JPH0747713B2 - Polish protectant - Google Patents

Description

Detailed Description of the Invention

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a polishing protector for objects such as marble, granite, tiles and other materials .

[0002]

2. Description of the Related Art When a conventional polishing agent mainly composed of natural wax and synthetic wax is used for polishing the surface of stones such as marble and granite, the stone particles are innumerable due to the abrasive particles contained in the polishing agent. It is common to have scratches on the skin, and as a result, molds and the like will be generated on the wound, and dirt will be noticeable.Because surface dirt cannot be completely removed, it is possible to maintain beauty for a long period of time. There were drawbacks such as difficulty.

[0003]

[0007] Accordingly, the present invention is large <br/> management stones, by polishing and protecting without damaging the surface of the fine stone such as granite, facilitating wiping of the front surface contamination holds I cotton was beautiful of the surface a long time in the, it is an object to provide a polish protective agent so as to give a glossy deep in stone surface.

[0004] Further, the present invention is, in addition to the stone, tile, wood, metal material, synthetic resin material, a glass material, dropping dirt from the simple object of surface constituted by various materials such as rubber material At the same time, it is an object of the present invention to provide a polishing protector capable of maintaining beauty over a long period of time.

[0005]

According to the present invention, natural wax and synthetic wax are 9.5 to 30%, and petroleum solvent is 90 to 60%.
And 0.5 to 10% of pigment in a semi-kneaded state, which is a polishing protector.

[0006]

[Function] When it is desired to wipe off various stains on a surface such as a floor surface or a wall surface constructed by using a stone material, a wood material, a synthetic resin material or the like, the agent of the present invention is applied to a sponge and the like. Abut the dirty surface and polish. Then, the present invention agent to penetrate the dirt layer, such as only to biting on the surface of the material,
The stains such as the stains are sucked up, and the stains are eventually lifted. When this happens, you can wipe it off completely.

[0007]

EXAMPLES The constituents of the polish protectant of the present invention are as follows. Natural wax and synthetic wax 9.5-30% Petroleum solvent 90-60% Pigment 0.5-10%

(1) As the natural wax, carnauba wax, montan wax, beeswax, paraffin wax, etc. are used. (2) For synthetic wax, Fischer-Tropsch wax,
Oxidized polyethylene wax, microcrystalline wax, fatty acid ester wax, etc. are used. (3) As the petroleum solvent, an iso or normal paraffin petroleum solvent having a boiling point of 100 to 200 ° C. is used. (4) As the pigment, a pigment of any color such as white, black, or red is used. This is because it is necessary to change the hue of the polishing agent depending on the application.

The specific formulation examples are as follows. Carnauba wax (natural wax) 3% Fischer-Tropsch wax (synthetic wax) 10% Fatty acid ester wax (same as above) 1% Oxidized polyethylene wax (same as above) 1% Mineral spirit (petroleum solvent) 83% Mine (pigment) 2% 100% ( Parts by weight)

The polishing protection agent thus constituted is in a semi-kneaded state.

In the present invention, the natural wax and the synthetic wax are used for the purpose of polishing and protecting the stone surface. The reason why the petroleum solvent is used is to stably disperse the pigment on the entire surface and remove oily stains on the surface.

The pigment is used in order to enhance the cleaning property for oily stains on the protective coating on the stone surface and the cleaning property for aqueous stains and bulky stains.

[0013] For washing Kiyoshisaku by the pigment, from weaker than general abrasive particles, there is no damage the surface of the target material. In addition, the pigment applied according to the hue of the stone material makes it possible to improve the total surface area as compared with the film formed by only the wax.
It will give depth to gloss surface by immersion Toru action.

[0014]

Effect of the Invention] Dali stone, not only raise beautifully polished without damaging the surface of the fine stone such as granite, the table
By penetrating into the inside of the surface, it becomes possible to create a gloss with a three-dimensional depth, and it can be used for building holes and parts.
It is a very effective polish protector for the maintenance and management of various stones and tiles used on the inside and outside of the building 's walls and floors.
It

Further, the agent of the present invention is also effective for polishing a metal surface of an automobile body or the like and removing stains .

[0016] Also, floors, wall surfaces, and ceiling surfaces of painted wood
Even if it gets dirty, it will penetrate the wood.
It can be removed by sucking it up,
Normal without any effect such as peeling off the painted surface
Can be kept in a good condition, and even if a protective agent is applied, this
Since it penetrates into the interior, the applied floor surface does not slip and it is safe
Then you can walk.

The present invention, the material, no matter what, but to create a protective coating that beautifully retains its polished surface over time with decreasing the Re-fouling Mitsui has various on the surface of the target completely.

Claims (1)

[Claims] 1. A polishing protector comprising a natural wax and a synthetic wax in an amount of 9.5 to 30%, a petroleum solvent in an amount of 90 to 60%, and a pigment in an amount of 0.5 to 10% in a semi-kneaded state.