JPH0364501A - Good smell stocking and its production - Google Patents
Good smell stocking and its productionInfo
- Publication number
- JPH0364501A JPH0364501A JP20096889A JP20096889A JPH0364501A JP H0364501 A JPH0364501 A JP H0364501A JP 20096889 A JP20096889 A JP 20096889A JP 20096889 A JP20096889 A JP 20096889A JP H0364501 A JPH0364501 A JP H0364501A
- Authority
- JP
- Japan
- Prior art keywords
- stockings
- microcapsules
- fragrance
- urethane binder
- treatment bath
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【発明の詳細な説明】
（産業上の利用分野）
本発明は、芳香性を有するストッキング、詳しくは編立
てられたストッキングに香料を含有するマイクロカプセ
ルを付着せしめて、耐久性のある芳香を付与したストッ
キング及びその製造方法に関するものである。Detailed Description of the Invention (Industrial Application Field) The present invention provides a durable fragrance by attaching microcapsules containing a fragrance to fragrant stockings, specifically knitted stockings. The present invention relates to stockings and a method for manufacturing the same.
（従来の技術）
従来から、芳香を有する衣類については様々な開発がな
され、市場にも多く出回っていた。ところが、これらの
多くは単に最終製品に香水をスプレーしただけのもの、
或いは香気物質を表面に塗布しただけのものであって、
−旦香料が蒸発すれば芳香が完全に消失してしまうもの
であった。また耐洗濯性に乏しく、１回の洗濯で完全に
香料が脱落してしまうようなものであった。(Prior Art) Conventionally, various developments have been made regarding fragranced clothing, and many of them have been on the market. However, many of these products are simply sprayed with perfume on the final product;
Or, it is simply a product with an aromatic substance applied to its surface.
-If the fragrance material evaporated, the fragrance would completely disappear. In addition, it had poor washing resistance, and the fragrance completely came off after one wash.
そこで、芳香を長期間持続させるための加工方法が、特
公昭５！−４７４４０号公報、特開昭５４１１２２８３
号公報等に多数提案されている。Therefore, a processing method was developed to maintain the fragrance for a long time. -47440 Publication, JP 54112283
Many proposals have been made in publications such as issues.
このような中で、ストッキングに対しても芳香を付与す
ることが種々試みられてきた。これも、従来は、仕上の
時点で香水をスプレーするか、或いは包装時に包装袋の
中に芳香紙を封入し、または芯紙を芳香紙とし、その香
りをストッキングに移すというようなものであった。Under these circumstances, various attempts have been made to add fragrance to stockings. Conventionally, this method involved spraying perfume on the stockings at the time of finishing, or enclosing scented paper in a packaging bag during packaging, or using scented paper as the core paper, and transferring the scent to the stockings. Ta.
（発明が解決しようとする課題）
しかしながら、上記のようにして得られたストッキング
は、その芳香が耐久性に乏しく、たった１回の洗濯で完
全に芳香が消失してしまい、極めて商品価値の低いもの
であった。更に、着用中外気に接触することにより、す
ぐに香料が蒸発してしまい、着用後僅か数時間しか芳香
を維持することのできないものさえもあった。また、包
装袋の中で芳香紙の香りをストッキングに移すものにお
いては、袋密封後の経過時間によって与えられる芳香の
強さが異なり、結果的にこれが快香とならず商品自体が
欠陥品となってしまう場合があった。(Problem to be Solved by the Invention) However, the stockings obtained as described above have poor fragrance durability, and the fragrance completely disappears after just one washing, resulting in extremely low commercial value. It was something. Furthermore, the fragrance quickly evaporates when it comes into contact with the outside air while being worn, and some products even maintain their fragrance for only a few hours after being worn. In addition, in cases where the scent of aromatic paper is transferred to the stockings in a packaging bag, the strength of the fragrance varies depending on the time elapsed after the bag is sealed, and as a result, the fragrance does not become pleasant and the product itself may be defective. There were cases where this happened.
本発明者等は、上述のような実情に鑑み、耐久性のある
芳香をストッキングに付与することを目３
的に鋭意検討を重ねた結果、香料を含有するマイクロカ
プセルを用いることがストッキングの芳香加工に好適で
あるとの知見を得た。このマイクロカプセルに関しては
従来から様々な製造方法が開発されており、代表的なも
のとしては特公昭５７−７７２４号公報に記載された方
法が挙げられる。In view of the above-mentioned circumstances, the inventors of the present invention have conducted extensive studies with the aim of imparting a durable fragrance to stockings. It was found that it is suitable for processing. Various manufacturing methods have been developed for these microcapsules, and a representative example is the method described in Japanese Patent Publication No. 57-7724.
また、マイクロカプセルを繊維に適用することも特開昭
４９−１９１９７号公報等で種々提案されている。Furthermore, various proposals have been made to apply microcapsules to fibers, such as in Japanese Patent Application Laid-Open No. 19197-1987.
然して、本発明は、香料を含有するマイクロカプセルを
ストッキングに付着せしめることにより芳香の持続性が
得られること、即ち着用中の摩擦で少しずつマイクロカ
プセルが破れて継続的な発散効果を奏することに着目し
たものである。ところが、ストッキングは極めて高密度
な編地からなり、且つその編成原糸をナイロンを中心と
する表面摩擦の少ないフィラメント糸としているため、
マイクロカプセルを付着せしめることが非常に困難であ
る。即ち、多孔質化学繊維等にマイクロカプセルをひっ
かけて付着させることは比較的容易−
であるが、ナイロンフィラメント等を編成原糸とするス
トッキングに対してはこの付着は難しく、また付着量を
多くすることのみを目的として煩雑な加工を行なっても
、香りがきつくなるだけで風合を劣化せしめる傾向があ
り、芳香ストッキングとしては不適であった。つまり、
ストッキングの場合は、製品自体の耐久性を考慮すれば
、２０回。However, the present invention is capable of maintaining the fragrance by attaching microcapsules containing a fragrance to stockings, that is, the microcapsules are gradually torn by friction during wear, resulting in a continuous release effect. This is what we focused on. However, stockings are made of extremely high-density knitted fabric, and the knitting material is filament yarn, mainly nylon, with low surface friction.
It is very difficult to attach microcapsules. In other words, it is relatively easy to hook and attach microcapsules to porous chemical fibers, etc., but it is difficult to attach them to stockings made of nylon filaments, etc., and the amount of adhesion may be large. Even if complicated processing was performed for the sole purpose of this, the fragrance would only become stronger and the texture would deteriorate, making it unsuitable for use as aromatic stockings. In other words,
In the case of stockings, considering the durability of the product itself, it can be used 20 times.
３０回もの耐洗濯性を追求したものよりも、微妙な良い
香りをある適度の期間持続しうるものが商品価値の高い
ものなのである。Rather than products that are designed to withstand up to 30 washes, products that can maintain a subtle, pleasant fragrance for a reasonable period of time are of higher commercial value.
本発明は、上述のような知見のもとでなされたものであ
って、ストッキング自体の柔らかい風合、伸縮性等を損
なうことなく、“好ましい香りの発散と１芳香の持続性
”との両娑件を満足しうる芳香ストッキングの提供を目
的とするものである。The present invention was made based on the above-mentioned knowledge, and it is possible to achieve both "desirable fragrance emission and the persistence of one fragrance" without impairing the soft texture, elasticity, etc. of the stockings themselves. The purpose of the present invention is to provide aromatic stockings that can satisfy people's needs.
（課題を解決するための手段）
上記の目的を達成する本発明のストッキングは、香料入
りマイクロカプセルを編地の略々全面に均一に付着せし
めたストッキングであって、マイクロカプセルとウレタ
ン系バインダーとが５＝１〜１：δの割合（重量比）で
与えられ、且つこれら両者の付着量が乾燥状態のストッ
キング総重量の１．０〜８．０％を占めている芳香スト
ッキングである。(Means for Solving the Problems) The stockings of the present invention that achieve the above objects are stockings in which perfumed microcapsules are uniformly adhered to substantially the entire surface of the knitted fabric, and the microcapsules and the urethane binder are bonded together. is given in a ratio (weight ratio) of 5=1 to 1:δ, and the amount of both of these substances attached accounts for 1.0 to 8.0% of the total weight of the stocking in a dry state.
そして、この芳香ストッキングの製造方法としては、香
料入りマイクロカプセルとウレタン系バインダーとを５
＝１〜１：５の割合（重量比）で混合した処理浴にスト
ッキングを投入し、該処理浴の水素イオン濃度を緩衝剤
にて４〜６の範囲内に設定維持して、２．０〜８０℃の
加熱処理を行なう方法がある。The method for manufacturing these aromatic stockings is to prepare fragranced microcapsules and a urethane binder for 5 minutes.
The stockings were placed in a treatment bath mixed at a ratio (weight ratio) of 1 to 1:5, and the hydrogen ion concentration of the treatment bath was set and maintained within the range of 4 to 6 with a buffer to 2.0. There is a method of performing heat treatment at ~80°C.
（作用）
上記のように構成された芳香ストッキングを着用すると
、編地の略々全面に均一に付着された香料入りマイクロ
カプセルが、着用時の摩擦によって少しずつ壊れてほど
良い芳香が発散される。また、ウレタン系バインダーを
適宜量与えることにより、編地へのマイクロカプセルの
付着が充分なものとなり、洗濯により一気に脱落するこ
とが防止されることとなる。(Function) When the aromatic stockings configured as described above are worn, the fragrance-containing microcapsules, which are evenly adhered to almost the entire surface of the knitted fabric, are broken little by little by the friction when worn, releasing a nice fragrance. . Further, by applying an appropriate amount of the urethane binder, the adhesion of the microcapsules to the knitted fabric becomes sufficient, and they are prevented from falling off all at once during washing.
一
そして、その製造方法においては、香料入りマイクロカ
プセルとウレタン系バインダーとを混合した処理浴のｐ
Ｈを４〜６の範囲内の酸性浴とすることにより、マイク
ロカプセル／バインダー間の結合力及びマイクロカプセ
ル・バインダー／編地間の吸着性が適度に向上し、安定
した反応のもとて好適な付着量が得られるのである。In the manufacturing method, a treatment bath containing a fragrance-containing microcapsule and a urethane binder is prepared.
By using an acidic bath with H in the range of 4 to 6, the bonding force between microcapsules/binder and the adsorption between microcapsules/binder/knitted fabric are moderately improved, which is suitable for stable reaction. This results in a large amount of adhesion.
（実施例） 以下、本発明を具体的に説明する。(Example) The present invention will be explained in detail below.
本発明でいうストッキングとは、レッグ長が膝上までの
オーバーニーストッキング、大腿部付根までのフルレン
グスストッキング、及びパンティ部とストッキング部と
を一体化したパンティストッキング等、ストッキング類
全てを総称するものであって、その素材もナイロン繊維
、ポリエ／チル繊維等の合成繊維、綿繊維等の天然繊維
のいずれを選択してもよく、編組織についても特に限定
はされない。Stockings as used in the present invention refer to all types of stockings, including over-knee stockings with leg lengths above the knees, full-length stockings that extend to the base of the thighs, and pantyhose that integrate panty and stocking parts. The material may be any of synthetic fibers such as nylon fibers and polyester/chill fibers, and natural fibers such as cotton fibers, and the knitting structure is not particularly limited.
本発明において用いられる香料入りマイクロカプセルは
、適宜の摩擦によって壊れて芳香を発散するものであれ
ばその組成等は限定されないが、その壁膜の主成分（５
０重量優以上）をホルマリン系樹脂、好ましくは尿素−
ホルマリン系樹脂、メラミン−ホルマリン系樹脂とする
ものが耐熱性、耐圧性、耐水性に優れており好適である
。The fragrance-containing microcapsules used in the present invention are not limited in their composition as long as they break down with appropriate friction and emit fragrance;
0 weight or more) in a formalin-based resin, preferably urea-
Formalin-based resins and melamine-formalin-based resins are preferred because they have excellent heat resistance, pressure resistance, and water resistance.
また、このマイクロカプセルの大きさは通常２〜３００
μの範囲であり、ストッキングに付着させる場合には５
〜２０μの範囲が好ましい。また壁膜の含有量は、通常
マイクロカプセルの重量を基準として３〜５０重量鋒で
あり、ストッキングに付着させる場合には５〜２５重量
斧の範囲が好ましい。然して、本発明において用いられ
るマイクロカプセルは、適宜の摩擦によって壊れて香り
が発散するものであればその組成等は特に限定されない
が、低ホルマリンマイクロカプセルが好ましい。In addition, the size of this microcapsule is usually 2 to 300
μ range, and when attached to stockings, 5
A range of ~20μ is preferred. The content of the wall film is usually 3 to 50 weight units based on the weight of the microcapsules, and preferably 5 to 25 weight units when attached to stockings. However, the composition of the microcapsules used in the present invention is not particularly limited as long as they can be broken by appropriate friction and emit a fragrance, but low formalin microcapsules are preferred.
このマイクロカプセルは公知の方法によって製造するこ
とができる（例えば工業技術ライブラリー２５、マイク
ロカプセル、近藤朝士著日刊工業新聞社発行、昭和４５
年、特公昭５７−７７２４＝８
号公報）。ホルマリン系樹脂を壁膜とするものは、例え
ば少なくとも香料を配合した芯物質と尿素又はメラミン
とを水中に乳化させ（乳化剤はポリスチレンスルホン酸
ソーダ、ポリアクリル酸ソーダ、ポリビニルアルコール
、ポリエチレングリコール佐ど、必要によりｐＨ調整を
行う、また水温は４０℃）、次いでホルマリン水溶液を
加えた後撹拌下７０℃に昇温して重縮合反応させる。次
いで、主伐したマイクロカプセルを濾過・乾燥すると、
香料入りマイクロカプセルが得られる。尚、大きさは主
として撹拌の強弱と乳化剤の濃度により、壁膜の含有量
は主として油滴中の尿素又はメラミンの濃度により、ま
た壁膜の多孔性は主としてホルマリンの濃度によりコン
トロールする（緻密にするためには高濃度のホルマリン
を使う）。This microcapsule can be manufactured by a known method (for example, Industrial Technology Library 25, Microcapsule, written by Asashi Kondo, published by Nikkan Kogyo Shimbun, 1972).
1986, Special Publication No. 57-7724=8). For those whose walls are made of formalin-based resin, for example, at least a core substance containing a fragrance and urea or melamine are emulsified in water (emulsifiers include sodium polystyrene sulfonate, sodium polyacrylate, polyvinyl alcohol, polyethylene glycol soda, etc.). If necessary, the pH is adjusted (the water temperature is 40°C), and then, after adding an aqueous formalin solution, the temperature is raised to 70°C with stirring to carry out a polycondensation reaction. Next, when the harvested microcapsules are filtered and dried,
Flavored microcapsules are obtained. The size of the wall film is controlled mainly by the strength of stirring and the concentration of the emulsifier, the content of the wall film is controlled mainly by the concentration of urea or melamine in the oil droplets, and the porosity of the wall film is controlled mainly by the concentration of formalin. (Use highly concentrated formalin to do this.)
また、ウレタン系バインダーは、コーティング作用を奏
し、マイクロカプセルと編地との間の接着剤としての役
割を果たすものであり、特に、水への０分散性に優れ水
で容易に希釈可能なエマルジョン型のものが好ましい。In addition, the urethane binder has a coating effect and plays a role as an adhesive between the microcapsules and the knitted fabric.Especially, the urethane binder has excellent dispersibility in water and can be easily diluted with water. Types are preferred.
これは、水の蒸発により皮膜を形成するものであり、耐
久性のある接着効果を奏するものである。This forms a film through evaporation of water and provides a durable adhesive effect.
ウレタン系バインダーとしては、様々な公知のものを用
いることができるが、中でも反応型ポリウレタン水分散
体が好ましく、特に強制乳化型ポリウレタン水分散体が
、耐熱水性及び耐湿熱性に優れ好適である。これは、疎
水性ウレタンエラストマー骨格であるため、皮膜の耐水
、耐熱水、耐湿熱性が優れ、且つ架橋構造を有するため
耐溶剤性及び弾性回復率に優れているものである。Various known urethane binders can be used, but reactive polyurethane aqueous dispersions are preferred, and forced emulsification polyurethane aqueous dispersions are particularly preferred due to their excellent hot water resistance and moist heat resistance. Since this is a hydrophobic urethane elastomer skeleton, the film has excellent water resistance, hot water resistance, and moist heat resistance, and because it has a crosslinked structure, it has excellent solvent resistance and elastic recovery rate.
そして、このバインダーはマイクロカプセルの０．２〜
５倍（重量比）与えられ、充分な接着効果を発揮する。And this binder is 0.2 ~
5 times (weight ratio) and exhibits sufficient adhesive effect.
即ち、この量をマイクロカプセルの０．２倍よりも少な
くするとコーティング作用が極端に劣り、一方これを５
倍よりも多く与えてもマイクロカプセルの付着率はほと
んど変わらず、逆にストッキングの柔軟な風合や伸縮性
において問題が引き起こされ好ましくない。That is, if this amount is less than 0.2 times the amount of microcapsules, the coating effect will be extremely poor;
Even if more than twice the amount is given, the adhesion rate of the microcapsules hardly changes, and on the contrary, it causes problems in the soft feel and elasticity of the stockings, which is not preferable.
このように、マイクロカプセルとウレタン系バインダー
とを５：１〜１：５の割合で与えられた８−
１０
本発明のストッキングは、これら両者の付着量が乾燥状
態のストッキング総重量の１．０〜８．０％を占めるも
のとして構成されている。即ち、マイクロカプセルは、
ウレタン系バインダーを上記割合で与えられることによ
りストッキングに充分に付着するものであるから、これ
ら両者の付着量が前記１．０％よりも少ないものであれ
ば、芳香の強さ及び耐久性共に不充分であり、一方これ
が８．０％よりも多くなると、ストッキングとしての風
合面、伸縮性にかかわり、また−時に発散する香りがき
つくなりすぎるという問題も存在し、いずれも不適であ
る。つまり、好ましい香りの発散効果と共にストッキン
グとしての好適な風合及び柔軟性を有し、且つその芳香
が適宜の耐久性を有するという全ての要件を満たすもの
は、上記の付着量を、乾燥状態のストッキングにおいて
総重量の１．０〜８．０％、好ましくは２，０〜７．０
％とするものである。As described above, the 8-10 stockings of the present invention are provided with microcapsules and urethane binder in a ratio of 5:1 to 1:5, and the amount of both of them attached is 1.0 of the total weight of the stockings in a dry state. It is configured such that it accounts for ~8.0%. That is, microcapsules are
By adding the urethane binder in the above ratio, it will adhere to the stockings sufficiently, so if the amount of both of these binders is less than the above 1.0%, the strength and durability of the fragrance will be poor. On the other hand, if it exceeds 8.0%, it affects the feel and elasticity of stockings, and sometimes the scent emitted is too strong, and both are unsuitable. In other words, a stocking that satisfies all the requirements of having a desirable scent dispersion effect, a suitable texture and flexibility as a stocking, and having an appropriate fragrance durability, has the above-mentioned adhesion amount 1.0-8.0% of the total weight in stockings, preferably 2.0-7.0%
%.
次に、上述の芳香ストッキングの製造方法を説明する。Next, a method for manufacturing the above-mentioned aromatic stockings will be explained.
この製造方法において、香料入りマイクロカプセルを付
着せしめる処理は、ストッキングが染色されてフィック
ス処理を施された後の柔軟処理時に行なうと、効率的に
優れた処理効果を奏し好適である。In this manufacturing method, it is preferable that the process of attaching the fragrance-containing microcapsules is carried out during the softening process after the stockings have been dyed and subjected to the fix process, as this will efficiently produce excellent processing effects.
まず、処理機にマイクロカプセルとウレタン系バインダ
ーとを５：１〜１＝５の割合（重量比）で投入し、柔軟
剤と同浴の処理浴とする。この時、各薬品は、水で充分
に溶解、希釈した上で投入するものとする。そして、こ
れらが充分に均一になった時点で緩衝剤を投入する。こ
の緩衝剤とは、処理浴の水素イオン濃度を調整し、最適
ｐＨに設定維持するためのものであり、例えば結合燐酸
塩を主成分として優れたｐＨ緩衝力を発揮するもの等、
様々なものが挙げられるが、その性質と投入量により処
理浴のｐＨを４〜６の範囲内に設定維持しうるものであ
れば、特に限定されるものではない。即ち、処理浴を酸
性浴とすることにより処理が安定化すること、反応が促
進されること等から、マイクロカプセル／バインダー及
びマイクロカプセル・バインダー／編地の間の結合力が
強化され、吸着性が著しく向上することとなるのである
。従って、処理浴のｐｌ（は６未満とするが、方ｐＨが
４未満となり低過ぎると、マイクロカプセル、バインダ
ー、柔軟剤等が凝集してコンプレックスを形成し、これ
が付着斑を引き起こすこととなり不適である。従って、
処理浴のｐＨは、緩衝剤により４〜６の範囲内に設定し
、特に好適なｐＨ４，５〜５．５を目標値とするもので
ある。First, microcapsules and a urethane binder are put into a treatment machine at a ratio (weight ratio) of 5:1 to 1=5 to form a treatment bath that is the same bath as the softener. At this time, each chemical should be sufficiently dissolved and diluted with water before being added. Then, when these become sufficiently uniform, a buffer is added. This buffer is used to adjust the hydrogen ion concentration of the treatment bath and maintain it at the optimum pH.
Various types can be mentioned, but there are no particular limitations as long as the pH of the treatment bath can be set and maintained within the range of 4 to 6 depending on the properties and amount added. In other words, by making the treatment bath acidic, the treatment is stabilized and the reaction is accelerated, so the bonding force between the microcapsule/binder and the microcapsule/binder/knitted fabric is strengthened, and the adsorption property is increased. This results in a significant improvement. Therefore, the PL of the treatment bath should be less than 6, but if the pH is too low (less than 4), microcapsules, binders, softeners, etc. will aggregate to form a complex, which will cause adhesion spots and is not suitable. Yes. Therefore,
The pH of the treatment bath is set within the range of 4 to 6 using a buffer, with a particularly preferred target value of pH 4.5 to 5.5.
そして、この処理浴中にストッキングを適宜量投入し、
２０〜８０℃の加熱処理を行なう。この処理温度が２０
℃未満では、処理時間を長くしても満足な処理効果は得
られず、一方これを８０℃より高くしてしまうと、各薬
品にとってもストッキングにとっても好ましくなく、品
質面での問題が生じることとなることか、ら、上記の範
囲内とし、特に通常の柔軟処理温度である４０〜６０℃
とすることが好適である。尚、この処理の時間について
は、温度との関係もあるが、長くすれば優れた処理効果
が得られるというものでもなく、１５〜３０分程で充分
である。Then, put an appropriate amount of stockings into this treatment bath,
Heat treatment is performed at 20 to 80°C. This treatment temperature is 20
If the temperature is below 80°C, a satisfactory treatment effect cannot be obtained even if the processing time is extended, while if it is increased above 80°C, it is unfavorable for both the chemicals and the stockings, leading to quality problems. Therefore, the temperature should be within the above range, especially the normal softening temperature of 40 to 60°C.
It is preferable that It should be noted that the time for this treatment is related to the temperature, but longer treatment times do not necessarily result in better treatment effects; about 15 to 30 minutes is sufficient.
然して、このようにして得られた処理済のストッキング
は、次工程の脱水から乾燥、仕上セット工程へと送られ
て完成品となるのである。The treated stockings thus obtained are then sent to the next process of dehydration, drying, and final setting to become a finished product.
下記の２種類のストッキングを編立てて染色、フィック
ス処理終了後、上述の方法で処理を行なった。The following two types of stockings were knitted, dyed, fixed, and then treated using the method described above.
試験品；■パンティストッキング
レ ッ グ 部：１５ｄ／３ｆケンネル糸パンテイー・
トウ部：５０ｄ／８ｆ ウーリー糸■パンティストッキ
ング（サポートタイプ）レッグ部：
（２０Ｘ１３Ｘ１３ＤＯＹ）ＸＩ ３ｄ／３ ｆ録パン
ティ一部：
（ＨＩＸ３０ＰＯＹ）Ｘ５０ｄ／８ｆウーリー糸ト
ウ 部 ：
１３ｄ／ｌｆ生糸Ｘ５０ｄ／８ｆウーリー糸×７０ｄ／
１８ ｆウーリー糸
バインダー；スーパーフレックスＥ−２０００２％ｏｗ
ｆ〔第一工業製薬（銅」
緩衝剤；ウルトラＭＴ
〔御幣島化学工業（株）〕
尚、耐洗濯性の試験は、ＪＩＳ Ｌ０２１７１０３法
に準じて行ない、芳香の消失するまでの回数で表した。Test item: ■Pantyhose leg part: 15d/3f kennel thread pantyhose
Toe part: 50d/8f woolly thread ■Pantyhose (support type) Leg part: (20X13X13DOY) XI 3d/3 f Panty part: (HIX30POY)
C part: 13d/lf raw silk x50d/8f woolly thread x70d/
18 f woolly yarn binder; superflex E-20002%ow
f [Daiichi Kogyo Seiyaku (Copper)] Buffer; Ultra MT [Mitejima Chemical Industry Co., Ltd.] The washing resistance test was conducted according to JIS L0217103 method, and was expressed as the number of times until the fragrance disappeared.
また、芳香の評価は、１０人で夫々５段階評価（最適な
芳香を発散しているものを０点とし、その上下で強過ぎ
るものを＋１．＋２、弱過ぎるものを−１，−２とする
）を行ない、その平均点を評価点とした。また、風合に
ついては、同じく１０人が夫々特に劣ると感じたものの
みをチエツクし、チエツク数で表している。In addition, the fragrance was evaluated by 10 people on a 5-point scale (0 points are given for those emitting the optimal fragrance, +1 and +2 are given for those that are too strong above and below that, and -1 and -2 are given for those that are too weak). ), and the average score was used as the evaluation score. Regarding texture, each of the 10 people checked only those items that they felt were particularly poor, and the results are expressed in terms of the number of checks.
その結果を次表に示す。The results are shown in the table below.
この結果をみれば、本発明に係る芳香ストッキングが当
所の目的を達成していること、即ち、耐久性のある良い
香りと良好な風合を有するものとなっていることが明ら
かになるであろう。Looking at these results, it becomes clear that the aromatic stockings according to the present invention have achieved the objectives of our organization, that is, they have a durable, pleasant scent and a good texture. Dew.
（発明の効果）
本発明は、以上に述べた構成により、次のような効果を
奏する。(Effects of the Invention) The present invention achieves the following effects with the configuration described above.
まず、ストッキングの編地の略々全面に、均一に香料入
りマイクロカプセルを付着せしめているため、着用中の
摩擦により少しずつカプセルが破れて徐々に好適な香り
を発散する。従って、その香りは一気に発散されて消失
してしまうものではなく、充分な持続性を有するもので
ある。First, since the fragrance-containing microcapsules are uniformly adhered to almost the entire surface of the knitted fabric of the stockings, the capsules gradually break due to friction during wear, gradually releasing a suitable fragrance. Therefore, the fragrance does not emanate and disappear all at once, but has sufficient sustainability.
また、マイクロカプセルに対して適宜の割合でウレタン
系バインダーを与えることにより、接着力及び付着性を
著しく向上させて目的とする付着量及び香りの耐久性を
獲得している。Furthermore, by adding a urethane binder to the microcapsules in an appropriate ratio, the adhesive strength and adhesion properties are significantly improved, and the desired adhesion amount and fragrance durability are achieved.
そして、その製造方法は、煩雑な加工工程を必要とせず
、マイクロカプセルとウレタン系バインダーとを適宜の
割合で混合した処理浴を用い、その水素イオン濃度を好
適なものに設定維持してストッキングを投入し、加熱処
理を行なうことにより、本発明に係る芳香スＩ・ツキン
グを確実に製造しうる方法である。The manufacturing method does not require complicated processing steps, and uses a treatment bath in which microcapsules and urethane binder are mixed in an appropriate ratio, and the hydrogen ion concentration is set and maintained at a suitable level to produce stockings. This is a method that can reliably produce the aromatic sticks according to the present invention by adding the ingredients and performing heat treatment.
１８18
Claims (3)
一に付着せしめたストッキングであって、マイクロカプ
セルとウレタン系バインダーとが５：１〜１：５の割合
（重量比）で与えられ、且つこれら両者の付着量が乾燥
状態のストッキング総重量の１．０〜８．０％を占めて
いる芳香ストッキング。(1) Stockings in which fragrance-containing microcapsules are uniformly adhered to almost the entire surface of the knitted fabric, in which the microcapsules and the urethane binder are provided in a ratio (weight ratio) of 5:1 to 1:5, The fragranced stockings have an amount of both of these substances attached to the stockings in an amount of 1.0 to 8.0% of the total weight of the stockings in a dry state.
型ポリウレタン水分散体である芳香ストッキング。(2) A scented stocking, wherein the urethane binder according to claim 1 is a forced emulsification type polyurethane aqueous dispersion.
ーとを５：１〜１：５の割合（重量比）で混合した処理
浴にストッキングを投入し、該処理浴の水素イオン濃度
を緩衝剤にて４〜６の範囲内に設定維持して、２０〜８
０℃の加熱処理を行なうことを特徴とする芳香ストッキ
ングの製造方法。(3) The stockings are placed in a treatment bath containing a mixture of fragranced microcapsules and a urethane binder at a ratio (weight ratio) of 5:1 to 1:5, and the hydrogen ion concentration of the treatment bath is adjusted to 40% using a buffer. Keep the setting within the range of ~6, and set it to 20~8.
A method for producing aromatic stockings, which comprises performing a heat treatment at 0°C.