure-sensitive adhesive is coated with a silicone resin layer. The present invention relates to a silicone elastomer laminate characterized by comprising:
これを説明するに、シリコーンエラストマー成
形体は、有機過酸化物を硬化剤とする、いわゆる
熱硬化型のもの、白金系触媒を使用する、付加反
応硬化型のもの（通常LTVと称されている）、室
温硬化型のもの（通常RTVと称されている）、放
射線硬化型など、いずれのタイプのものであつて
もよい。その硬さは、エラストマー状でありさえ
すればよく特に限定されない。ただ、シリコーン
エラストマーは柔いほど汚れやすいので、硬さは
小さいほうがより本発明の効果が顕著となる。 To explain this, silicone elastomer molded products are of the so-called thermosetting type, which uses an organic peroxide as a curing agent, and of the addition reaction curing type, which uses a platinum-based catalyst (usually referred to as LTV). ), room temperature curing type (usually referred to as RTV), radiation curing type, etc. Its hardness is not particularly limited as long as it is elastomer-like. However, the softer the silicone elastomer, the more likely it is to get dirty, so the smaller the hardness, the more pronounced the effect of the present invention will be.
その形状は、特に限定されず、いかなる形状で
もよく、シート状、管状、ロツド状、角柱状、球
状、半球状、不定形状が例示される。これら形状
のうち、シート状のものは表面積が広いため汚れ
が目立ちやすいので本発明の効果がより顕著とな
る。また、異種固体材料で補強されたシリコーン
エラストマー成形体におけるシリコーンエラスト
マー成形体についても同様である。この異種固体
材料はシリコーン以外の固体材料であつて、これ
には織物、編物、不織布、金属部材、金属線、プ
ラスチツクフイルム、プラスチツク部材、セラミ
ツク部材、石材が例示される。異種固体材料はシ
リコーンエラストマー成形体に内在させても、裏
打ちしたものであつてもよい。また、土木構築物
や建築物の１部であつてもよい。 Its shape is not particularly limited and may be any shape, including sheet, tubular, rod, prismatic, spherical, hemispherical, and irregular shapes. Among these shapes, the sheet-like shape has a large surface area and therefore stains are easily noticeable, so that the effects of the present invention are more pronounced. The same applies to a silicone elastomer molded product reinforced with a different solid material. This different solid material is a solid material other than silicone, and examples thereof include woven fabrics, knitted fabrics, nonwoven fabrics, metal members, metal wires, plastic films, plastic members, ceramic members, and stone. The dissimilar solid material may be internal to or lined with the silicone elastomer molding. Moreover, it may be a part of a civil engineering structure or a building.
これらシリコーンエラストマー成形体は、その
表面がまずシリコーン感圧接着剤の薄膜により被
覆されている。もつとも、シリコーンエラストマ
ー成形体はその全表面がシリコーン感圧接着剤に
より被覆されている必要は必ずしもなく、汚れ防
止を必要とする部分だけが被覆されていてもよ
い。 The surface of these silicone elastomer molded bodies is first coated with a thin film of silicone pressure-sensitive adhesive. However, the entire surface of the silicone elastomer molded article does not necessarily have to be coated with the silicone pressure-sensitive adhesive, and only the portions requiring stain prevention may be coated.
シリコーン感圧接着剤を薄層とするのは、肉厚
が大きすぎると、その表面を被覆するシリコーン
レジン層がずれ動いたり、耐引掻性が低下する傾
向がでてくるからである。具体的には、厚みが
100μｍ以下であることが好ましい。なお、この
厚みは、シリコーン感圧接着剤に一般に添加され
ている有機溶剤が揮散した後の厚みをいう。 The silicone pressure-sensitive adhesive is made into a thin layer because if the thickness is too large, the silicone resin layer covering the surface tends to shift and the scratch resistance decreases. Specifically, the thickness
It is preferably 100 μm or less. Note that this thickness refers to the thickness after the organic solvent that is generally added to silicone pressure-sensitive adhesives has volatilized.
これらシリコーンエラストマー成形体の表面を
被覆したシリコーン感圧接着剤薄層は、その全表
面がシリコーンレジン層により被覆されている。
このシリコーンレジンは、加熱硬化型、室温硬化
型、紫外線硬化型などのいずれでもよく、前二者
は縮合反応硬化型、付加反応硬化型のいずれでも
よい。 The entire surface of the silicone pressure-sensitive adhesive thin layer covering the surface of these silicone elastomer molded bodies is covered with a silicone resin layer.
This silicone resin may be of a heat curing type, a room temperature curing type, or an ultraviolet curing type, and the former two may be of a condensation reaction curing type or an addition reaction curing type.
シリコーンレジンは、これらシリコーンエラス
トマー成形体の動きに追随して動けることが好ま
しく、そうした観点から、比較的柔いシリコーン
レジンであることが好ましい。また、あまり柔ら
すぎるとそれ自身が汚れやすくなるので、Ｒ／Si
の平均モル比（ここで、Ｒはケイ素原子結合有機
基である）が1.3〜1.8であることが好ましい。 It is preferable that the silicone resin can move following the movement of these silicone elastomer molded bodies, and from this point of view, it is preferable that the silicone resin is relatively soft. Also, if it is too soft, it will easily get dirty, so R/Si
The average molar ratio of (where R is a silicon-bonded organic group) is preferably from 1.3 to 1.8.
シリコーンレジン層の厚みはあまり厚すぎると
折り曲げたときに亀裂がはいりやすく、あまり薄
いと下地のシリコーン感圧接着剤が露出するおそ
れがあるので10〜300μｍが好ましい。 The thickness of the silicone resin layer is preferably 10 to 300 μm, since if it is too thick, cracks will easily occur when it is bent, and if it is too thin, the underlying silicone pressure-sensitive adhesive may be exposed.
本発明のシリコーンエラストマー積層体は、シ
リコーンエラストマー成形体または異種固体材料
で補強されたシリコーンエラストマー成形体の表
面にシリコーン感圧接着剤を薄く塗布し、シリコ
ーン感圧接着剤が有機溶剤を含有しているときは
風乾し、ついでシリコーンレジン液を塗布し、室
温下放置、加熱または紫外線照射などしてシリコ
ーンレジンを硬化させることにより容易に製造で
きる。 The silicone elastomer laminate of the present invention is produced by coating a silicone pressure-sensitive adhesive thinly on the surface of a silicone elastomer molded product or a silicone elastomer molded product reinforced with a different solid material, and in which the silicone pressure-sensitive adhesive contains an organic solvent. It can be easily manufactured by air-drying the silicone resin, then applying a silicone resin solution, and curing the silicone resin by leaving it at room temperature, heating it, or irradiating it with ultraviolet rays.
本発明のシリコーンエラストマー積層体は、上
述のようにシリコーンレジン層とシリコーンエラ
ストマー成形体の間にシリコーン感圧接着剤の薄
層を介在させることにより、各層間が強固に接着
して一体となつている。したがつて、シリコーン
レジン層の接着耐久性がすぐれ、長期間麈埃によ
り汚染されないという特徴を有する。 As described above, the silicone elastomer laminate of the present invention has a thin layer of silicone pressure-sensitive adhesive interposed between the silicone resin layer and the silicone elastomer molded body, so that each layer is firmly bonded and integrated. There is. Therefore, the silicone resin layer has excellent adhesive durability and is free from contamination with dust for a long period of time.
次に、従来例及び本発明の実施例を図面に基づ
いて説明する。 Next, a conventional example and an embodiment of the present invention will be described based on the drawings.
第１図は、シート状の熱硬化型シリコーンエラ
ストマー成形体１の両面全部が厚さ100μｍの付
加反応硬化型シリコーンレジン層５により直接被
覆された従来のシート状シリコーンエラストマー
積層体の断面部分拡大図である。この積層体は屈
曲を繰返すとシリコーンレジン層５がシリコーン
エラストマー成形体１からはがれたため、麈埃に
より汚れやすくなつた。 FIG. 1 is an enlarged partial cross-sectional view of a conventional sheet-like silicone elastomer laminate in which both sides of a sheet-like thermosetting silicone elastomer molded body 1 are directly coated with an addition reaction-curing silicone resin layer 5 having a thickness of 100 μm. It is. When this laminate was repeatedly bent, the silicone resin layer 5 was peeled off from the silicone elastomer molded body 1, so that it was easily stained by dust.
第２図は、本発明の実施例のシリコーンエラス
トマー積層体の断面部分拡大図であり、シート状
の熱硬化型シリコーンエラストマー成形体１の両
面全部が厚さ約20μｍのシリコーン感圧接着剤の
薄層４により被覆され、該シリコーン感圧接着剤
薄層４の全表面が厚さ100μｍの付加反応硬化型
シリコーンレジン層５により被覆されている。こ
の積層体はシリコーンエラストマー成形体１とシ
リコーン感圧接着剤薄層４とシリコーンレジン層
５が一体化しており、屈曲を繰返してもシリコー
ンレジン層５がはがれるということがなく、防汚
性がすぐれていた。 FIG. 2 is an enlarged partial cross-sectional view of a silicone elastomer laminate according to an embodiment of the present invention, in which both surfaces of a sheet-like thermosetting silicone elastomer molded article 1 are made of a silicone pressure-sensitive adhesive having a thickness of about 20 μm. The entire surface of the silicone pressure sensitive adhesive thin layer 4 is covered with an addition reaction curable silicone resin layer 5 having a thickness of 100 μm. This laminate has a silicone elastomer molded body 1, a silicone pressure-sensitive adhesive thin layer 4, and a silicone resin layer 5 integrated into one, and the silicone resin layer 5 does not peel off even after repeated bending, and has excellent stain resistance. was.
第３図は、本発明の別の実施例のシリコーンエ
ラストマー積層体の断面部分拡大図であり、シー
ト状の室温硬化型シリコーンエラストマー成形体
１の両面全部が厚さ約30μｍのシリコーン感圧接
着剤の薄層４により被覆され、該シリコーン感圧
接着剤薄層４の全表面が厚さ200μｍの室温硬化
型シリコーンレジン層５により被覆されている。
この積層体は、シリコーンエラストマー成形体１
とシリコーン感圧接着剤薄層４とシリコーンレジ
ン層５が一体化しており、屈曲を繰返してもシリ
コーンレジン層５がはがれるということがなく、
防汚性がすぐれていた。 FIG. 3 is a partially enlarged cross-sectional view of a silicone elastomer laminate according to another embodiment of the present invention, in which both sides of a sheet-like room temperature-curing silicone elastomer molded body 1 are coated with a silicone pressure-sensitive adhesive having a thickness of about 30 μm. The entire surface of the silicone pressure sensitive adhesive thin layer 4 is covered with a room temperature curing silicone resin layer 5 having a thickness of 200 μm.
This laminate is a silicone elastomer molded product 1
The silicone pressure-sensitive adhesive thin layer 4 and the silicone resin layer 5 are integrated, and the silicone resin layer 5 will not peel off even after repeated bending.
It had excellent stain resistance.
第４図は、本発明の別の実施例のシリコーンエ
ラストマー積層体の断面部分拡大図であり、シー
ト状の付加反応硬化型シリコーンエラストマー成
形体はガラス繊維織物２により補強されている。
このシート状シリコーンエラストマー成形体１の
両面全部が厚さ50μｍのシリコーン感圧接着剤の
薄層４により被覆されており、該シリコーン感圧
接着剤薄層４の全表面が厚さ280μｍの室温硬化
型シリコーンレジン層５により被覆されている。
この積層体は、シリコーンレジン層５が一体化し
ており、屈曲を繰返してもシリコーンレジン層５
がはがれるということがなく、防汚性がすぐれて
いた。 FIG. 4 is a partially enlarged cross-sectional view of a silicone elastomer laminate according to another embodiment of the present invention, in which a sheet-like addition reaction-curable silicone elastomer molded product is reinforced with a glass fiber fabric 2. FIG.
Both sides of this sheet-like silicone elastomer molded body 1 are coated with a thin layer 4 of silicone pressure-sensitive adhesive having a thickness of 50 μm, and the entire surface of the thin layer 4 of silicone pressure-sensitive adhesive having a thickness of 280 μm is cured at room temperature. The mold is covered with a silicone resin layer 5.
In this laminate, the silicone resin layer 5 is integrated, and even after repeated bending, the silicone resin layer 5
It did not peel off and had excellent stain resistance.
第５図は、本発明の別の実施例のシリコーンエ
ラストマー積層体の断面部分拡大図であり、膜状
の熱硬化型シリコーンエラストマー成形体１がポ
リエステル繊維織物３の片面上に形成されて一体
化しており、該シリコーンエラストマー成形体１
の表面全部が厚さ約16μｍのシリコーン感圧接着
剤の薄層４により被覆されており、該シリコーン
感圧接着剤薄層４の全表面が厚さ140μｍの付加
反応硬化型シリコーンレジン層５により被覆され
ている。この積層体は、シリコーンエラストマー
成形体１とシリコーン感圧接着剤薄層４とシリコ
ーンレジン層５が一体化しており、シリコーンレ
ジン層５がはがれるということがなく、防汚性が
すぐれていた。 FIG. 5 is a partially enlarged cross-sectional view of a silicone elastomer laminate according to another embodiment of the present invention, in which a film-like thermosetting silicone elastomer molded body 1 is formed on one side of a polyester fiber fabric 3 and integrated. The silicone elastomer molded article 1
The entire surface of is coated with a thin layer 4 of silicone pressure-sensitive adhesive having a thickness of approximately 16 μm, and the entire surface of the thin layer 4 of silicone pressure-sensitive adhesive 4 is coated with an addition reaction-curing silicone resin layer 5 having a thickness of 140 μm. Covered. In this laminate, the silicone elastomer molded body 1, the silicone pressure-sensitive adhesive thin layer 4, and the silicone resin layer 5 were integrated, and the silicone resin layer 5 did not peel off, and the stain resistance was excellent.
なお、第１図、第２図、第５図における付加反
応硬化型シリコーンレジンは白金化合物触媒含有
タイプのものであり、Ｒ／Siの平均モル比が1.46
である（ここで、Ｒはケイ素原子結合メチル基と
ビニル基である）。第３図、第４図における室温
硬化型シリコーンレジンはチタン化合物触媒含有
タイプのものであり、Ｒ／Siの平均モル比が1.68
である（ここで、Ｒはケイ素原子結合メチル基と
フエニル基である）。また第１図、第２図および
第５図におけるシリコーン感圧接着剤は、白金化
合物触媒含有タイプのものであり、第３図および
第４図におけるシリコーン感圧接着剤は触媒非含
有タイプのものである。 The addition reaction curing silicone resins shown in Figures 1, 2, and 5 are those containing a platinum compound catalyst, and the average molar ratio of R/Si is 1.46.
(where R is a silicon-bonded methyl group and a vinyl group). The room temperature curing silicone resin shown in Figures 3 and 4 is of the type containing a titanium compound catalyst, and has an average R/Si molar ratio of 1.68.
(where R is a silicon-bonded methyl group and a phenyl group). The silicone pressure-sensitive adhesives shown in Figures 1, 2, and 5 are those containing a platinum compound catalyst, and the silicone pressure-sensitive adhesives shown in Figures 3 and 4 are those that do not contain a catalyst. It is.
第１図は従来例のシリコーンエラストマー積層
体の断面部分拡大図であり、第２図〜第５図は本
発明のシリコーンエラストマー積層体の断面部分
拡大図である。
１……シリコーンエラストマー成形体、２……
ガラス繊維織物、３……ポリエステル繊維織物、
４……シリコーン感圧接着剤の薄層、５……シリ
コーンレジン層。
FIG. 1 is a partially enlarged cross-sectional view of a conventional silicone elastomer laminate, and FIGS. 2 to 5 are partially enlarged cross-sectional views of the silicone elastomer laminate of the present invention. 1... Silicone elastomer molded body, 2...
Glass fiber fabric, 3... Polyester fiber fabric,
4... Thin layer of silicone pressure sensitive adhesive, 5... Silicone resin layer.
Claims (1)
リコーンエラストマー成形体の表面がシリコーン
感圧接着剤の薄層により被覆され、該シリコーン
感圧接着剤薄層の表面がシリコーンレジン層によ
り被覆されていることを特徴とするシリコーンエ
ラストマー積層体。 ２ シリコーンエラストマー成形体がシート状で
ある特許請求の範囲第１項記載のシリコーンエラ
ストマー積層体。 ３ 異種固体材料で補強されたシリコーンエラス
トマー積層体においてシリコーンエラストマー成
形体の表面がシリコーン感圧接着剤の薄層により
被覆され、該シリコーン感圧接着剤薄層の表面が
シリコーンレジン層により被覆されていることを
特徴とするシリコーンエラストマー積層体。[Scope of Claims] 1 In a silicone elastomer laminate, the surface of the silicone elastomer molded body is coated with a thin layer of silicone pressure-sensitive adhesive, and the surface of the thin layer of silicone pressure-sensitive adhesive is coated with a silicone resin layer. A silicone elastomer laminate characterized by: 2. The silicone elastomer laminate according to claim 1, wherein the silicone elastomer molded product is in the form of a sheet. 3. In a silicone elastomer laminate reinforced with different solid materials, the surface of the silicone elastomer molded body is coated with a thin layer of silicone pressure-sensitive adhesive, and the surface of the thin layer of silicone pressure-sensitive adhesive is coated with a silicone resin layer. A silicone elastomer laminate characterized by: