JPH07304143A - Packaging material - Google Patents
Packaging materialInfo
- Publication number
- JPH07304143A JPH07304143A JP12445694A JP12445694A JPH07304143A JP H07304143 A JPH07304143 A JP H07304143A JP 12445694 A JP12445694 A JP 12445694A JP 12445694 A JP12445694 A JP 12445694A JP H07304143 A JPH07304143 A JP H07304143A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- packaging material
- density polyethylene
- barrier layer
- adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、酒、ボディソープ、パ
ーマ液、練り歯磨きなどの浸透性の高い成分を含む内容
物を包装する用途に好適な包装材料に関するものであ
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a packaging material suitable for packaging contents containing highly penetrating ingredients such as liquor, body soap, perm solution and toothpaste.
【０００２】[0002]
【従来の技術】一般に種々の容器に用いられる包装材料
は、内容物に対しバリヤー性を有することを重視して選
択されることが多く、特に食品等の内容物に対しては内
容物の保存のみならず酸素、水蒸気等に対するバリヤー
性も含め高バリヤー層が用いられている。このようなバ
リヤー層としては、一般にアルミニウム等の金属箔、酸
化ケイ素等の無機物を蒸着したフィルム等が用いられ、
このバリヤー層の内側にヒートシール層として低密度ポ
リエチレンフィルム、または押し出しコートした低密度
ポリエチレン層を積層したものが用いられ、通常これら
は接着剤やアンカー剤を用いて積層されていた。2. Description of the Related Art In general, packaging materials used for various containers are often selected with an emphasis on having barrier properties with respect to contents, and particularly for contents such as foods, preservation of the contents. Not only is a high barrier layer used, including barrier properties against oxygen and water vapor. As such a barrier layer, a metal foil such as aluminum, a film deposited with an inorganic substance such as silicon oxide, or the like is generally used,
A low-density polyethylene film or an extrusion-coated low-density polyethylene layer is used as a heat-sealing layer on the inside of this barrier layer, and these are usually laminated using an adhesive or an anchoring agent.
【０００３】[0003]
【発明が解決しようとする課題】しかしながら、このよ
うな接着剤またはアンカー剤により貼り合わせた低密度
ポリエチレンをヒートシール層とした積層フィルムを用
いた包装材料を種々の浸透性の高い成分を含む内容物の
パッケージに適用させた場合、内容物に含まれる浸透性
の高い成分がバリヤー層で遮断されて内側の隣接層との
間に滞留し、その結果、例えば接着剤を侵し、層間の剥
離（デラミネーション）をひきおこす問題を生じる。ま
た、内容物の浸透性の高い成分がバリヤー層で完全には
遮断されず一部透過した場合には、バリヤー層の外側の
接着剤も侵してしまい、この部位での層間剥離を引き起
こす場合もあった。However, a packaging material using a laminated film having a heat-sealing layer of low-density polyethylene bonded with such an adhesive or anchor agent contains various highly permeable components. When applied to the packaging of a product, a highly permeable component contained in the content is blocked by the barrier layer and stays between the inner adjacent layer, and as a result, for example, it attacks the adhesive and peels between layers ( Delamination) causes a problem. In addition, when a highly permeable component of the content is not completely blocked by the barrier layer but partially penetrates, the adhesive on the outer side of the barrier layer is also attacked, which may cause delamination at this site. there were.
【０００４】一方、積層する際、接着剤を用いずに、熱
溶融樹脂（例えばポリエチレン等）を押し出しながら貼
り合わせるいわゆるサンドラミネーション法による積層
方法も従来より知られているが、バリヤー層である酸化
ケイ素やアルミニウム等の蒸着層は熱に弱く、場合によ
ってはクラックが生じてバリヤー性が損なわれるという
問題がある。さらに、このサンドラミネーション法によ
る積層方法は接着剤を用いる方法に比べると、バリヤー
層とヒートシール性樹脂層との組み合わせの自由度が低
く、用いる樹脂が特定され内容物に対応する包装材料の
選定が困難で、接着剤を用いた積層方法を採用する方が
内容物に対応した包装材料が選定し易く好ましいと言え
る。On the other hand, a laminating method by a so-called sand lamination method in which a hot-melt resin (for example, polyethylene) is bonded while being extruded without using an adhesive at the time of laminating is conventionally known, but oxidation as a barrier layer is known. The vapor-deposited layer of silicon, aluminum, or the like is vulnerable to heat, and there is a problem that in some cases cracks occur and the barrier property is impaired. In addition, the laminating method by the sand lamination method has a lower degree of freedom in combination of the barrier layer and the heat-sealable resin layer as compared with the method using an adhesive, and the resin to be used is specified and the packaging material corresponding to the contents is selected. It is difficult to do so, and it can be said that it is preferable to adopt a laminating method using an adhesive because a packaging material corresponding to the contents can be easily selected.
【０００５】ところで、本発明者等は、上記の接着剤を
用いて積層した場合の層間剥離の問題を解決するべく、
接着剤の改良及びヒートシール層の改良について検討し
たが、接着剤の改良については耐薬品性が優れた４種類
ほどの代表的な接着剤を用いバリヤー層と低密度ポリエ
チレンフィルムとを積層した包装材料について検討した
ところ特に有意な差は見られず改良効果はなかった。ま
た、ヒートシール層の改良については、従来の低密度ポ
リエチレンの代わりに耐薬品性の優れたポリアクリロニ
トリル、エチレン−酢酸ビニル共重合体ケン化物、ポリ
エステル等を用いることが考えられるが、ヒートシール
条件、製袋等の加工適性、シール強度等に問題があり、
いずれも使用には不適当であった。By the way, the present inventors have tried to solve the problem of delamination when laminated using the above adhesive.
The improvement of the adhesive and the improvement of the heat-sealing layer were examined. Regarding the improvement of the adhesive, a package in which a barrier layer and a low density polyethylene film were laminated using about four types of typical adhesives having excellent chemical resistance. When the materials were examined, no significant difference was found and there was no improvement effect. Further, for the improvement of the heat-sealing layer, it is conceivable to use polyacrylonitrile having excellent chemical resistance, saponified ethylene-vinyl acetate copolymer, polyester or the like instead of conventional low-density polyethylene, under heat-sealing conditions. , There is a problem in processing suitability such as bag making, sealing strength, etc.
Neither was suitable for use.
【０００６】そこで、ヒートシール層の材質として、上
記問題のない、コスト的にも低密度ポリエチレンと同等
の中密度ポリエチレンを用いて耐薬品保存テストを行っ
たところ、香料等の浸透性の高い成分を含む内容物、例
えばパーマ液においてもバリヤー層と接着剤を介した隣
接層との間の密着性が良好であり層間剥離の改良効果が
あることを見いだし、本発明を為すに到ったものであ
る。Therefore, as a material of the heat-sealing layer, a medium-density polyethylene having the above-mentioned problems and having the same cost as the low-density polyethylene was used, and a chemical resistance storage test was conducted. It has been found that, even in a content containing, for example, a perm solution, the adhesion between the barrier layer and the adjacent layer via the adhesive is good and the effect of improving delamination is improved, and the present invention has been accomplished. Is.
【０００７】すなわち、本発明の目的とするところは、
浸透性の高い成分を含む内容物に対して層間剥離等の不
具合を生じることなく優れたバリヤー性を有する包装材
料を提供することにある。That is, the object of the present invention is to
It is an object of the present invention to provide a packaging material having an excellent barrier property without causing a problem such as delamination of contents containing a component having high permeability.
【０００８】[0008]
【課題を解決するための手段】上記目的を達成するため
に、本発明の包装材料は、少なくとも、バリヤー層の内
容物と接する側に接着剤を介して中密度ポリエチレンフ
ィルムを積層してなることを特徴としている。To achieve the above object, the packaging material of the present invention comprises at least a medium density polyethylene film laminated with an adhesive on the side of the barrier layer which is in contact with the contents. Is characterized by.
【０００９】また、本発明の包装材料は、前記中密度ポ
リエチレンフィルムを最内層としたことを特徴としてい
る。Further, the packaging material of the present invention is characterized in that the medium density polyethylene film is used as the innermost layer.
【００１０】また、本発明の包装材料は、前記中密度ポ
リエチレンフィルムを介在層とし、さらに内容物と接す
る側に低密度ポリエチレンからなる最内層を設けたこと
を特徴としている。The packaging material of the present invention is characterized in that the medium density polyethylene film is used as an intervening layer, and an innermost layer made of low density polyethylene is provided on the side in contact with the contents.
【００１１】さらに、本発明の包装材料は、前記バリヤ
ー層の外方の面に基材層を積層してなることを特徴とし
ている。Further, the packaging material of the present invention is characterized in that a base material layer is laminated on the outer surface of the barrier layer.
【００１２】さらにまた、本発明の包装材料は、前記バ
リヤー層が、無機化合物や金属等を蒸着したプラスチッ
クフィルムであることを特徴としている。Furthermore, the packaging material of the present invention is characterized in that the barrier layer is a plastic film formed by vapor deposition of an inorganic compound, a metal or the like.
【００１３】以下、本発明の構成を更に詳しく説明す
る。The structure of the present invention will be described in more detail below.
【００１４】本発明の包装材料は、図１に示すように、
バリヤー層３の内容物と接する面にヒートシール層とし
て中密度ポリエチレンフィルム５を接着剤４を介して積
層したものである。または、図２に示すように、中密度
ポリエチレンフィルム５を介在層とし、接着剤を介さず
に直接低密度ポリエチレンを溶融押し出しして最内層６
を形成した包装材料である。The packaging material of the present invention, as shown in FIG.
A medium density polyethylene film 5 is laminated as a heat-sealing layer on the surface of the barrier layer 3 in contact with the contents with an adhesive 4 interposed therebetween. Alternatively, as shown in FIG. 2, the medium density polyethylene film 5 is used as an intervening layer, and the low density polyethylene is directly melt extruded without using an adhesive to form the innermost layer 6
Is a packaging material formed.
【００１５】本発明における中密度ポリエチレンとは、
密度が０．９２５〜０．９４０ｇ／ｃｍ3 の範囲にある
ポリエチレンをいう。密度がこのような範囲にある中密
度ポリエチレンフィルムをヒートシール層または介在層
として用いることにより、接着剤を用いた積層方法を採
用した場合において、内容物として香料等の浸透性の高
い成分を含む例えばパーマ液などを充填しても、バリヤ
ー層との層間の接着強度が低下せず、層間剥離を防止で
きる。また、中密度ポリエチレンフィルムを介在層と
し、さらに最内層として低密度ポリエチレンを溶融押し
出し形成することにより、両層が溶融一体化するので、
両層の剥離が発生しない。The medium density polyethylene in the present invention means
It refers to polyethylene having a density in the range of 0.925 to 0.940 g / cm 3 . By using a medium-density polyethylene film having a density in such a range as a heat-sealing layer or an intervening layer, when a lamination method using an adhesive is adopted, the content contains a highly permeable component such as a fragrance. For example, even when a perm solution or the like is filled, the adhesive strength between the barrier layer and the interlayer does not decrease, and delamination can be prevented. In addition, since a medium density polyethylene film is used as an intervening layer, and low density polyethylene is melt-extruded and formed as the innermost layer, both layers are melted and integrated,
Peeling of both layers does not occur.
【００１６】本発明におけるバリヤー層３は例えば、ポ
リエステル樹脂等のプラスチックフィルム１の少なくと
も一方の面にＳｉＯｘ（ｘは１〜２）、ＭｇＯ等の無機
化合物やＡｌ等の金属の蒸着層２を形成したものであ
る。プラスチックフィルムとしてはナイロン、延伸ポリ
ビニルアルコール、延伸ポリプロピレン、ポリエチレン
テレフタレート等が好ましく用いられる。また、蒸着層
の厚さとしては、例えばＳｉＯｘは３００〜２０００オ
ングストローム、Ａｌは３００〜１０００オングストロ
ームが好ましい。また、バリヤー層としてＡｌ箔等の金
属箔を用いることもできる。なお、プラスチックフィル
ムに蒸着層を設ける際、アンカー剤層を介して設けるこ
とが、蒸着層の密着強度の向上、経時的な密着強度の低
下が小さく好ましい。As the barrier layer 3 in the present invention, for example, a vapor deposition layer 2 of an inorganic compound such as SiOx (x is 1 to 2), MgO or a metal such as Al is formed on at least one surface of a plastic film 1 such as a polyester resin. It was done. As the plastic film, nylon, drawn polyvinyl alcohol, drawn polypropylene, polyethylene terephthalate, etc. are preferably used. The thickness of the vapor deposition layer is preferably 300 to 2000 angstroms for SiOx and 300 to 1000 angstroms for Al. Alternatively, a metal foil such as an Al foil may be used as the barrier layer. When the vapor deposition layer is provided on the plastic film, it is preferable that the vapor deposition layer is provided via an anchor agent layer because the adhesion strength of the vapor deposition layer is improved and the adhesive strength is not lowered with time.
【００１７】また、上記バリヤー層がプラスチックフィ
ルムの一方の面のみに蒸着層を有するものである場合、
これを包装材料として用いるときは蒸着層を内側、すな
わち内容物と接する側とすることが好ましい。これは、
内容物の浸透性の高い成分を蒸着層で遮断することによ
りプラスチックフィルムと蒸着層との密着強度が低下す
ることを防止できるからである。When the barrier layer has a vapor deposition layer on only one surface of the plastic film,
When this is used as a packaging material, it is preferable that the vapor-deposited layer is on the inside, that is, on the side in contact with the contents. this is,
This is because it is possible to prevent the adhesive strength between the plastic film and the vapor deposition layer from being lowered by blocking the highly permeable components of the contents with the vapor deposition layer.
【００１８】本発明の包装材料は上述の如く、バリヤー
層の内容物と接する面に中密度ポリエチレンフィルムを
積層したものであるが、さらに包装材料としての適当な
剛性を付与し包装材料を例えば図３に示す液体紙容器８
や図４に示すラミネートチューブ容器９として用いるに
好適な構成として、バリヤー層の中密度ポリエチレンフ
ィルムを積層した側と反対の面に基材層７を積層するこ
とが出来る。この基材層として、液体紙容器の場合、紙
を、ラミネートチューブ容器の場合、積層プラスチック
フィルムを用いる。具体的には、ポリエステル、延伸ナ
イロン等のプラスチックフィルム、プラスチックフィル
ムと紙の積層体等が好ましく用いられる。As described above, the packaging material of the present invention comprises a medium density polyethylene film laminated on the surface of the barrier layer which is in contact with the contents. Liquid paper container 8 shown in FIG.
As a structure suitable for use as the laminated tube container 9 shown in FIG. 4 and FIG. 4, the substrate layer 7 can be laminated on the surface opposite to the side on which the medium density polyethylene film of the barrier layer is laminated. As the base material layer, paper is used for a liquid paper container, and a laminated plastic film is used for a laminated tube container. Specifically, a plastic film such as polyester or stretched nylon, a laminate of a plastic film and paper, or the like is preferably used.
【００１９】図３に示す液体紙容器に用いる包装材料の
具体例としては以下の構成が例示できる。The following constitutions can be given as specific examples of the packaging material used for the liquid paper container shown in FIG.
【００２０】 また、図４に示すラミネートチューブ容器の胴部材に用
いる包装材料の具体例としては以下の構成が例示でき
る。[0020] The following constitutions can be given as specific examples of the packaging material used for the body member of the laminated tube container shown in FIG.
【００２１】 ここで、上記の（ ）の数字は厚さを示し、蒸着層はオ
ングストロームの単位、紙および接着剤はｇ／ｍ2 の単
位、その他はμｍの単位である。[0021] Here, the numbers in parentheses () indicate the thickness, the vapor deposition layer is in the unit of Angstrom, the paper and the adhesive are in the unit of g / m 2 , and the others are in the unit of μm.
【００２２】ＬＤＰＥ：低密度ポリエチレン ＭＤＰＥ：中密度ポリエチレン ＰＥＴ：ポリエチレンテレフタレート ＥＭＡＡ：エチレン−メタアクリル酸共重合体 ＡＤ：接着剤 Ａｌ箔：アルミニウム箔 乳白ＰＥ：乳白低密度ポリエチレン ＳｉＯｘ：酸化ケイ素蒸着層LDPE: Low density polyethylene MDPE: Medium density polyethylene PET: Polyethylene terephthalate EMAA: Ethylene-methacrylic acid copolymer AD: Adhesive Al foil: Aluminum foil Milky white PE: Milky low density polyethylene SiOx: Silicon oxide vapor deposition layer
【００２３】[0023]
【作用】本発明の包装材料は、バリヤー層の内容物と接
する側の面にヒートシール層または介在層として中密度
ポリエチレンフィルムを接着剤を介して積層することに
より、接着剤を用いた積層方法を採用した場合におい
て、内容物として浸透性の高い成分を含む例えばパーマ
液などを充填しても、内容物の浸透によりバリヤー層と
の層間の接着強度が低下するのを防ぐため、層間剥離を
防止できる。In the packaging material of the present invention, a medium density polyethylene film as a heat seal layer or an intervening layer is laminated on the surface of the barrier layer which is in contact with the contents with an adhesive, whereby a laminating method using an adhesive is used. In the case of adopting, the delamination is performed in order to prevent the adhesive strength between the barrier layer and the interlayer from decreasing due to the permeation of the content even if the content is filled with, for example, a perm solution containing a highly permeable component. It can be prevented.
【００２４】したがって、本発明の包装材料は、浸透性
の高い成分を含む内容物の容器の包装材料として特に好
適である。Therefore, the packaging material of the present invention is particularly suitable as a packaging material for a container of a content containing a highly permeable component.
【００２５】[0025]
【実施例】以下に実施例を示して本発明を更に具体的に
説明する。EXAMPLES The present invention will be described more specifically with reference to the following examples.
【００２６】表面をポリエステルウレタンコートした厚
さ１２μｍのポリエチレンテレフタレートフィルムの一
方の面にＳｉＯｘを４００オングストロームの厚さに真
空蒸着により形成してなるバリヤー層の内側、即ちＳｉ
Ｏｘの蒸着面に二液硬化型接着剤Ａ−５１５（武田薬品
工業（株）製）を３ｇ／ｍ2 塗布し、厚さ５０μｍの中
密度ポリエチレンフィルム（タマポリ（株）製：ＮＢ−
１；密度０．９３０ｇ／ｃｍ3 ）を積層して本発明の構
成に係る包装材料を作製した。The inside of a barrier layer formed by vacuum deposition of SiOx to a thickness of 400 angstroms on one surface of a polyethylene terephthalate film having a thickness of 12 μm and having a surface coated with polyester urethane, that is, Si
Two-component curing adhesive A-515 (manufactured by Takeda Pharmaceutical Co., Ltd.) was applied on the vapor deposition surface of Ox at 3 g / m 2 , and a medium-density polyethylene film having a thickness of 50 μm (manufactured by Tama Poly Corporation: NB-) was applied.
1; a density of 0.930 g / cm 3 ) was laminated to produce a packaging material according to the constitution of the present invention.
【００２７】また、比較例として、上記構成の中密度ポ
リエチレンの代わりに、厚さ６０μｍの低密度ポリエチ
レンフィルム（タマポリ（株）製：ＡＪ−１；密度０．
９２０ｇ／ｃｍ3 ）を積層した包装材料を作製した。As a comparative example, a low-density polyethylene film having a thickness of 60 μm (manufactured by Tama Poly Co., Ltd .: AJ-1; density 0.
A packaging material was prepared by laminating 920 g / cm 3 ).
【００２８】次いで、上記本発明及び比較例の構成を有
する包装材料を用いて１０×１０ｃｍ（内寸）の大きさ
の四方シールパウチをそれぞれ作製し、それぞれに３０
ｃｃの市販のパーマ液を充填密封し、これらを２０℃、
４０℃にて１ケ月の保存テストを行い、保存後のラミネ
ート強度を測定した。Next, using the packaging materials having the constitutions of the present invention and the comparative example described above, four-sided seal pouches each having a size of 10 × 10 cm (inner dimension) were prepared, and 30 pieces each were prepared.
cc commercially available perm solution is filled and sealed, and these are kept at 20 ° C.,
A storage test was carried out at 40 ° C. for 1 month, and the laminate strength after storage was measured.
【００２９】表１および表２にその結果を示す。なお、
ラミネート強度の単位はｇ／１５ｍｍ（試料の幅１５ｍ
ｍ、９０度剥離、剥離スピード３００ｍｍ／分）で示し
た。The results are shown in Tables 1 and 2. In addition,
The unit of laminate strength is g / 15mm (width of sample is 15m
m, 90 degree peeling, peeling speed 300 mm / min).
【表１】 [Table 1]
【００３０】[0030]
【表２】 表１および表２の結果から、内容物を充填する前の初期
強度は、本発明、比較例ともほぼ同じ強度を示している
が、保存テストを行うと、ラミネート強度に約２倍の差
がみられ、本発明の包装材料は、浸透性の高い成分を含
むパーマ液においてもバリヤー層との層間の密着性が良
好であり、内容物の浸透による剥離を防止できることが
わかる。[Table 2] From the results of Table 1 and Table 2, the initial strength before filling the contents is almost the same in the present invention and the comparative example, but when a storage test is conducted, there is a difference of about 2 times in the laminate strength. It can be seen that the packaging material of the present invention has good adhesion between the barrier layer and the layer even in a perm solution containing a highly permeable component, and can prevent peeling of the contents due to permeation.
【００３１】[0031]
【発明の効果】以上詳細に説明したように、本発明の包
装材料によれば、バリヤー層の内容物と接する側の面に
ヒートシール層または介在層として中密度ポリエチレン
フィルムを接着剤を介して積層することにより、接着剤
を用いた積層方法を採用した場合において、内容物とし
て浸透性の高い成分を含む例えばパーマ液などを充填し
ても、内容物の浸透によりバリヤー層との層間の接着強
度が低下するのを防ぎ、層間剥離を防止できるという優
れた効果を奏する。As described in detail above, according to the packaging material of the present invention, a medium-density polyethylene film is used as a heat-sealing layer or an intervening layer on the surface of the barrier layer which is in contact with the contents through an adhesive. By laminating, when a laminating method using an adhesive is adopted, even if a perm solution containing a highly permeable component is filled as the content, the adhesion of the layer to the barrier layer due to the permeation of the content It has an excellent effect that the strength is prevented from being lowered and the delamination can be prevented.
【００３２】すなわち、本発明の包装材料は、浸透性の
高い成分を含む内容物を包装するためのヒートシールに
より組立て密封する液体紙容器、フレキシブルパウチ、
ラミネートチューブ容器に用いることが可能となった。That is, the packaging material of the present invention is a liquid paper container, a flexible pouch, which is assembled and sealed by heat sealing for packaging contents containing highly penetrating components.
It became possible to use it for a laminated tube container.
【図１】本発明の包装材料の一例を示す断面図である。FIG. 1 is a cross-sectional view showing an example of a packaging material of the present invention.
【図２】本発明の包装材料の他の例を示す断面図であ
る。FIG. 2 is a cross-sectional view showing another example of the packaging material of the present invention.
【図３】本発明の包装材料を用いた容器の一例を示す斜
視図である。FIG. 3 is a perspective view showing an example of a container using the packaging material of the present invention.
【図４】本発明の包装材料を用いた容器の他の例を示す
斜視図である。FIG. 4 is a perspective view showing another example of a container using the packaging material of the present invention.
１ プラスチックフィルム ２ 蒸着層 ３ バリヤー層 ４ 接着剤 ５ 中密度ポリエチレンフィルム ６ 最内層 ７ 基材層 1 Plastic Film 2 Deposition Layer 3 Barrier Layer 4 Adhesive 5 Medium Density Polyethylene Film 6 Innermost Layer 7 Base Material Layer
Claims (5)
る側に接着剤を介して中密度ポリエチレンフィルムを積
層してなることを特徴とする包装材料。1. A packaging material, characterized in that a medium density polyethylene film is laminated at least on the side of the barrier layer which is in contact with the contents with an adhesive.
層としたことを特徴とする請求項１記載の包装材料。2. The packaging material according to claim 1, wherein the medium density polyethylene film is the innermost layer.
層とし、その内容物と接する側に低密度ポリエチレンか
らなる最内層を設けたことを特徴とする請求項１記載の
包装材料。3. The packaging material according to claim 1, wherein the medium-density polyethylene film is used as an intervening layer, and an innermost layer made of low-density polyethylene is provided on the side in contact with the contents.
層してなることを特徴とする請求項１乃至３のいずれか
に記載の包装材料。4. The packaging material according to claim 1, wherein a substrate layer is laminated on the outer surface of the barrier layer.
を蒸着したプラスチックフィルムであることを特徴とす
る請求項１乃至４のいずれかに記載の包装材料。5. The packaging material according to claim 1, wherein the barrier layer is a plastic film on which an inorganic compound, a metal or the like is vapor-deposited.