JPH09286077A - プラスチックフイルム - Google Patents
プラスチックフイルムInfo
- Publication number
- JPH09286077A JPH09286077A JP8102103A JP10210396A JPH09286077A JP H09286077 A JPH09286077 A JP H09286077A JP 8102103 A JP8102103 A JP 8102103A JP 10210396 A JP10210396 A JP 10210396A JP H09286077 A JPH09286077 A JP H09286077A
- Authority
- JP
- Japan
- Prior art keywords
- film
- moisture permeability
- plastic film
- water
- pebax
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】
【目的】 本発明は、適度の透湿性と低い水滴付着性を
有するプラスチックフイルムを提供することにある。 【構成】 ＪＩＳＺ０２０８に規定する透湿度が１００
０ｇ／ｍ２／２４ｈ未満であるプラスチックフイルムに
おいて、透湿度が１０００ｇ／ｍ２／２４ｈ以上である
フイルムと積層されていることを特徴とするプラスチッ
クフイルム。
有するプラスチックフイルムを提供することにある。 【構成】 ＪＩＳＺ０２０８に規定する透湿度が１００
０ｇ／ｍ２／２４ｈ未満であるプラスチックフイルムに
おいて、透湿度が１０００ｇ／ｍ２／２４ｈ以上である
フイルムと積層されていることを特徴とするプラスチッ
クフイルム。
Description
【０００１】
【産業上の利用分野】本発明はプラスチックフイルムに
関する。その目的とするところは、低温高湿度下に置か
れても水滴付着による曇りの少ないフイルムを提供する
ことにある。
関する。その目的とするところは、低温高湿度下に置か
れても水滴付着による曇りの少ないフイルムを提供する
ことにある。
【０００２】
【従来の技術】従来より種々の機能を持ったフイルムは
広く知られている。特に食品や花等の植物包装分野にお
いては保存と外観の点から適度の透湿性や透明性が要求
されている。透湿性が高すぎると乾燥してしまい、逆に
透湿性が低すぎると中に水分がたまり、内容物がこれと
接触すると腐ったり傷んだりする。更に冷蔵庫中等低温
で保管されると水分が凝集して水滴となってフイルム上
に付着し、内容物を見にくくしたり、傷みの原因とな
る。このうち水滴付着防止に対してはフイルム表面に親
水性物質、例えば脂肪酸エステルや酸化エチレン付加物
等を塗布したり練り込んだり、逆に水滴ができてもはじ
けるように撥水性を高める処理がなされたりしている。
広く知られている。特に食品や花等の植物包装分野にお
いては保存と外観の点から適度の透湿性や透明性が要求
されている。透湿性が高すぎると乾燥してしまい、逆に
透湿性が低すぎると中に水分がたまり、内容物がこれと
接触すると腐ったり傷んだりする。更に冷蔵庫中等低温
で保管されると水分が凝集して水滴となってフイルム上
に付着し、内容物を見にくくしたり、傷みの原因とな
る。このうち水滴付着防止に対してはフイルム表面に親
水性物質、例えば脂肪酸エステルや酸化エチレン付加物
等を塗布したり練り込んだり、逆に水滴ができてもはじ
けるように撥水性を高める処理がなされたりしている。
【０００３】
【発明が解決しようとする課題】しかしこれらは表面が
べたついたり練り込んだ物が滲み出したりして製品とし
て不都合があったり、塗布後乾操工程を必要としてコス
トがかかる等の問題があった。本発明は塗布や乾燥を必
要とせず、押出のみによって得られる防曇性フイルムを
提供するものである。
べたついたり練り込んだ物が滲み出したりして製品とし
て不都合があったり、塗布後乾操工程を必要としてコス
トがかかる等の問題があった。本発明は塗布や乾燥を必
要とせず、押出のみによって得られる防曇性フイルムを
提供するものである。
【０００４】
【課題を解決するための手段】本発明はＪＩＳＺ０２０
８に規定する透湿度が１０００ｇ／ｍ２／２４ｈ未満で
あるプラスチックフイルムにおいて、透湿度が１０００
ｇ／ｍ２／２４ｈ以上であるフイルムと積層されている
ことを特徴とするプラスチックフイルムであり、またフ
イルムの素材がポリエーテルポリアミドブロック共重合
体、熱可塑性ポリエステルエラストマー、熱可塑性ポリ
ウレタンの群から選ばれた少なくとも一種であることを
特徴とする前記プラスチックフイルムである。
８に規定する透湿度が１０００ｇ／ｍ２／２４ｈ未満で
あるプラスチックフイルムにおいて、透湿度が１０００
ｇ／ｍ２／２４ｈ以上であるフイルムと積層されている
ことを特徴とするプラスチックフイルムであり、またフ
イルムの素材がポリエーテルポリアミドブロック共重合
体、熱可塑性ポリエステルエラストマー、熱可塑性ポリ
ウレタンの群から選ばれた少なくとも一種であることを
特徴とする前記プラスチックフイルムである。
【０００５】本発明において「透湿度」とは、ＪＩＳＺ
０２０８に規定された方法により、条件Ｂ（４０℃、９
０％関係湿度）に於いて測定した値である。
０２０８に規定された方法により、条件Ｂ（４０℃、９
０％関係湿度）に於いて測定した値である。
【０００６】本発明において「プラスチックフイルム」
は、透湿度が１０００ｇ／ｍ２／２４ｈ未満のものをそ
の対象とする。１０００ｇ／ｍ２／２４ｈ以上のものに
あっては、水滴付着が少なく、本発明による必要がな
い。好ましくは１０〜９００、更に好ましくは５０〜８
００ｇ／ｍ２／２４ｈである。
は、透湿度が１０００ｇ／ｍ２／２４ｈ未満のものをそ
の対象とする。１０００ｇ／ｍ２／２４ｈ以上のものに
あっては、水滴付着が少なく、本発明による必要がな
い。好ましくは１０〜９００、更に好ましくは５０〜８
００ｇ／ｍ２／２４ｈである。
【０００７】本発明のプラスチックフイルムは透湿度が
１０００ｇ／ｍ２／２４ｈ以上のフイルムと積層されて
いる。積層方法は、両成分を同時に押し出す共押出法、
一方をまずフイルム状に押し出し、その上に他方の樹脂
を押し出すいわゆる押し出しラミネーション法、両フイ
ルムを熱圧着する方法等、従来公知の方法が用いられ
る。
１０００ｇ／ｍ２／２４ｈ以上のフイルムと積層されて
いる。積層方法は、両成分を同時に押し出す共押出法、
一方をまずフイルム状に押し出し、その上に他方の樹脂
を押し出すいわゆる押し出しラミネーション法、両フイ
ルムを熱圧着する方法等、従来公知の方法が用いられ
る。
【０００８】本発明のフイルムを構成する樹脂は、前記
性能を有するものであるならば何でも良いが、透湿度の
点からポリエーテルポリアミドブロック共重合、熱可塑
性ポリエステルエラストマー、熱可塑性ポリウレタンの
群から選ばれた少なくとも一種であることが好ましい。
性能を有するものであるならば何でも良いが、透湿度の
点からポリエーテルポリアミドブロック共重合、熱可塑
性ポリエステルエラストマー、熱可塑性ポリウレタンの
群から選ばれた少なくとも一種であることが好ましい。
【０００９】本発明に於いて「ポリエーテルポリアミド
ブロック共重合体（以下ＰＥＢＡと略記することがあ
る）」とは、ポリ（オキシアルキレン）鎖（ａ）と、炭
素数６以上のアミノカルボン酸又はラクタムもしくは炭
素数６以上のジアミンとジカルボン酸との塩の重合体で
あるポリアミド鎖（ｂ）とが連結したものである。
（ａ）と（ｂ）とが炭素数４〜２０のジカルボン酸
（ｃ）を介して交互に連結されたものは、一般にポリエ
−テルエステルアミドと呼ばれる。本ポリマーは、例え
ば特公昭５６−４５４１９号公報等の方法によって製造
される。具体的には、ペバックス（エルフアトケム
社）、ＥＬＹ（エムス社）、ベスタミド（ヒュルス社）
等が例示される。本発明において用いられるＰＥＢＡの
ポリアミド成分及びポリエ−テル成分の種類と含有量比
率は、目的と用途によって選ばれる。
ブロック共重合体（以下ＰＥＢＡと略記することがあ
る）」とは、ポリ（オキシアルキレン）鎖（ａ）と、炭
素数６以上のアミノカルボン酸又はラクタムもしくは炭
素数６以上のジアミンとジカルボン酸との塩の重合体で
あるポリアミド鎖（ｂ）とが連結したものである。
（ａ）と（ｂ）とが炭素数４〜２０のジカルボン酸
（ｃ）を介して交互に連結されたものは、一般にポリエ
−テルエステルアミドと呼ばれる。本ポリマーは、例え
ば特公昭５６−４５４１９号公報等の方法によって製造
される。具体的には、ペバックス（エルフアトケム
社）、ＥＬＹ（エムス社）、ベスタミド（ヒュルス社）
等が例示される。本発明において用いられるＰＥＢＡの
ポリアミド成分及びポリエ−テル成分の種類と含有量比
率は、目的と用途によって選ばれる。
【００１０】本発明に於いて「熱可塑性ポリエステルエ
ラストマー（以下ＴＰＥＥと略記することがある）」と
は、ポリ（オキシアルキレン）鎖（ａ）或いは脂肪族ポ
リエステル鎖（ａ’）と、炭素数６以上のオキシカルボ
ン酸又は炭素数２以上のジヒドロキシ化合物と芳香族ジ
カルボン酸との重合体であるポリエステル鎖（ｃ）とが
連結したものである。又これら前記（ｃ）成分は、２種
以上を併用してもよい。本ポリマーは例えばＵＳＰ４７
３９０１２明細書等に詳述されている。具体的にはハイ
トレル（デユポン社）、ペルプレン（東洋紡）、レクセ
（帝人）等が例示される。本発明において用いられるＴ
ＰＥＥの前記（ａ）及び／又は（ａ’）成分と（ｂ）成
分との重量比率は、目的と用途によって決められる。
ラストマー（以下ＴＰＥＥと略記することがある）」と
は、ポリ（オキシアルキレン）鎖（ａ）或いは脂肪族ポ
リエステル鎖（ａ’）と、炭素数６以上のオキシカルボ
ン酸又は炭素数２以上のジヒドロキシ化合物と芳香族ジ
カルボン酸との重合体であるポリエステル鎖（ｃ）とが
連結したものである。又これら前記（ｃ）成分は、２種
以上を併用してもよい。本ポリマーは例えばＵＳＰ４７
３９０１２明細書等に詳述されている。具体的にはハイ
トレル（デユポン社）、ペルプレン（東洋紡）、レクセ
（帝人）等が例示される。本発明において用いられるＴ
ＰＥＥの前記（ａ）及び／又は（ａ’）成分と（ｂ）成
分との重量比率は、目的と用途によって決められる。
【００１１】本発明に於いて「熱可塑性ポリウレタン
（以下ＴＰＵと略記することがある）」としては、ポリ
エーテルウレタン、ポリエステルウレタン（アジペ−ト
型、カプロラクトン型）が例示される。具体的には、通
常、有機ジイソシアネートと分子量５００〜６０００の
ポリエーテル及び／又はポリエステルジオールとの反応
によって得られる、場合により触媒の存在下で連鎖を伸
長させたポリウレタンである。イソシアネートとして
は、トルイレンジイソシアネート、ジフェニルメタンジ
イソシアネート等、ポリエーテルとしてはポリオキシテ
トラメチレン、ポリオキシプロピレン等、ポリエステル
としてはブチレンアジペート、カプロラクトン等が好ま
しく用いられる。
（以下ＴＰＵと略記することがある）」としては、ポリ
エーテルウレタン、ポリエステルウレタン（アジペ−ト
型、カプロラクトン型）が例示される。具体的には、通
常、有機ジイソシアネートと分子量５００〜６０００の
ポリエーテル及び／又はポリエステルジオールとの反応
によって得られる、場合により触媒の存在下で連鎖を伸
長させたポリウレタンである。イソシアネートとして
は、トルイレンジイソシアネート、ジフェニルメタンジ
イソシアネート等、ポリエーテルとしてはポリオキシテ
トラメチレン、ポリオキシプロピレン等、ポリエステル
としてはブチレンアジペート、カプロラクトン等が好ま
しく用いられる。
【００１２】本発明に於いてこれらＰＥＢＡ、ＴＰＥ
Ｅ、ＴＰＵは単独でも、これらの混合体でも、またブロ
ック共重合体にあってはそれぞれの樹脂のソフトセグメ
ント／ハードセグメント比の違う２種以上のポリマーの
混合体でもよく、更には他の樹脂とのブレンド体であっ
ても、透湿度が上記範囲内であればよい。
Ｅ、ＴＰＵは単独でも、これらの混合体でも、またブロ
ック共重合体にあってはそれぞれの樹脂のソフトセグメ
ント／ハードセグメント比の違う２種以上のポリマーの
混合体でもよく、更には他の樹脂とのブレンド体であっ
ても、透湿度が上記範囲内であればよい。
【００１３】本発明のプラスチックフイルムには、従来
公知の酸化防止剤、熱分解防止剤、紫外線吸収剤、耐加
水分解改良剤、着色剤（染料、顔料）、帯電防止剤、導
電剤、結晶核剤、結晶促進剤、可塑剤、易滑剤、潤滑
剤、離型剤、難燃剤、難燃助剤等を本発明のフイルム特
性を損なわない範囲で任意に含有せしめることが出来
る。
公知の酸化防止剤、熱分解防止剤、紫外線吸収剤、耐加
水分解改良剤、着色剤（染料、顔料）、帯電防止剤、導
電剤、結晶核剤、結晶促進剤、可塑剤、易滑剤、潤滑
剤、離型剤、難燃剤、難燃助剤等を本発明のフイルム特
性を損なわない範囲で任意に含有せしめることが出来
る。
【００１４】
【作用】本発明のプラスチックフイルムは透湿度に優
れ、且つ水滴付着が少なくて、特に食品、花等植物の保
存用フイルムとして有用である。
れ、且つ水滴付着が少なくて、特に食品、花等植物の保
存用フイルムとして有用である。
【００１５】
【実施例】以下、実施例によって本発明を具体的に説明
するが、本発明はこれだけに限定されるものでないこと
は言うまでもない。各種の特性は、以下の方法によって
測定、評価したものである。 （１）透湿度 ＪＩＳＺ０２０８に基づき、条件Ｂ（４０℃、９０％関
係湿度）で測定した。 （２）水滴付着テスト １００ｍｌビーカーに４０℃の水を８０ｍｌ入れ、ビー
カー口部をフイルムでカバーし、５℃冷蔵庫中に入れ
た。４時間後に取り出し、フイルムへの水滴付着状況を
観察した。
するが、本発明はこれだけに限定されるものでないこと
は言うまでもない。各種の特性は、以下の方法によって
測定、評価したものである。 （１）透湿度 ＪＩＳＺ０２０８に基づき、条件Ｂ（４０℃、９０％関
係湿度）で測定した。 （２）水滴付着テスト １００ｍｌビーカーに４０℃の水を８０ｍｌ入れ、ビー
カー口部をフイルムでカバーし、５℃冷蔵庫中に入れ
た。４時間後に取り出し、フイルムへの水滴付着状況を
観察した。
【００１６】
【実施例１、比較例１】ポリエーテルポリアミドブロッ
ク共重合体であるペバックス６３３３および１０４１
（エルフアトケム社製）を乾燥後、多層用一軸押し出し
機を用いて２００℃にて、ペバックス６３３３側２０
μ、１０４１側１０μとなるように２層フイルムを押し
出した。得られたフイルムの透湿度は７００ｇ／ｍ２／
２４ｈであり，ペバックス１０４１側が内側となるよう
に４０℃水入りビーカーをカバーしたところ、水滴付着
は皆無であった。比較にペバックス６３３３のみからな
る３０μフイルムの透湿度は６６０、水滴付着テストで
はフイルムに多数の水滴が見られた。尚、ペバックス１
０４１のみからなる２５μフイルムの透湿度は２７００
ｇ／ｍ２／２４ｈで、水滴の付着は一切なかった。
ク共重合体であるペバックス６３３３および１０４１
（エルフアトケム社製）を乾燥後、多層用一軸押し出し
機を用いて２００℃にて、ペバックス６３３３側２０
μ、１０４１側１０μとなるように２層フイルムを押し
出した。得られたフイルムの透湿度は７００ｇ／ｍ２／
２４ｈであり，ペバックス１０４１側が内側となるよう
に４０℃水入りビーカーをカバーしたところ、水滴付着
は皆無であった。比較にペバックス６３３３のみからな
る３０μフイルムの透湿度は６６０、水滴付着テストで
はフイルムに多数の水滴が見られた。尚、ペバックス１
０４１のみからなる２５μフイルムの透湿度は２７００
ｇ／ｍ２／２４ｈで、水滴の付着は一切なかった。
【００１７】
【実施例２、比較例２】エルフアトケム社製ペバックス
７０３３の２５μフイルム上に、ペバックス１０７４を
５μ厚さに押し出し、ラミネートした。この２層ラミネ
ーションフイルムの透湿度は３００、ペバックス１０７
４側を内側にした水滴付着テストでは水滴の付着は見ら
れなかった。比較にペバックス７０３３のみからなる３
０μフイルムの透湿度は２６０、水滴付着テストでは多
数の水滴の付着が見られた。又、ペバックス１０７４の
みからなる２５μフイルムの透湿度は４３００ｇ／ｍ２
／２４ｈであった。
７０３３の２５μフイルム上に、ペバックス１０７４を
５μ厚さに押し出し、ラミネートした。この２層ラミネ
ーションフイルムの透湿度は３００、ペバックス１０７
４側を内側にした水滴付着テストでは水滴の付着は見ら
れなかった。比較にペバックス７０３３のみからなる３
０μフイルムの透湿度は２６０、水滴付着テストでは多
数の水滴の付着が見られた。又、ペバックス１０７４の
みからなる２５μフイルムの透湿度は４３００ｇ／ｍ２
／２４ｈであった。
【００１８】
【比較例３】ペバックス７０３３ ９０部にペバックス
１０７４を１０部ブレンドし、一軸押し出し機にて２５
μ厚さのフイルムを製膜した。本フイルムの透湿度は４
００、水滴付着テストでは多数の水滴の付着が認められ
た。
１０７４を１０部ブレンドし、一軸押し出し機にて２５
μ厚さのフイルムを製膜した。本フイルムの透湿度は４
００、水滴付着テストでは多数の水滴の付着が認められ
た。
【００１９】
【実施例３、４】実施例２においてペバックス１０７４
の代わりにハイトレル４７６７（デユポン社製熱可塑性
ポリエステルエラストマー）、東洋紡ウレタンＥ３０８
０Ａ（東洋紡製）を用いてペバックス７０３３フイルム
上にラミネートし、３０μ厚さのフイルム（実施例３、
４）を得た。透湿度はそれぞれ２７０、２８０であり、
水滴付着テストではいずれも水滴は見られなかった。
の代わりにハイトレル４７６７（デユポン社製熱可塑性
ポリエステルエラストマー）、東洋紡ウレタンＥ３０８
０Ａ（東洋紡製）を用いてペバックス７０３３フイルム
上にラミネートし、３０μ厚さのフイルム（実施例３、
４）を得た。透湿度はそれぞれ２７０、２８０であり、
水滴付着テストではいずれも水滴は見られなかった。
【００２０】
【実施例５】実施例１においてペバックス６３３３の代
わりに東洋紡ウレタンＡ３０６４Ｄを用いた以外は実施
例１と同様にして２８μ厚さのウレタン／ペバックス２
層フイルムを共押出した。本フイルムの透湿度は６００
で、水滴付着は見られなかった。
わりに東洋紡ウレタンＡ３０６４Ｄを用いた以外は実施
例１と同様にして２８μ厚さのウレタン／ペバックス２
層フイルムを共押出した。本フイルムの透湿度は６００
で、水滴付着は見られなかった。
【００２１】
【発明の効果】以上説明したように、本発明のプラスチ
ックフイルムは適度の透湿度と低い水滴付着性を有し、
果物や野菜、花等を包装して低温で保存しても水滴によ
るフイルム曇りの少ないことが期待できる。
ックフイルムは適度の透湿度と低い水滴付着性を有し、
果物や野菜、花等を包装して低温で保存しても水滴によ
るフイルム曇りの少ないことが期待できる。
Claims (2)
- 【請求項１】 ＪＩＳＺ０２０８に規定する透湿度が１
０００ｇ／ｍ２／２４ｈ未満であるプラスチックフイル
ムにおいて、透湿度が１０００ｇ／ｍ２／２４ｈ以上で
あるフイルムと積層されていることを特徴とするプラス
チックフイルム。 - 【請求項２】 フイルムの素材がポリエーテルポリアミ
ドブロック共重合体、熱可塑性ポリエステルエラストマ
ー、熱可塑性ポリウレタンの群から選ばれた少なくとも
一種であることを特徴とする請求項１のプラスチックフ
イルム。