JPH0960768A - 耐蝕性ヒューム管 - Google Patents
耐蝕性ヒューム管Info
- Publication number
- JPH0960768A JPH0960768A JP21152195A JP21152195A JPH0960768A JP H0960768 A JPH0960768 A JP H0960768A JP 21152195 A JP21152195 A JP 21152195A JP 21152195 A JP21152195 A JP 21152195A JP H0960768 A JPH0960768 A JP H0960768A
- Authority
- JP
- Japan
- Prior art keywords
- fume tube
- corrosion
- metal ions
- mortar
- sulfur
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】
【課題】 下水配管等における硫酸還元細菌やチオバチ
ルス属等の硫黄酸化細菌の増殖により生成する硫黄の酸
化を効率的に且つ長時間に渡って防止して、腐蝕や劣化
を起こさない耐蝕性ヒューム管を提供すること。 【解決手段】 コンクリート、モルタル又は高分子材料
よりなるヒューム管において、抗菌性金属イオンを担持
した無機粉末を含有することを特徴とする耐蝕性ヒュー
ム管。
ルス属等の硫黄酸化細菌の増殖により生成する硫黄の酸
化を効率的に且つ長時間に渡って防止して、腐蝕や劣化
を起こさない耐蝕性ヒューム管を提供すること。 【解決手段】 コンクリート、モルタル又は高分子材料
よりなるヒューム管において、抗菌性金属イオンを担持
した無機粉末を含有することを特徴とする耐蝕性ヒュー
ム管。
Description
【０００１】
【発明の属する技術分野】本発明は、耐蝕性ヒューム管
に関し、更に詳しくは下水処理施設等におけるチオバチ
ルス属（Thiobacillus sp.）等の硫黄酸化細菌に対し耐
蝕性を有するヒューム管に関する。
に関し、更に詳しくは下水処理施設等におけるチオバチ
ルス属（Thiobacillus sp.）等の硫黄酸化細菌に対し耐
蝕性を有するヒューム管に関する。
【０００２】
【従来の技術】従来より、下水処理施設等から発生する
硫化水素や硫酸によるヒューム管等のコンクリート又は
モルタル構造物の石膏化や塗料の剥離による劣化が知ら
れている。このような劣化の原因として、一般に土壌・
水中に存在するチオバチルス属の硫黄酸化細菌が硫化水
素を酸化し硫酸を生成するために、前記構造成分の腐蝕
が引起こされることが知られている。すなわち、下水中
での硫化物の生成は主として無機性の硫黄化合物の生物
化学的な還元によって生ずる。多くの細菌が硫酸塩を硫
化物に還元するが、硫酸還元細菌、特にDesulfovibrio
desulfuricans が下水中の硫酸塩と有機物から硫化水素
を生成する。発生した硫化水素は大気中に拡散し、コン
クリート表面に棲息するチオバチルス属の硫黄酸化細菌
Thiobacillus concretivorus により硫酸に酸化され
る。こられの微生物は低いpHに対して非常に強い耐性を
持ち、硫酸濃度が７％になっても活性を保持している。
この結果、硫酸によりコンクリートまたはモルタルの中
性化が促進され、腐蝕が発生する。この劣化の防止方法
としては、種々の提案がなされているが、経済的で有効
な方法は開示されていない。チオバチルス属の硫黄酸化
細菌に対して抗菌性を示す薬剤をヒューム管に適用する
試みがなされている。抗菌剤として例えば、シクロヘキ
シミド、チアベンタゾール等の有機薬剤や水難溶性金
属、金属酸化物粒子（特開平４−１４９０５３号）を挙
げているが、抗菌性能の有効性や持続性の点で不十分で
あった。
硫化水素や硫酸によるヒューム管等のコンクリート又は
モルタル構造物の石膏化や塗料の剥離による劣化が知ら
れている。このような劣化の原因として、一般に土壌・
水中に存在するチオバチルス属の硫黄酸化細菌が硫化水
素を酸化し硫酸を生成するために、前記構造成分の腐蝕
が引起こされることが知られている。すなわち、下水中
での硫化物の生成は主として無機性の硫黄化合物の生物
化学的な還元によって生ずる。多くの細菌が硫酸塩を硫
化物に還元するが、硫酸還元細菌、特にDesulfovibrio
desulfuricans が下水中の硫酸塩と有機物から硫化水素
を生成する。発生した硫化水素は大気中に拡散し、コン
クリート表面に棲息するチオバチルス属の硫黄酸化細菌
Thiobacillus concretivorus により硫酸に酸化され
る。こられの微生物は低いpHに対して非常に強い耐性を
持ち、硫酸濃度が７％になっても活性を保持している。
この結果、硫酸によりコンクリートまたはモルタルの中
性化が促進され、腐蝕が発生する。この劣化の防止方法
としては、種々の提案がなされているが、経済的で有効
な方法は開示されていない。チオバチルス属の硫黄酸化
細菌に対して抗菌性を示す薬剤をヒューム管に適用する
試みがなされている。抗菌剤として例えば、シクロヘキ
シミド、チアベンタゾール等の有機薬剤や水難溶性金
属、金属酸化物粒子（特開平４−１４９０５３号）を挙
げているが、抗菌性能の有効性や持続性の点で不十分で
あった。
【０００３】
【発明が解決しようとする課題】本発明の目的は、下水
配管等における硫酸還元細菌やチオバチルス属等の硫黄
酸化細菌の増殖により生成する硫黄の酸化を効率的に且
つ長時間に渡って防止して、腐蝕や劣化を起こさない耐
蝕性ヒューム管を提供することにある。
配管等における硫酸還元細菌やチオバチルス属等の硫黄
酸化細菌の増殖により生成する硫黄の酸化を効率的に且
つ長時間に渡って防止して、腐蝕や劣化を起こさない耐
蝕性ヒューム管を提供することにある。
【０００４】
【課題を解決するための手段】本発明は、コンクリー
ト、モルタル又は高分子材料よりなるヒューム管におい
て、抗菌性金属イオンを担持した無機粉末を含有するこ
とを特徴とする耐蝕性ヒューム管を提供するものであ
る。本発明のヒューム管は、長期間にわたって耐蝕性を
維持する。
ト、モルタル又は高分子材料よりなるヒューム管におい
て、抗菌性金属イオンを担持した無機粉末を含有するこ
とを特徴とする耐蝕性ヒューム管を提供するものであ
る。本発明のヒューム管は、長期間にわたって耐蝕性を
維持する。
【０００５】
【発明の実施の形態】本発明において抗菌性金属イオン
を担持する無機粉体は、金属や金属酸化物に比べて硫黄
還元細菌やチオバチルス属等の硫黄酸化細菌に対する抗
菌性能が強い金属イオンを用いるのが好ましい。しか
し、金属イオンは非常に不安定であり、このままコンク
リート、モルタルや高分子材料に混合してもすぐに化学
変化を起こし、効果的な抗菌作用は期待できない。その
ため、金属イオンを安定に保持する担体として種々の無
機粉末を該金属イオンの担持体として用いる。これら無
機粉末としては、種々の金属イオンを安定してイオン交
換にて保持できる材料を使用できる。例えば、シリカゲ
ル（SiO2・nH2O）、含水アルミナ（Al2O3 ・nH2O）、含
水酸化チタン（TiO2・nH2O）、含水酸化ジルコニウム
（ZrO2・nH2O）、含水酸化マンガン（MnO2・nH2O）、含
水酸化アンチモン（Sb2O5 ・nH2O）等の含水酸化物、リ
ン酸チタン（Ti(HPO4)2 ・nH2O）、リン酸ジルコニウム
(Zr(HPO4)2・nH 2O）等のリン酸塩、アンチモン酸チタン
（TiO2・mSb2O5・nH2O) 、アンチモン酸スズ（SnO2・lS
b2O5・nH2O) 等のアンチモン酸塩、ゼオライト等のアル
ミノケイ酸塩、カオリナイト、モンモリロナイト等の粘
土鉱物やハイドロキシアパタイト、ヘテロポリ酸を挙げ
ることができる。この内、耐酸性に富み耐蝕持続性が良
い点から含水酸化物、リン酸塩およびケイ素分の多い
（SiO2含有率６０％以上）のアルミノケイ酸塩が好まし
い。
を担持する無機粉体は、金属や金属酸化物に比べて硫黄
還元細菌やチオバチルス属等の硫黄酸化細菌に対する抗
菌性能が強い金属イオンを用いるのが好ましい。しか
し、金属イオンは非常に不安定であり、このままコンク
リート、モルタルや高分子材料に混合してもすぐに化学
変化を起こし、効果的な抗菌作用は期待できない。その
ため、金属イオンを安定に保持する担体として種々の無
機粉末を該金属イオンの担持体として用いる。これら無
機粉末としては、種々の金属イオンを安定してイオン交
換にて保持できる材料を使用できる。例えば、シリカゲ
ル（SiO2・nH2O）、含水アルミナ（Al2O3 ・nH2O）、含
水酸化チタン（TiO2・nH2O）、含水酸化ジルコニウム
（ZrO2・nH2O）、含水酸化マンガン（MnO2・nH2O）、含
水酸化アンチモン（Sb2O5 ・nH2O）等の含水酸化物、リ
ン酸チタン（Ti(HPO4)2 ・nH2O）、リン酸ジルコニウム
(Zr(HPO4)2・nH 2O）等のリン酸塩、アンチモン酸チタン
（TiO2・mSb2O5・nH2O) 、アンチモン酸スズ（SnO2・lS
b2O5・nH2O) 等のアンチモン酸塩、ゼオライト等のアル
ミノケイ酸塩、カオリナイト、モンモリロナイト等の粘
土鉱物やハイドロキシアパタイト、ヘテロポリ酸を挙げ
ることができる。この内、耐酸性に富み耐蝕持続性が良
い点から含水酸化物、リン酸塩およびケイ素分の多い
（SiO2含有率６０％以上）のアルミノケイ酸塩が好まし
い。
【０００６】本発明において使用される抗菌性金属イオ
ンとしては、銀、銅、亜鉛、ニッケル、コバルト、水
銀、カドミウム、鉛、すず、パラジウム、ロジウム、モ
リブデンの各イオンを挙げることができる。この内チオ
バチルス属に対する抗菌性能が強く、ヒューム管に添加
する量が比較的少量で良い銀、銅、亜鉛、ニッケル、コ
バルトの各イオンが好ましい。前記の抗菌性金属イオン
の無機粉末に担持する量は、銀、銅、亜鉛、ニッケル、
コバルトの各イオンについては１種または２種以上の金
属イオンの量で0.５〜２0.０重量％、水銀、カドミウ
ム、鉛、すず、パラジウム、ロジウム、モリブデンの各
イオンについては１種または２種以上の金属イオンの量
で５〜４０重量％が適当である。
ンとしては、銀、銅、亜鉛、ニッケル、コバルト、水
銀、カドミウム、鉛、すず、パラジウム、ロジウム、モ
リブデンの各イオンを挙げることができる。この内チオ
バチルス属に対する抗菌性能が強く、ヒューム管に添加
する量が比較的少量で良い銀、銅、亜鉛、ニッケル、コ
バルトの各イオンが好ましい。前記の抗菌性金属イオン
の無機粉末に担持する量は、銀、銅、亜鉛、ニッケル、
コバルトの各イオンについては１種または２種以上の金
属イオンの量で0.５〜２0.０重量％、水銀、カドミウ
ム、鉛、すず、パラジウム、ロジウム、モリブデンの各
イオンについては１種または２種以上の金属イオンの量
で５〜４０重量％が適当である。
【０００７】無機粉体の粒子径は、コンクリート、モル
タルや高分子材料に容易に且つ均一に混合し得るように
するため微粉末状であるのが望ましく、特に平均粒径0.
００１〜0.１mmの微粉末であることが好ましい。抗菌性
金属イオンを担持した無機粉体の、コンクリート、モル
タルや高分子材料に添加する量は、１〜５０重量％が好
ましく、さらに好ましくは３〜１０重量％である。本発
明においてヒューム管を成型する材料としては、従来よ
り知られているコンクリート、モルタル及び高分子材料
を挙げることができ、いずれの材料も適用できる。高分
子材料としては、ポリ塩化ビニル、エポキシ樹脂、不飽
和ポリエステル樹脂、ポリエチレン、ポリプロピレン等
を挙げることができる。なおヒューム管成型にあたり、
減水剤としてナフタレンスルホン酸・ホルムアルデヒド
縮合物、アクリル酸塩、メタクリル酸塩等を加えること
もできる。
タルや高分子材料に容易に且つ均一に混合し得るように
するため微粉末状であるのが望ましく、特に平均粒径0.
００１〜0.１mmの微粉末であることが好ましい。抗菌性
金属イオンを担持した無機粉体の、コンクリート、モル
タルや高分子材料に添加する量は、１〜５０重量％が好
ましく、さらに好ましくは３〜１０重量％である。本発
明においてヒューム管を成型する材料としては、従来よ
り知られているコンクリート、モルタル及び高分子材料
を挙げることができ、いずれの材料も適用できる。高分
子材料としては、ポリ塩化ビニル、エポキシ樹脂、不飽
和ポリエステル樹脂、ポリエチレン、ポリプロピレン等
を挙げることができる。なおヒューム管成型にあたり、
減水剤としてナフタレンスルホン酸・ホルムアルデヒド
縮合物、アクリル酸塩、メタクリル酸塩等を加えること
もできる。
【０００８】本発明においてヒューム管の成型方法は、
従来より知られている方法のいずれも可能である。この
内、無機粉末をヒューム管の内壁部に高濃度に配合でき
る遠心成型法が好ましい。遠心成型方法としては、例え
ば特開昭６３−６０１４２号に記載の方法がある。本発
明のヒューム管の材料である、抗菌性金属イオンを担持
した無機粉末を含有するコンクリート、モルタル又は高
分子材料を使用して、ヒューム管のほか、下水処理設備
で使用するタンク材、板材等の種々の形状の成型物を製
造することもできる。
従来より知られている方法のいずれも可能である。この
内、無機粉末をヒューム管の内壁部に高濃度に配合でき
る遠心成型法が好ましい。遠心成型方法としては、例え
ば特開昭６３−６０１４２号に記載の方法がある。本発
明のヒューム管の材料である、抗菌性金属イオンを担持
した無機粉末を含有するコンクリート、モルタル又は高
分子材料を使用して、ヒューム管のほか、下水処理設備
で使用するタンク材、板材等の種々の形状の成型物を製
造することもできる。
【０００９】
【発明の効果】本発明の耐蝕性ヒューム管は、下水処理
施設で発生する硫黄酸化細菌による腐蝕や劣化を長期間
に渡って防止することができる。
施設で発生する硫黄酸化細菌による腐蝕や劣化を長期間
に渡って防止することができる。
【００１０】
【実施例】以下、本発明を実施例に基づき詳細に説明す
る。
る。
【参考例１】 含水酸化チタン系及びリン酸ジルコニウ
ム系無機粉体の調製 市販の含水酸化チタン（平均粒径4.２μｍ）またはリン
酸ジルコニウム（平均粒径1.２μｍ）１Kgに、イオン交
換のために抗菌性金属イオンを含む水溶液２Ｌを加え、
室温で２４時間攪拌し、平衡状態に保持した。終了後、
固相を濾過し温水にて固相中の過剰の金属イオンがなく
なるまで水洗した。次に試料を１１０℃で加熱、乾燥、
粉砕し、無機粉末を得た。得られた試料のデータを表１
に示す。なおイオン交換のための溶液として硝酸銀、硝
酸銅、硝酸亜鉛、硝酸ニッケル、モリブデン酸アンモニ
ウムの各水溶液を用いた。
ム系無機粉体の調製 市販の含水酸化チタン（平均粒径4.２μｍ）またはリン
酸ジルコニウム（平均粒径1.２μｍ）１Kgに、イオン交
換のために抗菌性金属イオンを含む水溶液２Ｌを加え、
室温で２４時間攪拌し、平衡状態に保持した。終了後、
固相を濾過し温水にて固相中の過剰の金属イオンがなく
なるまで水洗した。次に試料を１１０℃で加熱、乾燥、
粉砕し、無機粉末を得た。得られた試料のデータを表１
に示す。なおイオン交換のための溶液として硝酸銀、硝
酸銅、硝酸亜鉛、硝酸ニッケル、モリブデン酸アンモニ
ウムの各水溶液を用いた。
【００１１】
【参考例２】 アルミノケイ酸塩系無機粉体の調製 １１０℃で１６時間加熱乾燥したＹ型ゼオライト粉末
（Na2O・ Al2O3・4.８SiO2 ,SiO2率６４％，平均粒径0.
７μｍ）、無定形アルミノケイ酸塩粉末（1.８Na 2O・ A
l2O3・9.２SiO2 ,SiO2率７２％，平均粒径3.２μｍ）お
よびクリノプチロライト粉末（Na2O, K2O)・ Al2O3・10
SiO2 ,SiO2率７６％，平均粒径0.０５mm）に水を加えて
1.３Ｌのスラリーとし、その後攪拌して脱気し、さらに
適量の0.５Ｎ硝酸溶液と水を加えてｐＨを7.０に調整し
全容1.８Ｌとした。次にイオン交換のために硝酸銀、硝
酸銅、硝酸ニッケル、硝酸水銀、硝酸カドミウム、硝酸
鉛、硫酸すず、硫酸パラジウム、硫酸ロジウムの水溶液
を加えて全容4.８Ｌとして、このスラリーを２５〜４８
℃に保持し２４時間攪拌平衡状態に保持した。終了後、
アルミノケイ酸塩相を濾過し温水にてアルミノケイ酸塩
相中の過剰のイオンがなくなるまで水洗した。次に試料
を１１０℃で加熱、乾燥、粉砕し、無機粉末を得た。得
られた試料のデータを表１に示す。
（Na2O・ Al2O3・4.８SiO2 ,SiO2率６４％，平均粒径0.
７μｍ）、無定形アルミノケイ酸塩粉末（1.８Na 2O・ A
l2O3・9.２SiO2 ,SiO2率７２％，平均粒径3.２μｍ）お
よびクリノプチロライト粉末（Na2O, K2O)・ Al2O3・10
SiO2 ,SiO2率７６％，平均粒径0.０５mm）に水を加えて
1.３Ｌのスラリーとし、その後攪拌して脱気し、さらに
適量の0.５Ｎ硝酸溶液と水を加えてｐＨを7.０に調整し
全容1.８Ｌとした。次にイオン交換のために硝酸銀、硝
酸銅、硝酸ニッケル、硝酸水銀、硝酸カドミウム、硝酸
鉛、硫酸すず、硫酸パラジウム、硫酸ロジウムの水溶液
を加えて全容4.８Ｌとして、このスラリーを２５〜４８
℃に保持し２４時間攪拌平衡状態に保持した。終了後、
アルミノケイ酸塩相を濾過し温水にてアルミノケイ酸塩
相中の過剰のイオンがなくなるまで水洗した。次に試料
を１１０℃で加熱、乾燥、粉砕し、無機粉末を得た。得
られた試料のデータを表１に示す。
【実施例及び比較例】 耐蝕性モルタル供試体の作成 セメント１００重量部、砂２００重量部、水５０重量部
からなるモルタル成分に、参考例１及び２で調製した無
機粉末を所定量加え、モルタルミキサーにより充分混合
攪拌した後、４×４×１０cmに成型しモルタル供試体を
作成した。比較例として同様の方法にて、無機粉末無添
加のものと平均粒径が0.１mmの銅粉と含硫黄系抗菌剤
（東京ファインケミカル製ファインサイドＡ−３）を添
加した供試体も作成した。各供試体のデータを表２に示
す。
からなるモルタル成分に、参考例１及び２で調製した無
機粉末を所定量加え、モルタルミキサーにより充分混合
攪拌した後、４×４×１０cmに成型しモルタル供試体を
作成した。比較例として同様の方法にて、無機粉末無添
加のものと平均粒径が0.１mmの銅粉と含硫黄系抗菌剤
（東京ファインケミカル製ファインサイドＡ−３）を添
加した供試体も作成した。各供試体のデータを表２に示
す。
【試験例】 モルタル供試体の腐蝕性試験 このようにして得られたモルタル供試体を、下水処理場
の汚泥施設の気中部に暴露した。施行後、６か月間汚泥
に暴露した後、端部４cmを切出し、供試体の表面を１×
１mmメッシュに分割した際の欠損面積を目視により測定
することにより、劣化状態を調べた。欠損面積の結果を
表２に示す。同時に供試体の表面を歯磨き用ブラシで滅
菌済みリン酸緩衝液５０mlにて洗浄し、その洗浄液中の
菌数を固体ＯＮＭ培地を用いて計測した。なお培養は３
０℃で１０日間とした。固体ＯＮＭ培地は、下記の組成
のものを使用した。 （NH4)2SO4 2.０ｇ CaCl2・2H2O 0.３ｇ FeSO4 ・7H2O 0.０１ｇ KH2PO4 4.０ｇ MgSO4・7H2O 0.３ｇ Na2S2O3・5H2O ４0.０ｇ ブロムフェノールブルー 0.００２ｇ 寒天 １5.０ｇ 精製水 １Ｌ
の汚泥施設の気中部に暴露した。施行後、６か月間汚泥
に暴露した後、端部４cmを切出し、供試体の表面を１×
１mmメッシュに分割した際の欠損面積を目視により測定
することにより、劣化状態を調べた。欠損面積の結果を
表２に示す。同時に供試体の表面を歯磨き用ブラシで滅
菌済みリン酸緩衝液５０mlにて洗浄し、その洗浄液中の
菌数を固体ＯＮＭ培地を用いて計測した。なお培養は３
０℃で１０日間とした。固体ＯＮＭ培地は、下記の組成
のものを使用した。 （NH4)2SO4 2.０ｇ CaCl2・2H2O 0.３ｇ FeSO4 ・7H2O 0.０１ｇ KH2PO4 4.０ｇ MgSO4・7H2O 0.３ｇ Na2S2O3・5H2O ４0.０ｇ ブロムフェノールブルー 0.００２ｇ 寒天 １5.０ｇ 精製水 １Ｌ
【００１２】
【表１】 ──────────────────────────────── サンプル 無 機 粉 体 無機粉末中の抗菌性金属 Ｎｏ． イオン存在量（％） １ 含水酸化チタン Ａｇ 5.０，Ｚｎ 5.０ ２ 〃 Ｎｉ 7.０, Ｍｏ 1.０ ３ リン酸ジルコニウム Ｎｉ 3.０ ４ 〃 Ａｇ 2.０，Ｃｕ 1.０ ５ Ｙ型ゼオライト Ａｇ 2.５，Ｎｉ 6.５ ６ 〃 Ｈｇ 0.５，Ｃｄ 9.５ ７ 〃 Ｒｈ 1.５，Ｃｄ 8.５ ８ 無定形アルミノケイ酸塩 Ｃｕ 16.５，Ｐｂ 2.５ ９ クリノプチロライト Ａｇ 0.７ １０ 〃 Ｃｏ 5.８１１ 〃 Ｓｎ 2.５，Ｐｄ 3.０
【００１３】
【表２】 ───────────────────────────────── Ｎｏ． 無機粉末 無機粉末 欠損面積 菌 数 Ｎｏ． 添加率(%) (mm2) （個/cm2) 実施例１ １ 3.０ ０ １０以下 実施例２ １ １0.０ ０ １０以下 実施例３ ２ 3.０ ０ １０以下 実施例４ ３ 5.０ ０ １０以下 実施例５ ４ 5.０ ０ １０以下 実施例６ ５ 2.５ ０ １０以下 実施例７ ５ 5.０ ０ １０以下 実施例８ ５ 7.５ ０ １０以下 実施例９ ６ ２0.０ ０ ５×１０ 実施例１０ ７ ５0.０ ０ １０以下 実施例１１ ８ 1.０ ０ ７×１０ 実施例１２ ９ 5.０ ０ １０以下 実施例１３ ９ １0.０ ０ １０以下 実施例１４ ９ １5.０ ０ １０以下 実施例１５ １０ 4.０ ０ １０以下 実施例１６ １１ ２5.０ ０ １０以下 比較例１ 無添加 0.０ ２１０ ６×１０4 比較例２ 銅 粉 3.０ ８５ ８×１０3 比較例３ Ａ−３ 3.０ １２５ １×１０3
───────────────────────────────────────────────────── フロントページの続き (72)発明者 栗原 靖夫 愛知県名古屋市瑞穂区豊岡通３丁目35番地 (72)発明者 中山 一郎 愛知県知多市西巽が丘２丁目９番５号
Claims (2)
- 【請求項１】 コンクリート、モルタル又は高分子材料
よりなるヒューム管において、抗菌性金属イオンを担持
した無機粉末を含有することを特徴とする耐蝕性ヒュー
ム管。 - 【請求項２】 抗菌性金属イオンが銀、銅、亜鉛、ニッ
ケル及びコバルトから成る群より選ばれた１種または２
種以上の金属イオンである請求項１記載の耐蝕性ヒュー
ム管。