JPS5714614A - Phenol-aldehyde resin composition,adhesive coating composition containing it,tire cord using composition and manufacture of cord - Google Patents
Phenol-aldehyde resin composition,adhesive coating composition containing it,tire cord using composition and manufacture of cordInfo
- Publication number
- JPS5714614A JPS5714614A JP4384881A JP4384881A JPS5714614A JP S5714614 A JPS5714614 A JP S5714614A JP 4384881 A JP4384881 A JP 4384881A JP 4384881 A JP4384881 A JP 4384881A JP S5714614 A JPS5714614 A JP S5714614A
- Authority
- JP
- Japan
- Prior art keywords
- aldehyde
- phenolic compound
- adhesive
- cord
- mixture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A method of preparing a thermoplastic, water-soluble, phenolic aldehyde resin involves two steps. Firstly, the phenolic compound and aldehyde are reacted to less than 100 percent completion at an aldehyde to phenolic compound mole ratio of 0.6 to 1.5 and at a pH of 3.5 to 5.5 for 3 to 10 hours at a temperature of 13 to 32 DEG C. Secondly the pH of the reaction is adjusted to above 7.0 to 7.5 and the reaction is continued between the unreacted phenolic compound and aldehyde and resinous mixture to produce a resinous mixture that has a predominant amount of trimer polymer with slight cross-linking and a minor amount of dimer and higher oligomers. The phenolic compound is preferably resorcinol or a mixture of resorcinol and phenol. The resin mixture is processed into an adhesive by combining it with one or more elastomeric latex and various latex additives. The adhesive is aged and has added to it an amine or ammonia to tie up any unreacted aldehyde. Also additional phenolic compound may be added. The adhesive is used to coat filamentary materials in particular glass fibres and the coated filamentary materials are dried to produce reinforcement material for rubber. Uses:- Tyre cords adhesives
Applications Claiming Priority (1)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| US16335580A | 1980-06-26 | 1980-06-26 |
Publications (1)
| Publication Number | Publication Date |
|---|---|
| JPS5714614A true JPS5714614A (en) | 1982-01-25 |
Family
ID=22589667
Family Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| JP4384881A Pending JPS5714614A (en) | 1980-06-26 | 1981-03-24 | Phenol-aldehyde resin composition,adhesive coating composition containing it,tire cord using composition and manufacture of cord |
Country Status (8)
| Country | Link |
|---|---|
| JP (1) | JPS5714614A (en) |
| BE (1) | BE887384A (en) |
| CA (1) | CA1173580A (en) |
| DE (1) | DE3121382A1 (en) |
| FR (1) | FR2485435A1 (en) |
| GB (1) | GB2082607A (en) |
| IT (1) | IT1146738B (en) |
| NL (1) | NL8100369A (en) |
Cited By (1)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| CN108641624A (en) * | 2014-02-06 | 2018-10-12 | 米其林集团总公司 | It is coated with the steel reinforcing element of the adhesive composition comprising aromatic aldehyde and polyphenol |
Families Citing this family (13)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| GB2125451B (en) * | 1982-08-13 | 1986-01-02 | Borg Warner | Extrusion coated continuous tape |
| CN1969083B (en) * | 2004-06-28 | 2010-06-16 | 日本板硝子株式会社 | Cord for rubber reinforcement, method for producing same, and rubber product using same |
| FR2978769B1 (en) | 2011-08-04 | 2013-09-27 | Michelin Soc Tech | AQUEOUS ADHESIVE COMPOSITION BASED ON POLYALDEHYDE AND POLYPHENOL |
| FR2978770B1 (en) | 2011-08-04 | 2013-09-27 | Michelin Soc Tech | AQUEOUS ADHESIVE COMPOSITION BASED ON POLYALDEHYDE AND PHLOROGLUCINOL |
| FR2978771B1 (en) | 2011-08-04 | 2013-09-27 | Michelin Soc Tech | AQUEOUS ADHESIVE COMPOSITION BASED ON POLYALDEHYDE AND 2,2 ', 4,4'-TETRAHYDROXYDIPHENYL SULFIDE |
| FR3008707B1 (en) * | 2013-07-16 | 2017-11-10 | Michelin & Cie | AQUEOUS ADHESIVE COMPOSITION BASED ON BIOSOURCE ALDEHYDE AND POLYPHENOL |
| FR3031745A1 (en) | 2015-01-21 | 2016-07-22 | Michelin & Cie | HIGH RIGIDITY RUBBER COMPOSITION |
| WO2016116468A1 (en) | 2015-01-21 | 2016-07-28 | Compagnie Generale Des Etablissements Michelin | High-rigidity rubber composition |
| FR3031746A1 (en) | 2015-01-21 | 2016-07-22 | Michelin & Cie | HIGH RIGIDITY RUBBER COMPOSITION |
| CN109266283A (en) * | 2018-08-06 | 2019-01-25 | 岳西县明杰电子有限公司 | A kind of ageing-resistant insulation adhesive of transformer |
| CN109456516B (en) * | 2018-11-19 | 2021-03-05 | 北京彤程创展科技有限公司 | Bisphenol compound modified resorcinol resin, rubber composition and preparation method thereof |
| CN111088700A (en) * | 2019-12-03 | 2020-05-01 | 浙江尤夫科技工业有限公司 | Rubber canvas gum dipping formula, preparation method thereof and preparation method of rubber canvas |
| CN115353710A (en) * | 2022-08-19 | 2022-11-18 | 山东北方现代化学工业有限公司 | Nylon-reinforced high-strength glass fiber phenolic composite material and preparation method thereof |
Family Cites Families (3)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| DE365286C (en) * | 1920-06-17 | 1922-12-14 | Hoechst Ag | Process for the preparation of resinous condensation products from phenols and acetaldehyde |
| US2494537A (en) * | 1946-07-26 | 1950-01-17 | Glen E Babcock | Cold-setting resorcinol glue composition and process of preparation |
| GB1034950A (en) * | 1963-11-15 | 1966-07-06 | Pirelli | Improvements in or relating to the preparation of liquid adhesive compositions for the treatment of textile materials and to the treatment of textile materials with suchcompositions |
-
1981
- 1981-01-12 CA CA000368266A patent/CA1173580A/en not_active Expired
- 1981-01-27 NL NL8100369A patent/NL8100369A/en not_active Application Discontinuation
- 1981-02-03 IT IT67145/81A patent/IT1146738B/en active
- 1981-02-04 BE BE0/203697A patent/BE887384A/en not_active IP Right Cessation
- 1981-02-17 FR FR8103100A patent/FR2485435A1/en not_active Withdrawn
- 1981-03-24 JP JP4384881A patent/JPS5714614A/en active Pending
- 1981-05-29 DE DE19813121382 patent/DE3121382A1/en not_active Withdrawn
- 1981-06-04 GB GB8117118A patent/GB2082607A/en not_active Withdrawn
Cited By (1)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| CN108641624A (en) * | 2014-02-06 | 2018-10-12 | 米其林集团总公司 | It is coated with the steel reinforcing element of the adhesive composition comprising aromatic aldehyde and polyphenol |
Also Published As
| Publication number | Publication date |
|---|---|
| GB2082607A (en) | 1982-03-10 |
| DE3121382A1 (en) | 1982-02-25 |
| IT1146738B (en) | 1986-11-19 |
| FR2485435A1 (en) | 1981-12-31 |
| CA1173580A (en) | 1984-08-28 |
| BE887384A (en) | 1981-08-04 |
| IT8167145A0 (en) | 1981-02-03 |
| NL8100369A (en) | 1982-01-18 |
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| US2128635A (en) | Laminated structure and method for preparing same | |
| CA1050182A (en) | Phenol-formaldehyde-resorcinol resins and adhesives | |
| IT1146738B (en) | PROCEDURE FOR THE PREPARATION OF AN ALDEHYDIDE PHENOL RESIN AND RESIN COMPOSITION FOR THE TREATMENT OF GLASS FIBERS USED FOR TIRES REINFORCEMENT | |
| US2746898A (en) | Dry adhesion method for adhering textile material to rubber | |
| FI60221B (en) | COMPOSITION FOR IMPREGNERING OF GLASFIBER MATERIAL | |
| US3437122A (en) | Cord dip of improved stability | |
| US3897583A (en) | Adhesion of metal to rubber | |
| US3644256A (en) | Resorcinol-formaldehyde-latex adhesive containing triallyl cyanurate with high-ringbound chlorine content | |
| US3663268A (en) | Process for adhering polyester tire cord to rubber | |
| ES2058193T3 (en) | METHOD FOR OBTAINING A CHEMICAL UNION BETWEEN POLYPHENYLENE-BASED MOLDING COMPOUNDS; ON THE ONE PART AND EP (D) M RUBBER, VULCANIZED WITH PEROXIDE, ON THE OTHER PART. | |
| US3222238A (en) | Process for bonding rubber to linear condensation polyester structures | |
| GB1396184A (en) | Adhesive composition for bonding polyester fibre to rubber | |
| US3793130A (en) | Fiber reinforced elastomers | |
| CA1114540A (en) | Rubber compound and method of preparing same | |
| US2927051A (en) | Bonding textiles to rubbers with resorcinol and diaryl guanidinine formaldehyde reaction product | |
| US3212955A (en) | Tire cord bonding with polymethylolmelamine resins | |
| US3361617A (en) | Tire cord bonding with aminoplast resins and butadiene/vinylpyridine latex | |
| US3706619A (en) | Method of bonding wood and other materials with rapid-curing adhesives using a primer composition | |
| GB1181482A (en) | Adhering Textiles to Rubber | |
| US2413624A (en) | Hardenable urea-aldehyde resins | |
| US2839443A (en) | Adhesion of textile fabric to butyl rubber | |
| US2489145A (en) | Synthetic resin compositions employing curing catalysts | |
| US3464878A (en) | Process of bonding rubber to polyester tire cord and composition | |
| US3074904A (en) | Laminate structures | |
| ATE10107T1 (en) | PROCESS FOR THE MANUFACTURE OF REINFORCED RUBBER VULCANISATES. |