JPS60131845A - 1.90以上の屈折率、25以上のアツベ数および高い化学安定性を有する光学ガラス - Google Patents
1.90以上の屈折率、25以上のアツベ数および高い化学安定性を有する光学ガラスInfo
- Publication number
- JPS60131845A JPS60131845A JP59250648A JP25064884A JPS60131845A JP S60131845 A JPS60131845 A JP S60131845A JP 59250648 A JP59250648 A JP 59250648A JP 25064884 A JP25064884 A JP 25064884A JP S60131845 A JPS60131845 A JP S60131845A
- Authority
- JP
- Japan
- Prior art keywords
- glass according
- weight
- glass
- refractive index
- chemical stability
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
産業上の利用分野
本発明は、光学ガラスに関し、さらに詳しくは、1.9
0以上の屈折率、25以上のアツベ数、高い化学安定性
、及び大寸法の注型ができる程の高い結晶化安定性を有
する光学ガラスに関するものである。
0以上の屈折率、25以上のアツベ数、高い化学安定性
、及び大寸法の注型ができる程の高い結晶化安定性を有
する光学ガラスに関するものである。
従来の技術
yh、o、を含有するガラスキ特開昭57−38342
号に記載されているが、このガラスは良好な透過につい
ての要求を満足しうるものではない。これらは、約90
0rLmの波長において非常に強い吸収を示す。
号に記載されているが、このガラスは良好な透過につい
ての要求を満足しうるものではない。これらは、約90
0rLmの波長において非常に強い吸収を示す。
現在の技術状況は幾つかの特許文献に記載されている。
例えは、特開昭54−133506号に記載のガラスは
、屈折率ルd≦1.95及び33〜39の範囲のアツベ
数を有しておシ、またここでは、nd を増大させるた
めには、十分に安定なガラスを得るためにGg0.含有
を増加させることも必要となり、従って、フリット(ガ
ラス原料)の価格も実質的に増大することになる。
、屈折率ルd≦1.95及び33〜39の範囲のアツベ
数を有しておシ、またここでは、nd を増大させるた
めには、十分に安定なガラスを得るためにGg0.含有
を増加させることも必要となり、従って、フリット(ガ
ラス原料)の価格も実質的に増大することになる。
屈折率≦1.95で同様のアツベ数を有するガラスも特
開昭54−790218号及び特開昭54−10341
号に記載されているが、これらのガラスも、屈折率を増
大させるほど、増加した量のWO,と十分な結晶化安定
性を得るための非常に高価なGeO2を多量含有させる
ことになる。
開昭54−790218号及び特開昭54−10341
号に記載されているが、これらのガラスも、屈折率を増
大させるほど、増加した量のWO,と十分な結晶化安定
性を得るための非常に高価なGeO2を多量含有させる
ことになる。
1.95以上の屈折率を有するガラスの人造は、しかし
ながら、ノ 294203B (nd< 1.97 )
及び1981年7月30日西独特許出願1)E−O53
130039号に記載の組成範囲内士のみ可能である。
ながら、ノ 294203B (nd< 1.97 )
及び1981年7月30日西独特許出願1)E−O53
130039号に記載の組成範囲内士のみ可能である。
上記J 2942038 明細書に記載のガラスは、S
i 0.の存在下で錯イオン(S’ (’tt (’
40 ) ) の重金属塩を形成し結晶化する傾向が極
めて大きいか、あるいはもしSt 01が削除されれば
化学安定性が極めて劣るかのいずれかであることで特徴
付けられる。さらに、これらのガラスは、高い屈折率を
得るために、35重量%までのtpo。
i 0.の存在下で錯イオン(S’ (’tt (’
40 ) ) の重金属塩を形成し結晶化する傾向が極
めて大きいか、あるいはもしSt 01が削除されれば
化学安定性が極めて劣るかのいずれかであることで特徴
付けられる。さらに、これらのガラスは、高い屈折率を
得るために、35重量%までのtpo。
と31重量%までの非常に高価なTa!011を含有す
ることが要求される。一方、西ドイツ特許用1iADE
−O53130039号に記載のガラスは、20以上の
屈折率と25〜43の範囲のアツベ数を有するが、それ
らの結晶化傾向のために、ガラス塊の急速な冷却が確保
されねばならず、小さな注型製造用にのみ使用すること
ができる。
ることが要求される。一方、西ドイツ特許用1iADE
−O53130039号に記載のガラスは、20以上の
屈折率と25〜43の範囲のアツベ数を有するが、それ
らの結晶化傾向のために、ガラス塊の急速な冷却が確保
されねばならず、小さな注型製造用にのみ使用すること
ができる。
非常に高い屈折率は非常に高価なTα、0.の量を増加
させ(20重量%まで)またPbOとTie。
させ(20重量%まで)またPbOとTie。
を付加(13重inまで)することによつ人のみ達成で
き、これは反面、ガラスの透過度に著しい悪影響を及は
す。
き、これは反面、ガラスの透過度に著しい悪影響を及は
す。
DE−O53130039号に特定されている5i0y
Bv Os = 1.3〜1.9という最適比は、本発
明による系において見い出されたものとは一致しない。
Bv Os = 1.3〜1.9という最適比は、本発
明による系において見い出されたものとは一致しない。
発明が解決しようとする問題点
本発明の目的は、比較的に低い分散性(アツベ数vd>
25)、高い化学安定性、及び丈寸法(例えば200
X 200 XlOom)の注型品が良好な光学品質で
注型できるように、すなわち気泡がt’sとんどなく、
またtlとんど光学的に不均質(zchli grdn
)でなく結晶もないように製造されるような高い結晶化
安定性を有する高−ないし超−屈折光学ガラス(nd〉
1.90 )としうる光学ガラス用組成範囲を見い出す
ことにある。さらに、これらの主たる要求を満足する他
に、500〜2400 nmの広いスペクトル域にわた
って高くまた一様な透過要求をも満足する光学ガラスを
提供することにある。
25)、高い化学安定性、及び丈寸法(例えば200
X 200 XlOom)の注型品が良好な光学品質で
注型できるように、すなわち気泡がt’sとんどなく、
またtlとんど光学的に不均質(zchli grdn
)でなく結晶もないように製造されるような高い結晶化
安定性を有する高−ないし超−屈折光学ガラス(nd〉
1.90 )としうる光学ガラス用組成範囲を見い出す
ことにある。さらに、これらの主たる要求を満足する他
に、500〜2400 nmの広いスペクトル域にわた
って高くまた一様な透過要求をも満足する光学ガラスを
提供することにある。
問題点を解決するための手段
本発明に係るガラスは、主としてS i 0.−B、0
゜−La、O3−Y 203−Tie、−Nb、O,−
Gd20.系1)範囲内にある。5番0v /Bt O
s比は0.1から1.6好1しくけ0.2から1.5の
範囲を有する。1.90以上の高い屈折率を得るために
は、35〜55重量%のLa2O1!並びに0.5〜l
0ift%のY2O3、並びに1〜16重量%好ましく
は10〜16重杯″チT i O,及びまた0、5〜1
51m%好ましくは1.5〜13重量%のNb、0.、
並びに0〜10M(量チのGd2O3が必要である。任
意成分として、0〜15重量%のTa2O,及び0〜2
重量−のYb、0sも含有することができる。B a
O及びPbOはZrLo、 SrO,Ca0 により置
き換えることができる。これらの酸化物の合計は0〜I
’5m8%が好ましい。本発明の系には、Zro、は0
〜10重量%好ましくは0〜8重量−の割合が望ましい
。さらに可能な成分は、0〜3重廿チ好ましくは0〜2
重−jk%p* o*、0〜2 M m、’ % Sn
0. 、 Q〜4重量%F、Q〜2重禁tlbBα0で
ある。
゜−La、O3−Y 203−Tie、−Nb、O,−
Gd20.系1)範囲内にある。5番0v /Bt O
s比は0.1から1.6好1しくけ0.2から1.5の
範囲を有する。1.90以上の高い屈折率を得るために
は、35〜55重量%のLa2O1!並びに0.5〜l
0ift%のY2O3、並びに1〜16重量%好ましく
は10〜16重杯″チT i O,及びまた0、5〜1
51m%好ましくは1.5〜13重量%のNb、0.、
並びに0〜10M(量チのGd2O3が必要である。任
意成分として、0〜15重量%のTa2O,及び0〜2
重量−のYb、0sも含有することができる。B a
O及びPbOはZrLo、 SrO,Ca0 により置
き換えることができる。これらの酸化物の合計は0〜I
’5m8%が好ましい。本発明の系には、Zro、は0
〜10重量%好ましくは0〜8重量−の割合が望ましい
。さらに可能な成分は、0〜3重廿チ好ましくは0〜2
重−jk%p* o*、0〜2 M m、’ % Sn
0. 、 Q〜4重量%F、Q〜2重禁tlbBα0で
ある。
すなわち、本発明に係る光学ガラスは重知°チで以下の
組成を有すること全特徴とするものである。
組成を有すること全特徴とするものである。
Sin、 OA+、10
Bt Us 2〜20
Al、0. 0−2
XSi0.、B、O3、Al、O3’75〜25T i
0. l〜16 ZrO,O〜10 Lα、0. 35〜55 Y、0. 0.5〜1O Nhy’e O,5〜l 5 Gtt、0sO〜I 0 Ta2O110〜15 P、 060〜3 その仙、o〜10重R% OBi、08.0〜2重iチ
のCt 0..0〜3重:ftt % ” jFOs’
k 含有ス;b ?ニー トもできる。
0. l〜16 ZrO,O〜10 Lα、0. 35〜55 Y、0. 0.5〜1O Nhy’e O,5〜l 5 Gtt、0sO〜I 0 Ta2O110〜15 P、 060〜3 その仙、o〜10重R% OBi、08.0〜2重iチ
のCt 0..0〜3重:ftt % ” jFOs’
k 含有ス;b ?ニー トもできる。
また、LaZOSが全部又は部分的に他の稀土類酸化物
によジ置換されてもよく、この場合の稀土類酸化物の合
計量は30〜55重おチであることが望ましい。
によジ置換されてもよく、この場合の稀土類酸化物の合
計量は30〜55重おチであることが望ましい。
発明の効果
本発明に係るガラスの奉賀的な特徴は、上記ガラス系に
あシ、前記したように結晶化安定性があシ、化学的に安
定で(例えば0.5 AI llNO3による麿き面か
ら、1μmの浸蝕時間が50時間以上である)、良好な
透過性及び良好な光学品質を有する高屈折乃至超高屈折
ガラスを生産可hヒである。
あシ、前記したように結晶化安定性があシ、化学的に安
定で(例えば0.5 AI llNO3による麿き面か
ら、1μmの浸蝕時間が50時間以上である)、良好な
透過性及び良好な光学品質を有する高屈折乃至超高屈折
ガラスを生産可hヒである。
実施例
好適な組成範囲の16の例を表−2に示す。
本発明に係るガラスは以下のようにして製造される:
原材料(酸化物、炭酸塩、硝酸塩、フッ化物)を計量し
、A〜03などの清澄剤をα1〜1重蓋チ添加し、全体
を十分に混合する。ついで、レリットを約1350〜+
450’Cでセラミックまたは白金るつは中で溶製し、
1500〜+550”cでBmし、攪拌器具により十分
に均質化する。約1350℃の注型温度及び約1 Q
dpasの粘度でガラスを金属製型中に注入する。
、A〜03などの清澄剤をα1〜1重蓋チ添加し、全体
を十分に混合する。ついで、レリットを約1350〜+
450’Cでセラミックまたは白金るつは中で溶製し、
1500〜+550”cでBmし、攪拌器具により十分
に均質化する。約1350℃の注型温度及び約1 Q
dpasの粘度でガラスを金属製型中に注入する。
1000kF 計算ガラスについての溶融例を下記表−
1に示す。
1に示す。
表−1
酸化物型iチ原材料計量重侮: (kg)Sin、 4
.50 45.09 B雪Os I O,O1lsBOs l 77、30L
cLxij35.0 Lavas 353.22F!
Us 10.OYxom 101.0fGd、O,7,
6Q Gd、0. 76、00Tie、 l’5.80
Tie、 158.15”Ox 7.50 Zr0.
75.25A’l)t(Jg 9’ 50 /l’b
tCJg 95−041081.06 清澄剤 AすUs 1.00 1082.05kgフリット このガラスの特性は表−2の例9に記載されている。
.50 45.09 B雪Os I O,O1lsBOs l 77、30L
cLxij35.0 Lavas 353.22F!
Us 10.OYxom 101.0fGd、O,7,
6Q Gd、0. 76、00Tie、 l’5.80
Tie、 158.15”Ox 7.50 Zr0.
75.25A’l)t(Jg 9’ 50 /l’b
tCJg 95−041081.06 清澄剤 AすUs 1.00 1082.05kgフリット このガラスの特性は表−2の例9に記載されている。
第1頁の続き
■Int、CI、’ 識別記号 庁内整理番号CD3
C47006674−4G @発 明 者 ヴオルクマール、ガイ ドイツ連邦共和
国、ラー ウスリング 239 @発 明 者 カール、メンネマン ドイツ連邦共和国
、ネンヴエーク 3 0発 明 者 ゲオルグ、グリ−メロ ドイツ連邦共和
国、−ス ウスリング 52
C47006674−4G @発 明 者 ヴオルクマール、ガイ ドイツ連邦共和
国、ラー ウスリング 239 @発 明 者 カール、メンネマン ドイツ連邦共和国
、ネンヴエーク 3 0発 明 者 ゲオルグ、グリ−メロ ドイツ連邦共和
国、−ス ウスリング 52
Claims (1)
- 【特許請求の範囲】 1、 重量%で以下の組成 Sin、 C1〜10 B、0. 2〜20 Al、0. o〜2 ΣS i O,、Bρ3、At、O,7,5〜25Ti
e、 ’1〜16 Zr0. O〜l 0 La2Om35〜55 Yt Os 0.5〜I 0 7Vh、0. 0.5〜15 Gd*0s O〜10 Ta!0110〜15 P宜0. Q〜3 を有することを特徴とする、屈折率≧1.90.アツベ
数≧25で、特に優れた化学安定性(0,5N11NO
8による麿き面から1μmの浸蝕時間が50時間以上で
ある)並びに+oodPα3未満の粘度範囲において高
い結晶化安定性をイjする光学ガラス。 ・ 2 重−ta:チで以下の組成 S i O,0,5〜1O B、 O,2〜20 At、0. 0〜1,5 Gem2’ 0〜2.0 ΣSiO,、GaO,、B、O3、Al、OB 7.5
〜25Tie、 IQ〜16 Zr0. O〜8 La20335〜55 Y、O,0,5〜l0 Nb、0. 1.5〜13 Tαρ、 0〜10 Pt0* 022 Gd、、0. 0〜10 を有することを特徴とする特許請求の範囲第1項に記載
のガラス。 3.0〜10重量%のBi、0.を含有することを特徴
とする特許請求の範囲第1項または第2項に記載のガラ
ス。 4.0〜2重′1に%の5rLO,を含有することを特
徴とする特I11!l−梢求の範囲第1項乃至第3項の
いずれかに記載のガラス。 5.0〜4重量%のF−を含有することを特徴とする特
許請求の範囲第1項乃至第4項のいずれかに記載のガラ
ス。 6、Btus 含量に対するSin、含量の比がα1〜
1.6の範囲にあることを特徴とする特許請求の範囲第
1項乃至第5項のいずれかに記載のガラスO 70〜15重JWc%の#O(コこでMo Cab、
SrO。 Bad、 ZnO,Pb0 )を含有することを特徴と
する特許請求の範囲第1項乃至第6項のいずれかに記載
のガラス。 8.0〜2重i’チのyb、o、全含有することを特徴
とする特許請求の範囲m1項乃至第7項のいずれかに記
載のガラス。 q、Nb!011とTα、0.との合計量が9〜20重
量係であることを特徴とする特許請求の範囲第1項乃至
第8項のいずれかに記載のガラス。 10、La、O,が全部又は部分的に他の稀土類酸化物
により置換され、また稀土類酸化物の合計量が30〜5
5重量%であることを特徴とする特許請求の範囲第1項
乃至第9項のいずれかに記載のガラス。 11.0〜2重量%のCgらを含有することを特徴とす
る特許請求の範囲第1項乃至第10項のいずれかに記載
のガラス。 12、 0〜3重iA:%のVIO8を含有することを
特徴とする特許請求の範囲第1項乃至第11項に記載の
ガラス。