JPH1180746A - Treatment of waste plastics containing PVC resin - Google Patents
Treatment of waste plastics containing PVC resinInfo
- Publication number
- JPH1180746A JPH1180746A JP24512797A JP24512797A JPH1180746A JP H1180746 A JPH1180746 A JP H1180746A JP 24512797 A JP24512797 A JP 24512797A JP 24512797 A JP24512797 A JP 24512797A JP H1180746 A JPH1180746 A JP H1180746A
- Authority
- JP
- Japan
- Prior art keywords
- hydrochloric acid
- waste plastics
- polyvinyl chloride
- decomposition
- chloride resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】
【課題】 ポリ塩化ビニール樹脂を含有する廃プラスチ
ックスを化学的に分解処理し、ポリ塩化ビニール樹脂中
に含有されている塩素分を除去し、塩素を含まない良質
の燃料を得ると共に、ポリ塩化ビニール樹脂の分解によ
って生成した塩化水素を、高純度の塩酸または塩化物と
して回収する。
【解決手段】 ポリ塩化ビニール樹脂を含有する廃プラ
スチックスを、溶融槽４において化学的に分解処理し燃
料を得ると共に、ポリ塩化ビニール樹脂の分解によって
生じた塩化水素を、吸収塔５において塩酸または各種塩
化物として回収し、次いで精製処理槽８において、回収
された塩酸または各種塩化物の水溶液中に過酸化水素を
添加し、塩酸または各種塩化物の水溶液中に含有されて
いる有機物を、過酸化水素と反応させて酸化分解し除去
する。
(57) [Summary] [PROBLEMS] A high quality fuel which does not contain chlorine by chemically decomposing waste plastics containing a PVC resin to remove chlorine contained in the PVC resin. And the hydrogen chloride produced by the decomposition of the polyvinyl chloride resin is recovered as high-purity hydrochloric acid or chloride. SOLUTION: Waste plastics containing a polyvinyl chloride resin is chemically decomposed in a melting tank 4 to obtain a fuel, and hydrogen chloride generated by the decomposition of the polyvinyl chloride resin is converted into hydrochloric acid or Hydrogen peroxide is added to the recovered aqueous solution of hydrochloric acid or various chlorides in the purifying treatment tank 8 to remove organic substances contained in the aqueous solution of hydrochloric acid or various chlorides. It reacts with hydrogen oxide to oxidatively decompose and remove.
Description
【０００１】[0001]
【発明の属する技術分野】この発明は、ポリ塩化ビニー
ル樹脂を含有する廃プラスチックスを化学的に分解処理
し、ポリ塩化ビニール樹脂の分解によって生じた塩化水
素を、塩酸または各種の塩化物として回収する廃プラス
チックスの処理方法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for chemically decomposing waste plastics containing a polyvinyl chloride resin, and recovering hydrogen chloride produced by the decomposition of the polyvinyl chloride resin as hydrochloric acid or various chlorides. The present invention relates to a method for treating waste plastics.
【０００２】[0002]
【従来の技術】ポリ塩化ビニール樹脂を含有する廃プラ
スチックスを化学的に分解処理して、固体または液体の
燃料を得る廃プラスチックスの処理方法には、従来から
種々のプロセスが知られており、その典型的なプロセス
として、廃プラスチックスを加熱処理し、廃プラスチッ
クス中のポリ塩化ビニールを熱分解することにより、ポ
リ塩化ビニール中に含有されている塩素分を塩化水素と
して除去し、塩素を含まない良質の燃料を得ると共に、
ポリ塩化ビニールの熱分解時に、分解ガス中に含まれて
いる塩化水素を水に吸収させ塩酸として回収し、また
は、前記分解ガス中に含まれている塩化水素を水酸化ナ
トリウムなどのアルカリ性物質と反応させ、各種塩化物
として回収する方法（以下、先行技術という）が知られ
ている。2. Description of the Related Art Various processes are conventionally known as a method for treating waste plastics which obtains solid or liquid fuel by chemically decomposing waste plastics containing a polyvinyl chloride resin. As a typical process, heat treatment of waste plastics and thermal decomposition of polyvinyl chloride in waste plastics removes chlorine contained in polyvinyl chloride as hydrogen chloride, And obtain high quality fuel without
During the thermal decomposition of polyvinyl chloride, hydrogen chloride contained in the decomposition gas is absorbed in water and recovered as hydrochloric acid, or the hydrogen chloride contained in the decomposition gas is mixed with an alkaline substance such as sodium hydroxide. A method of reacting and recovering as various chlorides (hereinafter referred to as prior art) is known.
【０００３】図２は、先行技術の一例として塩酸を回収
する場合の工程図である。図面に示すように、破砕機
１、ホッパー２、スクリューフィーダー３、溶融槽４お
よび塩酸吸収塔５がこの順序で配置されており、廃プラ
スチックスは、破砕機１において破砕された後、ホッパ
ー２およびスクリューフィーダー３を介して溶融槽４に
供給される。FIG. 2 is a process diagram in the case of recovering hydrochloric acid as an example of the prior art. As shown in the drawing, a crusher 1, a hopper 2, a screw feeder 3, a melting tank 4 and a hydrochloric acid absorption tower 5 are arranged in this order, and after waste plastics is crushed in the crusher 1, the hopper 2 And, it is supplied to the melting tank 4 via the screw feeder 3.
【０００４】廃プラスチックスは、溶融槽４および／ま
たはスクリューフィーダー３において適宜の手段により
所定温度に加熱される。その結果、廃プラスチックス中
のポリ塩化ビニールは、他に共存するプラスチックスが
あればそのプラスチックスと共に溶融して熱分解反応を
起こす。[0004] Waste plastics is heated to a predetermined temperature in the melting tank 4 and / or the screw feeder 3 by an appropriate means. As a result, the polyvinyl chloride in the waste plastics melts together with the plastics, if any, and causes a thermal decomposition reaction.
【０００５】溶融槽４における廃プラスチックスの熱分
解反応時に発生した、塩化水素を含む分解ガスは、溶融
槽４内に吹き込まれた窒素ガス等のキャリアーガスによ
って塩酸吸収塔５に吹き込まれる。塩酸吸収塔５内に吹
き込まれた分解ガスは、塔内上部から噴射された水によ
りスクラビングされ、水に吸収されて粗塩酸となり、塔
底部に設けられた排出口から排出され回収される。The decomposition gas containing hydrogen chloride generated during the thermal decomposition reaction of the waste plastics in the melting tank 4 is blown into the hydrochloric acid absorption tower 5 by a carrier gas such as nitrogen gas blown into the melting tank 4. The cracked gas blown into the hydrochloric acid absorption tower 5 is scrubbed with water injected from the upper part of the tower, absorbed by water to become crude hydrochloric acid, and discharged and recovered from an outlet provided at the bottom of the tower.
【０００６】塩酸吸収塔５において水に吸収されないオ
フガスは、吸収塔５の上部のガス排出口から排出され、
オフガス処理ユニット６において燃焼処理された後、大
気中に放散される。一方、溶融槽４の底部に設けられた
排出口からは、塩素分が除去された溶融プラスチックス
が排出され、燃料処理ユニット７において、目的に応じ
た形態の燃料になるように処理される。[0006] The off-gas that is not absorbed by water in the hydrochloric acid absorption tower 5 is discharged from a gas outlet at the upper part of the absorption tower 5,
After being burned in the off-gas processing unit 6, it is released into the atmosphere. On the other hand, the molten plastic from which chlorine has been removed is discharged from a discharge port provided at the bottom of the melting tank 4 and is processed in the fuel processing unit 7 so that the fuel has a form suitable for the purpose.
【０００７】[0007]
【発明が解決しようとする課題】しかしながら上述した
従来の方法には、次のような問題がある。即ち、回収さ
れた塩酸または塩化物中には、プラスチックス自体、ま
たは、プラスチックスに通常添加されている可塑剤の熱
分解による主要生成物である各種炭化水素類のような有
機物が混入しているために、回収した塩酸や塩化物の品
質低下を招いている。上記回収した塩酸や塩化物を、品
質の優れた商品価値の高い高純度製品にするためには、
蒸留や再晶析等のような再処理工程が必要であり、従っ
て、作業が複雑化すると共に製造コストの上昇が避けら
れない。However, the above-mentioned conventional method has the following problems. That is, in the recovered hydrochloric acid or chloride, plastics itself or organic substances such as various hydrocarbons which are main products by thermal decomposition of a plasticizer usually added to the plastics are mixed. Therefore, the quality of the recovered hydrochloric acid and chloride is reduced. In order to make the recovered hydrochloric acid or chloride into a high-purity product with excellent quality and commercial value,
A reprocessing step such as distillation or recrystallization is required, which complicates the operation and inevitably increases the production cost.
【０００８】従って、この発明の目的は、上述した問題
を解決し、ポリ塩化ビニール樹脂を含有する廃プラスチ
ックスを化学的に分解処理し、ポリ塩化ビニール樹脂中
に含有されている塩素分を除去し、塩素を含まない良質
の燃料を得ると共に、ポリ塩化ビニール樹脂の分解によ
って生成した塩化水素を、高純度の塩酸または各種塩化
物として、容易に且つ経済的に回収することができる方
法を提供することにある。Accordingly, an object of the present invention is to solve the above-mentioned problems and to chemically decompose waste plastics containing a polyvinyl chloride resin to remove chlorine contained in the polyvinyl chloride resin. And a method for obtaining a high-quality fuel containing no chlorine and for easily and economically recovering hydrogen chloride produced by the decomposition of polyvinyl chloride resin as high-purity hydrochloric acid or various chlorides. Is to do.
【０００９】[0009]
【課題を解決するための手段】本発明者等は、上述した
観点から、廃プラスチックスの化学的分解処理時に、ポ
リ塩化ビニール樹脂の分解によって生じた塩化水素を、
高純度の塩酸または各種塩化物として、簡単な設備によ
り容易に且つ経済的に回収することができる方法を開発
すべく鋭意研究を重ねた。その結果、塩酸吸収塔から回
収された、炭化水素のような不純物を含有する塩酸また
は塩化物の水溶液に過酸化水素水を添加し、過酸化水素
水によって前記不純物である炭化水素を酸化、分解すれ
ば、高純度の塩酸または塩化物を回収し得ることを知見
した。SUMMARY OF THE INVENTION From the above-mentioned viewpoint, the present inventors have considered that hydrogen chloride generated by the decomposition of polyvinyl chloride resin during the chemical decomposition treatment of waste plastics is used.
Intensive research has been conducted to develop a method for easily and economically recovering high-purity hydrochloric acid or various chlorides with simple equipment. As a result, hydrogen peroxide solution is added to an aqueous solution of hydrochloric acid or chloride containing impurities such as hydrocarbons recovered from the hydrochloric acid absorption tower, and the hydrocarbons as impurities are oxidized and decomposed by the hydrogen peroxide solution. Then, it was found that high-purity hydrochloric acid or chloride could be recovered.
【００１０】この発明は、上記知見に基づいてなされた
ものであって、請求項１に記載の発明は、ポリ塩化ビニ
ール樹脂を含有する廃プラスチックスを化学的に分解処
理して、固体または液体の燃料を得ると共に、前記ポリ
塩化ビニール樹脂の分解によって生じた塩化水素を、塩
酸または各種の塩化物として回収する廃プラスチックス
の処理方法において、前記回収された塩酸または各種塩
化物の水溶液に過酸化水素を添加し、前記塩酸または各
種塩化物の水溶液中に含有されている有機物を前記過酸
化水素と反応させ、前記有機物を酸化、分解して除去す
ることにより、高純度の塩酸または各種塩化物として回
収することに特徴を有するものである。[0010] The present invention has been made based on the above findings, and the invention according to claim 1 is a method for chemically decomposing waste plastics containing a polyvinyl chloride resin to obtain a solid or liquid. In the method of treating waste plastics for recovering hydrogen chloride generated by the decomposition of the polyvinyl chloride resin as hydrochloric acid or various chlorides while obtaining the above fuel, the recovered hydrochloric acid or various chlorides are transferred to an aqueous solution. By adding hydrogen oxide, an organic substance contained in the aqueous solution of the hydrochloric acid or various chlorides is reacted with the hydrogen peroxide, and the organic substance is oxidized, decomposed and removed, thereby obtaining high-purity hydrochloric acid or various chlorides. It is characterized in that it is collected as an object.
【００１１】請求項２に記載の発明は、請求項１に記載
の方法におけるポリ塩化ビニール樹脂の分解を、前記廃
プラスチックスを２００℃から３６０℃の温度まで加熱
することにより誘起される熱分解によって行うことを特
徴とするものである。請求項３に記載の発明は、請求項
１に記載の方法において、ポリ塩化ビニール樹脂の分解
によって生成した塩化水素を、水を吸収媒体としてスク
ラビングすることにより塩酸となし、前記塩酸を前記過
酸化水素と反応させることを特徴とするものであり、そ
して、請求項４に記載の発明は、上記ポリ塩化ビニール
樹脂の分解によって生成した塩化水素を、アルカリ性物
質の水溶液と反応させて各種塩化物の水溶液となし、前
記各種塩化物の水溶液を前記過酸化水素と反応させるこ
とに特徴を有するものである。According to a second aspect of the present invention, the decomposition of the polyvinyl chloride resin in the method of the first aspect is performed by heating the waste plastics to a temperature of 200 ° C. to 360 ° C. This is characterized by the following. According to a third aspect of the present invention, in the method according to the first aspect, hydrogen chloride generated by decomposition of the polyvinyl chloride resin is converted into hydrochloric acid by scrubbing with water as an absorbing medium. The invention is characterized by reacting with hydrogen, and the invention according to claim 4 reacts hydrogen chloride generated by decomposition of the polyvinyl chloride resin with an aqueous solution of an alkaline substance to form various chlorides. An aqueous solution is formed, and the aqueous solution of the various chlorides is reacted with the hydrogen peroxide.
【００１２】[0012]
【発明の実施の形態】次に、この発明を図面を参照しな
がら説明する。図１は、本発明方法の一実施態様を示す
工程図である。図面に示すように、ポリ塩化ビニール樹
脂を含有する廃プラスチックスは、溶融槽４および／ま
たはスクリューフィーダー３により、所定温度に加熱さ
れて溶融し熱分解反応を起こし、熱分解反応時に発生し
た分解ガスは、溶融槽４内に吹き込まれたキャリアーガ
スによって塩酸吸収塔５に導かれ、吸収塔５内において
水を吸収媒体としてスクラビングすることにより、水に
吸収された上、粗塩酸として塔底部に設けられた排出口
から排出されると共に、水に吸収されないオフガスは、
塩酸吸収塔５から排出され、オフガス処理ユニット６に
おいて燃焼処理された後、大気中に放散され、また、溶
融槽４から排出された、塩素の除去された溶融プラスチ
ックスは、燃料処理ユニット７において、目的に応じた
燃料形態になるように処理されることは従来と同様であ
る。Next, the present invention will be described with reference to the drawings. FIG. 1 is a process chart showing one embodiment of the method of the present invention. As shown in the drawing, waste plastics containing a polyvinyl chloride resin is heated to a predetermined temperature and melted by a melting tank 4 and / or a screw feeder 3 to cause a thermal decomposition reaction. The gas is guided to the hydrochloric acid absorption tower 5 by the carrier gas blown into the melting tank 4, and is scrubbed in the absorption tower 5 with water as an absorbing medium to be absorbed by the water, and then as crude hydrochloric acid at the bottom of the tower. Off-gas that is discharged from the provided outlet and not absorbed by water,
After being discharged from the hydrochloric acid absorption tower 5 and burned in the off-gas processing unit 6, the molten plastics discharged into the atmosphere and discharged from the melting tank 4 and from which chlorine has been removed are removed in the fuel processing unit 7. It is the same as in the prior art that the fuel is processed so as to meet the purpose.
【００１３】この発明においては、塩酸吸収塔５の次に
精製処理槽８が設けられており、塩酸吸収塔５から排出
された粗塩酸を、精製処理槽８に送り込み、精製処理槽
８において、所定量の過酸化水素を添加し混合すること
により、前記粗塩酸中に含有されている有機物を、過酸
化水素と反応せしめて酸化分解し除去する。このように
して、精製処理槽８において、高純度の精製塩酸が得ら
れる。In the present invention, a purifying treatment tank 8 is provided next to the hydrochloric acid absorption tower 5, and the crude hydrochloric acid discharged from the hydrochloric acid absorption tower 5 is sent to the purification treatment tank 8. By adding and mixing a predetermined amount of hydrogen peroxide, the organic substances contained in the crude hydrochloric acid are reacted with hydrogen peroxide, oxidatively decomposed, and removed. In this way, high-purity purified hydrochloric acid is obtained in the purification tank 8.
【００１４】ポリ塩化ビニール樹脂の分解によって生じ
た塩化水素を各種塩化物として回収する場合には、溶融
槽４おける熱分解反応時に発生した分解ガスを、吸収塔
において水酸化ナトリウム等のアルカリ性物質水溶液と
反応させることにより各種塩化物の水溶液となす。この
各種塩化物水溶液を精製処理槽８に送り込み、精製処理
槽８において、所定量の過酸化水素を添加し混合するこ
とにより、前記塩化物水溶液中に含有されている有機物
を、前記過酸化水素と反応せしめて酸化分解し除去す
る。このようにして、精製処理槽８において、高純度の
各種塩化物が得られる。When hydrogen chloride generated by the decomposition of the polyvinyl chloride resin is recovered as various chlorides, the decomposition gas generated during the thermal decomposition reaction in the melting tank 4 is converted into an aqueous solution of an alkaline substance such as sodium hydroxide in an absorption tower. To form aqueous solutions of various chlorides. The various chloride aqueous solutions are sent to the purification treatment tank 8, and a predetermined amount of hydrogen peroxide is added and mixed in the purification treatment tank 8 to remove the organic substances contained in the chloride aqueous solution. And oxidatively decompose and remove. In this manner, various high-purity chlorides can be obtained in the purification tank 8.
【００１５】前記溶融槽４において行われるポリ塩化ビ
ニール樹脂の分解は、廃プラスチックスを２００℃から
３６０℃の温度まで加熱することにより誘起される熱分
解によって行うことが好ましい。廃プラスチックスに対
する加熱温度が２００℃未満では熱分解が生ぜず、一
方、加熱温度が３６０℃を超えると、溶融物がコーキン
グ化する問題が生ずる。好ましい加熱温度は、２５０〜
３５０℃の範囲内である。The decomposition of the polyvinyl chloride resin in the melting tank 4 is preferably performed by thermal decomposition induced by heating the waste plastics to a temperature of from 200 ° C. to 360 ° C. If the heating temperature of the waste plastics is lower than 200 ° C., no thermal decomposition occurs, while if the heating temperature is higher than 360 ° C., there is a problem that the melt is coked. The preferred heating temperature is from 250 to
Within the range of 350 ° C.
【００１６】[0016]
【実施例】次に、この発明を実施例により説明する。図
１に示した工程に従って廃プラスチックスを処理した。
即ち、破砕機１において破砕された廃プラスチックス
を、ホッパー２、スクリューフィーダー３を経て溶融槽
４に供給し、溶融槽４において３００℃の温度で溶融し
た。Next, the present invention will be described with reference to embodiments. Waste plastics were treated according to the process shown in FIG.
That is, the waste plastics crushed in the crusher 1 was supplied to the melting tank 4 via the hopper 2 and the screw feeder 3 and was melted in the melting tank 4 at a temperature of 300 ° C.
【００１７】溶融槽４内には、キャリアーガスとして窒
素ガスを吹込み、廃プラスチックスの溶融による熱分解
反応によって生じた分解ガスを、キャリアーガスによっ
て塩酸吸収塔５に吹き込んだ。吸収塔５に吹き込まれた
分解ガスは、塔内においてその上部から噴射される水に
吸収され、ＣＯＤとして約５０００ｐｐｍの炭化水素を
含有する約２０wt.%の濃度の粗塩酸として回収した。Nitrogen gas was blown into the melting tank 4 as a carrier gas, and the decomposition gas generated by the thermal decomposition reaction due to the melting of the waste plastics was blown into the hydrochloric acid absorption tower 5 by the carrier gas. The cracked gas blown into the absorption tower 5 was absorbed by water injected from the upper part in the tower, and was recovered as crude hydrochloric acid having a concentration of about 20 wt.% And containing about 5000 ppm of hydrocarbon as COD.
【００１８】吸収塔５において回収された上記粗塩酸を
精製処理槽８に送り込み、精製処理槽８において、粗塩
酸１００重量部に対し３．５重量部の量の３０％過酸化
水素水を、粗塩酸に添加し混合攪拌して両者を反応させ
た。その結果、粗塩酸中の炭化水素は実質的に全部除去
された精製塩酸が得られた。The crude hydrochloric acid recovered in the absorption tower 5 is sent to a purifying treatment tank 8, where 3.5 parts by weight of 30% hydrogen peroxide solution is added to 100 parts by weight of the crude hydrochloric acid. The mixture was added to the crude hydrochloric acid, mixed and stirred, and reacted. As a result, purified hydrochloric acid was obtained in which hydrocarbons in the crude hydrochloric acid were substantially completely removed.
【００１９】なお、精製処理前の粗塩酸の濃度は、過酸
化水素水の希釈水および酸化反応による生成水によって
若干希釈され、当初の２０wt.%から１９．４wt.%まで低
下したが、これによる実質的な障害は生じなかった。The concentration of the crude hydrochloric acid before the purification treatment was slightly diluted with the dilution water of the hydrogen peroxide solution and the water produced by the oxidation reaction, and decreased from the initial 20 wt.% To 19.4 wt.%. Did not cause any substantial damage.
【００２０】[0020]
【発明の効果】以上述べたように、この発明によれば、
ポリ塩化ビニール樹脂を含有する廃プラスチックスを化
学的に分解処理し、ポリ塩化ビニール樹脂の分解によっ
て生じた塩化水素を、高純度の塩酸または各種塩化物と
して、簡単な設備により容易に且つ経済的に回収するこ
とができる、工業上有用な効果がもたらされる。As described above, according to the present invention,
Waste plastics containing PVC resin are chemically decomposed and the hydrogen chloride generated by the decomposition of PVC resin is converted into high-purity hydrochloric acid or various chlorides easily and economically with simple equipment. An industrially useful effect can be obtained.
【図１】この発明の方法の一実施態様を示す工程図であ
る。FIG. 1 is a process chart showing one embodiment of the method of the present invention.
【図２】従来方法の一例を示す工程図である。FIG. 2 is a process chart showing an example of a conventional method.
１ 破砕機 ２ ホッパー ３ スクリューフィーダー ４ 溶融槽 ５ 塩酸吸収塔 ６ オフガス処理ユニット ７ 燃料処理ユニット ８ 精製処理槽 DESCRIPTION OF SYMBOLS 1 Crusher 2 Hopper 3 Screw feeder 4 Melting tank 5 Hydrochloric acid absorption tower 6 Off gas processing unit 7 Fuel processing unit 8 Purification processing tank
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 ＦＩ Ｃ０８Ｊ 11/10 ＣＥＶ Ｃ０８Ｊ 11/16 ＣＥＶ 11/12 ＣＥＶ Ｃ１０Ｌ 5/48 11/16 ＣＥＶ Ｂ０９Ｂ 3/00 ＺＡＢ Ｃ１０Ｌ 5/48 ３０２Ａ // Ｂ２９Ｋ 27:06 105:26 ──────────────────────────────────────────────────の Continued on the front page (51) Int.Cl. 6 Identification code FI C08J 11/10 CEV C08J 11/16 CEV 11/12 CEV C10L 5/48 11/16 CEV B09B 3/00 ZAB C10L 5/48 302A // B29K 27:06 105: 26
Claims (4)
スチックスを化学的に分解処理して、固体または液体の
燃料を得ると共に、前記ポリ塩化ビニール樹脂の分解に
よって生じた塩化水素を、塩酸または各種の塩化物とし
て回収する廃プラスチックスの処理方法において、 前記回収された塩酸または各種塩化物の水溶液に過酸化
水素を添加し、前記塩酸または各種塩化物の水溶液中に
含有されている有機物を、前記過酸化水素と反応させて
酸化、分解し除去することにより、高純度の塩酸または
各種塩化物として回収することを特徴とする、ポリ塩化
ビニール樹脂を含有する廃プラスチックスの処理方法。1. A waste plastics containing a polyvinyl chloride resin is chemically decomposed to obtain a solid or liquid fuel, and hydrogen chloride produced by the decomposition of the polyvinyl chloride resin is converted into hydrochloric acid or various kinds of fuel. In a method for treating waste plastics to be recovered as chloride, hydrogen peroxide is added to the recovered aqueous solution of hydrochloric acid or various chlorides, and an organic substance contained in the aqueous solution of hydrochloric acid or various chlorides is A method for treating waste plastics containing a polyvinyl chloride resin, wherein the waste plastics are recovered as high-purity hydrochloric acid or various chlorides by reacting with the hydrogen peroxide to oxidize, decompose and remove.
記廃プラスチックスを２００℃から３６０℃の温度まで
加熱することにより誘起される熱分解によって行う、請
求項１に記載の方法。2. The method according to claim 1, wherein the decomposition of the polyvinyl chloride resin is carried out by pyrolysis induced by heating the waste plastics to a temperature of 200 ° C. to 360 ° C.
て生成した塩化水素を、水を吸収媒体としてスクラビン
グすることにより塩酸となし、前記塩酸を前記過酸化水
素と反応させる、請求項１に記載の方法。3. The method according to claim 1, wherein the hydrogen chloride produced by the decomposition of the polyvinyl chloride resin is converted into hydrochloric acid by scrubbing with water as an absorbing medium, and the hydrochloric acid is reacted with the hydrogen peroxide. .
て生成した塩化水素を、アルカリ性物質の水溶液と反応
させて各種塩化物の水溶液となし、前記各種塩化物の水
溶液を前記過酸化水素と反応させる、請求項１に記載の
方法。4. Hydrogen chloride produced by decomposition of the polyvinyl chloride resin is reacted with an aqueous solution of an alkaline substance to form aqueous solutions of various chlorides, and the aqueous solutions of various chlorides are reacted with the hydrogen peroxide. The method of claim 1.