JPH07173560A - 耐食性に優れたNi基合金 - Google Patents

耐食性に優れたNi基合金

Info

Publication number
JPH07173560A
JPH07173560A JP34428493A JP34428493A JPH07173560A JP H07173560 A JPH07173560 A JP H07173560A JP 34428493 A JP34428493 A JP 34428493A JP 34428493 A JP34428493 A JP 34428493A JP H07173560 A JPH07173560 A JP H07173560A
Authority
JP
Japan
Prior art keywords
based alloy
corrosion resistance
excellent corrosion
phase
continuous electroplating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP34428493A
Other languages
English (en)
Other versions
JP3175457B2 (ja
Inventor
Hiroaki Komoto
宏明 甲元
Masahiro Wada
正弘 和田
Taku Nakajima
卓 中嶋
Tsutomu Oka
勉 岡
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mitsubishi Materials Corp
Original Assignee
Mitsubishi Materials Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitsubishi Materials Corp filed Critical Mitsubishi Materials Corp
Priority to JP34428493A priority Critical patent/JP3175457B2/ja
Publication of JPH07173560A publication Critical patent/JPH07173560A/ja
Application granted granted Critical
Publication of JP3175457B2 publication Critical patent/JP3175457B2/ja
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

(57)【要約】 【目的】 化学プラント機器用部品、連続電気メッキラ
インのコンダクターロールなど、酸溶液による腐蝕が問
題になる部分の構造部材製造用Ni基合金を提供する。 【構成】 重量%で、Cr:34〜50%、Mo:10
〜25%を含有し、残り:Niおよび不可避不純物から
なる組成を有し、かつ、P相を含まないことを特徴とす
る耐食性に優れたNi基合金。

Description

【発明の詳細な説明】
【0001】
【産業上の利用分野】この発明は、化学プラント機器、
連続電気メッキラインのコンダクターロールなど、酸溶
液による腐蝕が問題になる部分の構造部材製造用Ni基
合金に関するものである。
【0002】
【従来の技術】一般に、化学プラントの機器、連続電気
メッキラインのコンダクターロールなど酸溶液による腐
蝕が問題になる部分の構造部品は、Cr:25〜33
%、Mo:16〜23%を含有し、残り:Niおよび不
可避不純物からなるNi基合金を原料粉末とし、これを
熱間静水圧プレスすることにより製造していた。このよ
うにして製造した圧密化体は、耐摩耗性に優れ、かつ耐
食性にも優れていることが知られている(特開平1−1
16098号公報参照)。
【0003】
【発明が解決しょうとする課題】しかし、最近の化学プ
ラントに用いられる機器、連続電気メッキラインのコン
ダクターロールなどは、高耐摩耗性を有するだけでな
く、酸化性酸に対してさらなる耐食性を有することが要
求され、さらに、出来るかぎり機器の交換回数を少なく
して保守の周期を長くし、長期にわたって続けて運転操
業できることが要求される傾向にある。
【0004】このような状況に対して、上記従来のNi
基合金で作製された化学プラントに用いられる機器およ
び連続電気メッキラインのコンダクターロールなどは、
上記要求に対して、十分満足出来るものではなかった。
【0005】
【課題を解決するための手段】そこで、本発明者らは、
かかる要求に対処すべく、従来よりも一層優れた耐腐蝕
性を有するNi基合金からなる化学プラントの機器、連
続電気メッキラインのコンダクターロールなどを製造す
べく研究を行った結果、(1) 上記従来のNi基合金
には、微量ながらP相が析出していることがあり、この
P相が析出しているNi基合金を化学プラント用機器部
品および連続電気メッキラインのコンダクターロールな
どの素地中に析出すると、局部電池作用により腐蝕が進
行しやすく、十分な耐腐蝕性が得られなくなる、(2)
従来のNi基合金よりもCr量の多いNi基合金粉末
を1210℃〜1250℃の温度で熱間静水圧プレスす
ると、P相が析出しないNi基合金が得られる、などの
知見を得たのである。
【0006】この発明は、かかる知見に基づいて成され
たものであって、重量%で、Cr:34〜50%、M
o:16〜25%となるように含有し、残り:Niおよ
び不可避不純物からなる組成を有し、かつ、P相を含ま
ないNi基合金にに特徴を有するものである。
【0007】つぎに、この発明のNi基合金の成分組成
を上記のごとく限定した理由について説明する。
【0008】(a)Cr Crは、34%未満ではP相が出現することがあって耐
蝕性に悪影響を及ぼすので好ましくなく、一方、50%
を越えると延性を持つγ相の分率が減少し、靭性が劣化
するので好ましくないところからCr:34〜50%に
定めた。
【0009】(b)Mo Mo成分は、10%未満では耐摩耗性に効果のあるσ相
が出現しないので十分な耐摩耗性が得られず、一方、2
5%を越えると、延性を持つγ相の分率が減少し、靭性
が劣化するので好ましくないところからMo:10〜2
5%に定めた。
【0010】
【実施例】つぎに、この発明を、実施例にもとづいて具
体的に説明する。
【0011】通常の真空高周波加熱炉を用い、真空度:
10-4torrの真空雰囲気中で溶解し、表1に示した
成分組成となるように溶湯を調製し、このNi基合金溶
湯の温度を1500℃に保持し、予熱したタンディッシ
ュ内に注湯し、その底に設けたノズルより落下せしめ、
それを専用の噴霧ノズルより窒素ガスを圧力:25kg
/cm2 、流量:12Nm3 /minなる条件で粉末化
を行い、Ni基合金粉末を製造した。このようにして得
られたNi基合金粉末をステンレス製のカプセルに充填
し、加熱温度:400℃、真空度:10-5torrの真
空雰囲気下で12時間保持し、粉末表面に吸着したガス
の真空脱ガス処理を行い、密封して真空密封構造物を作
製した。
【0012】上記真空密封構造物を表1に示される条件
で熱間静水圧プレスし、表1に示した成分組成を有する
本発明Ni基合金1〜9および従来Ni基合金を製造し
た。このようにして得られたNi基合金の金属組織を観
察してP相の有無を調べた後、耐腐蝕性を評価する目的
で、50%H2 SO4 +42gFe2 (SO4 3 の沸
騰溶液に24時間浸漬するASTM G28の試験を行
い、これらの測定結果をそれぞれ表1に示した。
【0013】
【表1】
【0014】表1に示される結果から、本発明Ni合金
1〜9は、従来Ni基合金よりも極めて優れた耐食性を
有することが分かる。
【0015】
【発明の効果】上述のように、この発明のNi基合金
は、極めて優れた耐食性を有し、化学プラント機器およ
び連続電気メッキラインのコンダクターロールの構造部
材として用いるとすぐれた効果を発揮するものである。
───────────────────────────────────────────────────── フロントページの続き (72)発明者 岡 勉 埼玉県桶川市上日出谷1230 三菱マテリア ル株式会社桶川製作所内

Claims (1)

    【特許請求の範囲】
  1. 【請求項1】 重量%で、 Cr:34〜50%、 Mo:10〜25%、 を含有し、残り:Niおよび不可避不純物からなる組成
    を有し、かつ、P相を含まないことを特徴とする耐食性
    に優れたNi基合金。
JP34428493A 1993-12-17 1993-12-17 熱間静水圧プレスにより得られた耐食性に優れたNi基燒結合金 Expired - Lifetime JP3175457B2 (ja)