JPH08196662A - Ball for ball game - Google Patents
Ball for ball gameInfo
- Publication number
- JPH08196662A JPH08196662A JP3435095A JP3435095A JPH08196662A JP H08196662 A JPH08196662 A JP H08196662A JP 3435095 A JP3435095 A JP 3435095A JP 3435095 A JP3435095 A JP 3435095A JP H08196662 A JPH08196662 A JP H08196662A
- Authority
- JP
- Japan
- Prior art keywords
- leather
- ball
- printing
- layer
- pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、表面に印刷模様を有す
る表皮からなる球技用ボールに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a ball for ball game comprising a skin having a printed pattern on its surface.
【０００２】[0002]
【従来の技術】サッカーボール、バレーボール、バスケ
ットボール、ハンドボール等表面が激しく磨耗する球技
用ボールにあっては、その表面に印刷された模様を長期
間維持するために、様々な方法が提案されている。例え
ば、実公平5-10834 号公報には、ポリウレタン等の接着
剤層に顔料と染料を併含させて樹脂層を形成し、これを
剥離層を介してベースフィルムに載せ、ベースフィルム
を皮革表面に重ねて、所定の形状を有する金型を加熱し
て押圧し、樹脂層を皮革表面へ転写する方法が開示され
ている。転写された樹脂層のうち、顔料は皮革表面に残
り、染料は表面下の繊維組織まで浸透するのである。か
くすれば表面の顔料層が初期の段階で磨耗により取り除
かれても、その下の染料層により模様は長期間維持され
る。2. Description of the Related Art For soccer balls, volleyballs, basketballs, handballs, and other ball games whose surfaces are heavily worn, various methods have been proposed to maintain the pattern printed on the surfaces for a long period of time. . For example, in Japanese Utility Model Publication No. 5-10834, a resin layer is formed by including a pigment and a dye in an adhesive layer such as polyurethane, and the resin layer is placed on a base film via a release layer. And a mold having a predetermined shape is heated and pressed to transfer the resin layer to the leather surface. In the transferred resin layer, the pigment remains on the leather surface and the dye penetrates into the fiber structure below the surface. Thus, even if the surface pigment layer is removed by abrasion at an early stage, the pattern is maintained for a long time by the dye layer thereunder.
【０００３】[0003]
【発明が解決しようとする課題】上記構造のボールにあ
っては、印刷が、ホットスタンピング法、即ち転写箔を
加熱された模様形状の金型で、皮革に圧力を加えて押し
当てることにより行われる。この方法では、その金型の
形状で模様が決まるため、精巧な模様を描くことができ
ないという問題がある。また顔料と染料が接着性ある樹
脂層に混合されるため、多色を使用した複雑かつ精巧な
模様の印刷例えば「ぼかし」印刷等は難しいという問題
がある。本発明は、このような問題を解決するためにな
されたもので、複雑かつ精巧な模様或いは多色の印刷を
可能にするとともに磨耗に対する優れた耐久性を有する
球技用ボールを実現したものである。In the case of the ball having the above structure, printing is performed by a hot stamping method, that is, a transfer foil is pressed by pressing the leather with a pattern-shaped mold. Be seen. This method has a problem that a delicate pattern cannot be drawn because the pattern is determined by the shape of the mold. In addition, since the pigment and the dye are mixed in the adhesive resin layer, there is a problem that it is difficult to print a complicated and delicate pattern using multiple colors, for example, "blur" printing. The present invention has been made to solve such a problem, and realizes a ball game ball which enables complicated and delicate patterns or multicolor printing and has excellent durability against abrasion. .
【０００４】[0004]
【課題を解決するための手段】本発明は、最外層が皮革
にて形成されるとともに、該皮革の表面に所定の模様が
印刷されてなる球技用ボールにおいて基材フィルム上に
昇華性染料を含有したインキにて、スクリーン印刷また
はオフセット印刷により上記模様が印刷されてなる転写
フィルムを、上記皮革の表面に重ねて加圧かつ加熱する
こと上により、上記皮革表面に上記模様が転写されてな
るものである。According to the present invention, a sublimable dye is formed on a base film in a ball for ball game in which the outermost layer is made of leather and a predetermined pattern is printed on the surface of the leather. A transfer film having the above pattern printed by screen printing or offset printing with the contained ink is overlaid on the surface of the above leather and pressed and heated to transfer the above pattern onto the above leather surface. It is a thing.
【０００５】[0005]
【作用】転写フィルムが、皮革の表面に重ねられて加圧
加熱されると、インキに含まれる顔料は皮革表面に固定
され、染料は、昇華して皮革内部に浸透する。顔料及び
染料を含むインキは、スクリーン印刷またはオフセット
印刷により基材フィルム上に印刷されるから、印刷後の
顔料層の厚さは、通常より厚く例えば球技用ボールにお
いて必要な印刷堅牢度が得られる20ミクロン程度が可能
である。When the transfer film is superposed on the surface of the leather and heated under pressure, the pigment contained in the ink is fixed on the surface of the leather, and the dye sublimes and penetrates into the leather. Since the ink containing the pigment and the dye is printed on the substrate film by screen printing or offset printing, the thickness of the pigment layer after printing is thicker than usual, and for example, the printing fastness required for ball games is obtained. 20 microns is possible.
【０００６】[0006]
【実施例】図１および図２において、１はサッカーボー
ルで、表皮層が複数枚の６角形及び５角形の皮革２，
２．．．にて構成される。ここで皮革２には、天然皮革
及び合成皮革が含まれる。３は、皮革２の表面に印刷さ
れた模様であり、文字、記号等を含む。皮革２は、表皮
層４及びその下に位置する繊維組織５よりなる。模様３
は、表皮層４に固定された顔料層６と、繊維組織５に浸
透された染料層７よりなる。８は、圧搾空気が密封され
たチューブで、球形に縫い合わされた皮革パネル内に収
納されている。このチューブ８は、ブチルゴム製中空球
形体にて形成され、図示しないバルブを介して空気が注
入される。上記構造のボールは、縫いボールと称される
が、このほか貼りボールと称されるボールもあり、これ
は球形チューブの外側に糸を巻いて補強層を形成し、さ
らにこの上に薄いゴム層を介して、複数の皮革パネルを
ゴム糊で接着したものである。EXAMPLES In FIGS. 1 and 2, 1 is a soccer ball, and a hexagonal and pentagonal leather 2 having a plurality of skin layers 2.
2. ． ． Composed of. Here, the leather 2 includes natural leather and synthetic leather. 3 is a pattern printed on the surface of the leather 2, and includes characters, symbols and the like. The leather 2 is composed of an epidermis layer 4 and a fibrous structure 5 located below the epidermis layer 4. Pattern 3
Consists of a pigment layer 6 fixed to the skin layer 4 and a dye layer 7 permeated into the fibrous tissue 5. Reference numeral 8 is a tube in which compressed air is sealed, and is housed in a leather panel sewn in a spherical shape. The tube 8 is formed of a hollow spherical body made of butyl rubber, and air is injected through a valve (not shown). The ball with the above structure is called a sewing ball, but there is also a ball called a pasting ball, in which a thread is wound on the outside of a spherical tube to form a reinforcing layer, and a thin rubber layer is further formed on the reinforcing layer. A plurality of leather panels are bonded to each other with a rubber paste.
【０００７】図３は、転写フィルム９を示し、基材フィ
ルム１０上に、剥離層１１、インキ層１２、接着層１３
が積層されて被着されている。剥離層１１、インキ層１
２および接着層１３は、所定の模様を有している。イン
キ層１２は、昇華性染料、顔料及びビヒクルよりなる。
ビヒクルを構成する樹脂は、昇華性染料と親和性の小さ
い樹脂、例えばアクリル樹脂、アルキッド樹脂が使用さ
れる。顔料は、ビヒクルと親和性のあるものが使用され
る。練肉は、ボール・ミル、サンドミル或いはロールミ
ル等によりなされる。図３において、基材フィルム１
０、剥離層１１、インキ層１２及び接着層１３は、説明
の必要上厚さを誇張して描いているが、実際には基材フ
ィルム１０の厚さは、約250 ミクロン、剥離層１１、イ
ンキ層１２及び接着層１３の厚さは、それぞれ約１ない
し３ミクロン，約２０ミクロン，約１０ミクロンであ
る。FIG. 3 shows a transfer film 9, which comprises a base film 10, a release layer 11, an ink layer 12, and an adhesive layer 13.
Are laminated and deposited. Release layer 11, ink layer 1
2 and the adhesive layer 13 have a predetermined pattern. The ink layer 12 is composed of a sublimable dye, a pigment and a vehicle.
As the resin constituting the vehicle, a resin having a low affinity with the sublimable dye, for example, an acrylic resin or an alkyd resin is used. A pigment having an affinity with the vehicle is used. The kneaded meat is formed by a ball mill, a sand mill, a roll mill or the like. In FIG. 3, the base film 1
0, the release layer 11, the ink layer 12 and the adhesive layer 13 are exaggerated for the sake of explanation, but in reality, the thickness of the base film 10 is about 250 μm, the release layer 11, The thicknesses of the ink layer 12 and the adhesive layer 13 are about 1 to 3 μm, about 20 μm, and about 10 μm, respectively.
【０００８】以下にインキの処方例を示す。 例１ スクリーンインキ配合（黒色） 重量％ 染料 キノフタロン系染料原末 １０．００ 顔料 カーボンブラック ７．００ ビヒクル 酢酸セルロース ２０．００ 溶剤 キシレン ４０．００ ダイアセトンアルコール １８．００ イソホロン ５．００ （１００．００） 例２ スクリーンインキ配合（青色） 重量％ 染料 1,4 ジアミノAQ系染料原末 ８．００ 顔料 フタロシャニンブルー １０．００ ビヒクル アクリル樹脂 ２０．００ 溶剤 キシレン ３０．００ シクロヘキサノン ２０．００ ブチルアルコール １２．００ （１００．００） 例３ オフセットインキ配合（赤色） 重量％ 染料 1,アミノ,4, ヒドロキシAQ系染料原末 １０．００ 顔料 キナクリドン レッドHR １０．００ ビヒクル 長油性アルキッド樹脂 ４０．００ 溶剤 重合アマニ油 ２０．００ 高沸点芳香族溶剤 １５．００ ベンジルアルコール ５．００ （１００．００）An example of ink formulation is shown below. Example 1 Screen ink formulation (black)% by weight Dye quinophthalone dye bulk powder 10.00 Pigment carbon black 7.00 Vehicle cellulose acetate 20.00 Solvent xylene 40.00 Diacetone alcohol 18.00 Isophorone 5.00 (100.00 ) Example 2 Screen ink formulation (blue) wt% Dye 1,4 Diamino AQ dye bulk powder 8.00 Pigment Phthaloshanin blue 10.00 Vehicle acrylic resin 20.00 Solvent xylene 30.00 Cyclohexanone 20.00 Butyl alcohol 12. 00 (100.00) Example 3 Offset ink formulation (red) wt% Dye 1, amino, 4, hydroxy AQ dye bulk powder 10.00 Pigment quinacridone red HR 10.00 Vehicle long oil alkyd resin 40.00 Solvent polymerized flax Oil 20.00 Boiling aromatic solvent 15.00 Benzyl alcohol 5.00 (100.00)
【０００９】基材フィルム１０として、ポリエステルフ
ィルム、ポリカーボネートフィルム、ポリイミドフィル
ム等の耐熱性フィルムまたはセロハン、パーチメント紙
（硫酸紙）等が適している。また剥離層１１として、シ
リコン、ワックス等の剥離性樹脂が使用され、接着層１
３としてポリエステル樹脂、ポリウレタン樹脂等が使用
される。As the substrate film 10, a heat-resistant film such as a polyester film, a polycarbonate film, a polyimide film, cellophane, parchment paper (sulfuric acid paper), or the like is suitable. Further, as the peeling layer 11, a peeling resin such as silicon or wax is used.
Polyester resin, polyurethane resin or the like is used as 3.
【００１０】基材フィルム１０へのインキの印刷は、ス
クリーン印刷またはオフセット印刷によりなされる。一
般に印刷方法として、上記スクリーン印刷、オフセット
印刷のほか、グラビア印刷、フレキソ印刷等があるが、
スクリーン印刷またはオフセット印刷のみが堅牢度の高
い層の厚い印刷を可能とする。即ちスクリーン印刷で
は、顔料層６の厚さを、１０ないし５０ミクロン程度ま
で可能であり、またオフセット印刷では平凹版システム
即ち一定深さエッチングした凹みにインキを印刷する方
法では約１０ミクロン程度まで可能である。これに対
し、グラビア印刷及びフレキソ印刷では、５ないし６ミ
クロンまでであり、強い摩擦力が加わると短時間の内に
容易に削り取られてしまう。それ故スクリーン印刷また
はオフセット印刷による印刷のみが、最も堅牢度が高く
球技用ボールの印刷に最適なのである。The ink is printed on the base film 10 by screen printing or offset printing. Generally, as the printing method, there are gravure printing, flexo printing, etc. in addition to the above screen printing and offset printing.
Only screen printing or offset printing allows thick printing of layers with high fastness. That is, in the screen printing, the thickness of the pigment layer 6 can be up to about 10 to 50 μm, and in the offset printing, it can be up to about 10 μm by the planographic intaglio system, that is, the method of printing the ink in the recesses etched to a certain depth. Is. On the other hand, in gravure printing and flexographic printing, the size is up to 5 to 6 microns, and when a strong frictional force is applied, it is easily scraped off within a short time. Therefore, only screen printing or offset printing is the most robust and optimal for printing ball games balls.
【００１１】図４に示すように、皮革２が平坦な基板１
４上に載置され、これに上記構成の転写フィルム９が、
皮革表面にその接着層１３（図３）が接触するよう重ね
合わされ、基材フィルム１０上面から金属製熱板１５が
押し当てられる。この熱板１５の加圧圧力は、約10kg/c
m2ないし約１,000kg/cm2の範囲が適している。圧力がこ
の範囲より小さいと、顔料の固定性及び染料の浸透性が
悪く、またこの範囲より大きいと、皮革が押しつぶさ
れ、薄くかつ硬くなるおそれがあるからである。また熱
板の温度は、80℃ないし 150℃の範囲で使用される。温
度が、この範囲より低いと、染料の昇華性が悪くなり、
浸透性が低下し、他方この範囲より高いと皮革が熱によ
る劣化をうけるおそれがあるからである。また転写印刷
に要する時間即ち加熱加圧時間は、皮革の材質、インク
層の厚さによって異なるが、一般的に３ないし５秒であ
る。As shown in FIG. 4, a substrate 1 on which leather 2 is flat
4, and the transfer film 9 having the above-mentioned structure is placed on it.
The adhesive layer 13 (FIG. 3) is overlaid on the surface of the leather, and the metallic hot plate 15 is pressed from the upper surface of the base film 10. The pressure applied to the hot plate 15 is about 10 kg / c.
A range of m 2 to about 1,000 kg / cm 2 is suitable. If the pressure is lower than this range, the fixability of the pigment and the penetrability of the dye will be poor, and if the pressure is higher than this range, the leather may be crushed and thin and hard. The temperature of the hot plate is used in the range of 80 ℃ to 150 ℃. If the temperature is lower than this range, the sublimability of the dye will deteriorate,
This is because the permeability is lowered, and when it is higher than this range, the leather may be deteriorated by heat. The time required for transfer printing, that is, the heating / pressurizing time is generally 3 to 5 seconds, although it varies depending on the material of the leather and the thickness of the ink layer.
【００１2 】[0012]
【発明の効果】本発明にに係る球技用ボールは、昇華性
染料および顔料を含有させたインキを使用し、スクリー
ン印刷またはオフセット印刷により基材フィルムに所定
の模様を印刷した転写フィルムを、皮革に熱転写するこ
とにより、印刷したものであるから、染料は皮革内部に
深く浸透しており、また顔料層も厚くかつ強固に皮革表
面に固定されている。それ故皮革表面が磨耗されても、
その模様を長期間安定に維持することができる。INDUSTRIAL APPLICABILITY The ball for a ball game according to the present invention uses a transfer film obtained by printing a predetermined pattern on a base film by screen printing or offset printing using an ink containing a sublimable dye and a pigment. The dye is deeply penetrated into the leather because it is printed by thermal transfer to, and the pigment layer is thick and firmly fixed to the leather surface. Therefore, even if the leather surface is worn,
The pattern can be stably maintained for a long period of time.
【００１２】本発明によれば、フィルム基材への印刷が
スクリーン印刷またはオフセット印刷によりなされるか
ら多色を使用した複雑かつ精巧な模様を容易に得ること
ができ、色彩豊かな球技用ボールを実現することができ
る。According to the present invention, since the printing on the film base material is performed by screen printing or offset printing, a complicated and delicate pattern using multiple colors can be easily obtained, and a ball ball for ball game with rich colors can be obtained. Can be realized.
【図１】本発明の実施例の正面図である。FIG. 1 is a front view of an embodiment of the present invention.
【図２】図１のＡ−Ａ線断面図である。FIG. 2 is a sectional view taken along the line AA of FIG.
【図３】転写フィルムの斜視図である。FIG. 3 is a perspective view of a transfer film.
【図４】同実施例における印刷を説明するための断面図
である。FIG. 4 is a sectional view for explaining printing in the embodiment.
１………サッカーボール ２………皮革 ３………模様 ４………表皮層 ５………繊維組織 ６………顔料層 ７………染料層 ８………チューブ ９………転写フィルム １０………基材フィルム １１………剥離層 １２………インキ層 １３………接着層 １４………基板 １５………熱板 1 ………… Soccer ball 2 ………… Leather 3 ………… Pattern 4 ………… Surface layer 5 ………… Fibrous structure 6 ………… Pigment layer 7 ……… Dye layer 8 ……… Tube 9 ……… Transfer Film 10 ... Base film 11 ... Release layer 12 ... Ink layer 13 ... Adhesive layer 14 ... Substrate 15 ... Hot plate
Claims (1)
該皮革の表面に所定の模様が印刷されてなる球技用ボー
ルにおいて、基材フィルム上に昇華性染料及び顔料を含
有したインキにて、スクリーン印刷またはオフセット印
刷により上記模様が印刷されてなる転写フィルムを、上
記皮革の表面に重ねて加圧かつ加熱することにより、上
記皮革表面に上記模様が転写されてなることを特徴とす
る球技用ボール1. The outermost layer is made of leather, and
A ball for ball game having a predetermined pattern printed on the surface of the leather, wherein the pattern is printed by screen printing or offset printing with an ink containing a sublimable dye and a pigment on a base film. Is superposed on the surface of the leather and pressed and heated to transfer the pattern to the surface of the leather.