JPH0367971B2 - - Google Patents
Info
- Publication number
- JPH0367971B2 JPH0367971B2 JP58096833A JP9683383A JPH0367971B2 JP H0367971 B2 JPH0367971 B2 JP H0367971B2 JP 58096833 A JP58096833 A JP 58096833A JP 9683383 A JP9683383 A JP 9683383A JP H0367971 B2 JPH0367971 B2 JP H0367971B2
- Authority
- JP
- Japan
- Prior art keywords
- core
- samples
- ferrite
- molding
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】
本発明は磁気記録装置の消去ヘツドのコアに用
いられるMn−Znフエライトに関し、特に、コア
をヘツドに組み込む際の樹脂モールド処理による
特性劣化の小さい消去ヘツドコア用Mn−Znフエ
ライトに関する。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to Mn-Zn ferrite used in the core of an erasing head of a magnetic recording device, and particularly relates to a Mn-Zn ferrite for erasing head cores that exhibits less characteristic deterioration due to resin molding when the core is assembled into the head. Regarding ferrite.
従来の消去ヘツドコア用Mn−Znフエライト
は、モールド前には優れた特性を有していても、
モールド後に特性が大きく劣化する欠点があつ
た。 Although conventional Mn-Zn ferrite for erase head cores has excellent properties before molding,
The drawback was that the characteristics deteriorated significantly after molding.
第１表を参照すると、従来の消去ヘツド用の
Mn−Znフエライトコアの組成がNo.１〜No.６の試
料について示されている。また、第２表には、第
１表のNo.１〜No.６の試料のモールド前及びモール
ド後の諸特性が示されている。第２表において、
μは透磁率、ＱはいわゆるＱ特性、B10は10エル
ステツドの磁場中での磁束密度（Gauss）、Brは
残留磁束密度（Gauss）、Hcは抗磁力（Oe）であ
る。 Referring to Table 1, the
The compositions of the Mn-Zn ferrite cores are shown for samples No. 1 to No. 6. Further, Table 2 shows various properties of the samples No. 1 to No. 6 in Table 1 before and after molding. In Table 2,
μ is the magnetic permeability, Q is the so-called Q characteristic, B 10 is the magnetic flux density (Gauss) in a magnetic field of 10 Oersteds, Br is the residual magnetic flux density (Gauss), and Hc is the coercive force (Oe).
コアをヘツドに組み立てる場合には有機樹脂で
モールド処理するため、その樹脂効果によつて、
コアに物理的歪が加わり、その歪により上述の諸
特性が変化する。従来のコアの組成では、磁歪定
数λSが０より大きいため、モールドによる諸特性
の劣化が著しい。 When assembling the core into the head, it is molded with organic resin, so the resin effect
Physical strain is applied to the core, and the above-mentioned characteristics change due to the strain. In the conventional core composition, since the magnetostriction constant λ S is larger than 0, the deterioration of various properties due to molding is significant.
この結果、第２表にも示されているモールド後
における目標値、μ≧200、Ｑ≧25、B10≧4000
（Gauss）、Br≦1600（Gauss）、Hc≦1.0（Oe）を
同時に満足するものは、第１表のNo.１〜No.６の試
料にはない。 As a result, the target values after molding, which are also shown in Table 2, μ≧200, Q≧25, B 10 ≧4000
(Gauss), Br≦1600 (Gauss), and Hc≦1.0 (Oe) are not found among the samples No. 1 to No. 6 in Table 1.
本発明の目的は、モールドによる諸特性の劣化
が小さく、しかも温度特性の良い消去ヘツドコア
用Mn−Znフエライトを提供することにある。 SUMMARY OF THE INVENTION An object of the present invention is to provide a Mn--Zn ferrite for an erase head core that exhibits little deterioration of various properties due to molding and has good temperature characteristics.
本発明は、磁歪定数λSを０として、モールドに
よる諸特性の劣化を小さくするために、Fe2O3を
51.8〜52.2モル％、MnOを31.6〜35.4モル％、
MnOを31.6〜35.4モル％含む組成としたものであ
る。更に、本発明は、これら主成分にSiO2と
CaOとを加え、結晶粒界にSiO2とCaOとの複合
被覆を生成させ、電気抵抗を高め損失を小さくし
たもので、それらの好ましい量はSiO2が0.015〜
0.022重量％、CaOが0.02〜0.05重量％である。そ
して、本発明は、温度特性を改善するために、上
述の特性を損うことのないSnO2を1.5〜2.0重量％
同時に添加したものである。 In the present invention, in order to set the magnetostriction constant λ S to 0 and to reduce the deterioration of various properties due to molding, Fe 2 O 3 is used.
51.8-52.2 mol%, MnO 31.6-35.4 mol%,
The composition contains 31.6 to 35.4 mol% of MnO. Furthermore, the present invention adds SiO 2 and
CaO is added to form a composite coating of SiO 2 and CaO at the grain boundaries, increasing electrical resistance and reducing loss.The preferred amount of SiO 2 is 0.015~
0.022% by weight, CaO 0.02-0.05% by weight. And, in order to improve the temperature characteristics, the present invention adds 1.5 to 2.0% by weight of SnO2 without impairing the above characteristics.
It was added at the same time.
次に本発明の実施例について図面を参照して説
明する。 Next, embodiments of the present invention will be described with reference to the drawings.
第３表を参照すると、Mn−Znフエライトの組
成がNo.７〜No.10の試料について示されている。No.
７〜No.10の試料の主成分（Fe2O3、MnO、ZnO）
は、いずれも磁歪定数λS＝０を満足している。ま
た、第４表には、第３表のNo.７〜No.10の試料のモ
ールド前及びモールド後の磁気特性が示されてい
る。 Referring to Table 3, the compositions of Mn-Zn ferrite are shown for samples No. 7 to No. 10. No.
Main components of samples No. 7 to No. 10 (Fe 2 O 3 , MnO, ZnO)
All satisfy the magnetostriction constant λ S =0. Furthermore, Table 4 shows the magnetic properties of the samples No. 7 to No. 10 in Table 3 before and after molding.
一方、第１図には、第１表のNo.１〜No.６の試料
と第３表のNo.７〜No.10の試料について、主成分の
MnO−ZnO−Fe2O3の割合がプロツトされた三元
図が示されており、プロツトされた点の番号１〜
１０は試料No.１〜No.10にそれぞれ対応している。 On the other hand, Figure 1 shows the main components of samples No. 1 to No. 6 in Table 1 and samples No. 7 to No. 10 in Table 3.
A ternary diagram in which the proportion of MnO−ZnO−Fe 2 O 3 is plotted is shown, and the plotted points number 1 to
10 corresponds to samples No. 1 to No. 10, respectively.
No.１〜No.10の試料のうち、上述した目標値を、
すべての項目（μ、Ｑ、B10、Br、Hc）におい
て満足するものは、第２表及び第４表から明らか
なように、No.８とNo.９の試料であつた。なお、主
成分のMnO−ZnO−Fe2O3については、第１図に
おいてＡの範囲内にあれば、上述した目標値を満
足することが確認された。 Among the samples No. 1 to No. 10, the target values mentioned above are
As is clear from Tables 2 and 4, samples No. 8 and No. 9 were satisfactory in all items (μ, Q, B 10 , Br, Hc). It was confirmed that the main component MnO-ZnO-Fe 2 O 3 satisfies the above-mentioned target value if it is within the range A in FIG.
上述のように、No.８とNo.９の試料や第１図のＡ
の範囲内にあるものは、上述した目標値を満足す
るものの、透磁率μの温度係数T〓が２×10-6〜
５×10-6（１／℃）と大きい。そこで、温度係数
T〓を小さくするために、SnO2を添加する。第５
表はNo.８の試料の組成に、更にSnO2を同時に添
加したMn−Znフエライト（No.11〜No.14）のモー
ルド前のμとＱの値を示している。No.11の試料は
0.5重量％、No.12の試料は1.0重量％、No.13の試料
は1.5重量％、No.14の試料は2.0重量％、SnO2を含
有している、本発明に従うNo.13やNo.14のように、
SnO2を1.5〜2.0重量％含有すると、温度勾配が改
善され、0.8×10-6（１／℃）以下の温度係数が得
られることが確認された。 As mentioned above, samples No. 8 and No. 9 and A in Fig.
Those within the range satisfy the above-mentioned target value, but the temperature coefficient T〓 of magnetic permeability μ is 2 × 10 -6 ~
It is large at 5×10 -6 (1/℃). Therefore, the temperature coefficient
SnO 2 is added to reduce T〓. Fifth
The table shows the μ and Q values before molding of Mn-Zn ferrites (No. 11 to No. 14) in which SnO 2 was added simultaneously to the composition of sample No. 8. Sample No.11 is
No. 13 or No. 2 according to the present invention contains SnO2 of 0.5 wt%, No. 12 sample 1.0 wt%, No. 13 sample 1.5 wt%, No. 14 sample 2.0 wt%. Like .14,
It was confirmed that when SnO 2 was contained in an amount of 1.5 to 2.0% by weight, the temperature gradient was improved and a temperature coefficient of 0.8×10 −6 (1/° C.) or less was obtained.
第６表を参照すると、第２図のダブルギヤツプ
の磁気消去ヘツドを構成した場合のコアとコア
の材料の組み合せと、それらに対応するヘツド
Ａ〜Ｆの特性（インピーダンスＺ，Ｑ、末梢率、
高域減磁）が示されている。コアはセンターコ
アで、コアはＣ型コアで材料のNo.は前述した試
料No.と同一である。本発明に従うNo.13の試料をコ
ア及びコアとして用いた消去ヘツドＦは、Ｑ
が高く、消去率60dB以上であり、高域減磁が
0.7dBと極めて小さく、優れている。 Referring to Table 6, we can see the combinations of cores and core materials when constructing the double-gap magnetic erasing head shown in Fig. 2, and the corresponding characteristics of heads A to F (impedances Z, Q, peripheral ratio,
High-frequency demagnetization) is shown. The core is a center core, the core is a C-shaped core, and the material number is the same as the sample number described above. The erasing head F using sample No. 13 according to the present invention as the core is Q
is high, the erasure rate is over 60dB, and the high-frequency demagnetization is
It is extremely low at 0.7dB, which is excellent.
第７表を参照すると、本発明の他の実施例（No.
15〜No.18）の組成が示されている。また、第８表
には、第７表の各実施例のモールド前及びモール
ド後の諸特性が示されている。これら本発明に従
うNo.15〜No.18の試料においても、SiO2が0.015〜
0.022重量％、CaOが0.02〜0.05重量％、SnO2が
1.5〜2.0重量％含まれていることにより、第２表
の最下部に示した目標値がすべての項目について
満足され、しかも透磁率μの温度係数T〓を±0.8
×10-6（１／℃）以下にすることができた。 Referring to Table 7, other embodiments of the present invention (No.
15 to No. 18) are shown. Further, Table 8 shows various characteristics before and after molding of each example in Table 7. Also in these samples No. 15 to No. 18 according to the present invention, SiO 2 was 0.015 to 0.015.
0.022 wt%, CaO 0.02-0.05 wt%, SnO2
By containing 1.5 to 2.0% by weight, the target values shown at the bottom of Table 2 are satisfied for all items, and the temperature coefficient T of magnetic permeability μ is ±0.8.
We were able to reduce the temperature to below ×10 -6 (1/℃).
以上説明したように、本発明によれば、コアを
ヘツドに組み込む際の樹脂モールド処理による諸
特性の劣化が小さく、しかも温度特性の良い消去
ヘツドコア用Mn−Znフエライトが得られる。 As explained above, according to the present invention, it is possible to obtain Mn--Zn ferrite for an erase head core that has little deterioration in properties due to resin molding when the core is assembled into a head and has good temperature characteristics.
なお、本発明のフエライトは、μが小さいた
め、記録又は再生ヘツドコア用としては適してい
ない。 Note that the ferrite of the present invention has a small μ, so it is not suitable for use in recording or reproducing head cores.
第１図は本発明の主成分（Fe2O3、MnO、
ZnO）の組成範囲を示した図、第２図はダブルギ
ヤツプの消去ヘツドを示した図である。
Figure 1 shows the main components of the present invention (Fe 2 O 3 , MnO,
FIG. 2 is a diagram showing a double-gap erase head.
【表】【table】
【表】【table】
【表】【table】
【表】【table】
【表】【table】
【表】【table】
【表】【table】
【表】【table】
Claims (1)
〜52.2モル％、MnOを31.6〜35.4モル％、ZnOを
12.8〜16.2モル％、SiO2を0.015〜0.022重量％、
CaOを0.02〜0.05重量％、SnO2を1.5〜2.0重量％
含んだ組成を有することを特徴とする消去ヘツド
コア用Mn−Znフエライト。1 In Mn-Zn ferrite, Fe 2 O 3 is 51.8
~52.2 mol%, MnO 31.6~35.4 mol%, ZnO
12.8-16.2 mol%, SiO2 0.015-0.022 wt%,
0.02-0.05 wt% CaO, 1.5-2.0 wt% SnO2
A Mn-Zn ferrite for an erase head core, characterized in that it has a composition containing Mn-Zn ferrite.