JPH11267253A - Golf club head - Google Patents
Golf club headInfo
- Publication number
- JPH11267253A JPH11267253A JP10092284A JP9228498A JPH11267253A JP H11267253 A JPH11267253 A JP H11267253A JP 10092284 A JP10092284 A JP 10092284A JP 9228498 A JP9228498 A JP 9228498A JP H11267253 A JPH11267253 A JP H11267253A
- Authority
- JP
- Japan
- Prior art keywords
- hard material
- sole
- golf club
- face
- club head
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】
【課題】 ヘッド本体のフェイス面及び／またはソール
面に、ビッカース硬度１０００以上の金属化合物を主成
分とするフェイス用硬質物質及び／またはソール用硬質
物質を装着し、前記フェイス用硬質物質が有する反発性
能や耐久性、及び／または前記ソール用硬質物質が有す
る耐久性を半永久的に発揮させることにより、飛距離を
増大させ、打球時の衝撃による傷や摩耗等に対する耐久
性を向上させたゴルフクラブヘッドを提供する。
【解決手段】 ステンレススチール製のヘッド本体２ａ
のフェイス面３ａ及びソール面６ａに、Ｓｉ3 Ｎ4 を主
成分とする厚みが３．５ｍｍの板（比重約３．２、ビッ
カース硬度３０００程度）より成るフェイス用硬質物質
５ａ及びＴａＮを主成分とする厚みが２．０ｍｍの湾曲
板（比重約１３．８、ビッカース硬度２０００程度）よ
り成るソール用硬質物質８ａを、接着剤を用いて装着し
たゴルフクラブヘッドとした。
(57) Abstract: A hard material for a face and / or a hard material for a sole mainly composed of a metal compound having a Vickers hardness of 1000 or more is mounted on a face surface and / or a sole surface of a head main body. The semi-permanent display of the resilience and durability of the hard material for the sole and / or the semi-permanent durability of the hard material for the sole increases the flight distance and the durability against scratches and abrasion caused by impact when hitting a ball. The present invention provides a golf club head having an improved golf club head. SOLUTION: A head body 2a made of stainless steel is provided.
The face hard material 5a and TaN made of a 3.5 mm-thick plate (specific gravity: about 3.2, Vickers hardness: about 3000) mainly composed of Si 3 N 4 are provided on the face surface 3a and the sole surface 6a. The golf club head was provided with a hard material 8a for sole made of a curved plate having a thickness of 2.0 mm (specific gravity of about 13.8, Vickers hardness of about 2000) using an adhesive.
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、ゴルフクラブヘッ
ドに関するものであり、更に詳細には、フェイス面及び
／またはソール面に、フェイス用硬質物質及び／または
ソール用硬質物質を装着したゴルフクラブヘッドに関す
るものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a golf club head, and more particularly to a golf club head having a face hard material and / or a hard hard material for a sole mounted on a face surface and / or a sole surface. It is about.
【０００２】[0002]
【従来の技術】従来より、ゴルフクラブヘッドの表面被
覆方法は塗装やめっきが主流であるが、これらの方法
は、ボールとの衝突による傷つき、芝や砂との摩耗に対
する耐久性が十分ではなく、短期間の使用でフェイス面
やソール面に傷や摩耗が発生していた。近年、このよう
な傷つきや摩耗に対する耐久性の改善や飛距離の一層の
向上を目的として、ヘッド表面に物理蒸着法又は化学蒸
着法により硬質物質の皮膜を被覆したゴルフクラブヘッ
ドが知られている。2. Description of the Related Art Conventionally, coating and plating are mainly used as a method of coating the surface of a golf club head. However, these methods are not sufficiently durable against damage due to collision with a ball and abrasion with turf or sand. For a short period of time, the face and sole surfaces were scratched and worn. In recent years, golf club heads in which a hard material film is coated on the head surface by a physical vapor deposition method or a chemical vapor deposition method for the purpose of improving durability against such scratches and wear and further improving the flight distance have been known. .
【０００３】例えば実開平３―７６１号には、金属材料
からなるゴルフクラブヘッドの周面に周期律表第６族又
は第５族に属する元素の合金又は化合物をイオンプレー
ティングして被覆層を形成したゴルフクラブヘッドが開
示されている。For example, Japanese Utility Model Application Laid-Open No. 3-761 discloses that a coating layer is formed by ion plating an alloy or compound of an element belonging to Group 6 or 5 of the periodic table on the peripheral surface of a golf club head made of a metal material. A formed golf club head is disclosed.
【０００４】又、登録実用新案第３０２８７２６号に
は、金属素材から形成されたゴルフクラブヘッドの表面
に、湿式めっきによって皮膜層を形成し、該皮膜層の上
に金属化合物皮膜層を蒸着やイオンプレーティング等の
物理蒸着法により形成したゴルフクラブヘッドが開示さ
れている。[0004] Japanese Utility Model Registration No. 3028726 discloses that a coating layer is formed by wet plating on the surface of a golf club head formed of a metal material, and a metal compound coating layer is formed on the coating layer by vapor deposition or ion deposition. A golf club head formed by physical vapor deposition such as plating is disclosed.
【０００５】[0005]
【発明が解決しようとする課題】しかしながら、前記実
開平３―７６１号に記載されたゴルフクラブヘッドは、
イオンプレーティングにより周期律表第６族又は第５族
に属する元素の合金又は化合物の原子イオンを直接、ゴ
ルフクラブヘッドの周面に打ち込んで被覆層を形成して
なるゴルフクラブヘッドであるから、一般的な塗装や、
めっきに比べて耐久性は改善されているものの、前記被
覆層の厚みが１０μｍ以下と非常に薄いために、繰り返
し打球することにより芝や砂との摩耗で前記被覆層が早
く失われてしまい、前記被覆層が有する反発性能や耐久
性が発揮されなくなってしまうという問題があった。However, the golf club head described in Japanese Utility Model Application Laid-Open No. 3-761 has the following problems.
Since the golf club head is formed by directly implanting atomic ions of an alloy or compound of an element belonging to Group 6 or 5 of the periodic table into the peripheral surface of the golf club head by ion plating to form a coating layer, General painting,
Although the durability is improved as compared with plating, the thickness of the coating layer is very thin, 10 μm or less, so that the coating layer is quickly lost due to wear with turf and sand by repeatedly hitting a ball, There is a problem that the resilience performance and durability of the coating layer are not exhibited.
【０００６】又、登録実用新案第３０２８７２６号記載
のゴルフクラブヘッドにおいても、金属化合物皮膜層の
厚みが非常に薄いために、前述した実開平３―７６１号
に記載されたゴルフクラブヘッドと同様の問題があると
同時に、前記登録実用新案第３０２８７２６号記載のゴ
ルフクラブヘッドは、金属素材からなるゴルフクラブヘ
ッドと物理蒸着法により形成された金属化合物皮膜層と
の間に、湿式めっき皮膜層を形成しているが、めっきに
よって形成される皮膜は電気的な吸引力により前記金属
素材の表面に付着しているに過ぎないため密着性が悪
く、繰り返し打球することによる衝撃で前記めっき皮膜
層が前記金属化合物皮膜層を伴って前記金属素材から容
易に剥離してしまうという問題があった。Also, in the golf club head described in Japanese Utility Model No. 3028726, the thickness of the metal compound film layer is extremely small, so that the same golf club head as that described in Japanese Utility Model Laid-Open No. 3-761 is used. At the same time, the golf club head described in the registered utility model No. 3028726 has a wet plating film layer formed between a golf club head made of a metal material and a metal compound film layer formed by physical vapor deposition. However, the film formed by plating has poor adhesion because it is only attached to the surface of the metal material due to the electric attraction, and the plating film layer is formed by the impact of repeated hitting. There is a problem that the metal compound film layer is easily separated from the metal material with the metal compound film layer.
【０００７】[0007]
【課題を解決するための手段】本発明は、前記問題点を
解決し、飛距離を増大させ、打球時の衝撃による傷や摩
耗等に対する耐久性を向上させたゴルフクラブヘッドを
提供しようとするものである。SUMMARY OF THE INVENTION The present invention has been made to solve the above-mentioned problems, and has an object to provide a golf club head having an increased flight distance and improved durability against scratches, abrasion, and the like caused by impact upon hitting a ball. Things.
【０００８】前記目的を達成するために、請求項１の発
明は、ヘッド本体のフェイス面及び／またはソール面
に、ビッカース硬度１０００以上の金属化合物を主成分
とするフェイス用硬質物質及び／またはソール用硬質物
質を装着したことを特徴とするゴルフクラブヘッドであ
る。[0008] In order to achieve the above object, the present invention is directed to a face hard material and / or sole containing a metal compound having a Vickers hardness of 1000 or more as a main component on a face surface and / or a sole surface of a head body. The golf club head is equipped with a hard material for use.
【０００９】請求項２の発明は、請求項１のゴルフクラ
ブヘッドにおいて、前記フェイス用硬質物質及び前記ソ
ール用硬質物質は、Ａｌ化合物、Ｔｉ化合物、Ｔａ化合
物、Ｃｒ化合物、Ｚｒ化合物、Ｎｂ化合物、Ｈｆ化合
物、Ｗ化合物、Ｓｉ化合物、Ｍｏ化合物、Ｖ化合物、Ｂ
化合物の中から、少なくとも１種類以上の金属化合物を
主成分とするゴルフクラブヘッドである。According to a second aspect of the present invention, in the golf club head of the first aspect, the hard material for the face and the hard material for the sole are an Al compound, a Ti compound, a Ta compound, a Cr compound, a Zr compound, a Nb compound, Hf compound, W compound, Si compound, Mo compound, V compound, B
It is a golf club head mainly containing at least one or more metal compounds among the compounds.
【００１０】請求項３の発明は、請求項１又は２のゴル
フクラブヘッドにおいて、前記フェイス用硬質物質は、
比重が８．０未満で、且つ厚みが１．５〜４．０ｍｍで
あり、前記ソール用硬質物質は、比重が８．０以上で、
且つ厚みが１．５〜４．０ｍｍであるゴルフクラブヘッ
ドである。According to a third aspect of the present invention, in the golf club head according to the first or second aspect, the hard material for the face comprises:
The specific gravity is less than 8.0, the thickness is 1.5 to 4.0 mm, and the hard material for sole has a specific gravity of 8.0 or more,
A golf club head having a thickness of 1.5 to 4.0 mm.
【００１１】[0011]
【発明の実施の形態】以下、本発明の実施の形態を図面
に基づいて詳細に説明する。図１は、本発明の第1 実施
例のゴルフクラブヘッド１ａを示した正面図、図２はそ
の底面図、図３はそのＡ−Ａ線切断断面図である。図１
及び図２に示すように、ゴルフクラブヘッド１ａは、フ
ェイス面３ａとソール面６ａを含むヘッド本体２ａと、
前記フェイス面３ａに装着されるビッカース硬度１００
０以上の金属化合物を主成分とするフェイス用硬質物質
５ａと、前記ソール面６ａに装着されるビッカース硬度
１０００以上の金属化合物を主成分とするソール用硬質
物質８ａとから構成されている。すなわち、図３に示す
ように、ゴルフクラブヘッド１ａは、ヘッド本体２ａの
フェイス面３ａに形成されているフェイス凹部４ａに前
記フェイス用硬質物質５ａが、同様に、ヘッド本体２ａ
のソール面６ａに形成されているソール凹部７ａに前記
ソール用硬質物質８ａが、それぞれ装着されている。Embodiments of the present invention will be described below in detail with reference to the drawings. FIG. 1 is a front view showing a golf club head 1a according to a first embodiment of the present invention, FIG. 2 is a bottom view thereof, and FIG. 3 is a sectional view taken along line AA of FIG. FIG.
As shown in FIG. 2, the golf club head 1a includes a head body 2a including a face surface 3a and a sole surface 6a.
Vickers hardness 100 mounted on the face surface 3a
It is composed of a face hard material 5a containing 0 or more metal compounds as a main component, and a sole hard material 8a containing a metal compound having a Vickers hardness of 1000 or more attached to the sole surface 6a. That is, as shown in FIG. 3, the golf club head 1a has the face hard material 5a in the face recess 4a formed in the face surface 3a of the head body 2a, and the head body 2a.
The sole hard material 8a is mounted on a sole concave portion 7a formed on the sole surface 6a.
【００１２】本実施例では、ヘッド本体２ａをステンレ
ススチールにより形成し、フェイス用硬質物質５ａをＳ
ｉ3 Ｎ4 を主成分とする厚みが３．５ｍｍの板（比重約
３．２、ビッカース硬度３０００程度）により形成し、
ソール用硬質物質８ａをＴａＮを主成分とする厚みが
２．０ｍｍの湾曲板（比重約１３．８、ビッカース硬度
２０００程度）により形成してあり、前記フェイス用硬
質物質５ａと前記ソール用硬質物質８ａは、前記ヘッド
本体２ａのフェイス凹部４ａとソール凹部７ａに、それ
ぞれ接着剤を用いた接着によって装着されている。In this embodiment, the head main body 2a is formed of stainless steel, and the hard material 5a for the face is made of S
It is formed of a 3.5 mm thick plate (specific gravity of about 3.2, Vickers hardness of about 3000) containing i 3 N 4 as a main component,
The hard material 8a for sole is formed of a curved plate (specific gravity of about 13.8, Vickers hardness of about 2000) having TaN as a main component and having a thickness of 2.0 mm, and the hard material for face 5a and the hard material for sole are formed. Reference numeral 8a is attached to the face recess 4a and the sole recess 7a of the head body 2a by bonding using an adhesive.
【００１３】故に、ゴルフクラブヘッド１ａは、従来の
塗装やめっき、或いは物理蒸着法又は化学蒸着法により
硬質物質の皮膜を被覆したゴルフクラブヘッドに比べ
て、繰り返し打球することにより芝や砂との摩耗でフェ
イス用硬質物質５ａ及びソール用硬質物質８ａが消失し
てしまうことがなく、前記フェイス用硬質物質５ａが有
する反発性能や耐久性、及び前記ソール用硬質物質８ａ
が有する耐久性を半永久的に発揮することができる。ま
た、前記フェイス用硬質物質５ａ及び前記ソール用硬質
物質８ａは、接着剤によってヘッド本体２ａに接着され
ているので、繰り返し打球することによる衝撃で容易に
剥離することがない。更にまた、フェイス用硬質物質５
ａを比重約３．２の、Ｓｉ3 Ｎ4 を主成分とする厚みが
３．５ｍｍの板により形成し、ソール用硬質物質８ａを
比重約１３．８の、ＴａＮを主成分とする厚みが２．０
ｍｍの湾曲板により形成してあるので、重心位置が低
く、且つ重心深度が深い、打ちやすいゴルフクラブヘッ
ドになっている。[0013] Therefore, the golf club head 1a is made of a golf club head that is hit with turf or sand by repeatedly hitting a ball, as compared with a golf club head coated with a hard material film by conventional painting, plating, or physical vapor deposition or chemical vapor deposition. The hard material for face 5a and the hard material for sole 8a do not disappear due to abrasion, and the resilience performance and durability of the hard material for face 5a and the hard material for sole 8a
Can exhibit semi-permanent durability. Since the hard material for face 5a and the hard material for sole 8a are adhered to the head main body 2a with an adhesive, they are not easily separated by the impact of repeated hitting. Furthermore, a hard material for face 5
a is formed of a plate having a specific gravity of about 3.2 and a thickness of 3.5 mm mainly composed of Si 3 N 4 , and the hard material for sole 8 a having a specific gravity of about 13.8 and a thickness mainly composed of TaN is formed. 2.0
Since the golf club head is formed of a curved plate having a diameter of mm, the position of the center of gravity is low and the depth of the center of gravity is deep, and the golf club head is easy to hit.
【００１４】尚、本発明は前記第１実施例に限定される
ものではなく、様々な変形実施が可能である。例えば、
前記第１実施例ではフェイス用硬質物質５ａとソール用
硬質物質８ａを両方装着したゴルフクラブヘッドであっ
たが、どちらか一方のみを装着したゴルフクラブヘッド
でもよい。The present invention is not limited to the first embodiment, and various modifications can be made. For example,
In the first embodiment, the golf club head is equipped with both the hard material 5a for the face and the hard material 8a for the sole. However, a golf club head equipped with only one of them may be used.
【００１５】また、ヘッド本体のフェイス面及び／また
はソール面に、フェイス用硬質物質及び／またはソール
用硬質物質を装着する方法としては、接着剤を用いた接
着以外に、圧入、溶接、ろう付け、ビス止め等の方法
を、後述するヘッド本体の素材に応じて使用することが
できる。As a method of mounting a hard material for the face and / or a hard material for the sole on the face surface and / or the sole surface of the head main body, in addition to bonding using an adhesive, press fitting, welding, brazing, and the like. A method such as screwing can be used depending on the material of the head body described later.
【００１６】ヘッド本体の素材については、ステンレス
スチールに限定されるものではなく、チタン、チタン合
金、アルミ合金、軟鉄等の金属素材の他、木材、ＦＲ
Ｐ、セラミック、サーメット等の素材を使用することが
できる。The material of the head body is not limited to stainless steel, but may be wood, FR, etc., in addition to metal materials such as titanium, titanium alloy, aluminum alloy and soft iron.
Materials such as P, ceramic, and cermet can be used.
【００１７】また、ヘッド本体の構造については、前記
第１実施例では、ヘッド本体２ａのフェイス凹部４ａの
底面にフェイス用硬質物質５ａの背面全体が接する構造
としているが、その他、図４に示す第２実施例のよう
に、フェイス凹部４ｂの底面のうち、内周縁部９を残し
て他の部分を貫通させた貫通穴構造とすることもできる
し、図５に示す第３実施例のように、中空部１０を有す
る中空構造とすることもできる。尚、図４及び図５に示
す符号において、前記第１実施例と対応する部分に対し
ては同一数字を用い、図４ではこれに添字ｂを、図５で
はこれに添字ｃを、それぞれ付してある。In the first embodiment, the structure of the head body is such that the entire back surface of the face hard material 5a is in contact with the bottom surface of the face recess 4a of the head body 2a. As in the second embodiment, the bottom surface of the face concave portion 4b may have a through-hole structure in which the inner peripheral edge portion 9 is left and another portion is penetrated, as in the third embodiment shown in FIG. Alternatively, a hollow structure having a hollow portion 10 may be employed. In the reference numerals shown in FIGS. 4 and 5, the same numerals are used for the parts corresponding to those of the first embodiment, and in FIG. 4, the suffix b is added thereto, and in FIG. 5, the suffix c is added thereto. I have.
【００１８】更にまた、フェイス用硬質物質及びソール
用硬質物質を形成する主成分としての金属化合物は、Ｓ
ｉ3 Ｎ4 及びＴａＮに限定されるものではなく、ビッカ
ース硬度１０００以上の種々の金属化合物、例えば、Ａ
ｌＮ、Ａｌ2 Ｏ3 等のＡｌ化合物、ＴｉＮ、ＴｉＣ、Ｔ
ｉＣＮ、ＴｉＡｌＮ、ＴｉＢ等のＴｉ化合物、ＴａＣ、
ＴａＢ等のＴａ化合物、ＣｒＮ、ＣｒＣ、ＣｒＢ等のＣ
ｒ化合物、ＺｒＮ、ＺｒＣ、ＺｒＢ等のＺｒ化合物、Ｎ
ｂＮ、ＮｂＣ、ＮｂＢ等のＮｂ化合物、ＨｆＮ、Ｈｆ
Ｃ、ＨｆＢ等のＨｆ化合物、ＷＮ、ＷＣ、ＷＢ等のＷ化
合物、ＳｉＣ等のＳｉ化合物、ＭｏＢ等のＭｏ化合物、
ＶＮ、ＶＣ、ＶＢ等のＶ化合物、ＢＮ、ＢＣ、ＭｎＢ、
ＣｏＢ等のＢ化合物の中から、少なくとも１種類以上の
金属化合物を主成分とすることができ、それぞれの色相
や比重等を考慮して自由に選択することができる。尚、
ビッカース硬度が１０００未満の金属化合物では、打球
時の反発性能や傷つき、摩耗等に対する耐久性が十分な
ものにならないため、好ましくない。前記フェイス用硬
質物質及び前記ソール用硬質物質を形成する主成分とし
ての金属化合物の一例を表１に示す。Further, the metal compound as a main component forming the hard material for the face and the hard material for the sole is S
It is not limited to i 3 N 4 and TaN, and various metal compounds having a Vickers hardness of 1000 or more, for example, A
1N, Al compounds such as Al 2 O 3 , TiN, TiC, T
Ti compounds such as iCN, TiAlN and TiB, TaC,
Ta compound such as TaB, C such as CrN, CrC, CrB
r compound, Zr compound such as ZrN, ZrC, ZrB, N
Nb compounds such as bN, NbC, NbB, HfN, Hf
C, Hf compounds such as HfB, W compounds such as WN, WC, WB, Si compounds such as SiC, Mo compounds such as MoB;
V compounds such as VN, VC, VB, BN, BC, MnB,
At least one or more metal compounds can be used as a main component from B compounds such as CoB, and can be freely selected in consideration of their respective hues and specific gravities. still,
A metal compound having a Vickers hardness of less than 1000 is not preferable because resilience performance at the time of hitting the ball, durability against damage, abrasion and the like is not sufficient. Table 1 shows an example of a metal compound as a main component forming the hard material for the face and the hard material for the sole.
【００１９】[0019]
【表１】 [Table 1]
【００２０】尚、前記フェイス用硬質物質は、比重が
８．０未満で、且つ厚みが１．５〜４．０ｍｍであるこ
とが望ましい。比重が８．０以上になると前記フェイス
用硬質物質は重くなるため、重心位置が高く、且つ重心
深度が浅い、打ち難いゴルフクラブヘッドになってしま
う。また、厚みが１．５ｍｍより薄いと強度が弱くな
り、４．０ｍｍより厚いと重量の重いゴルフクラブヘッ
ドになってしまう。Preferably, the hard material for a face has a specific gravity of less than 8.0 and a thickness of 1.5 to 4.0 mm. If the specific gravity is 8.0 or more, the hard material for the face becomes heavier, so that the golf club head is difficult to hit because the center of gravity is high and the depth of the center of gravity is shallow. On the other hand, if the thickness is less than 1.5 mm, the strength becomes weak, and if it is more than 4.0 mm, the golf club head becomes heavy.
【００２１】同様に、前記ソール用硬質物質は、比重が
８．０以上で、且つ厚みが１．５〜４．０ｍｍであるこ
とが望ましい。比重が８．０未満になると前記ソール用
硬質物質は軽くなるため、重心位置が高く、且つ重心深
度が浅い、打ち難いゴルフクラブヘッドになってしま
う。また、厚みが１．５ｍｍより薄いと強度が弱くな
り、４．０ｍｍより厚いと比重は小さいものの、体積が
大きくなるために、結果として重量の重いゴルフクラブ
ヘッドになってしまう。Similarly, the hard material for sole preferably has a specific gravity of 8.0 or more and a thickness of 1.5 to 4.0 mm. When the specific gravity is less than 8.0, the hard material for sole becomes lighter, so that the golf club head has a high center of gravity and a shallow depth of the center of gravity and is difficult to hit. When the thickness is less than 1.5 mm, the strength is weak. When the thickness is more than 4.0 mm, the specific gravity is small, but the volume is large, resulting in a heavy golf club head.
【００２２】[0022]
【発明の効果】以上説明したように本発明に係るゴルフ
クラブヘッドは、ヘッド本体のフェイス面及び／または
ソール面に、ビッカース硬度１０００以上の金属化合物
を主成分とするフェイス用硬質物質及び／またはソール
用硬質物質を装着したから、従来の塗装やめっき、或い
は物理蒸着法又は化学蒸着法により硬質物質の皮膜を被
覆したゴルフクラブヘッドに比べて、繰り返し打球する
ことにより芝や砂との摩耗でフェイス用硬質物質及び／
またはソール用硬質物質が消失してしまうことがなく、
前記フェイス用硬質物質が有する反発性能や耐久性及び
／または前記ソール用硬質物質が有する耐久性を半永久
的に発揮することができる。また、前記フェイス用硬質
物質及び／または前記ソール用硬質物質は、接着、圧
入、溶接、ろう付け、ビス止め等によって装着したか
ら、繰り返し打球することによる衝撃で容易に剥離する
ことがない。As described above, in the golf club head according to the present invention, a face hard material and / or a metal compound having a Vickers hardness of 1000 or more as a main component is formed on the face surface and / or sole surface of the head body. Wearing a hard material for soles, compared to a conventional golf club head coated with a hard material film by painting, plating, or physical vapor deposition or chemical vapor deposition, wears the grass and sand by repeatedly hitting the ball. Hard material for face and / or
Or without the hard material for sole disappears,
The resilience and durability of the face hard material and / or the durability of the sole hard material can be exhibited semipermanently. In addition, since the hard material for the face and / or the hard material for the sole is attached by bonding, press fitting, welding, brazing, screwing, or the like, the hard material for the face does not easily peel off due to the impact of repeated hitting.
【００２３】そして、前記フェイス用硬質物質及び／ま
たは前記ソール用硬質物質は、ビッカース硬度１０００
以上のＡｌＮ、Ａｌ2 Ｏ3 等のＡｌ化合物、ＴｉＮ、Ｔ
ｉＣ、ＴｉＣＮ、ＴｉＡｌＮ、ＴｉＢ等のＴｉ化合物、
ＴａＮ、ＴａＣ、ＴａＢ等のＴａ化合物、ＣｒＮ、Ｃｒ
Ｃ、ＣｒＢ等のＣｒ化合物、ＺｒＮ、ＺｒＣ、ＺｒＢ等
のＺｒ化合物、ＮｂＮ、ＮｂＣ、ＮｂＢ等のＮｂ化合
物、ＨｆＮ、ＨｆＣ、ＨｆＢ等のＨｆ化合物、ＷＮ、Ｗ
Ｃ、ＷＢ等のＷ化合物、Ｓｉ3 Ｎ4 、ＳｉＣ等のＳｉ化
合物、ＭｏＢ等のＭｏ化合物、ＶＮ、ＶＣ、ＶＢ等のＶ
化合物、ＢＮ、ＢＣ、ＭｎＢ、ＣｏＢ等のＢ化合物の中
から、少なくとも１種類以上の金属化合物を主成分とす
ることによって、飛距離の大きい、傷つきや摩耗等に対
する耐久性に優れた、多種多様の色相、輝度のゴルフク
ラブヘッドとなる。The hard material for the face and / or the hard material for the sole has a Vickers hardness of 1000.
The above Al compounds such as AlN and Al 2 O 3 , TiN, T
Ti compounds such as iC, TiCN, TiAlN, TiB,
Ta compounds such as TaN, TaC and TaB, CrN, Cr
Cr compounds such as C and CrB; Zr compounds such as ZrN, ZrC and ZrB; Nb compounds such as NbN, NbC and NbB; Hf compounds such as HfN, HfC and HfB;
W compounds such as C and WB, Si compounds such as Si 3 N 4 and SiC, Mo compounds such as MoB, and V compounds such as VN, VC and VB
Compounds, BN, BC, MnB, CoB and other B compounds, as a main component, at least one or more metal compounds, a long flight distance, excellent durability against scratches, abrasion, etc., a wide variety Hue and brightness of the golf club head.
【００２４】更に、前記フェイス用硬質物質は、比重が
８．０未満で、且つ厚みが１．５〜４．０ｍｍであり、
前記ソール用硬質物質は、比重が８．０以上で、且つ厚
みが１．５〜４．０ｍｍであることによって、重心の位
置が低くて深度が深い、且つ適切な強度と重量を有す
る、打ちやすいゴルフクラブヘッドとなる。Further, the hard substance for a face has a specific gravity of less than 8.0 and a thickness of 1.5 to 4.0 mm,
The hard material for sole has a specific gravity of 8.0 or more and a thickness of 1.5 to 4.0 mm, so that the center of gravity is low and the depth is deep, and has a suitable strength and weight. An easy golf club head.
【図１】本発明の第１実施例のゴルフクラブヘッドを示
す正面図である。FIG. 1 is a front view showing a golf club head according to a first embodiment of the present invention.
【図２】本発明の第１実施例のゴルフクラブヘッドを示
す底面図である。FIG. 2 is a bottom view showing the golf club head according to the first embodiment of the present invention.
【図３】図１のＡ−Ａ線断面図である。FIG. 3 is a sectional view taken along line AA of FIG. 1;
【図４】本発明の第２実施例のゴルフクラブヘッドを示
す断面図である。FIG. 4 is a sectional view showing a golf club head according to a second embodiment of the present invention.
【図５】本発明の第３実施例のゴルフクラブヘッドを示
す断面図である。FIG. 5 is a sectional view showing a golf club head according to a third embodiment of the present invention.
１ａ ゴルフクラブヘッド １ｂ ゴルフクラブヘッド １ｃ ゴルフクラブヘッド ２ａ ヘッド本体 ２ｂ ヘッド本体 ２ｃ ヘッド本体 ３ａ フェイス面 ３ｂ フェイス面 ３ｃ フェイス面 ４ａ フェイス凹部 ４ｂ フェイス凹部 ４ｃ フェイス凹部 ５ａ フェイス用硬質物質 ５ｂ フェイス用硬質物質 ５ｃ フェイス用硬質物質 ６ａ ソール面 ６ｂ ソール面 ６ｃ ソール面 ７ａ ソール凹部 ７ｂ ソール凹部 ７ｃ ソール凹部 ８ａ ソール用硬質物質 ８ｂ ソール用硬質物質 ８ｃ ソール用硬質物質 ９ 内周縁部 １０ 中空部 1a Golf club head 1b Golf club head 1c Golf club head 2a Head body 2b Head body 2c Head body 3a Face surface 3b Face surface 3c Face surface 4a Face recess 4b Face recess 4c Face recess 5a Hard material for face 5b Hard material for face 5c Hard material for face 6a Sole surface 6b Sole surface 6c Sole surface 7a Sole recess 7b Sole recess 7c Sole recess 8a Sole hard material 8b Sole hard material 8c Sole hard material 9 Inner peripheral edge 10 Hollow portion
───────────────────────────────────────────────────── フロントページの続き (72)発明者 相澤 克幸 岐阜県養老郡養老町高田3877−８ 美津濃 株式会社養老工場内 (72)発明者 大田原 孝清 大阪府大阪市中央区平野町１丁目８番７号 小池産業株式会社内 (72)発明者 山浦 重信 東京都中央区日本橋室町２丁目１番１号 三井金属鉱業株式会社内 ──────────────────────────────────────────────────続 き Continuing from the front page (72) Katsuyuki Aizawa, 3877-8 Takada, Yoro-cho, Yoro-gun, Gifu Prefecture Mizuno Co., Ltd. Yoro Plant Co., Ltd. (72) Takayoshi Kiyoshi Ohtahara 1-8-8 Hirano-cho, Chuo-ku, Osaka-shi, Osaka No. 7 Inside Koike Sangyo Co., Ltd. (72) Inventor Shigenobu Yamaura 2-1-1 Nihonbashi Muromachi, Chuo-ku, Tokyo Mitsui Kinzoku Mining Co., Ltd.
Claims (3)
ール面に、ビッカース硬度１０００以上の金属化合物を
主成分とするフェイス用硬質物質及び／またはソール用
硬質物質を装着したことを特徴とするゴルフクラブヘッ
ド。1. A golf club wherein a hard face material and / or a hard sole material mainly composed of a metal compound having a Vickers hardness of 1000 or more is mounted on a face surface and / or a sole surface of a head body. head.
用硬質物質は、Ａｌ化合物、Ｔｉ化合物、Ｔａ化合物、
Ｃｒ化合物、Ｚｒ化合物、Ｎｂ化合物、Ｈｆ化合物、Ｗ
化合物、Ｓｉ化合物、Ｍｏ化合物、Ｖ化合物、Ｂ化合物
の中から、少なくとも１種類以上の金属化合物を主成分
とすることを特徴とする請求項１記載のゴルフクラブヘ
ッド。2. The hard material for a face and the hard material for a sole include an Al compound, a Ti compound, a Ta compound,
Cr compound, Zr compound, Nb compound, Hf compound, W
2. The golf club head according to claim 1, wherein at least one metal compound is a main component among compounds, Si compounds, Mo compounds, V compounds, and B compounds.
０未満で、且つ厚みが１．５〜４．０ｍｍであり、前記
ソール用硬質物質は、比重が８．０以上で、且つ厚みが
１．５〜４．０ｍｍであることを特徴とする請求項１又
は２記載のゴルフクラブヘッド。3. The hard material for a face has a specific gravity of 8.
0 and a thickness of 1.5 to 4.0 mm, and the hard material for sole has a specific gravity of 8.0 or more and a thickness of 1.5 to 4.0 mm. Item 3. The golf club head according to item 1 or 2.