JPS61280989A - 光学記録媒体 - Google Patents

光学記録媒体

Info

Publication number
JPS61280989A
JPS61280989A JP60119160A JP11916085A JPS61280989A JP S61280989 A JPS61280989 A JP S61280989A JP 60119160 A JP60119160 A JP 60119160A JP 11916085 A JP11916085 A JP 11916085A JP S61280989 A JPS61280989 A JP S61280989A
Authority
JP
Japan
Prior art keywords
recording film
tiox
recording
content
recording medium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP60119160A
Other languages
English (en)
Inventor
Yoichi Tsuchiya
洋一 土屋
Osamu Oota
修 太田
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sanyo Electric Co Ltd
Original Assignee
Sanyo Electric Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sanyo Electric Co Ltd filed Critical Sanyo Electric Co Ltd
Priority to JP60119160A priority Critical patent/JPS61280989A/ja
Publication of JPS61280989A publication Critical patent/JPS61280989A/ja
Pending legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】 印　産業上の利用分野 本発明は、レーザ光等の光及び熱エネルギーを用いて情
報を高密度に記録し、且つ再生可能な光学記録媒体に関
する。
（ロ）従来の技術 レーザ光等のエネルギービームを照射して、基板上の金
属等の薄膜を溶隔あるいは蒸発させ、ピットを形成する
方式の記録材料として社感度が高く、基板上の記録層の
膜厚が均一でちゃ、化学的、物理的にも安定で、長期に
わたって記録再生ができなければならない。この方式の
記録材料としてテルル（Ｔｅ）が一般的に知られている
。Ｔｅは熱伝導率が低く、光吸収係数が大きく、低線点
であるので感度の良い記鋒膜が得られるが、空気中の水
分によって容易に激化され、光学的に透明な二酸化テル
ル（Ｔｅ０２）ｉ’（変化するため信号が再生できなく
なり、長期間の情報の記録は非常に難しい。すなわち記
録寿命が短いという欠点を有している。
更に、Ｔｏ単体では、これにエネルギービームを照射し
、Ｔｅを蒸発除去して凹部あるいは孔を形成した場合、
凹部あるいはビットの形状が良好とならず、記録した信
号の再生信号０７Ｎ比を十分に向上せしめることができ
ない。
そこで、特公昭５９−５５５５６号公報に見られるよう
に、５〜５０原子数％のセレン（Ｓ６）をＴｏに含有せ
しめ、長寿命化を図ると共に再生信号０／Ｎ比を向上せ
しめた光学記録媒体が提案されている。
しかし乍ら、８ｅは人体にとって有害な物質であシ、光
学記録媒体の製造時あるいは使用時等において十分な注
意が必要となる。
また１本出願人は、特願昭６Ｏ−４５８７Ｓ号において
、長期間にわたって安定した情報の記録及び再生を行な
い得る改良された光学記録媒体として、Ｔａ（１００−
β）　（Ｔ　ｉｏａ　）β（ただし、０くα≦２．２≦
β≦１５；α、βはモル％を示す）からなる記録膜を基
板上に形成したものを提案している。
ｅ→　発明が解決しようとする問題点 ところで、光学記録媒体は、アクリル、ポリカーボネイ
ト等の透明樹脂を基板とし、該基板上に記ａｍを形成し
た構成である。従って、基板の熱膨張の影響により、記
録膜に放射状のクラックが発生する。
上述のＴｏ単体の記録膜においては、温度６０℃、湿度
９０％の雰囲気中に放置後、わずか１日でクラックが発
生し、また上述の改良された光学記録媒体においても、
数日から１週間でクラックが発生した。
こうしたクラックの発生は、情報の記録及び再生に大き
な悪影響を及ぼし、光学記録媒体の長寿薔化を妨ける。
従って、本発明の目的は、長期に亙ってクラックの発生
を防止することＫある。
に）問題点を解決するための手段 本発明は、基板上に形成された記録膜にエネヤギーを照
射することによって情報を記録する光学記録媒体におい
て、上記記録膜は、ＴｏとＴｉ０Ｘ（ｆｃだし、０＜１
≦２；ｘはモＡ／％を示す）とＩｎ％Ｐｂ、Ｂｉ、８ｎ
及び８ｂの群から選択された少なくとも１つとからな夛
、Ｔｏの含有率は７０モル％以上であると共ＫＴ４１及
びＴｉＯｘ以外の含有率は１０モル九から２０モル九の
範囲であることを特徴とする。
（ホ）作　用 Ｉｎ、Ｐｂ％Ｂｉ、８ｎ及び８ｂは粘性を有する元素で
あシ、これら元素を記録膜に含有せしめることＫよって
記録膜のクラックの発生が防止される。
（へ）実施例 第１図は本発明の一実施例を示す断面斜視図である。記
録膜（１）を内面に形成した円板状の透明基板（２）と
保護板（３）とが、２つのリング状スペーサ（４）（５
）により一定の間隔を空けて固定されている。なお、保
護板（３）を記録膜を形成した透明基板に変えることに
よって両面記録が可能となる。
透明基板（２）は、アクリル樹脂、ポリカーボネイト樹
脂、ポリメチルメタクリレート樹脂もしくはガラス等か
らなる。
記録膜（１）は、本発明の特徴であり、ＴｏとＴｉＯｘ
とＩｎ％Ｐｂ、Ｂｉ％８ｎ及び８ｂの群から選択された
少なくとも１つとから成・る。
以下、Ｅｌ＆膜（１）トしてＴｅ（１００−ｙ−ｚ）（
ＴｉＯｘ）ｙＩｎｓ（ただしＯ＜１≦２．１０≦２≦２
０、ｙ＋ｚ＜５０　ｔ　ｘｓ　ｙｓ　　ｚはモル％を示
す）なる組成を採用し、この記録膜（１）をアクリル樹
脂から成る透明基板（２）上に約３００人の厚さに形成
した実施例に対して行なった各種特性の試験結果にりい
て説明する。
第２図は、温度６０℃、湿度９０％の雰囲気中での加速
試験における経過日数と透過率（相対値）との関係を示
す。
また、第３図は、光学記録媒体の回転数６０Ｏｒｐｍ、
記録周波数２　Ｍ　Ｉｌ　ｚの条件で所望品位の記録再
生特性を満たすために半導体レーザに要求されるパワー
と光学記録媒体の半径との関係を示す。
なお、両図において、実線は本発明の記録膜で６ルＴ６
８２　（’ｌ’　ｉｏ！　）　３　Ｉ　ｎ１６及びＴ　
ｎ７８　（ＴｉＯり７Ｉｎ１５の特性を示し、破線は上
述の改良された記録膜であるＴａ５ｙ（ＴｉＯｘ）ａ及
び’ｌ！ｅ９３（ＴｉＯｘ）７Ｏ特性ヲ示シテイル。
両図から明らかなよ５に、本発明の記録膜は、改良され
た記＊＊とはとんと同じ寿命を有し、また半導体レーザ
の出力パワー上＠（７〜８ｍＷ）内の範囲で十分記録を
行な％Ａｌする。
ところで、本発明の特徴は、記録膜におけるクラックの
発生を防止したことにある。上述の改良された記録膜で
あるＴａＯ２（ＴｉＯＸ）３及びＴａＢ２（ＴｉＯＸ）
７と本発明の記録膜であるＴ。
８２（ＴｉＯＸ）３Ｉｎ１５及びＴ４１７８（Ｔ　ｉＯ
ｚ　）７　Ｉ　ｎ　１６とを夫々温度６０℃、湿度９０
％の雰囲気中に放置した結果、ＴａＯ２（ＴｉＯＸ）３
及びＴａＯ３（ＴｊＯｘ）７においては、放置開始後数
日から１週間でクラックが発生したのに対し、ＴａＢ２
（Ｔ　ｉＯｘ　）　３１　ｎ１Ｍ及びＴｅｙ８（ＴｉＯ
ｘ）７Ｉｎ１５においては、６０日経過後もクラックは
発生しない。更に、上記雰囲気中での放置実験を行なっ
た結果、Ｉｎの含有率が１０モル％以上の場合で゛あれ
ば、クラック発生を効果的に防止することができる。
一方、第４図はＴｏ（９ｓ−ｚ　）（Ｔｉ０ｘ）ｓＩｎ
ｚＫおけるＩｎの含有率２と再生信号０／Ｎ比との関係
を示す。なお、斯る関係は光学記録媒体の回転数７０Ｏ
ｒｐｍ、再生信号周波数２Ｍｌ１２の条件によるもので
ある。Ｉｎの含有率２が増茄するに従って再生信号のＣ
７Ｎ比は低下するが、Ｉｎの含有率２が２０モル％以下
であれば、４５ｄＢ以上のＣ／Ｎ比を得ることができ、
光学記録媒体として使用可能である。
以上のことから、Ｉｎの含有率２は１０≦２≦２０が好
ましい。
また、Ｔｅ（１００−７−２）（ＴｉＯｚ）ｙＩｎｚに
おいて、Ｔ　ｉＯｘ及びＩｎの含有率（ｙ＋Ｚ）が３０
モル％を越えると信号記録時の凹部あるいはビットの形
状を良好に行なうことができ。
ない。従って、Ｔ　ｉＯｘ及びＩｎの含有率（ｙ＋２）
はｙ＋ｚ＜ｓｏであることが望ましい。
更に％Ｔｉの酸化物ＴｉＯｘは’ｒｉＯ％Ｔｉｚ０３も
しくはＴｉＯ２のいずれかの形態で形成されるので、Ｏ
＜１≦２となる。
上述から明らかなように、Ｔｅ（１ｏｏ−ｙ−ｚ）（Ｔ
ｉＯｘ）ｙＩｎｚ（２）記録膜において、０＜Ｘ、Ｓ２
．１０≦２≦２０及び７＋Ｚ＜３０の条件を満たすこと
Ｋよって記録膜として使用し得るに必要な寿命及び特性
を備えると共にクラックの発生を防止することができる
。
１ｎＫ代えて、Ｐｂ％Ｂｉ、８ｎ及びＳｂのいずれかの
元素を使用しても、上述とほは同様の特性及び効果が得
られる。
（ト）発明の効果 本発明によれば、クラックの発生を防止することができ
、光学記録媒体のよシ一層の長寿命化を図ることができ
る。
【図面の簡単な説明】
各図は本発明の一実施例に係り、第１図は光学記録媒体
の断面斜視図、第２図は相対的透過率の加速試験結果を
示す特性図、第３図は光学記録媒体の半径とレーザパワ
ーとの関係を示す特性図、第４図はＩｎの含有率と再生
信号のＣ／Ｎ比との関係を示す特性図である。 （１）・・・・・・記録膜。 出麩三洋電機株式会社

Claims (1)

    【特許請求の範囲】
  1. （１）基板上に形成された記録膜にエネルギーを照射す
    ることによって情報を記録する光学記録媒体において、
    上記記録膜は、ＴｅとＴｉＯ＿ｘ（ただし、０＜ｘ≦２
    ；ｘはモル％を示す）とＩｎ、Ｐｂ、Ｂｉ、Ｓｎ及びＳ
    ｂの群から選択された少なくとも１つとからなり、Ｔｅ
    の含有率は７０モル％以上であると共にＴｅ及びＴｉＯ
    ＿ｘ以外の含有率は１０モル％から２０モル％の範囲で
    あることを特徴とする光学記録媒体。
JP60119160A 1985-05-31 1985-05-31 光学記録媒体 Pending JPS61280989A (ja)