JPS6237571A - Conductive oil seal - Google Patents
Conductive oil sealInfo
- Publication number
- JPS6237571A JPS6237571A JP60178077A JP17807785A JPS6237571A JP S6237571 A JPS6237571 A JP S6237571A JP 60178077 A JP60178077 A JP 60178077A JP 17807785 A JP17807785 A JP 17807785A JP S6237571 A JPS6237571 A JP S6237571A
- Authority
- JP
- Japan
- Prior art keywords
- conductive
- oil seal
- rubber
- rolling bearing
- rubber composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【発明の詳細な説明】
〔産業上の利用分野〕
この発明は、自動車等に装着されるころがり軸受と併用
されるオイルシールに関し、更に詳しくは、導電性材料
をもって形成された導電性オイルシールに関する。[Detailed Description of the Invention] [Industrial Application Field] The present invention relates to an oil seal used in combination with a rolling bearing installed in an automobile, etc., and more particularly relates to a conductive oil seal formed of a conductive material. .
−Ｓに、自動車の車輪に対する回転駆動手段には、第１
図に例示するように、ハウジング１および回転軸２の間
に介挿されたころがり軸受３が使用されて、このころが
り軸受３に対する潤滑剤のシール手段として、ゴム状弾
性材料をもって製せられ、回転側周面と弾性的に接触し
て摺動する１９７１部４およびダストリップ部５とを具
えるシール部片６を有するオイルシール７が使用されて
いる。-S, the rotary drive means for the wheels of the automobile includes a first
As illustrated in the figure, a rolling bearing 3 inserted between a housing 1 and a rotating shaft 2 is used as a lubricant sealing means for the rolling bearing 3, and is made of a rubber-like elastic material and is An oil seal 7 is used which has a sealing piece 6 with a 1971 part 4 and a dust lip part 5 sliding in elastic contact with the side circumferential surface.
（発明が解決しようとする問題点〕
上記した軸受構造においては、ころがり軸受け３が、回
転中に電気的絶縁状態に陥り、それに伴い、ころがり軸
受内における静電気の放電現象が惹起されるために、こ
れを解決する手段を講しることが要求されている。(Problems to be Solved by the Invention) In the bearing structure described above, the rolling bearing 3 falls into an electrically insulated state during rotation, and as a result, electrostatic discharge phenomenon occurs within the rolling bearing. There is a need to take measures to solve this problem.
一方、ころがり軸受３に対する潤滑剤の漏洩を阻止する
手段として併用されているオイルシール７は、ゴム様弾
性材料をもって製せられ、回転側の周面に弾性的に接触
してシール作用をなすソール部片６が電気的な絶縁性を
示すので、このオイルシールを経由する専電性回路の形
成を期待することができない。On the other hand, the oil seal 7, which is also used as a means for preventing leakage of lubricant from the rolling bearing 3, is made of a rubber-like elastic material, and has a sole that elastically contacts the circumferential surface of the rotating side to perform a sealing action. Since the piece 6 exhibits electrical insulation, it is not possible to expect the formation of an electrically exclusive circuit via this oil seal.
この発明は、上記したころがり軸受内における電気的絶
縁状態の発生に伴うトラブルを防止することを目的とす
るものである。The object of the present invention is to prevent troubles caused by the occurrence of the electrically insulated state within the rolling bearing described above.
この発明は、上記した従来技術による回転支持部におけ
る放電現像の問題に鑑み、ころがり軸受のためのＡ’８
／（ｆ剤の漏洩阻止手段として併設されるオイルシー
ルおよび接着剤に４電性を付与することにより、ころが
り軸受およびオイルシールを介挿されるハウジングとシ
ャフトの間に、オイルシールを経由する導電回路を形成
させて、ころがり軸受内における放電現像を防止するも
のである。In view of the above-mentioned problem of discharge development in a rotary support part according to the prior art, this invention provides an A'8
/(By imparting 4-electricity to the oil seal and adhesive installed as means for preventing leakage of the f agent, a conductive circuit via the oil seal is created between the housing and the shaft in which the rolling bearing and oil seal are inserted. is formed to prevent discharge development within the rolling bearing.
オイルシールに対する導電性の付与は、オイルシールの
ゴム部分の導電性を示すゴム組成物を用いて形成するか
、或いは通常の組成によるゴム材＄４により成形された
ゴム部分の表面に導電性を示す組成のゴム材料による表
面被覆層を設定することが考えられる。Conductivity can be imparted to the oil seal by forming the rubber portion of the oil seal using a rubber composition that exhibits conductivity, or by imparting conductivity to the surface of the rubber portion molded from a rubber material with a normal composition. It is conceivable to provide a surface coating layer made of a rubber material having the composition shown below.
この場合、第３図示のようにゴム部分がオイルシールの
全体を覆っているものに関しては上記の２つのことは有
効であるが、第２図示のようにゴム部分が全体を覆って
いない場合は有効でない。In this case, the above two things are valid if the rubber part covers the entire oil seal as shown in the third diagram, but if the rubber part does not cover the entire oil seal as shown in the second diagram, Not valid.
ぷ電性を示すゴム組成物を用いたオイルシールではゴム
部分と金属との間の接着剤が絶縁物のために軸受けで生
じる静電気がハウジングへ逃げることがない。In an oil seal using a rubber composition exhibiting static electricity, the adhesive between the rubber part and the metal is an insulator, so static electricity generated in the bearing does not escape to the housing.
そこで、接着剤に導電性を付与する必要が生した。この
場合、接着剤としては、たとえば、塩化ゴム系、エポキ
シ樹脂系、フェノール樹脂系等が挙げられるが、これに
導電性物質、たとえば、カーボンブラック、グラファイ
ト、カーボン繊維、金属メッキしたガラス繊維や合成繊
維、金属粉、金属繊維等を、好ましくはカーボンブラッ
クＥＣ，アセチレンブラック、ＥＣＦカーボンを加えて
導電性接着剤として用いる。Therefore, it became necessary to impart electrical conductivity to the adhesive. In this case, adhesives include, for example, chlorinated rubber, epoxy resin, phenol resin, etc., but conductive substances such as carbon black, graphite, carbon fiber, metal-plated glass fiber, and synthetic Fibers, metal powder, metal fibers, etc. are used as the conductive adhesive, preferably with the addition of carbon black EC, acetylene black, or ECF carbon.
また、 導電性を示すゴム材料の組成としては、例えば
ニトリルゴム、弗素ゴム等の合成ゴム１００重部に対し
、２０〜６０重量部、成形性の面から、好ましくは３０
〜５０の重量部のグラファイトおよび１０〜８０重量部
、好ましくは４０〜６０重量部のカーボンブラックを配
合したものが良好な導電性を示し、導電性を確実にする
ためには、カーボンブラックとしてアセチレブラノクも
しくはケッチンブラックを使用することが好ましく、こ
れらを使用する場合は、カーボン量が少量であっても良
好な導電性が得られる。The composition of the conductive rubber material is, for example, 20 to 60 parts by weight per 100 parts of synthetic rubber such as nitrile rubber or fluorine rubber, and from the viewpoint of moldability, preferably 30 parts by weight.
A blend of ~50 parts by weight of graphite and 10-80 parts by weight, preferably 40-60 parts by weight of carbon black shows good electrical conductivity; Alternatively, it is preferable to use Kettin black, and when these are used, good conductivity can be obtained even if the amount of carbon is small.
カーボンブラックに代えて、金属粉または、例えば、酸
化鉄、硫化亜鉛、硫化銅等の金属化合物の微粉、もしく
はカーボン短繊維、メタライズド短繊維等を用いること
もできる。Instead of carbon black, metal powder or fine powder of a metal compound such as iron oxide, zinc sulfide, copper sulfide, carbon short fibers, metallized short fibers, etc. can also be used.
また、通常のゴム組成物に導電性ゴム材料で表面処理を
施したものについては、その表面処理を金属の部分にま
で施し全体を覆ってやればよい。Furthermore, if a normal rubber composition is surface-treated with a conductive rubber material, the surface treatment may be applied to the metal portion to cover the entire surface.
通常のゴム組成物を用いて成形したオイルシールに対し
、導電性を備えるゴム組成物による表面被覆層を施す手
段としては、ゴム部分の成形に先だって、通常の組成に
よるゴム材料および導電性組成によるゴム材料を配置し
て、二層成形をするか、通常のゴム材料により成形され
たゴム部分の被覆対象面を研磨またはスパンタエソチン
グ等の方法により表面を粗になした後に、液状の導電性
ゴム組成物をスプレーまたは刷手塗りにより積層する方
法が有効である。As a means of applying a surface coating layer of a conductive rubber composition to an oil seal molded using a normal rubber composition, prior to molding the rubber part, a rubber material of a normal composition and a conductive composition are applied. After arranging the rubber material and performing two-layer molding, or roughening the surface of the rubber part molded from ordinary rubber material by polishing or spunter etching, etc., liquid conductive An effective method is to laminate the rubber composition by spraying or hand-coating with a brush.
上記したように、導電性を備えるゴム組成物により成形
されるか、もしくは表面被覆層を形成された導電性オイ
ルシールと、導電性接着剤とを用いたころがり軸受構造
においては、ころがり軸受を介挿されるハウジングと回
転軸とが、導電性オイルシールにより電気的に接続され
る。As mentioned above, in a rolling bearing structure using a conductive oil seal molded from a conductive rubber composition or having a surface coating layer formed thereon, and a conductive adhesive, the rolling bearing is The inserted housing and rotating shaft are electrically connected by a conductive oil seal.
導電性ゴム組成物の配合の一例として下に示す表−１の
組成により材料を用いた。As an example of the formulation of the conductive rubber composition, materials were used according to the composition shown in Table 1 below.
表−１
〔以下、余白］
また、導電性接着剤組成物の配合の一例として下の組成
材料を用いた。Table 1 [Hereinafter, blank space] In addition, the composition materials below were used as an example of the formulation of the conductive adhesive composition.
メタロ、り １００
アセチレンブラツク １０
なお、メタロツクは東洋化学研究断裂であり、また、ア
セチレンブラックは電気化学工業■製である。Metallic 100 Acetylene Black 10 Metallic is manufactured by Toyo Kagaku Kenkyuken, and acetylene black is manufactured by Denki Kagaku Kogyo ■.
上記接着剤をオイルシール缶にスプレー塗布後、上記ゴ
ムと加硫接着した（１７０℃Ｘｌ０ｍ１ｎ ）。 この
ようにして作成したｉＴｌ性オイルシールのリップ部と
はめ合い部分との接触抵抗値は２．３Ｘ１０”Ωであっ
た。The above adhesive was spray applied to an oil seal can, and then vulcanized and bonded to the above rubber (170°C x 10ml). The contact resistance value between the lip portion and the fitting portion of the iTl oil seal thus prepared was 2.3×10”Ω.
なお、上記接着剤（メタロツクＮＴ）を用いた場合は６
．８Ｘ１０”Ωであった。In addition, when using the above adhesive (Metallock NT), 6
．． It was 8×10”Ω.
この発明は前記のようであるために、この発明による４
電性オイルシールを併設された軸受構造においては、こ
ろがり軸受を介挿されるハウジングと回転軸が、導電性
オイルシールにより、電気的に接続されるので、ころが
り軸受内部における放電現象が完全に防止されるなどの
すぐれた効果を有するものである。Since this invention is as described above, the four
In a bearing structure equipped with an electrically conductive oil seal, the housing into which the rolling bearing is inserted and the rotating shaft are electrically connected by the electrically conductive oil seal, completely preventing electrical discharge inside the rolling bearing. It has excellent effects such as:
第１図は、この発明の対象となる軸受部の構造を示す断
面図、第２図および第３図は一般的な構造を示す部分断
面図である。
１・・・・・・ハウジング
２・・・・・・回転軸
３・・・・・・ころがり軸受
４・・・・・・主リップ
５・・・・・・ダストリップ部
６・・・・・・シール都度
７・・・・・・オイルシール
第１図
第２図
第３図
手 続 粕１１ 正 書 （自発）
昭和６０年ＩＯ月２４日
１、￥田牛の表示 昭和６０年 特許間 第１７
８０７７号２、発明の名称 導電性オ イ ル シ
− ル３、補正をする者
門生との関係 特許出願人
住所 東京都港区芝大門１丁目１２番１５号氏
名 （名称） エヌオーケー株式会社４、代理人
■１０２ 置（イ）２６２−４７６１）住所
東京都千代田区九段南３丁目８番１３号７、補正の内容
■ 特許請求の範囲を別紙のように補正する。
■ 明細書第２頁第１９行目の「回転側Ｊを「回転軸」
と補正する。
■ 同書同頁第７行目の「主リップ」を「主リップ」と
補正する。
■ 同書第３頁第１１行目の「ゴム様弾性体」を「ゴム
状弾性体」と補正する。
■ 同書同頁第７行目の「回転側」を「回転軸」と補正
する。
■ 同書同頁第１９行目の「解決するこめの」を「解決
するための」と補正する。
■ 同書第５頁第１０行目〜第１１行目の「カーボンブ
ラックＥＣＪを「ケッチェンブラックＥＣＪと補正する
。
■ 同書第６頁第１行目の「ケッチンブラック」を「ケ
ッチェンブランクＥＣＪと補正する。
■ 同書第９頁第４行目の「メタロツク」を「メタロツ
クＮＴＪと補正する。
［相］ 同書同頁第７行目の「メタロツク」を「メタロ
ックＮＴＪと補正する。
■ 同書同頁第１０行目の「−ト記」の後に「組成の」
を挿入する。
＠ 同書同頁第１１行目〜第１２行目の［加硫接着・・
・・・・ｍｉｎ ）。」を「加硫接着しく１７０°Ｃ×
１０ｍ１ｎ ）第２図の様なオイルシールを作成した。
」と補正する。
■ 同書同頁第１４行目の１−であった。Ｊの後に「ま
た、第３図の様に全体を、ｉ７７電性ゴム組成物で覆っ
た形のオイルノールについても、この様な導電性接着剤
を用いることにより、ゴムと環とが導通し、ご通路が広
くなり、抵抗値が小さくなることは容易に考えられる。
」を挿入する。
■ 同書同頁第１５行目の「上記接着剤・・・・・・を
用いＪをｉ−接着剤としてメタロツクＮＴのみを用い」
と補正する。
■ 同書同頁第１６行目のｒ６．８Ｘ１０２Ω」をｒ６
．８Ｘ１０６Ω」と補正する。
［相］ 同書第１０頁第１３行目の「４・・・・・・主
゛ノツプ」を「４・・・・・・主リップ部」と補正する
。
Ｏ同書同頁第１５行目の１６・・・・ソール都度−１を
「６・・・・・・、ノール部片」と補正する。
８ 添付書題の目録
別紙 ・・・・・・ １通以上
別紙
特許請求の範囲
（１）導電性ゴム組成物と、導電性を有する補強環と、
導電性接着剤とにより形成された導電性オイルシール。
（２） 前記導電性ゴム組成物が、ゴムと導電性物質
とからなる特許請求の範囲第１項記載の導電性オイルシ
ール。
（３）前記導電性物質が、カーボンブラックである特許
請求の範囲第２項記載の導電性オイルシール。
（４）前記導電性ゴム組成物が、ゴム１００重量部に対
し、１０〜８０重量部のカーボンブラックと、２０〜６
０重里部のグラファイトとを含有している特許請求の範
囲第２項記載の導電性オイルシール。
（５）前記導電性ゴム組成物が、カーボンブラックの代
わりに金属粉、金属化合物の微粉、カーボン短繊維また
はメタライズド短繊維を含有している特許請求の範囲第
２項記載の導電性オイルシール。
（６）前記ｉｖ導電性接着剤、ゴムまたは樹脂と、カー
ボンブラック、金属粉等の導電性物質とからなる特許請
求の範囲第１１．Ｑ記載の導電性オイルシール。FIG. 1 is a cross-sectional view showing the structure of a bearing section to which the present invention is applied, and FIGS. 2 and 3 are partial cross-sectional views showing a general structure. 1...Housing 2...Rotating shaft 3...Rolling bearing 4...Main lip 5...Dust lip portion 6... ...Seal 7 each time...Oil seal Figure 1 Figure 2 Figure 3 Procedure Kasu 11 Original (self-motivated) IO month 24, 1985 1, ￥ Tagyu display 1985 Patent interval No. 17
8077 No. 2, Title of the invention Conductive oil seal 3, Relationship with the person making the amendment Patent applicant address 1-12-15 Shiba Daimon, Minato-ku, Tokyo Name (Name) NK Co., Ltd. 4 agent
■102 (I) 262-4761) Address
7-8-13, Kudanminami 3-chome, Chiyoda-ku, Tokyo Contents of amendment■ The scope of the claims will be amended as shown in the attached sheet. ■ "Rotation side J" on page 2, line 19 of the specification "rotation axis"
and correct it. ■ "Main lip" in line 7 on the same page of the same book is corrected to "main lip." ■ "Rubber-like elastic body" on page 3, line 11 of the same book is corrected to "rubber-like elastic body." ■ Correct "rotation side" in line 7 of the same page of the same book to "rotation axis". ■ In the 19th line of the same page of the same book, "to solve" is amended to "to solve". ■ "Carbon black ECJ" in lines 10 to 11 of page 5 of the same book is corrected to "Ketjen black ECJ." ■ "Ketjen black" in line 1 of page 6 of the same book is changed to "Ketjen blank ECJ. Correct. ■ “Metallock” in the 4th line of page 9 of the same book is corrected as “Metallock NTJ.” [Phase] “Metallock” in the 7th line of the same page of the same book is corrected as “Metallock NTJ.” ■ Same page of the same book After “-tki” in the 10th line, “composition”
Insert. @ Same book, same page, lines 11-12 [Vulcanized adhesive...
...min). ” to “vulcanized adhesive at 170°C
10m1n) An oil seal as shown in Figure 2 was created. ” he corrected. ■ It was 1- on the 14th line of the same page in the same book. J is followed by ``Also, for the oil nol whose entire body is covered with i77 conductive rubber composition as shown in Figure 3, by using such a conductive adhesive, the rubber and the ring will be electrically conductive. , it is easy to imagine that the passage will become wider and the resistance value will become smaller.'' ■ On the same page of the same book, line 15: “Use the above adhesive, use J as i-adhesive, and use only Metalock NT.”
and correct it. ■ “r6.8X102Ω” on the 16th line of the same page
．． 8×106Ω”. [Phase] "4...Main knob" on page 10, line 13 of the same book is corrected to "4...Main lip portion." O Same book, same page, line 15, 16... -1 for each sole is corrected to "6..., Knoll piece". 8 Attachment with list of attached document titles...One or more attached documentsClaims (1) A conductive rubber composition, a reinforcing ring having conductivity,
Conductive oil seal formed with conductive adhesive. (2) The conductive oil seal according to claim 1, wherein the conductive rubber composition comprises rubber and a conductive substance. (3) The conductive oil seal according to claim 2, wherein the conductive substance is carbon black. (4) The conductive rubber composition contains 10 to 80 parts by weight of carbon black and 20 to 6 parts by weight based on 100 parts by weight of rubber.
3. The electrically conductive oil seal according to claim 2, which contains graphite of zero weight. (5) The conductive oil seal according to claim 2, wherein the conductive rubber composition contains metal powder, fine metal compound powder, short carbon fibers, or metallized short fibers instead of carbon black. (6) Claim 11. The iv conductive adhesive, rubber or resin, and a conductive substance such as carbon black or metal powder. Conductive oil seal described in Q.
Claims (6)
れた導電性オイルシール。(1) A conductive oil seal formed from a conductive rubber composition and a conductive adhesive.
し、１０〜８０重量部のカーボンブラックと、２０〜６
０重量部のグラファイトとを含有している特許請求の範
囲第１項記載の導電性オイルシール。(2) The conductive rubber composition contains 10 to 80 parts by weight of carbon black and 20 to 6 parts by weight based on 100 parts by weight of rubber.
The conductive oil seal according to claim 1, which contains 0 parts by weight of graphite.
りに金属粉、金属化合物の微粉、カーボンカーボン短繊
維またはメタライズド短繊維を含有している特許請求の
範囲第２項記載の導電性オイルシール。(3) The conductive oil seal according to claim 2, wherein the conductive rubber composition contains metal powder, fine metal compound powder, carbon-carbon short fibers, or metallized short fibers instead of carbon black. .
る特許請求の範囲第１項記載の導電性オイルシール。(4) The conductive oil seal according to claim 1, wherein the entire rubber portion is formed of a conductive rubber composition.
覆層を付されてなる特許請求の範囲第１項に記載の導電
性オイルシール。(5) The conductive oil seal according to claim 1, wherein the surface of the rubber portion is provided with a surface coating layer made of a conductive rubber material.
ンブラック、金属粉等の導電性物質とからなる特許請求
の範囲第１項記載の導電性オイルシール。(6) The conductive oil seal according to claim 1, wherein the conductive adhesive comprises rubber or resin and a conductive substance such as carbon black or metal powder.