JPS5967390A - Case for wrist watch - Google Patents
Case for wrist watchInfo
- Publication number
- JPS5967390A JPS5967390A JP17577282A JP17577282A JPS5967390A JP S5967390 A JPS5967390 A JP S5967390A JP 17577282 A JP17577282 A JP 17577282A JP 17577282 A JP17577282 A JP 17577282A JP S5967390 A JPS5967390 A JP S5967390A
- Authority
- JP
- Japan
- Prior art keywords
- plating
- satin
- case
- finish
- resist film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】 本発明は、腕時計側の装飾に関するものである。[Detailed description of the invention] The present invention relates to decoration on a wristwatch.
時計の１！！Ｉ Ｖｃメッキし、その仕上状態が鏡面部
分と梨地Ｈ周部分の両者があるようにしたものである。Clock 1! ! It is plated with I Vc and has a mirror finish and a satin H circumference.
本発明にはメッキするだけで表面の仕上がホーニング又
はサンドプラストで得られる梨地と同様な外観が得られ
るメッキを使用する。The present invention uses plating that can provide a surface finish similar to the satin finish obtained by honing or sandplast simply by plating.
このメッキの原理は、メッキ液中にエマルジョンが形成
され、これがメッキの析出に作用して表面が梨地状にな
るものである。すなわち、メッキしている間、エマルジ
ョンは十数秒間カソードの表面に付着し、この間にメッ
キが行なわれるためエマルジョンの付着した部分はその
間メッキがつかず、エマルジョンが離れ去った後その部
分に半円状のマークができるわけである。このようにし
てエマルジョンはカソードに対して連続的に作用するの
で、全面が梨地状に仕上がる。この梨地状メッキを使う
ことによる効果は、従来梨地状仕上げは研摩＋ホーニン
グという機械的処理をしていたが、メッキするだけで梨
地状仕上げが得られるので、工程を簡素化してコストダ
ウンを図ることができると同時に優美な外観が得られる
ことである。The principle of this plating is that an emulsion is formed in the plating solution, and this acts on the precipitation of the plating, giving the surface a matte finish. That is, during plating, the emulsion adheres to the surface of the cathode for about 10 seconds, and since plating is performed during this time, the part to which the emulsion adhered is not plated during that time, and after the emulsion leaves, a semicircular shape is formed on that part. This creates a mark like this. In this way, the emulsion acts continuously on the cathode, resulting in a satin-like finish on the entire surface. The effect of using this satin-like plating is that conventionally a satin-like finish was achieved by mechanical processing of polishing and honing, but since a satin-like finish can be obtained just by plating, the process is simplified and costs are reduced. The goal is to be able to achieve an elegant appearance at the same time.
本発明方法の加工工程を説明する。The processing steps of the method of the present invention will be explained.
鏡面仕上げした時計の側に下地メッキを施し、一部にレ
ジストを塗布し、レジストのついてない部分に梨地メッ
キを施し、レジストを剥離して、全面に仕上メッキを施
せば、鏡面部と梨地部が混在した側を得ることができる
。この方法によジ、ホーニング、エツチング等の手段を
用いることなく、表面仕上げの一部のみを梨地状にする
ことができる。If you apply base plating to the side of a mirror-finished watch, apply resist to some parts, apply satin plating to the parts without resist, peel off the resist, and apply finish plating to the entire surface, the mirror and satin parts will be finished. You can get a mixed side. With this method, only a portion of the surface finish can be made satin-like without using means such as drilling, honing, etching, etc.
以下実施例に基づいて説明する。The following will be explained based on examples.
腕時計側を黄銅で形成して、全面鏡面仕上げした。次に
この側にニラゲル下地メッキを５μ施し／１０側の表面
にスクリーン印刷法によって耐酸レジストインクを模様
印刷し、約１時間室温で自然乾燥後８０℃で３０分間焼
付けた。次いでレジストインクがついた側を梨地状仕上
げの得られるニッケルメッキ浴に入れ、レジストのつい
ていない部分のみに梨地状メッキした。水洗後レジスト
を除去した。さらに側全体に金合金メッキを施した。The watch side is made of brass and has a mirror finish. Next, this side was coated with 5 microns of Nilagel underplating, and acid-resistant resist ink was pattern-printed on the surface of the 10 side by screen printing, air-dried at room temperature for about 1 hour, and then baked at 80° C. for 30 minutes. Next, the side to which the resist ink was applied was placed in a nickel plating bath that produced a satin-like finish, and satin-like plating was applied only to the portions to which no resist was applied. After washing with water, the resist was removed. Furthermore, the entire side is plated with gold alloy.
その構成は、１８にメッキ３μ、２２に仕上メッキ２μ
である。その結果、鏡面の中に梨地状の模様がある金色
の側を得ることができた。Its composition is 3μ plating on 18 and 2μ finish plating on 22.
It is. As a result, it was possible to obtain a golden side with a satin-like pattern within the mirror surface.
以上、実施例に述べたように本発明によれば、鏡面部と
梨地状部とが混在する側を容易に得ることができる。As described above in the embodiments, according to the present invention, it is possible to easily obtain a side in which mirror-finished portions and satin-finished portions coexist.
【図面の簡単な説明】
図面は本発明方法によシ作製した時計側の平面図である
。
１・・梨地状仕上部
２・・鏡ｒｆｔＴ仕上部
以 上
出願人 株式会社第二精工舎
代理人 弁理士液 上 務
／ ／BRIEF DESCRIPTION OF THE DRAWINGS The drawing is a plan view of the side of a watch manufactured by the method of the present invention. 1. Satin finish part 2. Mirror RFT T finish part and above Applicant Daini Seikosha Co., Ltd. Agent Patent attorney liquid / /
Claims (1)
部にレジスト膜を形成した状態において梨地状メッキを
施し、レジスト膜を剥離した後、全面に仕上メッキを施
すという工程にょシ製作した、鏡面部と梨地状部が混在
する腕時計側。The manufacturing process involved applying base plating to the mirror-finished wristwatch 1 side, applying satin-like plating with a resist film formed on a part of it, and then applying finish plating to the entire surface after peeling off the resist film. , The wristwatch side has a mixture of mirror-like parts and satin-like parts.