JPH0448621B2 - - Google Patents
Info
- Publication number
- JPH0448621B2 JPH0448621B2 JP59106531A JP10653184A JPH0448621B2 JP H0448621 B2 JPH0448621 B2 JP H0448621B2 JP 59106531 A JP59106531 A JP 59106531A JP 10653184 A JP10653184 A JP 10653184A JP H0448621 B2 JPH0448621 B2 JP H0448621B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- lid
- polyethylene terephthalate
- composite film
- heat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
ポリスチレンやポリプロピレンからなる容器に
蓋として複合フイルムを熱封着することが行われ
ているが、ポリエチレンテレフタレートからなる
容器や板紙にポリエチレンテレフタレートを押出
コーチングした後にプレス加工した容器に対して
熱封着性があり、且つ易開封性を備えた蓋を形成
することができる複合フイルムは未だ提供されて
いない。
本発明は、蓋用複合フイルムに於て、容器に熱
封着される第１層と、第１層と共押出積層された
第２層とを有し、第１層が膜厚0.5〜10μのポリエ
チレンテレフタレート層であり、第２層がエチレ
ン含有率が40〜90モル％、鹸化度が90モル％未満
のエチレン−酢酸ビニル共重合体部分鹸化物層で
あることを特徴とする内面がポリエチレンテレフ
タレートによつて形成された容器に対して熱封着
性があり、且つ易開封性を備えた蓋を形成するこ
とができる蓋用複合フイルムに関するものであ
る。
本発明に係わる蓋用複合フイルムは、ポリエチ
レンテレフタレートからなる容器や板紙にポリエ
チレンテレフタレートを押出コーチングした後に
プレス加工した容器に対して熱封着性があり、且
つ易開封性を備えた蓋を形成することができる。
以下、図面に従つて本発明を説明する。
第１図は本発明に係わる蓋用複合フイルムより
なる蓋を容器に熱封着した状態を示した断面図並
びに第２図は本発明に係わる蓋用複合フイルムよ
りなる蓋を開封した状態を示した断面図である。
第１層１は膜厚が0.5〜10μのポリエチレンテレ
フタレート層である。
第１層１と共押出積層された第２層２は、エチ
レン−酢酸ビニル共重合体部分鹸化物層である。
エチレン−酢酸ビニル共重合体部分鹸化物として
はエチレン含有率が40〜90モル％、鹸化度が90モ
ル％未満のものを使用する。第２層２には必要に
応じて低密度ポリエチレン、高密度ポリエチレ
ン、ポリプロピレン、エチレン−酢酸ビニル共重
合体の如きポリオレフイン樹脂を80重量％程度ま
で混合することができる。第２層２の膜厚は一般
に２〜60μとすることが好ましい。
本発明に係わる蓋用複合フイルムに於ては、必
要に応じて第２層２上に第３層３としてイソシア
ネート系接着剤を使用して二軸延伸ポリエチレン
テレフタレートフイルム、二軸延伸ポリプロピレ
ンフイルム、セロフアン、アルミニウム箔、紙等
の基材を貼り合せてもよいし、第１層１及び第２
層２とともに低密度ポリエチレン、高密度ポリエ
チレン、ポリプロピレン、ナイロンの如き熱可塑
性樹脂を共押出してもよいし、或いは第２層２上
に低密度ポリエチレンを溶融積層した上に第４層
としてイソシアネート系接着剤を使用して前記基
材を貼り合せてもよい。
蓋用複合フイルムの膜厚は一般に40〜100μと
することが好ましい。
蓋用複合フイルムを熱封着することができる容
器４としては、真空成形、圧空成形等によりポリ
エチレンテレフタレートシートから成形された開
口部周縁にフランジを有するトレー、射出成形等
によりポリエチレンテレフタレートによつて成形
された開口部周縁にフランジを有するカツプ等の
容器並びに板紙をポリエチレンテレフタレートを
押出コーチングするか、ポリエチレンテフタレー
トシートを接着剤等により貼り合せ、ポリエチレ
ンテレフタレート面を内面として成形された開口
部周縁にフランジを有するトレー等の容器の挙げ
ることができる。
蓋用複合フイルムを蓋として容器４に熱封着す
るには、蓋用複合フイルムの第１層１を容器４の
フランジ５と接触させ、圧力１〜３Kg／cm2、温度
140〜220℃、時間0.2〜２秒間の条件で熱封着す
ればよい。
容器４に熱封着された蓋を上方に引つ張ると、
第２図に示すように熱封着区域６の境界に於て第
１層１が破断するとともに熱封着区域６に於て第
１層１と第２層２とが層間剥離することにより、
極めて容易に開封することができる。
本発明に係わる蓋用複合フイルムは、耐油性が
優れ、冷凍保存および流通中に必要な熱封着強度
を有するとともに冷凍保存から取出し直後の低温
時や常温時及び電子レンジ、オーブンレンジでの
加熱調理後も開封が容易な蓋を形成し得るため、
グラタン、ピザ等の加熱調理食品を収納した容器
に対する蓋として好適に使用することができる。
次に、実施例により本発明を具体的に説明す
る。
実施例 １
ポリエチレンテレフタレート（密度1.33g／cc、
固有粘度0.7、融点233℃）と、エチレン−酢酸ビ
ニル共重合体部分鹸化物（エチレン含有率89モル
％、鹸化度36モル％、密度0.94g／cc、メルトイ
ンデツクス15、融点98℃）とエチレン−酢酸ビニ
ル共重合体（密度0.94g／cc、メルトインデツク
ス５、融点87℃）との重量比で１：１の混合物と
を共押出してポリエチレンテレフタレートより成
る膜厚2μの第１層１と、エチレン−酢酸ビニル
共重合体部分鹸化物を含む膜厚35μの第２層２と
を有する共押出二層フイルムを製造する。共押出
二層フイルムの第２層２の面をコロナ放電処理し
た後、イソシアネート系接着剤を使用して膜厚
12μの二軸延伸ポリエチレンテレフタレートフイ
ルム３を貼り合せ、蓋用複合フイルムとする。
板紙にポリエチレンテレフタレートを押出コー
チングし、ポリエチレンテレフタレート面を内面
として開口部周縁に幅１cmのフランジ５を有する
角型トレー４を成形する。
角型トレー４内にグラタン180gを入れ、蓋用
複合フイルムの第１層１を角型トレー４のフラン
ジ５と接触させ、温度160℃、180℃または200℃、
圧力２Kg／cm2、時間１秒間の条件で熱封着する。
グラタンを入れた角型トレー４を−23℃に冷凍
して５日間保管した後並びに−23℃に冷凍して５
日間保管してから電子レンジで15分間加熱後に、
蓋を開封したところ、蓋片の残りや破れもなく、
第２図に示すようにきれいに開封することができ
た。また、温度23℃、引張速度300mm／分、サン
プル幅15mm、180°剥離の条件下での剥離強度は、
次の通りであり、いずれも易開封性を有してい
た。
Composite films are heat-sealed as lids to containers made of polystyrene or polypropylene, but the heat-sealability is not good for containers made of polyethylene terephthalate or containers made of paperboard that has been extrusion coated with polyethylene terephthalate and then pressed. However, a composite film that can form a lid that is easy to open has not yet been provided. The present invention provides a composite film for lids, which has a first layer that is heat-sealed to a container, and a second layer that is laminated by coextrusion with the first layer, and the first layer has a film thickness of 0.5 to 10 μm. The inner surface is a polyethylene terephthalate layer, and the second layer is a partially saponified ethylene-vinyl acetate copolymer layer with an ethylene content of 40 to 90 mol% and a saponification degree of less than 90 mol%. The present invention relates to a composite film for lids that can be heat-sealed to containers made of terephthalate and can form lids that are easy to open. The composite film for lids according to the present invention forms lids that are heat-sealable and easy to open for containers made of polyethylene terephthalate or containers made by extrusion coating polyethylene terephthalate on paperboard and then press processing. be able to. The present invention will be explained below with reference to the drawings. FIG. 1 is a sectional view showing a state in which a lid made of a composite film for lids according to the present invention is heat-sealed to a container, and FIG. 2 shows a state in which the lid made from a composite film for lids according to the present invention is opened. FIG. The first layer 1 is a polyethylene terephthalate layer having a thickness of 0.5 to 10 μm. The second layer 2 coextruded with the first layer 1 is a partially saponified ethylene-vinyl acetate copolymer layer.
The partially saponified ethylene-vinyl acetate copolymer used has an ethylene content of 40 to 90 mol% and a degree of saponification of less than 90 mol%. In the second layer 2, up to about 80% by weight of a polyolefin resin such as low density polyethylene, high density polyethylene, polypropylene, or ethylene-vinyl acetate copolymer can be mixed, if necessary. The thickness of the second layer 2 is generally preferably 2 to 60 microns. In the composite film for lids according to the present invention, if necessary, an isocyanate adhesive is used as the third layer 3 on the second layer 2 to form a biaxially oriented polyethylene terephthalate film, a biaxially oriented polypropylene film, or a cellophane film. , aluminum foil, paper, etc., or the first layer 1 and the second layer
A thermoplastic resin such as low-density polyethylene, high-density polyethylene, polypropylene, or nylon may be coextruded together with layer 2, or low-density polyethylene may be melt laminated on the second layer 2 and then an isocyanate-based adhesive is applied as a fourth layer. The base materials may be bonded together using an adhesive. The thickness of the composite film for lids is generally preferably 40 to 100μ. The container 4 to which the composite film for the lid can be heat-sealed may be a tray having a flange around the opening formed from a polyethylene terephthalate sheet by vacuum forming, pressure forming, etc., or a tray formed from polyethylene terephthalate by injection molding, etc. Containers such as cups and paperboard that have a flange around the opening are extrusion coated with polyethylene terephthalate, or polyethylene terephthalate sheets are bonded together with an adhesive, etc., and a flange is formed around the opening that has been formed with the polyethylene terephthalate side as the inner surface. Examples include containers such as trays with In order to heat seal the lid composite film to the container 4 as a lid, the first layer 1 of the lid composite film is brought into contact with the flange 5 of the container 4, and the pressure is 1 to 3 kg/cm 2 and the temperature is applied.
Heat sealing may be performed at 140 to 220°C for 0.2 to 2 seconds. When the lid heat-sealed to container 4 is pulled upward,
As shown in FIG. 2, the first layer 1 ruptures at the boundary of the heat-sealed area 6, and the first layer 1 and the second layer 2 delaminate in the heat-sealed area 6.
Can be opened extremely easily. The composite film for lids according to the present invention has excellent oil resistance, has the necessary heat sealing strength during frozen storage and distribution, and can be heated at low temperatures immediately after being removed from frozen storage, at room temperature, in a microwave oven, or in an oven range. Because it can form a lid that is easy to open even after cooking,
It can be suitably used as a lid for a container containing cooked foods such as gratin and pizza. Next, the present invention will be specifically explained with reference to Examples. Example 1 Polyethylene terephthalate (density 1.33 g/cc,
(intrinsic viscosity 0.7, melting point 233°C) and partially saponified ethylene-vinyl acetate copolymer (ethylene content 89 mol%, degree of saponification 36 mol%, density 0.94 g/cc, melt index 15, melting point 98°C) A first layer 1 with a thickness of 2 μm made of polyethylene terephthalate was coextruded with a 1:1 mixture by weight of an ethylene-vinyl acetate copolymer (density 0.94 g/cc, melt index 5, melting point 87°C). A coextruded two-layer film is produced having a second layer 2 having a thickness of 35 μm and containing a partially saponified ethylene-vinyl acetate copolymer. After corona discharge treatment is applied to the surface of the second layer 2 of the coextruded two-layer film, the film thickness is adjusted using an isocyanate adhesive.
A 12μ biaxially stretched polyethylene terephthalate film 3 is laminated to form a composite film for a lid. A paperboard is extrusion coated with polyethylene terephthalate, and a rectangular tray 4 having a 1 cm wide flange 5 around the opening with the polyethylene terephthalate side as the inner surface is formed. 180 g of gratin was placed in the square tray 4, the first layer 1 of the composite film for lid was brought into contact with the flange 5 of the square tray 4, and the temperature was 160°C, 180°C or 200°C.
Heat sealing is performed under the conditions of a pressure of 2 kg/cm 2 and a time of 1 second. After freezing the square tray 4 containing gratin at -23℃ and storing it for 5 days, and after freezing it at -23℃ and storing it for 5 days.
After storing it for a day and heating it in the microwave for 15 minutes,
When I opened the lid, there were no pieces left or torn.
As shown in Figure 2, the package could be opened cleanly. In addition, the peel strength under the conditions of temperature 23℃, tensile speed 300mm/min, sample width 15mm, and 180° peeling is as follows.
They were as follows, and all had easy-to-open properties.
【表】
実施例 ２
ポリエチレンテレフタレート（実施例１と同じ
もの）と、エチレン−酢酸ビニル共重合体部分鹸
化物（実施例１と同じもの）と低密度ポリエチレ
ン（密度0.920g／cc、メルトインデツクス7.0、
融点105℃）との重量比で３：２の混合物と、低
密度ポリエチレン（密度0.920g／cc、メルトイン
デツクス7.0、融点105℃）とを共押出してポリエ
チレンテレフタレートより成る膜厚2μの第１層
１と、エチレン−酢酸ビニル共重合体部分鹸化物
を含む膜厚10μの第２層２と、低密度ポリエチレ
ンより成る膜厚15μの第３層３とを有する共押出
三層フイルムを製造する。共押出三層フイルムの
第３層３の面をコロナ放電処理した後、イソシア
ネート系接着剤を使用して膜厚12μの二軸延伸ポ
リエチレンテレフタレートフイルムを貼り合せ、
蓋用複合フイルムとする。
以下、実施例１と同様に、角型トレー４を成形
し、角型トレー４内にグラタンを入れて得られた
蓋用複合フイルムを熱封着させ、冷凍して保管後
並びにさらに電子レンジで加熱後に、蓋を開封し
たところ、蓋片の残りや破れもなく、第２図に示
すようにきれいに開封することができた。また、
その剥離強度は、次の通りであり、いずれも易開
封性を有していた。[Table] Example 2 Polyethylene terephthalate (same as Example 1), partially saponified ethylene-vinyl acetate copolymer (same as Example 1), and low density polyethylene (density 0.920 g/cc, melt index 7.0,
A 2μ thick first film made of polyethylene terephthalate was prepared by coextruding a mixture of 3:2 by weight (melting point 105°C) and low density polyethylene (density 0.920g/cc, melt index 7.0, melting point 105°C). A coextruded three-layer film is produced having a layer 1, a second layer 2 with a thickness of 10 μm containing a partially saponified ethylene-vinyl acetate copolymer, and a third layer 3 with a thickness of 15 μm made of low-density polyethylene. . After corona discharge treatment was applied to the surface of the third layer 3 of the coextruded three-layer film, a biaxially stretched polyethylene terephthalate film with a thickness of 12 μm was attached using an isocyanate adhesive.
Composite film for lid. Hereinafter, in the same manner as in Example 1, a square tray 4 is formed, gratin is placed inside the square tray 4, the obtained composite film for lid is heat sealed, and after being frozen and stored, it is further heated in a microwave oven. When the lid was opened after heating, there were no remaining lid pieces or tears, and the lid could be opened cleanly as shown in FIG. 2. Also,
The peel strength was as follows, and all had easy-to-open properties.
第１図は本発明に係わる蓋用複合フイルムより
なる蓋を容器に熱封着した状態を示した断面図並
びに第２図は本発明に係わる蓋用複合フイルムよ
りなる蓋を開封した状態を示した断面図である。
１……第１層、２……第２層。
FIG. 1 is a sectional view showing a state in which a lid made of a composite film for lids according to the present invention is heat-sealed to a container, and FIG. 2 shows a state in which the lid made from a composite film for lids according to the present invention is opened. FIG. 1...First layer, 2...Second layer.
Claims (1)
る第１層と、第１層と共押出積層された第２層と
を有し、第１層が膜厚0.5〜10μのポリエチレンテ
レフタレート層であり、第２層がエチレン含有率
が40〜90モル％、鹸化度が90モル％未満のエチレ
ン−酢酸ビニル共重合体部分鹸化物層であること
を特徴とする内面がポリエチレンテレフタレート
によつて形成された容器に対して熱封着性があ
り、且つ易開封性を備えた蓋を形成することがで
きる蓋用複合フイルム。1 A composite film for lids has a first layer that is heat-sealed to the container and a second layer that is coextruded and laminated with the first layer, and the first layer is made of polyethylene terephthalate with a film thickness of 0.5 to 10 μm. The inner surface is made of polyethylene terephthalate, and the second layer is a partially saponified ethylene-vinyl acetate copolymer layer with an ethylene content of 40 to 90 mol% and a saponification degree of less than 90 mol%. A composite film for a lid that can be heat-sealed to a container formed with a lid and can form a lid that is easy to open.