JPH06332187A - Image forming material - Google Patents

Abstract

(57) [Summary] [Object] It is an object of the present invention to provide an image forming material capable of obtaining a transfer material similar to a printed material as a prepress proof for color proofing. [Structure] A photosensitive layer containing a colorant is formed on a support, and a protective film is further provided on the photosensitive layer. Imagewise exposure is performed to transfer exposed and unexposed areas of the photosensitive layer. In an image-forming material that transfers an image to an image receptor such as paper due to the difference in adhesiveness, the photosensitive layer contains 0.01 to 5% by weight of a colorant and particles as a solid content of a mixture of a methacryloyl group-containing silicone and an acrylic oligomer. An image-forming material comprising an extender pigment having a diameter of 0.001 to 10 μm in an amount of 5 to 50% by weight of a colorant. [Effect] The image-forming material of the present invention does not cause blocking due to heat, and does not prevent transfer of the image-forming material for the second and subsequent colors even when superimposing multiple colors. It also enables the formation of matte images that take advantage of the characteristics of matte coated paper.

Description

Detailed Description of the Invention

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an image forming material. More specifically, it is an image-forming material by superposing a single color or multiple colors by utilizing the difference in adhesiveness between the exposed and unexposed areas of the photosensitive layer, and obtains a transfer similar to a print as a prepress proof for color proofing. The present invention relates to an image forming material that can be used.

[0002]

2. Description of the Related Art Conventionally, it is known in the field of printing industry to use a prepress proof as a means for confirming the finish, color tone and the like of a finally printed printed matter before printing. This prepress proof has an overlay method and a surprint method, and is properly used depending on the image quality finally obtained and the purpose of use in plate making and printing processes. In the overlay method, a transparent base film is provided with a photosensitive layer containing a color material corresponding to a color separation mask, the film and the mask are brought into close contact with each other, exposed, and developed, and the respective films are superposed. And calibrate.

Unlike the overlay method, the surprint method has a high utility value because it can obtain a hard copy. For example, as disclosed in US Pat. Nos. 3060023, 3060024 and 3060025. In this method, a photopolymer photosensitive layer consisting of several layers is laminated on a single support to sequentially form color separation images. In addition, JP-A-59-97410,
There is also a prepress proof as described in JP-A-61-1885377, which can be used in both the overlay method and the surprint method. This method is used when you want to check simple characters etc. according to the purpose of use.
The versatility is great in that if you want to obtain a hard copy for checking a subtle color portion such as a picture by checking only with the valley, you can transfer this to the transfer target. However, there is a drawback that the working environment is deteriorated because a developing process using an organic solvent is required.

On the other hand, the inventors of the present invention formed a photosensitive layer containing a dye and / or a pigment on a transparent support, and exposed the image to give a tackiness in transferring exposed and unexposed areas of the photosensitive layer. The prepress pull obtained by transferring the image to the image receptor by cohesive failure of the photosensitive layer between the roll nips using an image forming material that transfers the image to the image receptor such as paper. Unlike conventional prepress proofs, there is no layer such as an adhesive layer between the material to be printed and the image forming material, so that the image and texture very similar to the actual printed matter can be reproduced. Has already found.

These image-forming materials are usually composed of a transparent support, a photosensitive layer containing a dye and / or a pigment, and a protective film. When the image forming material is used, the transparent support and the image surface of the mask original plate are brought into close contact with each other, and image exposure is performed from the mask side.
Then, the protective film is removed, and the photosensitive layer and the image receptor are transferred while applying heat and pressure between the nip rolls. However, after imagewise exposure to cause a difference in adhesiveness between the exposed and unexposed areas of the photosensitive layer,
When the protective film is peeled off from the photosensitive layer, the image-forming material is heated by the radiation from the preheated image receptor, and a part of the unexposed portion of the photosensitive layer is transferred to the protective film. Since the so-called blocking occurs, a part of the unexposed portion that should be transferred is not transferred, and the image may not be faithfully reproduced as the original.

In order to prevent blocking by heat, it is important that the surface tension of the photosensitive layer does not change with heat. It is well known that a silicone compound or a low-molecular wax is generally added to lower the surface tension. When a silicone compound or wax is blended in the photosensitive layer, it partially floats on the surface, so blocking can be prevented. However, when the silicone compound and waxes are compounded in the photosensitive layer, they partially come out on the surface of the photosensitive layer after curing of the photosensitive layer after transfer. Moreover, not only the unexposed portion of the photosensitive layer, that is, the transfer portion, but also the surface of the photosensitive layer cured by light is exposed. Therefore, when the photosensitive layer of another color which has been image-exposed with another original is transferred after the transfer and the post-exposure to the image receptor, the silicone compound is partially or wholly transferred on the transfer surface at the first transfer. The surface tension of the image receptor is partly too low and the photosensitive layer of the next color cannot be transferred because the wax and wax are partly scooped or transferred. In this way, blocking and transferability have the opposite property, and it is difficult to design the photosensitive layer formulation.

Further, such an image forming material forms an image with high glossiness when transferred to smooth paper such as art-coated paper, but in printed matter, such fields are required only in such glossiness. Instead, so-called matte images, which are rather dull, are in great demand. In order to obtain a matte image, so-called matte coated paper having a smooth surface is used. However, in the method of forming an image by transferring the photosensitive layer, even if matte coated paper is used, the transfer surface is flattened by the action of the roll for transferring the photosensitive layer and the matte feeling of the paper disappears. It Moreover, since a plurality of images of different colors are transferred to form an image, the flattening of the transfer surface becomes remarkable as the colors overlap.

[0008]

The inventors of the present invention have made diligent studies to solve the above-mentioned problems and found that the photosensitive layer contains a photoreactive silicone composition and an extender pigment having a specific particle size. As a result, blocking due to heat is prevented, and the silicone compound in the portion cured by light does not migrate to the surface of the photosensitive layer even by heat, and further, a matte feeling can be retained on the transfer surface of the photosensitive layer even when color overlapping is performed. After discovering this, the present invention has been completed. Even if the photosensitive layer contains an extender pigment, blocking and partial repelling at the time of transfer do not occur by using the above photoreactive silicone composition.

[0009]

According to the present invention, a photosensitive layer containing a colorant is formed on a support, and a protective film is further provided on the photosensitive layer. In an image-forming material that transfers an image to an image receptor such as paper due to the difference in adhesiveness between the exposed and unexposed areas of the layer, the photosensitive layer contains a mixture of a methacryloyl group-containing silicone and an acrylic oligomer as a solid content. The present invention also provides an image forming material containing 0.01 to 5% by weight of a colorant and 5 to 50% by weight of an extender pigment having a particle size of 0.001 to 10 μm.

As the support, a material which is stable to heat, chemicals, light and the like and which sufficiently transmits actinic rays is preferable. For example, cellulose acetate, polystyrene, polyvinyl chloride, polyethylene terephthalate,
Examples of the film or sheet include polycarbonate and polypropylene, and polyethylene terephthalate is particularly preferable in terms of transparency, thermal stability, dimensional stability, and the like.

The photosensitive layer is a mixture of methacryloyl group-containing silicone and acrylic oligomer and has a particle size of 0.0
A layer having a thickness of 1 to 5 μm, which is composed of 01 to 10 μm extender pigment and (a) a photopolymerizable compound and a colorant (b) a photopolymerizable compound, a thermoplastic resin and a colorant, etc. A photopolymerization initiator, a photosensitizer, a thermal polymerization inhibitor, a resin plasticizer, a pigment dispersant, etc. may be used together. The mixture of the methacryloyl group-containing silicone and the acrylic oligomer is contained as solids in an amount of 0.01 to 5% by weight of the colorant.
If the content of the above mixture is less than 0.01% by weight of the colorant, blocking cannot be sufficiently prevented. Also, 5
If it exceeds the weight%, an adequate adhesion with the protective film cannot be obtained, and the gloss may increase after the image is transferred.

A mixture of a methacryloyl group-containing silicone and an acrylic oligomer has a methacryloyl group of 2
It is preferable that each of the silicone having one methacryloyl group and the acrylic oligomer be contained in an amount of 0.1 to 10 parts by weight per 1 part by weight of the silicone having one or more silicones. As the acrylic oligomer, one or more kinds of pentaerythritol triacrylate oligomer, ethylene glycol diacrylate oligomer, diethylene glycol diacrylate oligomer, trimethylolpropane triacrylate oligomer, etc. having a molecular weight of 500 to 2000 are used. The above mixture has good compatibility with the photopolymerizable compound and uniformly forms the coated surface of the photosensitive layer. Further, the above-mentioned mixture has a function of lowering the surface tension of the photosensitive layer, but when cured by light, it does not migrate to the surface of the photosensitive layer by heat.

The particle size is 0.001 to 10 μm, preferably 0.05 to 1
Mu extender pigments include silicon dioxide, barium sulfate, talc,
It is a so-called matting agent such as mica and calcium carbonate, and is used in the range of 5 to 50% by weight of the colorant. If the content of the extender pigment is less than 5% by weight of the colorant, the matting effect is small, and if it is more than 50%, the difference in the image density and the texture from the printed matter becomes remarkable. The extender pigment is used by being dispersed together with the resin or the photopolymerizable compound together with the colorant, but in the dispersion, it is necessary to adjust so as not to cause overdispersion. For example, it is preferable to prepare a coating liquid in which the pigment is well dispersed and then disperse the extender pigment with a stirrer such as a disper to adjust the coating liquid.

As the photopolymerizable compound, a monomer having an ethylenically unsaturated double bond, a prepolymer or the like can be used, but a compound capable of plasticizing a thermoplastic resin at room temperature is preferable. Typical compounds include 2-hydroxyethyl (meth) acrylate, ethylene glycol diacrylate, diethylene glycol diacrylate, 1,
6-hexanediol di (meth) acrylate, trimethylolpropane triacrylate, pentaerythritol triacrylate, dipentaerythritol hexaacrylate, etc. can be mentioned. These photopolymerizable compounds can be used alone or, if necessary, in combination of two or more. Good.

As the thermoplastic resin, it is possible to use a resin which is thermoplastic and has excellent compatibility with a photopolymerizable compound and which does not have photopolymerizability. For example, polyvinyl chloride, poly (meth)
Acrylic ester, epoxy resin, polyurethane resin, cellulose derivative (eg, ethyl cellulose, cellulose acetate, nitrocellulose), vinyl chloride-vinyl acetate copolymer, polyamide resin, polyvinyl acetal resin, diallyl phthalate resin, butadiene-acrylonitrile copolymer Synthetic rubbers such as the above are listed, and one or more of these thermoplastic resins are used according to the required physical properties.

As the photopolymerization initiator, those which have little absorption in the visible light region and those which have good compatibility with the photopolymerizable compound are preferable, and examples thereof include benzophenone, benzoin ethyl ether, benzyl dimethyl ketal, and azobisiso. Butyronitrile, 2-chlorothiozanzone, 2-methylthiozanzone, 2-ethylthiozanzone, 2-isopropylthiozanzone, 4'-isopropyl-2-hydroxy-2-
Methyl propiophenone and the like can be mentioned. In addition, a photosensitizer may be used in combination in order to increase the photopolymerization initiation efficiency. As the photosensitizer, an aromatic-fatty acid tertiary amine or the like can be used, and examples thereof include 4,4′-bisdiethylaminobenzophenone. Since the photosensitizer may turn yellow, it is selected in consideration of acceleration efficiency, yellowing, compatibility with the initiator, energy of the actinic ray to be used, and wavelength range.

Further, a thermal polymerization inhibitor may be used to suppress radicals for photopolymerization. When using a thermal polymerization inhibitor, what is important is the amount added and compatibility, and the amount must be such that it does not interfere with the generation of radicals for photopolymerization and that the radicals are thermally suppressed. Generally, aromatic derivatives such as hydroquinone, p-methoxyphenol, t-butylcatechol, and pyrogallol are used, but compounds other than aromatic compounds may be used in combination. As the colorant applied to the photosensitive layer, conventionally used dyes and pigments such as organic pigments, dyes and carbon black can be used. It is also possible to mix several dyes and pigments in order to obtain the required hue. The pigment or dye added to the photosensitive layer is preferably 5 to 45% by weight of the total solid content, more preferably 9 to 17% by weight.

The protective film may be composed of a single layer or a plurality of layers, but the surface in contact with the photosensitive layer has few fish eyes and has good releasability from the photosensitive layer, and is unnecessary. It is preferable that the plasticizer does not precipitate. Further, the protective film may be provided with a layer having a gas barrier property. The layer having a gas barrier property may or may not be in direct contact with the photosensitive layer. Examples of the compound used in the layer having a gas barrier property include polymer compounds such as polyvinyl alcohol (PVA) and ethylene vinyl alcohol (EvOH). Further, for the purpose of ensuring the rigidity of the image forming material, the protective film may be lined with another strong material on the surface which does not come into direct contact with the photosensitive layer. The material to be lined at this time is not particularly limited.

As such a protective film, a rigid sheet or film of polyethylene terephthalate, biaxially oriented polypropylene, high density polyethylene, etc., one or more of which are bonded with an adhesive, or as much as possible Thin high density polyethylene, medium density polyethylene, polystyrene, polypropylene, cellulose acetate, etc. with gas barrier properties and rigidity,
For example, polyethylene terephthalate or the like may be attached with an adhesive.

As a receptor for transferring and forming an image, a conventionally known printing paper is used, but it is preferable to use a paper having a rough surface called a matte coated paper.
In the present invention, the mat-coated paper of the grade called spur art (gloss), (dull), (mat), art (gloss), (dull), coat (gloss), (dull) is particularly targeted. Specifically, NK Whitelandal,
Examples of such products include NK matte color (white), NK Espel (manufactured by Nippon Specialty Paper Co., Ltd.), satin Kinfuji, New Age (manufactured by Kanzaki Paper Co., Ltd.), and Ulite (manufactured by Sanyo Kokusaku Pulp Co., Ltd.). Their average surface roughness is 1.5 to 5 μ. In the present invention, it is preferable to transfer at a temperature of 95 to 135 ° C. at a speed of 0.1 to 5 m / min in order to generate a matte feeling on such a rough surface.

[0021]

EXAMPLES The present invention will be described in more detail below with reference to examples, but the present invention is not limited thereto. In the examples, “part” means “part by weight” and “%” means “% by weight”. [Example 1] A dispersion liquid having the following composition was dispersed in a sand mill for 2 hours and then filtered through a 1-micron filter to prepare a coating liquid for a photosensitive layer. Diallyl isophthalate prepolymer (manufactured by Daiso) 11.40 parts Kayarad DPHA (manufactured by Nippon Kayaku Co., Ltd.) 7.10 parts Kayarad TPGDA (manufactured by Nippon Kayaku Co., Ltd.) 0.90 part Irgacure 907 (manufactured by Nippon Ciba Geigy) 1.20 parts Kayacure DETX-S (Nippon Kayaku Co., Ltd.) 0.60 part Irgacure 369 (Nippon Ciba Geigy Co., Ltd.) 0.20 part Solspers 24000 (ICI Japan Co., Ltd.) 0.10 part Methacryloyl group-containing mixed solution of silicone and acrylic oligomer 0.20 part ( Silicone having 2 methacryloyl groups / Silicone having 1 methacryloyl group / Pentaerythritol triacrylate oligomer (molecular weight 800) = 1 part / 1 part / 2 parts toluene / xylene solution, NV10%) Aerosil 300 (Japan Aerosil Co., Ltd.) 0.25 parts MA 7 (manufactured by Mitsubishi Chemical Industries, Ltd.) 2.50 parts R-51 (manufactured by Hoechst Japan) 0.80 parts of P- methoxyphenol (manufactured by Tokyo Kasei Kogyo Co., Ltd.) 0.18 parts Methyl ethyl ketone 75.00 parts

On the 12 μm transparent support (Q-21 made by Toray), the photosensitive layer coating solution is applied and dried to form a 2.3 μm photosensitive layer, and a protective film (100 μOPP film). Was laminated with a laminator so as to be in contact with the photosensitive layer to obtain an image forming material (black sheet). Adhere the transparent support side of the image forming material and the silver salt side of the original positive mask,
50mj with UV printer (HMW-201KB manufactured by Oak Manufacturing Co., Ltd.)
The actinic radiation of / cm ² was given. Next, the image forming material and the original positive mask are peeled off, the protective film is peeled off, and the matte coated paper (Matt Color White manufactured by Nippon Special Paper Co., Ltd.) and the photosensitive layer surface are brought into close contact with each other, and the first laminator (Taisei Laminator). Pressure 6 using the 8B-700 special type manufactured by the company
When transferred at the nip between rollers under the conditions of kg / cm ² , passing speed 35 cm / min, roller surface temperature 90 ° C, the unexposed area's photosensitive layer (thickness: 2.3μ) is transferred, which gives a normal printed matter and texture. A completely unchanged transcript was obtained. Also,
The image-forming material was stored in a thermostat at 25 ° C for 1 month, and was transferred by image exposure under the same exposure conditions. When the protective film was peeled off, blocking did not occur at all, and a transfer product that was the same as one month ago was obtained. I was able to get it.

Example 2 A cyan photosensitive layer coating solution having the following composition was prepared in the same manner as in Example 1. Diallyl isophthalate prepolymer (manufactured by Daiso) 11.81 parts Kayarad DPHA (manufactured by Nippon Kayaku Co., Ltd.) 7.49 parts Kayarad TPGDA (manufactured by Nippon Kayaku Co., Ltd.) 0.78 parts Illukagua 907 (manufactured by Ciba-Gaigi Co.) 1.19 parts Kayacure DETX-S (Japan) Kayaku Co., Ltd.) 0.57 parts Ilkagua 369 (Ciba-Gaigi Co., Ltd.) 0.04 parts Rionol Blue FG7330 (Toyo Ink Mfg. Co., Ltd.) 3.12 parts Mixed solution of methacryloyl group-containing silicone and acrylic oligomer 0.22 parts (has two methacryloyl groups) Silicone / Pentaerythritol triacrylate oligomer having one methacryloyl group (molecular weight 1000) = 1 part / 2 parts / 1 part mixture of toluene and xylene, NV10%) Aerosil R974 (Nippon Aerosil Co., Ltd.) 0.25 part Methyl ethyl ketone 75.00

A yellow color photosensitive layer coating solution having the following composition was prepared in the same manner as in Example 1. Diallyl isophthalate prepolymer (manufactured by Daiso) 11.81 parts Kayarad DPHA (manufactured by Nippon Kayaku Co., Ltd.) 7.49 parts Kayarad TPGDA (manufactured by Nippon Kayaku Co., Ltd.) 0.78 parts Illukagua 907 (manufactured by Ciba-Gaigi Co.) 1.19 parts Kayacure DETX-S (Japan) Kayaku Co., Ltd.) 0.54 parts Irukagua 369 (Ciba-Gaigi Co., Ltd.) 0.04 parts Lionol Yellow FG1310 (Toyo Ink Mfg. Co., Ltd.) 3.12 parts Mixed solution of methacryloyl group-containing silicone and acrylic oligomer 0.39 parts (has two methacryloyl groups) Silicone / Pentaerythritol triacrylate oligomer having one methacryloyl group (molecular weight 800) = toluene / xylene solution of a mixture of 2 parts / 1 part / 2 parts, NV10%) Syloid 244 (manufactured by Fuji Devison Chemical Co., Ltd.) 0.30 Part Methyl ethyl ketone 75. 00 copies

A magenta color photosensitive layer coating liquid having the following composition was prepared in the same manner as in Example 1. Diallyl isophthalate prepolymer (manufactured by Daiso) 11.81 parts Kayarad DPHA (manufactured by Nippon Kayaku Co., Ltd.) 7.49 parts Kayarad TPGDA (manufactured by Nippon Kayaku Co., Ltd.) 0.78 parts Illukagua 907 (manufactured by Ciba-Gaigi Co.) 1.19 parts Kayacure DETX-S (Japan) Kayaku Co., Ltd.) 0.57 parts Ilukagua 369 (Ciba-Gaigi Co., Ltd.) 0.04 parts Lionol Red Carmine 6BFG4200 (Toyo Ink Mfg. Co., Ltd.) 3.10 parts Mixed solution of methacryloyl group-containing silicone and acrylic oligomer 0.24 parts (two methacryloyl groups) Having silicone / methacryloyl group-containing silicone / pentaerythritol triacrylate oligomer (molecular weight 1200) = 2 parts / 1 part / 2 parts toluene / xylene solution, NV 10%) Aerosil TT (Nippon Aerosil Co., Ltd.) 0.30 Part methyl ethyl keto 75.00 parts

On a support (polyethylene terephthalate sheet) having a thickness of 12 μm, the coating solution for the photosensitive layer was dried to form a coating film of 2.2.
It was applied to have a thickness of μm, and the solvent component was volatilized by drying. Next, a protective film made by laminating 8 μm polypropylene and 100 μm polyethylene terephthalate (T-60 manufactured by Toray) with a 5 μm thick adhesive (Adcote 329A / 329B = 1/1 manufactured by Toyo Morton) is laminated. Then, image forming materials (cyan sheet, yellow sheet and magenta sheet) were obtained.

The transparent support side of each image-forming material and the silver salt surface of the original positive mask were brought into close contact with each other, and an actinic ray of 20 mj / cm ² was applied by a UV printer (HMW-201KB manufactured by Oak Manufacturing Co., Ltd.). Then, the image forming material and the original positive mask are peeled off, the protective film is further peeled off, the matte coated paper (Nippon Special Processing Paper Co., Ltd. Espel) and the image forming material are brought into close contact, and the first laminator (Taisei Laminator 8B- 7
00 special type) pressure 7kg / cm ² , passing speed 35cm / min,
When the transfer was performed at the roller surface temperature of 100 ° C by the nip between the rollers, the unexposed areas of the photosensitive layer (thickness
2.2 μ) was transferred, and a single-color transfer product was obtained in which the texture was completely the same as that of a normal matt print product.

On the other hand, the black sheet transfer material obtained in Example 1 is post-exposed, and then the yellow sheet, the magenta sheet and the cyan sheet are sequentially transferred under the above conditions, and the post-exposure is performed to form an image. As a result, no repellency was observed and a good overlay transfer image could be obtained. Further, in each color sheet, even if the protective film was peeled off, blocking of the photosensitive layer to the protective film was not observed.
Furthermore, the peelability of the protective film immediately after lamination is 3
It was well retained after a month.

Comparative Example 1 An image forming material was produced in the same manner as in Example 1 except that the mixed solution of the methacryloyl group-containing silicone and the acrylic oligomer of Example 1 was removed to prepare a coating solution. The coated surface of this sheet had a yuzu-like appearance, and the coated surface was not uniform. Further, when the protective film was peeled off, blocking of the photosensitive layer occurred, and the transferred image could not sufficiently reproduce the pattern of the positive mask. Comparative Example 2 A coating solution was prepared by using dimethyl silicone oil modified with a mercapto group in place of the mixed solution of the methacryloyl group-containing silicone and the acrylic oligomer of Example 2, and three colors were prepared in the same manner as in Example 2. The following image forming material was manufactured. With each color sheet, when the protective film was peeled off, the photosensitive layer was not blocked and good peeling was possible, but when the transferred images were superimposed, the image was partially repelled.

Comparative Example 3 A coating solution was prepared by using dimethylsiloxane modified with an acrylic photosensitive group instead of the mixed solution of the methacryloyl group-containing silicone and the acrylic oligomer of Example 2, and the same as in Example 2. To produce an image forming material. With each color sheet, when the protective film was peeled off, blocking of the photosensitive layer did not occur and good peeling could be performed, but when the transferred images were superimposed, the image was partially repelled. Further, peeling of the protective film was good immediately after lamination, but partial blocking was observed after 2 weeks. Comparative Example 4 An image forming material was produced in the same manner as in Example 1 except that Aerosil 300 of Example 1 was used to prepare a coating liquid. The transferred image surface was flattened and the matte feeling of the matte coated paper disappeared, resulting in glossiness.

Example 3 Instead of the protective film of Example 2, 25 μRPP (manufactured by Nisseki Goju Co., Ltd.) and 100 μl mirror
A three-color image forming material was manufactured using a protective film obtained by laminating # 100 T type (manufactured by Toray Industries, Inc.) with an adhesive, and a transfer image was formed in the same manner as in Example 2. The RPP was one in which an EvOH layer was formed between the polypropylene layers on both sides by the coextrusion method in order to secure the gas barrier property, and the oxygen permeability was 1.44 cc / m ³ · 24 hours. In each color sheet, even if the protective film was peeled off, blocking of the photosensitive layer to the protective film did not occur. Also, no repelling of the image was observed in the overlapping portion of each color, and good transfer of the mat-like image was observed. In addition, the peelability immediately after lamination was sufficiently retained even after 3 months.

The presence or absence of blocking of the photosensitive layer at the time of peeling the protective film was evaluated by attaching the image forming material to the image forming material mounting roll (40 ° C.) of a dedicated transfer machine and peeling the protective film. The presence or absence of blocking of the functional layer was visually determined.

[0033]

Since the image-forming material of the present invention contains a photoreactive silicone compound and an extender pigment, the surface tension of the photosensitive layer is low and does not cause blocking due to heat. In addition, since the silicone compound does not migrate to the surface of the photosensitive layer when it is cured by light, even when superimposing multiple colors, the silicone compound is not transferred to the entire transfer surface when transferring the first color, It does not interfere with the transfer of the image forming material for the second and subsequent colors. Further, since the extender pigment roughens the transfer surface, the matte feeling of the transferred image is maintained, and the matte image can be formed by utilizing the characteristics of the matte coated paper. Therefore, by using the image forming material of the present invention, it is possible to obtain a high-quality transfer material having the same material feeling as that of an ordinary matt printed material.

Continuation of the front page (51) Int.Cl. ⁵ Identification number Office reference number FI Technical indication location G03F 7/004 522 7/027 511 (72) Inventor Yasuharu Iida 2-3-3 Kyobashi, Chuo-ku, Tokyo Toyo Inki Manufacturing Co., Ltd.

Claims (1)

[Claims] 1. A photosensitive layer containing a colorant is formed on a support, and a protective film is further provided on the photosensitive layer. Imagewise exposure is performed to expose and unexposed areas of the photosensitive layer. In an image-forming material that transfers an image to an image receptor such as paper due to the difference in adhesiveness during transfer, the photosensitive layer contains 0.01 to 5 parts by weight of a colorant with a mixture of a methacryloyl group-containing silicone and an acrylic oligomer as a solid content. % And an extender pigment having a particle size of 0.001 to 10 μm in an amount of 5 to 50% by weight of the colorant.