JPH09328672A - Moisture-proof adhesive composition and method for producing porous laminate using the same - Google Patents
Moisture-proof adhesive composition and method for producing porous laminate using the sameInfo
- Publication number
- JPH09328672A JPH09328672A JP14708396A JP14708396A JPH09328672A JP H09328672 A JPH09328672 A JP H09328672A JP 14708396 A JP14708396 A JP 14708396A JP 14708396 A JP14708396 A JP 14708396A JP H09328672 A JPH09328672 A JP H09328672A
- Authority
- JP
- Japan
- Prior art keywords
- emulsion
- moisture
- adhesive composition
- proof
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】
【課題】 防湿材の貼付を必要とせずに、防湿コート剤
を用いなくても防湿性にすぐれた皮膜を形成しうる防湿
性接着剤組成物およびそれを用いた多孔質材積層板の製
造法を提供すること。
【解決手段】 （Ａ）合成樹脂エマルジョン、（Ｂ）タ
ッキファイヤーエマルジョン、ならびに（Ｃ）ワックス
エマルジョン、シリコーン樹脂エマルジョン、フッ素樹
脂エマルジョン、塩素化パラフィンエマルジョン、塩化
ビニリデン樹脂エマルジョンおよび金属石鹸ディスパー
ジョンから選ばれた撥水剤からなる防湿性接着剤組成
物、ならびに前記防湿性接着剤組成物を用いて２枚以上
の多孔質材をたがいに接着させることを特徴とする多孔
質材積層板の製造法。(57) 【Abstract】 PROBLEM TO BE SOLVED: To provide a moisture-proof adhesive composition capable of forming a film excellent in moisture-proof property without using a moisture-proof material and without using a moisture-proof coating agent, and a porous material using the same. To provide a method for manufacturing a timber laminate. SOLUTION: This is selected from (A) synthetic resin emulsion, (B) tackifier emulsion, and (C) wax emulsion, silicone resin emulsion, fluororesin emulsion, chlorinated paraffin emulsion, vinylidene chloride resin emulsion and metal soap dispersion. A moisture-proof adhesive composition comprising a water-repellent agent, and a method for producing a porous material laminate, which comprises bonding two or more porous materials to each other using the moisture-proof adhesive composition.
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、防湿性接着剤組成
物およびそれを用いた多孔質材積層板の製造法に関す
る。さらに詳しくは、各種建築用材料などとして好適に
使用しうる多孔質材積層板の製造法およびそれに用いら
れる防湿性接着剤組成物に関する。TECHNICAL FIELD The present invention relates to a moisture-proof adhesive composition and a method for producing a porous material laminate using the same. More specifically, the present invention relates to a method for producing a porous material laminate which can be suitably used as various building materials and the like, and a moisture-proof adhesive composition used therefor.
【０００２】[0002]
【従来の技術】従来、石膏ボードなどの建築用材料に代
表される多孔質材に防湿性を付与する方法としては、ポ
リサンド紙やフイルムなどの防湿材を貼付する方法、多
孔質材に防湿コート剤を塗工する方法などが知られてい
る。2. Description of the Related Art Conventionally, as a method of imparting moisture resistance to a porous material typified by a building material such as gypsum board, a method of attaching a moisture-proof material such as polysand paper or film, a moisture-proof coating to the porous material. A method of applying the agent is known.
【０００３】しかしながら、前記防湿材を貼付する方法
では、わざわざ防湿材を多孔質材に貼付しなければなら
ないため、その操作が煩雑であるのみならず、人件費や
材料費などが嵩むという欠点がある。However, in the method of applying the moisture-proof material, since the moisture-proof material has to be purposefully applied to the porous material, not only the operation is complicated but also the labor cost and material cost are increased. is there.
【０００４】また、前記多孔質材に防湿コート剤を塗工
する方法では、塗工、乾燥の工程に人件費や材料費がか
さむという欠点があり、また耐水性にすぐれた防湿層を
形成させるために、前記防湿コート剤として、有機溶剤
系防湿コート剤を用いたばあいには、該有機溶剤は、人
体や環境に悪影響を与えることが懸念されている。Further, the method of applying the moisture-proof coating agent to the porous material has a drawback that labor and material costs are increased in the coating and drying steps, and a moisture-proof layer excellent in water resistance is formed. Therefore, when an organic solvent-based moisture-proof coating agent is used as the moisture-proof coating agent, it is feared that the organic solvent adversely affects the human body and the environment.
【０００５】[0005]
【発明が解決しようとする課題】本発明は、前記従来技
術に鑑みてなされたものであり、防湿材の貼付を必要と
せずに、防湿コート剤を用いなくても防湿性にすぐれた
皮膜を形成しうる防湿性接着剤組成物およびそれを用い
た多孔質材積層板の製造法を提供することを目的とす
る。DISCLOSURE OF THE INVENTION The present invention has been made in view of the above-mentioned prior art, and does not require the application of a moisture-proof material and provides a film excellent in moisture-proof property without using a moisture-proof coating agent. An object is to provide a moisture-proof adhesive composition that can be formed and a method for producing a porous material laminate using the same.
【０００６】[0006]
【課題を解決するための手段】本発明は、（Ａ）合成樹
脂エマルジョン、（Ｂ）タッキファイヤーエマルジョ
ン、ならびに（Ｃ）ワックスエマルジョン、シリコーン
樹脂エマルジョン、フッ素樹脂エマルジョン、塩素化パ
ラフィンエマルジョン、塩化ビニリデン樹脂エマルジョ
ンおよび金属石鹸ディスパージョンから選ばれた撥水剤
からなる防湿性接着剤組成物、ならびに前記防湿性接着
剤組成物を用いて２枚以上の多孔質材をたがいに接着さ
せることを特徴とする多孔質材積層板の製造法に関す
る。The present invention provides (A) synthetic resin emulsion, (B) tackifier emulsion, and (C) wax emulsion, silicone resin emulsion, fluororesin emulsion, chlorinated paraffin emulsion, vinylidene chloride resin. A moisture-proof adhesive composition comprising a water-repellent agent selected from an emulsion and a metal soap dispersion, and two or more porous materials are adhered to each other using the moisture-proof adhesive composition. The present invention relates to a method for manufacturing a porous material laminated plate.
【０００７】[0007]
【発明の実施の形態】本発明の防湿性接着剤組成物は、
前記したように、（Ａ）合成樹脂エマルジョン、（Ｂ）
タッキファイヤーエマルジョン、ならびに（Ｃ）ワック
スエマルジョン、シリコーン樹脂エマルジョン、フッ素
樹脂エマルジョン、塩素化パラフィンエマルジョン、塩
化ビニリデン樹脂エマルジョンおよび金属石鹸ディスパ
ージョンから選ばれた撥水剤で構成される。BEST MODE FOR CARRYING OUT THE INVENTION The moisture-proof adhesive composition of the present invention comprises:
As described above, (A) synthetic resin emulsion, (B)
It is composed of a tackifier emulsion and a water repellent selected from (C) wax emulsion, silicone resin emulsion, fluororesin emulsion, chlorinated paraffin emulsion, vinylidene chloride resin emulsion and metal soap dispersion.
【０００８】前記合成樹脂エマルジョンの合成樹脂のガ
ラス転移温度は、耐熱性を維持させ、またその使用後に
接着強度が保持されるようにするために、−２０℃以
上、好ましくは−１０℃以上とすることが望ましく、ま
た多孔質材同士を好適に接着させることができ、形成さ
れた接着剤層に柔軟性を付与するために、３０℃以下、
好ましくは１０℃以下とすることが望ましい。The glass transition temperature of the synthetic resin of the synthetic resin emulsion is -20.degree. C. or higher, preferably -10.degree. C. or higher in order to maintain heat resistance and maintain the adhesive strength after use. In order to allow the porous materials to adhere to each other, and to impart flexibility to the formed adhesive layer,
It is desirable to set the temperature to 10 ° C. or lower.
【０００９】前記合成樹脂のガラス転移温度の調整は、
その合成樹脂の種類を選択することによって行なっても
よく、またたとえばジブチルフタレート、ジオクチルフ
タレートなどの可塑剤を配合することによって行なって
もよい。The glass transition temperature of the synthetic resin can be adjusted by
It may be carried out by selecting the kind of the synthetic resin, or may be carried out by blending a plasticizer such as dibutyl phthalate or dioctyl phthalate.
【００１０】前記合成樹脂エマルジョンの代表例として
は、たとえば酢酸ビニル樹脂エマルジョン、酢酸ビニル
／（メタ）アクリル酸アルキルエステル樹脂エマルジョ
ン、エチレン／酢酸ビニル樹脂エマルジョン、（メタ）
アクリル酸アルキルエステル樹脂エマルジョン、塩化ビ
ニル／酢酸ビニル樹脂エマルジョン、エチレン／塩化ビ
ニル樹脂エマルジョン、スチレン／（メタ）アクリル酸
アルキルエステル／不飽和カルボン酸共重合体エマルジ
ョンなどがあげられる。これらの合成樹脂エマルジョン
のなかでは、スチレン／（メタ）アクリル酸アルキルエ
ステル／不飽和カルボン酸共重合体エマルジョンは、多
孔質材との密着性にすぐれ、多孔質材への塗工適性が良
好であり、耐水性にすぐれるという点で、好適に使用し
うるものである。Representative examples of the synthetic resin emulsion include vinyl acetate resin emulsion, vinyl acetate / (meth) acrylic acid alkyl ester resin emulsion, ethylene / vinyl acetate resin emulsion, (meth).
Examples thereof include acrylic acid alkyl ester resin emulsion, vinyl chloride / vinyl acetate resin emulsion, ethylene / vinyl chloride resin emulsion, and styrene / (meth) acrylic acid alkyl ester / unsaturated carboxylic acid copolymer emulsion. Among these synthetic resin emulsions, the styrene / (meth) acrylic acid alkyl ester / unsaturated carboxylic acid copolymer emulsion has excellent adhesion to the porous material and has good coating suitability for the porous material. It is suitable for use because it has excellent water resistance.
【００１１】前記スチレン／（メタ）アクリル酸アルキ
ルエステル／不飽和カルボン酸共重合体エマルジョンの
樹脂成分であるスチレン／（メタ）アクリル酸アルキル
エステル／不飽和カルボン酸共重合体に用いられている
（メタ）アクリル酸アルキルエステルの具体例として
は、たとえばアクリル酸メチル、メタクリル酸メチル、
アクリル酸エチル、メタクリル酸エチル、アクリル酸ブ
チル、メタクリル酸ブチル、アクリル酸２−エチルヘキ
シルなどのエステル部分のアルキル基の炭素数が１〜１
０の（メタ）アクリル酸アルキルエステルなどがあげら
れ、これらは単独でまたは２種以上を混合して用いられ
る。It is used in the styrene / (meth) acrylic acid alkyl ester / unsaturated carboxylic acid copolymer which is a resin component of the styrene / (meth) acrylic acid alkyl ester / unsaturated carboxylic acid copolymer emulsion ( Specific examples of the (meth) acrylic acid alkyl ester include, for example, methyl acrylate, methyl methacrylate,
The alkyl group in the ester moiety of ethyl acrylate, ethyl methacrylate, butyl acrylate, butyl methacrylate, 2-ethylhexyl acrylate, etc. has 1 to 1 carbon atoms.
Examples thereof include 0 (meth) acrylic acid alkyl ester, and these may be used alone or in admixture of two or more.
【００１２】また、前記不飽和カルボン酸の具体例とし
ては、たとえばアクリル酸、メタクリル酸、マレイン
酸、イタコン酸などがあげられ、これらは単独でまたは
２種以上を混合して用いられる。Specific examples of the unsaturated carboxylic acid include acrylic acid, methacrylic acid, maleic acid and itaconic acid, which may be used alone or in admixture of two or more.
【００１３】スチレン／（メタ）アクリル酸アルキルエ
ステル／不飽和カルボン酸共重合体には、スチレンが用
いられていなくてもよいが、スチレン、（メタ）アクリ
ル酸アルキルエステルおよび不飽和カルボン酸の原料モ
ノマーに、好ましくは５重量％以上含有されていること
が望ましく、また多孔質材への接着性および耐熱性の点
から、７０重量％以下、好ましくは６０重量％以下含有
されていることが望ましい。また（メタ）アクリル酸ア
ルキルエステルの原料モノマー中における含有量は、多
孔質材への接着性および耐水性の点から、２０重量％以
上、好ましくは３０重量％以上とすることが望ましく、
またエマルジョンの安定性および耐熱性の点から、９
９．７重量％以下、好ましくは９０重量％以下とするこ
とが望ましい。また、不飽和カルボン酸の原料モノマー
中における含有量は、エマルジョンの安定性および耐熱
性の点から、０．３重量％以上、好ましくは０．５重量
％以上であることが望ましく、また形成された接着剤組
成物の皮膜の耐水性および多孔質材同士の接着性の点か
ら、２０重量％以下、好ましくは１０重量％以下である
ことが望ましい。Although styrene may not be used in the styrene / (meth) acrylic acid alkyl ester / unsaturated carboxylic acid copolymer, raw materials for styrene, (meth) acrylic acid alkyl ester and unsaturated carboxylic acid are used. The content of the monomer is preferably 5% by weight or more, and from the viewpoint of adhesion to the porous material and heat resistance, it is preferably 70% by weight or less, preferably 60% by weight or less. . Further, the content of the (meth) acrylic acid alkyl ester in the raw material monomer is preferably 20% by weight or more, and more preferably 30% by weight or more, from the viewpoint of adhesion to the porous material and water resistance.
From the viewpoint of emulsion stability and heat resistance, 9
It is desirable that the amount is 9.7% by weight or less, preferably 90% by weight or less. The content of the unsaturated carboxylic acid in the raw material monomer is preferably 0.3% by weight or more, and more preferably 0.5% by weight or more, from the viewpoint of emulsion stability and heat resistance. From the viewpoint of the water resistance of the film of the adhesive composition and the adhesion between the porous materials, the content is preferably 20% by weight or less, and more preferably 10% by weight or less.
【００１４】スチレン、（メタ）アクリル酸アルキルエ
ステルおよび不飽和カルボン酸からなる原料モノマーを
乳化重合させる際には、前記原料モノマーの配合量は、
とくに制限がないが、通常、溶媒（水）１００重量部に
対して１５〜２００重量部程度であることが好ましい。When emulsion-polymerizing a raw material monomer consisting of styrene, an alkyl (meth) acrylate and an unsaturated carboxylic acid, the blending amount of the raw material monomer is
Although not particularly limited, it is usually preferably about 15 to 200 parts by weight with respect to 100 parts by weight of the solvent (water).
【００１５】前記原料モノマーを乳化重合させる際に
は、保護コロイドとして水溶性高分子化合物を用いるこ
とが好ましい。このように水溶性高分子化合物を用いた
ばあいには、えられる接着剤組成物の多孔質材への塗工
適性がよくなり、また形成された接着剤組成物の皮膜の
耐水性が向上するという利点がある。When emulsion-polymerizing the raw material monomers, it is preferable to use a water-soluble polymer compound as a protective colloid. Thus, when the water-soluble polymer compound is used, the adhesiveness of the obtained adhesive composition to the porous material is improved, and the water resistance of the film of the formed adhesive composition is improved. There is an advantage of doing.
【００１６】前記水溶性高分子化合物としては、たとえ
ばケン化度７０〜１００モル％および重合度３００〜３
０００のポリビニルアルコール、ヒドロキシエチルセル
ロース、メチルセルロース、カルボキシメチルセルロー
ス、α−オレフィン−不飽和カルボン酸共重合体塩、ス
チレン−不飽和カルボン酸共重合体塩、ポリプロピレン
オキサイド、ポリエチレンオキサイド、（メタ）アクリ
ル酸アルキルエステル−不飽和カルボン酸共重合体、デ
ンプン、それらの変性物などがあげられ、これらは、単
独でまたは２種以上を混合して用いられる。Examples of the water-soluble polymer compound include a saponification degree of 70 to 100 mol% and a polymerization degree of 300 to 3
Polyvinyl alcohol, hydroxyethyl cellulose, methyl cellulose, carboxymethyl cellulose, α-olefin-unsaturated carboxylic acid copolymer salt, styrene-unsaturated carboxylic acid copolymer salt, polypropylene oxide, polyethylene oxide, (meth) acrylic acid alkyl ester -Unsaturated carboxylic acid copolymers, starch, modified products thereof and the like can be mentioned, and these can be used alone or in admixture of two or more.
【００１７】前記水溶性高分子化合物の配合量は、通
常、溶媒（水）１００重量部に対して、エマルジョンの
安定性の点から、１重量部以上、なかんづく３重量部以
上であることが好ましく、また形成された接着剤組成物
の皮膜の耐水性の点から、２０重量部以下、なかんづく
１０重量部以下であることが好ましい。From the viewpoint of emulsion stability, the amount of the water-soluble polymer compound is usually 1 part by weight or more, preferably 3 parts by weight or more, relative to 100 parts by weight of the solvent (water). From the viewpoint of water resistance of the formed adhesive composition film, the amount is preferably 20 parts by weight or less, and more preferably 10 parts by weight or less.
【００１８】なお、前記水溶性高分子化合物の存在下で
前記原料モノマーを共重合させる際には、徐々に前記原
料モノマーを添加し、たとえば過硫酸アンモニウムなど
の重合開始剤を添加し、撹拌しながら６０〜８０℃程度
に加熱することが好ましい。When the raw material monomer is copolymerized in the presence of the water-soluble polymer compound, the raw material monomer is gradually added, a polymerization initiator such as ammonium persulfate is added, and the mixture is stirred. It is preferable to heat to about 60 to 80 ° C.
【００１９】かくして水溶性高分子化合物を保護コロイ
ドとして乳化重合によってえられたスチレン／（メタ）
アクリル酸アルキルエステル／不飽和カルボン酸共重合
体エマルジョンは、多孔質材への塗工適性および形成さ
れた接着剤組成物の皮膜の耐水性にすぐれるとともに、
多孔質材同士の接着性にもすぐれるので、本発明におい
ては、とくに好適に使用しうるものである。Styrene / (meth) thus obtained by emulsion polymerization using the water-soluble polymer compound as a protective colloid.
The acrylic acid alkyl ester / unsaturated carboxylic acid copolymer emulsion has excellent coating suitability for a porous material and excellent water resistance of the formed adhesive composition film,
Since the porous materials are also excellent in adhesiveness, they can be used particularly preferably in the present invention.
【００２０】なお、前記合成樹脂エマルジョンにおける
固形分量は、とくに限定がなく、通常、１０〜７０重量
％、なかんづく２０〜６０重量％程度であればよい。The solid content of the synthetic resin emulsion is not particularly limited, and is usually 10 to 70% by weight, preferably about 20 to 60% by weight.
【００２１】前記タッキファイヤーエマルジョンは、形
成された接着剤組成物の皮膜に、防湿性を付与する成分
である。The tackifier emulsion is a component that imparts moisture resistance to the formed film of the adhesive composition.
【００２２】前記タッキファイヤーエマルジョンの代表
例としては、たとえば石油樹脂エマルジョン、ロジンエ
ステル樹脂エマルジョン、テルペン−フェノール樹脂エ
マルジョン、クマロンインデン樹脂エマルジョン、それ
らの変性物などがあげられる。Representative examples of the tackifier emulsion include petroleum resin emulsion, rosin ester resin emulsion, terpene-phenol resin emulsion, coumarone indene resin emulsion, and modified products thereof.
【００２３】前記タッキファイヤーエマルジョンの固形
分は、合成樹脂エマルジョンの固形分１００重量部に対
して、形成された接着剤組成物の皮膜に防湿性を付与す
るために、５重量部以上、なかんづく７重量部以上とす
ることが好ましく、また接着性を良好にするために、５
０重量部以下、なかんづく４５重量部以下とすることが
好ましい。The solid content of the tackifier emulsion is 5 parts by weight or more, especially 7 parts by weight to give 100% by weight of the solid content of the synthetic resin emulsion to the film of the formed adhesive composition. It is preferable to add more than 5 parts by weight, and in order to improve the adhesiveness, 5
It is preferably 0 parts by weight or less, especially 45 parts by weight or less.
【００２４】前記撥水剤は、形成された接着剤組成物の
皮膜に、防湿性を付与する成分である。The water repellent is a component that imparts moisture resistance to the formed film of the adhesive composition.
【００２５】前記撥水剤としては、ワックスエマルジョ
ン、シリコーン樹脂エマルジョン、フッ素樹脂エマルジ
ョン、塩素化パラフィンエマルジョン、塩化ビニリデン
樹脂エマルジョンおよび金属石鹸ディスパージョンから
選ばれた１種または２種以上が用いられる。As the water repellent, one or more selected from wax emulsion, silicone resin emulsion, fluororesin emulsion, chlorinated paraffin emulsion, vinylidene chloride resin emulsion and metal soap dispersion are used.
【００２６】前記撥水剤の固形分量は、合成樹脂エマル
ジョンの固形分１００重量部に対して、形成された接着
剤組成物の皮膜に防湿性を付与するために、３重量部以
上、なかんづく５重量部以上とすることが好ましく、ま
た接着性を良好にするために、５０重量部以下、なかん
づく３０重量部以下とすることが好ましい。The solid content of the water-repellent agent is 3 parts by weight or more, especially 5 parts by weight based on 100 parts by weight of the solid content of the synthetic resin emulsion in order to impart moisture resistance to the formed adhesive composition film. The amount is preferably not less than 50 parts by weight, and is preferably not more than 50 parts by weight, more preferably not more than 30 parts by weight in order to improve the adhesiveness.
【００２７】前記（Ａ）合成樹脂エマルジョン、（Ｂ）
タッキファイヤーエマルジョン、ならびに（Ｃ）ワック
スエマルジョン、シリコーン樹脂エマルジョン、フッ素
樹脂エマルジョン、塩素化パラフィンエマルジョン、塩
化ビニリデン樹脂エマルジョンおよび金属石鹸ディスパ
ージョンから選ばれた撥水剤を混合することにより、本
発明の防湿性接着剤組成物がえられるが、さらに造膜助
剤を適宜配合してもよい。(A) Synthetic resin emulsion, (B)
The tackifier emulsion and the water repellent selected from (C) a wax emulsion, a silicone resin emulsion, a fluororesin emulsion, a chlorinated paraffin emulsion, a vinylidene chloride resin emulsion and a metal soap dispersion are mixed to obtain the moisture-proof property of the present invention. Although a hydrophilic adhesive composition can be obtained, a film-forming aid may be appropriately added.
【００２８】前記造膜助剤の具体例としては、たとえば
トルエン、キシレンなどの低沸点溶剤をはじめ、２，
２，４−トリメチル−１，３−ペンタンジオールモノイ
ソブチレートなどがあげられる。Specific examples of the film forming aid include low boiling point solvents such as toluene and xylene, and
2,4-trimethyl-1,3-pentanediol monoisobutyrate and the like can be mentioned.
【００２９】本発明の防湿性接着剤組成物は、水性であ
るので、取扱いが容易であり、また多孔質材との接着力
にすぐれるのみならず、すぐれた防湿性を呈する皮膜を
形成するものである。Since the moisture-proof adhesive composition of the present invention is water-based, it is easy to handle, and not only has an excellent adhesive force with a porous material, but also forms a film having excellent moisture-proof property. It is a thing.
【００３０】したがって、本発明の防湿性接着剤組成物
は、防湿性が要求される多孔質材積層板の製造に好適に
使用しうるものである。Therefore, the moisture-proof adhesive composition of the present invention can be suitably used for the production of a porous material laminate which requires moisture-proof property.
【００３１】本発明の多孔質材積層板の製造法によれ
ば、前記防湿性接着剤組成物を用いて２枚以上の多孔質
材をたがいに接着させることによって多孔質材積層板が
えられる。According to the method for producing a porous material laminate of the present invention, a porous material laminate is obtained by adhering two or more porous materials with each other using the moisture-proof adhesive composition. .
【００３２】前記多孔質材の代表例としては、たとえば
石膏ボード、パーティクルボード、ＭＤＦ（中密度木質
ファイバーボード）、ハードボード、発泡ポリスチレン
ボード、発泡ポリウレタンボード、発泡ポリオレフィン
ボード、合板などがあげられる。Typical examples of the porous material include gypsum board, particle board, MDF (medium density wood fiber board), hard board, expanded polystyrene board, expanded polyurethane board, expanded polyolefin board and plywood.
【００３３】前記防湿性接着剤組成物の多孔質材への塗
布量は、接着性および防湿性の点から、２０ｇ／ｍ2以
上、なかんづく３０ｇ／ｍ2以上とすることが好まし
く、またコストおよび乾燥性の点から、５００ｇ／ｍ2
以下、なかんづく３００ｇ／ｍ2以下とすることが好ま
しい。The amount of the moisture-proof adhesive composition applied to the porous material is preferably 20 g / m 2 or more, particularly 30 g / m 2 or more, from the viewpoint of adhesiveness and moisture-proof property, and the cost and From the point of dryness, 500 g / m 2
Hereinafter, it is preferably 300 g / m 2 or less.
【００３４】前記防湿性接着剤組成物を多孔質材に塗布
する方法としては、たとえばロールコーティング法、フ
ローコーティング法、スプレーコーティング法、ハケ塗
り法などがあげられる。Examples of methods for applying the moisture-proof adhesive composition to the porous material include roll coating, flow coating, spray coating, and brush coating.
【００３５】前記防湿性接着剤組成物を多孔質材に塗布
したのち、その塗布面に樹脂プレートを貼付し、適宜室
温で養生することにより、多孔質材積層体がえられる。A porous material laminate is obtained by applying the moisture-proof adhesive composition to a porous material, attaching a resin plate to the application surface, and aging at room temperature.
【００３６】本発明の製造法によってえられた多孔質材
積層板は、前記防湿性接着剤組成物にもとづいてすぐれ
た防湿層を有するので、たとえば壁材、床材、ドアなど
の材料などとして好適に使用しうるものである。Since the porous material laminate obtained by the production method of the present invention has an excellent moisture-proof layer based on the moisture-proof adhesive composition, it can be used as a material for wall materials, floor materials, doors, etc. It can be preferably used.
【００３７】[0037]
【実施例】つぎに、本発明の防湿性接着剤組成物および
それを用いた多孔質材積層板の製造法を実施例にもとづ
いてさらに詳細に説明するが、本発明は、かかる実施例
のみに限定されるものではない。EXAMPLES Next, the moisture-proof adhesive composition of the present invention and a method for producing a porous material laminate using the same will be described in more detail with reference to Examples. However, the present invention is not limited to these Examples. It is not limited to.
【００３８】製造例１ 攪拌機、還流冷却機、滴下ロートおよび温度計を備えた
１リットル容のセパラブルフラスコに、水４７０ｇおよ
びポリビニルアルコール（平均重合度５００、ケン化度
８８モル％）３０ｇを添加し、９０℃に加熱して溶解せ
しめたのち、重合開始剤として過硫酸アンモニウム２ｇ
を添加し、ついでモノマーとしてスチレン２２０ｇ、ア
クリル酸２−エチルヘキシル２７０ｇおよびアクリル酸
１０ｇの混合物を７５℃で３時間連続滴下して重合さ
せ、合成樹脂エマルジョン（固形分量５３重量％、合成
樹脂のガラス転移温度−７．４℃）をえた。Production Example 1 To a 1-liter separable flask equipped with a stirrer, a reflux condenser, a dropping funnel and a thermometer, 470 g of water and 30 g of polyvinyl alcohol (average polymerization degree: 500, saponification degree: 88 mol%) were added. Then, after heating to 90 ° C. to dissolve it, 2 g of ammonium persulfate as a polymerization initiator
Then, a mixture of 220 g of styrene as a monomer, 270 g of 2-ethylhexyl acrylate and 10 g of acrylic acid was continuously added dropwise at 75 ° C. for 3 hours to polymerize, and a synthetic resin emulsion (solid content 53% by weight, glass transition of synthetic resin Temperature -7.4 ° C).
【００３９】実施例１〜１３および比較例１〜５ 以下に示す合成樹脂エマルジョン、タッキファイヤーエ
マルジョン、撥水剤および造膜助剤を表１に示すように
配合して防湿性接着剤組成物をえた。Examples 1 to 13 and Comparative Examples 1 to 5 A synthetic resin emulsion, a tackifier emulsion, a water repellent, and a film-forming aid shown below were blended as shown in Table 1 to obtain a moisture-proof adhesive composition. I got it.
【００４０】なお、表１中の各略号は、以下のことを意
味する。The abbreviations in Table 1 mean the following.
【００４１】（Ａ）合成樹脂エマルジョン ＥＭ−Ｉ：製造例１でえられた樹脂エマルジョン（固形
分量５３重量％） ＥＭ−ＩＩ：酢酸ビニル樹脂エマルジョン（リカボンド
ＷＨ−９０９、中央理化工業（株）製、固形分量５２重
量％） ＥＭ−ＩＩＩ：エチレン−酢酸ビニル樹脂エマルジョン
（リカボンドＢＥ−８００、中央理化工業（株）製、固
形分量５５重量％） （Ｂ）タッキファイヤーエマルジョン ＴＥ−Ｉ：テルペン−フェノール樹脂エマルジョン（ス
タロン２１３０、ヤスハラケミカル（株）製、固形分量
４６重量％） ＴＥ−ＩＩ：石油樹脂エマルジョン（ＡＭ−１００２、
荒川化学工業（株）製、固形分量４５重量％） ＴＥ−ＩＩＩ：ロジンエステル樹脂エマルジョン（スー
パーエステルＥ−７２０、荒川化学工業（株）製、固形
分量５０重量％） （Ｃ）撥水剤 ＷＲ−Ｉ：ワックスエマルジョン（ダイジットＥＫ、互
応化学工業（株）製、固形分量３０重量％） ＷＲ−ＩＩ：フッ素樹脂エマルジョン（アサヒガードＡ
Ｇ−３１０、明成化学工業（株）製、固形分量２７重量
％） ＷＲ−ＩＩＩ：金属石鹸ディスパージョン（ハイドリン
Ｚ−７、中京油脂（株）製、固形分量３１重量％） ＷＲ−ＩＶ：シリコーン樹脂エマルジョン（ＴＳＷ−８
３１、東芝シリコーン（株）製、固形分量３０重量％） ＷＲ−Ｖ：塩化ビニリデン樹脂エマルジョン（呉羽化学
工業（株）製、クレハロンＤＯＡ、固形分量４８重量
％） ＷＲ−ＶＩ：塩素化パラフィンエマルジョン（東洋化成
工業（株）製、ハードレンＣ−４２０、固形分量４０重
量％） （Ｄ）造膜助剤 ＦＡ：２，２，４−トリメチル−１，３−ペンタンジオ
ールモノイソブチレート つぎに、えられた防湿性接着剤組成物を石膏ボート（厚
さ１０ｍｍ、吉野石膏（株）製）に塗布量が５０ｇ／ｍ
2（固形分）となるようにロールコーティング法によっ
て塗布し、これに発泡ポリスチレンボード（厚さ１０ｍ
ｍ）を貼付し、室温で１日間養生して多孔質材積層板を
えた。(A) Synthetic resin emulsion EM-I: Resin emulsion obtained in Preparation Example 1 (solid content 53% by weight) EM-II: Vinyl acetate resin emulsion (Ricabond WH-909, manufactured by Chuo Rika Kogyo Co., Ltd.) , Solid content 52% by weight) EM-III: ethylene-vinyl acetate resin emulsion (Ricabond BE-800, manufactured by Chuo Rika Kogyo Co., Ltd., solid content 55% by weight) (B) tackifier emulsion TE-I: terpene-phenol Resin emulsion (Staron 2130, Yasuhara Chemical Co., Ltd., solid content 46% by weight) TE-II: Petroleum resin emulsion (AM-1002,
Arakawa Chemical Industry Co., Ltd., solid content 45% by weight) TE-III: Rosin ester resin emulsion (Super Ester E-720, Arakawa Chemical Industry Co., Ltd., solid content 50% by weight) (C) Water repellent WR -I: Wax emulsion (manufactured by Dygit EK Co., Ltd., Kyosho Chemical Industry Co., Ltd., solid content 30% by weight) WR-II: Fluororesin (Asahi Guard A)
G-310, manufactured by Meisei Chemical Industry Co., Ltd., solid content: 27% by weight) WR-III: Metal soap dispersion (Hydrin Z-7, manufactured by Chukyo Yushi Co., Ltd., solid content: 31% by weight) WR-IV: Silicone Resin emulsion (TSW-8
31, Toshiba Silicone Co., Ltd., solid content 30% by weight WR-V: Vinylidene chloride resin emulsion (Kureha Chemical Industry Co., Ltd., Kurehalon DOA, solid content 48% by weight) WR-VI: Chlorinated paraffin emulsion ( Toray Kasei Kogyo Co., Ltd., Hardlen C-420, solid content 40% by weight) (D) Film-forming auxiliary agent FA: 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate The applied moisture-proof adhesive composition is applied to a gypsum boat (thickness: 10 mm, manufactured by Yoshino Gypsum Co., Ltd.) at a coating amount of 50 g / m.
2 (solid content) was applied by the roll coating method, and expanded polystyrene board (thickness 10m
m) was attached and cured at room temperature for 1 day to obtain a porous material laminate.
【００４２】えられた多孔質材積層板の透湿度を、ＪＩ
Ｓ Ｚ−０２０８の防湿包装材料の透湿度試験方法（カ
ップ法）に準拠して、温度４０℃、相対湿度９０％の雰
囲気中に１日間放置して測定した。The moisture permeability of the obtained porous material laminated plate was measured by JI
According to the moisture permeability test method (cup method) of the moisture-proof packaging material of SZ-0208, the measurement was carried out by leaving it in an atmosphere at a temperature of 40 ° C. and a relative humidity of 90% for 1 day.
【００４３】なお、接着されていない発泡ポリスチレン
ボードのみの透湿度を同様にして調べ、ブランクとし
た。その結果を表１に示す。The moisture permeability of only the non-adhered expanded polystyrene board was examined in the same manner and used as a blank. Table 1 shows the results.
【００４４】[0044]
【表１】 [Table 1]
【００４５】表１に示された結果から、実施例１〜１３
でえられた多孔質材積層板は、透湿度が低く、防湿性に
すぐれたものであることがわかる。From the results shown in Table 1, Examples 1 to 13
It can be seen that the obtained porous material laminate has a low moisture permeability and an excellent moisture resistance.
【００４６】[0046]
【発明の効果】本発明の防湿性接着剤組成物は、防湿材
の貼付を必要とせずに、防湿コート剤を塗工せずにすぐ
れた皮膜を形成するものである。The moisture-proof adhesive composition of the present invention forms an excellent film without applying a moisture-proof material and without applying a moisture-proof coating agent.
【００４７】したがって、本発明の防湿性接着剤組成物
は、防湿性が要求される多孔質材積層板に好適に使用し
うるものである。Therefore, the moisture-proof adhesive composition of the present invention can be suitably used for a porous laminate having a moisture-proof property.
Claims (4)
ッキファイヤーエマルジョン、ならびに（Ｃ）ワックス
エマルジョン、シリコーン樹脂エマルジョン、フッ素樹
脂エマルジョン、塩素化パラフィンエマルジョン、塩化
ビニリデン樹脂エマルジョンおよび金属石鹸ディスパー
ジョンから選ばれた撥水剤からなる防湿性接着剤組成
物。1. A synthetic resin emulsion selected from (A) synthetic resin emulsion, (B) tackifier emulsion, (C) wax emulsion, silicone resin emulsion, fluororesin emulsion, chlorinated paraffin emulsion, vinylidene chloride resin emulsion and metal soap dispersion. Moisture-proof adhesive composition comprising a water repellent.
化合物を保護コロイドとして乳化重合によってえられた
スチレン／（メタ）アクリル酸アルキルエステル／不飽
和カルボン酸共重合体エマルジョンである請求項１記載
の防湿性接着剤組成物。2. The synthetic resin emulsion is a styrene / (meth) acrylic acid alkyl ester / unsaturated carboxylic acid copolymer emulsion obtained by emulsion polymerization using a water-soluble polymer compound as a protective colloid. Moisture-proof adhesive composition.
量部に対してタッキファイヤーエマルジョンの固形分５
〜５０重量部および撥水剤の固形分３〜５０重量部を配
合してなる防湿性接着剤組成物。3. The solid content of the tackifier emulsion is 5 to the solid content of 100 parts by weight of the synthetic resin emulsion.
A moisture-proof adhesive composition comprising ˜50 parts by weight and a solid content of a water repellent of 3 to 50 parts by weight.
剤組成物を用いて２枚以上の多孔質材をたがいに接着さ
せることを特徴とする多孔質材積層板の製造法。4. A method for producing a porous material laminated plate, which comprises bonding two or more porous materials to each other using the moisture-proof adhesive composition according to claim 1, 2, or 3.