JPH0832906B2 - Water-insoluble oil agent for threading water pipes - Google Patents
Water-insoluble oil agent for threading water pipesInfo
- Publication number
- JPH0832906B2 JPH0832906B2 JP1052829A JP5282989A JPH0832906B2 JP H0832906 B2 JPH0832906 B2 JP H0832906B2 JP 1052829 A JP1052829 A JP 1052829A JP 5282989 A JP5282989 A JP 5282989A JP H0832906 B2 JPH0832906 B2 JP H0832906B2
- Authority
- JP
- Japan
- Prior art keywords
- water
- oil
- threading
- agent
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】 産業上の利用分野 本発明は、水道管のねじ切り加工用油剤に関する。TECHNICAL FIELD The present invention relates to an oil agent for threading a water pipe.
従来の技術 亜鉛めっき鋼管が主として使用されている水道管は、
接続するためにねじ切り加工される。ねじ切り加工にお
いては、高いねじ精度を得ると共に、工具と加工面との
間に作用する大きな摩擦力を軽減するために、切削性能
に優れた切削油剤を用いることが必要である。Conventional technology Water pipes, which are mainly used for galvanized steel pipes,
Threaded to connect. In thread cutting, it is necessary to use a cutting fluid with excellent cutting performance in order to obtain high thread precision and reduce the large frictional force acting between the tool and the machined surface.
したがって、ねじ切り加工においては、塩素系や硫黄
系の極圧剤を含有する不水溶性の切削油剤が使用されて
いる。切削性に優れた不水溶性の切削油剤を使用すれば
良好なねじ精度は得られるが、水道管の内面には切削油
剤が付着しているため、このままでは配管に使用するこ
とはできない。Therefore, in thread cutting, a water-insoluble cutting oil containing a chlorine-based or sulfur-based extreme pressure agent is used. If a water-insoluble cutting oil with excellent machinability is used, good screw precision can be obtained, but since the cutting oil adheres to the inner surface of the water pipe, it cannot be used as it is for piping.
そこで、従来は有機溶剤による洗浄を行っているが、
有機溶剤は人体に対する毒性や引火の危険性がある。Therefore, conventionally, cleaning with an organic solvent is performed,
Organic solvents are toxic to humans and may cause fire.
一方、水で希釈して使用する水溶性の切削油剤を用い
れば、洗浄性は良好となるが、反面切削性が劣っている
ため、ねじ精度や加工能率等に問題を生じる。On the other hand, if a water-soluble cutting oil that is used after diluting with water is used, the cleaning property will be good, but on the other hand, the cutting property will be inferior, and therefore problems will occur in screw precision, processing efficiency, and the like.
発明が解決しようとする問題点 上記の現状であるから、本発明の目的は、切削性に優
れ、かつねじ切り加工後の水道管に付着した切削油剤を
水で容易に洗浄することができる水道管ねじ切り加工用
油剤を提供することにある。DISCLOSURE OF THE INVENTION Problems to be Solved by the Invention Under the present circumstances, an object of the present invention is to provide a water pipe which is excellent in machinability and can be easily washed with water to remove the cutting oil adhering to the water pipe after thread cutting. To provide an oil agent for thread cutting.
問題点を解決するための手段 本発明者らは、前記目的を達成するために鋭意研究し
た結果、鉱油及び／または硫化鉱油を基油として用い、
該基油に油性剤および極圧添加剤を含有した従来の切削
油剤に対して、界面活性剤を加えた特定粘度を有する油
剤が、切削性を低下させることがなく、水で容易に除去
することができることを見いだして本発明を完成した。Means for Solving the Problems As a result of intensive studies to achieve the above-mentioned object, the present inventors have used mineral oil and / or sulfurized mineral oil as a base oil,
In contrast to the conventional cutting oil containing an oiliness agent and an extreme pressure additive in the base oil, an oil containing a surfactant and having a specific viscosity is easily removed with water without lowering the machinability. The present invention has been completed by finding out that it is possible.
すなわち、本発明の要旨は、鉱油および／または硫化
鉱油、油性剤および極圧添加剤を必須成分として含有す
る切削油剤において、ノニオン系および／またはアニオ
ン系の界面活性剤を５ないし30重量％含有し、40℃にお
ける動粘度が５ないし50mm2/secであることを特徴とす
る水道管ねじ切り加工用の不水溶性油剤である。That is, the gist of the present invention is to provide a cutting fluid containing mineral oil and / or sulfide mineral oil, an oiliness agent and an extreme pressure additive as essential components, containing 5 to 30% by weight of a nonionic and / or anionic surfactant. However, it is a water-insoluble oil agent for threading of water pipes, which has a kinematic viscosity at 40 ° C. of 5 to 50 mm 2 / sec.
以下に本発明の構成要素について詳細に説明する。 Hereinafter, the components of the present invention will be described in detail.
本発明に使用する界面活性剤は、基油、油性剤および
極圧添加剤等と均一に溶解するものであれば、ノニオン
系またはアニオン系を問わず使用することができる。界
面活性剤は１種だけを使用しても良いが、２種以上を混
合して使用することをも妨げない。The surfactant used in the present invention may be a nonionic or anionic surfactant as long as it can be uniformly dissolved in the base oil, the oiliness agent, the extreme pressure additive and the like. Although only one type of surfactant may be used, it is possible to use a mixture of two or more types.
界面活性剤の添加量は５ないし30重量％、好ましくは
10ないし20重量％である。界面活性剤の添加量が５重量
％未満では水による洗浄性を満足することができない。
また、界面活性剤の添加量が30重量％を越えると、経済
的に好ましくない。The amount of surfactant added is 5 to 30% by weight, preferably
10 to 20% by weight. If the added amount of the surfactant is less than 5% by weight, the detergency with water cannot be satisfied.
Further, if the amount of the surfactant added exceeds 30% by weight, it is not economically preferable.
本発明に使用することができるノニオン系界面活性剤
としては、高級アルコールエチレンオキサイド付加物、
アルキルフェノールエチレンオキサイド付加物、ペンタ
エリスリトールの脂肪酸エステル、ソルビタンの脂肪酸
エステル、脂肪酸アマイド等を例示することができる。Nonionic surfactants that can be used in the present invention include higher alcohol ethylene oxide adducts,
Examples thereof include alkylphenol ethylene oxide adduct, pentaerythritol fatty acid ester, sorbitan fatty acid ester, and fatty acid amide.
また、アニオン系界面活性剤としては、石油スルホン
酸ナトリウム塩、石油スルホン酸カリウム塩、脂肪酸石
けん、脂肪酸アミン塩、硫酸エステルナトリウム塩等を
例示することができる。Examples of the anionic surfactant include sodium petroleum sulfonate, potassium petroleum sulfonate, fatty acid soap, fatty acid amine salt, sodium sulfate ester salt and the like.
本発明の水道管ねじ切り加工用油剤は、40℃の動粘度
が５ないし50mm2/secであることが必要である。動粘度
が5mm2/sec未満では引火点が低くなるので好ましくな
い。また、動粘度が50mm2/secを越えると、水による洗
浄性が低下すると共に、作業性が悪化するので好ましく
ない。The oil agent for threading a water pipe of the present invention needs to have a kinematic viscosity at 40 ° C. of 5 to 50 mm 2 / sec. When the kinematic viscosity is less than 5 mm 2 / sec, the flash point becomes low, which is not preferable. On the other hand, if the kinematic viscosity exceeds 50 mm 2 / sec, the washing property with water is deteriorated and the workability is deteriorated, which is not preferable.
本発明の水道管ねじ切り加工用油剤は、不水溶性切削
油剤と同様にして使用する。The water agent for threading a water pipe of the present invention is used in the same manner as the water-insoluble cutting agent.
なお、本発明の水道管ねじ切り加工用油剤に対して
は、必要に応じて、酸化防止剤、金属防食剤、消泡剤
等、従来の不水溶性切削油剤に用いられている助剤をも
添加することができる。In addition, for the water agent for threading the water pipe of the present invention, if necessary, an auxiliary agent used in the conventional water-insoluble cutting fluid, such as an antioxidant, a metal anticorrosive agent, or a defoaming agent. It can be added.
実 施 例 次に実施例および比較例によって本発明を具体的に説
明する。ただし、本発明はこれらの実施例および比較例
によってなんら制限されるものではない。EXAMPLES Next, the present invention will be specifically described with reference to Examples and Comparative Examples. However, the present invention is not limited to these Examples and Comparative Examples.
なお、下記の実施例および比較例において、成分の含
有量を示す数値の単位は重量％である。In the following examples and comparative examples, the unit of the numerical value indicating the content of the component is% by weight.
実施例１ マシン油（JIS K2238ISO VG10相当） 72％ 塩素化パラフィン（塩素分50重量％） ５％ ジラウリルペンタスルフィッド ３％ 硫化豚脂（硫黄分10重量％） ５％ RO（CH2CH2O）9H ９％ （上式においてＲは炭素原子数が13ないし15のアルキル
基を総括的に示す。） ペンタエリスリトールセスキオレエート ６％ （動粘度は−40℃において17.2mm2/sec、引火点は170℃
のものである。） 実施例２ マシン油（JIS K2238ISO VG5相当） 72％ 塩素化パラフィン（塩素分50重量％） ５％ ジラウリルペンタスルフィッド ３％ 硫化豚脂（硫黄分10重量％） ５％ ノニルフェノールエチレンオキサイド８モル付加物10％ ソルビタンセスキオレエート ５％ （動粘度は−40℃において8.2mm2/sec、引火点は138℃
のものである。） 実施例３ マシン油（JIS K2238ISO VG10相当） 12％ マシン油（JIS K2238ISO VG46相当） 55％ 塩素化パラフィン（塩素分50重量％） ５％ ジラウリルペンタスルフィッド ３％ 硫化豚脂（硫黄分10重量％） ５％ ノニルフェノールエチレンオキサイド８モル付加物５％ ソルビタンセスキオレエート ５％ 石油スルホネートナトリウム塩 10％ （動粘度は−40℃において46.5mm2/sec、引火点は184℃
のものである。） 実施例４ マシン油（JIS K2238ISO VG10相当） 45％ マシン油（JIS K2238ISO VG46相当） 42％ 塩素化パラフィン（塩素分50重量％） ５％ ノニルフェノールエチレンオキサイド８モル付加物５％ ソルビタンセスキオレエート ３％ （動粘度は−40℃において250mm2/sec、引火点は178℃
のものである。） 比較例１ マシン油（JIS K2238ISO VG10相当） 68％ マシン油（JIS K2238ISO VG46相当） 19％ 塩素化パラフィン（塩素分50重量％） ５％ ジラウリルペンタスルフィッド ３％ 硫化豚脂（硫黄分10重量％） ５％ （動粘度は−40℃において15.0mm2/sec、引火点は166℃
のものである。） 比較例２ 水溶性切削油剤（JIS K2241 W1種１号相当品）の10重
量％希釈液（希釈水は水道水） 〔性能評価試験〕 本発明の実施例および比較例の組成物について洗浄性
および切削性を評価した。Example 1 Machine oil (JIS K2238ISO VG10 equivalent) 72% Chlorinated paraffin (Chlorine content 50% by weight) 5% Dilauryl pentasulfide 3% Sulfided butter fat (Sulfur content 10% by weight) 5% RO (CH 2 CH 2 O) 9 H 9% (In the above formula, R generally represents an alkyl group having 13 to 15 carbon atoms.) Pentaerythritol sesquioleate 6% (Kinematic viscosity is 17.2 mm 2 / sec at −40 ° C.) , Flash point is 170 ℃
belongs to. ) Example 2 Machine oil (corresponding to JIS K2238 ISO VG5) 72% Chlorinated paraffin (Chlorine content 50% by weight) 5% Dilauryl pentasulfide 3% Sulfided butter fat (Sulfur content 10% by weight) 5% Nonylphenol ethylene oxide 8 Molar adduct 10% sorbitan sesquioleate 5% (Kinematic viscosity is 8.2 mm 2 / sec at -40 ℃, flash point is 138 ℃
belongs to. ) Example 3 Machine oil (JIS K2238ISO VG10 equivalent) 12% Machine oil (JIS K2238ISO VG46 equivalent) 55% Chlorinated paraffin (Chlorine content 50% by weight) 5% Dilauryl pentasulfide 3% Sulfided butter fat (Sulfur content) 10% by weight) 5% Nonylphenol ethylene oxide 8 mol adduct 5% Sorbitan sesquioleate 5% Petroleum sulfonate sodium salt 10% (Kinematic viscosity is 46.5 mm 2 / sec at -40 ° C, flash point is 184 ° C)
belongs to. ) Example 4 Machine oil (JIS K2238ISO VG10 equivalent) 45% Machine oil (JIS K2238ISO VG46 equivalent) 42% Chlorinated paraffin (Chlorine content 50% by weight) 5% Nonylphenol ethylene oxide 8 mol adduct 5% Sorbitan sesquioleate 3 % (Kinematic viscosity is 250 mm 2 / sec at -40 ℃, flash point is 178 ℃
belongs to. ) Comparative Example 1 Machine oil (JIS K2238ISO VG10 equivalent) 68% Machine oil (JIS K2238ISO VG46 equivalent) 19% Chlorinated paraffin (Chlorine content 50% by weight) 5% Dilauryl pentasulfide 3% Sulfided butter fat (Sulfur content) 10% by weight) 5% (Kinematic viscosity is 15.0 mm 2 / sec at -40 ℃, flash point is 166 ℃
belongs to. Comparative Example 2 10% by weight dilution of a water-soluble cutting fluid (JIS K2241 W1 type 1 equivalent product) (dilution water is tap water) [Performance evaluation test] Detergency of the compositions of Examples and Comparative Examples of the present invention And the machinability was evaluated.
冷間圧延鋼板（JIS Ｇ 3141 spccダル仕上げ、80
×60×1.2mm）を試料油剤中に浸漬した後に取り出し、
室内に５分間懸垂して試験片とした。Cold rolled steel plate (JIS G 3141 spcc dull finish, 80
X 60 x 1.2 mm) soaked in the sample oil solution and then taken out,
The test piece was suspended in the room for 5 minutes.
一方、第１図に示すような２容のビーカー４に水道
水２をいれ、スターラー３で撹拌（回転数は200回転／
分）する洗浄試験装置を作った。On the other hand, tap water 2 is put into a 2 volume beaker 4 as shown in FIG. 1 and stirred by a stirrer 3 (rotation speed is 200 rotations /
A cleaning test device was prepared.
この中に、上記試験片１を５分間懸垂して洗浄した後
に取り出し、水分を乾燥させた。試験前後の付着油分量
を測定し、洗浄性の指標とした。The test piece 1 was suspended therein for 5 minutes, washed, taken out, and dried. The amount of adhered oil before and after the test was measured and used as an index of detergency.
なお、試験は水温25℃にて行った。その結果を第１表
に示す。The test was conducted at a water temperature of 25 ° C. The results are shown in Table 1.
第１表によれば、本発明の油剤はいずれも良好な洗浄
性を有することが認められるが、従来の不水溶性切削油
剤は水ではほとんど除去できないことが判る。 From Table 1, it can be seen that all of the oil solutions of the present invention have good detergency, but conventional water-insoluble cutting oil solutions can hardly be removed with water.
本発明の実施例および比較例の組成物について、チェ
ザーによる水道管のねじ切り加工を行い、切削面の状態
を観察して切削性の指標とした。試験条件を第２表に示
し、試験結果を第３表に示す。With respect to the compositions of Examples and Comparative Examples of the present invention, a water pipe was threaded by a checker, and the state of the cut surface was observed and used as an index of machinability. The test conditions are shown in Table 2 and the test results are shown in Table 3.
発明の効果 本発明の水道管ねじ切り加工用油剤は、従来の不水溶
性切削油剤と同等の切削性能を有し、加工後、付着した
油剤は水で容易に除去することができる。 EFFECTS OF THE INVENTION The oil agent for threading a water pipe of the present invention has cutting performance equivalent to that of a conventional water-insoluble cutting oil, and after processing, the attached oil agent can be easily removed with water.
したがって、本発明の水道管ねじ切り加工用油剤を使
用すれば、加工後に特別な洗浄操作を必要としないの
で、非常に経済的である。Therefore, when the oil agent for threading a water pipe of the present invention is used, no special washing operation is required after processing, which is very economical.
添付の第１図は、本発明の水道管ねじ切り加工用油剤の
性能を試験するために使用した装置の概略説明図であ
る。 図において、１は試験片、２は水道水、３はスターラ
ー、４は２容ビーカーを示す。The attached FIG. 1 is a schematic explanatory view of an apparatus used for testing the performance of the oil agent for threading a water pipe of the present invention. In the figure, 1 is a test piece, 2 is tap water, 3 is a stirrer, and 4 is a 2-volume beaker.
フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｃ１０Ｍ 129:74） Ｃ１０Ｎ 30:02 30:06 40:22 (56)参考文献 特開 昭62−185793（ＪＰ，Ａ) 特開 昭63−63792（ＪＰ，Ａ) 特開 昭52−114853（ＪＰ，Ａ) 特開 昭62−115094（ＪＰ，Ａ) 特開 平１−123897（ＪＰ，Ａ) 特公 昭48−39562（ＪＰ，Ｂ１) 特公 昭56−25479（ＪＰ，Ｂ２)Continuation of the front page (51) Int.Cl. 6 Identification number Office reference number FI technical display location C10M 129: 74) C10N 30:02 30:06 40:22 (56) Reference JP-A-62-185793 (JP , A) JP-A-63-63792 (JP, A) JP-A-52-114853 (JP, A) JP-A-62-115094 (JP, A) JP-A-1-123897 (JP, A) JP-B 48-39562 (JP, B1) JP-B-56-25479 (JP, B2)
Claims (1)
び極圧添加剤を必須成分として添加した切削油剤におい
て、ノニオン系および／またはアニオン系の界面活性剤
を５ないし30重量％含有し、40℃における動粘度が５な
いし50mm2/secであることを特徴とする水道管ねじ切り
加工用の不水溶性油剤。1. A cutting fluid containing mineral oil and / or sulfide mineral oil, an oiliness agent and an extreme pressure additive as essential components, containing 5 to 30% by weight of a nonionic and / or anionic surfactant, A water-insoluble oil agent for threading a water pipe, which has a kinematic viscosity at 5 ° C of 5 to 50 mm 2 / sec.