JPH07237132A - Film tape for scrubbing brush - Google Patents
Film tape for scrubbing brushInfo
- Publication number
- JPH07237132A JPH07237132A JP5302394A JP5302394A JPH07237132A JP H07237132 A JPH07237132 A JP H07237132A JP 5302394 A JP5302394 A JP 5302394A JP 5302394 A JP5302394 A JP 5302394A JP H07237132 A JPH07237132 A JP H07237132A
- Authority
- JP
- Japan
- Prior art keywords
- film
- resin layer
- scrubbing
- film tape
- surfactant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、偏平糸状のたわし用フ
イルムテープに関し、詳細には、食器や鍋類や流し台、
あるいは浴槽やタイルや車のタイヤのホイールなどを研
磨・洗浄する場合に使用するたわし用の素材として特に
有益な、偏平糸状のたわし用フイルムテープに係るもの
である。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a flat thread-like film tape for scrubbing, and more particularly to tableware, pots and sinks,
Alternatively, the present invention relates to a flat thread-like scrubbing film tape, which is particularly useful as a scrubbing material used when polishing and cleaning bathtubs, tiles, wheels of car tires, and the like.
【０００２】[0002]
【従来の技術】たわし用の素材として従来、プラスチッ
クフイルムからなる偏平糸状のたわし用フイルムテープ
が知られている（実公昭５６−６０５８号公報、実公昭
５７−４４９４２号公報、実開昭６３−１６９０６７号
の全文明細書等参照）。2. Description of the Related Art As a material for scrubbing brushes, flat thread-shaped scrubbing film tapes made of plastic film have been known (Japanese Utility Model Publication No. 56-6058, Japanese Utility Model Publication No. 57-44942, and Japanese Utility Model Publication No. Sho 63-). (See full text specification, etc. of No. 169067).
【０００３】[0003]
【発明が解決しようとする課題】しかし、上記従来のた
わし用フイルムテープは、これをたわしに使用したとき
には、主として、フイルムテープの表面部分ではなくフ
イルムテープのエッヂすなわち両端部分の角を利用して
研磨・洗浄するものであるから、研磨・洗浄の効率が悪
く、また、洗剤や石鹸が必要であった。本発明は上記の
欠点を除去するものである。However, when the conventional film tape for scrubbing is used as a scrubbing brush, the edge of the film tape, that is, the corners at both ends of the film tape is mainly utilized, not the surface portion of the film tape. Since it is to be polished and washed, the efficiency of polishing and washing was poor, and detergent and soap were required. The present invention eliminates the above drawbacks.
【０００４】[0004]
【課題を解決するための手段】本発明は次のたわし用フ
イルムテープである。 （１）プラスチックフイルムの表面に、粒子状の研磨剤
と界面活性剤を混入した樹脂層を形成したことを特徴と
する偏平糸状のたわし用フイルムテープ。 （２）プラスチックフイルムの表面に、粒子状の研磨剤
を混入した樹脂層を形成したことを特徴とする偏平糸状
のたわし用フイルムテープ。 （３）プラスチックフイルムの表面に、界面活性剤を混
入した樹脂層を形成したことを特徴とする偏平糸状のた
わし用フイルムテープ。 （４）プラスチックフイルムが金属層を備えたものであ
る上記（１）〜（３）のうちのいずれかに記載の偏平糸
状のたわし用フイルムテープ。The present invention is the following film tape for scrubbing brush. (1) A flat yarn-like film tape for scrubbing, wherein a resin layer containing a particulate abrasive and a surfactant is formed on the surface of a plastic film. (2) A flat yarn-shaped film tape for scrubbing, wherein a resin layer containing a particulate abrasive is formed on the surface of a plastic film. (3) A flat thread-shaped film tape for scrubbing, which is characterized in that a resin layer containing a surfactant is formed on the surface of a plastic film. (4) The flat thread-like film tape for scrubbing according to any one of the above (1) to (3), wherein the plastic film has a metal layer.
【０００５】以下、本発明を図面を参照しつつ説明す
る。プラスチックフイルム１０としては、ポリエステル
フイルム、塩化ビニルフイルム、ウレタンフイルムなど
の各種のプラスチックフイルムが使用できる。プラスチ
ックフイルム１０の厚さは特に限定しないが、６〜７５
μｍが好ましい。プラスチックフイルム１０の厚さが６
μｍより薄いと弱すぎて切れやすく、また、たわしの使
用に際してやわらかすぎる。また、６μｍより薄いと、
樹脂層を形成して乾燥するときの熱でプラスチックフイ
ルムに皺が入って伸びる。プラスチックフイルム１０の
厚さが７５μｍより厚いとフイルムにいわゆる腰があり
すぎるからかたすぎて、たわしの使用に際して被研磨物
・被洗浄物に傷をつけやすい。プラスチックフイルム１
０は、その表面すなわち片面又は両面に、Ａｌ等の各種
の金属層を真空蒸着、スパッタリング、イオンブレーテ
イング等の各種の方法で形成して金属層を備えたもので
もよく、また、適宜の染料や顔料で着色したものでもよ
く、さらに、金属層を備えかつ着色したものでもよい。The present invention will be described below with reference to the drawings. As the plastic film 10, various plastic films such as polyester film, vinyl chloride film and urethane film can be used. The thickness of the plastic film 10 is not particularly limited, but is 6 to 75
μm is preferred. The thickness of the plastic film 10 is 6
If it is thinner than μm, it is too weak and easy to cut, and it is too soft when using scrubbing brush. If it is thinner than 6 μm,
The heat when forming and drying the resin layer causes the plastic film to wrinkle and stretch. When the thickness of the plastic film 10 is thicker than 75 μm, the film is so stiff that it is too hard and is likely to damage the object to be polished or the object to be cleaned when the scrubber is used. Plastic film 1
0 may be provided with a metal layer on its surface, that is, one or both sides, by forming various metal layers such as Al by various methods such as vacuum vapor deposition, sputtering, and ion blading, and an appropriate dye. It may be colored with a pigment or a pigment, and may be colored with a metal layer.
【０００６】プラスチックフイルム１０の表面には、図
１に例示するように、粒子状の研磨剤と界面活性剤を混
入した樹脂層２０を形成する。樹脂層は、界面活性剤を
混入せずに、図２に例示するように、粒子状の研磨剤を
混入した樹脂層３０でもよい。また、樹脂層は、粒子状
の研磨剤を混入せずに、図３に例示するように、界面活
性剤を混入した樹脂層４０でもよい。樹脂層２０を形成
した場合は、研磨・洗浄したときに研磨と洗浄がバラン
スよく行える。樹脂層３０を形成した場合は、研磨・洗
浄したときに特に研磨効果が顕著であるから、汚れがひ
どいときに適している。樹脂層４０を形成した場合は、
研磨・洗浄したときに特に洗浄効果が顕著であるから、
汚れがそれ程ひどくないときに適している。On the surface of the plastic film 10, as illustrated in FIG. 1, a resin layer 20 containing a particulate abrasive and a surfactant is formed. The resin layer may be a resin layer 30 in which a particulate abrasive is mixed as illustrated in FIG. 2 without mixing a surfactant. Further, the resin layer may be a resin layer 40 in which a surfactant is mixed, as illustrated in FIG. 3, without mixing in a particulate abrasive. When the resin layer 20 is formed, polishing and cleaning can be performed in a well-balanced manner when polishing and cleaning. When the resin layer 30 is formed, the polishing effect is particularly remarkable when it is polished and washed, and therefore it is suitable when the stain is severe. When the resin layer 40 is formed,
Since the cleaning effect is particularly remarkable when polishing and cleaning,
Suitable when dirt is not so bad.
【０００７】樹脂層に混入する粒子状の研磨剤として
は、例えば、粒子径約３０μｍのα−酸化アルミナが挙
げられるが、これに限るものではなく、研磨・洗浄効果
がある粒子状のものであれば粒子状の研磨剤として使用
できる。Examples of the particulate abrasive mixed in the resin layer include α-alumina oxide having a particle diameter of about 30 μm. However, it is not limited to this, and the particulate abrasive having a polishing / cleaning effect. If it can be used as a particulate abrasive.
【０００８】樹脂層に混入する界面活性剤としては、例
えば、ポリオキシエチレン系、ポリオキシブロビレン
系、ポリアルキルオキサイド系などの非イオン系活性剤
が挙げられるが、これに限るものではなく、研磨・洗浄
効果特に洗浄効果がある界面活性剤であればこの発明の
界面活性剤として使用できる。Examples of the surfactant mixed in the resin layer include, but are not limited to, nonionic surfactants such as polyoxyethylene-based, polyoxybrobylene-based and polyalkyl oxide-based surfactants. Polishing / cleaning effect Any surfactant having a cleaning effect can be used as the surfactant of the present invention.
【０００９】樹脂層に使用する樹脂としては、ポリエス
テル系樹脂、アクリル系樹脂、塩酢ビ系樹脂、エポキシ
系樹脂、メラミン系樹脂、ポリアミド系樹脂、ニトロセ
ルロース系樹脂、ウレタン系樹脂、あるいはこれらの複
合物などの各種の樹脂が挙げられるが、これに限るもの
ではなく、研磨剤や界面活性剤の相溶性、分散性がある
樹脂であればこの発明の樹脂層に使用できる。The resin used in the resin layer is a polyester resin, an acrylic resin, a vinyl chloride-based resin, an epoxy resin, a melamine resin, a polyamide resin, a nitrocellulose resin, a urethane resin, or these resins. Examples of the resin include various resins such as composites, but the resin is not limited thereto, and any resin having compatibility and dispersibility of an abrasive or a surfactant can be used in the resin layer of the present invention.
【００１０】樹脂層２０や樹脂層３０や樹脂層４０は、
プラスチックフイルム１０の表面すなわち片面又は両面
に、リバースコート法、グラビアコート法、コンマコー
ター法などの各種のコーテイング法により形成できる。The resin layer 20, the resin layer 30, and the resin layer 40 are
It can be formed on the surface of the plastic film 10, that is, on one side or both sides, by various coating methods such as a reverse coating method, a gravure coating method and a comma coater method.
【００１１】樹脂層には、より研磨効果を出すために樹
脂層をもろくして粒子状の研磨剤の脱粒を促進させた
り、樹脂層の耐熱性を向上させたり、チキソトロピー付
与したりするために、各種の添加物を適宜添加してもよ
い。添加物としては例えば、樹脂層をもろくして粒子状
の研磨剤の脱粒を促進させる塩ビフェノール、イソシア
ネート、シリカ、耐熱性を向上させる塩ビフェノール、
イソシアネート、チキソトロピー付与するシリカなどが
挙げられる。In order to further enhance the polishing effect, the resin layer is fragile to accelerate the shedding of the particulate abrasive, improve the heat resistance of the resin layer, and impart thixotropy. Various additives may be added as appropriate. As the additive, for example, vinyl chloride phenol which accelerates the degranulation of the particulate abrasive by fragile the resin layer, isocyanate, silica, vinyl chloride which improves heat resistance,
Examples thereof include isocyanate and silica that imparts thixotropy.
【００１２】本発明に係る偏平糸状のたわし用フイルム
テープの幅は特に限定しないが、０．５〜５．０ｍｍが
好ましい。フイルムテープの幅が０．５ｍｍより細いと
弱すぎて切れやすく、また、たわしの使用に際してやわ
らかすぎる。フイルムテープの幅が５．０ｍｍより太い
とかたすぎてたわしの使用に際して被研磨物・被洗浄物
に傷をつけやすい。The width of the flat yarn-shaped film tape for scrubbing according to the present invention is not particularly limited, but is preferably 0.5 to 5.0 mm. If the width of the film tape is smaller than 0.5 mm, it is too weak and easy to cut, and it is too soft when using the scrubbing brush. If the width of the film tape is thicker than 5.0 mm, it will be too hard and easily scratch the object to be polished or cleaned when using the scrubbing brush.
【００１３】本発明に係る偏平糸状のたわし用フイルム
テープを使用したたわし自体の構成は特に問わない。例
えば、本発明に係る偏平糸状のたわし用フイルムテープ
を単独で又は他の繊維糸とともに織成又は編成したり、
また、別途繊維糸を織成又は編成してなる生地に、本発
明に係る偏平糸状のたわし用フイルムテープのパイルが
表面に露出するように適宜に織り込んだりしてたわしを
構成することができる。たわしは、スポンジなどの芯体
を中にして袋状にしてもよく、また、芯棒に貼りつけた
り編んだり、芯棒を中にして筒状にしてもよく、いずれ
にしてもたわし自体は自由に構成できる。The structure of the scrubber itself using the flat yarn-shaped film film for scrubbing according to the present invention is not particularly limited. For example, the flat yarn-like scrubbing film tape according to the present invention is woven or knitted alone or together with other fiber yarns,
Further, a scrubber can be constructed by appropriately weaving a pile of the flat yarn-like film tape for scrubbing according to the present invention so as to be exposed on the surface of a cloth obtained by separately weaving or knitting fiber threads. The scourer may be in the shape of a bag with a sponge or other core inside, or may be attached to or knitted on a core rod, or may be cylindrical with the core rod inside. Can be configured to.
【００１４】[0014]
実施例１（粒子状の研磨剤と界面活性剤を混入した実施
例） 厚さ２５μｍの広幅長尺なポリエチレンテレフタレート
フイルムの片面に、真空蒸着により厚さ４５０ÅのＡｌ
蒸着層を形成して金属層とし、該金属層の上に、粒子状
の研磨剤として粒子径約３０μｍのα−酸化アルミナ
を、界面活性剤としてポリアルキルオキサイド系界面活
性剤をそれぞれ使用して、下記の組成の塗料により粒子
状の研磨剤と界面活性剤を混入した厚さ４０μｍの樹脂
層をリバースコートにより形成した。 ポリエステル樹脂 １５．０重量部 （東洋紡績社製） α−酸化アルミナ １７．５重量部 （フジミインコーポレーテッド社製ＷＡ−４００） ポリアルキルオキサイド系界面活性剤 ０．１重量部 （第一工業製薬社製パオゲンＰＰ−１５） トルエン ７．５重量部 ＭＥＫ ７．５重量部 次に、上記のようにして得た、金属層を備えており、か
つ、表面に粒子状の研磨剤と界面活性剤を混入した樹脂
層を形成したポリエチレンテレフタレートフイルムを、
１ｍｍの幅で縦長にスリットして、本発明に係る偏平糸
状のたわし用フイルムテープを得た。次いで、偏平糸状
のたわし用フイルムテープを、別途繊維糸を編成してな
る生地に、該フイルムテープのパイルが表面に露出する
ように織り込んでたわしとした。また、このたわしを使
用し、芯体であるスポンジを中にして袋状にして、別の
たわしとした。Example 1 (Example in which a particulate abrasive and a surfactant were mixed) On one side of a wide and long polyethylene terephthalate film having a thickness of 25 μm, a 450 Å-thick Al film was formed by vacuum deposition.
A vapor-deposited layer is formed as a metal layer, and α-alumina oxide having a particle diameter of about 30 μm is used as a particulate abrasive and a polyalkyl oxide-based surfactant is used as a surfactant on the metal layer. A resin layer having a thickness of 40 μm, in which a particulate abrasive and a surfactant were mixed, was formed by reverse coating using a paint having the following composition. Polyester resin 15.0 parts by weight (manufactured by Toyobo Co., Ltd.) α-alumina oxide 17.5 parts by weight (WA-400 manufactured by Fujimi Incorporated) Polyalkyl oxide surfactant 0.1 parts by weight (Daiichi Kogyo Seiyaku Co., Ltd.) PAOGEN PP-15) Toluene 7.5 parts by weight MEK 7.5 parts by weight Next, provided with the metal layer obtained as described above, and provided with a particulate abrasive and a surfactant on the surface. Polyethylene terephthalate film formed with mixed resin layer,
A 1 mm wide slit was formed into a longitudinal slit to obtain a flat thread-like film tape for scrubbing according to the present invention. Next, a flat yarn-shaped film tape for scrubbing was woven into a fabric formed by separately knitting fiber yarns so that the pile of the film tape was exposed on the surface, and used as a scrubbing brush. Also, using this scrubbing brush, a sponge as a core was put inside to form a bag, which was used as another scrubbing brush.
【００１５】実施例２（粒子状の研磨剤を混入した実施
例） 厚さ２５μｍの広幅長尺なポリエチレンテレフタレート
フイルムの片面に、真空蒸着により厚さ４５０ÅのＡｌ
蒸着層を形成して金属層とし、該金属層の上に、粒子状
の研磨剤として粒子径約３０μｍのα−酸化アルミナを
使用して、下記の組成の塗料により粒子状の研磨剤を混
入した厚さ４０μｍの樹脂層をリバースコートにより形
成した。 ポリエステル樹脂 １５．０重量部 （東洋紡績社製） α−酸化アルミナ １７．５重量部 （フジミインコーポレーテッド社製ＷＡ−４００） ポリアルキルオキサイド系界面活性剤 ０．１重量部 （第一工業製薬社製パオゲンＰＰ−１５） トルエン ７．５重量部 ＭＥＫ ７．５重量部 次に、上記のようにして得た、金属層を備えており、か
つ、表面に粒子状の研磨剤を混入した樹脂層を形成した
ポリエチレンテレフタレートフイルムを、１．５ｍｍの
幅で縦長にスリットして、本発明に係る偏平糸状のたわ
し用フイルムテープを得た。次いで、偏平糸状のたわし
用フイルムテープを、別途繊維糸を編成してなる生地
に、該フイルムテープのパイルが表面に露出するように
織り込んでたわしとした。また、このたわしを使用し、
芯体であるスポンジを中にして袋状にして、別のたわし
とした。Example 2 (Example in which a particulate abrasive was mixed) On one side of a wide and long polyethylene terephthalate film having a thickness of 25 μm, a 450 Å-thick Al film was formed by vacuum deposition.
A vapor-deposited layer is formed to form a metal layer, and α-alumina oxide having a particle diameter of about 30 μm is used as a particulate abrasive on the metal layer, and the particulate abrasive is mixed with a paint having the following composition. A resin layer having a thickness of 40 μm was formed by reverse coating. Polyester resin 15.0 parts by weight (manufactured by Toyobo Co., Ltd.) α-alumina oxide 17.5 parts by weight (WA-400 manufactured by Fujimi Incorporated) Polyalkyl oxide surfactant 0.1 parts by weight (Daiichi Kogyo Seiyaku Co., Ltd.) PAOGEN PP-15) Toluene 7.5 parts by weight MEK 7.5 parts by weight Next, a resin layer having the metal layer obtained as described above and having a surface mixed with a particulate abrasive. The polyethylene terephthalate film thus formed was slit longitudinally with a width of 1.5 mm to obtain a flat yarn-shaped film tape for scrubbing according to the present invention. Next, a flat yarn-shaped film tape for scrubbing was woven into a fabric formed by separately knitting fiber yarns so that the pile of the film tape was exposed on the surface, and used as a scrubbing brush. Also, using this scourer,
The sponge, which is the core, was put inside to form a bag and used as another scrubbing brush.
【００１６】実施例３（界面活性剤を混入した実施例） 厚さ２５μｍの広幅長尺なポリエチレンテレフタレート
フイルムの片面に、真空蒸着により厚さ４５０ÅのＡｌ
蒸着層を形成して金属層とし、該金属層の上に、界面活
性剤としてポリアルキルオキサイド系界面活性剤を使用
して、下記の組成の塗料により界面活性剤を混入した厚
さ２μｍの樹脂層をグラビアコートにより形成した。 エポキシ変性ポリエステル １０．０重量部 （東洋紡績社製） ポリアルキルオキサイド系界面活性剤 １．０重量部 （第一工業製薬社製パオゲンＰＰ−１５） トルエン ５．０重量部 ＭＥＫ ２．５重量部 次に、上記のようにして得た、金属層を備えており、か
つ、表面に界面活性剤を混入した樹脂層を形成したポリ
エチレンテレフタレートフイルムを、２ｍｍの幅で縦長
にスリットして、本発明に係る偏平糸状のたわし用フイ
ルムテープを得た。次いで、偏平糸状のたわし用フイル
ムテープを、別途繊維糸を編成してなる生地に、該フイ
ルムテープのパイルが表面に露出するように織り込んで
たわしとした。また、このたわしを使用し、芯体である
スポンジを中にして袋状にして、別のたわしとした。Example 3 (Example in which a surfactant was mixed) On one side of a wide and long polyethylene terephthalate film having a thickness of 25 μm, a 450 Å-thick Al film was formed by vacuum deposition.
A resin having a thickness of 2 μm in which a vapor-deposited layer is formed to form a metal layer, and a polyalkyl oxide-based surfactant is used as a surfactant on the metal layer, and the surfactant is mixed with a paint having the following composition. The layer was formed by gravure coating. Epoxy-modified polyester 10.0 parts by weight (manufactured by Toyobo Co., Ltd.) Polyalkyl oxide-based surfactant 1.0 part by weight (Paogen PP-15 manufactured by Dai-ichi Kogyo Seiyaku Co., Ltd.) Toluene 5.0 parts by weight MEK 2.5 parts by weight Next, the polyethylene terephthalate film provided with the metal layer and having the surface on which the resin layer mixed with the surfactant is formed is slit vertically with a width of 2 mm to obtain the present invention. The flat yarn-shaped film tape for scrubbing according to the above was obtained. Next, a flat yarn-shaped film tape for scrubbing was woven into a fabric formed by separately knitting fiber yarns so that the pile of the film tape was exposed on the surface, and used as a scrubbing brush. Also, using this scrubbing brush, a sponge as a core was put inside to form a bag, which was used as another scrubbing brush.
【００１７】[0017]
【発明の効果】この発明は、プラスチックフイルムの表
面に、粒子状の研磨剤と界面活性剤の両方又は一方を混
入した樹脂層を形成したから、これをたわしに使用した
ときには次のような効果がある。 フイルムテープのエッヂすなわち両端部分の角で研
磨・洗浄出来るばかりでなく、フイルムテープの表面部
分でも研磨・洗浄出来るから、研磨・洗浄の効率が非常
によい。 研磨・洗浄の効率が非常によいから、汚れがひどく
ない場合には、特に洗剤や石鹸を使用しなくても研磨・
洗浄出来る。 樹脂層に粒子状の研磨剤と界面活性剤を混入した場
合は、研磨・洗浄したときに研磨と洗浄がバランスよく
行える。 樹脂層に粒子状の研磨剤を混入した場合は、研磨・
洗浄したときに特に研磨効果が顕著であるから、汚れが
ひどいときに適している。 樹脂層に界面活性剤を混入した場合は、研磨・洗浄
したときに特に洗浄効果が顕著であるから、汚れがそれ
程ひどくないときに適している。According to the present invention, since a resin layer containing a particulate abrasive and / or a surface active agent is formed on the surface of a plastic film, the following effects are obtained when the resin layer is used as a scrubbing brush. There is. Not only can the edges of the film tape, that is, the corners at both ends, be polished and cleaned, but the surface of the film tape can also be polished and cleaned, so the polishing and cleaning efficiency is very good. The efficiency of polishing / cleaning is very good, so if dirt is not severe, polishing / cleaning can be performed without using detergent or soap.
Can be washed. When a particulate abrasive and a surfactant are mixed in the resin layer, polishing and cleaning can be performed in a well-balanced manner during polishing and cleaning. If a particulate abrasive is mixed in the resin layer,
Since the polishing effect is particularly remarkable when washed, it is suitable when the dirt is severe. When a surfactant is mixed in the resin layer, the cleaning effect is particularly remarkable when polishing / cleaning, and therefore it is suitable when the stain is not so severe.
【図１】この発明の一実施例を示す一部拡大断面図であ
る。FIG. 1 is a partially enlarged sectional view showing an embodiment of the present invention.
【図２】この発明の一実施例を示す一部拡大断面図であ
る。FIG. 2 is a partially enlarged sectional view showing an embodiment of the present invention.
【図３】この発明の一実施例を示す一部拡大断面図であ
る。FIG. 3 is a partially enlarged sectional view showing an embodiment of the present invention.
１０ プラスチックフイルム ２０ 粒子状の研磨剤と界面活性剤を混入した樹脂層 ３０ 粒子状の研磨剤を混入した樹脂層 ４０ 界面活性剤を混入した樹脂層 10 Plastic Film 20 Resin Layer Incorporating Particulate Abrasive and Surfactant 30 Resin Layer Incorporating Particle Abrasive 40 Resin Layer Incorporating Surfactant
フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｂ３２Ｂ 27/18 Ｚ 8413−4Ｆ Ｄ０１Ｆ 1/10 Continuation of the front page (51) Int.Cl. 6 Identification number Office reference number FI technical display location B32B 27/18 Z 8413-4F D01F 1/10
Claims (4)
研磨剤と界面活性剤を混入した樹脂層を形成したことを
特徴とする偏平糸状のたわし用フイルムテープ。1. A flat yarn-like film tape for scrubbing, wherein a resin layer containing a particulate abrasive and a surfactant is formed on the surface of a plastic film.
研磨剤を混入した樹脂層を形成したことを特徴とする偏
平糸状のたわし用フイルムテープ。2. A flat yarn-shaped film tape for scrubbing, comprising a resin layer containing a particulate abrasive mixed on the surface of a plastic film.
剤を混入した樹脂層を形成したことを特徴とする偏平糸
状のたわし用フイルムテープ。3. A flat yarn-shaped film tape for scrubbing, wherein a resin layer containing a surfactant is formed on the surface of a plastic film.
のである請求項１〜３のいずれか１項に記載の偏平糸状
のたわし用フイルムテープ。4. The flat thread-like film tape for scrubbing brush according to claim 1, wherein the plastic film is provided with a metal layer.