JPH0597917A - Water-soluble polyvinyl acetal resin and ink composition for marking pen - Google Patents
Water-soluble polyvinyl acetal resin and ink composition for marking penInfo
- Publication number
- JPH0597917A JPH0597917A JP25648791A JP25648791A JPH0597917A JP H0597917 A JPH0597917 A JP H0597917A JP 25648791 A JP25648791 A JP 25648791A JP 25648791 A JP25648791 A JP 25648791A JP H0597917 A JPH0597917 A JP H0597917A
- Authority
- JP
- Japan
- Prior art keywords
- degree
- water
- mol
- ink composition
- polyvinyl acetal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】
【目的】 適度な柔軟性を有し、かつ無機物や有機物等
との分散性においても優れた水溶性ポリビニルアセター
ル樹脂及び該水溶性ポリビニルアセタール樹脂を用いた
水性マーキングペン用インキ組成物を得る。
【構成】 −ＣＯＯＭ、─ＳＯ3 Ｍ、−ＯＳＯ3 Ｍ、−
ＰＯ（ＯＭ）2 、
【化１】
（但し、Ｒは、アルキル基、Ｍは、Ｈ、Ｌｉ、Ｎａ、Ｋ
を示す。）、第三級アミン、第四級アンモニウム塩及び
ベタインからなる群から選択した少なくとも一種の親水
性基団を含むユニットの割合が０．０１〜５モル％であ
る、重合度３００〜３５００及びケン化度７５〜９９．
８モル％の変性ポリビニルアルコールを、アセトアルデ
ヒド及び／またはブチルアルデヒドにより、１０≦（Ａ
＋３Ｂ）≦５０の関係を満たすように（但し、Ａはアセ
トアセタール化度、Ｂはブチラール化度）アセタール化
してなる、水溶性ポリビニルアセタール樹脂。(57) [Abstract] [Purpose] Water-soluble polyvinyl acetal resin having appropriate flexibility and excellent dispersibility with inorganic substances and organic substances, and ink for water-based marking pens using the water-soluble polyvinyl acetal resin Obtain the composition. [Configuration] -COOM, ─SO 3 M, -OSO 3 M, -
PO (OM) 2 , embedded image (However, R is an alkyl group, M is H, Li, Na, K
Indicates. ), A tertiary amine, a quaternary ammonium salt, and betaine, the proportion of units containing at least one hydrophilic group selected from the group consisting of 0.01 to 5 mol%, a degree of polymerization of 300 to 3500, and a ken. Degree of chemical conversion 75-99.
8 mol% of modified polyvinyl alcohol was treated with acetaldehyde and / or butyraldehyde for 10 ≦ (A
+ 3B) A water-soluble polyvinyl acetal resin obtained by acetalization so as to satisfy the relationship of ≦ 50 (where A is an acetoacetalization degree and B is a butyralization degree).
Description
【０００１】[0001]
【産業上の利用分野】本発明は、水溶性ポリビニルアセ
タール樹脂及び該水溶性ポリビニルアセタール樹脂を用
いたマーキングペン用インキ組成物に関し、より詳細に
は、柔軟性、無機物及び有機物との分散性並びに接着性
に優れた水溶性ポリビニルアセタール樹脂と、該水溶性
ポリビニルアセタール樹脂を用いることにより、経時筆
記性及び安定性に優れ、かつ消去性マーキングペン用イ
ンキ組成物の場合には経時的な消去性が高められている
水性マーキングペン用インキ組成物に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a water-soluble polyvinyl acetal resin and an ink composition for a marking pen using the water-soluble polyvinyl acetal resin, more specifically, flexibility, dispersibility with an inorganic substance and an organic substance, and By using a water-soluble polyvinyl acetal resin having excellent adhesiveness and the water-soluble polyvinyl acetal resin, excellent writability and stability over time, and erasability in the case of an erasable marking pen ink composition The present invention relates to an ink composition for a water-based marking pen, which has a high viscosity.
【０００２】[0002]
【従来の技術】ポリビニルアルコールは水溶性高分子で
あるため、フィルム材やセラミック・バインダーとして
従来より広く用いられている。しかしながら、ポリビニ
ルアルコールからなるフィルムは、比較的硬いため、用
途によっては、より柔軟なフィルムが要望されている。
また、セラミック・バインダーとして用いる場合におい
ても、ポリビニルアルコールは比較的硬いため、ハンド
リング性が十分でないという問題があった。水溶性、特
に冷水に対する可溶性を高めた材料として、特開昭６２
−１５６１１２号には、完全ケン化ポリビニルアルコー
ルと言われるケン化度９８モル％以上のポリビニルアル
コールであって、アセタール環におけるアルキル基の平
均鎖長の炭素数が０．３４〜１．７０となるように、平
均重合度が比較的低いものをアセタール化することによ
り得られたポリビニルアセタール樹脂が提案されてい
る。しかしながら、上記先行技術のポリビニルアセター
ル樹脂は、冷水可溶性において優れているものの、やは
り、柔軟性が十分でなかった。2. Description of the Related Art Since polyvinyl alcohol is a water-soluble polymer, it has been widely used as a film material or a ceramic binder. However, since a film made of polyvinyl alcohol is relatively hard, a softer film is desired depending on the application.
Further, even when used as a ceramic binder, polyvinyl alcohol is relatively hard, and thus there is a problem that the handling property is not sufficient. As a material having improved water solubility, particularly in cold water, JP-A-62-62
No. 156112 is a polyvinyl alcohol having a saponification degree of 98 mol% or more, which is referred to as completely saponified polyvinyl alcohol, and the average chain length of the alkyl group in the acetal ring is 0.34 to 1.70. Thus, there has been proposed a polyvinyl acetal resin obtained by acetalizing a resin having a relatively low average degree of polymerization. However, although the polyvinyl acetal resin of the above-mentioned prior art is excellent in cold water solubility, it is still insufficient in flexibility.
【０００３】他方、従来、多孔性樹脂や樹脂含浸された
繊維束からなるペン先を備えたマーキングペンが広く用
いられている。この種のマーキングペン用インキ組成物
としては、一般に、着色剤及び樹脂その他の添加剤を有
機溶剤に分散もしくは溶解させて調製されたものが用い
られている。上記有機溶剤としては、通常、アルコール
類、ケトン類または芳香族炭化水素類が多用されている
（例えば、特開昭４９−２９号、特開昭６２−９１４９
号）。しかしながら、上記のような有機溶剤のうち、ケ
トン類や芳香族炭化水素類は毒性が強いという問題があ
った。同様に、アルコール類の中では、メタノールは毒
性が高く、悪臭を発するという問題があった。他方、エ
タノールについては、毒性は比較的少ないものの、コス
トが高くつくという問題があった。On the other hand, conventionally, a marking pen having a pen tip made of a fiber bundle impregnated with a porous resin or a resin has been widely used. As this type of ink composition for marking pens, those prepared by dispersing or dissolving a colorant, a resin and other additives in an organic solvent are generally used. Alcohols, ketones or aromatic hydrocarbons are often used as the organic solvent (for example, JP-A-49-29 and JP-A-62-1149).
issue). However, among the above organic solvents, ketones and aromatic hydrocarbons have a problem that they are highly toxic. Similarly, among alcohols, methanol is highly toxic and has a problem of giving off a bad odor. On the other hand, ethanol has a problem that the cost is high although the toxicity is relatively low.
【０００４】そこで、近年、水性マーキングペン用イン
キ組成物として種々の組成のものが提案されている。例
えば特開平１−１７４５７７号公報には、消去性マーキ
ングペン用インキ組成物として、着色剤の分散性を高め
るために、並びに筆記面に形成された筆跡の造膜性を高
めるために、ポリビニルアルコール等の水溶性樹脂を配
合してなるものが提案されている。しかしながら、ポリ
ビニルアルコールでは、分子中の水酸基が分子内及び分
子間で会合するため、インキ組成物の粘度が経時によっ
て高くなり、筆記性が低下しがちであった。例えば、こ
のマーキングペン用インキ組成物をマーキングペンに充
填した後、長時間にわたり保存した場合には、マーキン
グペン用インキ組成物がペン先を浸透・透過し難くな
り、その結果、筆跡がかすれたり、ひいては筆記不能に
なるという問題があった。Therefore, in recent years, various compositions have been proposed as an aqueous marking pen ink composition. For example, Japanese Patent Application Laid-Open No. 1-174577 discloses a polyvinyl alcohol as an erasable marking pen ink composition for increasing the dispersibility of a colorant and for improving the film-forming property of a handwriting formed on a writing surface. Those prepared by blending a water-soluble resin such as However, in the case of polyvinyl alcohol, since the hydroxyl groups in the molecule associate with each other in the molecule and between the molecules, the viscosity of the ink composition tends to increase with time, and the writability tends to deteriorate. For example, when the marking pen ink composition is filled in a marking pen and then stored for a long time, the marking pen ink composition becomes difficult to penetrate and permeate through the pen tip, and as a result, handwriting may be faint. Then, there was a problem that writing became impossible.
【０００５】また、ポリビニルアルコールを配合した水
性マーキングペン用インキ組成物を、特に、消去性マー
キングペンに用いた場合には、ポリビニルアルコール分
子中の水酸基の数、すなわち筆記面と密着している水酸
基の数が比較的多いため、経時により筆記面との密着性
が高まる結果、消去性が経時的に劣化するという問題も
あった。When an aqueous marking pen ink composition containing polyvinyl alcohol is used in an erasable marking pen, the number of hydroxyl groups in the polyvinyl alcohol molecule, that is, the hydroxyl groups in close contact with the writing surface. Since there is a relatively large number of marks, there is a problem that the erasability deteriorates with time as a result of the increased adhesion to the writing surface over time.
【０００６】[0006]
【発明が解決しようとする課題】本発明は、柔軟性に優
れ、しかも、無機物や有機物との分散性及び接着性に優
れた水溶性ポリビニルアセタール樹脂を提供すること、
並びに経時の筆記性及び安定性に優れ、さらに消去性マ
ーキングペンに用いられるインキ組成物の場合には、経
時の消去性においても優れた水性マーキングペン用イン
キ組成物を提供することを目的とする。DISCLOSURE OF THE INVENTION The present invention provides a water-soluble polyvinyl acetal resin which is excellent in flexibility, and is excellent in dispersibility and adhesiveness with inorganic and organic substances.
Another object of the present invention is to provide an ink composition for a water-based marking pen, which is excellent in writability and stability over time and, in the case of an ink composition used for an erasable marking pen, is also excellent in erasability over time. ..
【０００７】[0007]
【課題を解決するための手段】本願発明者らは、上記課
題を達成すべく鋭意検討した結果、特定の親水性基団を
含む変性ポリビニルアルコールを、アセトアルデヒド及
び／またはブチルアルデヒドにより、アセタール化度を
所定の小さい範囲とすることにより、柔軟性に優れ、無
機物や有機物との分散性及び接着性においても優れた水
溶性ポリビニルアセタール樹脂の得られること、並びに
該水溶性ポリビニルアセタール樹脂を用いれば、経時の
筆記性及び安定性及び経時の消去性にも優れた水性マー
キングペン用インキ組成物が得られることを見出し、本
発明をなすに至った。Means for Solving the Problems As a result of intensive studies to achieve the above object, the inventors of the present invention have found that a modified polyvinyl alcohol containing a specific hydrophilic group is treated with acetaldehyde and / or butyraldehyde to obtain a degree of acetalization. By having a predetermined small range, excellent flexibility, to obtain a water-soluble polyvinyl acetal resin excellent in dispersibility and adhesiveness with inorganic and organic substances, and, if using the water-soluble polyvinyl acetal resin, The inventors have found that an ink composition for a water-based marking pen which is excellent in writability and stability over time and erasability over time can be obtained, and has completed the present invention.
【０００８】すなわち、請求項１に記載の発明にかかる
水溶性ポリビニルアセタール樹脂は、下記の親水性基団
の少なくとも１つを含むユニットを有し、かつ該ユニッ
トの割合が０．０１〜５モル％であり、重合度２００〜
３５００、ケン化度７５〜９９．８モル％の変性ポリビ
ニルアルコールを、アセトアセタール度をＡモル％（但
し、Ａ≧０）、ブチラール化度をＢモル％（但し、Ｂ≧
０）としたときに、 １０≦（Ａ＋３Ｂ）≦５０ の関係を満たすようにアセトアルデヒド及び／またはブ
チルアルデヒドによりアセタール化してなることを特徴
とする。なお、上記親水性基団は、−ＣＯＯＭ、−ＳＯ
3 Ｍ、−ＯＳＯ3 Ｍ、−ＰＯ（ＯＭ）2 、That is, the water-soluble polyvinyl acetal resin according to the invention of claim 1 has a unit containing at least one of the following hydrophilic groups, and the ratio of the unit is 0.01 to 5 mol. %, And the degree of polymerization is 200 to
3,500, modified polyvinyl alcohol having a saponification degree of 75 to 99.8 mol%, an acetoacetal degree of A mol% (however, A ≧ 0) and a butyralization degree of B mol% (however, B ≧ 0).
It is characterized by being acetalized with acetaldehyde and / or butyraldehyde so as to satisfy the relationship of 10 ≦ (A + 3B) ≦ 50 when 0). In addition, the said hydrophilic group is -COOM, -SO.
3 M, -OSO 3 M, -PO (OM) 2 ,
【０００９】[0009]
【化２】 [Chemical 2]
【００１０】（但し、Ｒはアルキル基を示し、上記Ｍ
は、Ｈ、Ｌｉ、ＮａまたはＫを示す。）、第三級アミ
ン、第四級アンモニウム塩及びベタインからなる群から
選択した少なくとも一種である。(However, R represents an alkyl group, and
Indicates H, Li, Na or K. ), A tertiary amine, a quaternary ammonium salt, and betaine.
【００１１】また、請求項２に記載の発明は、水、着色
剤及び樹脂を含有するマーキングペン用インキ組成物で
あって、前記樹脂が、上記請求項１に記載の発明にかか
る水溶性ポリビニルアセタール樹脂であることを特徴と
する、マーキングペン用インキ組成物である。以下、請
求項１，２に記載の発明の詳細を説明する。請求項１に
記載の水溶性ポリビニルアセタール樹脂を得るのに用い
られる変性ポリビニルアルコールとしては、重合度２０
０〜３５００及びケン化度７５〜９９．８モル％のもの
が用いられている。重合度が２００未満では、ポリビニ
ルアルコールの合成が困難であり、重合度が３５００を
超えると溶液粘度が高くなり過ぎ、種々の用途における
実用性が低下する。また、ケン化度７５〜９９．８モル
％のものを用いるのは、ケン化度が７５モル％未満では
水溶性が十分でないからであり、９９．８モル％を超え
るものはポリビニルアルコールの合成が困難であるとの
理由による。The invention described in claim 2 is an ink composition for a marking pen containing water, a colorant and a resin, wherein the resin is the water-soluble polyvinyl according to the invention described in claim 1. An ink composition for a marking pen, which is an acetal resin. The details of the invention described in claims 1 and 2 will be described below. The modified polyvinyl alcohol used to obtain the water-soluble polyvinyl acetal resin according to claim 1 has a degree of polymerization of 20.
Those having a saponification degree of 0 to 3500 and a saponification degree of 75 to 99.8 mol% are used. When the degree of polymerization is less than 200, it is difficult to synthesize polyvinyl alcohol, and when the degree of polymerization is more than 3500, the solution viscosity becomes too high and the practicality in various applications is deteriorated. Further, the reason why the saponification degree is 75 to 99.8 mol% is used because the water solubility is insufficient when the saponification degree is less than 75 mol%, and the saponification degree exceeding 99.8 mol% is a synthesis of polyvinyl alcohol. Because it is difficult.
【００１２】上記重合度及びケン化度を有する変性ポリ
ビニルアルコールを得る方法としては、予め親水性基団
を有するユニットを主鎖の形成時に共存させておく方法
が挙げられる。すなわち、ポリ酢酸ビニル合成時に、該
親水性基団によるエチレンのモノ置換体を付加重合させ
ておけばよい。もっとも、導入される親水性基団は、後
で行われる加水分解及びアセタール化に関与しないこと
が必要である。上記親水性基団によるエチレンのモノ置
換体としては、種々のものが考えられるが、例えば親水
性基団が−ＣＯＯＭの場合を例にとると、下記の化合物
（１），（２）が挙げられる。 （１） ＭＯＯＣ−ＣＨ＝ＣＨ−ＣＯＯＭAs a method for obtaining the modified polyvinyl alcohol having the above-mentioned degree of polymerization and saponification, there is a method in which a unit having a hydrophilic group is allowed to coexist at the time of forming the main chain. That is, at the time of synthesizing polyvinyl acetate, a mono-substituted product of ethylene with the hydrophilic group may be subjected to addition polymerization. However, it is necessary that the introduced hydrophilic group does not participate in the subsequent hydrolysis and acetalization. As the mono-substituted product of ethylene with the hydrophilic group, various ones are conceivable. For example, when the hydrophilic group is -COOM, the following compounds (1) and (2) are listed. Be done. (1) MOOC-CH = CH-COOM
【００１３】[0013]
【化３】 [Chemical 3]
【００１４】（１）の化合物を付加重合した変性ポリビ
ニルアルコールとしては、クラレ社製、商品名；ＫＭ−
１１８及びＫＭ−６１８等が市販されている。また、
（２）の化合物を付加重合した変性ポリビニルアルコー
ルとしては、クラレ社製、商品名；ＫＬ−１１８、ＫＬ
−３１８及びＫＬ−５０６等が市販されている。−ＳＯ
3 Ｍを含む親水性基団によるエチレンのモノ置換体とし
ては、下記の化合物（３）〜（１０）が挙げられる。 （３） ＣＨ2 ＝ＣＨ−ＳＯ3 Ｍ （４） ＣＨ2 ＝ＣＨ−ＣＨ2 −ＳＯ3 ＭThe modified polyvinyl alcohol obtained by addition-polymerizing the compound (1) is manufactured by Kuraray Co., Ltd. under the trade name; KM-.
118 and KM-618 are commercially available. Also,
The modified polyvinyl alcohol obtained by addition-polymerizing the compound (2) is manufactured by Kuraray Co., Ltd., trade name; KL-118, KL.
-318 and KL-506 are commercially available. -SO
The following compounds (3) to (10) can be mentioned as mono-substituted products of ethylene with a hydrophilic group containing 3 M. (3) CH 2 = CH- SO 3 M (4) CH 2 = CH-CH 2 -SO 3 M
【００１５】[0015]
【化４】 [Chemical 4]
【００１６】[0016]
【化５】 [Chemical 5]
【００１７】[0017]
【化６】 [Chemical 6]
【００１８】[0018]
【化７】 [Chemical 7]
【００１９】[0019]
【化８】 [Chemical 8]
【００２０】[0020]
【化９】 [Chemical 9]
【００２１】上記のようにして得た変性ポリビニルアル
コールは、変性度すなわち上記親水性基団を含むユニッ
トの割合が０．０１〜５モル％の範囲であることが必要
であり、この場合、変性ポリビニルアルコールを単独で
使用してもよく、あるいは、変性ポリビニルアルコール
と未変性ポリビニルアルコールとを混合し、全体として
の親水性基団含有ユニットの割合が０．０１〜５モル％
となるようにしてもよい。上記のように親水性基団含有
ユニットの割合を０．０１〜５モル％の範囲としたの
は、５モル％を超えると無機物や有機物との分散性及び
接着性を高めることができないからであり、他方、０．
０１モル％未満では、上記親水性基団含有ユニットを導
入したことによる接着性改善効果が十分に得られないか
らである。The modified polyvinyl alcohol obtained as described above is required to have a modification degree, that is, a ratio of units containing the above-mentioned hydrophilic group in the range of 0.01 to 5 mol%. Polyvinyl alcohol may be used alone, or modified polyvinyl alcohol and unmodified polyvinyl alcohol are mixed, and the ratio of the hydrophilic group-containing unit as a whole is 0.01 to 5 mol%.
May be As described above, the ratio of the hydrophilic group-containing unit is set in the range of 0.01 to 5 mol% because if it exceeds 5 mol%, the dispersibility and adhesiveness with an inorganic substance or an organic substance cannot be improved. Yes, on the other hand, 0.
This is because if it is less than 01 mol%, the effect of improving the adhesiveness due to the introduction of the hydrophilic group-containing unit cannot be sufficiently obtained.
【００２２】請求項１に記載の水溶性ポリビニルアセタ
ール樹脂は、上記のようにして得られる変性ポリビニル
アルコールまたは変性ポリビニルアルコール及び未変性
ポリビニルアルコールの混合物を、アセトアルデヒド及
び／またはブチルアルデヒドにより、アセトアセタール
化度をＡモル％（但し、Ａ≧０）、ブチラール化度Ｂモ
ル％（但し、Ｂ≧０）としたときに、１０≦Ａ＋３Ｂ≦
５０の関係を満たすようにアセタール化することにより
得られる。上記式で示されるアセタール化度（Ａ＋３
Ｂ）が１０モル％未満の場合には、得られたポリビニル
アセタール樹脂の可撓性が乏しくなり、実用的価値がな
くなるからであり、他方、５０モル％を超えると水不溶
性となるからである。The water-soluble polyvinyl acetal resin according to claim 1 is an acetoacetalization of the modified polyvinyl alcohol or the mixture of modified polyvinyl alcohol and unmodified polyvinyl alcohol obtained as described above with acetaldehyde and / or butyraldehyde. When the degree is A mol% (however A ≧ 0) and the butyralization degree is B mol% (however B ≧ 0), 10 ≦ A + 3B ≦
It is obtained by acetalization so as to satisfy the relationship of 50. Degree of acetalization represented by the above formula (A + 3
This is because when B) is less than 10 mol%, the obtained polyvinyl acetal resin becomes poor in flexibility and loses practical value, and when it exceeds 50 mol%, it becomes water-insoluble. .
【００２３】上記アセタール化の工程の一例をより具体
的に説明する。上記変性ポリビニルアルコールまたは変
性ポリビニルアルコール及び未変性ポリビニルアルコー
ルの混合物を水に溶解させる。次に、例えば、塩酸のよ
うな酸触媒の存在の下で上述した混合アセタール化度を
与えるように、所定量のアセトアルデヒド及び／または
ブチルアルデヒドと反応させた後、例えば水酸化ナトリ
ウムのようなアルカリで中和することにより上記水溶性
ポリアセタール樹脂を得ることができる。An example of the acetalization step will be described more specifically. The modified polyvinyl alcohol or a mixture of modified polyvinyl alcohol and unmodified polyvinyl alcohol is dissolved in water. Then, for example, after reacting with a predetermined amount of acetaldehyde and / or butyraldehyde in the presence of an acid catalyst such as hydrochloric acid to give the above-mentioned degree of mixed acetalization, an alkali such as sodium hydroxide is used. The water-soluble polyacetal resin can be obtained by neutralizing with.
【００２４】マーキングペン用インキ組成物 請求項２に記載のマーキングペン用インキ組成物は、上
記のようにして得られる請求項１に記載の水溶性ポリビ
ニルアセタール樹脂を用いて調製される。すなわち、マ
ーキングペン用インキ組成物は、上記のようにして得た
水溶性ポリビニルアセタール樹脂と、水と着色剤とを配
合することにより調製される。マーキングペン用インキ
組成物を構成する水溶性ポリビニルアセタール樹脂を得
るのに用いられる変性ポリビニルアルコールとしては、
重合度２００〜８００及びケン化度７５〜９９．８モル
％のものが特に好適に用いられる。重合度が２００未満
ではポリビニルアルコールの合成が困難であり、重合度
が８００を超えると溶液粘度が高くなり過ぎ、水溶性マ
ーキングペン用インキ組成物としての実用性が低下する
傾向にある。また、ケン化度が７５〜９９．８モル％の
ものを用いるのは、ケン化度が７５モル％未満では水溶
性が十分でないからであり、９９．８モル％を超えるも
のはポリビニルアルコールの合成が困難であるとの理由
による。 Ink Composition for Marking Pen The ink composition for marking pen according to claim 2 is prepared using the water-soluble polyvinyl acetal resin according to claim 1 obtained as described above. That is, the marking pen ink composition is prepared by mixing the water-soluble polyvinyl acetal resin obtained as described above, water, and a colorant. The modified polyvinyl alcohol used to obtain the water-soluble polyvinyl acetal resin constituting the marking pen ink composition,
Those having a degree of polymerization of 200 to 800 and a degree of saponification of 75 to 99.8 mol% are particularly preferably used. If the degree of polymerization is less than 200, it is difficult to synthesize polyvinyl alcohol, and if the degree of polymerization exceeds 800, the solution viscosity becomes too high, and the practicality as a water-soluble marking pen ink composition tends to be lowered. Further, the reason why the saponification degree is 75 to 99.8 mol% is that the saponification degree is less than 75 mol% because the water solubility is insufficient, and the saponification degree exceeding 99.8 mol% is the polyvinyl alcohol. The reason is that synthesis is difficult.
【００２５】水溶性ポリビニルアセタール樹脂は、通
常、マーキングペン用インキ組成物中０．５〜１５重量
％、好ましくは１〜６重量％の範囲で配合される。配合
量が０．５重量％未満では、マーキングペン用インキ組
成物における着色剤の分散性が不十分となり、筆跡の造
膜性も不十分となり、筆記性が劣化するからである。他
方、配合量が１５重量％を超えると、水性マーキングペ
ン用インキ組成物の粘度が高くなり過ぎ、同様に筆記性
が低下するからである。上記水溶性ポリビニルアセター
ル樹脂は、水に良好に溶解するため、本発明のマーキン
グペン用インキ組成物における溶剤としては、水が用い
られる。水性マーキングペン用インキ組成物における水
の配合量は、通常、４５〜９０重量％、好ましくは５０
〜８５重量％の範囲とされる。水に配合量が４５重量％
未満の場合では、マーキングペン用インキ組成物の粘度
が高くなり過ぎ、筆記性が低下するからであり、９０重
量％を超えると上記水溶性ポリビニルアセタール樹脂の
配合率が低下し、着色剤の分散が不十分となり、かつ筆
跡の造膜性も不十分となり、筆記性が劣化するからであ
る。The water-soluble polyvinyl acetal resin is usually added in the ink composition for a marking pen in an amount of 0.5 to 15% by weight, preferably 1 to 6% by weight. If the blending amount is less than 0.5% by weight, the dispersibility of the colorant in the ink composition for a marking pen becomes insufficient, the film forming property of the handwriting becomes insufficient, and the writability deteriorates. On the other hand, if the blending amount exceeds 15% by weight, the viscosity of the water-based marking pen ink composition becomes too high, and the writability similarly deteriorates. Since the water-soluble polyvinyl acetal resin is well dissolved in water, water is used as the solvent in the ink composition for a marking pen of the present invention. The content of water in the water-based marking pen ink composition is usually 45 to 90% by weight, preferably 50.
˜85% by weight. 45% by weight in water
If it is less than 90% by weight, the viscosity of the ink composition for a marking pen becomes too high, and the writability is lowered. If it exceeds 90% by weight, the compounding ratio of the water-soluble polyvinyl acetal resin is lowered and the colorant is dispersed. Is insufficient, and the film-forming property of the handwriting is also insufficient, so that the writability is deteriorated.
【００２６】本発明のマーキングペン用インキ組成物に
おいて用いられる着色剤としては、無彩色または有彩色
の染料または顔料が好ましい。染料としては、水溶性染
料が好ましく用いられるが、水不溶性染料であっても、
適宜の分散剤により組成物中に安定に分散させ得る限り
用いることができる。また、顔料としては、例えば、ア
ゾ系、アンスラキノン系、縮合ポリアゾ系、チオインジ
コ系、金属鎖塩系、フタロシアニン系、ペリノン・ペリ
レン系、ジオキサジン系、キナクリドン系等の有機顔
料、カーボンブラック、チタン白もしくは酸化鉄等の無
機顔料及び蛍光顔料等を用いることができる。なお、染
料または顔料は、上記したものに限定されるものではな
く、従来よりインキ組成物において用いられている任意
の染料または顔料を用いることができる。上記着色剤
は、マーキングペン用インキ組成物において、通常、１
〜３０重量％、好ましくは１〜２０重量％の範囲で配合
される。３０重量％を超えて配合されると、マーキング
ペン用インキ組成物の粘度が高くなり過ぎ、筆記性が低
下するからであり、１重量％未満の配合量では、着色剤
配合量が少なくなり、筆跡の濃度が薄くなり過ぎ、実用
性に欠けるからである。The colorant used in the ink composition for a marking pen of the present invention is preferably an achromatic or chromatic dye or pigment. As the dye, a water-soluble dye is preferably used, but even a water-insoluble dye,
Any suitable dispersant can be used as long as it can be stably dispersed in the composition. Examples of the pigment include azo-based, anthraquinone-based, condensed polyazo-based, thioindico-based, metal chain salt-based, phthalocyanine-based, perinone-perylene-based, dioxazine-based, quinacridone-based organic pigments, carbon black, and titanium white. Alternatively, an inorganic pigment such as iron oxide and a fluorescent pigment can be used. The dye or pigment is not limited to those described above, and any dye or pigment conventionally used in ink compositions can be used. The above colorant is generally used in the marking pen ink composition in an amount of 1
It is compounded in the range of -30 wt%, preferably 1-20 wt%. This is because if the amount is more than 30% by weight, the viscosity of the ink composition for a marking pen becomes too high, and the writability is deteriorated. If the amount is less than 1% by weight, the amount of the colorant is decreased. This is because the density of handwriting becomes too thin and it is not practical.
【００２７】なお、本発明のマーキングペン用インキ組
成物では、上記水溶性ポリビニルアセタール樹脂、水及
び着色剤の他、筆跡の乾燥性を高めるために乾燥促進剤
を添加してもよい。乾燥促進剤としては、低級脂肪族ア
ルコール、特に、エタノール、プロパノールもしくはブ
タノール等を好ましく用いることができる。このような
乾燥促進剤は、マーキングペン用インキ組成物におい
て、通常１５重量％以下、好ましくは１〜１０重量％の
範囲で配合される。また、請求項２に記載の発明のマー
キングペン用インキ組成物を、消去性のマーキングペン
のインキを構成するために用いる場合、すなわち消去性
マーキングペン用インキ組成物を構成する場合には、公
知の種々の剥離剤や該剥離剤の剥離作用を促進する、い
わゆる剥離助剤をさらに含有させてもよい。なお、消去
性マーキングペンとは、例えば、ホワイトボードのよう
な非吸収性ないし非透過性筆記面上に筆記した場合に、
軟らかい乾布や紙で容易に拭き消し得る筆跡を形成する
ようなマーキングペンを言う。In the marking pen ink composition of the present invention, in addition to the above-mentioned water-soluble polyvinyl acetal resin, water and colorant, a drying accelerator may be added to enhance the drying property of handwriting. As the drying accelerator, a lower aliphatic alcohol, particularly ethanol, propanol or butanol can be preferably used. Such a drying accelerator is generally added in the marking pen ink composition in an amount of 15% by weight or less, preferably 1 to 10% by weight. Further, when the ink composition for a marking pen according to claim 2 is used for forming an ink for an erasable marking pen, that is, when forming an ink composition for an erasable marking pen, it is known. These various releasing agents and so-called releasing aids that promote the releasing action of the releasing agent may be further contained. In addition, the erasable marking pen, for example, when writing on a non-absorbent or non-transparent writing surface such as a whiteboard,
A marking pen that forms handwriting that can be easily wiped with a soft dry cloth or paper.
【００２８】上記剥離剤としては、種々の微小な樹脂粒
子が用いられ、また、剥離助剤としては、例えば、常温
で液状の揮発性水溶性物質または常温で液状の難揮発性
水不溶性樹脂の水性エマルジョン等が用いられる。剥離
剤として使用し得る上記樹脂粒子としは、例えば、ポリ
メタクリル酸メチル、アクリル−スチレン重合体、ポリ
スチレン、ポリ塩化ビニル、エポキシ樹脂、メラミン樹
脂、ベンゾグアナミン樹脂等からなる微小粒子、または
ポリ酢酸ビニル、ポリスチレン、アクリル−スチレン共
重合体もしくはポリメタクリル酸メチル等からなる樹脂
エマルジョンが用いられる。上記剥離剤は、通常、水性
マーキングペン用インキ組成物中、１〜５０重量％、好
ましくは１〜４０重量％の範囲で含有される。剥離剤の
配合量が、１重量％未満では、筆跡の十分な消去性を得
ることができないからであり、他方、５０重量％を超え
て配合されると、筆跡の色調が変化するおそれがあり、
好ましくないからである。Various minute resin particles are used as the release agent, and examples of the release aid include volatile water-soluble substances which are liquid at room temperature or sparingly volatile water-insoluble resins which are liquid at room temperature. An aqueous emulsion or the like is used. Examples of the resin particles that can be used as a release agent include, for example, polymethylmethacrylate, acryl-styrene polymer, polystyrene, polyvinyl chloride, epoxy resin, melamine resin, fine particles made of benzoguanamine resin, or polyvinyl acetate, A resin emulsion made of polystyrene, an acrylic-styrene copolymer, polymethylmethacrylate, or the like is used. The release agent is usually contained in the aqueous marking pen ink composition in an amount of 1 to 50% by weight, preferably 1 to 40% by weight. This is because if the compounding amount of the release agent is less than 1% by weight, sufficient erasability of the handwriting cannot be obtained, while if it exceeds 50% by weight, the color tone of the handwriting may change. ,
This is because it is not preferable.
【００２９】上記剥離助剤として用いられる揮発性水溶
性物質としては、例えば、グリセリン、エチレングリコ
ール、プロピレングリコール等のグリコール類、または
ジエチレングリコール、トリエチレングリコール、ポリ
エチレングリコール、ジプロピルグリコール、トリプロ
ピルグリコールもしくはポリプロピレングリコール等の
ポリアルコキレングリコールを挙げることができる。常
温で液状の難揮発性水不溶性物質の水性エマルジョンと
しては、例えば、脂肪族カルボン酸エステル、グリセリ
ド、高級炭化水素等の水性エマルジョンを挙げることが
できる。Examples of the volatile water-soluble substance used as the peeling aid include glycols such as glycerin, ethylene glycol and propylene glycol, or diethylene glycol, triethylene glycol, polyethylene glycol, dipropyl glycol, tripropyl glycol or Mention may be made of polyalcoalkylene glycols such as polypropylene glycol. Examples of the aqueous emulsion of the hardly volatile water-insoluble substance that is liquid at room temperature include aqueous emulsions of aliphatic carboxylic acid esters, glycerides, higher hydrocarbons and the like.
【００３０】上記剥離助剤は、通常、本発明のマーキン
グペン用インキ組成物において、２０重量％以下、好ま
しくは、１０重量％以下の範囲で配合される。剥離助剤
の配合量が２０重量％を超えると剥離助剤の分散性が低
下し、得られた水性マーキングペン用インキ組成物の消
去性がかえって阻害されるからである。上記剥離剤ある
いは剥離助剤は、消去性マーキングペン用インキ組成物
分野において既に広く知られており、従って、本発明に
おいても、上記で例示した剥離剤及び剥離助剤に限定さ
れず、公知の種々の剥離剤及び剥離助剤を用い得ること
を指摘しておく。さらに、本発明の水性マーキングペン
用インキ組成物には、本発明の目的を達成し得る範囲内
において、必要に応じて、任意のｐＨ調整剤、防腐剤等
を含有させてもよい。The above-mentioned peeling aid is usually blended in the marking pen ink composition of the present invention in an amount of 20% by weight or less, preferably 10% by weight or less. This is because if the amount of the peeling aid compounded exceeds 20% by weight, the dispersibility of the peeling aid decreases, and the erasability of the resulting aqueous marking pen ink composition is rather impaired. The release agent or release aid is already widely known in the field of erasable marking pen ink compositions, and therefore, the present invention is not limited to the release agents and release aids exemplified above, and is well known. It should be pointed out that various release agents and release aids can be used. Further, the ink composition for a water-based marking pen of the present invention may contain any pH adjusting agent, preservative and the like, if necessary, within a range capable of achieving the object of the present invention.
【００３１】[0031]
【作用】請求項１に記載の水溶性ポリビニルアセタール
樹脂では、上記変性ポリビニルアルコールが上記特定の
アセタール度を有するようにアセトアルデヒド及び／ま
たはブチルアルデヒドでアセタール化されているため、
アセタール環の立体障害に起因する結晶化や水酸基相互
の分子間水素結合の生成が抑制される。その結果、十分
な水溶性を有しつつ、しかも柔軟性に優れたポリビニル
アセタール樹脂が構成されている。また、上記特定の親
水性基団を含むユニットを上記特定の割合で含有してい
るため、該親水性基団の作用により、無機物や有機物と
の分散性及び接着性が高められる。In the water-soluble polyvinyl acetal resin according to claim 1, since the modified polyvinyl alcohol is acetalized with acetaldehyde and / or butyraldehyde so as to have the specific acetal degree,
Crystallization due to steric hindrance of the acetal ring and formation of intermolecular hydrogen bonds between hydroxyl groups are suppressed. As a result, a polyvinyl acetal resin having sufficient water solubility and excellent flexibility is constituted. Further, since the unit containing the specific hydrophilic group is contained in the specific ratio, the action of the hydrophilic group enhances dispersibility and adhesiveness with an inorganic substance or an organic substance.
【００３２】また、請求項２に記載の水性マーキングペ
ン用インキ組成物では、着色剤の分散性を高めるため、
並びに筆跡の造膜性を高めるために上記特定の水溶性ポ
リビニルアセタール樹脂が配合されているが、上記特定
の水溶性ポリビニルアセタール樹脂では、水酸基の分子
内及び分子間における会合が生じ難い。従って、本発明
の水性マーキングペン用インキ組成物では、経時によっ
て粘度が増加しない。なお、剥離剤及び剥離助剤を含有
させた場合には、ポリビニルアルコールと異なり、上記
水溶性ポリビニルアセタール樹脂は、分子中にアルキル
基を有するものであるため、分子中の水酸基の数すなわ
ち筆記面と密着している水酸基の数が少なく、従って、
十分な消去性を発揮させることができる。しかも、上記
水溶性ポリビニルアセタール樹脂は、分子中に上記特定
の親水性基団を含むユニットを有するため、ポリビニル
アルコールに比べて、剥離剤、剥離助剤及び着色剤等と
の分散性が優れている。In the ink composition for a water-based marking pen according to claim 2, in order to enhance the dispersibility of the colorant,
In addition, the above-mentioned specific water-soluble polyvinyl acetal resin is blended in order to enhance the film forming property of the handwriting, but in the above-mentioned specific water-soluble polyvinyl acetal resin, intramolecular and intermolecular association of hydroxyl groups is unlikely to occur. Therefore, the viscosity of the aqueous marking pen ink composition of the present invention does not increase with time. When a release agent and a release aid are contained, unlike the polyvinyl alcohol, the water-soluble polyvinyl acetal resin has an alkyl group in the molecule, and therefore the number of hydroxyl groups in the molecule, that is, the writing surface. The number of hydroxyl groups in close contact with is small, therefore
Sufficient erasability can be exhibited. Moreover, since the water-soluble polyvinyl acetal resin has a unit containing the specific hydrophilic group in the molecule, it has excellent dispersibility with a release agent, a release aid, a colorant, etc., as compared with polyvinyl alcohol. There is.
【００３３】[0033]
【実施例】以下、本発明の非限定的な実施例及び各比較
例を挙げることにより、本発明を明らかにする。まず、
請求項１に記載の発明の水溶性ポリビニルアセタール樹
脂についての実施例１〜６及び比較のための比較例１〜
４を説明する。実施例１ 重合度３００、ケン化度９８モル％、イタコン酸変性度
２モル％のポリビニルアルコール２００ｇを水１６００
ｇに加え、９０℃で約２時間攪拌して溶解させた。次
に、得られた溶液を４５℃に冷却し、これに３５重量％
濃度の塩酸５０ｇを加え、さらに３５℃まで冷却した。The present invention will be clarified by giving non-limiting examples of the present invention and comparative examples. First,
Examples 1 to 6 of the water-soluble polyvinyl acetal resin of the invention according to claim 1 and Comparative examples 1 to 1 for comparison
4 will be described. Example 1 200 g of polyvinyl alcohol having a degree of polymerization of 300, a degree of saponification of 98 mol% and a degree of modification with itaconic acid of 2 mol% was added to 1600 of water.
In addition to g, it was dissolved by stirring at 90 ° C. for about 2 hours. The solution obtained is then cooled to 45 ° C., to which 35% by weight
50 g of concentrated hydrochloric acid was added, and the mixture was further cooled to 35 ° C.
【００３４】次いで、純度９９％のブチルアルデヒド２
０ｇ及び純度９９％のアセトアルデヒド２５ｇを２時間
かけて滴下し、３５℃で３時間反応させたところ、白濁
した反応混合物を得た。この反応混合物を２０℃まで冷
却し、攪拌下に１０重量％濃度の水酸化ナトリウム水溶
液１９２ｇを加えて、透明な溶液を得た。得られた溶液
をポリエチレンフィルム上に流延し、乾燥させ、透明な
フィルムを得た。このフィルムをＤＭＳＯ−ｄ6 に溶解
し、13Ｃ−ＮＭＲを用いてアセタール化度を測定したと
ころ、ブチラール化度は１０モル％、アセトアセタール
化度は１５モル％であった。Then, butyraldehyde 2 having a purity of 99%
When 0 g and 25 g of acetaldehyde having a purity of 99% were added dropwise over 2 hours and reacted at 35 ° C. for 3 hours, a cloudy reaction mixture was obtained. The reaction mixture was cooled to 20 ° C., and 192 g of a 10 wt% sodium hydroxide aqueous solution was added with stirring to obtain a transparent solution. The obtained solution was cast on a polyethylene film and dried to obtain a transparent film. When this film was dissolved in DMSO-d 6 and the degree of acetalization was measured using 13 C-NMR, the degree of butyralization was 10 mol% and the degree of acetoacetalization was 15 mol%.
【００３５】実施例２ 重合度１７００、ケン化度９８．５モル％、マレイン酸
変性度３モル％のポリビニルアルコール２００ｇに、実
施例１と同様にしてブチルアルデヒド１８ｇ及びアセト
アルデヒド１１ｇを反応させた後、２０℃に冷却し、水
酸化ナトリウム水溶液で中和して透明な溶液を得た。得
られた透明溶液を用い、実施例１と同様にしてフィルム
とし、アセタール化度を測定したところ、ブチラール化
度は１０モル％、アセトアセタール化度は５モル％であ
った。 Example 2 200 g of polyvinyl alcohol having a degree of polymerization of 1700, a degree of saponification of 98.5 mol% and a degree of modification with maleic acid of 3 mol% were reacted with 18 g of butyraldehyde and 11 g of acetaldehyde in the same manner as in Example 1. The solution was cooled to 20 ° C. and neutralized with an aqueous sodium hydroxide solution to obtain a transparent solution. Using the obtained transparent solution, a film was formed in the same manner as in Example 1, and the degree of acetalization was measured. The degree of butyralization was 10 mol% and the degree of acetoacetalization was 5 mol%.
【００３６】実施例３ 重合度３５００、ケン化度９４モル％、スルホン酸変性
度０．５モル％のポリビニルアルコール２００ｇに、実
施例１と同様にしてブチルアルデヒド１１ｇ及びアセト
アルデヒド３６ｇを反応させた後、２０℃に冷却し、水
酸化ナトリウム水溶液で中和して透明な溶液を得た。得
られた透明溶液を用い、実施例１と同様にしてフィルム
とし、アセタール化度を測定したところ、ブチラール化
度は６モル％、アセトアセタール化度は２５モル％であ
った。 Example 3 After reacting 200 g of polyvinyl alcohol having a degree of polymerization of 3500, a degree of saponification of 94 mol% and a degree of sulfonic acid modification of 0.5 mol% with 11 g of butyraldehyde and 36 g of acetaldehyde in the same manner as in Example 1. The solution was cooled to 20 ° C. and neutralized with an aqueous sodium hydroxide solution to obtain a transparent solution. Using the obtained transparent solution, a film was formed in the same manner as in Example 1 and the degree of acetalization was measured. The degree of butyralization was 6 mol% and the degree of acetoacetalization was 25 mol%.
【００３７】実施例４ 重合度２０００、ケン化度８０モル％、リン酸変性度
０．１モル％のポリビニルアルコール２００ｇに、実施
例１と同様にしてブチルアルデヒド１０ｇ及びアセトア
ルデヒド９ｇを反応させた後、２０℃に冷却し、水酸化
ナトリウム水溶液で中和して透明な溶液を得た。得られ
た透明溶液を用い、実施例１と同様にしてフィルムと
し、アセタール化度を測定したところ、ブチラール化度
は５モル％、アセトアセタール化度は６モル％であっ
た。 Example 4 200 g of polyvinyl alcohol having a degree of polymerization of 2000, a degree of saponification of 80 mol% and a degree of modification with phosphoric acid of 0.1 mol% were reacted with 10 g of butyraldehyde and 9 g of acetaldehyde in the same manner as in Example 1. The solution was cooled to 20 ° C. and neutralized with an aqueous sodium hydroxide solution to obtain a transparent solution. Using the obtained transparent solution, a film was formed in the same manner as in Example 1 and the degree of acetalization was measured. The degree of butyralization was 5 mol% and the degree of acetoacetalization was 6 mol%.
【００３８】実施例５ 重合度５００、ケン化度８８モル％、マレイン酸変性度
４モル％のポリビニルアルコール２００ｇに、実施例１
と同様にしてブチルアルデヒド２０ｇを反応させた後、
２０℃に冷却し、水酸化ナトリウム水溶液で中和して透
明な溶液を得た。得られた透明溶液を用い、実施例１と
同様にしてフィルムとし、アセタール化度を測定したと
ころ、ブチラール化度は１０モル％であった。 Example 5 Example 1 was added to 200 g of polyvinyl alcohol having a polymerization degree of 500, a saponification degree of 88 mol% and a maleic acid modification degree of 4 mol%.
After reacting 20 g of butyraldehyde in the same manner as
It was cooled to 20 ° C. and neutralized with an aqueous sodium hydroxide solution to obtain a transparent solution. Using the obtained transparent solution, a film was formed in the same manner as in Example 1, and the degree of acetalization was measured. The degree of butyral was 10 mol%.
【００３９】実施例６ 重合度１０００、ケン化度９５モル％、スルホン酸変性
度３モル％のポリビニルアルコール２００ｇに、実施例
１と同様にしてブチルアルデヒド４３ｇを反応させた
後、２０℃に冷却し、水酸化ナトリウム水溶液で中和し
て透明な溶液を得た。得られた透明溶液を用い、実施例
１と同様にしてフィルムとし、アセタール化度を測定し
たところ、アセトアセタール化度は３１モル％であっ
た。 Example 6 200 g of polyvinyl alcohol having a polymerization degree of 1000, a saponification degree of 95 mol% and a sulfonic acid modification degree of 3 mol% were reacted with butyraldehyde 43 g in the same manner as in Example 1, and then cooled to 20 ° C. Then, it was neutralized with an aqueous solution of sodium hydroxide to obtain a transparent solution. Using the obtained transparent solution, a film was formed in the same manner as in Example 1 and the degree of acetalization was measured. As a result, the degree of acetoacetalization was 31 mol%.
【００４０】比較例１ 重合度３００、ケン化度９８モル％、イタコン酸変性度
２モル％のポリビニルアルコール２００ｇに、実施例１
と同様にしてブチルアルデヒド２３ｇ及びアセトアルデ
ヒド３６ｇを反応させたところ、白色沈澱が生成した。
２０℃に冷却し、水酸化ナトリウム水溶液で中和した
が、上記白色沈澱は溶解しなかった。この溶液を用い、
実施例１と同様にしてアセタール化度を測定したとこ
ろ、ブチラール化度は１３モル％、アセトアセタール化
度は２５モル％であった。 Comparative Example 1 Example 1 was added to 200 g of polyvinyl alcohol having a polymerization degree of 300, a saponification degree of 98 mol% and an itaconic acid modification degree of 2 mol%.
When 23 g of butyraldehyde and 36 g of acetaldehyde were reacted in the same manner as above, a white precipitate was formed.
It was cooled to 20 ° C. and neutralized with an aqueous sodium hydroxide solution, but the above white precipitate did not dissolve. With this solution,
When the degree of acetalization was measured in the same manner as in Example 1, the degree of butyralization was 13 mol% and the degree of acetoacetalization was 25 mol%.
【００４１】比較例２ 重合度３５００、ケン化度９４モル％、スルホン酸変性
度０．５モル％のポリビニルアルコール２００ｇに、実
施例１と同様にしてブチルアルデヒド４９ｇ及びアセト
アルデヒド２９ｇを反応させたところ、白色沈澱が生成
した。２０℃に冷却し、水酸化ナトリウム水溶液で中和
したが、上記白色沈澱は溶解しなかった。この溶液を用
い、実施例１と同様にしてアセタール化度を測定したと
ころ、ブチラール化度は２５モル％、アセトアセタール
化度は２０モル％であった。 Comparative Example 2 When 200 g of polyvinyl alcohol having a polymerization degree of 3500, a saponification degree of 94 mol% and a sulfonic acid modification degree of 0.5 mol% were reacted with 49 g of butyraldehyde and 29 g of acetaldehyde in the same manner as in Example 1. , A white precipitate formed. It was cooled to 20 ° C. and neutralized with an aqueous sodium hydroxide solution, but the above white precipitate did not dissolve. When the acetalization degree was measured using this solution in the same manner as in Example 1, the butyralization degree was 25 mol% and the acetoacetalization degree was 20 mol%.
【００４２】比較例３ 重合度５００、ケン化度８８モル％、マレイン酸変性度
４モル％のポリビニルアルコール２００ｇに、実施例１
と同様にしてブチルアルデヒド６０ｇを反応させたとこ
ろ、白色沈澱が生成した。２０℃に冷却し、水酸化ナト
リウム水溶液で中和したが、上記白色沈澱は溶解しなか
った。この溶液を用い、実施例１と同様にしてアセター
ル化度を測定したところ、ブチラール化度は３０モル％
であった。 Comparative Example 3 Example 1 was added to 200 g of polyvinyl alcohol having a polymerization degree of 500, a saponification degree of 88 mol% and a maleic acid modification degree of 4 mol%.
When 60 g of butyraldehyde was reacted in the same manner as above, a white precipitate was formed. It was cooled to 20 ° C. and neutralized with an aqueous sodium hydroxide solution, but the above white precipitate did not dissolve. When the degree of acetalization was measured using this solution in the same manner as in Example 1, the degree of butyralization was 30 mol%.
Met.
【００４３】比較例４ 重合度１０００、ケン化度９５モル％、スルホン酸変性
度３モル％のポリビニルアルコール２００ｇに、実施例
１と同様にしてアセトアルデヒド８３ｇを反応させたと
ころ、白色沈澱が生成した。２０℃に冷却し、水酸化ナ
トリウム水溶液で中和したが、上記白色沈澱は溶解しな
かった。この溶液を用い、実施例１と同様にしてアセタ
ール化度を測定したところ、アセトアセタール化度は５
８モル％であった。 Comparative Example 4 When 200 g of polyvinyl alcohol having a polymerization degree of 1000, a saponification degree of 95 mol% and a sulfonic acid modification degree of 3 mol% were reacted with 83 g of acetaldehyde in the same manner as in Example 1, a white precipitate was formed. .. It was cooled to 20 ° C. and neutralized with an aqueous sodium hydroxide solution, but the above white precipitate did not dissolve. When the acetalization degree was measured using this solution in the same manner as in Example 1, the acetoacetalization degree was 5
It was 8 mol%.
【００４４】比較例５ 重合度３００、ケン化度９８モル％、イタコン酸変性度
２モル％のポリビニルアルコールを調製した。比較例６ 重合度１７００、ケン化度９８．５モル％、マレイン酸
変性度３モル％のポリビニルアルコールを調製した。 Comparative Example 5 A polyvinyl alcohol having a polymerization degree of 300, a saponification degree of 98 mol% and an itaconic acid modification degree of 2 mol% was prepared. Comparative Example 6 A polyvinyl alcohol having a polymerization degree of 1700, a saponification degree of 98.5 mol% and a maleic acid modification degree of 3 mol% was prepared.
【００４５】実施例１〜６及び比較例１〜６の評価 上記のようにして得られた実施例１〜６及び比較例１〜
６の樹脂を以下のようにして評価した。まず、各樹脂を
水に溶かして１０重量％溶液とし、温度２０℃における
水への溶解性を目視により調べた。結果を表１に示す。
次に、上記水溶液をポリエチレンフィルム上に流延し、
乾燥させ、透明な１００μｍのフィルムを得た。このフ
ィルムの柔軟性を手触りにより調べた。結果を表１に示
す。表１において、評価記号の意味は以下の通りであ
る。 ◎ … 極めて良好、 〇 … 良好、 × … 悪い Evaluation of Examples 1 to 6 and Comparative Examples 1 to 6 Examples 1 to 6 and Comparative Examples 1 to 1 obtained as described above.
The resin of No. 6 was evaluated as follows. First, each resin was dissolved in water to form a 10 wt% solution, and the solubility in water at a temperature of 20 ° C. was visually examined. The results are shown in Table 1.
Next, the aqueous solution is cast on a polyethylene film,
It was dried to obtain a transparent 100 μm film. The flexibility of this film was examined by touch. The results are shown in Table 1. In Table 1, the meanings of the evaluation symbols are as follows. ◎… Extremely good, ○… Good, ×… Poor
【００４６】[0046]
【表１】 [Table 1]
【００４７】次に、請求項２に記載の発明にかかる水性
マーキングペン用インキ組成物についての実施例７〜実
施例１１及び比較のための比較例５，６につき説明す
る。実施例７ 重合度５００、ケン化度８８モル％、イタコン酸変性度
２モル％のポリビニルアルコール２００ｇを水１６００
ｇに加え、９０℃で約２時間攪拌して溶解させた。次
に、このポリビニルアルコール水溶液を約４５℃に冷却
し、これに３５重量％濃度の塩酸５０ｇを加え、さらに
約３５℃まで冷却した。冷却後、純度９９％のブチルア
ルデヒド２０ｇを上記溶液に加え、約３５℃で３時間反
応させたところ、白濁した反応混合物を得た。Next, Examples 7 to 11 of the ink composition for a water-based marking pen according to the second aspect of the present invention and Comparative Examples 5 and 6 for comparison will be described. Example 7 200 g of polyvinyl alcohol having a degree of polymerization of 500, a degree of saponification of 88 mol%, and a degree of modification with itaconic acid of 2 mol% were added to 1600 of water.
In addition to g, it was dissolved by stirring at 90 ° C. for about 2 hours. Next, this polyvinyl alcohol aqueous solution was cooled to about 45 ° C., 50 g of 35 wt% concentration hydrochloric acid was added thereto, and further cooled to about 35 ° C. After cooling, 20 g of butyraldehyde having a purity of 99% was added to the above solution and reacted at about 35 ° C. for 3 hours to obtain a cloudy reaction mixture.
【００４８】得られた反応混合物を約２０℃まで冷却
し、攪拌下において１０重量％濃度の水酸化ナトリウム
水溶液１９２ｇを加えて、透明な溶液を得た。得られた
透明溶液をポリエチレンフィルム上に流延し、乾燥させ
て透明なフィルムを得た。得られた透明フィルムをＤＭ
ＳＯ−ｄ6 に溶解し、13Ｃ−ＮＭＲを用いてアセタール
化度を測定したところ、ブチラール化度は１０モル％で
あった。上記のようにして得られた透明溶液、すなわち
１０重量％濃度のポリビニルブチラール溶液３０ｇと、
カーボンブラック５ｇと、アクリル−スチレン共重合体
樹脂（昭和高分子社製、商品；ポリゾールＡＴ−２０１
１）６ｇと、ポリエチレングリコール（平均分子量＝２
００）２ｇとを、水５８ｇ及びエタノール７ｇを混合し
た混合溶液中に溶解し、分散させ、黒色の水性マーキン
グペン用インキ組成物を得た。The obtained reaction mixture was cooled to about 20 ° C., and 192 g of a 10 wt% aqueous sodium hydroxide solution was added with stirring to obtain a transparent solution. The resulting transparent solution was cast on a polyethylene film and dried to obtain a transparent film. DM the obtained transparent film
Was dissolved in SO-d 6, was measured degree of acetalization with 13 C-NMR, butyralization degree was 10 mol%. The transparent solution obtained as described above, that is, 30 g of a 10 wt% concentration polyvinyl butyral solution,
5 g of carbon black and acrylic-styrene copolymer resin (manufactured by Showa High Polymer Co., Ltd .; Polysol AT-201)
1) 6 g and polyethylene glycol (average molecular weight = 2
00g) was dissolved and dispersed in a mixed solution of 58 g of water and 7 g of ethanol to obtain a black aqueous ink composition for a marking pen.
【００４９】実施例８ 重合度５００、ケン化度９８モル％、スルホン酸変性度
３モル％のポリビニルアルコールを用いたこと、並びに
ブチルアルデヒドに代えてアセトアルデヒド４３ｇを用
いたこと以外は実施例１と同様にしてアセトアセタール
化度３１モル％のポリビニルアセトアセタールの１０重
量％水溶液を得た。上記のようにして得られた透明溶
液、すなわち１０重量％濃度のポリビニルアセトアセタ
ール溶液５０ｇと、カーボンブラック４ｇと、アクリル
−スチレン共重合体樹脂（昭和高分子社製、商品；ポリ
ゾールＡＴ−２０１１）４ｇと、ポリエチレングリコー
ル（平均分子量＝２００）２ｇとを、水４０ｇ及びエタ
ノール５ｇを混合した混合溶液中に溶解し、分散させ、
黒色の水性マーキングペン用インキ組成物を得た。 Example 8 Example 1 was repeated except that polyvinyl alcohol having a degree of polymerization of 500, a degree of saponification of 98 mol% and a degree of sulfonic acid modification of 3 mol% was used, and 43 g of acetaldehyde was used instead of butyraldehyde. Similarly, a 10 wt% aqueous solution of polyvinyl acetoacetal having an acetoacetalization degree of 31 mol% was obtained. The transparent solution obtained as described above, that is, 50 g of a 10 wt% concentration polyvinyl acetoacetal solution, 4 g of carbon black, and an acrylic-styrene copolymer resin (manufactured by Showa High Polymer Co., Ltd .; Polysol AT-2011) 4 g and polyethylene glycol (average molecular weight = 200) 2 g were dissolved and dispersed in a mixed solution in which 40 g of water and 5 g of ethanol were mixed,
A black water-based marking pen ink composition was obtained.
【００５０】実施例９ 重合度３００、ケン化度９８モル％、マレイン酸変性度
４モル％のポリビニルアルコールを用いたこと、アルデ
ヒドとして、ブチルアルデヒド１０ｇ及びアセトアルデ
ヒド９ｇを用いたこと以外は実施例１と同様にして、ブ
チラール化度５モル％及びアセトアセタール化度６モル
％のポリビニルアセタールの１５重量％水溶液を得た。
上記のようにして得られた透明溶液、すなわち１５重量
％濃度のポリビニルアセタール溶液３０ｇと、カーボン
ブラック６ｇと、ポリスチレン重量（旭化成工業社製、
商品；ラテックスＳＢＬ ８８０１）１５ｇと、ジエチ
レングリコール３ｇとを、水４０ｇ及びイソプロピルア
ルコール５ｇを混合した混合溶液中に溶解し、分散さ
せ、黒色の水性マーキングペン用インキ組成物を得た。 Example 9 Example 1 was repeated except that polyvinyl alcohol having a polymerization degree of 300, a saponification degree of 98 mol% and a maleic acid modification degree of 4 mol% was used, and 10 g of butyraldehyde and 9 g of acetaldehyde were used as aldehydes. In the same manner as above, a 15% by weight aqueous solution of polyvinyl acetal having a butyralization degree of 5 mol% and an acetoacetalization degree of 6 mol% was obtained.
The transparent solution obtained as described above, that is, 30 g of a polyvinyl acetal solution having a concentration of 15% by weight, 6 g of carbon black, and polystyrene weight (manufactured by Asahi Chemical Industry Co., Ltd.,
15 g of a commercial product; latex SBL 8801) and 3 g of diethylene glycol were dissolved and dispersed in a mixed solution of 40 g of water and 5 g of isopropyl alcohol to obtain a black aqueous marking pen ink composition.
【００５１】実施例１０ 重合度５００、ケン化度８８モル％、リン酸変性度０．
１モル％のポリビニルアルコールを用いたこと、アルデ
ヒドとして、ブチルアルデヒド１１ｇ及びアセトアルデ
ヒド３６ｇを用いたこと以外は実施例１と同様にして、
ブチラール化度６モル％及びアセトアセタール化度２５
モル％のポリビニルアセタールの１０重量％水溶液を得
た。上記のようにして得られた１０重量％濃度のポリビ
ニルアセタール溶液３０ｇと、カーボンブラック５ｇ
と、ポリスチレン樹脂（旭化成工業社製、商品；ラテッ
クスＳＢＬ ８８０１）１５ｇと、ポリエチレングリコ
ール（平均分子量＝２００）２ｇとを、水５８ｇ及びエ
タノール５ｇを混合した混合溶液中に溶解し、分散さ
せ、黒色の水性マーキングペン用インキ組成物を得た。 Example 10 Polymerization degree 500, saponification degree 88 mol%, phosphoric acid modification degree 0.
In the same manner as in Example 1 except that 1 mol% of polyvinyl alcohol was used and 11 g of butyraldehyde and 36 g of acetaldehyde were used as aldehydes.
Butyralization degree 6 mol% and acetoacetalization degree 25
A 10% by weight aqueous solution of mol% polyvinyl acetal was obtained. 30 g of a polyvinyl acetal solution having a concentration of 10% by weight obtained above and 5 g of carbon black
15 g of polystyrene resin (commercially available from Asahi Kasei Kogyo Co., Ltd .; Latex SBL 8801) and 2 g of polyethylene glycol (average molecular weight = 200) were dissolved and dispersed in a mixed solution of 58 g of water and 5 g of ethanol to disperse black. An aqueous ink composition for a water-based marking pen was obtained.
【００５２】実施例１１ 重合度７００、ケン化度８０モル％、スルホン酸変性度
１モル％のポリビニルアルコールを用いたこと、アルデ
ヒドとして、ブチルアルデヒド１８ｇ及びアセトアルデ
ヒド１１ｇを用いたこと以外は実施例１と同様にして、
ブチラール化度１０モル％及びアセトアセタール化度５
モル％のポリビニルアセタールの１０重量％水溶液を得
た。上記のようにして得られた１０重量％濃度のポリビ
ニルアセタール溶液１５ｇと、カーボンブラック３ｇ
と、アクリル−スチレン共重合体（昭和高分子社製、商
品；ポリゾールＡＴ−２０１１）１０ｇと、グリセリン
２ｇとを、水７５ｇ及びエタノール５ｇを混合した混合
溶液中に溶解し、分散させ、黒色の水性マーキングペン
用インキ組成物を得た。 Example 11 Example 1 was repeated except that polyvinyl alcohol having a degree of polymerization of 700, a degree of saponification of 80 mol% and a degree of sulfonic acid modification of 1 mol% was used, and 18 g of butyraldehyde and 11 g of acetaldehyde were used as aldehydes. In the same way as
Butyralization degree 10 mol% and acetoacetalization degree 5
A 10% by weight aqueous solution of mol% polyvinyl acetal was obtained. 15 g of a 10 wt% concentration polyvinyl acetal solution obtained as described above and 3 g of carbon black
And 10 g of an acrylic-styrene copolymer (manufactured by Showa Highpolymer Co., Ltd .; product: Polysol AT-2011) and 2 g of glycerin were dissolved and dispersed in a mixed solution prepared by mixing 75 g of water and 5 g of ethanol to give a black solution. An aqueous ink composition for a marking pen was obtained.
【００５３】比較例７ 重合度５００、ケン化度８８モル％のポリビニルアルコ
ール５ｇと、カーボンブラック４ｇと、アクリル−スチ
レン共重合体樹脂（昭和高分子社製、商品；ポリゾール
ＡＴ−２０１１）６ｇと、ポリエチレングリコール（平
均分子量＝２００）２ｇとを、水８２ｇ及びエタノール
８ｇを混合した混合溶液中に溶解し、分散させ、黒色の
水性マーキングペン用インキ組成物を得た。 Comparative Example 7 5 g of polyvinyl alcohol having a degree of polymerization of 500 and a saponification degree of 88 mol%, 4 g of carbon black, and 6 g of an acrylic-styrene copolymer resin (manufactured by Showa High Polymer Co., Ltd .; Polysol AT-2011). , 2 g of polyethylene glycol (average molecular weight = 200) were dissolved and dispersed in a mixed solution of 82 g of water and 8 g of ethanol to obtain a black aqueous marking pen ink composition.
【００５４】比較例８ 重合度３００、ケン化度９８モル％のポリビニルアルコ
ール８ｇと、カーボンブラック６ｇと、ポリスチレン共
重合体樹脂（旭化成工業社製、商品；ラテックスＳＢＬ
８８０１）１５ｇと、ジエチレングリコール３ｇと
を、水８５ｇ及びエタノール５ｇを混合した混合溶液中
に溶解し、分散させ、黒色の水性マーキングペン用イン
キ組成物を得た。 Comparative Example 8 8 g of polyvinyl alcohol having a degree of polymerization of 300 and a degree of saponification of 98 mol%, 6 g of carbon black, and a polystyrene copolymer resin (commercially available from Asahi Chemical Industry Co., Ltd .; latex SBL
8801) 15 g and diethylene glycol 3 g were dissolved and dispersed in a mixed solution of 85 g of water and 5 g of ethanol to obtain a black aqueous marking pen ink composition.
【００５５】実施例７〜１１及び比較例７，８の評価 上記のようにして得られた実施例７〜１１及び比較例
７，８の水性マーキングペン用インキ組成物を、以下の
ようにして評価した。まず、水性マーキングペン用イン
キ組成物を、ホウロウからなる非吸収性筆記面に筆記
し、５分間放置して乾燥させ、その筆跡を乾布で軽く擦
過したときの筆跡の消去性（筆記後初期消去性）と、温
度２５℃及び相対湿度６０％において筆跡を１カ月放置
した後の同様の消去性（筆記後経時消去性）とを目視に
より調べた。結果を表２に示す。表２において、評価記
号の意味は以下の通りである。 ◎ … 極めて良好、 〇 … 良好、 × … 悪い Evaluation of Examples 7 to 11 and Comparative Examples 7 and 8 The ink compositions for aqueous marking pens of Examples 7 to 11 and Comparative Examples 7 and 8 obtained as described above were prepared as follows. evaluated. First, an ink composition for a water-based marking pen is written on a non-absorbent writing surface made of enamel, left to stand for 5 minutes to dry, and the handwriting is lightly rubbed with a dry cloth to erase the handwriting (initial erasing after writing). And the similar erasability after leaving the handwriting for 1 month at a temperature of 25 ° C. and a relative humidity of 60% (erasability with time after writing) was visually examined. The results are shown in Table 2. In Table 2, the meanings of the evaluation symbols are as follows. ◎… Extremely good, ○… Good, ×… Poor
【００５６】次に、各水性マーキングペン用インキ組成
物を調製した直後に筆記することにより形成された筆跡
の消去性（調製後初期後消去性）と、インキ組成物を調
製した後に温度４０℃及び相対湿度６０％で１ケ月放置
した後に筆記することにより形成された筆跡の消去性
（調製後経時消去性）とを目視により調べた。結果を表
２に示す。さらに、上記において各水性マーキングペン
用インキ組成物を調製した直後に筆記した場合の筆記性
と、温度４０℃及び相対湿度６０％で１カ月放置した後
に筆記した場合の筆記性についての目視による評価結果
を表２に示す。Next, the erasability of the handwriting formed by writing immediately after preparing each of the aqueous marking pen ink compositions (erasing property after initial preparation) and the temperature of 40 ° C. after preparing the ink composition. Also, the erasability of the handwriting formed by writing after left for 1 month at a relative humidity of 60% (erasability after preparation) was visually examined. The results are shown in Table 2. Furthermore, the above-mentioned visual evaluation of the writability when written immediately after the preparation of each aqueous marking pen ink composition and the writability when left for one month at a temperature of 40 ° C. and a relative humidity of 60%. The results are shown in Table 2.
【００５７】[0057]
【表２】 [Table 2]
【００５８】表２から明らかなように、実施例７〜１１
の各水性マーキングペン用インキ組成物では、消去性及
び筆記性が経時によりさほど低下していないことがわか
る。これに対して、比較例７，８のポリビニルアルコー
ル含有水性マーキングペン用インキ組成物では、経時に
より消去性及び筆記性の低下することがわかる。なお、
ホウロウからなる上記非吸収性筆記面に換えて、メラミ
ン樹脂またはフッ素樹脂からなる各筆記面についても上
記と同様にして消去性及び筆記性を評価したところ、表
２と同様の結果の得られることが確かめられた。As is clear from Table 2, Examples 7 to 11
It can be seen that the erasability and writability of each of the water-based marking pen ink compositions of (3) above are not significantly deteriorated over time. On the other hand, in the polyvinyl alcohol-containing aqueous marking pen ink compositions of Comparative Examples 7 and 8, it is found that the erasability and the writability are deteriorated with time. In addition,
When the erasability and the writability were evaluated in the same manner as above for each writing surface made of melamine resin or fluororesin instead of the above non-absorbent writing surface made of enamel, the same results as in Table 2 were obtained. Was confirmed.
【００５９】[0059]
【発明の効果】以上のように、請求項１に記載の発明の
水溶性ポリビニルアセタール樹脂は、上記特定のアセタ
ール化度を有するようにアセトアルデヒド及び／または
ブチルアルデヒドでアセタール化されているため、十分
な柔軟性及び水溶性を示す。また、従来のポリビニルア
ルコールでは、主として水酸基を含むユニットで分散性
や接着性が担われていたが、本発明の水溶性ポリビニル
アセタール樹脂は、上記特定の親水性基団を含むユニッ
トを含有しているため、無機物や有機物との分散性及び
接着性が著しく改善されている。よって、本発明の水溶
性ポリビニルアセタール樹脂は、例えばセラミック・バ
インダーとして好適に用いることができる他、アセター
ル環の有するアルキル基及び／または上記親水性基団よ
り、有機顔料等の分散性にも優れているため、水性マー
カー、水性インクジェット記録用インク、水性インクジ
ェット記録紙用コーティング剤、親水性付与添加剤等に
も好適に用いることができる。また、本発明の水溶性ポ
リビニルアセタール樹脂は、水を溶剤として使用するこ
とができ、有機溶剤を使用する必要がないため、有機溶
剤の使用による環境問題を引き起こすことがない。As described above, since the water-soluble polyvinyl acetal resin of the invention according to claim 1 is acetalized with acetaldehyde and / or butyraldehyde so as to have the above-mentioned specific acetalization degree, it is sufficient. It exhibits excellent flexibility and water solubility. Further, in the conventional polyvinyl alcohol, the dispersibility and adhesiveness were mainly carried by the unit containing a hydroxyl group, but the water-soluble polyvinyl acetal resin of the present invention contains a unit containing the above specific hydrophilic group. Therefore, the dispersibility and adhesiveness with inorganic substances and organic substances are remarkably improved. Therefore, the water-soluble polyvinyl acetal resin of the present invention can be suitably used as, for example, a ceramic binder, and is excellent in dispersibility of an organic pigment or the like than an alkyl group in an acetal ring and / or the hydrophilic group. Therefore, it can be suitably used for a water-based marker, a water-based inkjet recording ink, a water-based inkjet recording paper coating agent, a hydrophilicity-imparting additive, and the like. Moreover, since the water-soluble polyvinyl acetal resin of the present invention can use water as a solvent and does not need to use an organic solvent, it does not cause an environmental problem due to the use of the organic solvent.
【００６０】請求項２に記載の発明の水性マーキングペ
ン用インキ組成物では、上記特定の水溶性ポリビニルア
セタール樹脂を、水及び着色剤と配合してなるため、着
色剤の分散性及び筆跡の造膜性が高められており、しか
も、ポリビニルアルコールとは異なり分子中の水酸基が
分子内及び分子間で配合することがないため、経時的に
粘度が増加しない。従って、長時間にわたり保存した場
合でも優れた筆記性を発揮する。In the ink composition for a water-based marking pen according to the second aspect of the present invention, the specific water-soluble polyvinyl acetal resin is blended with water and a coloring agent, so that the dispersibility of the coloring agent and the handwriting The film property is enhanced, and unlike polyvinyl alcohol, the hydroxyl groups in the molecule are not compounded intramolecularly or intermolecularly, so that the viscosity does not increase with time. Therefore, even when it is stored for a long time, it exhibits excellent writability.
【００６１】また、剥離剤及び剥離助剤を含有させた場
合には、水溶性ポリビニルアセタール樹脂が分子中にア
ルキル基を有するため、分子中の水酸基の数、すなわち
紙面と密着している水酸基の数がポリビニルアルコール
の場合に比べて少ないため、長期間保存したとしても、
優れた消去性を維持させることができる。しかも、上記
特定の水溶性ポリビニルアセタール樹脂は、分子中に、
上記親水性基団を含むユニットを含有しているため、ポ
リビニルアルコールと比べて、上記のように剥離剤、剥
離助剤及び着色剤等との分散性においても優れている。
よって、種々の剥離剤、剥離助剤及び着色剤等を用いて
容易に水性マーキングペン用インキ組成物を調製するこ
とができる。さらに、本発明の水性マーキングペン用イ
ンキ組成物は、主溶剤として水を用いるものであるた
め、安全性においても、有機溶剤を主溶剤として用いた
インキ組成物に比べて優れている。When the release agent and the release aid are contained, since the water-soluble polyvinyl acetal resin has an alkyl group in the molecule, the number of hydroxyl groups in the molecule, that is, the number of hydroxyl groups in close contact with the paper surface, Since the number is smaller than that of polyvinyl alcohol, even if stored for a long time,
Excellent erasability can be maintained. Moreover, the above specific water-soluble polyvinyl acetal resin has
Since it contains a unit containing the hydrophilic group, it is more excellent in dispersibility with a release agent, a release aid, a colorant and the like as described above, as compared with polyvinyl alcohol.
Therefore, the aqueous marking pen ink composition can be easily prepared by using various releasing agents, releasing aids, coloring agents and the like. Furthermore, since the water-based marking pen ink composition of the present invention uses water as a main solvent, it is also excellent in safety as compared with an ink composition using an organic solvent as a main solvent.
Claims (2)
3 Ｍ、−ＰＯ（ＯＭ）2 、 【化１】 （但し、Ｒはアルキル基を、Ｍは、Ｈ、Ｌｉ、Ｎａまた
はＫを示す。）、三級アミン、四級アンモニウム塩及び
ベタインからなる群から選択した少なくとも一つの親水
性基団を含むユニットを有し、かつ該ユニットの割合が
０．０１〜５モル％である重合度２００〜３５００、ケ
ン化度７５〜９９．８モル％の変性ポリビニルアセター
ルを、アセトアセタール化度をＡモル％（但し、Ａ≧
０）、ブチラール化度をＢモル％（但し、Ｂ≧０）とし
たときに、 １０≦（Ａ＋３Ｂ）≦５０ の関係を満たすようにアセトアルデヒド及び／またはブ
チルアルデヒドによりアセタール化してなることを特徴
とする、水溶性ポリビニルアセタール樹脂。1. --COOM, --SO 3 M, --OSO
3 M, -PO (OM) 2 , embedded image (However, R represents an alkyl group, M represents H, Li, Na or K.), a unit containing at least one hydrophilic group selected from the group consisting of a tertiary amine, a quaternary ammonium salt and betaine. And a modified polyvinyl acetal having a degree of polymerization of 200 to 3500 and a degree of saponification of 75 to 99.8 mol% in which the proportion of the unit is 0.01 to 5 mol%, and the degree of acetoacetalization is A mol% ( However, A ≧
0) and the degree of butyralization is B mol% (provided that B ≧ 0), it is acetalized with acetaldehyde and / or butyraldehyde so as to satisfy the relationship of 10 ≦ (A + 3B) ≦ 50. A water-soluble polyvinyl acetal resin.
ペン用インキ組成物であって、前記樹脂が、請求項１に
記載の水溶性ポリビニルアセタール樹脂であることを特
徴とする、マーキングペン用インキ組成物。2. An ink composition for a marking pen containing water, a colorant and a resin, wherein the resin is the water-soluble polyvinyl acetal resin according to claim 1. Ink composition.