JPH09241700A - Split leather and its production - Google Patents
Split leather and its productionInfo
- Publication number
- JPH09241700A JPH09241700A JP7824096A JP7824096A JPH09241700A JP H09241700 A JPH09241700 A JP H09241700A JP 7824096 A JP7824096 A JP 7824096A JP 7824096 A JP7824096 A JP 7824096A JP H09241700 A JPH09241700 A JP H09241700A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- leather
- split leather
- easily dyeable
- split
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本願発明は、天然皮革の銀面
を取り除いた天然床革上に、人工の銀面を形成した再生
皮革であるスプリットレザー及びその製造方法の改良に
関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a split leather, which is a regenerated leather having an artificial silver surface formed on a natural floor leather from which the silver surface of natural leather has been removed, and an improvement in a method for producing the split leather.
【０００２】[0002]
【従来の技術】従来、スプリットレザーの製造方法は、
天然床革にポリウレタンフィルムを離型紙転写する方法
が一般的に広く知られている。具体的には、例えば溶剤
系ポリウレタン樹脂を予めエンボス柄を付与した離型紙
にコーティングし乾燥したものを熱プレスや接着剤によ
りラミネートする方法である。ところが、この方法で
は、ポリウレタンフィルムが薄い場合は、折り曲げ等の
際に床革の傷等による模様が浮き上がり、一方、ポリウ
レタンフィルムを厚くすると、風合を損なう等の欠点が
あり、天然皮革や人工皮革の様な高級分野への利用は困
難である。一方、このような欠点を解消するものとし
て、人工皮革分野で多用されている発泡層を利用した方
法も知られている。この方法は、天然床革上に、６０〜
１００°Ｃ程度の温度の下で発泡させたポリウレタンエ
マルジョンを塗布し、乾燥後、更に６０〜１５０°Ｃ程
度の温度条件下で加圧成形する方法である。こうするこ
とにより、下地の床革の傷や凹凸等による模様の浮き上
がりを防止できる。しかしながら、発泡層を利用した方
法においては、発泡層を、エマルジョン系のものから構
成しているため、耐水性に問題があり、使用用途が限ら
れてしまう。又、６０〜１００°Ｃ程度の温度の下で発
泡させたポリウレタンエマルジョンを塗布し、乾燥後
に、更に６０〜１５０°Ｃ程度の温度にして加圧成形し
なければならず、製作が面倒であるという課題を有す
る。また、これら従来の方法により得られるスプリット
レザーに着色を施す場合、予め着色した表皮層を利用す
るか、表面にスプレー加工する方法が採られており、製
造されたスプリットレザーに再度着色を施すことは困難
である。そのため、多品種小ロットのものを製造する場
合には、効率が悪くなってしまうという課題がある。
又、予め着色した表皮層を利用した場合、得られたスプ
リットレザーを裁断すると裁断の切口には着色が施され
ていないため、体裁が悪くなってしまう。2. Description of the Related Art Conventionally, the manufacturing method of split leather is
A method of transferring a polyurethane film onto a natural floor leather by release paper is generally widely known. Specifically, for example, it is a method in which a solvent-based polyurethane resin is coated on a release paper having an embossed pattern in advance, dried, and laminated by hot pressing or an adhesive. However, in this method, when the polyurethane film is thin, the pattern due to scratches on the floor leather emerges when it is bent, and on the other hand, thickening the polyurethane film has drawbacks such as impairing the texture, and it is difficult to use natural leather or artificial leather. It is difficult to use in high-grade fields such as leather. On the other hand, as a method for solving such a drawback, a method using a foam layer which is widely used in the artificial leather field is also known. This method uses 60-
In this method, a polyurethane emulsion foamed at a temperature of about 100 ° C. is applied, dried, and then pressure-molded under a temperature condition of about 60 to 150 ° C. By doing so, it is possible to prevent the pattern from being lifted up due to scratches or unevenness of the underlying floor leather. However, in the method using the foam layer, since the foam layer is made of an emulsion type, there is a problem in water resistance, and its use is limited. Further, the polyurethane emulsion foamed at a temperature of about 60 to 100 ° C must be applied, dried and then pressure-molded at a temperature of about 60 to 150 ° C, which is troublesome to manufacture. Has the problem. When coloring the split leather obtained by these conventional methods, a pre-colored skin layer is used or a method of spray processing on the surface is adopted, and the manufactured split leather should be colored again. It is difficult. Therefore, there is a problem that efficiency is deteriorated when manufacturing a variety of small lots.
Further, when a pre-colored skin layer is used, when the obtained split leather is cut, the cut end is not colored, so that the appearance becomes poor.
【０００３】[0003]
【発明が解決しようとする課題】本願発明は、以上の実
情に鑑み提案されたもので、床革の傷等による模様の浮
き上がりがなく、しかも、耐水性の良いものであって、
天然皮革と同様の染色加工ができ、高級品の感を与える
ことのできるスプリットレザー及びその製造方法を提供
することを目的とする。DISCLOSURE OF THE INVENTION The present invention has been proposed in view of the above-mentioned circumstances, and is free from the rise of patterns due to scratches on floor leather and the like, and has good water resistance.
An object of the present invention is to provide a split leather which can be dyed in the same manner as natural leather and can give a feeling of high quality products, and a method for producing the split leather.
【０００４】[0004]
【課題を解決するための手段】本願発明は、以下の特徴
を有するスプリットレザーを提供することにより上記課
題を解決する。本願第１のスプリットレザーに係る発明
は、天然床革層１を備えたスプリットレザーにおいて、
スプリットレザーの表面層２が、易染性ポリウレタン樹
脂層からなるものであることを特徴とするものである。The present invention solves the above-mentioned problems by providing a split leather having the following features. The invention relating to the first split leather of the present application is a split leather provided with the natural floor leather layer 1,
The surface layer 2 of split leather is characterized by comprising an easily dyeable polyurethane resin layer.
【０００５】本願第２のスプリットレザーに係る発明
は、本願第１の発明に係るスプリットレザーの表面層２
と天然床革層１との間に有機溶剤系樹脂からなる発泡層
３が備えられたものであることを特徴とするものであ
る。The invention relating to the second split leather of the present application is the surface layer 2 of the split leather according to the first invention of the present application.
It is characterized in that a foam layer 3 made of an organic solvent-based resin is provided between and the natural floor leather layer 1.
【０００６】本願第３のスプリットレザーに係る発明
は、本願第１又は第２の発明に係るスプリットレザーの
表面層２の表面に、絞２ａが形成されたものであること
を特徴とするものである。The third split leather invention of the present application is characterized in that the diaphragm 2a is formed on the surface of the surface layer 2 of the split leather of the first or second invention. is there.
【０００７】又、本願発明は、以下の特徴を有するスプ
リットレザーの製造方法を提供することにより上記課題
を解決する。本願第１のスプリットレザーの製造方法に
係る発明は、まず、易染性ポリウレタン樹脂層を有する
樹脂層５を形成する。その後、この樹脂層５を天然床革
の上方側に接合することによって易染性ポリウレタン樹
脂層からなる表面層２を形成したものとする。そして、
その後、染色によって着色することを特徴とする製造方
法である。Further, the present invention solves the above problems by providing a method for manufacturing split leather having the following features. In the invention relating to the first split leather manufacturing method of the present application, first, the resin layer 5 having the easily dyeable polyurethane resin layer is formed. After that, the resin layer 5 is bonded to the upper side of the natural floor leather to form the surface layer 2 made of the easily dyeable polyurethane resin layer. And
Then, the manufacturing method is characterized by coloring by dyeing.
【０００８】本願第２のスプリットレザーの製造方法に
係る発明は、易染性ポリウレタン樹脂層を有する樹脂層
５を形成する。その後、この樹脂層５を天然床革の上方
側に接合することによって易染性ポリウレタン樹脂層か
らなる表面層２を形成したものとする。そして、その
後、それを裁断、打ち抜き、縫製等の加工手段によって
所定形状に形成し、次に、染色によって着色することを
特徴とする製造方法である。In the invention relating to the second split leather manufacturing method of the present application, the resin layer 5 having the easily dyeable polyurethane resin layer is formed. After that, the resin layer 5 is bonded to the upper side of the natural floor leather to form the surface layer 2 made of the easily dyeable polyurethane resin layer. Then, after that, it is formed into a predetermined shape by a processing means such as cutting, punching, or sewing, and then colored by dyeing.
【０００９】以上のように構成した本願第１のスプリッ
トレザーに係る発明においては、スプリットレザーの表
面層２を、易染性ポリウレタン樹脂層からなるものとす
るため、表面層２を染色によって着色することが可能と
なる。これにより、天然皮革と同様の染色による着色を
施すことができ、高級品の感を与えることができるもの
となる。In the invention according to the first split leather of the present invention configured as described above, since the surface layer 2 of the split leather is made of the easily dyeable polyurethane resin layer, the surface layer 2 is colored by dyeing. It becomes possible. As a result, the same coloring as natural leather can be applied, and a high-quality product can be provided.
【００１０】本願第２のスプリットレザーに係る発明に
おいては、表面層２と天然床革層１との間に有機溶剤系
樹脂からなる発泡層３を備えたものとするため、下地の
床革の傷や凹凸等による模様の浮き上がりを防止でき
る。又、発泡層３を有機溶剤系樹脂から構成することに
より、耐水性の良好なものにできる。In the invention of the second split leather of the present application, since the foam layer 3 made of an organic solvent resin is provided between the surface layer 2 and the natural floor leather layer 1, the floor leather of the base is It is possible to prevent the pattern from rising due to scratches or irregularities. In addition, by forming the foam layer 3 from an organic solvent-based resin, it is possible to obtain a good water resistance.
【００１１】本願第３のスプリットレザーに係る発明に
おいては、表面層２の表面に、絞４ａを形成したもので
あるため、自由に各種の革の風合いを出すことが出来、
より一層、高級感のある優れたものにできる。In the invention relating to the third split leather of the present application, since the diaphragm 4a is formed on the surface of the surface layer 2, various kinds of leather texture can be freely obtained.
It can be made even more luxurious and excellent.
【００１２】又、本願第１のスプリットレザーの製造方
法に係る発明においては、天然床革の上方側に易染性ポ
リウレタン樹脂層からなる表面層２を形成した後に、天
然皮革と同様の要領で染色によって着色するため、多品
種小ロットのものを製造する場合にも、ロット毎に染色
すれば良く、効率良く行うことができる。又、天然皮革
と同様の染色加工ができ、高級品の感を与えることので
きる製品を得ることができる。In the invention relating to the first split leather manufacturing method of the present application, after the surface layer 2 made of the easily dyeable polyurethane resin layer is formed on the upper side of the natural floor leather, it is processed in the same manner as the natural leather. Since coloring is performed by dyeing, even when manufacturing a large variety of small lots, it is sufficient to dye each lot, which can be efficiently performed. Further, it is possible to obtain a product which can be dyed in the same manner as natural leather and give a feeling of high quality.
【００１３】本願第２のスプリットレザーの製造方法に
係る発明においては、天然床革の上方に易染性ポリウレ
タン樹脂層からなる表面層２を形成し、それを裁断、打
ち抜き、縫製等の加工手段によって所定形状に形成した
後に、染色によって着色するため、切口等も表面と同色
に仕上げることができ、より一層高級品の感を与えるこ
とのできる製品を得ることができる。In the invention relating to the second split leather manufacturing method of the present application, the surface layer 2 made of the easily dyeable polyurethane resin layer is formed above the natural floor leather, and the processing means such as cutting, punching or sewing is performed. Since the product is formed into a predetermined shape and then colored by dyeing, the cut end and the like can be finished in the same color as the surface, and it is possible to obtain a product that can give a feeling of higher quality.
【００１４】[0014]
【発明の実施の形態】以下、図を基に本願発明の一実施
形態を具体的に説明する。図１は、本願発明の一実施形
態のスプリットレザーを断面にした説明図である。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS One embodiment of the present invention will be specifically described below with reference to the drawings. FIG. 1 is an explanatory view in which a split leather according to an embodiment of the present invention is shown in cross section.
【００１５】本願発明のスプリットレザーは、下層をな
す天然床革層１と、上層をなす樹脂層５と、これらの間
に配設された接着剤層４とを備えている。The split leather of the present invention comprises a natural floor leather layer 1 which is a lower layer, a resin layer 5 which is an upper layer, and an adhesive layer 4 which is arranged between them.
【００１６】天然床革層１は、天然皮革の銀面を取り除
いて得られる天然床革から構成されている。The natural floor leather layer 1 is composed of natural floor leather obtained by removing the silver surface of natural leather.
【００１７】樹脂層５は、易染性表皮層２と、易染性表
皮層２の下方側に配設された発泡層３とを備えている。The resin layer 5 comprises an easily dyeable skin layer 2 and a foam layer 3 disposed below the easily dyeable skin layer 2.
【００１８】易染性表皮層２は、スプリットレザー全体
の表面層２をなすもので、染色可能な易染性ポリウレタ
ン樹脂層から構成される。易染性ポリウレタン樹脂とし
ては、トーヨーポリマー社のペタルシリーズや、セーコ
ー化成社のラックスキンの易染性シリーズ、大日本印刷
社のクリスボンの易染性シリーズ等が例示できる。又、
易染性表皮層２の表面には、複数の絞２ａ…２ａが備え
られ、絞２ａ…２ａによって表面に模様が形成されてい
る。The easily dyeable skin layer 2 constitutes the surface layer 2 of the entire split leather and is composed of a dyeable easily dyeable polyurethane resin layer. Examples of the easily dyeable polyurethane resin include the Petal series of Toyo Polymer Co., Ltd., the easy dyeing series of Lax Skin by Seiko Kasei, and the easy dyeing series of Chris Bonn by Dai Nippon Printing Co., Ltd. or,
2a are provided on the surface of the easily dyeable skin layer 2, and a pattern is formed on the surface by the diaphragms 2a.
【００１９】発泡層３は、天然床革の傷等による模様の
浮き上がりを防止するとともに、天然床革を保護する等
の役目をなすもので、有機溶剤系樹脂を発泡させたもの
から構成されている。この発泡層３は、発泡性の有機溶
剤系樹脂を塗布した後、乾燥工程にて熱エネルギーを加
えることにより、当該有機溶剤系樹脂の硬化反応中に発
生するガスによって発泡が現出することによって、得ら
れるものである。発泡性樹脂として有機溶剤系のものを
使用しているのは、耐水性の良いものとし、用途範囲の
拡大を図ることができるようにするためである。この発
泡性の有機溶剤系樹脂としては、トーヨーポリマー社の
エーゲシリーズ等が例示できる。また、有機溶剤系樹脂
に別途の発泡剤を配合してもよく、これらの発泡性の有
機溶剤系樹脂や発泡剤は、スプリットレザーの用途、品
質、特性等に応じて、適宜変更して実施し得る。The foam layer 3 has a function of preventing the pattern from rising due to scratches on the natural floor leather and protecting the natural floor leather, and is made of a foamed organic solvent resin. There is. The foaming layer 3 is formed by applying a foaming organic solvent-based resin and then applying heat energy in a drying step, whereby foaming appears due to a gas generated during a curing reaction of the organic solvent-based resin. Is what you get. The reason why the organic solvent-based resin is used as the foaming resin is that it has good water resistance and can be used in a wide range of applications. Examples of the foamable organic solvent-based resin include Aye series manufactured by Toyo Polymer Co., Ltd. Further, a separate foaming agent may be added to the organic solvent-based resin, and these foamable organic solvent-based resin and foaming agent may be appropriately modified depending on the application, quality, characteristics, etc. of split leather. You can
【００２０】接着剤層４は、天然床革層１と、樹脂層５
における発泡層３とを接着させるためのものであり、こ
の接着剤層４を構成する接着剤としては、ポリウレタン
樹脂等の従来から知られている種々のものが使用でき
る。又、この接着剤層４を接着させるには、ウエットラ
ミ、ドライラミ、熱プレス等の方法によって行うことが
できる。The adhesive layer 4 comprises a natural floor leather layer 1 and a resin layer 5.
In order to adhere the foam layer 3 to the foam layer 3, various known adhesives such as polyurethane resin can be used as the adhesive constituting the adhesive layer 4. Further, the adhesive layer 4 can be adhered by a method such as wet laminating, dry laminating, or hot pressing.
【００２１】次に、このスプリットレザーの製造方法を
具体的に説明する。まず、図２に示すように、下面に突
起６ａ…６ａを有する離型紙６に、無色透明な液状の易
染性ポリウレタン樹脂をコーティングし乾燥することに
より、易染性表皮層２を形成する。その後、易染性表皮
層２の下面に、液状の有機溶剤系樹脂を塗布する。そし
て、この有機溶剤系発泡性樹脂を乾燥するが、その乾燥
を、有機溶剤系樹脂が発泡し得る温度で行う。こうする
ことにより、有機溶剤系樹脂を乾燥させながら、同時に
発泡させることができ、従来のエマルジョン系の発泡を
形成する場合のような特殊な装置を必要とせず、容易に
短時間で発泡層３を形成できる。これにより、易染性表
皮層２と発泡層３とで構成した樹脂層５を形成できる。Next, the method for manufacturing this split leather will be described in detail. First, as shown in FIG. 2, the release paper 6 having the projections 6a ... 6a on the lower surface is coated with a colorless and transparent liquid easily dyeable polyurethane resin and dried to form the easily dyeable skin layer 2. Then, a liquid organic solvent-based resin is applied to the lower surface of the easily dyeable skin layer 2. Then, the organic solvent-based foamable resin is dried, but the drying is performed at a temperature at which the organic solvent-based resin can foam. By doing so, the organic solvent-based resin can be simultaneously foamed while being dried, and a special device as in the case of forming a conventional emulsion-based foam is not required, and the foamed layer 3 can be easily and quickly formed. Can be formed. Thereby, the resin layer 5 composed of the easily dyeable skin layer 2 and the foam layer 3 can be formed.
【００２２】その後、形成された発泡層３の下面に、接
着剤を塗布し、接着剤層４を形成する。これにより、接
着剤層４を有する樹脂層５が形成される。本実施形態で
は、この接着剤層４の形成までが、一連の工程でなされ
る。次工程の樹脂層５と天然床革層１との接着工程は、
接着剤層４の形成後、連続して行ってもよいが、別工程
で、日時をおいて行ってもよい。After that, an adhesive is applied to the lower surface of the formed foam layer 3 to form the adhesive layer 4. Thereby, the resin layer 5 having the adhesive layer 4 is formed. In this embodiment, the formation of the adhesive layer 4 is performed in a series of steps. The next step is to bond the resin layer 5 and the natural floor leather layer 1 to each other.
After the adhesive layer 4 is formed, it may be continuously performed, or may be performed in a separate step at a certain date and time.
【００２３】次に、接着剤層４を有する樹脂層５を、接
着剤層４を介して天然床革の上面に接着させる。そし
て、離型紙６を剥がせば、図１に示すように突起６ａ…
６ａによって表面に絞２ａの形成された易染性表皮層２
からなる表面層を備えたスプリットレザー材が得られ
る。この状態でのスプリットレザー材の易染性表皮層２
は、無色透明を呈している。Next, the resin layer 5 having the adhesive layer 4 is adhered to the upper surface of the natural floor leather via the adhesive layer 4. Then, if the release paper 6 is peeled off, as shown in FIG.
The easily dyeable skin layer 2 having a diaphragm 2a formed on its surface by 6a.
A split leather material with a surface layer consisting of is obtained. Easy-to-dye skin layer 2 of split leather material in this state
Is colorless and transparent.
【００２４】そして、易染性表皮層２を適宜な色に着色
する場合は、染色することにより行う。本願発明では、
易染性表皮層２を染色可能な易染性ポリウレタン樹脂か
ら構成しているため、天然皮革と同様の染色をすること
ができる。又、この染色は、種々の形状の状態で行うこ
とができ、例えばスプリットレザー材を長尺状に形成し
た原反の状態で染色することはもちろん、得られたスプ
リットレザー材を所定形状に打ち抜き、裁断し、或いは
裁断したものを縫製又は接合させて最終製品の形状にし
た状態で行うことができる。打ち抜いたものや裁断した
後に染色することにより、表面とともに、切口をも同色
に仕上げることができ、より一層、高級感を与える製品
を得ることができる。When the easily dyeable skin layer 2 is colored in an appropriate color, it is dyed. In the present invention,
Since the easily dyeable skin layer 2 is made of an easily dyeable polyurethane resin that can be dyed, it can be dyed in the same manner as natural leather. Further, this dyeing can be carried out in various shapes, for example, not only dyeing a raw material in which a split leather material is formed into a long shape but also punching the obtained split leather material into a predetermined shape. It can be performed in the state of being cut, or the cut product is sewn or joined to form the final product. By punching or cutting and then dyeing, it is possible to finish not only the surface but also the cut end in the same color, and it is possible to obtain a product that gives an even higher sense of quality.
【００２５】上記の易染性表皮層２は、自由な色に染色
によって着色することができるが、淡色に着色する場
合、天然革床の色に影響され、綺麗な色が表現されない
おそれがある。そのため、例えば図３に示すように、易
染性表皮層２の下方に、より具体的には易染性表皮層２
と発泡層３との間に、着色樹脂層７を形成しておくこと
も望ましい。着色樹脂層７は、白色等の有色のポリウレ
タン樹脂等、淡色の樹脂層としておくことが、色の影響
を排除する点で好ましい。但し、スプリットレザーを濃
色（茶や黒）で染色することが明らかな場合等では、着
色樹脂層７として濃色（茶や黒）のものを用いてもよ
い。尚、本実施形態では、易染性表皮層２を染色によっ
て着色できるようにしているが、着色せずに使用するこ
とも可能である。また、上記の実施の形態に係る樹脂層
は、その一つの層として発泡層３を用いているが、これ
を用いずに易染性表皮層２のみで、或いは易染性表皮層
２と着色樹脂層７とで樹脂層を構成することもできる。The above-mentioned easily dyeable skin layer 2 can be colored in any color by dyeing. However, when it is colored in a light color, it may be affected by the color of the natural leather floor and a beautiful color may not be expressed. . Therefore, for example, as shown in FIG. 3, below the easily dyeable skin layer 2, more specifically, the easily dyeable skin layer 2 is used.
It is also desirable to form the colored resin layer 7 between the foam layer 3 and the foam layer 3. The colored resin layer 7 is preferably a light-colored resin layer such as a colored polyurethane resin such as white in order to eliminate the influence of color. However, when it is clear that the split leather is dyed in a dark color (brown or black), the colored resin layer 7 may be a dark color (brown or black). In the present embodiment, the easily dyeable skin layer 2 is colored by dyeing, but it can be used without being colored. Further, the resin layer according to the above-mentioned embodiment uses the foam layer 3 as one of the layers, but without using it, only the easily dyeable skin layer 2 or the easily dyeable skin layer 2 and the colored layer. It is also possible to form a resin layer with the resin layer 7.
【００２６】[0026]
【発明の効果】以上、本願発明の本願第１のスプリット
レザーに係る発明は、表面層を染色によって着色するこ
とが可能となる。これにより、天然皮革と同様の染色加
工ができ、高級品の感を与えることができる。As described above, according to the first split leather invention of the present invention, the surface layer can be colored by dyeing. As a result, the same dyeing process as that of natural leather can be performed, and a feeling of a high-grade product can be given.
【００２７】本願第２のスプリットレザーに係る発明
は、本願第１の発明の効果に加え、下地の床革の傷や凹
凸等による模様の浮き上がりを防止できる。又、発泡層
を有機溶剤系樹脂から構成することにより、耐水性の良
好なものにでき、用途的使用範囲を拡大できる。In addition to the effects of the first invention of the present application, the invention of the second split leather of the present application can prevent the pattern from being lifted up due to scratches or irregularities of the underlying floor leather. Further, by forming the foamed layer from an organic solvent-based resin, it is possible to obtain good water resistance, and it is possible to expand the range of use for purposes.
【００２８】本願第３のスプリットレザーに係る発明
は、本願第１の発明の効果に加え、表面層の表面に、絞
を形成したものするため、より一層、高級感のある優れ
たものにできる。In addition to the effect of the first invention of the present application, the invention of the third split leather of the present application has a diaphragm formed on the surface of the surface layer, so that it can be made even more luxurious and excellent. .
【００２９】又、本願第１のスプリットレザーの製造方
法に係る発明は、多品種小ロットのものを製造する場合
にも、ロット毎に染色すれば良く、効率良く行うことが
できる。しかも、天然皮革と同様の染色加工ができ、高
級品の感を与えることのできる製品を得ることができ
る。Further, the invention relating to the first split leather manufacturing method of the present invention can be efficiently carried out even when manufacturing a large variety of small lots by dyeing each lot. Moreover, a dyeing process similar to that of natural leather can be performed, and a product that can give a feeling of high-quality goods can be obtained.
【００３０】本願第２のスプリットレザーの製造方法に
係る発明は、本願第１のスプリットレザーの製造方法に
係る発明の効果に加え、天然床革の上方に易染性ポリウ
レタン樹脂層からなる表面層を形成し、それを裁断、打
ち抜き、縫製等の加工手段によって所定形状に形成した
後に、染色によって着色するため、切口等も表面と同色
に仕上げることができ、より一層高級品の感を与えるこ
とのできる製品を得ることができる。In addition to the effects of the invention relating to the method for producing split leather of the first aspect of the present invention, the invention relating to the method of producing split leather of the second aspect of the present invention has a surface layer consisting of an easily dyeable polyurethane resin layer above natural floor leather. After forming a shape and forming it into a predetermined shape by processing means such as cutting, punching, sewing, etc., it is colored by dyeing, so that the cut edge can be finished in the same color as the surface, giving a feeling of higher quality We can obtain products that can
【図１】本願発明のスプリットレザーの一実施形態の断
面説明図である。FIG. 1 is a cross-sectional explanatory view of an embodiment of a split leather of the present invention.
【図２】スプリットレザーの製造に際し、発泡層に接着
剤層を形成した状態の断面説明図である。FIG. 2 is a cross-sectional explanatory view showing a state in which an adhesive layer is formed on a foam layer during the production of split leather.
【図３】スプリットレザーの他の実施形態の断面説明図
である。FIG. 3 is a cross-sectional explanatory view of another embodiment of split leather.
１ 天然床革層 ２ 易染性表皮層 ２ａ 絞 ３ 発泡層 ４ 接着剤層 ５ 樹脂層 1 Natural Floor Leather Layer 2 Easy Dyeing Skin Layer 2a Squeezing 3 Foaming Layer 4 Adhesive Layer 5 Resin Layer
Claims (5)
において、このスプリットレザーの表面層(2) が、易染
性ポリウレタン樹脂層からなるものであることを特徴と
するスプリットレザー。1. A split leather provided with a natural floor leather layer (1), characterized in that the surface layer (2) of the split leather comprises an easily dyeable polyurethane resin layer.
溶剤系樹脂からなる発泡層(3) が備えられたものである
ことを特徴とする請求項１記載のスプリットレザー。2. The foam layer (3) made of an organic solvent resin is provided between the surface layer (2) and the natural floor leather layer (1), according to claim 1. Split leather.
ものであることを特徴とする請求項１又は２記載スプリ
ットレザー。3. The split leather according to claim 1, wherein the surface layer (2) has a diaphragm (2a) formed on the surface thereof.
(5) を形成した後、この樹脂層(5) を天然床革の上方側
に接合することによって易染性ポリウレタン樹脂層から
なる表面層(2) を形成し、その後、染色によって着色す
ることを特徴とするスプリットレザーの製造方法。4. A resin layer having an easily dyeable polyurethane resin layer
After forming (5), the resin layer (5) is joined to the upper side of the natural floor leather to form a surface layer (2) consisting of an easily dyeable polyurethane resin layer, and then colored by dyeing. A method for manufacturing split leather, characterized by:
(5) を形成した後、この樹脂層(5) を天然床革の上方側
に接合することによって易染性ポリウレタン樹脂層から
なる表面層(2) を形成し、その後、これを裁断、打ち抜
き、縫製等の加工手段によって所定形状に形成し、次
に、染色によって着色することを特徴とするスプリット
レザーの製造方法。5. A resin layer having an easily dyeable polyurethane resin layer
After forming (5), the resin layer (5) is joined to the upper side of the natural floor leather to form the surface layer (2) consisting of the easily dyeable polyurethane resin layer, which is then cut and punched. A method for producing split leather, which is characterized in that the split leather is formed into a predetermined shape by a processing means such as sewing and then colored by dyeing.