JPH0517738A - Mortar slurry for coke oven inlet seal - Google Patents
Mortar slurry for coke oven inlet sealInfo
- Publication number
- JPH0517738A JPH0517738A JP19508791A JP19508791A JPH0517738A JP H0517738 A JPH0517738 A JP H0517738A JP 19508791 A JP19508791 A JP 19508791A JP 19508791 A JP19508791 A JP 19508791A JP H0517738 A JPH0517738 A JP H0517738A
- Authority
- JP
- Japan
- Prior art keywords
- water
- mortar
- parts
- slurry
- chemical
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】
【構成】 本発明のモルタルスラリーは、モルタル１０
０部と、モンモリナイトを主成分とする鉱物、ベントナ
イト、粘土類、水ガラスから選ばれる一種以上の耐熱性
バインダー０．５〜１０．０部と、化１、化２から選ば
れる一種以上の水溶性分散剤０．０１部以上と、メチル
セルローズ、ヒドロキシメチルセルローズ、カルボキシ
メチルセルローズ、ポリビニルアルコール、低分子ポリ
アクリルアマイド、ポリアクリル酸塩、デンプン類、ガ
ム類から選ばれる一種以上の水溶性増粘剤０．０５〜
１．０部とを含有してなる。
【化１】
【化２】
【効果】 コークス炉の石炭装入口における乾留ガスの
漏洩を確実に防止し、しかもその分散安定性が優れてい
るので、スラリー供給装置等においてスケールを発生し
てラインを閉塞することがない。(57) [Summary] [Structure] The mortar slurry of the present invention comprises mortar 10
0 parts, 0.5-10.0 parts of one or more heat-resistant binders selected from minerals containing montmorillonite, bentonite, clays, and water glass, and one or more water-soluble compounds selected from chemical formulas 1 and 2 0.01 parts or more of a water-soluble dispersant and one or more water-soluble thickening agents selected from methyl cellulose, hydroxymethyl cellulose, carboxymethyl cellulose, polyvinyl alcohol, low molecular weight polyacrylic amide, polyacrylic acid salt, starches and gums Agent 0.05 ~
And 1.0 part. [Chemical 1] [Chemical 2] [Effect] Since the dry distillation gas is surely prevented from leaking at the coal charging port of the coke oven and the dispersion stability thereof is excellent, the scale is not generated in the slurry supply device or the like to block the line.
Description
【０００１】[0001]
【産業上の利用分野】本発明は、コークス炉の石炭装入
口におけるガスの漏洩を確実に防止し、特にその分散安
定性が良好であるコークス炉装入口シール用モルタルス
ラリーに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a mortar slurry for sealing the inlet of a coke oven which surely prevents gas leakage at the coal inlet of the coke oven and has good dispersion stability.
【０００２】[0002]
【従来の技術】コークス炉の石炭装入口は、乾留中、装
入蓋により閉塞されているが、この装入蓋と鉢との隙間
からは、乾留生成ガスが漏洩するため、作業環境の悪化
を引き起こすと共に、公害という見地からも問題とな
る。通常、上記した乾留生成ガスの漏洩を防止するため
には、ガスの漏洩部分、即ち、装入蓋と鉢との隙間に以
下のような特性を有するモルタルを主成分とする耐熱性
のシール材が用いられている。 懸濁性が良好で、沈殿しにくい。 締め切り後、固着することなく、残渣が固形化しな
い。 装入蓋にシールした後、モルタルが収縮しない。 品質 材質：粘土質（ＳｉＯ2 …８５％，Ａｌ2 Ｏ3 …１０
％） 状態：粉末状 耐火度：ＳＫ２６ 嵩比重：１．３ このような耐熱性シール材としては、概してモルタル：
水の重量比が１：１〜１：３のモルタルスラリーが使用
され、このモルタルスラリーをスラリー貯留槽及びスラ
リー輸送パイプライン等からなるスラリー供給装置を経
て前記した装入蓋と鉢との隙間に注入するのである。2. Description of the Related Art The coal charging port of a coke oven is closed by a charging lid during carbonization, but the gas produced by carbonization leaks from the gap between the charging lid and the bowl, which deteriorates the working environment. In addition to causing the pollution, it becomes a problem from the viewpoint of pollution. Usually, in order to prevent leakage of the above-mentioned gas produced by carbonization, a heat-resistant sealing material containing mortar as a main component having the following characteristics in the gas leakage portion, that is, in the gap between the charging lid and the pot. Is used. Has good suspendability and does not easily precipitate. After the deadline, the residue does not solidify without sticking. Mortar does not shrink after sealing to charging lid. Quality Material: Clay (SiO 2 … 85%, Al 2 O 3 … 10
%) State: powder state Fire resistance: SK26 Bulk specific gravity: 1.3 Generally, such a heat-resistant sealing material is mortar:
A mortar slurry having a weight ratio of water of 1: 1 to 1: 3 is used, and the mortar slurry is passed through a slurry supply device including a slurry storage tank and a slurry transportation pipeline to the gap between the charging lid and the pot. Inject.
【０００３】[0003]
【発明が解決しようとする課題】しかしながら、上記し
た従来のモルタルスラリーは、その分散安定性が悪く、
３０〜６０分程度で固液分離してしまうので、シール性
にムラを生じたり、スラリー貯留槽やスラリー輸送パイ
プライン等にスケールを生じてラインを閉塞し、スラリ
ー供給装置を運転不能にすることがあった。したがっ
て、装入蓋と鉢との隙間を確実にシールすることによ
り、ガスの漏洩を防止することができ、且つその分散安
定性が良好で、上記したような問題を生ずるおそれのな
いモルタルスラリーが嘱望されていた。However, the above-mentioned conventional mortar slurry has poor dispersion stability,
Since solid-liquid separation occurs in about 30 to 60 minutes, uneven sealing properties may occur, or scale may be generated in the slurry storage tank or slurry transport pipeline to block the line, rendering the slurry supply device inoperable. was there. Therefore, by reliably sealing the gap between the charging lid and the pot, it is possible to prevent the leakage of gas, and its dispersion stability is good, and a mortar slurry that does not cause the problems described above is obtained. It had been hoped for.
【０００４】[0004]
【課題を解決するための手段】本発明は、上記に鑑み提
案されたもので、（イ）モルタル１００部と、（ロ）モ
ンモリナイトを主成分とする鉱物、ベントナイト、粘土
類、水ガラスから選ばれる一種以上の耐熱性バインダー
０．５〜１０．０部と、（ハ）化３、化４から選ばれる
一種以上の水溶性分散剤０．０１部以上と、（ニ）メチ
ルセルローズ、ヒドロキシメチルセルローズ、カルボキ
シメチルセルローズ、ポリビニルアルコール、低分子ポ
リアクリルアマイド、ポリアクリル酸塩、デンプン類、
ガム類から選ばれる一種以上の水溶性増粘剤、０．０５
〜１．０部とを含有してなることを特徴とするコークス
炉装入口シール用モルタルスラリーに関するものであ
る。The present invention has been proposed in view of the above, and is selected from (a) 100 parts of mortar and (b) minerals containing montmorillonite as a main component, bentonite, clays, and water glass. 0.5 to 10.0 parts of one or more heat-resistant binders, 0.01 part or more of one or more water-soluble dispersants selected from (C) 3 and 4 and (D) methyl cellulose, hydroxymethyl Cellulose, carboxymethyl cellulose, polyvinyl alcohol, low molecular weight polyacrylic amide, polyacrylic acid salt, starches,
One or more water-soluble thickeners selected from gums, 0.05
The present invention relates to a mortar slurry for sealing coke oven charging, characterized in that the mortar slurry contains 1.0 to 1.0 part.
【化３】 [Chemical 3]
【化４】 [Chemical 4]
【０００５】上記した本発明に使用する（イ）成分であ
るモルタルとしては、通常使用されるモルタルを適用す
ることができ、前記した〜の特性を有するものを使
用しても良い。As the mortar which is the component (a) used in the present invention described above, a commonly used mortar can be applied, and those having the above-mentioned properties (1) to (3) may be used.
【０００６】また、本発明に使用する（ロ）成分である
耐熱性バインダーとしては、モンモリナイトを主成分と
する鉱物、ベントナイト、粘土類、水ガラス等を使用す
ることができ、これらの二種以上を混合して用いるよう
にしても良い。この耐熱性バインダーは、モルタル１０
０部に対し、少なくとも０．５部添加しないと接着効果
を付与することができず、一方添加量を増やすと耐熱性
バインダー成分が凝集しあって団子状となる傾向がみら
れ、１０．０部以上になると作業性に悪影響を与えるな
ど不都合を生じるようになる。Further, as the heat-resistant binder which is the component (b) used in the present invention, minerals containing montmorillonite as a main component, bentonite, clays, water glass and the like can be used, and two or more kinds of them can be used. You may make it mix and use. This heat resistant binder is mortar 10
Adhesive effect cannot be imparted unless at least 0.5 part is added to 0 part, whereas when the addition amount is increased, the heat-resistant binder components tend to aggregate to form a dumpling. If it is more than the number of copies, inconvenience will occur such that workability is adversely affected.
【０００７】さらに、（ハ）成分である水溶性分散剤と
しては、前記した化３で示されるアルキルフェノールス
ルフォン酸ソーダ、アルキルフェノール縮合物のスルフ
ォン酸ソーダ、リグニンスルフォン酸ソーダ、前記した
化４で示されるマレイン酸ソーダ低重合物、アクリル酸
ソーダ低重合物等を使用することができ、これらの二種
以上を混合して用いるようにしても良い。この水溶性分
散剤は、モルタル１００部に対し、少なくとも０．０１
部以上添加しないと分散効果を付与することができず、
本発明のモルタルスラリーは均一でなくなり、成分の一
部が分離沈降する。しかし、添加量が多くなり過ぎても
分散性は向上することなく、１．０部程度を越えると、
組成物の性状には特別悪影響をもたらさないが、経済的
に無駄となる。Further, as the water-soluble dispersant which is the component (c), the alkylphenol sulfonic acid soda represented by the above chemical formula 3, the sodium sulfonate of the alkylphenol condensate, the lignin sulfonic acid soda, and the above chemical formula 4 are shown. Sodium maleate low-polymerization products, sodium acrylate low-polymerization products and the like can be used, and two or more kinds of these may be mixed and used. This water-soluble dispersant is at least 0.01 per 100 parts of mortar.
The dispersion effect cannot be imparted unless more than one part is added,
The mortar slurry of the present invention becomes non-uniform and some of the components separate and settle. However, even if the added amount becomes too large, the dispersibility does not improve, and if it exceeds about 1.0 part,
It has no particular adverse effect on the properties of the composition, but is economically wasteful.
【０００８】また、（ニ）成分である水溶性増粘剤とし
ては、メチルセルローズ、ヒドロキシメチルセルロー
ズ、カルボキシメチルセルローズ、ポリビニルアルコー
ル、低分子ポリアクリルアマイド、ポリアクリル酸塩、
デンプン類、ガム類等を使用することができ、これらの
二種以上を混合して用いるようにしても良い。この水溶
性増粘剤は、本発明のモルタルスラリーをコークス炉装
入口シール用として使用する際に、作業に適した粘性
（５００〜５０００ｃｐ）とするために添加するもので
あり、その添加量はモルタル１００部に対し、０．０５
〜１．０部が良好であることを見出したものである。As the water-soluble thickener which is the component (d), methylcellulose, hydroxymethylcellulose, carboxymethylcellulose, polyvinyl alcohol, low molecular weight polyacrylic amide, polyacrylic acid salt,
Starches, gums and the like can be used, and two or more kinds of them may be mixed and used. This water-soluble thickener is added in order to make the viscosity (500 to 5000 cp) suitable for work when using the mortar slurry of the present invention for sealing the coke oven charging, and the addition amount thereof is 0.05 to 100 parts of mortar
It was found that a content of 1.0 part is good.
【０００９】本発明のモルタルスラリーは、前記（イ）
〜（ニ）成分の各所定量を水に混合し、攪拌することに
より作製することができる。この水は、本発明のモルタ
ルスラリーが前記したようなシール作業に適した粘性
（５００〜５０００ｃｐ）となると共に、実用性の面に
おいて、運搬性、乾燥性、シール効果に悪影響にならな
い範囲で添加するものであり、限定するものではない
が、モルタル１００部に対し、約１００〜２００部の範
囲が適当である。The mortar slurry of the present invention has the above (a)
It can be prepared by mixing each predetermined amount of the components (d) to (d) with water and stirring. This water is added in such a range that the mortar slurry of the present invention has a viscosity (500 to 5000 cp) suitable for the sealing operation as described above and, in terms of practicality, does not adversely affect the transportability, the drying property and the sealing effect. However, the range of about 100 to 200 parts is suitable for 100 parts of the mortar, although not limited thereto.
【００１０】尚、各成分の混合及び攪拌方法は、特に限
定するものでなく、また、均一で安定なスラリーを維持
できる範囲であれば、上記した各成分以外にも各種の添
加剤等を加えるようにしても良い。The method of mixing and stirring each component is not particularly limited, and various additives other than the above-mentioned components may be added as long as a uniform and stable slurry can be maintained. You may do it.
【００１１】上記した本発明のモルタルスラリーは、極
めて分散安定性に優れ、長時間に亙って沈殿分離するこ
とがなく、スケールを発生しないので、例えばピストン
型、ボールバルブ型、ピンチバルブ型等のいずれのスラ
リー供給装置を用いてもそのラインを閉塞して運転不能
とすることがなく、装入蓋と鉢との隙間に注入すること
により、確実に乾留生成ガスの漏洩を防止することがで
き、また、シール性のムラを生ずることがないので、確
実に乾留生成ガスの漏洩を防止することができる。The above-mentioned mortar slurry of the present invention has extremely excellent dispersion stability, does not precipitate and separate over a long period of time, and does not generate scale. Therefore, for example, piston type, ball valve type, pinch valve type, etc. No matter which slurry supply device is used, the line will not be blocked and operation will not be possible, and by injecting into the gap between the charging lid and the pot, it is possible to reliably prevent leakage of the carbonization product gas. In addition, since the sealing property is not unevenly generated, it is possible to reliably prevent the dry distillation product gas from leaking.
【００１２】[0012]
【実施例】以下に、本発明の実施例を示す。 実施例１〜３，比較例１〜２ 表１に示す配合の組成物を混合攪拌（１０００ｐｐｍ）
し、それぞれ実施例１〜３，比較例１〜２のモルタルス
ラリーを作製した。EXAMPLES Examples of the present invention will be shown below. Examples 1 to 3 and Comparative Examples 1 to 2 Mixing and stirring compositions of the formulations shown in Table 1 (1000 ppm)
Then, the mortar slurries of Examples 1 to 3 and Comparative Examples 1 and 2 were produced.
【００１３】[0013]
【表１】 [Table 1]
【００１４】分離試験 前記した実施例３種及び比較例２種のモルタルスラリー
を１０００ｌのタンクに投入した後、各時間における上
澄み分離液（モルタル懸濁物の量０．１％以下の水）の
水量（ｌ）を測定し、その結果を表２に示した。Separation Test After the mortar slurries of Example 3 and Comparative Example 2 described above were put into a 1000 l tank, the supernatant separated liquid (water with an amount of mortar suspension of 0.1% or less) at each time was added. The amount of water (l) was measured, and the results are shown in Table 2.
【００１５】[0015]
【表２】 [Table 2]
【００１６】[0016]
【発明の効果】以上説明したように、本発明のモルタル
スラリーは、コークス炉の石炭装入口における装入蓋と
鉢との空隙に注入することにより、乾留生成ガスの漏洩
を確実に防止することができる。特に、本発明のモルタ
ルスラリーは、極めて分散安定性に優れ、シール性のム
ラを生ずることがないので、装入蓋と鉢との隙間を確実
にシールすることができる。したがって、本発明のモル
タルスラリーは、作業環境の改善という見地からも公害
防止という見地からも極めて多大な貢献をするものであ
る。As described above, the mortar slurry of the present invention is surely prevented from leaking the carbonized product gas by injecting it into the gap between the charging lid and the bowl at the coal charging port of the coke oven. You can In particular, the mortar slurry of the present invention has extremely excellent dispersion stability and does not cause uneven sealing properties, so that the gap between the charging lid and the pot can be reliably sealed. Therefore, the mortar slurry of the present invention makes an extremely great contribution from the standpoint of improving the working environment and preventing pollution.
【００１７】また、スケールを発生しないので、例えば
スラリー供給装置を用いて装入蓋と鉢との隙間に注入す
る際においても、従来のモルタルスラリーのようにスラ
リー貯留槽やスラリー輸送パイプラインを閉塞すること
なく、その運転を停止させることもない。Further, since no scale is generated, the slurry storage tank and the slurry transportation pipeline are closed as in the case of the conventional mortar slurry when pouring into the gap between the charging lid and the pot using a slurry supply device. Without stopping the operation.
【００１８】さらに、特殊な原材料や特殊な加工処理装
置を使用する必要がないので、本発明のモルタルスラリ
ーは、極めて実用的価値が高いものである。Further, since it is not necessary to use special raw materials or special processing equipment, the mortar slurry of the present invention has extremely high practical value.
Claims (1)
ト、粘土類、水ガラスから選ばれる一種以上の耐熱性バ
インダー０．５〜１０．０部と、 （ハ）化１、化２から選ばれる一種以上の水溶性分散剤
０．０１部以上と、 （ニ）メチルセルローズ、ヒドロキシメチルセルロー
ズ、カルボキシメチルセルローズ、ポリビニルアルコー
ル、低分子ポリアクリルアマイド、ポリアクリル酸塩、
デンプン類、ガム類から選ばれる一種以上の水溶性増粘
剤０．０５〜１．０部とを含有してなることを特徴とす
るコークス炉装入口シール用モルタルスラリー。 【化１】 【化２】 Claims: (A) 100 parts of mortar, and (B) 0.5 to 1 or more heat-resistant binder selected from minerals containing montmorillonite as a main component, bentonite, clays, and water glass. 10.0 parts, and (c) 0.01 part or more of one or more water-soluble dispersants selected from Chemical Formula 1 and Chemical Formula 2, (d) Methyl cellulose, hydroxymethyl cellulose, carboxymethyl cellulose, polyvinyl alcohol, low molecular weight Polyacrylic amide, polyacrylate,
A mortar slurry for coke oven inlet sealing, which comprises 0.05 to 1.0 part of one or more water-soluble thickeners selected from starches and gums. [Chemical 1] [Chemical 2]