JPH068659A - Image receiving sheet for thermal transfer recording - Google Patents
Image receiving sheet for thermal transfer recordingInfo
- Publication number
- JPH068659A JPH068659A JP4169409A JP16940992A JPH068659A JP H068659 A JPH068659 A JP H068659A JP 4169409 A JP4169409 A JP 4169409A JP 16940992 A JP16940992 A JP 16940992A JP H068659 A JPH068659 A JP H068659A
- Authority
- JP
- Japan
- Prior art keywords
- ink
- image
- pigment
- pigments
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、熱溶融性インク層を有
する熱転写性インクシートから、加熱溶融によりインク
を受理するインク受像層を有する熱転写記録用受像シー
トに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an image receiving sheet for thermal transfer recording having an ink image receiving layer for receiving ink by heating and melting from a heat transferable ink sheet having a heat melting ink layer.
【０００２】[0002]
【従来の技術】近年、各種プレゼンテーション用資料の
フルカラー化が急速に進んでいる中で、簡単かつ、高画
質のフルカラー印刷物が得られる溶融型熱転写プリンタ
ーが注目されている。熱転写プリント方式は、サーマル
ヘッドを用いているため、プリンターの小型化が可能で
あり、さらに静粛性にも優れた方式であるため、各種フ
ルカラープリント方式の中でも優位なプリント方式であ
る。溶融型熱転写プリント方式は、熱溶融転写性インク
シートと受像シートを重ね合せ、インクシート側にサー
マルヘッドより熱を加え、インクを受像シートに転写さ
せるものであり、カラー画像を形成させる場合は、連続
インクシートに、イエロー、マゼンタ、シアンの３色あ
るいは、黒を加えた４色の異なるインク領域を設け、順
次１色ずつ、画像信号に応じたインクを受像シートに転
写する。このようにフルカラー画像は、３色あるいは４
色の重ね合せとして表現されているため、良好な画像を
得るためには、受像シート上に、各色のインクが再現性
良く転写されなければならず、受像シートの品質が溶融
型熱転写プリント方式の画像品質に大きな影響を与えて
いる。2. Description of the Related Art In recent years, full-color materials for various presentations have been rapidly developed, and a fusion-type thermal transfer printer which can obtain a simple and high-quality full-color printed matter has attracted attention. The thermal transfer printing method is a superior printing method among various full-color printing methods because it can reduce the size of the printer because it uses a thermal head and is also quiet. The melt-type thermal transfer printing method is a method in which a heat-melt transferable ink sheet and an image receiving sheet are superposed, heat is applied to the ink sheet side from a thermal head, and the ink is transferred to the image receiving sheet. The continuous ink sheet is provided with ink regions of three colors of yellow, magenta, and cyan, or four colors of which black is added, and ink corresponding to an image signal is sequentially transferred to the image receiving sheet one by one. In this way, a full-color image has 3 colors or 4 colors.
Since it is expressed as a superposition of colors, in order to obtain a good image, the inks of each color must be transferred onto the image receiving sheet with good reproducibility. It has a great impact on image quality.
【０００３】従来、熱転写用受像シートとして、良好な
画像品質を得るために、上質紙の平滑性を高めたもの、
あるいは無機顔料主体の塗工層を有するコート紙タイプ
の受像紙（特開昭57-182487 、特開昭60-192690 、特開
昭61-217289 など）が用いられてきた。Conventionally, as a thermal transfer image-receiving sheet, a high-quality paper having an improved smoothness in order to obtain good image quality,
Alternatively, a coated paper type image-receiving paper having a coating layer mainly composed of an inorganic pigment (JP-A-57-182487, JP-A-60-192690, JP-A-61-217289, etc.) has been used.
【０００４】[0004]
【発明が解決しようとする課題】しかるに、高度に平滑
化された上質紙に比べ、無機顔料を塗工した受像紙は、
インクの転移性および再現性に優れ、良好な印字品質を
得ることができる。However, as compared with high-quality paper that is highly smoothed, image-receiving paper coated with an inorganic pigment is
The ink transferability and reproducibility are excellent, and good print quality can be obtained.
【０００５】しかし、塗工紙であるがため以下の問題が
ありその改善が要望されていた。 (イ）１、２色目のインクをストライプ状に重ね、その
重なったインク部とその隣のインク部の間に、３色目、
４色目を転移しようとした場合、３、４色目のインクが
転移不良となる現象（以降谷間印字不良と呼ぶ）。However, since it is a coated paper, it has the following problems and its improvement has been demanded. (A) The first and second color inks are overlapped in a stripe shape, and the third color ink is placed between the overlapped ink portion and the adjacent ink portion.
When attempting to transfer the fourth color, a phenomenon in which the inks of the third and fourth colors cause transfer failure (hereinafter referred to as valley printing failure).
【０００６】（ロ）受像層を金属、たとえばコインなど
でこすった場合、金属と接触した部分が、黒く汚れる現
象（以降ブラッキングと呼ぶ）。(B) When the image receiving layer is rubbed with a metal, for example, a coin, a portion in contact with the metal is stained black (hereinafter referred to as blacking).
【０００７】したがって、本発明の課題は、前記の谷間
印字不良およびブラッキングの問題を解決し、印字品質
の優れた塗工紙を提供することにある。[0007] Therefore, an object of the present invention is to solve the problems of valley printing and blacking described above, and to provide a coated paper having excellent printing quality.
【０００８】[0008]
【課題を解決するための手段】本発明者は、前記の問題
を解決するために鋭意検討の結果、顔料として有機性顔
料をバインダーとして水溶性高分子樹脂を用いることで
谷間印字不良、ブラッキングの両者の問題を解決でき、
印字品質の優れた受像シートを得られることを見出し
た。Means for Solving the Problems As a result of intensive studies for solving the above problems, the present inventor has found that by using an organic pigment as a pigment and a water-soluble polymer resin as a binder, defective printing on valleys and blacking Both problems can be solved,
It has been found that an image receiving sheet having excellent print quality can be obtained.
【０００９】すなわち、本発明は、熱溶融性インク層を
有する熱転写性インクシートから、加熱溶融によりイン
クを受理するインク受像層を有する熱転写記録用受像シ
ートにおいて、前記インク受像層が顔料として有機性顔
料を全顔料中に１０重量％以上含み、バインダーが水溶
性高分子樹脂を主体とすることを特徴とするものであ
る。That is, according to the present invention, in a thermal transfer recording image-receiving sheet having an ink image-receiving layer for receiving ink by heating and melting from a heat-transferable ink sheet having a heat-melting ink layer, the ink image-receiving layer is organic as a pigment. The pigment is contained in an amount of 10% by weight or more in all pigments, and the binder is mainly composed of a water-soluble polymer resin.
【００１０】ここで、有機性顔料は尿素樹脂およびスチ
レン樹脂の少なくとも一方を含有し、その有機顔料の吸
油量が85ml／100 g 以上であるものとすることが好適で
ある。さらに、水溶性高分子樹脂として、ヒドロキシエ
チルセルロース、カルボキシメチルセルロース、カゼイ
ン、ＰＶＡおよびシラノール基変性ＰＶＡの群から選ば
れた一種類以上含有させることができる。なお、吸油量
はＪＩＳ Ｋ ５１０１に基づく。The organic pigment preferably contains at least one of a urea resin and a styrene resin, and the oil absorption of the organic pigment is 85 ml / 100 g or more. Furthermore, as the water-soluble polymer resin, one or more kinds selected from the group of hydroxyethyl cellulose, carboxymethyl cellulose, casein, PVA and silanol group-modified PVA can be contained. The oil absorption amount is based on JIS K 5101.
【００１１】[0011]
【作用】従来、炭酸カルシウムやクレーなどの無機顔料
を塗工した受像紙において、前述のブラッキング現象が
生じる原因は、コインなどによる擦りにより、無機顔料
が金属を研磨するためと考えられる。しかるに、本発明
では、顔料として、有機性顔料を用いているので、その
問題は生じない。In the conventional image receiving paper coated with an inorganic pigment such as calcium carbonate or clay, the cause of the blacking phenomenon is considered to be that the inorganic pigment polishes the metal by rubbing with a coin or the like. However, in the present invention, since the organic pigment is used as the pigment, that problem does not occur.
【００１２】有機顔料としてプスチックピグメントと称
せられる顔料が知られており、これらの顔料は、主に尿
素樹脂、スチレン樹脂、スチレン−アクリル樹脂等から
なるものの一種または複数種組み合わせて用いることが
できる。Pigments called plastic pigments are known as organic pigments, and these pigments can be used alone or in combination of two or more kinds mainly composed of urea resin, styrene resin, styrene-acrylic resin and the like.
【００１３】そこで、後述の実施例１に示すように、吸
油量が60ml／100 g 、65ml／100g、85ml／100g、100 〜
230ml／100gのプラスチックピグメントを使用して受像
層を形成して評価したところ、吸油量が65ml／100g以下
のプラスチックピグメントでは、ブラッキングは改善で
きるものの谷間印字不良の改善効果がみられず、85ml／
100g以上で、ブラッキング、谷間印字不良の両者を改善
できた。特に100 〜 230ml／100gのものは効果に著しい
ものがあった。Therefore, as shown in Example 1 described later, the oil absorption is 60 ml / 100 g, 65 ml / 100 g, 85 ml / 100 g, 100-
When an image receiving layer was formed using 230 ml / 100 g of plastic pigment and evaluated, a plastic pigment with an oil absorption of 65 ml / 100 g or less was able to improve blacking but did not show the effect of improving valley print defects. /
With 100g or more, it was possible to improve both blacking and defective valley printing. Especially, 100 to 230 ml / 100 g had a remarkable effect.
【００１４】また、吸油量100 〜 230ml／100gのプラス
チックピグメントを無機顔料と配合して使用したとこ
ろ、プラスチックピグメントが10重量％以上配合した場
合、谷間印字不良、ブラッキングと共に改善傾向が見ら
れ、100 ％ 配合時には、谷間印字不良、ブラッキング
は良好なものの転移したインクが太る現象がある。プラ
スチックピグメントの配合率は、50〜70重量％がインク
の太りも少なく良好である。また、有機性顔料と共に無
機顔料を配合する場合には、二次凝集炭酸カルシウムが
望ましいが、クレー、炭酸カルシウムなどの公知の無機
顔料を使用可能である。Further, when a plastic pigment having an oil absorption of 100 to 230 ml / 100 g was blended with an inorganic pigment and used, when the plastic pigment was blended in an amount of 10% by weight or more, a valley printing defect and a tendency to improve together with blacking were observed. When 100% is mixed, there are defects in valley printing and good blacking, but the transferred ink becomes thicker. The blending ratio of the plastic pigment is 50 to 70% by weight, which is good because the ink is not thickened. When an inorganic pigment is blended with an organic pigment, secondary agglomerated calcium carbonate is desirable, but known inorganic pigments such as clay and calcium carbonate can be used.
【００１５】本発明においては、バインダーとして、水
溶性高分子樹脂が用いられ、ポリビニルアルコール（Ｐ
ＶＡ）、ヒドロキシエチルセルロース（ＨＥＣ）、カル
ボキシメチルセルロース（ＣＭＣ）、シラノール基変性
ＰＶＡ（クラレ社製「Ｒ−ポリマー」）、カゼイン、澱
粉などを用いることができる。In the present invention, a water-soluble polymer resin is used as the binder, and polyvinyl alcohol (P
VA), hydroxyethyl cellulose (HEC), carboxymethyl cellulose (CMC), silanol group-modified PVA (“R-polymer” manufactured by Kuraray Co., Ltd.), casein, starch and the like can be used.
【００１６】これらの他に、ＳＢＲラテックスを用いた
が、充分な接着強度が得られず水溶性高分子樹脂のバイ
ンダーが接着強度において良好であることが知見され
た。特に、ＨＥＣ、カゼイン、ＰＶＡ、ＣＭＣが表面強
度が良好であり、ＨＥＣとＰＶＡなど複数種を組合わせ
て使用するのが望ましい。総バインダー中の水溶性高分
子樹脂の配合率は２０重量％程度で効果が出るが、好ま
しくは５０重量％以上が望ましい。また、前述の材料が
塗工された後、塗工表面をスーパーカレンダーにて、平
滑に仕上げるのが望ましい。In addition to these, SBR latex was used, but it was found that sufficient adhesive strength was not obtained, and the binder of the water-soluble polymer resin had good adhesive strength. In particular, HEC, casein, PVA, and CMC have good surface strength, and it is desirable to use a combination of multiple types such as HEC and PVA. The compounding ratio of the water-soluble polymer resin in the total binder is effective when it is about 20% by weight, but preferably 50% by weight or more. Further, after the above-mentioned materials are coated, it is desirable to finish the coated surface with a super calender to be smooth.
【００１７】バインダーの使用量は、全顔料100 重量部
に対して、10〜100 重量部、特に30〜80重量部が好まし
い。受像層を形成する塗布量としては、１ｇ／m2以上、
特に２〜20ｇ／m2が望ましい。塗布はエアナイフコータ
ー、ロールコーター、ブレードコーター、バーコーター
などの公知の塗布機により行うことができる。かくして
形成される受像層を有する受像シートと組み合わせて用
いられる転写シートは、受像シートと接する面に加熱時
に転写可能なインク層を有するものであるが、この熱溶
融性インク層を有する熱転写性インクシートの構成は、
公知のものを適宜用いることができる。The amount of the binder used is preferably 10 to 100 parts by weight, more preferably 30 to 80 parts by weight, based on 100 parts by weight of the total pigment. The coating amount for forming the image receiving layer is 1 g / m 2 or more,
Particularly, 2 to 20 g / m 2 is desirable. The coating can be carried out by a known coating machine such as an air knife coater, a roll coater, a blade coater or a bar coater. The transfer sheet used in combination with the image-receiving sheet having the image-receiving layer thus formed has an ink layer capable of transfer when heated on the surface in contact with the image-receiving sheet. The seat structure is
Known materials can be used as appropriate.
【００１８】[0018]
【実施例】以下実施例を示して本発明の効果を明らかに
する。 （実施例１）給油量の異なる各種のプラスチックピグメ
ントを顔料とし、バインダーとしてＨＥＣ（商品名ＡＬ
−15；フジケミカル社製）とＰＶＡ（商品名ＰＶＡ−11
0 ；クラレ社製）をそれぞれ顔料の30重量部、20重量部
配合して受容層カラーを調整した。EXAMPLES The effects of the present invention will be clarified by showing examples below. (Example 1) Various plastic pigments having different refueling amounts were used as pigments, and HEC (product name AL
-15; Fuji Chemical Co., Ltd. and PVA (trade name PVA-11)
0; manufactured by Kuraray Co., Ltd.) was mixed with 30 parts by weight and 20 parts by weight of pigments to adjust the color of the receiving layer.
【００１９】上質紙（坪量81.4g/m2）の片面に、ブレー
ドコーターで乾燥重量で8g/m2 を塗工後、ベック平滑度
が500 秒となるようにして、被転写紙１〜４を作成し
た。After coating a dry weight of 8 g / m 2 with a blade coater on one surface of a high-quality paper (basis weight 81.4 g / m 2 ), the Beck smoothness was set to 500 seconds, and the transferred paper 1 to Created 4.
【００２０】この被転写紙について、市販の熱転写プリ
ンター（セイコー電子工業社製「ＣＨ−4104」）を用い
て印字し、谷間印字不良、ブラッキングおよび転写イン
クの太りを評価したところ、表１の結果が得られた。This transfer paper was printed using a commercially available thermal transfer printer (“CH-4104” manufactured by Seiko Denshi Kogyo Co., Ltd.), and the defective valley printing, blacking and transfer ink thickening were evaluated. Results were obtained.
【００２１】[0021]
【表１】 [Table 1]
【００２２】この結果から、谷間印字不良を改善するに
は、プラスチックピグメントの吸油量が85ml/100g 以
上、好ましくは150 〜280ml/100gが好適であることが判
明する。From these results, it is clear that the oil absorption of the plastic pigment is 85 ml / 100 g or more, preferably 150 to 280 ml / 100 g, in order to improve the valley printing defect.
【００２３】（実施例２）吸油量が150 〜 280ml／100g
の尿素系のプラスチックピグメントを使用して、バイン
ダーの種類によって、谷間印字不良、ブラッキング、接
着強度を評価したところ、表２に示す結果が得られた。(Example 2) Oil absorption of 150 to 280 ml / 100 g
When the urea-based plastic pigment (1) was used to evaluate valley printing defects, blacking, and adhesive strength depending on the type of binder, the results shown in Table 2 were obtained.
【００２４】[0024]
【表２】 [Table 2]
【００２５】この結果によれば、総じて水溶性高分子樹
脂の場合は好適であるのに対して、ＳＢＲラテックスの
場合には、接着強度の点で採用できないことが判る。From these results, it is understood that the water-soluble polymer resin is generally suitable, whereas the SBR latex cannot be used in terms of adhesive strength.
【００２６】（実施例３）被転写紙−４について、尿素
系のプラスチックピグメントと共に、無機顔料を配合し
た。無機顔料には、二次凝集炭酸カルシウム（商品名タ
マパールＴＰ−ＣＰＣ；奥多摩工業社製）を用い、プラ
スチックピグメントとの配合比率を変更して受容層カラ
ーを調整した。実施例１と同様の方法で被転写紙を作成
後、前述の市販プリンターで谷間印字不良、ブラッキン
グ、および転写インクの太りを評価したところ表３の結
果が得られた。Example 3 With respect to the transferred paper-4, an inorganic pigment was blended together with a urea-based plastic pigment. Secondary inorganic calcium carbonate (Tamapearl TP-CPC, trade name, manufactured by Okutama Kogyo Co., Ltd.) was used as the inorganic pigment, and the mixing ratio with the plastic pigment was changed to adjust the color of the receiving layer. After the transfer paper was prepared in the same manner as in Example 1, the above-mentioned commercially available printer was used to evaluate the valley printing defect, blacking, and the thickening of the transfer ink, and the results in Table 3 were obtained.
【００２７】[0027]
【表３】 [Table 3]
【００２８】なお、表面の平滑性を測定する手段として
ベック平滑度を用いたが、平滑度の数値が高いほど谷間
印字不良は悪くなり、インク転写性は良くなった。ベッ
ク平滑度で200 〜1200秒が谷間印字不良改善、インク転
写性ともに良好であった。Beck's smoothness was used as a means for measuring the smoothness of the surface. The higher the value of the smoothness, the worse the valley printing defect and the better the ink transferability. A Beck's smoothness of 200 to 1,200 seconds was good for improving the valley printing defect and the ink transferability.
【００２９】[0029]
【発明の効果】以上の通り、本発明によれば、谷間印字
不良およびブラッキングの発生を防止できる。As described above, according to the present invention, defective valley printing and blacking can be prevented.
─────────────────────────────────────────────────────
─────────────────────────────────────────────────── ───
【手続補正書】[Procedure amendment]
【提出日】平成５年２月２６日[Submission date] February 26, 1993
【手続補正１】[Procedure Amendment 1]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】０００３[Name of item to be corrected] 0003
【補正方法】変更[Correction method] Change
【補正内容】[Correction content]
【０００３】従来、熱転写用受像シートとして、良好な
画像品質を得るために、上質紙の平滑性を高めたものな
ど、あるいは、有機顔料を配合したコート紙タイプの受
像紙（特開昭60−11492 号、特開昭61−266296号、特開
昭63-21185号）が提案されている。 Conventionally, as a thermal transfer image receiving sheet, in order to obtain a good image quality, it that enhance the smoothness of fine paper
, Or coated paper type receiving organic pigment
Image paper (JP-A-60-11492, JP-A-61-266296, JP-A-61-266296)
No. 63-21185) has been proposed.
【手続補正２】[Procedure Amendment 2]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００１４[Correction target item name] 0014
【補正方法】変更[Correction method] Change
【補正内容】[Correction content]
【００１４】また、吸油量100 〜 230ml／100gのプラス
チックピグメントを無機顔料と配合して使用したとこ
ろ、プラスチックピグメントを10重量％以上配合した場
合、谷間印字不良、ブラッキング共に改善傾向が見ら
れ、20重量％以上配合することで十分な品質を得ること
ができる。100 重量％配合時には、谷間印字、ブラッキ
ングは良好なものの転移したインクが太る（横方向に広
がる）現象がある。また、吸油量100 〜230 ml／100gの
プラスチックピグメントを30部を超えて配合すると、塗
工層強度が低下し、印字の際に塗工層の一部がインクフ
ィルムに取られる問題が生じる。この場合、バインダー
成分である水溶性高分子を多量に配合することで塗工層
強度の低下を防止できるが、バインダーの過度の配合は
多湿条件下での水溶性高分子の吸湿により紙がベタ付く
ため、給紙トラブルあるいはハンドリング上の不都合が
生じる。このことから、プラスチックピグメントの配合
比率は、10〜30重量％、好ましくは20〜30重量％で、谷
間印字、ブラッキング、塗工層強度、インクの太り等の
問題を解決し、最もバランスの良好な熱転写受像紙を提
供することができる。また、有機顔料と共に配合される
無機顔料には、炭酸カルシウム、クレー、などの公知の
顔料が使用されるが、吸油量80ml／100g以上の無機顔
料、例えば焼成クレー、合成シリカ等は塗工層強度の低
下を招くため使用不可能である。Further, when a plastic pigment having an oil absorption of 100 to 230 ml / 100 g was blended with an inorganic pigment, when the plastic pigment was blended in an amount of 10% by weight or more, valley printing defects and blacking tended to improve. , Obtain sufficient quality by blending more than 20% by weight
You can When 100% by weight is blended, cleavage printing, blacking
Ink is good, but the transferred ink is thicker (wider in the lateral direction).
There is a phenomenon. Also, the oil absorption of 100-230 ml / 100g
If more than 30 parts of plastic pigment are compounded,
The strength of the coating layer decreases, and when printing, part of the coating layer
There is a problem with the film. In this case, the binder
Coating layer by adding a large amount of water-soluble polymer as a component
Although it is possible to prevent the strength from decreasing, excessive blending of the binder
Paper sticks due to moisture absorption of water-soluble polymer under humid conditions
Therefore, there may be paper feeding problems or handling problems.
Occurs. From this, the formulation of plastic pigments
The ratio is 10 to 30% by weight, preferably 20 to 30% by weight.
Printing, blacking, coating layer strength, thickening of ink, etc.
Solving problems and providing the most well-balanced thermal transfer receiving paper
Can be offered. Also blended with organic pigments
Known inorganic pigments include calcium carbonate, clay, etc.
Inorganic face with oil absorption of 80ml / 100g or more, although pigments are used
Materials such as calcined clay and synthetic silica have low coating layer strength.
It is unusable because it invites the bottom .
【手続補正３】[Procedure 3]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００１７[Correction target item name] 0017
【補正方法】変更[Correction method] Change
【補正内容】[Correction content]
【００１７】バインダーの使用量は、全顔料100 重量％
に対して、10〜100 重量％、特に30〜80重量％が好まし
い。水溶性高分子が全顔料100 重量％に対して80重量％
を超えて配合することは、前述の水溶性高分子の吸湿に
よるトラブルが発生するため、不適である。塗布はエア
ナイフコーター、ロールコーター、ブレードコーター、
バーコーターなどの公知の塗布機により行うことができ
る。かくして形成される受像層を有する受像シートと組
み合わせて用いられる転写シートは、受像シートと接す
る面に加熱時に転写可能なインク層を有するものである
が、この熱溶融性インク層を有する熱転写性インクシー
トの構成は、公知のものを適宜用いることができる。The amount of binder used is 100 % by weight of all pigments.
On the other hand, 10 to 100 % by weight, particularly 30 to 80 % by weight are preferable. 80% by weight of water-soluble polymer based on 100% by weight of total pigment
Blending more than the above is not recommended for moisture absorption of the water-soluble polymer.
This is not suitable because it causes trouble . Application is air knife coater, roll coater, blade coater,
It can be performed by a known coating machine such as a bar coater. The transfer sheet used in combination with the image-receiving sheet having the image-receiving layer thus formed has an ink layer capable of transfer when heated on the surface in contact with the image-receiving sheet. As the structure of the sheet, a known structure can be appropriately used.
【手続補正４】[Procedure amendment 4]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００２７[Name of item to be corrected] 0027
【補正方法】変更[Correction method] Change
【補正内容】[Correction content]
【００２７】[0027]
【表３】 [Table 3]
Claims (3)
シートから、加熱溶融によりインクを受理するインク受
像層を有する熱転写記録用受像シートにおいて、 前記インク受像層が顔料として有機性顔料を全顔料中に
１０重量％以上含み、バインダーが水溶性高分子樹脂を
主体とすることを特徴とする感熱転写記録用受像シー
ト。1. A thermal transfer recording image-receiving sheet having an ink image-receiving layer for receiving ink by heating and melting from a thermal transferable ink sheet having a heat-melting ink layer, wherein the ink image-receiving layer contains all organic pigments as pigments. An image-receiving sheet for thermal transfer recording, characterized in that the content of the binder is 10% by weight or more, and the binder is mainly composed of a water-soluble polymer resin.
の少なくとも一方を含有し、その有機顔料の吸油量が85
ml／100 g 以上である請求項１記載の感熱転写記録用受
像シート。2. The organic pigment contains at least one of a urea resin and a styrene resin, and the organic pigment has an oil absorption of 85.
The image-receiving sheet for heat-sensitive transfer recording according to claim 1, which has a volume of at least 100 ml / ml.
ロース、カルボキシメチルセルロース、カゼイン、ＰＶ
Ａおよびシラノール基変性ＰＶＡの群から選ばれた一種
類以上含有する請求項１記載の感熱転写用受像シート3. The water-soluble polymer resin is hydroxyethyl cellulose, carboxymethyl cellulose, casein, PV
The heat-sensitive transfer image-receiving sheet according to claim 1, containing at least one selected from the group consisting of A and silanol group-modified PVA.