JPH03250064A - Photochromic coating film - Google Patents
Photochromic coating filmInfo
- Publication number
- JPH03250064A JPH03250064A JP2045582A JP4558290A JPH03250064A JP H03250064 A JPH03250064 A JP H03250064A JP 2045582 A JP2045582 A JP 2045582A JP 4558290 A JP4558290 A JP 4558290A JP H03250064 A JPH03250064 A JP H03250064A
- Authority
- JP
- Japan
- Prior art keywords
- coating film
- mica
- coating
- color
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【発明の詳細な説明】
（産業上の利用分野）
本発明は、例えば自動車車体あるいは部品の上塗り塗膜
等に適用して好ましい色彩可変塗膜に関する。DETAILED DESCRIPTION OF THE INVENTION (Field of Industrial Application) The present invention relates to a color variable coating film that is preferably applied to, for example, an automobile body or a top coating film for parts.
（従来の技術）
従来のメタリック塗装に代って干渉塗装と呼ばれる新規
な塗装が実用化されている。この干渉塗装の特徴は、着
色顔料を含むカラーベース塗膜上に、光輝性粉体として
真珠雲Ｉ１片（パールマイカ）を念むマイカベース塗膜
を形成した点である。すなわち、第４図に示すように、
被塗物表面１（例えは中塗り塗膜上）に着色顔料５を含
むカラーベース塗料を塗布し焼き付けることによりカラ
ーベース塗膜２を形成する。ついで、このカラーベース
塗膜２上に真珠方母片６を含むマイカベース塗膜３を塗
布し、さらにこの上にクリヤ塗料４をウェットオンウェ
ット塗装して乾燥させた塗装である。そして、マイカベ
ース塗膜３の隠蔽（いんぺい）力を故意に低下させるこ
とにより、クリヤ塗膜４、マイカベース塗膜３、及びカ
ラーベース塗膜２の各色が）１俟った色彩が観察される
。(Prior Art) A new coating called interference coating has been put into practical use in place of conventional metallic coating. The feature of this interference coating is that a mica base coating containing pearl cloud I pieces (pearl mica) as glittering powder is formed on a color base coating containing colored pigments. That is, as shown in Figure 4,
A color base paint film 2 is formed by applying a color base paint containing a colored pigment 5 to the surface 1 of the object to be coated (for example, on an intermediate coat film) and baking it. Next, a mica base coating film 3 containing mother-of-pearl pieces 6 is applied onto the color base coating film 2, and a clear coating material 4 is further applied wet-on-wet on this coating and dried. By intentionally lowering the hiding power of the mica base coating film 3, a color in which each color of the clear coating film 4, mica base coating film 3, and color base coating film 2 is slightly duller is observed. .
（発明が解決しようとする課題）
しかしながら、従来の干渉塗膜は、その何れもが見る角
度を変えると色彩が変化するものであり、見る角度以外
の要因によって色彩が変化する塗膜は現状のところ存在
しない。すなわち、上述したパールマイカに代表される
干渉塗膜は、カラーベース層とマイカベース層とのそれ
ぞれから反射される光を感じることにより塗膜全体の深
み感を与え、これにより色目を変化させるものであるか
ら、同じ角度で観察しただけでは従来のメタリック塗膜
と大きな違いはない。(Problem to be Solved by the Invention) However, in all conventional interference coatings, the color changes when the viewing angle changes, and the current coatings whose color changes depending on factors other than the viewing angle are However, it doesn't exist. In other words, the interference coating film typified by the pearl mica described above gives a sense of depth to the entire coating film by sensing the light reflected from each of the color base layer and the mica base layer, thereby changing the color. Therefore, if you just observe it from the same angle, there is no big difference from a conventional metallic coating.
本発明は、このような従来技術の問題点に鑑みてなされ
たものであり、塗膜性能を維持しつつ、見る角度を変え
なくとも色彩が変化する新規な塗膜を提供することを目
的とする。The present invention was made in view of the problems of the prior art, and aims to provide a novel coating film that changes color without changing the viewing angle while maintaining coating performance. do.
（課題を解決するだめの手段）
上記目的を達成するための本発明は、被塗物上に形成さ
れた着色顔料を含むカラーベース塗膜と、このカラーベ
ース塗膜上に形成されたフォトクロ物質を含むフォトク
ロ塗膜と、このフォトクロ塗膜」−に形成された光輝性
粉体を含むマイカベース塗膜と、さらに、このマイカベ
ース塗膜上に形成されたクリヤ塗膜とを有する色彩可変
塗膜である。(Another Means to Solve the Problems) The present invention for achieving the above object includes a color base coating film containing a colored pigment formed on an object to be coated, and a photochromic material formed on the color base coating film. A color variable coating comprising a photochromic coating film containing a photochromic coating, a mica-based coating film containing glittering powder formed on the photochromic coating film, and a clear coating film formed on the mica-based coating film. It is a coating film.
（作用）
このように構成した本発明にあっては、光の存在下にお
いては、クリヤ塗膜およびマイカベース塗膜を通過して
フォトクロ塗膜に到達した光によってフォトクロ物質か
変色し、この色目と、カラーベース塗膜およびマイカベ
ース塗膜の谷色目が相俟って塗膜全体が変色する。一方
、光の存在が少ない場合には、フォトクロ物質は本来の
色目に戻るから、この色目とカラーベース塗膜およびマ
イカベース塗膜の各色か相俟った色目の塗膜となる。(Function) In the present invention configured as described above, in the presence of light, the photochromic substance changes color due to the light that passes through the clear coating film and the mica base coating film and reaches the photochromic coating film, This color, together with the valley color of the color base coating film and the mica base coating film, causes the entire coating film to discolor. On the other hand, when there is little light, the photochrome substance returns to its original color, resulting in a coating film that combines this color with each color of the color base coating film and the mica base coating film.
また、フォトクロ塗膜上にマイカベース塗膜およびクリ
ヤ塗膜の２層の塗膜を形成することにより、フォトクロ
塗膜に到達する紫外線量を低減することができ、従来よ
り問題があったフォトクロ物質の耐候性を著しく向上さ
せることができる。In addition, by forming two layers of a mica-based coating and a clear coating on the Photochrome coating, it is possible to reduce the amount of ultraviolet rays that reach the Photochrome coating, which has previously been a problem. The weather resistance of photochromic substances can be significantly improved.
（実施例） 以下、本発明の一実施例を図面に基づいて説明する。(Example) Hereinafter, one embodiment of the present invention will be described based on the drawings.
第１図は本発明の一実施例を示す塗膜の断面図、第２図
は本発明の他の実施例を示す塗膜の断面図、第３図はク
リヤ塗膜に含まれる紫外線吸収剤の添加量と光透過率と
の関係を示すグラフである。Fig. 1 is a sectional view of a coating film showing one embodiment of the present invention, Fig. 2 is a sectional view of a coating film showing another embodiment of the invention, and Fig. 3 is an ultraviolet absorber contained in the clear coating film. It is a graph showing the relationship between the amount of addition and light transmittance.
本実施例の色彩可変塗膜は、被塗物１−にに形成された
カラーベース塗膜２、フォトクロ塗膜７、マイカベース
塗膜３、クリヤ塗膜４から構成されている。The color variable coating film of this embodiment is composed of a color base coating film 2, a photochromic coating film 7, a mica base coating film 3, and a clear coating film 4 formed on an object to be coated 1-.
被塗物１は、例えば自動車車体の外板、あるいは自動車
部品のような金属基板の場合には、その表面に電着塗膜
を形成し、この電着塗膜−Ｌに中塗り塗膜を形成したも
のである。一方、樹脂部品の場合には、プライマ塗膜、
あるいはプライマ塗膜」二に中塗り塗膜を形成したもの
である。In the case of the object 1 to be coated, for example, an outer panel of an automobile body or a metal substrate such as an automobile part, an electrodeposition coating film is formed on the surface thereof, and an intermediate coating film is applied to this electrodeposition coating film-L. It was formed. On the other hand, in the case of resin parts, primer coating,
Alternatively, an intermediate coating film is formed on a primer coating film.
ついで、この被塗物１上にカラーベース塗料を塗布し乾
燥させることによりカラーベース塗膜２を形成する。本
実施例に係るカラーベース塗料は、顔料５及び樹脂から
成る塗料であって、従来のパール塗装を目視した際に感
じる主たる色彩を呈する塗膜を構成する塗料である。こ
のカラーベース塗料は、膜厚１０〜３０μｍにて塗布し
、約り４０℃×２０分の乾燥条件により焼き付ける。Next, a color base paint is applied onto this object 1 and dried to form a color base paint film 2. The color base paint according to this example is a paint made of pigment 5 and a resin, and is a paint that constitutes a coating film that exhibits the main color that is perceived when viewing conventional pearl coating. This color base paint is applied to a film thickness of 10 to 30 μm and baked under drying conditions of approximately 40° C. for 20 minutes.
さらに、このカラーベース塗膜２上に、フォトクロ現象
を示す物質８（以下、フォトクロ物質と称する）を含む
フォトクロ塗料を塗布し乾燥させることによりフォトク
ロ塗膜７を形成する。このフォトクロ塗料は、膜厚１０
〜３０μｍにて塗布し、約１４０℃Ｘ２０分の乾燥条件
により焼き付ける。Furthermore, a photochromic paint containing a substance 8 exhibiting a photochromic phenomenon (hereinafter referred to as a photochromic substance) is applied onto the color base coating film 2 and dried to form a photochromic coating 7. This photochrome paint has a film thickness of 10
Apply at a thickness of ~30 μm and bake under drying conditions of approximately 140° C. for 20 minutes.
フォトクロ現象とは、ある種の物質か固体または溶液の
状態で光（紫外線または短波長の可視光線）の照射によ
って色を変え、暗所で再び元の色に戻る現象をいい、こ
のようなフォトクロ物質８として、各種のヒドラゾン、
オサゾン、フルギド、スチルベン、また、サリチルアル
デヒド、スピロピラン、ビイミダゾリルなどの誘導体、
ビアントロン等を挙げることができる。この変色は、無
色あるいは淡黄から青、紫、赤紫などに変わるなど著し
いものが多い。Photochromic phenomenon is a phenomenon in which a certain type of substance, solid or solution, changes color when irradiated with light (ultraviolet rays or short-wavelength visible light) and returns to its original color in the dark. As photochromic substances 8, various hydrazones,
Osazone, fulgide, stilbene, and derivatives such as salicylaldehyde, spiropyran, biimidazolyl,
Biantron etc. can be mentioned. This discoloration is often significant, such as changing from colorless or pale yellow to blue, purple, reddish-purple, etc.
ついで、このフォトクロ塗膜７上にマイカ／＜ −ス塗
料とクリヤ塗料とをウェットオンウェット塗装した後に
、両塗料を同時に乾燥させマイカベース塗膜３およびク
リヤ塗膜４を形成する。マイカベース塗料は膜厚１０〜
２０μｍにて塗布し、方クリヤ塗料は膜厚１５〜３０μ
ｍにて塗布し、両塗料を約１４０°Ｃ×２０分の乾燥条
件により焼き付ける。Next, a mica/<-base paint and a clear paint are wet-on-wet coated on the photochrome paint film 7, and then both paints are dried simultaneously to form a mica base paint film 3 and a clear paint film 4. Mica-based paint has a film thickness of 10~
Coat at a thickness of 20μm, and clear paint has a film thickness of 15 to 30μm.
Both paints were baked at approximately 140°C for 20 minutes under dry conditions.
本実施例に係るマイカベース塗料は、顔料を含まず、雲
母片６（マイカ）と樹脂とから成る塗料であり、クリヤ
塗膜４を通過して入射する光を雲母片６によって乱反射
させる塗膜を構成する。この＝ｃｔ片６は、従来のいわ
ゆるメタリック塗料に含有されたアルミ片とは異なる独
特の乱反射を弓き起し、これによって自動車車体の美観
を生じさせるものである。The mica-based paint according to this embodiment is a paint that does not contain pigment and is made of mica flakes 6 (mica) and a resin, and is a coating film that diffusely reflects light that passes through the clear coating film 4 and is incident on the mica flakes 6. Configure. This =ct piece 6 produces a unique diffused reflection that is different from the aluminum pieces contained in conventional so-called metallic paints, thereby giving the automobile body a beautiful appearance.
また、本実施例に係るクリヤ塗料は、樹脂のみにから成
る塗料であって、紫外線等による塗膜の劣化を防止する
と共に、本発明の色彩可変塗膜のツヤを提供するもので
ある。Further, the clear paint according to this example is a paint made only of resin, which prevents deterioration of the paint film due to ultraviolet rays, etc., and provides gloss to the color variable paint film of the present invention.
さらに、本実施例に係るクリヤ塗膜４には、紫外線吸収
剤を１．５〜３．０重量％、好ましくは２重量％配合し
ており、マイカベース塗膜３には、雲母片６を５〜２０
重量％、好ましくは１０〜１５重量％配重量ている。す
なわち、第３図に示すようにクリヤ塗膜４で紫外線（３
８０ｎｍ以下）の吸収量を多くし、しかも、マイカベー
ス塗膜３においても＝１ユ片６で紫外線を乱反射させる
ことにより、フォトクロ塗膜７への紫外線の到達口を極
力少なくしている。これにより、従来より問題かあった
フォトクロ物質８の耐候性を著しく向１−させることか
できる。Further, the clear coating film 4 according to this embodiment contains 1.5 to 3.0% by weight, preferably 2% by weight, of an ultraviolet absorber, and the mica base coating 3 contains mica flakes 6. 5-20
% by weight, preferably 10-15% by weight. That is, as shown in FIG.
80 nm or less) and diffusely reflect the ultraviolet rays in the mica-based coating 3 with a =1 u piece 6, thereby minimizing the number of ports through which the ultraviolet rays reach the photochromic coating 7. As a result, the weather resistance of the photochromic material 8, which has been problematic in the past, can be significantly improved.
このようなカラーベース塗料、フォトクロ塗料、マイカ
ベース塗料、クリヤ塗料は、エアー霧化式静電塗装ガン
あるいは回転霧化式静電塗装カンによって塗布すること
ができる。Such color base paints, photochrome paints, mica base paints, and clear paints can be applied using an air atomizing electrostatic coating gun or a rotary atomizing electrostatic coating can.
次に、本発明をさらに具体的な実施例に基づいて説明す
るが、本発明はその要旨を越えない限りにおいて種々に
変形することができる。Next, the present invention will be described based on more specific examples, but the present invention can be modified in various ways without departing from the gist thereof.
実施例１
７０Ｘ１５０ＸＯ，８ｍｍの鋼板テストピースをグラノ
ジン５Ｄ５０００ （日本ペイント（１社製リン酸塩素
系被膜化成処理剤）を用いて前処理し、次いでカチオン
電着塗料としてパワートップＵ−１００（日本ペイント
劃）社製）を用い、これを乾燥膜厚（以下、単に膜厚と
いう）で２０μｍ塗装し、１８０℃で２０分間焼き付け
た。Example 1 A 70X150XO, 8mm steel plate test piece was pretreated with Granozin 5D5000 (a chlorine phosphate film conversion treatment agent made by Nippon Paint), and then Power Top U-100 (Nippon Paint) was used as a cationic electrodeposition paint. This was coated with a dry film thickness (hereinafter simply referred to as "film thickness") of 20 μm using a coating film (manufactured by Haruka Co., Ltd.), and baked at 180° C. for 20 minutes.
次に、この電着塗膜上に、中塗り塗料としてハイエビコ
Ｎ０１（日本油脂帽）社製）を膜厚３５μｍで塗装し、
１４０℃で２０分間焼き付けた。Next, Hiebiko N01 (manufactured by NOF Co., Ltd.) was applied as an intermediate coating onto this electrodeposited film to a thickness of 35 μm.
It was baked at 140°C for 20 minutes.
得られた中塗り塗膜上に、カラーベース塗料としてベル
コートＮＯ６０００（日本油脂（ｒ４）社製）を塗装し
た後に、さらに５分間のフラッシュタイムをおいて、こ
のベルコートＮＯ６０００にフォトクロ物質スピロピラ
ンを１０重曾％配合したフォトクロ塗料をウェットオン
ウェット塗装し、１４０°Ｃで２０分間焼き付けた。After applying Bellcoat NO6000 (manufactured by Nihon Yushi (R4) Co., Ltd.) as a color base paint on the obtained intermediate coating film, a flash time of 5 minutes was allowed, and then the photochromic substance spiropyran was added to this Bellcoat NO6000. Wet-on-wet coating was applied with photochromic paint containing 10% sodium bicarbonate and baked at 140°C for 20 minutes.
さらに、マイカベース塗料としてベルコートＮ０６００
０にエクステリアマ−リンブライトホワイト（マール社
製ホワイトマイカ）を１０重量％配合した塗料を塗装し
た後に、さらに５分間のフラッシュタイムをおいて、ベ
ルコートＮＯ６０００クリヤに紫外線吸収剤ＴｌＮＵＶ
ｌＮ１１３０（チバガイギー社製）２重量％を配合した
塗料を膜厚３５μｍでウェットオンウェット塗装し、１
４０℃で２０分間焼き付けた。Additionally, Bellcoat N0600 is used as a mica-based paint.
After applying a paint containing 10% by weight of Exterior Marlin Bright White (white mica manufactured by Marl Co., Ltd.) to 0, after an additional 5 minutes of flash time, apply UV absorber TlNUV to Belcoat NO6000 Clear.
A paint containing 2% by weight of lN1130 (manufactured by Ciba Geigy) was applied wet-on-wet to a film thickness of 35 μm.
Baked at 40°C for 20 minutes.
実施例２
実施例１で用いた紫外線吸収剤の種類をＴｌＮＵＶｌＮ
９００ （チバカイギー社製）にした以外は、実施例１
と同様に塗装した。Example 2 The type of ultraviolet absorber used in Example 1 was TlNUVlN.
Example 1 except that 900 (manufactured by Ciba Kaigy) was used.
Painted the same way.
実施例３
実施例１で用いた紫外線吸収剤の種類をＴｌＮＵＶｌＮ
３２８ （チバガイギー社製）にした以外は、実施例１
と同様に塗装した。Example 3 The type of ultraviolet absorber used in Example 1 was TlNUVlN.
Example 1 except that 328 (manufactured by Ciba Geigy) was used.
Painted the same way.
実施例４
実施例１で用いた紫外線吸収剤の量を３重量％にした以
外は、実施例１と同様に塗装した。Example 4 Coating was carried out in the same manner as in Example 1, except that the amount of the ultraviolet absorber used in Example 1 was changed to 3% by weight.
実施例５
実施例２で用いた紫外線吸収剤の量を３重量％にした以
外は、実施例２と同様に塗装した。Example 5 Coating was carried out in the same manner as in Example 2, except that the amount of the ultraviolet absorber used in Example 2 was changed to 3% by weight.
実施例６
実施例３で用いた紫外線吸収剤の量を３重量％にした以
外は、実施例３と同様に塗装した。Example 6 Coating was carried out in the same manner as in Example 3, except that the amount of ultraviolet absorber used in Example 3 was changed to 3% by weight.
実施例７
実施例１で用いた紫外線吸収剤の量を１．５重量％にし
た以外は、実施例１と同様に塗装した。Example 7 Coating was carried out in the same manner as in Example 1, except that the amount of the ultraviolet absorber used in Example 1 was changed to 1.5% by weight.
実施例８
実施例２て用いた紫外線吸収剤の量を１．５重量％にし
た以外は、実施例２と同様に塗装した。Example 8 Coating was carried out in the same manner as in Example 2, except that the amount of the ultraviolet absorber used in Example 2 was changed to 1.5% by weight.
実施例９
実施例３で用いた紫外線吸収剤の量を１．５重量％にＬ
５た以外は、実施例３と同様に塗装した。Example 9 The amount of ultraviolet absorber used in Example 3 was reduced to 1.5% by weight.
Coating was carried out in the same manner as in Example 3, except for the coating.
実施例１０
実施例１で用いたマイカベース塗料のエクステリアマ−
リンブライトホワイトの濃度を２０重量％にした以外は
、実施例１と同様に塗装した。Example 10 Exterior paint of mica-based paint used in Example 1
Coating was carried out in the same manner as in Example 1, except that the concentration of Lin Bright White was 20% by weight.
実施例１１
実施例２で用いたマイカベース塗料のエクステリアマ−
リンブライトホワイトの濃度を２０重量％にした以外は
、実施例２と同様に塗装した。Example 11 Exterior paint of mica-based paint used in Example 2
Coating was carried out in the same manner as in Example 2, except that the concentration of Lin Bright White was 20% by weight.
実施例１２
実施例３で用いたマイカベース塗料のエクステリアマ−
リンブライトホワイトの濃度を２０重量％にした以外は
、実施例３と同様に塗装した。Example 12 Exterior paint of mica-based paint used in Example 3
Coating was carried out in the same manner as in Example 3, except that the concentration of Lin Bright White was 20% by weight.
実施例１３
実施例４で用いたマイカベース塗料のエフステノアマー
リンブライトホワイトの濃度を２０重量％にした以外は
、実施例４と同様に塗装した。Example 13 Coating was carried out in the same manner as in Example 4, except that the concentration of Efstenoa Marlin Bright White, the mica-based paint used in Example 4, was changed to 20% by weight.
実施例１４
実施例５で用いたマイカベース塗料のエクステリアマ−
リンブライトホワイトの濃度を２０重量％にした以外は
、実施例５と同様に塗装した。Example 14 Exterior paint of mica-based paint used in Example 5
Coating was carried out in the same manner as in Example 5, except that the concentration of Lin Bright White was 20% by weight.
実施例１５
実施例６で用いたマイカベース塗料のエクステリアマ−
リンブライトホワイトの濃度を２０重量％にした以外は
、実施例６と同様に塗装した。Example 15 Exterior paint of mica-based paint used in Example 6
Coating was carried out in the same manner as in Example 6, except that the concentration of Lin Bright White was 20% by weight.
実施例１６
実施例７で、用いたマイカベース塗料のエクステリアマ
−リンブライトホワイトの濃度を２０重量％にした以外
は、実施例７と同様に塗装した。Example 16 Painting was carried out in the same manner as in Example 7, except that the concentration of exterior marlin bright white in the mica-based paint used in Example 7 was changed to 20% by weight.
実施例１７
実施例８で用いたマイカベース塗料のエクステリアマ−
リンブライトホワイトの濃度を２０重量％にした以外は
、実施例８と同様に塗装した。Example 17 Exterior paint of mica-based paint used in Example 8
Coating was carried out in the same manner as in Example 8, except that the concentration of Lin Bright White was 20% by weight.
実施例１８
実施例って用いたマイカベース塗料のエクステリアマ−
リンブライトホワイトの濃度を２０重量％にした以外は
、実施例９と同様に塗装した。Example 18 Exterior paint of mica-based paint used in Example
Coating was carried out in the same manner as in Example 9, except that the concentration of Lin Bright White was 20% by weight.
ついて、これら実施例１〜１８のテストピースの光沢を
Ｊ ＩＳ Ｋ−５４００（６，７）６０゜鏡面光沢度
により測定し、また促進耐候性をＪＩＳ Ｋ−５４０
０（６，１７）により測定した。この結果を表に示す。The gloss of the test pieces of Examples 1 to 18 was measured by JIS K-5400 (6,7) 60° specular gloss, and the accelerated weather resistance was measured by JIS K-540.
0(6,17). The results are shown in the table.
なお、促進耐候性の評価は、５００時間後の目視評価に
より行い、「○」は変化のないパネル、「△」は僅かに
変化したパネル、「×」は著しく変化したパネルをそれ
ぞれ表わす。The accelerated weathering resistance was evaluated by visual evaluation after 500 hours, and "○" indicates a panel with no change, "△" indicates a panel with a slight change, and "x" indicates a panel with a significant change.
（以下余白）
この表から明らかなように、光沢については何れも問題
はないか、耐候性については、クリヤ塗料に含まれる紫
外線吸収剤が１．５重量％以下になると僅かに耐候性の
低下が観察された。(Left below) As is clear from this table, there is no problem with gloss, and weather resistance slightly decreases when the ultraviolet absorber contained in the clear paint is less than 1.5% by weight. was observed.
（発明の効果）
以」二述べたように本発明によれは、耐候性等の塗膜性
能を維持しながら、見る角度を変えなくとも色彩か変化
する塗膜を得ることかでき、意匠性に富んだ外観となる
。(Effects of the Invention) As described above, according to the present invention, it is possible to obtain a coating film whose color changes without changing the viewing angle while maintaining coating film performance such as weather resistance, and the designability is improved. It has a rich appearance.
第１図は本発明の一実施例を示す塗膜の断面図、第２図
は本発明の他の実施例を示す塗膜の断面図、第３図はク
リヤ塗膜に自まれる紫外線吸収剤の添加量と光透過率と
の関係を示すグラフ、第４図は従来の干渉色塗膜を示す
塗膜の断面図である。
１・・・被塗物、 ２・・・カラーヘース
、３・・・マイカベース、 ４・・・クリヤ、５
・・・養色顔料、 ６・・・マイカ片、７・・
・フォトクロ塗膜、 ８・・・フォトクロ物質＠Ａｌ
１
１３
―
痰表
（ｍｍ）Fig. 1 is a sectional view of a coating film showing one embodiment of the present invention, Fig. 2 is a sectional view of a coating film showing another embodiment of the invention, and Fig. 3 is a UV absorption inherent in the clear coating film. A graph showing the relationship between the amount of additive added and light transmittance, and FIG. 4 is a sectional view of a coating film showing a conventional interference color coating film. 1...Object to be coated, 2...Color haze, 3...Mica base, 4...Clear, 5
...color pigment, 6...mica pieces, 7...
・Photochrome coating film, 8...Photochrome substance @Al
1 13 - Sputum surface (mm)
Claims (1)
と、このカラーベース塗膜上に形成されたフォトクロ物
質を含むフォトクロ塗膜と、このフォトクロ塗膜上に形
成された光輝性粉体を含むマイカベース塗膜と、さらに
、このマイカベース塗膜上に形成されたクリヤ塗膜とを
有する色彩可変塗膜。A color base coating film containing a colored pigment formed on an object to be coated, a photochrome coating film containing a photochrome substance formed on this color base coating film, and a glittering powder formed on this photochrome coating film. A color variable coating film comprising a mica-based coating film including a body, and a clear coating film formed on the mica-based coating film.