JPH0890703A - Interior wall panel and manufacturing method thereof - Google Patents
Interior wall panel and manufacturing method thereofInfo
- Publication number
- JPH0890703A JPH0890703A JP6229349A JP22934994A JPH0890703A JP H0890703 A JPH0890703 A JP H0890703A JP 6229349 A JP6229349 A JP 6229349A JP 22934994 A JP22934994 A JP 22934994A JP H0890703 A JPH0890703 A JP H0890703A
- Authority
- JP
- Japan
- Prior art keywords
- adhesive
- wall panel
- self
- reinforcing material
- interior wall
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、住宅を構成する内装用
壁パネルおよびその製造方法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an interior wall panel that constitutes a house and a method for manufacturing the same.
【０００２】[0002]
【従来の技術】一般に、内装用壁パネルは、パネル表面
材、例えば、表面に化粧が施された化粧けい酸カルシウ
ム板と、裏打ち補強材、例えば、石膏ボードや断熱ボー
ドを一体化して構成されており、その接合には、合成樹
脂製の接着剤が使用されていた。2. Description of the Related Art Generally, an interior wall panel is constructed by integrating a panel surface material, for example, a calcium silicate board whose surface is made up with makeup, with a backing reinforcing material, for example, gypsum board or heat insulation board. However, a synthetic resin adhesive was used for the joining.
【０００３】[0003]
【発明が解決しようとする課題】しかしながら、前述し
たパネル表面材と裏打ち補強材とを合成樹脂製接着剤を
介して接合し、内装用壁パネルを製造する方法では、壁
パネルを持ち運びできるような接合強度に達するまでに
は、一定時間養生させて接着剤を反応硬化させる必要が
ある。However, in the method of manufacturing the interior wall panel by joining the above-mentioned panel surface material and the backing reinforcing material via the synthetic resin adhesive, the wall panel can be carried around. Before reaching the bonding strength, it is necessary to cure the adhesive for a certain period of time to cure the adhesive.
【０００４】なお、短時間で接合強度を上げるために
は、熱によって反応を促進させればよく、例えば、熱プ
レス法、ホットメルト法や高周波ウエルダー法などが知
られているが、壁パネルは熱容量が大きく、大容量の熱
源を必要とするなど、いずれも設備装置が大きくなる欠
点がある。特に、裏打ち補強材に断熱ボードを用いた場
合には、長時間加熱しなければならない他、熱に弱いパ
ネル表面材には採用できない問題もある。In order to increase the bonding strength in a short time, the reaction may be accelerated by heat. For example, the hot press method, hot melt method and high frequency welder method are known. Both have the disadvantages that the equipment is large, such as having a large heat capacity and requiring a large-capacity heat source. In particular, when a heat insulating board is used as the backing reinforcing material, it has to be heated for a long time, and there is a problem that it cannot be applied to a panel surface material which is weak against heat.
【０００５】本発明は、このような問題点に鑑みてなさ
れたもので、加熱することなく短時間で製造することの
できる内装用壁パネルおよびその製造方法を提供するも
のである。The present invention has been made in view of the above problems, and provides an interior wall panel which can be manufactured in a short time without heating and a manufacturing method thereof.
【０００６】[0006]
【課題を解決するための手段】本発明の内装用壁パネル
は、パネル表面材と裏打ち補強材を粘着材を介して接合
したことを特徴とするものである。The interior wall panel of the present invention is characterized in that the panel surface material and the backing reinforcing material are joined together via an adhesive material.
【０００７】また、本発明の内装用壁パネルの製造方法
は、裏打ち補強材に粘着材を塗布してパネル表面材を重
ね合わせた後、冷間圧締プレスで加圧することを特徴と
するものである。Further, the method for producing an interior wall panel of the present invention is characterized in that an adhesive material is applied to the backing reinforcing material, the panel surface materials are superposed, and then a cold pressing press is applied. Is.
【０００８】[0008]
【作用】裏打ち補強材に粘着剤を塗布した後、パネル表
面材を重ね合わせ、次いで、冷間圧締プレスで加圧す
る。After the adhesive is applied to the lining reinforcing material, the panel surface materials are superposed and then pressed by a cold pressing press.
【０００９】この結果、パネル表面材と裏打ち補強材と
の接合強度が加熱することなく短時間で得られる。As a result, the bonding strength between the panel surface material and the backing reinforcing material can be obtained in a short time without heating.
【００１０】[0010]
【実施例】以下、本発明の実施例を図面を参照して説明
する。Embodiments of the present invention will be described below with reference to the drawings.
【００１１】図１には、本発明の内装用壁パネル１が示
されている。この壁パネル１は、化粧けい酸カルシウム
板などのパネル表面材２と、石膏ボードなどの裏打ち補
強材３から構成されており、これらのパネル表面材２と
裏打ち補強材３との接合には粘着剤４が用いられてい
る。FIG. 1 shows an interior wall panel 1 of the present invention. This wall panel 1 is composed of a panel surface material 2 such as a decorative calcium silicate board and a backing reinforcing material 3 such as a gypsum board. Adhesion between the panel surface material 2 and the backing reinforcing material 3 is adhesive. Agent 4 is used.
【００１２】この内装用壁パネル１を製造するには、裏
打ち補強材、具体的には、石膏ボード３に対し、図示し
ないロールコータを用いてアクリルエマルジョン系粘着
剤４を塗布量４０ｇ／ｍ2 で全面に塗布する。この後、
パネル表面材、具体的には、化粧けい酸カルシウム板２
に重ね合わせ、次いで、パネル表面材２および裏打ち補
強材３の凹凸によって接合面積が減少するのを防止する
ため、冷間圧締プレス（図示せず）により加圧する。そ
の圧力および加圧時間は、５Ｋｇｆ／ｃｍ2 以上、１０
秒以上が好ましい。この結果、粘着剤４中の水分がパネ
ル表面材２および裏打ち補強材３に移行し、粘着剤４の
粘着強度が発現し、両者の接合が完了する。このよう
に、秒単位で接合強度が得られることから、従来の接着
剤を用いて時間単位で養生させる方式に比較して大幅に
製造時間を減少することができ、しかも、加熱装置が不
要であるから、設備装置をコンパクトに形成することが
できる。To manufacture this interior wall panel 1, an acrylic emulsion pressure-sensitive adhesive 4 is applied to a backing reinforcing material, specifically, gypsum board 3, using a roll coater (not shown) at a coating amount of 40 g / m 2. Apply to the entire surface with. After this,
Panel surface material, concretely calcium silicate board 2
Then, in order to prevent the joint area from being reduced due to the unevenness of the panel surface material 2 and the backing reinforcing material 3, pressure is applied by a cold pressing press (not shown). The pressure and the pressurizing time are 5 Kgf / cm 2 or more and 10
Seconds or more are preferable. As a result, the water content in the pressure-sensitive adhesive 4 is transferred to the panel surface material 2 and the backing reinforcing material 3, the adhesive strength of the pressure-sensitive adhesive 4 is developed, and the joining of both is completed. In this way, since the bonding strength can be obtained in seconds, it is possible to significantly reduce the manufacturing time as compared with the conventional method of curing the adhesive in hours. Therefore, the equipment can be formed compactly.
【００１３】[0013]
【発明の効果】以上のように本発明によれば、裏打ち補
強材に粘着剤を塗布してパネル表面材を重ね合わせた
後、冷間圧締プレスで加圧することにより、内装用壁パ
ネルを加熱装置を用いることなく短時間で製造すること
ができる。As described above, according to the present invention, an adhesive is applied to the backing reinforcing material, the panel surface materials are superposed on each other, and then pressed by a cold pressing press to form an interior wall panel. It can be manufactured in a short time without using a heating device.
【図１】本発明の内装用壁パネルの斜視図である。FIG. 1 is a perspective view of an interior wall panel of the present invention.
１ 内装用壁パネル ２ パネル表面材 ３ 裏打ち補強材 ４ 粘着剤 1 Wall panel for interior 2 Panel surface material 3 Reinforcing material 4 Adhesive
Claims (2)
介して接合したことを特徴とする内装用壁パネル。1. A wall panel for interior use, characterized in that a panel surface material and a backing reinforcing material are bonded together via an adhesive.
表面材を重ね合わせた後、冷間圧締プレスで加圧するこ
とを特徴とする内装用壁パネルの製造方法。2. A method for manufacturing an interior wall panel, which comprises applying a pressure-sensitive adhesive to a backing reinforcing material, stacking panel surface materials, and then applying pressure with a cold pressing press.