JPH09208828A - シリコーンゴム組成物 - Google Patents
シリコーンゴム組成物Info
- Publication number
- JPH09208828A JPH09208828A JP8037457A JP3745796A JPH09208828A JP H09208828 A JPH09208828 A JP H09208828A JP 8037457 A JP8037457 A JP 8037457A JP 3745796 A JP3745796 A JP 3745796A JP H09208828 A JPH09208828 A JP H09208828A
- Authority
- JP
- Japan
- Prior art keywords
- silicone rubber
- parts
- group
- weight
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】
【課題】 機械的強度と電気特性に優れたシリコーンゴ
ム組成物を提供する。 【解決手段】 (Ａ)ケイ素原子結合アルケニル基を有す
るオルガノポリシロキサン生ゴム、(Ｂ)水酸化アルミニ
ウム粉末、(Ｃ)アルケニル基含有シランまたはシロキサ
ンオリゴマー、(Ｄ)有機過酸化物からなるシリコーンゴ
ム組成物、および(Ａ)ケイ素原子結合アルケニル基を有
するオルガノポリシロキサン生ゴム、(Ｅ)アルケニル基
含有シランまたはシロキサンオリゴマーにより表面処理
されてなる水酸化アルミニウム粉末および(Ｄ)有機過酸
化物からなるシリコーンゴム組成物。
ム組成物を提供する。 【解決手段】 (Ａ)ケイ素原子結合アルケニル基を有す
るオルガノポリシロキサン生ゴム、(Ｂ)水酸化アルミニ
ウム粉末、(Ｃ)アルケニル基含有シランまたはシロキサ
ンオリゴマー、(Ｄ)有機過酸化物からなるシリコーンゴ
ム組成物、および(Ａ)ケイ素原子結合アルケニル基を有
するオルガノポリシロキサン生ゴム、(Ｅ)アルケニル基
含有シランまたはシロキサンオリゴマーにより表面処理
されてなる水酸化アルミニウム粉末および(Ｄ)有機過酸
化物からなるシリコーンゴム組成物。
Description
【０００１】
【発明の属する技術分野】本発明は、シリコーンゴム組
成物に関する。詳しくは、高い機械的強度と良好な電気
特性（耐トラッキング性、耐アーク性、耐エロージョン
性等）を有するシリコーンゴム組成物に関する。
成物に関する。詳しくは、高い機械的強度と良好な電気
特性（耐トラッキング性、耐アーク性、耐エロージョン
性等）を有するシリコーンゴム組成物に関する。
【０００２】
【従来の技術】従来、シリコーンゴム組成物に水酸アル
ミニウム粉末を配合してなる組成物は知られており、こ
の種の水酸化アルミニウム粉末を多量に含有するシリコ
ーンゴム組成物は、硬化して電気特性に優れたシリコー
ンゴム成形品になるということも知られている（特開平
５−１２８０５号公報，特開平７−５７５７４号公報参
照）。しかし、この種のシリコーンゴム組成物は、引張
強さ、引裂強さ等の機械的強度に劣り、用途によっては
使用できないものであった。
ミニウム粉末を配合してなる組成物は知られており、こ
の種の水酸化アルミニウム粉末を多量に含有するシリコ
ーンゴム組成物は、硬化して電気特性に優れたシリコー
ンゴム成形品になるということも知られている（特開平
５−１２８０５号公報，特開平７−５７５７４号公報参
照）。しかし、この種のシリコーンゴム組成物は、引張
強さ、引裂強さ等の機械的強度に劣り、用途によっては
使用できないものであった。
【０００３】
【発明が解決しようとする課題】本発明者らは、上記の
欠点を解消すべく鋭意研究した結果本発明に到達した。
即ち、本発明の目的は、補強性充填剤を含有しなくても
優れた機械的強度と電気特性を有するシリコーンゴム組
成物を提供することにある。
欠点を解消すべく鋭意研究した結果本発明に到達した。
即ち、本発明の目的は、補強性充填剤を含有しなくても
優れた機械的強度と電気特性を有するシリコーンゴム組
成物を提供することにある。
【０００４】
【課題の解決手段】 本発明は、(Ａ)平均組成式；ＲaＳｉＯ(4-a)/2（式中、Ｒは置換または非置換 の１価炭化水素基であり、ａは１.９５〜２.０５の数である。）で示され、１分 子中に少なくとも２個のケイ素原子結合アルケニル基を有するオルガノポリシロ キサン生ゴム １００重量部、 (Ｂ)水酸化アルミニウム粉末 １０〜３００重量部、 (Ｃ)アルケニル基およびアルコキシ基もしくは水酸基を有するシランまたはシロ キサンオリゴマー ０.１〜３０重量部、 および (Ｄ)有機過酸化物 ０.１〜１０重量部 からなるシリコーンゴム組成物、および (Ａ)平均組成式；ＲaＳｉＯ(4-a)/2（式中、Ｒは置換または非置換の１価炭化水 素基であり、ａは１.９５〜２.０５の数である。）で示され、１分子中に少なく とも２個のケイ素原子結合アルケニル基を有するオルガノポリシロキサン生ゴム １００重量部、 (Ｅ)アルケニル基およびアルコキシ基もしくは水酸基を有するシランまたはシロ キサンオリゴマーにより表面処理されてなる水酸化アルミニウム粉末 １０〜３００重量部、 (Ｄ)有機過酸化物 ０.１〜１０重量部 からなるシリコーンゴム組成物に関する。
【０００５】
【発明の実施の形態】これを説明すると、(Ａ)成分のオ
ルガノポリシロキサン生ゴムは、本発明組成物の主成分
であり、平均組成式；ＲaＳｉＯ(4-a)/2で示される。式
中、Ｒは置換または非置換の１価炭化水素基であり、例
えば、メチル基、エチル基、プロピル基などのアルキル
基；ビニル基、アリル基、ブチニル基、ヘキセニル基な
どのアルケニル基；フェニル基などのアリール基；３,
３,３−トリフルオロプロピル基、２−フェニルエチル
基、２−シアノエチル基が挙げられる。式中、ａは１.
９５〜２.０５の数である。本成分は１分子中に少なく
とも２個のケイ素原子結合アルケニル基を有する。この
アルケニル基の結合位置は、側鎖でも末端でもよく、ま
たその両方でもよい。本成分の分子構造は、直鎖状また
は一部に分岐を有する直鎖状である。本成分の重合度
は、通常１,０００〜２０,０００の範囲である。本成分
は単一重合体でも共重合体でもよく、あるいはこれらの
重合体の混合物でもよい。本成分を構成する単位の具体
例としては、ジメチルシロキサン単位、メチルフェニル
シロキサン単位、メチルビニルシロキサン単位、メチル
（３,３,３−トリフルオロプロピル）シロキサン単位が
挙げられる。また、本成分の分子末端基としては、トリ
メチルシロキシ基、ジメチルビニルシロキシ基、メチル
ビニルヒドロキシシロキシ基が例示される。このような
オルガノポリシロキサン生ゴムとしては、両末端ジメチ
ルビニルシロキシ基封鎖ジメチルシロキサン・メチルビ
ニルシロキサン共重合体生ゴム、両末端ジメチルビニル
シロキシ基封鎖ジメチルポリシロキサン生ゴム、両末端
シラノール基封鎖ジメチルシロキサン・メチルビニルシ
ロキサン共重合体生ゴム、両末端メチルビニルヒドロキ
シシロキシ基封鎖ジメチルシロキサン・メチルビニルシ
ロキサン共重合体生ゴムが挙げられる。
ルガノポリシロキサン生ゴムは、本発明組成物の主成分
であり、平均組成式；ＲaＳｉＯ(4-a)/2で示される。式
中、Ｒは置換または非置換の１価炭化水素基であり、例
えば、メチル基、エチル基、プロピル基などのアルキル
基；ビニル基、アリル基、ブチニル基、ヘキセニル基な
どのアルケニル基；フェニル基などのアリール基；３,
３,３−トリフルオロプロピル基、２−フェニルエチル
基、２−シアノエチル基が挙げられる。式中、ａは１.
９５〜２.０５の数である。本成分は１分子中に少なく
とも２個のケイ素原子結合アルケニル基を有する。この
アルケニル基の結合位置は、側鎖でも末端でもよく、ま
たその両方でもよい。本成分の分子構造は、直鎖状また
は一部に分岐を有する直鎖状である。本成分の重合度
は、通常１,０００〜２０,０００の範囲である。本成分
は単一重合体でも共重合体でもよく、あるいはこれらの
重合体の混合物でもよい。本成分を構成する単位の具体
例としては、ジメチルシロキサン単位、メチルフェニル
シロキサン単位、メチルビニルシロキサン単位、メチル
（３,３,３−トリフルオロプロピル）シロキサン単位が
挙げられる。また、本成分の分子末端基としては、トリ
メチルシロキシ基、ジメチルビニルシロキシ基、メチル
ビニルヒドロキシシロキシ基が例示される。このような
オルガノポリシロキサン生ゴムとしては、両末端ジメチ
ルビニルシロキシ基封鎖ジメチルシロキサン・メチルビ
ニルシロキサン共重合体生ゴム、両末端ジメチルビニル
シロキシ基封鎖ジメチルポリシロキサン生ゴム、両末端
シラノール基封鎖ジメチルシロキサン・メチルビニルシ
ロキサン共重合体生ゴム、両末端メチルビニルヒドロキ
シシロキシ基封鎖ジメチルシロキサン・メチルビニルシ
ロキサン共重合体生ゴムが挙げられる。
【０００６】(Ｂ)成分の水酸化アルミニウム粉末は、本
発明組成物を硬化させて得られるシリコーンゴムに機械
的強度と優れた電気特性を付与するために必須とされる
成分である。この水酸化アルミニウムはその粒子径が小
さいほど補強性効果が大きく、通常、０.２〜５０μｍ
の範囲内のものが使用され、０.２〜１０μｍのものが
好ましく使用される。本成分の配合量は、(Ａ)成分１０
０重量部に対して１０〜３００重量部であり、好ましく
は３０〜２００重量部である。これは(Ｂ)成分の配合量
が３０重量部より少ないと機械的強度の向上と電気絶縁
性について効果が不十分であり、２００重量部を越える
と硬化物の脆化が起こるからである。
発明組成物を硬化させて得られるシリコーンゴムに機械
的強度と優れた電気特性を付与するために必須とされる
成分である。この水酸化アルミニウムはその粒子径が小
さいほど補強性効果が大きく、通常、０.２〜５０μｍ
の範囲内のものが使用され、０.２〜１０μｍのものが
好ましく使用される。本成分の配合量は、(Ａ)成分１０
０重量部に対して１０〜３００重量部であり、好ましく
は３０〜２００重量部である。これは(Ｂ)成分の配合量
が３０重量部より少ないと機械的強度の向上と電気絶縁
性について効果が不十分であり、２００重量部を越える
と硬化物の脆化が起こるからである。
【０００７】(Ｃ)成分のシランまたはシロキサンオリゴ
マーは本発明の特徴をなす成分であり、本発明組成物中
の(Ｂ)成分の表面を処理し、本発明組成物の機械的強度
を向上させるために必須とされる成分である。本成分と
しては、ビニルトリメトキシシラン、ビニルトリアセト
キシシラン、アリルトリメトキシシラン、ブチニルトリ
メトキシシラン、ヘキセニルトリメトキシシラン、Ｎ−
β−（Ｎ−ビニルベンジルアミノエチル）−γ−アミノ
プロピルトリメトキシシラン等のアルケニルトリアルコ
キシシラン類、側鎖にアルケニル基を２５重量パーセン
ト以下を持ち、分子鎖末端にシラノール基もしくはアル
コキシ基を有する直鎖状オルガノシロキサンオリゴマ
ー、ＲＳｉＯ1.5単位（式中、Ｒは前記と同じであ
る。）（Ｔ単位）やＳｉＯ2単位（Ｑ単位）を持ち、Ｒ
の一部または全部がアルケニル基であるレジン状のシロ
キサンオリゴマー等が挙げられる。
マーは本発明の特徴をなす成分であり、本発明組成物中
の(Ｂ)成分の表面を処理し、本発明組成物の機械的強度
を向上させるために必須とされる成分である。本成分と
しては、ビニルトリメトキシシラン、ビニルトリアセト
キシシラン、アリルトリメトキシシラン、ブチニルトリ
メトキシシラン、ヘキセニルトリメトキシシラン、Ｎ−
β−（Ｎ−ビニルベンジルアミノエチル）−γ−アミノ
プロピルトリメトキシシラン等のアルケニルトリアルコ
キシシラン類、側鎖にアルケニル基を２５重量パーセン
ト以下を持ち、分子鎖末端にシラノール基もしくはアル
コキシ基を有する直鎖状オルガノシロキサンオリゴマ
ー、ＲＳｉＯ1.5単位（式中、Ｒは前記と同じであ
る。）（Ｔ単位）やＳｉＯ2単位（Ｑ単位）を持ち、Ｒ
の一部または全部がアルケニル基であるレジン状のシロ
キサンオリゴマー等が挙げられる。
【０００８】(Ｄ)成分の有機過酸化物は、本発明組成物
を加熱硬化させるための加硫剤である。本成分として
は、シリコーンゴム組成物の加硫剤として常用されてい
る従来公知の有機過酸化物が使用できる。このような有
機過酸化物としては、ベンゾイルパーオキサイド、ｔ−
ブチルパーベンゾエイト、２,４−ジクロロベンゾイル
パーオキサイド、ジクミルパーオキサイド、２,５−ジ
メチル−２,５−ジ（ｔ−ブチルパーオキシ）ヘキサン
が例示される。
を加熱硬化させるための加硫剤である。本成分として
は、シリコーンゴム組成物の加硫剤として常用されてい
る従来公知の有機過酸化物が使用できる。このような有
機過酸化物としては、ベンゾイルパーオキサイド、ｔ−
ブチルパーベンゾエイト、２,４−ジクロロベンゾイル
パーオキサイド、ジクミルパーオキサイド、２,５−ジ
メチル−２,５−ジ（ｔ−ブチルパーオキシ）ヘキサン
が例示される。
【０００９】本発明組成物は上記(Ａ)成分〜(Ｄ)成分か
らなるものであるが、上記(Ｂ)成分と上記(Ｃ)成分の代
わりに、予め(Ｃ)成分で(Ｂ)成分の表面を処理したもの
も使用できる。即ち、本発明のもう一つの発明は、 (Ａ)平均組成式；ＲaＳｉＯ(4-a)/2（式中、Ｒは置換または非置換の１価炭化水 素基であり、ａは１.９５〜２.０５の数である。）で示され、１分子中に少なく とも２個のケイ素原子結合アルケニル基を有するオルガノポリシロキサン生ゴム １００重量部、 (Ｅ)アルケニル基およびアルコキシ基もしくは水酸基を有するシランまたはシロ キサンオリゴマーにより表面処理されてなる水酸化アルミニウム粉末 １０〜３００重量部、 (Ｄ)有機過酸化物 ０.１〜１０重量部 からなるシリコーンゴム組成物である。
らなるものであるが、上記(Ｂ)成分と上記(Ｃ)成分の代
わりに、予め(Ｃ)成分で(Ｂ)成分の表面を処理したもの
も使用できる。即ち、本発明のもう一つの発明は、 (Ａ)平均組成式；ＲaＳｉＯ(4-a)/2（式中、Ｒは置換または非置換の１価炭化水 素基であり、ａは１.９５〜２.０５の数である。）で示され、１分子中に少なく とも２個のケイ素原子結合アルケニル基を有するオルガノポリシロキサン生ゴム １００重量部、 (Ｅ)アルケニル基およびアルコキシ基もしくは水酸基を有するシランまたはシロ キサンオリゴマーにより表面処理されてなる水酸化アルミニウム粉末 １０〜３００重量部、 (Ｄ)有機過酸化物 ０.１〜１０重量部 からなるシリコーンゴム組成物である。
【００１０】ここで使用される(Ａ)成分、(Ｄ)成分は上
記した(Ａ)成分、(Ｄ)成分と同じ物である。(Ｅ)成分は
アルケニル基およびアルコキシ基もしくは水酸基を有す
るシランまたはシロキサンオリゴマーにより表面処理さ
れてなる水酸化アルミニウム粉末である。この(Ｅ)成分
に使用されるアルケニル基およびアルコキシ基もしくは
水酸基を有するシランまたはシロキサンオリゴマーおよ
び水酸化アルミニウム粉末はそれぞれ上記(Ｂ)成分およ
び(Ｃ)成分と同じ物である。アルケニル基およびアルコ
キシ基もしくは水酸基を有するシランまたはシロキサン
オリゴマーで表面処理された水酸化アルミニウム粉末
は、水酸化アルミニウム粉末にアルケニル基およびアル
コキシ基もしくは水酸基を有するシランまたはシロキサ
ンオリゴマーを加えて加熱下に均一に混練することによ
り容易に調製できる。
記した(Ａ)成分、(Ｄ)成分と同じ物である。(Ｅ)成分は
アルケニル基およびアルコキシ基もしくは水酸基を有す
るシランまたはシロキサンオリゴマーにより表面処理さ
れてなる水酸化アルミニウム粉末である。この(Ｅ)成分
に使用されるアルケニル基およびアルコキシ基もしくは
水酸基を有するシランまたはシロキサンオリゴマーおよ
び水酸化アルミニウム粉末はそれぞれ上記(Ｂ)成分およ
び(Ｃ)成分と同じ物である。アルケニル基およびアルコ
キシ基もしくは水酸基を有するシランまたはシロキサン
オリゴマーで表面処理された水酸化アルミニウム粉末
は、水酸化アルミニウム粉末にアルケニル基およびアル
コキシ基もしくは水酸基を有するシランまたはシロキサ
ンオリゴマーを加えて加熱下に均一に混練することによ
り容易に調製できる。
【００１１】本発明組成物は、上記した(Ａ)成分，(Ｂ)
成分，(Ｃ)成分および(Ｄ)成分、あるいは、(Ａ)成分，
(Ｅ)成分および(Ｄ)成分からなるものであるが、これら
の成分に加えて、シリコーンゴム組成物に添加配合する
ことが周知とされる従来公知の各種添加剤、例えば、補
強充填剤、非補強性充填剤、顔料、耐熱剤、難燃剤、内
部離型剤、可塑剤等を添加配合することは、本発明の目
的を損なわない限り差し支えない。ここで、補強充填剤
としては、煙霧法シリカや沈降法シリカおよびオルガノ
シランまたはオルガノシロキサン処理した煙霧法シリ
カ、処理沈降法シリカが例示される。非補強性充填剤と
しては、けいそう土、石英粉末、マイカ、炭酸カルシウ
ム、炭酸亜鉛、炭酸マンガン、酸化アルミニウム、酸化
チタンが例示される。顔料としては、カーボンブラッ
ク、ベンガラが例示される。耐熱剤としては、稀土類酸
化物、稀土類水酸化物、セリウムシラノレート、セリウ
ム脂肪酸塩が例示される。
成分，(Ｃ)成分および(Ｄ)成分、あるいは、(Ａ)成分，
(Ｅ)成分および(Ｄ)成分からなるものであるが、これら
の成分に加えて、シリコーンゴム組成物に添加配合する
ことが周知とされる従来公知の各種添加剤、例えば、補
強充填剤、非補強性充填剤、顔料、耐熱剤、難燃剤、内
部離型剤、可塑剤等を添加配合することは、本発明の目
的を損なわない限り差し支えない。ここで、補強充填剤
としては、煙霧法シリカや沈降法シリカおよびオルガノ
シランまたはオルガノシロキサン処理した煙霧法シリ
カ、処理沈降法シリカが例示される。非補強性充填剤と
しては、けいそう土、石英粉末、マイカ、炭酸カルシウ
ム、炭酸亜鉛、炭酸マンガン、酸化アルミニウム、酸化
チタンが例示される。顔料としては、カーボンブラッ
ク、ベンガラが例示される。耐熱剤としては、稀土類酸
化物、稀土類水酸化物、セリウムシラノレート、セリウ
ム脂肪酸塩が例示される。
【００１２】本発明組成物は、上記した(Ａ)成分，(Ｂ)
成分，(Ｃ)成分および(Ｄ)成分、あるいは、(Ａ)成分，
(Ｅ)成分および(Ｄ)成分を均一に混合することにより容
易に製造できる。ここで、これらの成分を混合するため
の手段としては、シリコーンゴム組成物に使用されてい
る従来公知の混合手段が使用できる。かかる混合手段と
しては、ニーダーミキサーや２軸連続混練押出機、２本
ロール等が挙げられる。
成分，(Ｃ)成分および(Ｄ)成分、あるいは、(Ａ)成分，
(Ｅ)成分および(Ｄ)成分を均一に混合することにより容
易に製造できる。ここで、これらの成分を混合するため
の手段としては、シリコーンゴム組成物に使用されてい
る従来公知の混合手段が使用できる。かかる混合手段と
しては、ニーダーミキサーや２軸連続混練押出機、２本
ロール等が挙げられる。
【００１３】本発明組成物を硬化させるには、(Ｄ)成分
の有機過酸化物の分解温度以上に加熱し硬化させればよ
い。成形方法としては、圧縮成形、押出成形などの従来
公知の成形方法を目的に応じて適宜選択すればよい。
の有機過酸化物の分解温度以上に加熱し硬化させればよ
い。成形方法としては、圧縮成形、押出成形などの従来
公知の成形方法を目的に応じて適宜選択すればよい。
【００１４】以上のような本発明組成物は、引張強さ、
引裂強さ等の機械的強度に優れており、かつ、ＪＩＳ法
に比較してより過酷な耐トラッキング試験、ＩＥＣ．ｐ
ｕｂｌ．５８７法に合格する。そのため、かかる特性を
要求される用途、特には屋外で使用される高電圧電気絶
縁材を製造するためのシリコーンゴム組成物として好適
である。
引裂強さ等の機械的強度に優れており、かつ、ＪＩＳ法
に比較してより過酷な耐トラッキング試験、ＩＥＣ．ｐ
ｕｂｌ．５８７法に合格する。そのため、かかる特性を
要求される用途、特には屋外で使用される高電圧電気絶
縁材を製造するためのシリコーンゴム組成物として好適
である。
【００１５】
【実施例】次に実施例を挙げて本発明を説明する。実施
例中、部とあるのは重量部のことであり、粘度は２５℃
における測定値である。実施例中、機械的強度の測定，
電気特性の測定は次に示す方法に従って行った。 ○機械的強度の測定 ＪＩＳ Ｋ ６３０１ 加硫ゴムの物理特性測定方法に規
定された方法に準じて測定した。即ち、加熱硬化型シリ
コーンゴム組成物を１５０℃で１０分間の加熱条件下で
圧縮成形し、厚さ２mmのシリコーンゴムシートを成形し
た。このシリコーンゴムシートの機械的強度をＪＩＳ
Ｋ ６３０１に規定する方法に従って測定した。 ○電気特性の測定 ＩＥＣ．ｐｕｂｌ．５８７法に準じて、傾斜平板法耐ト
ラッキング性試験を日立化成工業製，ＨＡＴ−５２０形
を用いて行った。試験電圧は３.５ｋＶであった。表中
の判定Ａおよび判定Ｂは、前者は試験片を通して高圧回
路を流れる電流が６０ｍＡを超えるまでの時間（分）で
あり、後者は、試験片の表面上に下部電極から２５mmの
位置につけたマークにトラッキングが到達した時間
（分）である。
例中、部とあるのは重量部のことであり、粘度は２５℃
における測定値である。実施例中、機械的強度の測定，
電気特性の測定は次に示す方法に従って行った。 ○機械的強度の測定 ＪＩＳ Ｋ ６３０１ 加硫ゴムの物理特性測定方法に規
定された方法に準じて測定した。即ち、加熱硬化型シリ
コーンゴム組成物を１５０℃で１０分間の加熱条件下で
圧縮成形し、厚さ２mmのシリコーンゴムシートを成形し
た。このシリコーンゴムシートの機械的強度をＪＩＳ
Ｋ ６３０１に規定する方法に従って測定した。 ○電気特性の測定 ＩＥＣ．ｐｕｂｌ．５８７法に準じて、傾斜平板法耐ト
ラッキング性試験を日立化成工業製，ＨＡＴ−５２０形
を用いて行った。試験電圧は３.５ｋＶであった。表中
の判定Ａおよび判定Ｂは、前者は試験片を通して高圧回
路を流れる電流が６０ｍＡを超えるまでの時間（分）で
あり、後者は、試験片の表面上に下部電極から２５mmの
位置につけたマークにトラッキングが到達した時間
（分）である。
【００１６】
【実施例１】ジメチルシロキサン単位９９.８７モル％
とメチルビニルシロキサン単位０.１３モル％からな
り、両末端がジメチルビニルシロキシ基で封鎖されたジ
メチルシロキサン・メチルビニルシロキサン共重合体生
ゴム１００部と、表面をビニルトリメトキシシランで処
理した水酸化アルミニウム粉末［昭和電工(株)製，商品
名：ハイジライトＨ４２ＳＴＶ、平均粒子径：１μｍ］
を表１に示した割合でニーダーミキサーに投入して均一
に混練してシリコーンゴムベースコンパウンドを調製し
た。このシリコーンゴムベースコンパウンド１００部
に、２本ロール上で、２,５−ジメチル−２,５−ジ（ｔ
−ブチルパーオキシ）ヘキサンの５０重量％シリコーン
オイルペースト０.８部を添加し、均一に混合してシリ
コーンゴム組成物を得た。このシリコーンゴム組成物の
機械的強度と電気特性を測定して、それらの結果を表１
に示した。
とメチルビニルシロキサン単位０.１３モル％からな
り、両末端がジメチルビニルシロキシ基で封鎖されたジ
メチルシロキサン・メチルビニルシロキサン共重合体生
ゴム１００部と、表面をビニルトリメトキシシランで処
理した水酸化アルミニウム粉末［昭和電工(株)製，商品
名：ハイジライトＨ４２ＳＴＶ、平均粒子径：１μｍ］
を表１に示した割合でニーダーミキサーに投入して均一
に混練してシリコーンゴムベースコンパウンドを調製し
た。このシリコーンゴムベースコンパウンド１００部
に、２本ロール上で、２,５−ジメチル−２,５−ジ（ｔ
−ブチルパーオキシ）ヘキサンの５０重量％シリコーン
オイルペースト０.８部を添加し、均一に混合してシリ
コーンゴム組成物を得た。このシリコーンゴム組成物の
機械的強度と電気特性を測定して、それらの結果を表１
に示した。
【００１７】
【比較例１】実施例１において、表面をビニルトリメト
キシシランで処理した水酸化アルミニウム粉末［昭和電
工(株)製，商品名：ハイジライトＨ４２ＳＴＶ、平均粒
子径：１μｍ］の代わりに、未処理の水酸化アルミニウ
ム粉末［昭和電工(株)製，商品名：ハイジライトＨ４２
Ｍ、平均粒子径：１μｍ］を配合した以外は上記と同様
にしてシリコーンゴム組成物を調製した。このシリコー
ンゴム組成物の機械的強度と電気特性を実施例１と同様
にして測定した。それらの結果を表１に併記した。表１
の結果から本発明の組成物からなるシリコーンゴムは、
引張強さ，引裂強さが高く、優れた機械的強度を有する
ことが分かった。
キシシランで処理した水酸化アルミニウム粉末［昭和電
工(株)製，商品名：ハイジライトＨ４２ＳＴＶ、平均粒
子径：１μｍ］の代わりに、未処理の水酸化アルミニウ
ム粉末［昭和電工(株)製，商品名：ハイジライトＨ４２
Ｍ、平均粒子径：１μｍ］を配合した以外は上記と同様
にしてシリコーンゴム組成物を調製した。このシリコー
ンゴム組成物の機械的強度と電気特性を実施例１と同様
にして測定した。それらの結果を表１に併記した。表１
の結果から本発明の組成物からなるシリコーンゴムは、
引張強さ，引裂強さが高く、優れた機械的強度を有する
ことが分かった。
【表１】
【００１８】
【実施例２】ジメチルシロキサン単位９９.８７モル％
とメチルビニルシロキサン単位０.１３モル％からな
り、両末端がジメチルビニルシロキシ基で封鎖されたジ
メチルシロキサン・メチルビニルシロキサン共重合体生
ゴム１００部と、未処理の水酸化アルミニウム粉末［昭
和電工(株)製，商品名：ハイジライトＨ４２Ｍ、平均粒
子径：１μｍ］１５０部添加し、粘度３０センチポイズ
の両末端シラノール基封鎖ジメチルシロキサン・メチル
ビニルシロキサン共重合体オリゴマー５部（ビニル基
量：１０重量％）をニーダーミキサーに投入して均一に
混練してシリコーンゴムベースコンパウンドを調製し
た。このシリコーンゴムベースコンパウンド１００部に
比表面積１２０ｍ2／ｇのジメチルジクロロシラン処理
ヒュームドシリカ３０部［日本アエロジル(株)製、アエ
ロジルＲ９７２］を均一に混練して、シリコーンゴムベ
ースコンパウンドを調製した。このシリコーンゴムベー
スコンパウンド１００部に、２本ロール上で、２,５−
ジメチル−２,５−ジ（ｔ−ブチルパーオキシ）ヘキサ
ンの５０重量％シリコーンオイルペースト０.８部を添
加し、均一に混合してシリコーンゴム組成物を得た。こ
のシリコーンゴム組成物の機械的強度と電気特性を測定
して、それらの結果を表２に示した。
とメチルビニルシロキサン単位０.１３モル％からな
り、両末端がジメチルビニルシロキシ基で封鎖されたジ
メチルシロキサン・メチルビニルシロキサン共重合体生
ゴム１００部と、未処理の水酸化アルミニウム粉末［昭
和電工(株)製，商品名：ハイジライトＨ４２Ｍ、平均粒
子径：１μｍ］１５０部添加し、粘度３０センチポイズ
の両末端シラノール基封鎖ジメチルシロキサン・メチル
ビニルシロキサン共重合体オリゴマー５部（ビニル基
量：１０重量％）をニーダーミキサーに投入して均一に
混練してシリコーンゴムベースコンパウンドを調製し
た。このシリコーンゴムベースコンパウンド１００部に
比表面積１２０ｍ2／ｇのジメチルジクロロシラン処理
ヒュームドシリカ３０部［日本アエロジル(株)製、アエ
ロジルＲ９７２］を均一に混練して、シリコーンゴムベ
ースコンパウンドを調製した。このシリコーンゴムベー
スコンパウンド１００部に、２本ロール上で、２,５−
ジメチル−２,５−ジ（ｔ−ブチルパーオキシ）ヘキサ
ンの５０重量％シリコーンオイルペースト０.８部を添
加し、均一に混合してシリコーンゴム組成物を得た。こ
のシリコーンゴム組成物の機械的強度と電気特性を測定
して、それらの結果を表２に示した。
【００１９】
【比較例２】実施例２において、粘度３０センチポイズ
の両末端シラノール基封鎖ジメチルシロキサン・メチル
ビニルシロキサン共重合体オリゴマーを配合しなかった
以外は、実施例２と同様にしてシリコーンゴムベースコ
ンパウンドを調製した。このベースコンパウンドから実
施例２と同様にしてシリコーンゴム組成物を調製した。
このシリコーンゴム組成物の機械的強度と電気特性を実
施例２と同様にして測定した。それらの結果を表２に併
記した。表２の結果から本発明の組成物からなるシリコ
ーンゴムは、引張強さ，引裂強さが高く、優れた機械的
強度を有することが分かった。
の両末端シラノール基封鎖ジメチルシロキサン・メチル
ビニルシロキサン共重合体オリゴマーを配合しなかった
以外は、実施例２と同様にしてシリコーンゴムベースコ
ンパウンドを調製した。このベースコンパウンドから実
施例２と同様にしてシリコーンゴム組成物を調製した。
このシリコーンゴム組成物の機械的強度と電気特性を実
施例２と同様にして測定した。それらの結果を表２に併
記した。表２の結果から本発明の組成物からなるシリコ
ーンゴムは、引張強さ，引裂強さが高く、優れた機械的
強度を有することが分かった。
【表２】
【００２０】
【実施例３】比較例１で得られたシリコーンゴムベース
コンパウンド１００部に、２本ロール上で、ビニルトリ
メトキシシラン３部を添加し、均一に混練した後、１０
０℃／２４時間の熱処理を行なった後、冷却し、これに
２,５−ジメチル−２,５−ジ（ｔ−ブチルパーオキシ）
ヘキサン０.４部を添加配合してシリコーンゴム組成物
を調製した。このシリコーンゴム組成物の機械的強度と
電気特性を実施例１と同様にして測定して、それらの結
果を表３に示した。
コンパウンド１００部に、２本ロール上で、ビニルトリ
メトキシシラン３部を添加し、均一に混練した後、１０
０℃／２４時間の熱処理を行なった後、冷却し、これに
２,５−ジメチル−２,５−ジ（ｔ−ブチルパーオキシ）
ヘキサン０.４部を添加配合してシリコーンゴム組成物
を調製した。このシリコーンゴム組成物の機械的強度と
電気特性を実施例１と同様にして測定して、それらの結
果を表３に示した。
【表３】
【００２１】
【発明の効果】本発明のシリコーンゴム組成物は、(Ａ)
成分、(Ｂ)成分、(Ｃ)成分および(Ｄ)成分からなり、特
に(Ｂ)成分の水酸化アルミニウム粉末、(Ｃ)成分のアル
ケニル基およびアルコキシ基もしくは水酸基を有するシ
ランまたはシロキサンオリゴマーを含有しており、ま
た、(Ａ)成分、(Ｅ)成分および(Ｄ)成分からなり、特に
(Ｅ)成分のアルケニル基およびアルコキシ基もしくは水
酸基を有するシランまたはシロキサンオリゴマーにより
表面処理されてなる水酸化アルミニウム粉末を含有して
いるので、高い機械的強度と良好な電気特性を有すると
いう特徴を有する。
成分、(Ｂ)成分、(Ｃ)成分および(Ｄ)成分からなり、特
に(Ｂ)成分の水酸化アルミニウム粉末、(Ｃ)成分のアル
ケニル基およびアルコキシ基もしくは水酸基を有するシ
ランまたはシロキサンオリゴマーを含有しており、ま
た、(Ａ)成分、(Ｅ)成分および(Ｄ)成分からなり、特に
(Ｅ)成分のアルケニル基およびアルコキシ基もしくは水
酸基を有するシランまたはシロキサンオリゴマーにより
表面処理されてなる水酸化アルミニウム粉末を含有して
いるので、高い機械的強度と良好な電気特性を有すると
いう特徴を有する。
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｃ０８Ｋ 5/54 Ｃ０８Ｋ 5/54 9/06 9/06
Claims (2)
- 【請求項１】 (Ａ)平均組成式；ＲaＳｉＯ(4-a)/2（式中、Ｒは置換または 非置換の１価炭化水素基であり、ａは１.９５〜２.０５の数である。）で示され 、１分子中に少なくとも２個のケイ素原子結合アルケニル基を有するオルガノポ リシロキサン生ゴム １００重量部、 (Ｂ)水酸化アルミニウム粉末 １０〜３００重量部、 (Ｃ)アルケニル基およびアルコキシ基もしくは水酸基を有するシランまたはシロ キサンオリゴマー ０.１〜３０重量部、 および (Ｄ)有機過酸化物 ０.１〜１０重量部 からなるシリコーンゴム組成物。
- 【請求項２】 (Ａ)平均組成式；ＲaＳｉＯ(4-a)/2（式中、Ｒは置換または 非置換の１価炭化水素基であり、ａは１.９５〜２.０５の数である。）で示され 、１分子中に少なくとも２個のケイ素原子結合アルケニル基を有するオルガノポ リシロキサン生ゴム １００重量部、 (Ｅ)アルケニル基およびアルコキシ基もしくは水酸基を有するシランまたはシロ キサンオリゴマーにより表面処理されてなる水酸化アルミニウム粉末 １０〜３００重量部、 (Ｄ)有機過酸化物 ０.１〜１０重量部 からなるシリコーンゴム組成物。