JPH0860540A - セルロース系繊維布帛の加工方法 - Google Patents
セルロース系繊維布帛の加工方法Info
- Publication number
- JPH0860540A JPH0860540A JP19680794A JP19680794A JPH0860540A JP H0860540 A JPH0860540 A JP H0860540A JP 19680794 A JP19680794 A JP 19680794A JP 19680794 A JP19680794 A JP 19680794A JP H0860540 A JPH0860540 A JP H0860540A
- Authority
- JP
- Japan
- Prior art keywords
- processing
- fabric
- textile fabric
- cellulosic textile
- humectant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】
【目的】 セルロース系繊維布帛にバラツキのない均一
なイージーケアー性能を付与することができるホルムア
ルデヒドによる気相加工方法を提供する。 【構成】 セルロース系繊維布帛に保湿剤を付与し，乾
燥した後，ホルムアルデヒドガスを吸着させ，熱処理し
て架橋反応せしめるホルムアルデヒドガスによる気相加
工を施す。
なイージーケアー性能を付与することができるホルムア
ルデヒドによる気相加工方法を提供する。 【構成】 セルロース系繊維布帛に保湿剤を付与し，乾
燥した後，ホルムアルデヒドガスを吸着させ，熱処理し
て架橋反応せしめるホルムアルデヒドガスによる気相加
工を施す。
Description
【０００１】
【産業上の利用分野】本発明は，ホルムアルデヒドガス
を用いて行うセルロース系繊維布帛の気相加工方法に関
するものである。
を用いて行うセルロース系繊維布帛の気相加工方法に関
するものである。
【０００２】
【従来の技術】セルロース系繊維布帛にホルムアルデヒ
ドガスを用いて気相加工を施し，ホルムアルデヒドを繊
維のセルロース分子間に架橋することによりセルロース
系繊維布帛を改質し，イージーケアー性（ウォッシュ・
アンド・ウェアー性）を付与することは，従来から公知
であり，広く一般に行われている。
ドガスを用いて気相加工を施し，ホルムアルデヒドを繊
維のセルロース分子間に架橋することによりセルロース
系繊維布帛を改質し，イージーケアー性（ウォッシュ・
アンド・ウェアー性）を付与することは，従来から公知
であり，広く一般に行われている。
【０００３】しかしながら，この方法による問題点は，
加工に際し，布帛の水分率を均一に調節しておかない
と，改質にバラツキが生じることである。そのため，ホ
ルムアルデヒドガスを用いて気相加工を行う前に，布帛
を恒温恒湿室に数時間放置し，調湿しなければならなか
った。
加工に際し，布帛の水分率を均一に調節しておかない
と，改質にバラツキが生じることである。そのため，ホ
ルムアルデヒドガスを用いて気相加工を行う前に，布帛
を恒温恒湿室に数時間放置し，調湿しなければならなか
った。
【０００４】
【発明が解決しようとする課題】本発明は，このような
現状に鑑みて行われたもので，気相加工を行う前に調湿
しなくても均一に改質を行うことができるセルロース系
繊維布帛のイージーケアー（ウォッシュ・アンド・ウェ
アー）加工方法を得ることを目的とするものである。
現状に鑑みて行われたもので，気相加工を行う前に調湿
しなくても均一に改質を行うことができるセルロース系
繊維布帛のイージーケアー（ウォッシュ・アンド・ウェ
アー）加工方法を得ることを目的とするものである。
【０００５】
【課題を解決するための手段】本発明は，上記目的を達
成するもので，次の構成よりなるものである。すなわ
ち，本発明は，セルロース系繊維布帛に保湿剤を付与，
乾燥した後，ホルムアルデヒドガスを吸着させ，熱処理
して架橋反応せしめるホルムアルデヒドによる気相加工
を施すことを特徴とするセルロース系繊維布帛の加工方
法を要旨とするものである。
成するもので，次の構成よりなるものである。すなわ
ち，本発明は，セルロース系繊維布帛に保湿剤を付与，
乾燥した後，ホルムアルデヒドガスを吸着させ，熱処理
して架橋反応せしめるホルムアルデヒドによる気相加工
を施すことを特徴とするセルロース系繊維布帛の加工方
法を要旨とするものである。
【０００６】以下，本発明を詳細に説明する。
【０００７】本発明でいうセルロース系繊維布帛とは，
木綿，麻等の天然繊維，レーヨン，ポリノジック等の再
生セルロース繊維を含有する織物，編物，不織布等をい
い，その他の繊維としてポリエステル，ナイロン等の合
成繊維が混紡，混繊，交織等の形で混用されていてもよ
い。もちろん，セルロース系繊維１００％よりなる布帛
であってもよい。
木綿，麻等の天然繊維，レーヨン，ポリノジック等の再
生セルロース繊維を含有する織物，編物，不織布等をい
い，その他の繊維としてポリエステル，ナイロン等の合
成繊維が混紡，混繊，交織等の形で混用されていてもよ
い。もちろん，セルロース系繊維１００％よりなる布帛
であってもよい。
【０００８】本発明方法では，まず，上述のセルロース
系繊維布帛に保湿剤を付与する。ここで用いる保湿剤と
しては，ヒアルロン酸ナトリウム，ヒアルロン酸，コラ
ーゲン，スクワラン，スクワレン，ピロリドンカルボン
酸ナトリウム，キトサン，グリチルリチン酸，ラノリ
ン，尿素，蜜ろう，グリセリン，アルギン酸ソーダ，ポ
リエチレンオキサイド等を挙げることができ，これらの
うちの１種または２種以上を用いてセルロース系繊維布
帛に付与する。
系繊維布帛に保湿剤を付与する。ここで用いる保湿剤と
しては，ヒアルロン酸ナトリウム，ヒアルロン酸，コラ
ーゲン，スクワラン，スクワレン，ピロリドンカルボン
酸ナトリウム，キトサン，グリチルリチン酸，ラノリ
ン，尿素，蜜ろう，グリセリン，アルギン酸ソーダ，ポ
リエチレンオキサイド等を挙げることができ，これらの
うちの１種または２種以上を用いてセルロース系繊維布
帛に付与する。
【０００９】この保湿剤をセルロース系繊維布帛に付与
するには，まず，水に保湿剤を溶解し，その水溶液を通
常の方法で布帛に含浸し，乾燥させる方法によって行う
ことができる。実用的には，パッダー等で付着量をコン
トロールして付与することがより一層好ましい。縫製品
の場合には，上述の水溶液に浸漬後，均一に遠心脱水す
るか，またはスプレーにより均一に吹きつけて乾燥機で
乾燥する方法をとる。乾燥は，９０〜２００℃にて0.５
〜２分間行う。
するには，まず，水に保湿剤を溶解し，その水溶液を通
常の方法で布帛に含浸し，乾燥させる方法によって行う
ことができる。実用的には，パッダー等で付着量をコン
トロールして付与することがより一層好ましい。縫製品
の場合には，上述の水溶液に浸漬後，均一に遠心脱水す
るか，またはスプレーにより均一に吹きつけて乾燥機で
乾燥する方法をとる。乾燥は，９０〜２００℃にて0.５
〜２分間行う。
【００１０】次に，本発明では，上述の布帛にホルムア
ルデヒドガスを吸着させ，熱処理して架橋せしめるホル
ムアルデヒドによる気相加工を施す。
ルデヒドガスを吸着させ，熱処理して架橋せしめるホル
ムアルデヒドによる気相加工を施す。
【００１１】気相加工に際しては，密閉系の反応室を有
し，その内部へホルムアルデヒドガス等を送り込む吹き
込み装置，反応のための加熱装置，被加工体を固定する
装置を有してなる気相加工装置を用いることができ，具
体的気相加工装置としては，ＡＴＰ社（ American Text
ile Processing Co.) 製の気相加工装置（特開平５−１
１７９５８号）を用いることができる。
し，その内部へホルムアルデヒドガス等を送り込む吹き
込み装置，反応のための加熱装置，被加工体を固定する
装置を有してなる気相加工装置を用いることができ，具
体的気相加工装置としては，ＡＴＰ社（ American Text
ile Processing Co.) 製の気相加工装置（特開平５−１
１７９５８号）を用いることができる。
【００１２】この気相加工装置内でのホルムアルデヒド
ガス濃度は，１〜２０％の範囲が望ましく，１％以下で
あると，架橋反応が不十分となり，また，２０％以上に
なっても，効果はそれ以上あがらなくなる。
ガス濃度は，１〜２０％の範囲が望ましく，１％以下で
あると，架橋反応が不十分となり，また，２０％以上に
なっても，効果はそれ以上あがらなくなる。
【００１３】架橋反応をさせる際に用いる触媒は，予め
布帛に触媒溶液をパディングした後に気相処理を行って
もよいし，触媒溶液もしくは液化している触媒を気化さ
せて布帛に吸着させてもよい。
布帛に触媒溶液をパディングした後に気相処理を行って
もよいし，触媒溶液もしくは液化している触媒を気化さ
せて布帛に吸着させてもよい。
【００１４】触媒の種類に関しては，予め触媒をパディ
ングする場合は，従来の樹脂加工と同じ触媒，例えば，
硝酸亜鉛のような酸の金属塩，ルイス酸，フレンステッ
ド酸等を用いることができる。また，気化させる場合
は，塩化水素のような揮発性の沸点の低い酸が望まし
い。
ングする場合は，従来の樹脂加工と同じ触媒，例えば，
硝酸亜鉛のような酸の金属塩，ルイス酸，フレンステッ
ド酸等を用いることができる。また，気化させる場合
は，塩化水素のような揮発性の沸点の低い酸が望まし
い。
【００１５】触媒濃度に関しては，ガスで処理する場合
は0.１〜3.０％の範囲が望ましい。ガス濃度が0.１％以
下であると，架橋反応が不十分となり，また，3.０％以
上になっても，それ以上効果があがらなくなる。触媒を
水溶液でパディングしてつける場合の触媒濃度は，５〜
１００ｇ／リットルの範囲が望ましい。濃度が５ｇ／リ
ットル以下になると，架橋反応が不十分となり，１００
ｇ／リットル以上になっても，それ以上効果はあがらな
くなる。
は0.１〜3.０％の範囲が望ましい。ガス濃度が0.１％以
下であると，架橋反応が不十分となり，また，3.０％以
上になっても，それ以上効果があがらなくなる。触媒を
水溶液でパディングしてつける場合の触媒濃度は，５〜
１００ｇ／リットルの範囲が望ましい。濃度が５ｇ／リ
ットル以下になると，架橋反応が不十分となり，１００
ｇ／リットル以上になっても，それ以上効果はあがらな
くなる。
【００１６】ホルムアルデヒドガスを吸着させた後，布
帛を熱処理して架橋反応を行うが，この熱処理は，１０
０〜１８０℃の範囲の温度で，0.５〜１０分間の処理を
行うことにより架橋反応を完結することができる。
帛を熱処理して架橋反応を行うが，この熱処理は，１０
０〜１８０℃の範囲の温度で，0.５〜１０分間の処理を
行うことにより架橋反応を完結することができる。
【００１７】本発明は，以上の構成よりなるものであ
る。
る。
【００１８】
【作用】本発明のごとく，セルロース系繊維布帛に保湿
剤を付与，乾燥後，ホルムアルデヒドによる気相加工を
施すと，保湿剤の作用によって布帛の吸湿性が均一化さ
れるので，外気の湿度に影響されず，布帛の全体にわた
って水分率を均一に保つことができるため，均一な改質
加工を行うことができるようになる。
剤を付与，乾燥後，ホルムアルデヒドによる気相加工を
施すと，保湿剤の作用によって布帛の吸湿性が均一化さ
れるので，外気の湿度に影響されず，布帛の全体にわた
って水分率を均一に保つことができるため，均一な改質
加工を行うことができるようになる。
【００１９】
【実施例】次に，本発明を実施例によってさらに具体的
に説明するが，実施例における布帛の性能の測定，評価
は，それぞれ１０点ずつランダムに採取した試料につい
て下記の方法で行った。
に説明するが，実施例における布帛の性能の測定，評価
は，それぞれ１０点ずつランダムに採取した試料につい
て下記の方法で行った。
【００２０】（１）イージーケアー性 洗濯後のしわ ＡＡＴＣＣ−１２４ パッカリング性 ＡＡＴＣＣ−８８−１９６４Ｔ プリーツ性 ＡＡＴＣＣ−８８Ｃ−１９６４
Ｔ
Ｔ
【００２１】実施例１ 木綿５０％，ポリエステル５０％よりなる混紡糸５０番
手単糸を用いた平織物（経糸１５５本／吋，緯糸８０本
／吋）に，通常の糊抜，精練，漂白，シルケットを行っ
た後，これをマングルにて下記処方１の保湿剤処理液に
浸漬し，ピックアップ６０％でパディング後，１００℃
にて1.５分間の乾燥を行った。 処方１ ヒアルロン酸ナトリウム（１％液） ５００ｇ／リ
ットル
手単糸を用いた平織物（経糸１５５本／吋，緯糸８０本
／吋）に，通常の糊抜，精練，漂白，シルケットを行っ
た後，これをマングルにて下記処方１の保湿剤処理液に
浸漬し，ピックアップ６０％でパディング後，１００℃
にて1.５分間の乾燥を行った。 処方１ ヒアルロン酸ナトリウム（１％液） ５００ｇ／リ
ットル
【００２２】この布帛を用いてドレスシャツ１０点を縫
製後，ＡＴＰ社（American TextileProcessing Co.)製
の気相加工装置（ステンレス製の幅６フィート，長さ１
０フィート，高さ７フィートの常圧密閉型反応室）を使
用して，この加工装置に上記ドレスシャツを入れ，密閉
し，１７psi 及び約２２０°Ｆのスチームで，インジェ
クタおよびスチーム導管を介して，フォルムアルデヒド
水溶液を1.５分間室内に供給し，２４００ｇのフォルム
アルデヒド水溶液を注入した。次いで亜硫酸ガス１５lb
s を注入し, ２分間浸漬後，シャツに保持されなかった
遊離のフォルムアルデヒドおよび亜硫酸ガスを排気し，
室内温度を２６０°Ｆに上昇させた後，６０psi のスチ
ームを５分間注入して残存フォルムアルデヒドを除き，
冷却してシャツを取り出した。
製後，ＡＴＰ社（American TextileProcessing Co.)製
の気相加工装置（ステンレス製の幅６フィート，長さ１
０フィート，高さ７フィートの常圧密閉型反応室）を使
用して，この加工装置に上記ドレスシャツを入れ，密閉
し，１７psi 及び約２２０°Ｆのスチームで，インジェ
クタおよびスチーム導管を介して，フォルムアルデヒド
水溶液を1.５分間室内に供給し，２４００ｇのフォルム
アルデヒド水溶液を注入した。次いで亜硫酸ガス１５lb
s を注入し, ２分間浸漬後，シャツに保持されなかった
遊離のフォルムアルデヒドおよび亜硫酸ガスを排気し，
室内温度を２６０°Ｆに上昇させた後，６０psi のスチ
ームを５分間注入して残存フォルムアルデヒドを除き，
冷却してシャツを取り出した。
【００２３】本発明との比較のため，本実施例において
処方１の保湿剤処理を省くほかは，本実施例と全く同一
の方法により比較用のドレスシャツ（比較例１）を得
た。また，参考までに，本実施例において保湿剤処理直
前の未加工布帛を用いてドレスシャツ１０点（比較例
２）を縫製し，比較用に供した。
処方１の保湿剤処理を省くほかは，本実施例と全く同一
の方法により比較用のドレスシャツ（比較例１）を得
た。また，参考までに，本実施例において保湿剤処理直
前の未加工布帛を用いてドレスシャツ１０点（比較例
２）を縫製し，比較用に供した。
【００２４】本発明および比較用のドレスシャツの性能
を測定，評価し，その結果を合わせて表１に示した。
を測定，評価し，その結果を合わせて表１に示した。
【００２５】
【表１】
【００２６】表１より明らかなごとく，本発明方法によ
るドレスシャツは，イージーケアー性能のバラツキがな
く，優れたイージーケアー性を有していることが分か
る。
るドレスシャツは，イージーケアー性能のバラツキがな
く，優れたイージーケアー性を有していることが分か
る。
【００２７】
【発明の効果】本発明方法によれば，性能にバラツキの
ない均一なイージーケアー性能に優れたホルムアルデヒ
ドによる気相加工を行うことができる。
ない均一なイージーケアー性能に優れたホルムアルデヒ
ドによる気相加工を行うことができる。
Claims (2)
- 【請求項１】 セルロース系繊維布帛に保湿剤を付与，
乾燥した後，ホルムアルデヒドガスを吸着させ，熱処理
して架橋せしめるホルムアルデヒドによる気相加工を施
すことを特徴とするセルロース系繊維布帛の加工方法。 - 【請求項２】 保湿剤が，ヒアルロン酸ナトリウム，コ
ラーゲン，スクワラン，スクワレン，ピロリドンカルボ
ン酸ナトリウム，キトサン，グリチルリチン酸，ラノリ
ン，尿素，密ロウ，グリセリン，アルギン酸ソーダ，ポ
リエチレンオキサイドからなる群より選ばれた少なくと
も１種であることを特徴とする請求項１記載のセルロー
ス系繊維布帛の加工方法。