JPH08106253A - label - Google Patents
labelInfo
- Publication number
- JPH08106253A JPH08106253A JP24109994A JP24109994A JPH08106253A JP H08106253 A JPH08106253 A JP H08106253A JP 24109994 A JP24109994 A JP 24109994A JP 24109994 A JP24109994 A JP 24109994A JP H08106253 A JPH08106253 A JP H08106253A
- Authority
- JP
- Japan
- Prior art keywords
- label
- layer
- paper
- base material
- sealing layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、ビール瓶等容器に貼着
して用いるラベルに関するもので、耐水性と洗浄時の剥
離性の両方を兼ね備えたラベルに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a label which is attached to a container such as a beer bottle and used, and more particularly to a label which has both water resistance and peelability during washing.
【０００２】[0002]
【従来の技術】ビール、酒等が充填されているガラス瓶
等の容器には、商品名や内容を表示するため、予め前記
内容等が印刷されたラベルを、接着剤を介して貼着して
いる。このようにラベルを貼着した瓶等の容器は、冷蔵
庫に入れて冷却する等して、ラベルの表面に水滴が付着
した場合、ラベルにしわが発生したり、ラベル表面に設
けた印刷層に亀裂が発生することがあった。2. Description of the Related Art To a container such as a glass bottle filled with beer, liquor, etc., a label on which the above contents are printed is attached by an adhesive in order to display the product name and contents. There is. Containers such as bottles with the label attached in this way are placed in a refrigerator and cooled, and if water drops adhere to the surface of the label, wrinkles occur on the label or cracks occur in the printing layer provided on the label surface. May occur.
【０００３】また、容器がガラス瓶の場合、容器を再使
用するため、使用後回収された瓶は、５０〜８０℃に加
熱された、濃度が３％前後の水酸化ナトリウム水溶液
（アルカリ溶液）に浸漬したり、あるいはブラシ掛けに
より洗浄し、ラベルを剥離していた。Further, when the container is a glass bottle, since the container is reused, the bottle recovered after use is heated to 50 to 80 ° C., and the aqueous sodium hydroxide solution (alkali solution) having a concentration of about 3% is used. The label was peeled off by dipping or washing with a brush.
【０００４】使用時あるいは保管時に、ラベルにしわが
発生したり、ラベル表面に設けた印刷層に亀裂が発生し
たりすることを防止するため、例えば実開昭５９−１７
０８６９号には、基材に用いる紙として、水中伸度が
２．５％以下と小さいものを用いることが提案されてい
る。なお、上記「水中伸度」は、試料に予め１０ｃｍ間
隔の標点を記し、水に１２時間浸漬したときの標点間隔
を測定し、その伸び率を表したものである。また、この
ラベルでは、アルカリ溶液によるラベルの剥離性（洗瓶
性）を高めるため、印刷層やオーバーコート層の樹脂に
アルカリ可溶な樹脂を採用している。In order to prevent the label from wrinkling or the printing layer provided on the surface of the label from cracking during use or storage, for example, in Japanese Utility Model Laid-Open No. 59-17.
No. 0869 proposes to use paper having a small underwater elongation of 2.5% or less as a base material. In addition, the above-mentioned "underwater elongation" expresses the elongation rate by marking the mark points at 10 cm intervals in advance on the sample, measuring the mark point intervals when immersed in water for 12 hours. Further, in this label, an alkali-soluble resin is used as the resin of the printing layer or the overcoat layer in order to enhance the peelability (washing property) of the label with an alkaline solution.
【０００５】しかし、前記のように、基材の紙自体の水
中伸度を小さくするのにも限度があり、水中伸度が約１
％の紙を用いた場合でも、ラベルにしわが発生したり、
ラベル表面に設けた印刷層に亀裂が発生する場合がある
ことが判った。However, as described above, there is a limit to reducing the underwater elongation of the base paper itself, and the underwater elongation is about 1 or less.
Wrinkles on the label,
It has been found that cracks may occur in the printed layer provided on the label surface.
【０００６】[0006]
【発明が解決しようとする課題】このように、従来の技
術では、しわが発生したり印刷層等に亀裂が発生するこ
とがない耐水性を有し、しかもアルカリ溶液で簡単に剥
離することができるラベル、すなわち、ガラス瓶等の容
器に貼着したときの安定した耐水性、剥離性を兼ね備え
たラベルを得ることが困難であった。As described above, according to the prior art, it has water resistance that does not cause wrinkles or cracks in the printed layer, and can be easily peeled off with an alkaline solution. It has been difficult to obtain a label that can be produced, that is, a label that has stable water resistance and peelability when attached to a container such as a glass bottle.
【０００７】そこで本発明は、従来と同等の剥離性を維
持したまま、高い耐水性を有するラベルを提供すること
を目的とする。[0007] Therefore, it is an object of the present invention to provide a label having high water resistance while maintaining the peelability equivalent to the conventional one.
【０００８】[0008]
【課題を解決するための手段】すなわち本発明は、片面
にアルカリ可溶な樹脂からなる目止め層を設けた紙から
なる基材の前記目止め層上に少なくとも印刷層を設け
た、容器貼着用ラベルにおいて、前記基材の水中伸度を
０．５％以下としたことを特徴としたラベルである。上
記ラベルにおいて、基材の紙には故紙を１０％以内の範
囲で含む紙を用いることができる。また、基材の裏面
（紙の目止め層を設けていない面）には接着層を設ける
ことができる。[Means for Solving the Problems] That is, the present invention provides a container sticker in which at least a printing layer is provided on the sealing layer of a base material made of paper having a sealing layer made of an alkali-soluble resin on one surface. In a worn label, the underwater elongation of the base material is 0.5% or less. In the above label, as the base paper, paper containing waste paper within 10% can be used. Further, an adhesive layer can be provided on the back surface of the base material (the surface of the paper on which the sealing layer is not provided).
【０００９】[0009]
基材；すなわち紙に目止め層を設けた状態での水中伸度
を０．５％以下とすることにより、基材上に設けた印刷
層等に亀裂が発生することを防止でき、また、ラベルの
しわの発生を防止することができる。また、紙の上に直
接印刷層等を設けず、アルカリ溶液に可溶な目止め層を
介して設けているので、使用後容器からラベルを容易に
洗浄剥離することが可能である。Base material; that is, by setting the underwater elongation to 0.5% or less in the state where the sealing layer is provided on the paper, it is possible to prevent cracks from occurring in the printed layer or the like provided on the base material, and Wrinkles on the label can be prevented. In addition, since the printing layer or the like is not directly provided on the paper but is provided via the sealing layer which is soluble in the alkaline solution, it is possible to easily wash and peel the label from the container after use.
【００１０】[0010]
【実施例】図１に示した本発明の一実施例のラベルは、
紙１の片面にアルカリ溶液に可溶な樹脂からなる目止め
層２を設けた基材８、この目止め層２上に印刷層３、オ
ーバーコート層４を順次設けたラベルである。このラベ
ルは、例えば澱粉糊を用いて容器に貼着することができ
る。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The label of one embodiment of the present invention shown in FIG.
This is a label in which a base material 8 in which a sealing layer 2 made of a resin soluble in an alkaline solution is provided on one surface of a paper 1, a printing layer 3 and an overcoat layer 4 are sequentially provided on the sealing layer 2. The label can be applied to the container using, for example, starch paste.
【００１１】また、図２に示した本発明の他の実施例の
ラベルは、上記ラベルの紙１の裏面に、予め接着層７を
設けた構成のラベルである。この接着層７に用いる接着
剤は、８０℃以上に加熱されると粘着性を発揮する、デ
ィレードタック型接着剤が好ましい。特に、アクリル系
ディレードタック型接着剤は、特開平５−７７８３５号
公報に示されたようなマスキング剤が擦り傷防止のため
にコートされたガラス瓶に対しても優れた接着性を示
し、また、アルカリ溶液に可溶で、ラベルに塗布形成し
ても洗瓶性を損なうことがない。The label of another embodiment of the present invention shown in FIG. 2 is a label having an adhesive layer 7 previously provided on the back surface of the paper 1 of the above label. The adhesive used for the adhesive layer 7 is preferably a delayed tack type adhesive that exhibits tackiness when heated to 80 ° C. or higher. In particular, the acrylic delayed tack type adhesive shows excellent adhesiveness even to a glass bottle coated with a masking agent for preventing scratches as disclosed in JP-A-5-77835, and also has an alkaline property. It is soluble in the solution and does not impair the bottle washability even when applied to the label.
【００１２】本発明のラベルには、金属光沢を付与する
ためにアルミニウム蒸着層を設けてもよく、この場合
は、図３に示すように、目止め層２上にアルミニウム蒸
着層５、アンカーコート層６を順次設け、さらに印刷層
３、およびオーバーコート層４を順に設けた構成とする
ことができる。The label of the present invention may be provided with an aluminum vapor deposition layer for imparting a metallic luster. In this case, as shown in FIG. 3, the aluminum vapor deposition layer 5 and the anchor coat are provided on the sealing layer 2. The layer 6 may be sequentially provided, and the printing layer 3 and the overcoat layer 4 may be sequentially provided.
【００１３】ここで、ラベルに用いる目止め層２は上述
のようにアルカリ可溶なものを用いるが、印刷層３、オ
ーバーコート層４、およびアンカーコート層６のいずれ
についても同様に、洗瓶時のアルカリ溶液に可溶な材料
を用いることが望ましい。Here, as the sealing layer 2 used for the label, the one soluble in alkali is used as described above, but the printing layer 3, the overcoat layer 4 and the anchor coat layer 6 are similarly washed in bottles. It is desirable to use a material that is soluble in the alkaline solution at that time.
【００１４】次に本発明のラベルに用いる材料について
具体的に説明する。Next, the material used for the label of the present invention will be specifically described.
【００１５】まず、紙１は、水中伸度が２．５％以下の
ものを用いる必要がある。これは、ラベルを貼着したビ
ール瓶等を冷却した後、瓶に水滴が付着するとラベルが
伸びるが、水中伸度が２．５％を超える紙を用いた場
合、後述する目止め層２を設けても基材８全体としての
伸びを抑えることができず、基材８上に設けられた印刷
層３、アルミニウム蒸着層５、アンカーコート層６など
に亀裂が生じ、外観が低下したり、上記亀裂から水が紙
１に多量にしみ込み、ラベルが破れたりする等の問題が
ある。First, it is necessary to use the paper 1 having an underwater elongation of 2.5% or less. This is because when a beer bottle or the like with a label attached thereto is cooled and water drops adhere to the bottle, the label extends, but when a paper having an underwater elongation of more than 2.5% is used, a sealing layer 2 to be described later is provided. However, the elongation of the substrate 8 as a whole cannot be suppressed, and the printed layer 3, the aluminum vapor deposition layer 5, the anchor coat layer 6 and the like provided on the substrate 8 are cracked and the appearance is deteriorated. There is a problem that a large amount of water permeates the paper 1 through the cracks and the label is torn.
【００１６】この紙１には、故紙を含有させることがで
きる。故紙を含有させた紙は紙自体の伸びが一般的には
低く抑えられるので好ましく、また、カールが少ないと
いう利点がある。故紙の含有量は、ラベルとしたときの
取り扱い性（機械適性、札貼適性等）を考慮して、１０
％以内とすることが好ましい。The paper 1 may contain waste paper. The paper containing the waste paper is preferable because the elongation of the paper itself is generally kept low, and there is an advantage that curling is small. The content of waste paper is 10 in consideration of handleability (machine suitability, label sticking suitability, etc.) when used as a label.
It is preferably within%.
【００１７】目止め層２は、耐水性、およびアルカリ溶
液に溶解する洗瓶適性を有するものであればよく、例え
ば、特公平３−２８３１４号、実公平５−８６１５号、
実公平１−２１３２８号に記載された樹脂からなる。こ
の目止め層２を設けることにより、基材８の伸びが抑え
られるのであり、その塗布量は２〜５ｇ／ｍ2 とするこ
とが好ましい。２ｇ／ｍ2 以下では基材の伸びを抑える
効果が低く、５ｇ／ｍ2 よりも多いと、目止め層の乾燥
（硬化）に要する時間が長くなり、製造スピードが低下
するという問題がある。The sealing layer 2 may be any one having water resistance and suitability for washing in a bottle which dissolves in an alkaline solution. For example, Japanese Examined Patent Publication No. 3-28314, Japanese Utility Model Publication No. 5-8615,
It consists of the resin described in Japanese Utility Model Publication No. 1-21328. By providing the sealing layer 2, the elongation of the base material 8 can be suppressed, and the coating amount thereof is preferably 2 to 5 g / m 2 . If it is 2 g / m 2 or less, the effect of suppressing the elongation of the base material is low, and if it is more than 5 g / m 2 , there is a problem that the time required for drying (curing) the sealing layer becomes long and the production speed is reduced.
【００１８】アンカーコート層６は、アルカリ可溶な樹
脂で、シェラック、アクリル系樹脂、ニトロセルロース
系樹脂、ニトロセルロース系樹脂に脂肪酸エステルを混
合した混合樹脂、この混合樹脂にさらにアルキッド樹脂
を混合した樹脂を用いることができる。The anchor coat layer 6 is an alkali-soluble resin and is a shellac, an acrylic resin, a nitrocellulose resin, a mixed resin obtained by mixing a nitrocellulose resin with a fatty acid ester, and an alkyd resin mixed with this mixed resin. A resin can be used.
【００１９】印刷層３は、上記と同様にアルカリ可溶と
するために、ニトロセルロース系樹脂、ポリアミド樹
脂、またはこれらを混合した混合樹脂をビヒクルとした
インキ、またはさらにアルキッド樹脂やマレイン酸を添
加したインキからなることが好ましい。In order to make the printed layer 3 alkali-soluble as described above, an ink using a nitrocellulose resin, a polyamide resin, or a mixed resin obtained by mixing these as a vehicle, or an alkyd resin or maleic acid is further added. It is preferable that the ink is composed of the above ink.
【００２０】さらに、オーバーコート層４は、前記印刷
層３に用いたインキのビヒクルからなり、いずれもアル
カリに可溶な樹脂からなることが好ましい。Further, the overcoat layer 4 is made of the vehicle of the ink used in the printing layer 3, and it is preferable that both are made of a resin soluble in alkali.
【００２１】以下、具体例を挙げて説明する。A specific example will be described below.
【００２２】＜実施例１＞水中伸度が１．２％のクレー
コート紙（商品名：コモーラントＶＭＴＳ、坪量６０ｇ
／ｍ2 、富士加工株式会社製）のクレーコート面に、グ
ラビアコート法により、フェノール系樹脂にアミノアル
キッド樹脂を１３重量％混合した樹脂溶液を３ｇ／ｍ2
（固形分）の塗布量で塗布し目止め層を設け、基材を作
成した。この基材の水中伸度を測定したところ、０．５
％であった。この基材の目止め層の上に印刷層、および
オーバーコート層を順次設け、本発明のラベルを製造し
た（ラベル１）。ここで、印刷層には、ポリアミド樹脂
およびニトロセルロースをビヒクルとし、さらにマレイ
ン酸を５％添加したインキ、オーバーコート層には、ニ
トロセルロース樹脂を用いた。<Example 1> Clay-coated paper having an elongation in water of 1.2% (trade name: COMORANT VMTS, basis weight 60 g)
/ M 2 , manufactured by Fuji Kako Co., Ltd.) and 3 g / m 2 of a resin solution prepared by mixing 13% by weight of an aminoalkyd resin with a phenolic resin by a gravure coating method on the clay-coated surface.
A coating material was applied at a coating amount of (solid content) to form a filling layer to prepare a base material. When the underwater elongation of this substrate was measured, it was 0.5.
%Met. A printing layer and an overcoat layer were sequentially provided on the sealing layer of this base material to manufacture a label of the present invention (Label 1). Here, for the printing layer, an ink containing polyamide resin and nitrocellulose as a vehicle, and 5% of maleic acid was further added, and for the overcoat layer, a nitrocellulose resin was used.
【００２３】＜実施例２＞目止め層の表面に４００オン
グストロームのアルミニウム蒸着層、スチレン−アクリ
ル系樹脂からなるアンカーコート層をこの順に設け、こ
のアンカーコート層上に印刷層、オーバーコート層を設
けた以外は前記ラベル１と同様にして、本発明のラベル
を得た（ラベル２）。Example 2 A 400 angstrom aluminum vapor deposition layer and an anchor coat layer made of styrene-acrylic resin are provided in this order on the surface of the sealing layer, and a printing layer and an overcoat layer are provided on the anchor coat layer. A label of the present invention was obtained in the same manner as Label 1 except for the above (Label 2).
【００２４】＜実施例３＞クレーコート紙に代えて、故
紙を６％含み、クレーコート層を有する坪量６２ｇ／ｍ
2 の紙（水中伸度：１．１％）を用いた以外は、前記ラ
ベル１と同様にして、本発明のラベルを得た（ラベル
３）。なお、このラベル３の基材の水中伸度は０．２％
であった。Example 3 Instead of clay-coated paper, 6% waste paper was included and a clay-coated layer was used, and the basis weight was 62 g / m 2.
A label of the present invention was obtained in the same manner as Label 1 except that the paper of No. 2 (elongation in water: 1.1%) was used (Label 3). The underwater elongation of the label 3 base material is 0.2%.
Met.
【００２５】＜実施例４＞クレーコート紙に代えて、故
紙を１０％含み、クレーコート層を有する坪量６２ｇ／
ｍ2 の紙（水中伸度：１．１％）を用いた以外は、前記
ラベル２と同様にして、本発明のラベルを得た（ラベル
４）。なお、このラベル４の基材の水中伸度は０．２％
であった。Example 4 Instead of the clay-coated paper, 10% of waste paper is contained and the basis weight of the clay-coated layer is 62 g /
A label of the present invention was obtained in the same manner as Label 2 except that m 2 paper (elongation in water: 1.1%) was used (Label 4). The underwater elongation of the base material of this label 4 is 0.2%.
Met.
【００２６】＜比較例１＞水中伸度が１．９％のアート
紙単体上に直接、印刷層、およびオーバーコート層を設
け、ラベルを製造した（ラベル５）。ここで、印刷層に
用いたインキ、およびオーバーコート層に用いた樹脂
は、ラベル１で用いたものと同じものを用いた。Comparative Example 1 A label was manufactured by directly providing a printing layer and an overcoat layer on a piece of art paper having an elongation in water of 1.9% (Label 5). Here, the ink used for the printing layer and the resin used for the overcoat layer were the same as those used for Label 1.
【００２７】＜比較例２＞紙の片面に目止め層を設けた
構成で、水中伸度が０．８５％の基材を用い、この目止
め層の上に印刷層、およびオーバーコート層を順次設
け、ラベルを製造した（ラベル６）。ここで、印刷層に
用いたインキ、およびオーバーコート層に用いた樹脂
は、ラベル１と同じものを用いた。<Comparative Example 2> A base material having a sealing layer provided on one side of paper and having an underwater elongation of 0.85% was used, and a printing layer and an overcoat layer were formed on the sealing layer. Labels were manufactured sequentially (label 6). Here, the ink used for the printing layer and the resin used for the overcoat layer were the same as those used for Label 1.
【００２８】これらのラベルについて耐水性、アルカリ
溶液による洗瓶性、およひ耐摩擦性についてテストを行
った。この結果を表１に示す。These labels were tested for water resistance, bottle washability with an alkaline solution, and abrasion resistance. Table 1 shows the results.
【００２９】[0029]
【表１】 [Table 1]
【００３０】[0030]
【発明の効果】本発明のラベルは、紙のみでなく、紙に
目止め層を設けた状態での、すなわち基材の状態での水
中伸度を０．５％以下とすることにより、耐水性を良好
なものとすることができ、使用時におけるラベルのしわ
の発生、使用後のラベルの剥離の問題を解消することが
できた。また、洗瓶性も従来のものと比べて遜色無く、
アルカリ溶液により確実に剥離させることができる。ま
た、紙として故紙を含むものを使用すると、基材の伸び
が一層低く抑えられ、印刷層の亀裂やラベルのしわ発生
がより一層抑えられる。EFFECTS OF THE INVENTION The label of the present invention is not limited to paper, and when the paper has a sealing layer, that is, the underwater elongation of the base material is 0.5% or less, water resistance can be improved. The property was good, and the problems of wrinkling of the label during use and peeling of the label after use could be solved. In addition, the bottle washability is comparable to the conventional one,
It can be reliably peeled off with an alkaline solution. Further, when paper containing waste paper is used as the paper, the elongation of the base material is further suppressed, and cracks in the printing layer and wrinkling of the label are further suppressed.
【００３１】また、ラベルの貼着時に接着剤を塗布する
のではなく、予めラベル基材の裏面に、加熱により粘着
性を発揮する接着層を設けておくことにより、ラベルの
貼着（札貼）時に接着剤を塗布する必要がなく、接着層
の塗布量を容易に調整できるうえ、貼着時には、接着剤
の飛散等による汚染がないので衛生的であり、また作業
環境の悪化を防止することができる。Further, instead of applying an adhesive at the time of sticking the label, an adhesive layer exhibiting adhesiveness by heating is provided on the back surface of the label base material in advance, so that the sticking of the label (tag sticking ) There is no need to apply adhesive at the time, the amount of adhesive layer applied can be easily adjusted, and there is no contamination due to splashing of adhesive during attachment, which is hygienic and prevents deterioration of the working environment. be able to.
【図１】本発明の一実施例を示す断面図である。FIG. 1 is a sectional view showing an embodiment of the present invention.
【図２】本発明の他の実施例を示す断面図である。FIG. 2 is a sectional view showing another embodiment of the present invention.
【図３】本発明のさらに他の実施例を示す断面図であ
る。FIG. 3 is a sectional view showing still another embodiment of the present invention.
１…紙 ２…目止め層 ３…印刷層 ４…オーバーコート層 ５…アルミニウム蒸着層 ６…アンカーコート層 ７…接着層 ８…基材 DESCRIPTION OF SYMBOLS 1 ... Paper 2 ... Sealing layer 3 ... Printing layer 4 ... Overcoat layer 5 ... Aluminum vapor deposition layer 6 ... Anchor coat layer 7 ... Adhesive layer 8 ... Substrate
Claims (5)
層を設けた紙からなる基材の前記目止め層上に少なくと
も印刷層を設けた、容器貼着用ラベルにおいて、前記基
材の水中伸度を０．５％以下としたことを特徴としたラ
ベル。1. A container sticking label comprising a base material made of paper having a sealing layer made of an alkali-soluble resin on one surface and at least a printing layer provided on the base material. A label having an elongation of 0.5% or less.
請求項１に記載のラベル。2. The label according to claim 1, wherein a paper containing waste paper within 10% is used.
請求項２のいずれかに記載のラベル。3. The label according to claim 1, wherein an adhesive layer is provided on the back surface of the paper.
着剤であることを特徴とする、請求項３に記載のラベ
ル。4. The label according to claim 3, wherein the adhesive of the adhesive layer is a delayed tack type adhesive.
着するラベルであって、アクリル系ディレードタック型
接着剤を用いたことを特徴とする、請求項４に記載のラ
ベル。5. The label according to claim 4, wherein the label is attached to a glass bottle coated with a masking agent, and an acrylic delayed tack type adhesive is used.