JPH0572985A - Production of election display board - Google Patents
Production of election display boardInfo
- Publication number
- JPH0572985A JPH0572985A JP23195191A JP23195191A JPH0572985A JP H0572985 A JPH0572985 A JP H0572985A JP 23195191 A JP23195191 A JP 23195191A JP 23195191 A JP23195191 A JP 23195191A JP H0572985 A JPH0572985 A JP H0572985A
- Authority
- JP
- Japan
- Prior art keywords
- resin film
- film
- bulletin board
- election
- resistant resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、選挙の際に立候補者の
ポスターを貼付けるための選挙掲示板の製造方法に関す
るものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method of manufacturing an election bulletin board for sticking a poster of a candidate for an election.
【０００２】[0002]
【従来の技術】従来、選挙の際に立候補者のポスターを
貼付けるための選挙掲示板は、表面に防水白色塗料を塗
布して、区画された各領域に数字が付された合板を支柱
により立設したもので、通常、次に示す〜の工程に
より製造されている。 合板の表面にシルクスクリーン印刷を施すことによ
って白色のシルクスクリーンインキを１〜２回印刷し
て、耐水性のある、白色度が７０％以上の基板を形成す
る。 次に、これを乾燥した後、該基板上に立候補者の枠
取りを黒色のスクリーンインキにてシルクスクリーン印
刷する。 そして、これを乾燥した後、前記枠内に、再度、黒
色のスクリーンインキにて番号をシルクスクリーン印刷
して乾燥する。 得られた掲示板の裏面に支柱などを取り付ける。2. Description of the Related Art Conventionally, an election bulletin board for sticking posters of candidates for elections is coated with waterproof white paint on the surface, and a plywood board with numbers attached to each divided area is erected by a pillar. It is provided and is usually manufactured by the following steps (1) to (3). By applying silk screen printing on the surface of the plywood, white silk screen ink is printed once or twice to form a water resistant substrate having a whiteness of 70% or more. Next, after drying this, the frame of the candidacy is silk-screen printed on the substrate with black screen ink. Then, after this is dried, a number is silk-screen printed again with black screen ink in the frame and dried. Supports are attached to the back of the obtained bulletin board.
【０００３】[0003]
【発明が解決しようとする課題】しかし、このようにし
て製造された選挙掲示板は、シルクスクリーン印刷によ
る工程数が３〜４回と多く、その度に乾燥を行なわなけ
ればならないし、作業に手間が掛かり、しかも、白色の
シルクスクリーンインキも白色度が低く、下地の合板の
模様が表面に浮き出たりしていた。However, the election bulletin board manufactured in this way has a large number of steps of 3 to 4 by silk screen printing, and it has to be dried every time, which is troublesome for the work. In addition, the white silk screen ink had a low degree of whiteness, and the pattern of the underlying plywood was raised on the surface.
【０００４】[0004]
［発明の概要］本発明者らは、上記問題点に鑑みて鋭意
研究を重ねた結果、選挙掲示板の製造方法において、不
透明度及び白色度に優れた耐水性樹脂フィルムを予め枠
組と掲示番号をオフセットインキで同時印刷して、これ
を接着剤を介して合板に貼り合せることによって製造す
れば、印刷回数も少なく、作業に手間が掛からないとい
った利点もあり、しかも、得られた選挙掲示板は降雨に
より紙が伸びたり縮んだりせず皺も寄り難く、極めて良
好な掲示板になるとの知見に基づき本発明を完成するに
至ったものである。すなわち、本発明の選挙掲示板の製
造方法は、不透明度（ＪＩＳ−Ｐ８１３８）が９０％以
上、白色度（ＪＩＳ−Ｌ１０７４）が９０％以上の耐水
性樹脂フィルムの表面に枠組と掲示番号をオフセットイ
ンキで同時印刷し、この印刷した樹脂フィルムの印刷さ
れた反対側の面に合板を接着剤で貼り合せたことを特徴
とするものである。[Summary of the Invention] The present inventors have conducted extensive studies in view of the above problems, and as a result, in a method of manufacturing an election bulletin board, a water-resistant resin film excellent in opacity and whiteness was previously provided with a frame and a bulletin number. If offset ink is printed at the same time, and it is attached to plywood with an adhesive, it can be printed less often, and the work is labor-free. The present invention has been completed based on the finding that the paper does not stretch or shrink, and wrinkles do not easily come close to it, resulting in an extremely good bulletin board. That is, according to the method for manufacturing the election bulletin board of the present invention, the framing (JIS-P8138) is 90% or more and the whiteness (JIS-L1074) is 90% or more. Is printed at the same time, and a plywood is attached to the surface of the printed resin film opposite to the printed surface with an adhesive.
【０００５】［発明の具体的説明］ [I] 選挙掲示板 (1) 合 板 本発明の選挙掲示板の製造方法において選挙掲示板の基
板として用いられる合板としては、その強度、加工性、
入手のし易さ、コストなどの点から、一般に板厚が２〜
２４ｍｍの合板が用いられる。これら合板は立候補者の
人数が多い場合にはポスターの貼り付け面積を広げるた
めに裏面より補強用素材により連結されて使用される。[Detailed Description of the Invention] [I] Election Bulletin Board (1) Plywood The plywood used as the board of the election bulletin board in the method of manufacturing the election bulletin board of the present invention has strength, workability,
Generally, the plate thickness is 2 to 3 in terms of availability and cost.
24 mm plywood is used. When the number of candidates is large, these plywoods are used by connecting them with a reinforcing material from the back side in order to increase the area where the posters are attached.
【０００６】(2) 耐水性樹脂フィルム (a) 耐水性 上記合板の表面に貼り付けられて、立候補者のポスター
を貼付けるための選挙掲示板の表示部となる耐水性樹脂
フィルムとしては、該選挙掲示板が通常、屋外に掲示さ
れることから、選挙期間中において十分に風雨に耐える
素材でなければならないので、耐水性を有していること
が重要であり、そのために耐水性樹脂フィルムの素材は
基本的に水に不溶性の耐水性を有した樹脂が用いられ
る。(2) Water-Resistant Resin Film (a) Water-Resistant Water-Resistant Resin Film, which is affixed to the surface of the above-mentioned plywood and serves as a display part of an election bulletin board for a poster of a candidate, Since the bulletin board is usually posted outdoors, it must be a material that can withstand wind and rain during the election period, so it is important to have water resistance. Therefore, the material of the water resistant resin film is Basically, a resin having water resistance that is insoluble in water is used.
【０００７】(b) 不透明度及び白色度 上記耐水性樹脂フィルムは、裏面の合板の木目模様や色
彩が透けて見えると、立候補者のポスターの文字や写真
が不鮮明になって読みに難くなり、立候補者のメッセー
ジが選挙民に伝わり難くなったり、区割りされた位置に
よって差異が生じると公平な選挙が行ない難くなること
から、不透明度が９０％以上、好ましくは９３％以上
で、かつ白色度が９０％以上、好ましくは９４％以上の
ものであることが重要である。これら不透明度の測定は
ＪＩＳ−Ｐ８１３８によって、また、白色度の測定はＪ
ＩＳ−Ｌ１０７４によって求められる値である。(B) Opacity and whiteness In the above water-resistant resin film, when the wood grain pattern or color of the plywood on the back surface can be seen through, the characters and photographs on the poster of the candidate become unclear, making it difficult to read. The opacity is 90% or more, preferably 93% or more, and the whiteness is high, because it is difficult to convey the message of the candidate to the electoral people and it becomes difficult to hold a fair election if there are differences due to the divided positions. It is important that it is 90% or more, preferably 94% or more. These opacity are measured according to JIS-P8138, and whiteness is measured according to J-P8138.
It is a value obtained by IS-L1074.
【０００８】(c) 構 造 このような耐水性樹脂フィルムは、例えば無機微細粉末
を含む熱可塑性樹脂フィルムを該樹脂の融点より低い温
度で延伸して得られるフィルム内部に微細なボイドを多
数有する延伸樹脂フィルムの単独層、又は該延伸樹脂フ
ィルムと他の樹脂フィルムとを積層した積層フィルム構
造とすることができる。このような耐水性樹脂フィルム
としては、具体的には無機微細粉末を含有する二軸延伸
樹脂微多孔フィルム、該二軸延伸樹脂フィルムをコア層
とし、その片面又は両面に無機微細粉末を含有する一軸
延伸微多孔フィルムが積層された多層構造の延伸樹脂フ
ィルムとすることができる。(C) Structure Such a water resistant resin film has a large number of fine voids inside the film obtained by, for example, stretching a thermoplastic resin film containing inorganic fine powder at a temperature lower than the melting point of the resin. A single layer of the stretched resin film or a laminated film structure in which the stretched resin film and another resin film are laminated can be used. As such a water-resistant resin film, specifically, a biaxially stretched resin microporous film containing an inorganic fine powder, the biaxially stretched resin film as a core layer, containing an inorganic fine powder on one or both sides thereof. It can be a stretched resin film having a multilayer structure in which uniaxially stretched microporous films are laminated.
【０００９】(d) 耐水性樹脂フィルムの製造 このような耐水性樹脂フィルムは、一般に以下に示す原
材料及び製造方法によって製造される。 ＜原材料＞無機微細粉末 上記耐水性樹脂フィルムの製造の際に用いられる無機微
細粉末としては、焼成クレー、炭酸カルシウム、珪藻
土、酸化チタン、パームキュライト、タルクなどを挙げ
ることができ、該無機微細粉末は、粒径が一般に０．０
３〜１５μｍ、好ましくは０．１〜５μｍのものが用い
られる。熱可塑性樹脂 また、上記熱可塑性樹脂としては、ポリプロピレン、ポ
リエチレン、エチレン・プロピレン共重合体、エチレン
・ブテン−１共重合体、エチレン・４−メチルペンテン
−１共重合体、プロピレン・エチレン・ブテン−１共重
合体、ポリスチレン、ポリエチレンテレフタレート、ナ
イロン−６、ナイロン−６，６、ナイロン−６，１０、
ナイロン−６，１２などの耐水性のある樹脂を使用する
こと。(D) Production of Water Resistant Resin Film Such a water resistant resin film is generally produced by the following raw materials and production method. <Raw material> Inorganic fine powder As the inorganic fine powder used in the production of the water-resistant resin film, there can be mentioned calcined clay, calcium carbonate, diatomaceous earth, titanium oxide, permculite, talc and the like. Powders generally have a particle size of 0.0
Those having a thickness of 3 to 15 μm, preferably 0.1 to 5 μm are used. Thermoplastic resin As the thermoplastic resin, polypropylene, polyethylene, ethylene / propylene copolymer, ethylene / butene-1 copolymer, ethylene / 4-methylpentene-1 copolymer, propylene / ethylene / butene- 1 copolymer, polystyrene, polyethylene terephthalate, nylon-6, nylon-6,6, nylon-6,10,
Use water-resistant resin such as nylon-6,12.
【００１０】＜製造方法＞フイルム成形工程 上記無機微細粉末及び熱可塑性樹脂を、該熱可塑性樹脂
の融点以上の温度で、混練機、押出機などを用いて十分
に混練させた後、Ｔダイ法、カレンダー法、キャスト
法、インフレーション法などの各種成形加工法によりフ
ィルム状に成形される。延伸工程 上記無機微細粉末を含む熱可塑性樹脂フィルムは、該熱
可塑性樹脂の融点より低い温度で延伸される。この時の
延伸は一方向或いは二方向に、従って、延伸軸数は一軸
又は二軸である。また、該延伸時の倍率はそれぞれ一般
に１．３〜１５倍、好ましくは３．５〜１０倍である。
この延伸工程により熱可塑性樹脂フィルムは延伸される
ことによって、表面に微細なボイド（空隙）が形成され
て、該フィルムの白色度や不透明度が増す。また、必要
に応じて他の樹脂フィルムが、延伸工程の前に或いは後
に積層される。<Manufacturing Method> Film Forming Step The inorganic fine powder and the thermoplastic resin are sufficiently kneaded at a temperature not lower than the melting point of the thermoplastic resin by using a kneader, an extruder or the like, and then the T-die method. It is formed into a film by various forming methods such as a calendering method, a casting method and an inflation method. Stretching Step The thermoplastic resin film containing the inorganic fine powder is stretched at a temperature lower than the melting point of the thermoplastic resin. The stretching at this time is unidirectional or bidirectional, and therefore the number of stretching axes is uniaxial or biaxial. The stretching ratio is generally 1.3 to 15 times, preferably 3.5 to 10 times.
By stretching the thermoplastic resin film by this stretching step, fine voids (voids) are formed on the surface, and the whiteness and opacity of the film are increased. In addition, another resin film is laminated before or after the stretching step, if necessary.
【００１１】＜物 性＞ボイド 本発明の選挙掲示板の製造方法において用いられる耐水
性樹脂フィルムは、無機微細粉末を核に微細なボイド
（空隙）を多数有している。このような延伸樹脂フィル
ムは次式で計算された空隙率を４〜６０％、好ましくは
８〜５０％有している。 空隙率＝［（ρ0 −ρ）／ρ0 ］×１００ ρ0 ：延伸前のフィルムの密度 ρ ：延伸後のフィルムの密度平滑度（ベック指数） 上記延伸工程によってフィルムを延伸することによっ
て、表面に微細なボイド（空隙）が形成されて、該フィ
ルム表面を粗面に、好ましくは平滑度（ベック指数）を
約２００〜１，０００秒程度に、形成することにより、
接着剤により選挙ポスター紙を強固に接着することがで
きる。上記平滑度の測定は、ベック式平滑度試験器によ
り行なわれる。具体的には、ＪＩＳ−Ｐ８１１９により
規定される測定法により行なわれる。肉 厚 前記合板に貼り付けられる耐水性樹脂フィルムの肉厚
は、一般に１５〜１８０μｍ、好ましくは４０〜１００
μｍのものが用いられる。<Physical Properties> Void The water resistant resin film used in the method for manufacturing the election bulletin board of the present invention has a large number of fine voids (voids) with the inorganic fine powder as the core. Such a stretched resin film has a porosity of 4 to 60%, preferably 8 to 50% calculated by the following formula. Porosity = [(ρ 0 −ρ) / ρ 0 ] × 100 ρ 0 : Density of film before stretching ρ: Density smoothness of film after stretching (Beck index) By stretching the film by the above stretching step, By forming fine voids (voids) on the surface and forming the film surface as a rough surface, preferably with a smoothness (Beck index) of about 200 to 1,000 seconds,
The adhesive can firmly adhere the election poster paper. The smoothness is measured by a Beck's smoothness tester. Specifically, it is performed by the measuring method specified by JIS-P8119. Thickness The thickness of the water resistant resin film attached to the plywood is generally 15 to 180 μm, preferably 40 to 100 μm.
The one with μm is used.
【００１２】＜印 刷＞オフセットインキ 前記不透明度及び白色度を示す耐水性樹脂フィルムの表
面には、予め選挙掲示板である旨の表示や立候補者のポ
スターの貼り付け領域を規定する枠組や貼り付け位置を
表示する掲示番号などをオフセットインキにて印刷され
ていることが重要である。該枠組や掲示番号などを印刷
する際に用いられるオフセットインキは一般に以下の成
分より構成されている。<Printing> Offset ink On the surface of the water-resistant resin film showing the opacity and whiteness, a frame or a sticker that preliminarily indicates an election bulletin board and a sticker area for a poster of a candidate is attached. It is important that the bulletin number indicating the position is printed with offset ink. The offset ink used for printing the frame and the bulletin number is generally composed of the following components.
【００１３】[0013]
【表１】 [Table 1]
【００１４】印 刷 これらオフセットインキを用いて行なわれる印刷は、版
面上のインキを一旦ゴムブランケットに転移し、次いで
耐水性樹脂フィルムの表面に転移させるいわゆるオフセ
ット方式による印刷と、直接、版から紙へ転移する方式
による印刷とがある。上記オフセット方式による印刷、
すなわちオフセット印刷は平板の印刷で、版面の画線を
一度ゴム面に移し、これを仲介として紙に印刷するため
の印刷機、多くは輪転式で版胴・ゴム胴・圧胴の３胴の
組み合わせにより印刷をする。前記枠組や掲示番号など
の印刷はオフセット印刷により一回の印刷で同時に行な
われる。 Printing Printing using these offset inks includes printing by a so-called offset method in which the ink on the plate surface is once transferred to a rubber blanket and then to the surface of the water resistant resin film, and directly from the plate to the paper. There is printing by the method of transferring to. Printing by the above offset method,
That is, offset printing is a flat plate printing, and a printing machine for transferring the image of the plate surface to the rubber surface once and printing it on the paper using this as an intermediary. Print by combining. Printing of the frame, the bulletin board number, etc. is performed simultaneously by one printing by offset printing.
【００１５】(3) 接着剤 (a) 種 類 上記合板に前記耐水性樹脂フィルムを貼着する際に使用
される接着剤としては、例えば、溶剤型ポリイソシアネ
ート系樹脂、アクリル酸アルキルエステル・酢酸ビニル
共重合体エマルジョン、エチレン・酢酸ビニル共重合体
エマルジョン、溶剤型ポリエステル樹脂などの塗布型接
着剤、或いは、ウレタンプレポリマー、液状ポリエステ
ル、イソシアネート系、ポリエステルイソシアネート
系、ボリエーテルイソシアネート系、ポリエチレンイミ
ン系、有機チタネート系などのアンカーコート剤、或い
は、低密度ポリエチレン、エチレン・酢酸ビニル共重合
体、エチレン・アクリル酸共重合体などのホットメルト
接着剤などを挙げることができる。これら接着剤の中で
は、溶剤型ポリイソシアネート系樹脂、アクリル酸アル
キルエステル・酢酸ビニル共重合体エマルジョン、エチ
レン・酢酸ビニル共重合体エマルジョン、溶剤型ポリエ
ステル樹脂などが好適であり、これら接着剤は以下に示
す接着剤製品として市販されている。(3) Adhesive (a) Type Examples of the adhesive used when the water resistant resin film is attached to the above-mentioned plywood are, for example, solvent type polyisocyanate resin, acrylic acid alkyl ester / acetic acid. Coating adhesive such as vinyl copolymer emulsion, ethylene / vinyl acetate copolymer emulsion, solvent type polyester resin, or urethane prepolymer, liquid polyester, isocyanate type, polyester isocyanate type, polyether isocyanate type, polyethyleneimine type Examples thereof include anchor coating agents such as organic titanate-based agents, and hot melt adhesives such as low density polyethylene, ethylene / vinyl acetate copolymers, ethylene / acrylic acid copolymers, and the like. Among these adhesives, solvent-type polyisocyanate-based resin, acrylic acid alkyl ester / vinyl acetate copolymer emulsion, ethylene / vinyl acetate copolymer emulsion, solvent-type polyester resin, etc. are preferable. Is commercially available as the adhesive product shown in.
【００１６】溶剤型ポリイソシアネート系樹脂 ：東洋モートン（株）製「ＢＬＳ−ＰＧ８」アクリル酸アルキルエステル・酢酸ビニル共重合体エマ
ルジョン ：中央理化工業（株）製「ＡＣ−５００」 ：サイデン化学（株）製「ＤＢ−１９５」エチレン・酢酸ビニル共重合体エマルジョン ：新田ゼラチン（株）製「ＳＰ−２８１」 ：コニシ（株）製「ＳＰ−２８１」溶剤型ポリエステル樹脂 ：東洋モートン（株）製「ＡＤ−５７８Ａ／Ｂ」 などを挙げることができる。 Solvent type polyisocyanate resin : "BLS-PG8" manufactured by Toyo Morton Co., Ltd. Alkyl acrylate / vinyl acetate copolymer emma
Rojon : Chuo Rika Kogyo Co., Ltd. "AC-500": Saiden Chemical Co., Ltd. "DB-195" Ethylene / vinyl acetate copolymer emulsion : Nitta Gelatin Co., Ltd. "SP-281": Konishi ( "SP-281" solvent-type polyester resin : manufactured by Toyo Morton Co., Ltd. "AD-578A / B".
【００１７】(b) 塗 布 塗布型の接着剤は一般に１０〜５０ｇ／ｍ２（固形
分）、好ましくは３０〜４０ｇ／ｍ２（固形分）の量で
用いられる。ホットメルト型接着剤は溶融押出ラミネー
トされ、一般に８〜３０μｍの厚みで使用される。従っ
て、このような接着剤層は一般に１〜３０μｍ、好まし
くは２〜１５μｍの厚みに形成される。(B) Coating Fabric The coating type adhesive is generally used in an amount of 10 to 50 g / m 2 (solid content), preferably 30 to 40 g / m 2 (solid content). The hot melt adhesive is melt extrusion laminated and is generally used in a thickness of 8 to 30 μm. Therefore, such an adhesive layer is generally formed to a thickness of 1 to 30 μm, preferably 2 to 15 μm.
【００１８】(4) 支柱 本発明の選挙掲示板を屋外に掲示するためには、一般に
前記合板の裏面側に通常２〜３本の木製の支柱を釘など
により固着したり、或いは鋼鉄製の支柱にボルトなどに
より固着される。(4) Posts In order to display the election bulletin board of the present invention outdoors, generally, two to three wooden posts are usually fixed to the back side of the plywood by nails or steel posts. It is fixed with bolts, etc.
【００１９】[II] 選挙掲示板の製造 本発明の選挙掲示板の製造方法について、以下にその実
施例を挙げて図面に基づき具体的に説明する。図１は本
発明の選挙掲示板の斜視図であり、図２は図１のＡ−Ａ
線断面図であり、図３は印刷された耐水性樹脂フィルム
の断面図である。本発明の選挙掲示板の製造方法にて製
造される選挙掲示板１は、図１に示すように、選挙掲示
板１の本体部分１ａとそれに付属する脚部分１ｂ等とか
ら基本的に形成されている。このような選挙掲示板１は
以下に示す方法によって製造される。[II] Manufacturing of Election Bulletin Board A method of manufacturing an election bulletin board of the present invention will be specifically described below with reference to the accompanying drawings showing examples thereof. FIG. 1 is a perspective view of an election bulletin board of the present invention, and FIG. 2 is AA of FIG.
It is a line sectional view, and Drawing 3 is a sectional view of a printed waterproof resin film. As shown in FIG. 1, an election bulletin board 1 manufactured by the method for manufacturing an election bulletin board of the present invention is basically formed of a main body portion 1a of the election bulletin board 1 and leg portions 1b attached to it. Such an election bulletin board 1 is manufactured by the following method.
【００２０】(1) 選挙掲示板の本体部分の製造 耐水性樹脂フィルムへの枠組や掲示番号などの印刷 本発明の選挙掲示板の製造方法において用いられる前記
不透明度及び白色度を示す耐水性樹脂フィルム２は、単
層であっても良いが、図３に示すように、基材層２ａに
表面層２ｂ及び裏面層２ｃを積層した三層とすることが
できる。これら各層２ａ，２ｂ，２ｃには無機微細粉末
２ｄを核に微細なボイド（空隙）２ｅが多数存在してお
り、これらボイド２ｅによって不透明度及び白色度を増
加させている。また、これら耐水性樹脂フィルム２は、
合板３に貼り付ける前に、その表面に選挙掲示板である
旨の表示４ａや立候補者のポスターの貼り付け領域を規
定する枠組４ｂや貼り付け位置を表示する掲示番号４ｃ
などをオフセットインキにて印刷する。これらオフセッ
トインキを用いて行なわれる印刷４は、版面上のインキ
を一旦ゴムブランケットに転移し、次いで耐水性樹脂フ
ィルム２の表面に転移させるいわゆるオフセット方式に
よる印刷４と、直接、版から紙へ転移する方式による印
刷４とがある。上記オフセット方式による印刷４、すな
わちオフセット印刷は平板の印刷で、版面の画線を一度
ゴム面に移し、これを仲介として紙に印刷するための印
刷機、多くは輪転式で版胴・ゴム胴・圧胴の三胴の組み
合わせにより印刷をする。前記枠組４ｂや掲示番号４ｃ
などの印刷４はオフセット印刷により一回の印刷で同時
に行なわれる。(1) Manufacture of main body of election bulletin board Printing of frame and notice number on water resistant resin film Water resistant resin film 2 showing the opacity and whiteness used in the method of manufacturing election bulletin board of the present invention May be a single layer, but as shown in FIG. 3, it may be three layers in which a front surface layer 2b and a back surface layer 2c are laminated on a base material layer 2a. Each of these layers 2a, 2b, 2c has a large number of fine voids (voids) 2e with the inorganic fine powder 2d as a core, and these voids 2e increase opacity and whiteness. In addition, these water-resistant resin film 2,
Before sticking to the plywood 3, a display 4a indicating that it is an election bulletin board, a frame 4b defining a sticking area for posters of candidates and a posting number 4c displaying a sticking position on the surface thereof.
Etc. are printed with offset ink. Printing 4 performed using these offset inks is printing 4 by a so-called offset method in which the ink on the plate surface is once transferred to a rubber blanket and then to the surface of the water resistant resin film 2, and directly from the plate to the paper. There is printing 4 by the method. The printing 4 by the offset method, that is, the offset printing is a flat plate printing, and a printing machine for transferring the image of the plate surface to the rubber surface once and printing it on the paper by using this as a medium, most of which are a rotary type plate cylinder / blanket cylinder. -Print using a combination of three impression cylinders. The frame 4b and the bulletin number 4c
Printing 4 such as is performed simultaneously by one printing by offset printing.
【００２１】 貼り合せ 前記印刷された耐水性樹脂フィルム２の印刷された面の
反対側に、前記接着剤５を塗布するか、或いは、合板３
側の表面に接着剤５を塗布した後、両者を合わせて耐水
性樹脂フィルム２を合板３に貼り合せることによって選
挙掲示板１の本体部分１ａが形成される。Lamination: The adhesive 5 is applied to the opposite side of the printed surface of the printed water resistant resin film 2 or the plywood 3
After applying the adhesive 5 on the side surface, the main body portion 1a of the election bulletin board 1 is formed by bonding the both and bonding the water resistant resin film 2 to the plywood 3.
【００２２】(2) 脚部部分等の製造 前記選挙掲示板１は、そのまま紐などを取り付けて吊り
下げることができるように形成するか、或いは、該掲示
板１の裏面側に釘６などにより支柱７を固着して脚部分
１ｂを形成させて、支柱７の下部７ａを土中に埋めて選
挙掲示板１を立設させることができるように形成され
る。(2) Manufacture of leg portions, etc. The election bulletin board 1 is formed so that it can be directly hung by attaching a string or the like, or a pillar 7 is attached to the back side of the bulletin board 1 by a nail 6 or the like. Is fixed to form the leg portion 1b, and the lower portion 7a of the pillar 7 is buried in the soil so that the election bulletin board 1 can be erected.
【００２３】(3) 選挙ポスターの貼り付け 前記選挙掲示板１の表示部の印刷された耐水性樹脂フィ
ルム２の表面に、合成紙などにより製造された立候補者
の顔写真及びメッセージをカラー印刷した選挙用ポスタ
ー８を接着剤９を介して貼り合わせるには、各種接着剤
５の中から選択して用いることができるが、特に両面ア
クリル系粘着剤テープを用いて接着するか、溶剤型のポ
リエーテルポリイソシアネート（東洋モートン（株）製
「接着剤ＢＨＳ−６０２０Ａ」）を使用するか、二液溶
剤型ポリエーテル・ポリイソシアネート（東洋モートン
（株）製「接着剤ＢＨＳ−６０２０Ａ／Ｃ」）を使用し
て接着させることが好ましい。(3) Pasting election posters An election in which a face photograph and a message of a candidate made of synthetic paper or the like are printed in color on the surface of the water-resistant resin film 2 printed on the display part of the election bulletin board 1. In order to attach the poster 8 for use with the adhesive 9, it is possible to select and use from among various kinds of adhesives 5. Especially, the double-sided acrylic adhesive tape is used for adhesion, or solvent type polyether is used. Use polyisocyanate ("Adhesive BHS-6020A" manufactured by Toyo Morton Co., Ltd.) or use two-component solvent type polyether polyisocyanate ("Adhesive BHS-6020A / C" manufactured by Toyo Morton Co., Ltd.) It is preferable to bond them.
【００２４】[0024]
実施例１耐水性樹脂延伸フィルムの製造 (1) メルトインデックス（ＭＩ）０．８ｇ／１０分のポ
リプロピレン８１重量％に、高密度ポリエチレン３重量
％及び平均粒径１．５μｍの炭酸カルシウム１６重量％
を混合した組成物（Ａ）を２７０℃に設定した押出機に
て混練した後、シート状に押し出し、冷却装置により冷
却して、無延伸シートを得た。そして、このシートを１
４０℃の温度にまで再度加熱した後、縦方向（ＭＤ）に
５倍延伸した。Example 1 Production of Water-Resistant Resin Stretched Film (1) 81% by weight of melt index (MI) polypropylene of 0.8 g / 10 min, 3% by weight of high-density polyethylene and 16% by weight of calcium carbonate having an average particle size of 1.5 μm
The composition (A) mixed with was kneaded with an extruder set at 270 ° C., then extruded into a sheet and cooled by a cooling device to obtain an unstretched sheet. And this sheet 1
After heating again to a temperature of 40 ° C., it was stretched 5 times in the machine direction (MD).
【００２５】(2) ＭＩが４．０ｇ／１０分のポリプロピ
レン５４重量％と、平均粒径１．５μｍの炭酸カルシウ
ム４６重量％を混合した組成物（Ｂ）を別の押出機にて
混練させた後、これをダイよりシート状に押し出し、こ
れを(1) の５倍延伸フィルムの両面に積層して三層構造
の積層フィルムを得た。次いで、この三層構造の積層フ
ィルムを６０℃まで冷却した後、再び約１６０℃の温度
にまで加熱して、テンターを用いて横方向（ＴＤ）に
７．５倍延伸し、１６５℃の温度でアニーリング処理し
て、６０℃の温度にまで冷却し、耳部をスリットして三
層構造（一軸延伸／二軸延伸／一軸延伸）の、肉厚１１
０μｍ（Ｂ／Ａ／Ｂ＝３０μｍ／５０μｍ／３０μｍ）
の基材層を得た。(2) A composition (B) prepared by mixing 54% by weight of polypropylene having an MI of 4.0 g / 10 min and 46% by weight of calcium carbonate having an average particle size of 1.5 μm is kneaded in another extruder. After that, this was extruded in a sheet form from a die, and this was laminated on both sides of the 5 times stretched film of (1) to obtain a laminated film having a three-layer structure. Then, after cooling the laminated film having the three-layer structure to 60 ° C., it is heated again to a temperature of about 160 ° C., stretched 7.5 times in the transverse direction (TD) using a tenter, and heated at a temperature of 165 ° C. Annealing treatment at 60 ° C, cooling to a temperature of 60 ° C, slitting the ears, three-layer structure (uniaxial stretching / biaxial stretching / uniaxial stretching), wall thickness 11
0 μm (B / A / B = 30 μm / 50 μm / 30 μm)
A base material layer of
【００２６】各層のボイド率は（Ｂ／Ａ／Ｂ＝３０％／
３３．７％／３０％）であった。また、その他の物性は
以下に示す通りであった。 秤 量：８５ｇ／ｍ２、 密 度：０．７８ｇ／ｃｍ３、 白 色 度 ：９５％、 不透明度 ：９４％、 引張り強さ ＭＤ方向：１０ｋｇ／１５ｍｍ幅 ＴＤ方向：２２ｋｇ／１５ｍｍ幅 エルメンドルフ引裂強度 ＭＤ方向：４２ｇ／１５ｍｍ幅 ＴＤ方向：２８ｇ／１５ｍｍ幅 クラーク剛度、 ＭＤ方向：４０ｋｇ／１５ｍｍ幅 ＴＤ方向：７８ｋｇ／１５ｍｍ幅 ベック平滑度：５６０秒The void ratio of each layer is (B / A / B = 30% /
33.7% / 30%). The other physical properties were as shown below. Weighing: 85 g / m 2 , Density: 0.78 g / cm 3 , White chromaticity: 95%, Opacity: 94%, Tensile strength MD direction: 10 kg / 15 mm width TD direction: 22 kg / 15 mm width Elmendorf tear Strength MD direction: 42 g / 15 mm width TD direction: 28 g / 15 mm width Clark stiffness, MD direction: 40 kg / 15 mm width TD direction: 78 kg / 15 mm width Beck smoothness: 560 seconds
【００２７】選挙掲示板の本体部分の製造 (1) 上記耐水性樹脂延伸フィルムの表面側に、オフセ
ット印刷機を用いて東洋インキ製造（株）製「オフセッ
トインキ黒」ＴＳＰ−４００にて、選挙掲示板である旨
の表示や立候補者のポスターの貼り付け領域を規定する
枠組や貼り付け位置を表示する掲示番号などを一度に印
刷することができた。 (2) 板厚４ｍｍの合板の表面側に、酢酸ビニル・アク
リル酸アルキルエステル共重合体エマルジョン（中央理
化工業（株）製接着剤）ＡＣ−５００を７０ｇ／ｍ
２（固形分で３５ｇ／ｍ２）の塗布量で塗布した。 (3) 次いで、この合板の接着剤塗布面に、上記枠組や
掲示番号などを印刷した耐水性樹脂延伸フィルムの裏面
側を貼り合わせて、選挙掲示板の本体部分を製造した。 (4) 前記選挙掲示板の本体部分の裏面側に、断面が７
０ｍｍ×７０ｍｍ、長さが２ｍの支柱を釘にて打ち付け
て脚部を形成した。次いで、該支柱の下部５０ｃｍを土
中に埋めて選挙掲示板を立設させた。 Manufacture of main part of election bulletin board (1) Election bulletin board on the surface side of the above water-resistant resin stretched film using an offset printing machine with "Offset Ink Black" TSP-400 manufactured by Toyo Ink Mfg. Co., Ltd. It was possible to print at once the display indicating that, the frame that defines the pasting area of the candidate poster, and the bulletin number that indicates the pasting position. (2) 70 g / m of AC-500 vinyl acetate / alkyl acrylate copolymer emulsion (adhesive manufactured by Chuo Rika Kogyo Co., Ltd.) AC-500 on the surface side of a plywood having a plate thickness of 4 mm.
The coating amount was 2 (35 g / m 2 in terms of solid content). (3) Then, the back surface side of the water resistant resin stretched film on which the above frame, bulletin number, etc. were printed was bonded to the adhesive coated surface of this plywood to manufacture the main part of the election bulletin board. (4) The cross section is 7 on the back side of the main part of the election bulletin board.
A leg of 0 mm x 70 mm and a length of 2 m was struck with a nail to form a leg. Then, 50 cm of the lower part of the pillar was buried in the soil to stand an election bulletin board.
【００２８】選挙ポスターの貼り付け 王子油化合成紙（株）製「ＹＵＰＯ ＧＦＧ＃１１０」
に立候補者の顔写真及びメッセージをカラー印刷した選
挙用ポスターの裏面側に、溶剤型のポリエーテルポリイ
ソシアネート（東洋モートン（株）製「接着剤ＢＨＳ−
６０２０Ａ」）を塗布した後、前記選挙掲示板の指定さ
れた番号の位置に貼り合わせた。 Pasting election posters "YUPO GFG # 110" manufactured by Oji Yuka Synthetic Paper Co., Ltd.
Solvent-type polyether polyisocyanate (“Adhesive BHS-made by Toyo Morton Co., Ltd.”
6020A ”) and then pasted to the designated number position on the election bulletin board.
【００２９】評 価 この選挙掲示板に貼られた立候補者の選挙ポスターは裏
面に不透明度の高い、白色度の高い耐水性樹脂フィルム
が全面に貼られているので合板の木目や色彩が透けて見
えることが無く、立候補者のポスターの文字や写真が鮮
明で読み易く、立候補者のメッセージが選挙民に伝わり
易く、区割りされた位置によって差異が生じることが無
いので、公平な選挙を行なうことができる。また、耐水
性樹脂フィルムは降雨によっても、該フィルムが伸びた
り、縮んだりすることがないので、皺になり難く、選挙
期間中選挙民にそのメッセージを十分に伝えることがで
きる。更に、本発明の選挙掲示板の製造方法は、不透明
度及び白色度に優れた耐水性樹脂フィルムを予め枠組と
掲示番号をオフセットインキで同時印刷し、これを接着
剤を介して合板に貼り合せているので、印刷回数も少な
く、作業に手間が掛からずに製造することができる。 Evaluation : The election poster for the candidate placed on this election bulletin board has a water resistant resin film with high opacity and high whiteness on the back surface, so the grain and color of plywood can be seen through. In addition, the letters and photos on the posters of the candidacy are clear and easy to read, the message of the candidacy is easy to convey to the electoral people, and there is no difference due to the divided position, so a fair election can be held. .. Further, since the water-resistant resin film does not stretch or shrink even when it is rained, it is difficult for the water-resistant resin film to be wrinkled, and the message can be sufficiently transmitted to the voters during the election period. Furthermore, in the method for manufacturing an election bulletin board of the present invention, a water-resistant resin film having excellent opacity and whiteness is preliminarily simultaneously printed with a frame and a bulletin number with an offset ink, and this is attached to a plywood via an adhesive. Therefore, the number of times of printing is small, and the manufacturing can be performed without troublesome work.
【００３０】実施例２ 下記に示す方法によって耐水性フィルムを製造した以外
は、実施例１と同様の方法によって選挙掲示板を製造し
た結果、実施例１と同様な結果が得られた。耐水性樹脂延伸フィルムの製造 (1) メルトインデックス（ＭＩ）０．８ｇ／１０分のポ
リプロピレン８１重量％に、高密度ポリエチレン３重量
％及び平均粒径１．５μｍの炭酸カルシウム１６重量％
を混合した組成物（Ａ）を２７０℃に設定した押出機に
て混練した後、シート状に押し出し、冷却装置により冷
却して、無延伸シートを得た。そして、このシートを１
４０℃の温度にまで再度加熱した後、縦方向（ＭＤ）に
５倍延伸した。Example 2 An election bulletin board was produced in the same manner as in Example 1 except that a water resistant film was produced by the method shown below. As a result, the same results as in Example 1 were obtained. Manufacture of stretched water-resistant resin film (1) Melt index (MI) 81% by weight of polypropylene of 0.8 g / 10 min, 3% by weight of high-density polyethylene and 16% by weight of calcium carbonate having an average particle size of 1.5 μm
The composition (A) mixed with was kneaded with an extruder set at 270 ° C., then extruded into a sheet and cooled by a cooling device to obtain an unstretched sheet. And this sheet 1
After heating again to a temperature of 40 ° C., it was stretched 5 times in the machine direction (MD).
【００３１】(2) ＭＩが０．４ｇ／１０分のポリプロピ
レン５４重量％と、平均粒径１．５μｍの炭酸カルシウ
ム４６重量％を混合した組成物（Ｂ）と、ＭＩが４．０
ｇ／１０分のポリプロピレン８１重量％に高密度ポリエ
チレン３重量％及び平均粒径１．５μｍの炭酸カルシウ
ム１６重量％を混合した組成物（Ｃ）とを、別の押出機
にて混練させた後、これをダイよりシート状に押し出
し、これを(1) の５倍延伸フィルムの両面に積層し、三
層構造の積層フィルムを得た。次いで、この三層構造の
積層フィルムを６０℃まで冷却した後、再び約１６０℃
の温度にまで加熱して、テンターを用いて横方向（Ｔ
Ｄ）に７．５倍延伸し、１６５℃の温度でアニーリング
処理して、６０℃の温度にまで冷却し、耳部をスリット
して三層構造（一軸延伸／二軸延伸／一軸延伸）の、肉
厚１１０μｍ（Ｂ／Ａ／Ｂ＝３０μｍ／５０μｍ／３０
μｍ）の基材層を得た。(2) A composition (B) in which 54% by weight of polypropylene having an MI of 0.4 g / 10 min and 46% by weight of calcium carbonate having an average particle size of 1.5 μm are mixed, and an MI of 4.0
After kneading 81% by weight of polypropylene for 10 minutes per minute with 3% by weight of high-density polyethylene and 16% by weight of calcium carbonate having an average particle size of 1.5 μm in a different extruder. This was extruded in a sheet form from a die and laminated on both sides of the 5-fold stretched film of (1) to obtain a laminated film having a three-layer structure. Then, after cooling the laminated film having the three-layer structure to 60 ° C., it is again heated to about 160 ° C.
Heat to the temperature of the
D) was stretched 7.5 times, annealed at a temperature of 165 ° C., cooled to a temperature of 60 ° C., and the ears were slit to form a three-layer structure (uniaxial stretching / biaxial stretching / uniaxial stretching). , Wall thickness 110 μm (B / A / B = 30 μm / 50 μm / 30
to obtain a base material layer having a thickness of μm).
【００３２】また、各層のボイド率は（Ｂ／Ａ／Ｂ＝３
０％／２９．７％／３．０％）であった。また、その他
の物性は以下に示す通りであった。 秤 量：９１ｇ／ｍ２、 密 度：０．８３ｇ／ｃｍ３、 白 色 度 ：９５％、 不透明度 ：９２％、 引張り強さ ＭＤ方向：８ｋｇ／１５ｍｍ幅 ＴＤ方向：２５ｋｇ／１５ｍｍ幅 エルメンドルフ引裂強度 ＭＤ方向：４８ｇ／１５ｍｍ幅 ＴＤ方向：２５ｇ／１５ｍｍ幅 クラーク剛度、 ＭＤ方向：４０ｋｇ／１５ｍｍ幅 ＴＤ方向：８６ｋｇ／１５ｍｍ幅 ベック平滑度：６１０秒The void ratio of each layer is (B / A / B = 3
0% / 29.7% / 3.0%). The other physical properties were as shown below. Weighing: 91 g / m 2 , Density: 0.83 g / cm 3 , White chromaticity: 95%, Opacity: 92%, Tensile strength MD direction: 8 kg / 15 mm width TD direction: 25 kg / 15 mm width Elmendorf tear Strength MD direction: 48 g / 15 mm width TD direction: 25 g / 15 mm width Clark stiffness, MD direction: 40 kg / 15 mm width TD direction: 86 kg / 15 mm width Beck smoothness: 610 seconds
【００３３】[0033]
【発明の効果】このようにして得られた選挙掲示板は、
合板の表面に貼られた耐水性樹脂フィルムが雨水により
紙が伸びたり、収縮したりせず、皺になり難いなどの利
点があるし、製造時における印刷の回数も１回だけであ
ることから、その製造工程も短縮することができ、決め
て有用な方法である。しかも、耐水性樹脂フィルムの不
透明度や白色度も高く、下地の合板の模様が表面に浮き
出ることもない。The election bulletin board obtained in this way is
The water-resistant resin film attached to the surface of the plywood has the advantage that the paper does not stretch or shrink due to rainwater, making it difficult to wrinkle, and the number of times of printing during manufacturing is only once. The manufacturing process can be shortened, which is a useful method. In addition, the opacity and whiteness of the water resistant resin film are high, and the pattern of the plywood as the base does not stand out on the surface.
【図１】図１は本発明実施例の選挙掲示板の斜視図であ
る。FIG. 1 is a perspective view of an election bulletin board according to an embodiment of the present invention.
【図２】図２は図１の選挙掲示板のＡ−Ａ断面図であ
る。FIG. 2 is a cross-sectional view taken along the line AA of the election bulletin board in FIG.
【図３】図３は表面に印刷を施した耐水性樹脂フィルム
の部分拡大断面図である。FIG. 3 is a partially enlarged cross-sectional view of a waterproof resin film having a printed surface.
１ 選挙掲示板 １ａ 本体部分 １ｂ 脚部分 ２ 耐水性樹脂フィルム ２ａ 基材層 ２ｂ 表面層 ２ｃ 裏面層 ２ｄ 無機微細粉末 ２ｅ 微細なボイド（空隙） ３ 合板 ４ 印刷 ４ａ 選挙掲示板である旨の表紙 ４ｂ 立候補者のポスターの貼り付け領域を規定する枠
組 ４ｃ 貼り付け位置を表示する掲示番号 ５ 接着剤 ８ 立候補者の顔写真及びメッセージをカラー印刷した
選挙用ポスター ９ 接着剤1 Election Bulletin Board 1a Body Part 1b Leg Part 2 Water Resistant Resin Film 2a Base Layer 2b Surface Layer 2c Back Layer 2d Inorganic Fine Powder 2e Fine Voids 3 Plywood 4 Printing 4a Election Bulletin Board Cover 4b Candidates 4c that defines the pasting area of the poster of the poster 4c Posting number that displays the pasting position 5 Adhesive 8 Election poster with color print of the candidate's face photograph and message 9 Adhesive
Claims (2)
以上、白色度（ＪＩＳ−Ｌ１０７４）が９０％以上の耐
水性樹脂フィルムの表面に枠組と掲示番号をオフセット
インキで同時印刷し、この印刷した樹脂フィルムの印刷
された反対側の面に合板を接着剤で貼り合せたことを特
徴とする選挙掲示板の製造方法。1. Opacity (JIS-P8138) is 90%.
As described above, a frame and a bulletin number are simultaneously printed with an offset ink on the surface of a water-resistant resin film having a whiteness (JIS-L1074) of 90% or more, and a plywood is adhered to the opposite surface of the printed resin film. A method for manufacturing an election bulletin board, which is characterized by being bonded with an agent.
〜３０重量％含有するポリオレフィンの二軸延伸フィル
ムを基材層とし、この表面を裏面に無機微細粉末を８〜
６５重量％含有するポリオレフィンの一軸延伸微多孔フ
ィルムの一軸延伸微多孔フィルムであり肉厚が６０〜３
００μｍ、密度が０．６５〜１．１ｇ／ｃｍ３、平滑度
（ベック指数）が２００〜１，０００秒のものであるこ
とを特徴とする請求項１に記載の選挙掲示板の製造方
法。2. A water resistant resin film containing no inorganic fine powder.
A biaxially stretched film of a polyolefin containing 30 to 30% by weight is used as a base material layer, and the front surface of the base material is the back surface of the inorganic fine powder of 8 to
A uniaxially stretched microporous film of polyolefin containing 65% by weight and having a wall thickness of 60 to 3
The method for manufacturing an election bulletin board according to claim 1, wherein the election bulletin board has a density of 00 μm, a density of 0.65 to 1.1 g / cm 3 , and a smoothness (Beck index) of 200 to 1,000 seconds.