Prior art keywords
weight
brush
alloy material
sliding contact
sliding
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
JP24622083A
Other languages
Japanese (ja)
Other versions
JPS60138865A (en
Inventor
Susumu Fujishima
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tanaka Kikinzoku Kogyo KK
Original Assignee
Tanaka Kikinzoku Kogyo KK
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tanaka Kikinzoku Kogyo KK filed Critical Tanaka Kikinzoku Kogyo KK
Priority to JP24622083A priority Critical patent/JPS60138865A/en
Publication of JPS60138865A publication Critical patent/JPS60138865A/en
Publication of JPH0351074B2 publication Critical patent/JPH0351074B2/ja
Granted legal-status Critical Current

Links

Landscapes

  • Contacts (AREA)

Description

【発明の詳細な説明】[Detailed description of the invention]

本発明は、摺動接点装置に係り、特にそれを構
成するブラシとコンミテータ又はスリツプリング
の材料の改良に関する。 従来の摺動接点装置は、Pd87〜93重量%、
Ru7〜13重量%の合金材料にて構成したブラシ
と、Ag−Cd0.5〜15重量%の合金材料にて構成し
たコンミテータ又はスリツプリングとを組合わせ
て成るものである。 ところで、この摺動接点装置のブラシは、コン
ミテータ又はスリツプリングとの摺動時の凝着に
より耐摩耗性が劣り、摩耗粉が生じ易く接触抵抗
が不安定となつていた。 一方、コンミテータ又はスリツプリングは、
Ag−Cd0.5〜15重量%の合金材料により構成さ
れ、ブラシとの摺動時、粘着性が高く耐摩耗性に
劣るものであつた。 本発明は、斯かる欠点を解消すべくなされたも
のであり、ブラシの耐摩耗性及び接触抵抗特性を
向上させ、コンミテータ又はスリツプリングの耐
摩耗性を向上させた摺動接点装置を提供せんとす
るものである。 本発明の摺動接点装置は、組成比Pd87〜93重
量%、Ru7〜13重量%のPd−Ruが95〜99.5重量
%及び残部がCo、Sn及びTiの少なくとも1種を
合計で0.5〜5重量%から成る合金材料にて構成
したブラシと、Ag−Cu3〜12重量%又はAg−
Cu3〜12重量%−Cd5重量%以下の合金材料にて
構成したコンミテータ又はスリツプリングとを組
合わせて成るものである。 本発明の摺動接点装置に於いて、ブラシを組成
比でPd87〜93重量%、Ru7〜13重量%のPd−Ru
が95〜99.5重量%及び残部がCo、Sn及びTiの少
なくとも1種を合計で0.5〜5重量%から成る合
金材料にて構成した理由は、前記Rd−Ruの合金
材料の耐摩耗性を向上すべく析出物を適量発生さ
せ凝着を防止する為で、0.5重量%未満では析出
物の発生量が少なくてその効果を発揮できず、5
重量%を超えると酸化物の発生量が多くなり、接
触抵抗が高くなり、その上不安定となるものであ
る。また、Pd、Ruの含有量は、前記従来の合金
材料の組成比に変更を加えない範囲とすることに
より、従来の合金材料の特性は損なわれることな
く発揮されることとなるものである。 コンミテータ又はスリツプリングを、Ag−
Cu3〜12重量%又はAg−Cu3〜12重量%−Cd5重
量%以下の合金材料にて構成した理由は、ブラシ
との摺動時の粘着性を抑えて耐摩耗性を向上させ
る為で、Cuの含有量が3重量%未満ではその効
果が得られず、12重量%を超えると摺動時に発生
する酸化物の量が多くなりすぎて接触抵抗が高く
不安定になり、Cdの含有量が5重量%を超える
とこれが酸化Cdのなつた際、接触抵抗が高くな
り、耐摩耗性が劣下するものである。従つて、
Cuの含有量は3〜12重量%、Cdの含有量は5重
量%を超えないようにしたものである。 次に本発明による摺動接点装置の具体的な実施
例と従来例について説明する。 下記の表−1の左欄に示す成分組成の実施例及
び従来例の合金材料より成る線径0.7mmのブラシ
線材を各々長さ8mmに切断し、2本並列させて一
端を幅10mm、長さ13mm、厚さ0.2mmの台材に溶接
し、他端に2Rの円弧状の接触部を曲成してブラ
シを作つた。一方下記の表−1の右欄に示す成分
組成の実施例及び従来例の合金材料により成る厚
さ0.5mmの板材を打抜いて直径50mmのスリツプリ
ングを作つた。然してこれらブラシ及びスリツプ
リングを夫々組合わせて摺動接点装置を作り、
夫々ブラシをスリツプリングに接触させ、スリツ
プリングを正逆回転させて下記の試験条件にて摺
動試験を行ない、ブラシ及びスリツプリングの摩
耗量と接触抵抗を測定した処、下記の表−2に示
すような結果を得た。 試験条件 電 流 :0.6A 電 圧 :12V 負 荷 :抵抗負荷 回転数 :1000回転/分 周速度 :120〜130m/min 接触力 :100g 摺動時間:7時間
The present invention relates to a sliding contact device, and particularly to improvements in the materials of the brush, commutator, or slip ring constituting the sliding contact device. Conventional sliding contact device has Pd87~93% by weight,
It is a combination of a brush made of an alloy material containing 7 to 13% by weight of Ru and a commutator or slip ring made of an alloy material containing 0.5 to 15% by weight of Ag-Cd. By the way, the brush of this sliding contact device has poor wear resistance due to adhesion during sliding with the commutator or slip ring, and abrasion powder is likely to be generated, resulting in unstable contact resistance. On the other hand, a commutator or slip ring is
It was composed of an alloy material containing 0.5 to 15% by weight of Ag-Cd, and had high stickiness and poor abrasion resistance when sliding with a brush. The present invention has been made in order to eliminate such drawbacks, and it is an object of the present invention to provide a sliding contact device that improves the abrasion resistance and contact resistance characteristics of the brush and improves the abrasion resistance of the commutator or slip ring. It is something to do. The sliding contact device of the present invention has a composition ratio of 87 to 93% by weight of Pd, 7 to 13% by weight of Pd-Ru, 95 to 99.5% by weight, and the balance of at least one of Co, Sn, and Ti in total of 0.5 to 5% by weight. A brush composed of an alloy material consisting of 3% to 12% by weight of Ag-Cu or Ag-
It is combined with a commutator or slip ring made of an alloy material containing 3 to 12% by weight of Cu and 5% by weight of Cd. In the sliding contact device of the present invention, the brush has a Pd-Ru composition ratio of 87 to 93% by weight of Pd and 7 to 13% by weight of Ru.
The reason why it is made of an alloy material consisting of 95 to 99.5% by weight and the balance being 0.5 to 5% by weight of at least one of Co, Sn, and Ti in total is to improve the wear resistance of the Rd-Ru alloy material. This is to prevent adhesion by generating an appropriate amount of precipitates, and if it is less than 0.5% by weight, the amount of precipitates generated is small and the effect cannot be achieved.
If it exceeds % by weight, the amount of oxides generated will increase, contact resistance will increase, and furthermore, it will become unstable. Furthermore, by setting the contents of Pd and Ru within a range that does not change the composition ratio of the conventional alloy material, the characteristics of the conventional alloy material can be exhibited without being impaired. Commutator or slip spring, Ag-
The reason why it is made of an alloy material containing less than 3 to 12 weight % Cu or 3 to 12 weight % Ag-Cu and 5 weight % Cd is to suppress the stickiness when sliding with the brush and improve wear resistance. If the content of Cd is less than 3% by weight, the effect cannot be obtained, and if it exceeds 12% by weight, the amount of oxide generated during sliding becomes too large, resulting in high contact resistance and instability. If it exceeds 5% by weight, when the oxidized Cd wears off, contact resistance increases and wear resistance deteriorates. Therefore,
The content of Cu is 3 to 12% by weight, and the content of Cd is not more than 5% by weight. Next, specific embodiments and conventional examples of the sliding contact device according to the present invention will be described. Brush wire rods with a wire diameter of 0.7 mm made of alloy materials of the example and conventional example shown in the left column of Table 1 below were each cut into lengths of 8 mm, and two wire rods were placed in parallel with one end having a width of 10 mm and a length of 8 mm. A brush was made by welding it to a base material with a length of 13 mm and a thickness of 0.2 mm, and a 2R arc-shaped contact part was curved at the other end. On the other hand, slip rings with a diameter of 50 mm were made by punching out 0.5 mm thick plates made of alloy materials having the compositions shown in the right column of Table 1 below. Therefore, a sliding contact device was made by combining these brushes and slip rings, respectively.
A sliding test was conducted under the following test conditions by bringing each brush into contact with the slip ring and rotating the slip ring in forward and reverse directions.The wear amount and contact resistance of the brush and slip ring were measured, and the results are shown in Table 2 below. We obtained the results shown below. Test conditions Current: 0.6A Voltage: 12V Load: Resistance load Rotation speed: 1000 rotations/divided speed: 120-130m/min Contact force: 100g Sliding time: 7 hours

【表】【table】

【表】 上記の表−2で明らかなように実施例1〜13の
摺動接点装置のブラシとスリツプリングは、夫々
従来例1、2の摺動接点のブラシとスリツプリン
グに比し摩耗量が著しく少なく、接触抵抗は低く
安定していることが判る。これはひとえに実施例
1〜13の摺動接点装置のブラシを構成している合
金材料が、Co、Sn、Tiの少なくとも1種の添加
による析出者により凝着が防止され、耐摩耗性が
向上し、また摺動時に発生するCu、Sn、Tiの酸
化物の量が摩耗量とバランスしているからに他な
らない。また実施例1〜13の摺動接点装置のスリ
ツプリングを構成している合金材料のCuによつ
て摺動時の粘着性が高くなるのが抑えられて耐摩
耗性が向上しているからに他ならない。 以上詳記した通り本発明の摺動接点装置は、従
来の摺動接点装置に比べブラシとコンミテータ又
はスリツプリングの耐摩耗性が著しく優れてい
て、摩耗粉の発生量が極めて少なく、また接触抵
抗についても低く安定しているので、従来の摺動
接点装置にとつて代わることのできる画期的なも
のと云える。
[Table] As is clear from Table 2 above, the brushes and slip rings of the sliding contact devices of Examples 1 to 13 have a higher amount of wear than the brushes and slip rings of the sliding contact devices of Conventional Examples 1 and 2, respectively. It can be seen that the contact resistance is low and stable. This is because the alloy material constituting the brush of the sliding contact device of Examples 1 to 13 is prevented from adhesion by the precipitate added with at least one of Co, Sn, and Ti, and the wear resistance is improved. However, this is because the amount of Cu, Sn, and Ti oxides generated during sliding is in balance with the amount of wear. In addition, the Cu alloy material constituting the slip ring of the sliding contact devices of Examples 1 to 13 suppresses the increase in stickiness during sliding and improves wear resistance. None other than that. As detailed above, the sliding contact device of the present invention has significantly superior wear resistance of the brush and commutator or slip ring compared to conventional sliding contact devices, generates extremely little wear powder, and has contact resistance. Since it is also low and stable, it can be said to be an epoch-making device that can replace conventional sliding contact devices.

Claims (1)

【特許請求の範囲】[Claims] 1 組成比でPd87〜93重量%、Ru7〜13重量%
のPd−Ruが95〜99.5重量%及び残部がCo、Sn及
びTiの少なくとも1種を合計で0.5〜5重量%か
ら成る合金材料にて構成したブラシと、Ag−
Cu3〜12重量%又はAg−Cu3〜12重量%−Cd5重
量%以下の合金材料にて構成したコンミテータ又
はスリツプリングとを組合わせて成る摺動接点装
置。
1 Composition ratio: Pd 87-93% by weight, Ru 7-13% by weight
A brush made of an alloy material consisting of 95 to 99.5% by weight of Pd-Ru and the balance of a total of 0.5 to 5% by weight of at least one of Co, Sn, and Ti;
A sliding contact device that is combined with a commutator or slip ring made of an alloy material containing 3 to 12% by weight of Cu or 3 to 12% by weight of Ag-Cu and 5% by weight of Cd.
JP24622083A 1983-12-27 1983-12-27 Slide contact unit Granted JPS60138865A (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP24622083A JPS60138865A (en) 1983-12-27 1983-12-27 Slide contact unit

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
JP24622083A JPS60138865A (en) 1983-12-27 1983-12-27 Slide contact unit

Publications (2)

Publication Number Publication Date
JPS60138865A JPS60138865A (en) 1985-07-23
JPH0351074B2 true JPH0351074B2 (en) 1991-08-05

Family

ID=17145295

Family Applications (1)

Application Number Title Priority Date Filing Date
JP24622083A Granted JPS60138865A (en) 1983-12-27 1983-12-27 Slide contact unit

Country Status (1)

Country Link
JP (1) JPS60138865A (en)

Also Published As

Publication number Publication date
JPS60138865A (en) 1985-07-23

Similar Documents

Publication Publication Date Title
JPH0351074B2 (en)
JPH0354814B2 (en)
JPH0351263B2 (en)
JPH056770B2 (en)
JPH0332871B2 (en)
JPH0351073B2 (en)
JPH0354809B2 (en)
JPH0332872B2 (en)
JPH0351267B2 (en)
JPH0351262B2 (en)
JPH0351072B2 (en)
JPH0354807B2 (en)
JPH0351071B2 (en)
JPH0332869B2 (en)
JPH0332866B2 (en)
JPH056769B2 (en)
JPH0354810B2 (en)
JPH0354812B2 (en)
JPH056772B2 (en)
JPH0351078B2 (en)
JPH0332870B2 (en)
JPH0351266B2 (en)
JPH0354815B2 (en)
JPH056773B2 (en)
JPH0354818B2 (en)