JPH06176403A - Optical recording medium and its production - Google Patents
Optical recording medium and its productionInfo
- Publication number
- JPH06176403A JPH06176403A JP4351272A JP35127292A JPH06176403A JP H06176403 A JPH06176403 A JP H06176403A JP 4351272 A JP4351272 A JP 4351272A JP 35127292 A JP35127292 A JP 35127292A JP H06176403 A JPH06176403 A JP H06176403A
- Authority
- JP
- Japan
- Prior art keywords
- recording medium
- film
- optical recording
- color tone
- reflection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、光記録媒体およびその
製造方法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an optical recording medium and its manufacturing method.
【０００２】[0002]
【従来の技術】光記録媒体は、レーザ光を用いて記録を
読み出す記録媒体であって、コンパクトディスク、レー
ザーディスク、ＣＤ−Ｒ、ミニディスク等が知られてい
る。これらの光記録媒体は、レーザ光反射型が一般的で
あって、そのため、反射膜を備えている。この反射膜
は、高い反射率を得るために、従来、ＡｌやＡｕのスパ
ッタ膜が使用されている。2. Description of the Related Art An optical recording medium is a recording medium for reading a record by using a laser beam, and a compact disc, a laser disc, a CD-R, a mini disc and the like are known. These optical recording media are generally of the laser light reflection type, and therefore have a reflection film. As the reflective film, a sputtered film of Al or Au is conventionally used in order to obtain a high reflectance.
【０００３】[0003]
【発明が解決しようとする課題】したがって、従来の光
記録媒体は、上記反射膜の材料の色を呈し、画一的なも
のとなり、また、トップコート中に染料を入れたり、印
刷レーベル等を用いて着色する方法が採られているが、
そうすると、反射膜の持つ美しい金属光沢を生かすこと
ができず、面白みに欠けるという問題があった。Therefore, the conventional optical recording medium has a uniform color by exhibiting the color of the material of the above-mentioned reflective film, and also has a dye in the top coat, a print label or the like. Although the method of coloring is used,
Then, the beautiful metallic luster of the reflective film cannot be utilized and there is a problem that it lacks in fun.
【０００４】そこで、本発明は、反射膜としては、銀あ
るいは銀を主体とする合金を画一的に用いるが、色々な
色調を呈することのできる光記録媒体およびその製造方
法を提供することを目的とするものである。Therefore, the present invention uniformly provides silver or an alloy mainly composed of silver as a reflective film, but provides an optical recording medium capable of exhibiting various color tones and a method for producing the same. It is intended.
【０００５】[0005]
【課題を解決するための手段】このような目的は、下記
（１）〜（１０）の発明によって達成される。 （１）レーザ光を用いて、反射により記録を読み出す光
記録媒体において、銀を主体とする反射膜を有し、該反
射膜上に、Ｓｉを主体とする色調制御膜を設けたことを
特徴とする光記録媒体。 （２）前記反射膜の銀含有率が６０atm%以上である上記
（１）の光記録媒体。 （３）前記色調制御膜のＳｉの含有率が４０atm%以上で
ある上記（１）または（２）の光記録媒体。 （４）前記色調制御膜の複素光学定数の実部ｎと、虚部
ｋとが、可視光領域において０．５≦ｎ≦５．０、
０．００１≦ｋ≦５．０であり、前記反射制御層の厚さ
ｔが、４nm≦ｔ≦５００nmである上記（１）〜（３）の
いずれかの光記録媒体。 （５）前記色調制御膜上に、さらにほぼ透明の保護層を
有する上記（１）〜（４）のいずれかの光記録媒体。 （６）レーザ光を用いて、反射により記録を読み出す光
記録媒体の製造方法において、銀を主体とする反射膜を
形成する工程、および該反射膜上に、Ｓｉを主体とする
色調制御膜を形成する工程を有し、色調制御膜の形成工
程において、その材料組成および膜厚の少なくとも一方
を変えることによって、呈する色調を変化させることを
特徴とする光記録媒体の製造方法。 （７）前記反射膜の銀含有量が６０atm%以上である上記
（６）の光記録媒体の製造方法。 （８）前記色調制御膜のＳｉの含有率が４０atm%以上で
ある上記（６）または（７）の光記録媒体。 （９）前記反射制御層の複素光学定数の実部ｎと、虚部
ｋとが可視光領域において０．５≦ｎ≦５．０，０．０
０１≦ｋ≦５．０であり、前記反射制御層の厚さｔが、
４nm≦ｔ≦５００nmである上記（６）〜（８）のいずれ
かの光記録媒体の製造方法。 （１０）前記反射制御層上に、さらにほぼ透明の保護層
を設ける上記（６）〜（９）のいずれかの光記録媒体の
製造方法。The above objects are achieved by the inventions (1) to (10) below. (1) An optical recording medium for reading a record by reflection using a laser beam, which has a reflective film mainly composed of silver, and a color tone control film mainly composed of Si is provided on the reflective film. And an optical recording medium. (2) The optical recording medium as described in (1) above, wherein the silver content of the reflective film is 60 atm% or more. (3) The optical recording medium according to (1) or (2), wherein the color tone control film has a Si content of 40 atm% or more. (4) The real part n and the imaginary part k of the complex optical constant of the color tone control film are 0.5 ≦ n ≦ 5.0 in the visible light region,
The optical recording medium according to any one of (1) to (3) above, wherein 0.001 ≦ k ≦ 5.0 and the thickness t of the reflection control layer is 4 nm ≦ t ≦ 500 nm. (5) The optical recording medium according to any one of (1) to (4) above, which further has a substantially transparent protective layer on the color tone control film. (6) In a method of manufacturing an optical recording medium for reading a record by reflection using a laser beam, a step of forming a reflective film mainly composed of silver, and a color tone control film mainly composed of Si on the reflective film. A method of manufacturing an optical recording medium, which comprises a step of forming the color tone control film, wherein the color tone exhibited is changed by changing at least one of the material composition and the film thickness in the step of forming the color tone control film. (7) The method for producing an optical recording medium according to (6), wherein the silver content of the reflective film is 60 atm% or more. (8) The optical recording medium according to (6) or (7), wherein the color tone control film has a Si content of 40 atm% or more. (9) The real part n and the imaginary part k of the complex optical constant of the reflection control layer are 0.5 ≦ n ≦ 5.0, 0.0 in the visible light region.
01 ≦ k ≦ 5.0, and the thickness t of the reflection control layer is
The method for producing an optical recording medium according to any one of (6) to (8), wherein 4 nm ≦ t ≦ 500 nm. (10) The method for producing an optical recording medium according to any one of the above (6) to (9), wherein a substantially transparent protective layer is further provided on the reflection control layer.
【０００６】[0006]
【作用】本発明は、銀層の上に反射制御層である色調制
御膜を設けて、反射光のスペクトル制御によって種々の
色調を得るという新しい発想のものである。すなわち、
反射を銀で得、得たい色調の反射スペクトルを得るため
に、特定の吸収をもつ反射制御層すなわち色調制御膜を
用いるのである。そして、その結果、反射膜として画一
的に銀を用いるものの、種々の色調を得ることができる
ものである。The present invention has a novel idea of providing a color tone control film, which is a reflection control layer, on a silver layer to obtain various color tones by controlling the spectrum of reflected light. That is,
In order to obtain reflection with silver and obtain a reflection spectrum of a desired color tone, a reflection control layer having a specific absorption, that is, a color tone control film is used. As a result, although silver is uniformly used as the reflective film, various color tones can be obtained.
【０００７】[0007]
【具体的構成】以下、この出願の発明の具体的構成につ
いて詳細に説明する。本発明の反射膜は銀を主体とし、
光記録媒体に通常使用される透明基板上に形成される。
銀を主体とするとは、銀が６０at% 以上、特に８５〜１
００atm%であることを意味する。そして、反射膜は通常
４０nm〜０．５mm程度の厚さとする。また、基板と反射
膜間には中間下地層やレーザ光を用いて記録可能な層を
設けてもよい。Specific Structure The specific structure of the invention of this application will be described in detail below. The reflective film of the present invention is mainly composed of silver,
It is formed on a transparent substrate usually used for optical recording media.
Mainly composed of silver means that silver is 60 at% or more, especially 85 to 1
It means that it is 00 atm%. The reflective film is usually about 40 nm to 0.5 mm thick. In addition, an intermediate underlayer or a layer that can be recorded using laser light may be provided between the substrate and the reflective film.
【０００８】上記反射膜上には、反射制御層である色調
制御膜が設けられる。反射制御層は、その可視光領域
（λ＝４５０〜８００nmの波長域）における複素光学定
数の実部をｎ、虚部をｋ、その厚さをｔとしたとき、ｎ
＝０．５〜５．０、ｋ＝０．００１〜５．０、ｔ＝４〜
５００nmであることが好ましい。このような光学定数で
あれば、上記の膜厚ｔ範囲内で、後に詳述する反射スペ
クトルプロファイルを得る膜厚ｔを容易に実験的に求め
ることができる。A color tone control film, which is a reflection control layer, is provided on the reflection film. When the real part of the complex optical constant in the visible light region (λ = 450 to 800 nm wavelength region) is n, the imaginary part is k, and its thickness is t, the reflection control layer is n
= 0.5 to 5.0, k = 0.001 to 5.0, t = 4 to
It is preferably 500 nm. With such an optical constant, the film thickness t for obtaining a reflection spectrum profile, which will be described in detail later, can be easily obtained experimentally within the above-mentioned film thickness t range.
【０００９】このようなｎおよびｋをもつ材質として
は、Ｓｉ、Ｓｉの酸化物、窒化物、炭化物を採用するこ
とができる。As materials having such n and k, Si, oxides of Si, nitrides and carbides can be adopted.
【００１０】このような色調制御膜は反射膜表面に直接
形成されていてもよいが、色調制御膜と反射膜表面との
間には、透明層が形成されていてもよい。透明層のλ＝
４５０〜８００nmでのｎおよびｋは、ｎ＝１．０〜３．
０、ｋ＝０．００１〜２．０程度であることが好まし
く、その膜厚は通常２〜５００nm程度である。Although such a color tone control film may be directly formed on the surface of the reflection film, a transparent layer may be formed between the color tone control film and the surface of the reflection film. Λ of transparent layer =
N and k at 450-800 nm are n = 1.0-3.
0, k is preferably about 0.001 to 2.0, and the film thickness is usually about 2 to 500 nm.
【００１１】色調制御膜の形成は、通常、蒸着、スパッ
タ等の各種気相成膜法に従うが、この際、色調制御膜側
の反射率スペクトルが所定のプロファイルをもつように
その膜厚を制御する。この反射率スペクトルのプロファ
イルにおいては、波長λ＝４５０〜８００nmにおける反
射率Ｒが重要である。この波長範囲のＲを所定範囲に制
御することによって、見た者に種々の色調を呈すること
ができるからである。例えば、金色の場合λ＝４５０〜
８００nmにおけるＲ（％）は、図１中（λ，Ｒ）にて、
点Ａ（４５０，０）、Ｂ（４５０，４５）、Ｃ（５５
０，１００）、Ｄ（８００，１００）、Ｆ（８００，８
０）、Ｆ（６００，８０）およびＡを順に結ぶ直線上、
およびその直線で囲まれた範囲内に存在しなければなら
ない。なお、４５０nm未満および８００nm超のλにおけ
るＲについては制限がないことが確認されている。ま
た、図１中には、２４金（６−９以上）の２００nmのス
パッタ膜の反射率スペクトルが示される。この出願の発
明で必要とする反射率スペクトルプロファイルは、実際
の金の反射率スペクトルときわめて類似したものであ
る。この出願の発明によれば、銀の反射膜上に、その膜
厚を制御して、所定波長域にて設定色調類似反射スペク
トルを示す反射制御層である色調制御膜を設けさえすれ
ば、所定の色調を得ることができる。なお、反射制御層
の形成は常法に従えばよい。The color control film is usually formed by various vapor deposition methods such as vapor deposition and sputtering. At this time, the film thickness is controlled so that the reflectance spectrum on the color control film side has a predetermined profile. To do. In the profile of this reflectance spectrum, the reflectance R at the wavelength λ = 450 to 800 nm is important. This is because by controlling R in this wavelength range to a predetermined range, it is possible to give the viewer various color tones. For example, in the case of gold, λ = 450-
R (%) at 800 nm is (λ, R) in FIG.
Points A (450,0), B (450,45), C (55
0,100), D (800,100), F (800,8)
0), F (600,80), and A on a straight line,
And must be within the range enclosed by the line. It has been confirmed that there is no limitation on R at λ less than 450 nm and more than 800 nm. Further, FIG. 1 shows the reflectance spectrum of a 200 nm sputtered film of 24 gold (6-9 or more). The reflectance spectrum profile required by the invention of this application is very similar to the reflectance spectrum of actual gold. According to the invention of this application, if the film thickness is controlled on the silver reflection film and a color tone control film that is a reflection control layer exhibiting a set color tone similar reflection spectrum in a predetermined wavelength range is provided, The color tone of can be obtained. The reflection control layer may be formed by a conventional method.
【００１２】このような色調制御膜の上には、ほぼ透明
な各種保護層が設けられていてもよい。On such a color tone controlling film, various transparent protective layers may be provided.
【００１３】[0013]
【実施例】以下、本発明の具体的実施例を示し、本発明
をさらに詳細に説明する。EXAMPLES The present invention will be described in more detail below by showing specific examples of the present invention.
【００１４】実施例１ ポリカーボネート基板上に、以下の条件で厚さ１００nm
のＡｇスパッタ膜を形成した。Example 1 A 100 nm thick film was formed on a polycarbonate substrate under the following conditions.
Of Ag sputtered film was formed.
【００１５】ターゲット：Ａｇ（純度９５atm%） 投入電力：１ｋＷ ＲＦ 真空度：０．６４Ｐａ ガス種：Ａｒ ガス流量：４０ｓｃｃｍ スパッタ時間：２４０ｓｅｃTarget: Ag (purity: 95 atm%) Input power: 1 kW RF Vacuum degree: 0.64 Pa Gas type: Ar Gas flow rate: 40 sccm Sputtering time: 240 sec
【００１６】以上の条件で、ポリカーボネート基板上に
厚さ１００nmのＡｇ反射膜を得た。Under the above conditions, a 100 nm thick Ag reflective film was obtained on a polycarbonate substrate.
【００１７】次いで、以下の条件で、上記反射膜上に厚
さ２０nmのＳｉスパッタ膜を形成した。Then, a 20-nm-thick Si sputtered film was formed on the reflective film under the following conditions.
【００１８】ターゲット：Ｓｉ（Ｂドーピングしたも
の） 投入電力：１ｋＷ ＤＣ 真空度：０．２Ｐａ ガス種：Ａｒ ガス流量：１００ｓｃｃｍ スパッタ時間：２００ｓｅｃTarget: Si (B-doped) Input power: 1 kW DC Vacuum degree: 0.2 Pa Gas type: Ar Gas flow rate: 100 sccm Sputtering time: 200 sec
【００１９】以上により、反射膜上に厚さ２０nmのＳｉ
色調制御膜を形成した。色調制御膜は、Ｘ線分析によ
り、Ｓｉのアモルファス膜であることが確認され、看者
にブルーの色調を呈した。その反射スペクトルを図２に
示した。As described above, Si having a thickness of 20 nm is formed on the reflective film.
A color tone control film was formed. It was confirmed by X-ray analysis that the color tone control film was an amorphous film of Si, and the viewer exhibited a blue color tone. The reflection spectrum is shown in FIG.
【００２０】実施例２ 実施例１で作製したＡｇ反射膜上に、以下の条件で、厚
さ４０nmのＳｉＮスパッタ膜を形成した。Example 2 A SiN sputtered film having a thickness of 40 nm was formed on the Ag reflective film produced in Example 1 under the following conditions.
【００２１】ターゲット：Ｓｉ 投入電力：３００Ｗ ＲＦ 真空度：０．８Ｐａ ガス種：Ａｒ＋Ｎ2 混合ガス ガス流量：Ａｒ １８ｓｃｃｍ Ｎ2 ２ｓｃｃｍ スパッタ時間：４００ｓｅｃTarget: Si Input power: 300 W RF Vacuum degree: 0.8 Pa Gas type: Ar + N 2 mixed gas Gas flow rate: Ar 18 sccm N 2 2 sccm Sputtering time: 400 sec
【００２２】以上により、反射膜上に厚さ４０nmのＳｉ
Ｎ色調制御膜を形成した。色調制御膜は、オージェ分析
により、膜中にＮが検出され、看者にピンクの色調を呈
した。その反射スペクトルを図３に示した。As described above, Si having a thickness of 40 nm is formed on the reflective film.
An N color tone control film was formed. In the color tone control film, N was detected in the film by Auger analysis, and the viewer exhibited a pink color tone. The reflection spectrum is shown in FIG.
【００２３】実施例３ 実施例１で作製したＡｇ反射膜上に、以下の条件で、厚
さ１６０nmのＳｉＯスパッタ膜を形成した。Example 3 An SiO sputtered film having a thickness of 160 nm was formed on the Ag reflective film produced in Example 1 under the following conditions.
【００２４】ターゲット：ＳｉＯ 投入電力：３００Ｗ ＲＦ 真空度：０．５Ｐａ ガス種：Ａｒ ガス流量：１０ｓｃｃｍ スパッタ時間：５２０ｓｅｃTarget: SiO 2 Input power: 300 W RF Vacuum degree: 0.5 Pa Gas type: Ar Gas flow rate: 10 sccm Sputtering time: 520 sec
【００２５】以上により、反射膜上に厚さ１６０nmのＳ
ｉＯ色調制御膜を形成した。色調制御膜は、看者に金色
の色調を呈した。その反射スペクトルを図４に示した。As described above, the S film having a thickness of 160 nm is formed on the reflective film.
An iO color tone control film was formed. The color tone control film gave the viewer a golden color tone. The reflection spectrum is shown in FIG.
【００２６】実施例４ 実施例１で作製したＡｇ反射膜上に、以下の条件で、厚
さ７．５nmＳｉスパッタ膜を形成した。Example 4 A 7.5 nm-thick Si sputtered film was formed on the Ag reflective film produced in Example 1 under the following conditions.
【００２７】ターゲット：Ｓｉ（Ｂドーピングしたも
の） 投入電力：１ｋＷ ＤＣ 真空度：０．２Ｐａ ガス種：Ａｒ ガス流量：１００ｓｃｃｍ スパッタ時間：７５ｓｅｃTarget: Si (B-doped) Input power: 1 kW DC Vacuum degree: 0.2 Pa Gas type: Ar Gas flow rate: 100 sccm Sputtering time: 75 sec
【００２８】以上により、反射膜上に厚さ１５nmのＳｉ
色調制御膜を形成した。色調制御膜は、Ｘ線分析によ
り、Ｓｉのアモルファス膜であることが確認され、看者
に金色の色調を呈した。その反射スペクトルを図５に示
した。From the above, a 15 nm thick Si film is formed on the reflective film.
A color tone control film was formed. It was confirmed by X-ray analysis that the color tone control film was an amorphous film of Si, and the viewer exhibited a golden color tone. The reflection spectrum is shown in FIG.
【００２９】実施例５ 実施例１で作製したＡｇ反射膜上に、以下の条件で、厚
さ１５nmＳｉスパッタ膜を形成した。Example 5 A 15 nm-thick Si sputtered film was formed on the Ag reflective film produced in Example 1 under the following conditions.
【００３０】ターゲット：Ｓｉ（Ｂドーピングしたも
の） 投入電力：１ｋＷ ＤＣ 真空度：０．２Ｐａ ガス種：Ａｒ ガス流量：１００ｓｃｃｍ スパッタ時間：１５０ｓｅｃTarget: Si (B-doped) Input power: 1 kW DC Vacuum degree: 0.2 Pa Gas type: Ar Gas flow rate: 100 sccm Sputtering time: 150 sec
【００３１】以上により、反射膜上に厚さ７．５nmのＳ
ｉ色調制御膜を形成した。色調制御膜は、Ｘ線分析によ
り、Ｓｉのアモルファス膜であることが確認され、看者
にルビー色の色調を呈した。その反射スペクトルを図６
に示した。As described above, S of 7.5 nm in thickness is formed on the reflective film.
An i color tone control film was formed. It was confirmed by X-ray analysis that the color tone control film was an amorphous film of Si, and the viewer exhibited a ruby color tone. The reflection spectrum is shown in FIG.
It was shown to.
【００３２】実施例６ 実施例１で作製したＡｇ反射膜上に、以下の条件で、厚
さ３０nmのＳｉＮスパッタ膜を形成した。Example 6 A 30 nm thick SiN sputtered film was formed on the Ag reflective film produced in Example 1 under the following conditions.
【００３３】ターゲット：Ｓｉ 投入電力：３００Ｗ ＲＦ 真空度：０．８Ｐａ ガス種：Ａｒ＋Ｎ2 混合ガス ガス流量：Ａｒ １８ｓｃｃｍ Ｎ2 ２ｓｃｃｍ スパッタ時間：３００ｓｅｃTarget: Si Input power: 300 W RF Vacuum degree: 0.8 Pa Gas type: Ar + N 2 mixed gas Gas flow rate: Ar 18 sccm N 2 2 sccm Sputtering time: 300 sec
【００３４】以上により、反射膜上に厚さ３０nmのＳｉ
Ｎ色調制御膜を形成した。色調制御膜は、オージェ分析
により、膜中にＮが検出され、看者に金色の色調を呈し
た。その反射スペクトルを図７に示した。As described above, Si having a thickness of 30 nm is formed on the reflective film.
An N color tone control film was formed. In the color tone control film, N was detected in the film by Auger analysis, and the viewer exhibited a golden color tone. The reflection spectrum is shown in FIG.
【００３５】[0035]
【発明の効果】反射膜を画一的にＡｇ膜で形成しても、
Ｓｉを主体とする色調制御膜を設けることにより、光記
録媒体は種々の色を呈することができる。[Effect of the Invention] Even if the reflective film is uniformly formed of an Ag film,
By providing a color tone control film mainly containing Si, the optical recording medium can exhibit various colors.
【図１】金色を呈する反射スペクトルのプロファイルに
必要な条件を説明するためのグラフである。FIG. 1 is a graph for explaining conditions necessary for a profile of a reflection spectrum that exhibits a gold color.
【図２】本発明の実施例１の光記録媒体の反射スペクト
ルである。FIG. 2 is a reflection spectrum of the optical recording medium of Example 1 of the present invention.
【図３】本発明の実施例２の光記録媒体の反射スペクト
ルである。FIG. 3 is a reflection spectrum of the optical recording medium of Example 2 of the present invention.
【図４】本発明の実施例３の光記録媒体の反射スペクト
ルである。FIG. 4 is a reflection spectrum of the optical recording medium of Example 3 of the present invention.
【図５】本発明の実施例４の光記録媒体の反射スペクト
ルである。FIG. 5 is a reflection spectrum of the optical recording medium of Example 4 of the present invention.
【図６】本発明の実施例５の光記録媒体の反射スペクト
ルである。FIG. 6 is a reflection spectrum of the optical recording medium of Example 5 of the present invention.
【図７】本発明の実施例６の光記録媒体の反射スペクト
ルである。FIG. 7 is a reflection spectrum of the optical recording medium of Example 6 of the present invention.
─────────────────────────────────────────────────────
─────────────────────────────────────────────────── ───
【手続補正書】[Procedure amendment]
【提出日】平成５年２月３日[Submission date] February 3, 1993
【手続補正１】[Procedure Amendment 1]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００１２[Correction target item name] 0012
【補正方法】変更[Correction method] Change
【補正内容】[Correction content]
【００１２】このような色調制御膜の上には、ほぼ透明
な各種保護層が設けられていてもよい。あるいは酸化に
よる反射制御層の屈折率変化を防ぐために、制御層の上
下両方、あるいは一方を制御層と同様の材料の酸化物、
窒化物の層によって保護しても良い。On such a color tone controlling film, various transparent protective layers may be provided. Alternatively, in order to prevent a change in the refractive index of the reflection control layer due to oxidation, the upper and lower sides of the control layer, or one of the oxides of the same material as the control layer
It may be protected by a layer of nitride.
フロントページの続き (72)発明者 川島 康 東京都中央区日本橋一丁目13番１号 ティ ーディーケイ株式会社内Front Page Continuation (72) Inventor Yasushi Kawashima 1-13-1 Nihonbashi, Chuo-ku, Tokyo TDC Corporation
Claims (10)
み出す光記録媒体において、銀を主体とする反射膜を有
し、該反射膜上に、Ｓｉを主体とする色調制御膜を設け
たことを特徴とする光記録媒体。1. An optical recording medium for reading a record by reflection using a laser beam, having a reflective film mainly composed of silver, and a color tone control film mainly composed of Si provided on the reflective film. An optical recording medium characterized by:
ある請求項１の光記録媒体。2. The optical recording medium according to claim 1, wherein the silver content of the reflective film is 60 atm% or more.
m%以上である請求項１または２の光記録媒体。3. The content ratio of Si of the color tone control film is 40 at
The optical recording medium according to claim 1, which has a content of m% or more.
と、虚部ｋとが、可視光領域において０．５≦ｎ≦５．
０、 ０．００１≦ｋ≦５．０であり、前記反射制御層
の厚さｔが、４nm≦ｔ≦５００nmである請求項１〜３の
いずれかの光記録媒体。4. The real part n of the complex optical constant of the color tone control film.
And imaginary part k are 0.5 ≦ n ≦ 5.
4. The optical recording medium according to claim 1, wherein 0, 0.001 ≦ k ≦ 5.0, and the thickness t of the reflection control layer is 4 nm ≦ t ≦ 500 nm.
保護層を有する請求項１〜４のいずれかの光記録媒体。5. The optical recording medium according to claim 1, further comprising a substantially transparent protective layer on the color tone control film.
み出す光記録媒体の製造方法において、銀を主体とする
反射膜を形成する工程、および該反射膜上に、Ｓｉを主
体とする色調制御膜を形成する工程を有し、色調制御膜
の形成工程において、その材料組成および膜厚の少なく
とも一方を変えることによって、呈する色調を変化させ
ることを特徴とする光記録媒体の製造方法。6. A method of manufacturing an optical recording medium for reading a record by reflection using a laser beam, the step of forming a reflective film mainly composed of silver, and the color tone control mainly composed of Si on the reflective film. A method of manufacturing an optical recording medium, which comprises a step of forming a film, wherein the color tone to be exhibited is changed by changing at least one of the material composition and the film thickness in the step of forming the color tone control film.
ある請求項６の光記録媒体の製造方法。7. The method of manufacturing an optical recording medium according to claim 6, wherein the silver content of the reflective film is 60 atm% or more.
m%以上である請求項６または７の光記録媒体。8. The content ratio of Si of the color tone control film is 40 at
The optical recording medium according to claim 6, which has a content of m% or more.
と、虚部ｋとが可視光領域において０．５≦ｎ≦５．
０，０．００１≦ｋ≦５．０であり、前記反射制御層の
厚さｔが、４nm≦ｔ≦５００nmである請求項６〜８のい
ずれかの光記録媒体の製造方法。9. The real part n of the complex optical constant of the reflection control layer
And imaginary part k are 0.5 ≦ n ≦ 5.
9. The method of manufacturing an optical recording medium according to claim 6, wherein 0.001 ≦ k ≦ 5.0, and the thickness t of the reflection control layer is 4 nm ≦ t ≦ 500 nm.
の保護層を設ける請求項６〜９のいずれかの光記録媒体
の製造方法。10. The method of manufacturing an optical recording medium according to claim 6, further comprising providing a substantially transparent protective layer on the reflection control layer.