KR20200055837A - Decoration film expressing metalic appearance and manufacturing method of the same - Google Patents

Decoration film expressing metalic appearance and manufacturing method of the same Download PDF

Info

Publication number
KR20200055837A
KR20200055837A KR1020180138317A KR20180138317A KR20200055837A KR 20200055837 A KR20200055837 A KR 20200055837A KR 1020180138317 A KR1020180138317 A KR 1020180138317A KR 20180138317 A KR20180138317 A KR 20180138317A KR 20200055837 A KR20200055837 A KR 20200055837A
Authority
KR
South Korea
Prior art keywords
pigment
layer
metal
colored
coating layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
KR1020180138317A
Other languages
Korean (ko)
Inventor
김현철
김진호
정재헌
배수연
성태현
Original Assignee
주식회사 상보
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 상보 filed Critical 주식회사 상보
Priority to KR1020180138317A priority Critical patent/KR20200055837A/en
Publication of KR20200055837A publication Critical patent/KR20200055837A/en
Ceased legal-status Critical Current

Abstract

본 발명은 금속 외관 효과를 가지는 데코레이션 필름에 관한 것으로, 보다 상세하게는 기재층; 상기 기재층 하부에 위치하는 유색의 패턴층; 상기 패턴층 하부에 위치하는 유색 또는 투명 코팅층; 및 상기 코팅층 하부에 위치하는 반사층;을 포함하고, 상기 반사층은 상기 코팅층 일면에 금속을 웨트(wet) 코팅 방식으로 분사하여 제조함으로써, 별도의 금속증착층 또는 금속시트를 사용하지 않더라도 패턴 후면으로 입사된 빛을 상기 반사층을 통해 반사시킴으로써 우수한 금속 질감을 구현할 수 있는 데코레이션 필름에 관한 것이다.The present invention relates to a decoration film having a metal appearance effect, more specifically, a base layer; A colored pattern layer located under the base layer; A colored or transparent coating layer located under the pattern layer; And a reflective layer located under the coating layer, wherein the reflective layer is manufactured by spraying a metal on one surface of the coating layer by a wet coating method, so that a separate metal deposition layer or a metal sheet is not used, but is incident on the back of the pattern. It relates to a decoration film that can implement an excellent metal texture by reflecting the light through the reflective layer.

Description

금속 외관 효과를 가지는 데코레이션 필름 및 그 제조방법{Decoration film expressing metalic appearance and manufacturing method of the same}Decoration film expressing metalic appearance and manufacturing method of the same}

본 발명은 금속 외관 효과를 가지는 데코레이션 필름 및 그 제조방법에 관한 것이다.The present invention relates to a decoration film having a metallic appearance effect and a method for manufacturing the same.

최근 모바일기기 등을 비롯한 가전기기나 가구 등은 금속판재를 사용하지 않고도 금속 외관 효과를 갖는 필름을 부착하여, 마치 금속과 같은 외관상 미려하고 고급스런 이미지를 갖도록 하면서도 제작비용은 낮출 수 있는 효과를 얻고 있다. 과거에는 금속 소재를 직접 사용하다보니 절단, 절삭 및 굴곡 등의 가공이 어려운 문제가 있었고, 가격도 고가라는 문제점이 있었으나, 최근에는 가공성이 우수하고, 비교적 가격이 저렴한 플라스틱 소재에 금속 소재와 유사한 질감 효과를 구현하여 인테리어 등과 같은 데코레이션 소재로 널리 사용되고 있는 실정이다. 이러한 금속 외관 효과를 얻는 대표적인 방법으로, 플라스틱 필름을 이루는 기재층 사이에 헤어라인(hairline) 무늬를 형성하는 것을 들 수 있다. 이를 위해 종래에는 PET 필름 상부 또는 하부에 헤어라인 무늬를 갖도록 스크린 인쇄 후, 인쇄면 상에 금속증착층을 형성하여 합성수지 필름을 제조하였다. 그러나, 이러한 종래 방식은 금속증착(또는 금속스퍼터링) 공정을 거쳐야 하므로 비용이 올라가는 원인이 되었을 뿐만 아니라 공정과정도 복잡해지는 한계가 있었다.Recently, home appliances, furniture, etc., including mobile devices, have the effect of lowering the production cost while attaching a film with a metallic appearance effect without using a metal plate, so as to have a beautiful and luxurious image like a metal. have. In the past, there was a problem in that machining such as cutting, cutting, and bending was difficult due to the direct use of a metal material, and there was a problem in that the price was high, but recently, a plastic material with excellent processability and relatively low price has similar texture to the metal material. It has been widely used as a decoration material such as interiors by realizing effects. As a representative method for obtaining such a metal appearance effect, forming a hairline pattern between the base layers forming the plastic film may be mentioned. To this end, conventionally, after screen printing to have a hairline pattern on the top or bottom of the PET film, a metal deposition layer was formed on the printing surface to produce a synthetic resin film. However, such a conventional method has a limitation in that the process is complicated as well as causing a cost increase since a metal deposition (or metal sputtering) process is required.

이에 본 발명은 상기와 같은 문제점을 해결하기 위하여, 데코레이션 필름의 적층 구조가 기재층; 상기 기재층 하부에 위치하는 유색의 패턴층; 상기 패턴층 하부에 위치하는 코팅층; 및 상기 코팅층 하부에 위치하는 반사층을 포함하도록 하되, 상기 코팅층 일면에 금속을 웨트(wet) 코팅 방식으로 분사하여 상기 반사층을 제조함으로써, 별도의 금속소재를 증착 또는 스퍼터링하거나 별도의 금속소재 시트를 사용하지 않더라도 우수한 금속 외관 효과를 구현할 수 있는 데코레이션 필름을 제공하는데 목적이 있다.Accordingly, the present invention is to solve the above problems, the laminate structure of the decoration film is a base layer; A colored pattern layer located under the base layer; A coating layer positioned under the pattern layer; And to include a reflective layer located under the coating layer, by spraying a metal on one surface of the coating layer by a wet (wet) coating method to prepare the reflective layer, by depositing or sputtering a separate metal material or using a separate metal material sheet An object of the present invention is to provide a decoration film capable of realizing an excellent metal appearance effect.

상기의 목적을 달성하기 위하여, 본 발명의 일 구현예는 기재층; 상기 기재층 하부에 위치하는 유색의 패턴층; 상기 패턴층 하부에 위치하는 유색 또는 투명 코팅층; 및 상기 코팅층 하부에 위치하는 반사층; 을 포함하고, 상기 반사층은 상기 코팅층 일면에 금속을 웨트(wet) 코팅 방식으로 분사하여 제조되는 것을 특징으로 한다.In order to achieve the above object, an embodiment of the present invention is a substrate layer; A colored pattern layer located under the base layer; A colored or transparent coating layer located under the pattern layer; And a reflective layer positioned under the coating layer. Including, the reflective layer is characterized in that it is produced by spraying a metal on one surface of the coating layer by a wet (wet) coating method.

상기 금속은 알루미늄일 수 있다.The metal may be aluminum.

상기 반사층은 20nm 내지 5㎛의 두께를 가질 수 있다.The reflective layer may have a thickness of 20nm to 5㎛.

상기 코팅층은 무색의 자외선 경화형 수지일 수 있다.The coating layer may be a colorless UV curable resin.

상기 코팅층 및 패턴층은 각각 독립적으로 유색의 자외선 경화형 수지일 수 있다.The coating layer and the pattern layer may be independently colored UV curable resins.

상기 코팅층 및 패턴층은 각각 독립적으로 착색제가 혼합된 자외선 경화형 수지 조성물에 의해 형성되며, 상기 착색제는 나노 입자를 가지는 무기 안료, 유기 안료, 염료 또는 잉크를 포함할 수 있다.Each of the coating layer and the pattern layer is independently formed by an ultraviolet curable resin composition in which a colorant is mixed, and the colorant may include an inorganic pigment having nanoparticles, an organic pigment, dye or ink.

상기 자외선 경화형 수지 조성물은 아크릴레이트 올리고머와 모노머, 광개시제 및 첨가제를 포함할 수 있다.The ultraviolet curing resin composition may include an acrylate oligomer and a monomer, a photoinitiator, and additives.

상기 유기 안료는 페릴렌, 프탈로시아닌 안료, 시아닌 안료, 나프탈로시아닌 안료, 니트로소 안료, 모노-아조 안료, 디-아조 안료, 디-아조 축합 안료, 염기성 안료, 알칼리 블루 안료, 블루 레이크 안료, 프록신 안료, 퀴나크리돈 안료, 이소-인돌리논 안료, 디-옥사진 안료, 카바졸 디-옥사진 바이올렛 안료, 알리자린 레이크 안료, 프탈록시 아민 안료, 카민 레이크 안료, 테트라클로로이소인돌리논 안료, 페리논 안료, 티오-인디고 안료, 안트라퀴논 안료, 퀴노프탈론 안료 또는 이들의 조합을 포함할 수 있다.The organic pigment is perylene, phthalocyanine pigment, cyanine pigment, naphthalocyanine pigment, nitroso pigment, mono-azo pigment, di-azo pigment, di-azo condensation pigment, basic pigment, alkali blue pigment, blue lake pigment, proxine Pigment, quinacridone pigment, iso-indolinone pigment, di-oxazine pigment, carbazole di-oxazine violet pigment, alizarin lake pigment, phthaloxyamine pigment, carmine lake pigment, tetrachloroisoindolinone pigment, perinone Pigments, thio-indigo pigments, anthraquinone pigments, quinophthalone pigments, or combinations thereof.

상기 무기 안료는 금속 산화물, 카본블랙 안료, 금속 황화물, 금속 염화물 또는 이들의 조합을 포함할 수 있다.The inorganic pigment may include metal oxide, carbon black pigment, metal sulfide, metal chloride, or a combination thereof.

상기 기재층은 PET(polyethylene terephthalate), TPU(Thermoplastic Poly Urethane), PBT(polybutylene terephthalate), PP(polypropylene), PE(polyethylene), PVC(poly vinyl chloride), PMMA(poly methyl methacrylate), ABS(acrylonitrile-butadiene-styrene), PC(polycarbonate), SAN(styrene-acrylonitrile copolymer) 또는 이들의 조합일 수 있다.The substrate layer is PET (polyethylene terephthalate), TPU (Thermoplastic Poly Urethane), PBT (polybutylene terephthalate), PP (polypropylene), PE (polyethylene), PVC (poly vinyl chloride), PMMA (poly methyl methacrylate), ABS (acrylonitrile) -butadiene-styrene), polycarbonate (PC), styrene-acrylonitrile copolymer (SAN), or a combination thereof.

본 발명의 다른 일 구현예는 기재층을 형성하는 단계; 상기 기재층의 배면에 유색의 자외선 경화형 수지에 미세 패턴이 형성된 마스터 몰드를 압착한 후 자외선을 투사함으로써 경화시켜 입체적인 미세 패턴을 구비하는 유색의 패턴층을 형성하는 단계; 상기 패턴층의 배면에 유색 또는 무색의 자외선 경화형 수지를 코팅한 후 자외선을 투사함으로써 경화시킨 코팅층을 형성하는 단계; 및 상기 코팅층의 배면에 금속을 웨트(wet) 코팅 방식으로 분사하여 반사층을 형성하는 단계로 이루어지는 데코레이션 필름의 제조방법을 제공한다.Another embodiment of the present invention includes forming a base layer; Forming a colored pattern layer having a three-dimensional fine pattern by pressing and curing a master mold having a fine pattern formed on a colored ultraviolet curable resin on the back surface of the base layer and then projecting ultraviolet rays; Coating a colored or colorless ultraviolet curable resin on the back surface of the pattern layer and then forming a cured coating layer by projecting ultraviolet light; And it provides a method for producing a decoration film comprising the step of forming a reflective layer by spraying a metal on the back surface of the coating layer by a wet (wet) coating method.

기타 본 발명의 측면들의 구체적인 사항은 이하의 상세한 설명에 포함되어 있다.Other details of aspects of the present invention are included in the detailed description below.

본 발명에 따르면 별도의 금속 소재를 사용하지 않더라도 유색의 패턴층과 패턴 사이에 존재하는 공기층 간의 굴절율 차이에 의하여 금속 외관 효과를 구현할 수 있으며, 금속 소재를 증착하거나 별도의 금속 시트를 사용하지 않음으로써 제조비용을 낮출 수 있을 뿐만 아니라 종래 필수 구성 중 하나인 증착 공정 또는 금속시트 접착공정이 필요하지 않게 되므로 제조공정을 더욱 효율적으로 운영할 수 있는 효과가 있다.According to the present invention, even if a separate metal material is not used, a metal appearance effect can be realized by a difference in refractive index between a colored pattern layer and an air layer existing between the patterns, and by not depositing a metal material or using a separate metal sheet Not only can the manufacturing cost be lowered, but a deposition process or a metal sheet adhesion process, which is one of the essential components of the prior art, is not required, so that the manufacturing process can be operated more efficiently.

도 1은 본 발명에 따른 데코레이션 필름의 제1 실시예를 개략적으로 나타내는 단면도이다.1 is a cross-sectional view schematically showing a first embodiment of a decoration film according to the present invention.

본 발명의 바람직한 실시예들을 상세히 설명하기로 한다. 그러나, 본 발명은 여기서 설명되는 실시예에 한정되지 않고 다른 형태로 구체화될 수도 있다. 오히려, 여기서 소개되는 실시예들은 개시된 내용이 철저하고 완전해질 수 있도록 그리고 당업자에게 본 발명의 사상이 충분히 전달될 수 있도록 하기 위해 제공되는 것이다. It will be described in detail preferred embodiments of the present invention. However, the present invention is not limited to the embodiments described herein and may be embodied in other forms. Rather, the embodiments introduced herein are provided to ensure that the disclosed contents are thorough and complete and that the spirit of the present invention is sufficiently conveyed to those skilled in the art.

이하에서는 첨부된 도면을 참조하여 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 본 발명을 용이하게 실시할 수 있도록 바람직한 실시예를 상세히 설명한다. 다만, 본 발명의 바람직한 실시예를 상세하게 설명함에 있어, 관련된 공지 기능 또는 구성에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명을 생략한다. 또한, 유사한 기능 및 작용을 하는 부분에 대해서는 도면 전체에 걸쳐 동일 또는 유사한 부호를 사용한다.Hereinafter, preferred embodiments will be described in detail with reference to the accompanying drawings so that those skilled in the art to which the present invention pertains can easily implement the present invention. However, in the detailed description of the preferred embodiment of the present invention, when it is determined that a detailed description of related known functions or configurations may unnecessarily obscure the subject matter of the present invention, the detailed description will be omitted. In addition, the same or similar reference numerals are used throughout the drawings for parts having similar functions and functions.

덧붙여, 명세서 전체에서, 어떤 부분이 다른 부분과 '연결'되어 있다고 할 때, 이는 '직접적으로 연결'되어 있는 경우뿐만 아니라, 그 중간에 다른 소자를 사이에 두고 '간접적으로 연결'되어 있는 경우도 포함한다. 또한, 어떤 구성요소를 '포함'한다는 것은, 특별히 반대되는 기재가 없는 한 다른 구성요소를 제외하는 것이 아니라 다른 구성요소를 더 포함할 수 있다는 것을 의미한다.In addition, throughout the specification, when a part is said to be 'connected' to another part, it is not only 'directly connected', but also 'indirectly connected' with another element in between. Includes. In addition, "including" a component means that other components may be further included instead of excluding other components, unless otherwise stated.

이하, 첨부한 도면에 참고로 하여 본 발명에 따른 데코레이션 필름(10)을 상세히 설명하기로 한다. 참고로, 본 발명의 데코레이션 필름(10)에서 상하 구분은 최종 완성된 제품을 기준으로 한 것이다. 일 예로, 유색의 패턴층(110) 하부에 위치하는 유색 또는 투명 코팅층(120)의 의미는 완성된 데코레이션 필름(10)을 기준으로 유색의 패턴층(110) 하부에 유색 또는 투명 코팅층(120)이 위치하는 상태를 표현한 것이며, 실제 패턴층(110) 형성 시 편의에 따라 데코레이션 필름(10) 뒤집은 상태에서 유색의 패턴층 위로 유색 또는 투명 코팅층(120)을 형성시켜 위치하도록 할 수 있다. 또한, 상기 '~층 하부에 위치'한다는 의미가 반드시 하부에 접착된 형태만을 의미하지 않으며, 필요에 따라 별도의 접착층 또는 이형 필름층이 삽입된 경우도 포함할 수 있다. 또한, 본 발명의 명세서에서 사용하는 '금속 외관 효과'의 의미는 금속과 같이 일정 무늬의 빛을 반사하고 광택을 내는 질감 효과를 갖는 것을 의미한다.Hereinafter, the decoration film 10 according to the present invention will be described in detail with reference to the accompanying drawings. For reference, the top and bottom division in the decoration film 10 of the present invention is based on the final finished product. For example, the meaning of the colored or transparent coating layer 120 positioned under the colored pattern layer 110 is based on the finished decoration film 10, colored or transparent coating layer 120 under the colored pattern layer 110. This is a representation of the position, and in accordance with convenience when the actual pattern layer 110 is formed, the colored or transparent coating layer 120 can be positioned over the colored pattern layer in a state where the decoration film 10 is turned over. In addition, the meaning of 'located at the bottom of the layer' does not necessarily mean a form adhered to the bottom, and may include a case where a separate adhesive layer or a release film layer is inserted as necessary. In addition, the meaning of 'metal appearance effect' used in the specification of the present invention means that it has a texture effect that reflects light of a certain pattern and gives a gloss like metal.

도 1은 본 발명에 따른 데코레이션 필름(10)의 제1 실시예를 개략적으로 나타내는 단면도이다. 도 1에 도시된 바와 같이, 상기 데코레이션 필름(10)은 기재층(100); 상기 기재층(100) 하부에 위치하는 유색의 패턴층(110); 상기 유색의 패턴층(110) 하부에 위치하는 유색 또는 투명 코팅층(120); 및 상기 코팅층(120) 하부에 위치하는 반사층(130)을 포함하는 형태이며, 특별히 상기 반사층(130)은 상기 코팅층(120) 일면에 금속을 웨트(wet) 코팅 방식으로 분사하여 제조되는 것이 특징이다.1 is a cross-sectional view schematically showing a first embodiment of the decoration film 10 according to the present invention. As shown in Figure 1, the decoration film 10 is a base layer 100; A colored pattern layer 110 positioned under the base layer 100; A colored or transparent coating layer 120 positioned under the colored pattern layer 110; And a reflective layer 130 located under the coating layer 120. In particular, the reflective layer 130 is manufactured by spraying a metal on one surface of the coating layer 120 by a wet coating method. .

종래에는 코팅층 일면에 금속을 증착하거나 스퍼터링하여 금속층을 형성시킨 후 상기 코팅층과 접촉하지 않는 상기 금속층의 다른 일면에 기재층을 형성시키거나, 박판 형태를 가지는 별도의 금속 시트를 상기 코팅층 일면에 접착제를 도포한 후 부착함으로써, 상기 금속층 또는 금속 시트를 통해 일정 무늬의 빛을 반사시켜, 금속 질감을 구현하였다.Conventionally, after depositing or sputtering a metal on one side of the coating layer to form a metal layer, a base layer is formed on the other side of the metal layer that does not contact the coating layer, or a separate metal sheet having a thin plate form is attached to the adhesive side of the coating layer. By applying and attaching after coating, a certain pattern of light is reflected through the metal layer or metal sheet to realize a metal texture.

그러나, 종래 방식으로 금속 질감을 구현하기 위해서는 별도의 증착 또는 스퍼터링 공정이나 접착 공정이 필요한데, 상기 공정을 수행하는 기기가 고가이고, 또 접착 공정을 수행하기 위해서는 별도의 접착층을 추가해야 해서, 최종적으로 제조되는 데코레이션 필름의 가격을 낮추는 데 한계가 있었으며, 이는 저렴한 가격으로 고급스런 금속 질감의 이미지를 구현하고자 하는 수요자들의 요구를 온전히 반영하지 못하는 가장 큰 요인 중 하나였다. 또한, 증착 또는 스퍼터링 공정의 경우 그 두께를 수십 나노미터 단위 정도까지 늘릴 수 있었고, 그보다 두꺼운 마이크로미터 단위 정도까지 두께를 늘리는 데는 한계가 있어, 종래의 데코레이션 필름은 이를 적용할 수 있는 어플리케이션에도 한계가 있었다.However, in order to implement a metal texture in a conventional manner, a separate deposition or sputtering process or an adhesion process is required, and the equipment for performing the process is expensive, and a separate adhesive layer must be added to perform the adhesion process. There was a limit to lowering the price of the decoration film being manufactured, and this was one of the biggest factors that could not fully reflect the demands of consumers who wanted to realize a high-quality metal texture image at an affordable price. In addition, in the case of a deposition or sputtering process, it was possible to increase the thickness to about several tens of nanometers, and there is a limit to increase the thickness to a thicker micrometer, so the conventional decoration film has limitations in the application to which it can be applied. there was.

그러나, 일 구현예에 따르면 별도의 증착이나 스퍼터링 공정도 불요하고, 별도의 금속 시트를 접착할 필요도 없이, 기재층; 상기 기재층 하부에 위치하는 유색의 패턴층; 상기 패턴층 하부에 위치하는 유색 또는 투명 코팅층; 및 상기 코팅층 하부에 위치하는 반사층을 포함하는 적층 구조에서, 금속을 웨트 코팅 방식으로 상기 유색의 패턴층과 접촉하지 않는 상기 코팅층의 일면에 분사하여 상기 반사층을 제조함으로써, 종래와 동등한 수준의 금속 질감을 가지는 데코레이션 필름을 매우 경제적으로 제조할 수 있다. 나아가, 일 구현예에 따르면 금속을 웨트 코팅 방식으로 분사하여 제조하는 바, 상기 반사층의 두께를 수십 나노미터 단위에서 마이크로미터 단위까지 늘릴 수 있어, 매우 다양한 어플리케이션, 예컨대 모바일 기기, 가전기기, 가구 및 내장재 등에 적용할 수 있다.However, according to one embodiment, a separate deposition or sputtering process is also unnecessary, and there is no need to adhere a separate metal sheet, the base layer; A colored pattern layer located under the base layer; A colored or transparent coating layer located under the pattern layer; And in a layered structure including a reflective layer located under the coating layer, by spraying a metal on one surface of the coating layer that does not contact the colored pattern layer by wet coating method to prepare the reflective layer, the metal texture equivalent to the conventional level Decoration film having a can be produced very economically. Furthermore, according to an embodiment, the metal is spray-coated to produce a bar, and the thickness of the reflective layer can be increased from tens of nanometers to micrometers, so a wide variety of applications such as mobile devices, home appliances, furniture, and It can be applied to interior materials.

상기 금속은 알루미늄일 수 있다.The metal may be aluminum.

상기 반사층은 20nm 내지 5㎛의 두께를 가질 수 있다.The reflective layer may have a thickness of 20nm to 5㎛.

유색의 패턴층(110)은 유색의 자외선 경화형 수지일 수 있는데, 이는 기재층(100)에 자외선 경화형 수지 조성물을 도포한 다음 미세 패턴이 형성된 성형롤러 또는 마스터 몰드(미도시)로 미세 패턴을 형성시킨 후 자외선 경화 과정을 거치게 되면, 기재층(110) 하부에 보다 용이하게 입체적인 미세 패턴을 구비하는 유색의 패턴층(110)을 형성시킬 수 있다. The colored pattern layer 110 may be a colored UV curable resin, which is coated with a UV curable resin composition on the base layer 100 and then forms a fine pattern with a molding roller or master mold (not shown) on which a fine pattern is formed. After being subjected to an ultraviolet curing process, a colored pattern layer 110 having a three-dimensional fine pattern may be more easily formed under the base layer 110.

기재층(100)은 PET(polyethylene terephthalate), TPU(Thermoplastic Poly Urethane), PBT(polybutylene terephthalate), PP(polypropylene), PE(polyethylene), PVC(poly vinyl chloride), PMMA(poly methyl methacrylate), ABS(acrylonitrile-butadiene-styrene), PC(polycarbonate), SAN(styrene-acrylonitrile copolymer) 또는 이들의 조합을 사용할 수 있으며, 바람직하게는 투명의 필름일 때 빛의 투과율이 높아 입사 빛에 미치는 영향이 적어진다. 상기 필름 중 PET 필름 또는 TPU 필름을 사용하게 되면 두께를 얇게 할 수 있고, 균일성 및 투명도가 우수하다. 참고로, 기재층(100)의 두께는 15㎛ 내지 200㎛ 인 것이 바람직하다.The base layer 100 is PET (polyethylene terephthalate), TPU (Thermoplastic Poly Urethane), PBT (polybutylene terephthalate), PP (polypropylene), PE (polyethylene), PVC (poly vinyl chloride), PMMA (poly methyl methacrylate), ABS (acrylonitrile-butadiene-styrene), PC (polycarbonate), SAN (styrene-acrylonitrile copolymer), or a combination thereof can be used. Preferably, when the film is transparent, the light transmittance is high, so the effect on incident light is reduced. . If a PET film or a TPU film is used, the thickness can be reduced, and uniformity and transparency are excellent. For reference, the thickness of the base layer 100 is preferably 15㎛ to 200㎛.

기재층(100) 하부에는 유색의 패턴층(110)이 위치하고, 상기 유색의 패턴층 하부에는 유색 또는 투명 코팅층(120)이 위치한다. 상기 투명 코팅층은 무색의 자외선 경화형 수지일 수 있다. 예컨대, 상기 코팅층은 유색 코팅층일 수 있으며, 상기 유색 코팅층은 데코레이션 필름(10)의 배면방향으로부터 입사되는 광을 차폐하는 역할을 수행할 수 있다. 유색의 패턴층(110) 및 유색의 코팅층(120)은 각각 독립적으로 유색의 자외선 경화형 수지인 것이 바람직한데, 이는 기재층(100)에 자외선 경화형 수지 조성물을 도포하고 미세 패턴이 형성된 성형롤러 또는 마스터 몰드(미도시)로 미세 패턴을 형성시킨 후 자외선 경화를 시키면, 기재층(100) 하부에 보다 용이하게 입체적인 미세 패턴을 구비하는 유색의 패턴층(110)을 형성시킬 수 있기 때문이다. 참고로 유색의 패턴층(110)의 두께는 5㎛ 내지 50㎛ 인 것이 미세 패턴 라인이 육안으로 현저하게 관측되지 않고, 자연스러운 금속 질감을 구현할 수 있다는 측면에서 유리할 수 있다. 또한, 유색의 패턴층(110)에 형성된 미세 패턴은 2㎛ 내지 40㎛ 깊이로 홈을 형성하는 것이 상기 유색의 패턴층과 상기 유색 또는 투명 코팅층(120) 간의 접착력 확보 및 자연스러운 금속 질감 구현 측면에서 유리할 수 있다.A colored pattern layer 110 is positioned below the base layer 100, and a colored or transparent coating layer 120 is positioned below the colored pattern layer. The transparent coating layer may be a colorless UV curable resin. For example, the coating layer may be a colored coating layer, and the colored coating layer may serve to shield light incident from the rear direction of the decoration film 10. It is preferable that the colored pattern layer 110 and the colored coating layer 120 are each independently a colored UV curable resin, which is coated with a UV curable resin composition on the base layer 100 and formed with a fine patterned forming roller or master. This is because the colored pattern layer 110 having a three-dimensional fine pattern can be more easily formed under the base layer 100 by ultraviolet curing after forming a fine pattern with a mold (not shown). For reference, the thickness of the colored pattern layer 110 may be advantageous in that the fine pattern lines are not significantly observed with the naked eye and a natural metal texture can be realized. In addition, in the fine pattern formed on the colored pattern layer 110, forming grooves with a depth of 2 µm to 40 µm in terms of securing adhesion between the colored pattern layer and the colored or transparent coating layer 120 and realizing a natural metal texture It can be advantageous.

상기 자외선 경화형 수지 조성물은 아크릴레이트 올리고머와 모노머, 광개시제 및 첨가제를 포함할 수 있다. The ultraviolet curing resin composition may include an acrylate oligomer and a monomer, a photoinitiator, and additives.

상기 아크릴계 올리고머로는 우레탄계, 에폭시계, 에스테르계, 에테르계 또는 실리콘계 중 선택된 하나일 수 있으며, 바람직하게는 디이소시아네이트, 폴리올 및 메타아크릴레이트를 반응시켜 제조한 폴리우레탄 아크릴레이트를 사용하는 것일 수 있다. 또한, 상기 광개시제는 통상적인 것으로 아세토페논계 화합물, 벤조페논계 화합물, 티오크산톤계 화합물, 벤조인계 화합물, 트리아진계 화합물, 옥심계 화합물 등을 사용할 수 있고, 예컨대, Irgacure 184, SPI-03 등과 같은 광개시제를 사용할 수 있고, Tinuvin 400과 같은 광안정제를 병용할 수 있다.The acrylic oligomer may be one selected from urethane-based, epoxy-based, ester-based, ether-based or silicone-based, preferably using a polyurethane acrylate prepared by reacting diisocyanate, polyol and methacrylate. . In addition, the photoinitiator is a common acetophenone compound, benzophenone compound, thioxanthone compound, benzoin compound, triazine compound, oxime compound, etc. can be used, for example, Irgacure 184, SPI-03, etc. The same photoinitiator can be used, and a photostabilizer such as Tinuvin 400 can be used in combination.

유색의 패턴층(110)은 착색제가 혼합된 자외선 경화형 수지 조성물에 의해 형성될 수 있다. 상기 착색제는 나노 입자를 가지는(10 nm 이상 1000 nm 미만의 크기를 가지는) 무기 안료, 유기 안료, 염료 또는 잉크를 포함할 수 있다. 상기 안료의 일 예를 들면, 자가-분산된 안료, 중합체-코팅된 안료, 또는 분쇄된 안료와 같은 통상의 안료일 수 있다. 상기 자외선 경화형 수지 조성물 내에 안료를 적절하게 현탁시키기 위하여 별개의 분산제가 사용될 수 있다. 상기 분산제는 상기 안료가 분산액 내에 균일하게 분산되도록 도와주며, 비이온성, 음이온성 또는 양이온성의 분산제 모두 사용할 수 있다. 구체적으로는 폴리알킬렌 글리콜 또는 이의 에스테르, 폴리옥시 알킬렌, 다가 알콜 에스테르 알킬렌 옥사이드 부가물, 알코올 알킬렌 옥사이드 부가물, 술폰산 에스테르, 술폰산 염, 카르복시산 에스테르, 카르복시산 염, 알킬 아미드 알킬렌 옥사이드 부가물, 알킬 아민 등을 사용할 수 있으며, 이들은 단독으로 또는 2종 이상을 혼합하여 사용할 수 있다.The colored pattern layer 110 may be formed of an ultraviolet curable resin composition mixed with a colorant. The colorant may include an inorganic pigment having nanoparticles (having a size of 10 nm or more and less than 1000 nm), an organic pigment, dye or ink. For example, the pigment may be a conventional pigment such as a self-dispersed pigment, a polymer-coated pigment, or a ground pigment. A separate dispersant may be used to properly suspend the pigment in the UV curable resin composition. The dispersant helps the pigment to be uniformly dispersed in the dispersion, and any nonionic, anionic or cationic dispersant can be used. Specifically, polyalkylene glycol or an ester thereof, polyoxyalkylene, polyhydric alcohol ester alkylene oxide adduct, alcohol alkylene oxide adduct, sulfonic acid ester, sulfonic acid salt, carboxylic acid ester, carboxylic acid salt, alkyl amide alkylene oxide addition Water, alkyl amines, and the like can be used, and these may be used alone or in combination of two or more.

상기 안료는 흑색, 청색, 갈색, 시안색, 녹색, 백색, 보라색, 마젠타색, 적색, 오렌지색 및 황색을 포함한 특정 색상뿐만 아니라 이들의 혼합물로부터 얻어지는 스폿 컬러(spot color)일 수 있다. 유기 안료의 예로는, 예시적이고 비제한적이지만, 페릴렌, 프탈로시아닌 안료(예를 들면, 프탈로 그린, 프탈로 불루), 시아닌 안료(Cy3, Cy5, 및 Cy7), 나프탈로시아닌 안료, 니트로소안료, 모노-아조 안료, 디-아조 안료, 디-아조 축합 안료, 염기성 안료, 알칼리 블루 안료, 블루 레이크 안료, 프록신 안료, 퀴나크리돈 안료, 이소-인돌리논 안료, 디-옥사진 안료, 카바졸 디-옥사진 바이올렛 안료, 알리자린 레이크 안료, 프탈록시 아민 안료, 카민 레이크 안료, 테트라클로로이소인돌리논 안료, 페리논 안료, 티오-인디고 안료, 안트라퀴논 안료 및 퀴노프탈론 안료, 및 상기 안료들 중 2가지 이상의 혼합물 및 상기 안료의 유도체를 포함한다. 상기 자외선 경화형 수지 조성물 내에 존재할 수 있는 무기 안료는, 예를 들면, 금속 산화물(예를 들면, 이산화티타늄, 전기전도성 이산화티타늄, 산화철(예를 들면, 적색 산화철, 황색 산화철, 흑색 산화철 및 투명 산화철), 산화알루미늄, 산화규소), 카본블랙 안료(예를 들면, 퍼니스 블랙(furnace black)), 금속 황화물, 금속 염화물, 및 이들 중 2가지 이상의 혼합물을 포함할 수 있다. 상기 착색제는 자외선 경화형 수지 조성물 총 중량의 0.1 중량% 내지 10 중량%의 범위에서 포함되는 것이 금속 외관 효과에 바람직하다.The pigments can be spot colors obtained from certain colors, including black, blue, brown, cyan, green, white, purple, magenta, red, orange and yellow, as well as mixtures thereof. Examples of organic pigments include, but are not limited to, perylene, phthalocyanine pigments (e.g., phthalo green, phthalofluoro), cyanine pigments (Cy3, Cy5, and Cy7), naphthalocyanine pigments, nitroso pigments, Mono-azo pigment, di-azo pigment, di-azo condensation pigment, basic pigment, alkali blue pigment, blue lake pigment, proxine pigment, quinacridone pigment, iso-indolinone pigment, di-oxazine pigment, carbazole Di-oxazine violet pigment, alizarin lake pigment, phthaloxy amine pigment, carmine lake pigment, tetrachloroisoindolinone pigment, perinone pigment, thio-indigo pigment, anthraquinone pigment and quinophthalone pigment, and among these pigments Mixtures of two or more and derivatives of the pigments. Inorganic pigments that may be present in the UV curable resin composition include, for example, metal oxides (eg titanium dioxide, electrically conductive titanium dioxide, iron oxides (eg, red iron oxide, yellow iron oxide, black iron oxide, and transparent iron oxide). , Aluminum oxide, silicon oxide), carbon black pigments (eg, furnace black), metal sulfides, metal chlorides, and mixtures of two or more of these. The colorant is preferably included in the range of 0.1% to 10% by weight of the total weight of the ultraviolet curable resin composition for metal appearance effect.

상기 염료로는 트리아릴메탄계 염료, 안트라퀴논계 염료, 벤질리덴계 염료, 시아닌계 염료, 프탈로시아닌계 염료, 아자포피린계 염료, 인디고계 염료, 크산텐계 염료 등을 사용할 수 있으나, 반드시 이에 한정되는 것은 아니다.As the dye, a triarylmethane-based dye, anthraquinone-based dye, benzylidene-based dye, cyanine-based dye, phthalocyanine-based dye, azapophyrin-based dye, indigo-based dye, and xanthene-based dye may be used, but are not limited thereto. It is not.

상기 잉크는 금속 분말을 포함할 수 있다. 상기 잉크에 포함되는 금속 분말은 플레이크(flake)나 펄(pearl) 등의 형태를 가지며, 후술하는 반사층뿐만 아니라 상기 금속 분말을 통해서도 금속 색상을 나타내도록 할 수 있다. The ink may include metal powder. The metal powder contained in the ink may have a flake or pearl shape, and may exhibit a metallic color through the metal powder as well as the reflective layer described later.

코팅층(120) 하부에는 금속을 웨트 코팅 방식으로 분사하여 형성된 반사층(130)이 위치하여 패턴 후면 표면으로 입사된 빛을 반사시켜 우수한 금속 질감을 구현할 수 있다. 유색의 패턴층(110) 및 코팅층(120) 사이 그리고 코팅층(120) 및 반사층(130) 사이에는 별도의 접착층 등이 위치하지 않을 수 있으며, 접착층을 형성하지 않는 대신, 금속을 유색의 패턴층(110) 하부에 위치하는 코팅층(120) 하부에 금속을 웨트 코팅 방식으로 분사해 형성함으로써, 보다 경제적이며 다양한 어플리케이션에 적용이 가능한, 종래와 동등 수준 이상의 우수한 금속 질감을 표현하여 미려한 외관을 구현할 수 있는 데코레이션 필름을 제공할 수 있다.The reflective layer 130 formed by spraying metal with a wet coating method is positioned under the coating layer 120 to reflect light incident on the rear surface of the pattern to realize excellent metal texture. A separate adhesive layer or the like may not be located between the colored pattern layer 110 and the coating layer 120 and between the coating layer 120 and the reflective layer 130, and instead of forming an adhesive layer, the metal is formed of a colored pattern layer ( 110) By spraying and forming the metal under the coating layer 120 located at the bottom by wet coating, it can be applied to more economical and various applications, and it can realize a beautiful appearance by expressing excellent metal texture equivalent to or higher than the conventional one. A decoration film can be provided.

이하에서는 본 발명에 따른 금속 외관 효과를 가지는 데코레이션 필름의 제조예들을 설명한다. 그러나 본 발명의 권리범위는 이하에서 개시되는 제조예에 한정되는 것이 아니며, 본 발명의 청구항의 기재에 의해 정해지는 것은 당연하다 할 것이다.Hereinafter, manufacturing examples of a decoration film having a metal appearance effect according to the present invention will be described. However, the scope of the present invention is not limited to the manufacturing examples disclosed below, and it will be obvious that it is determined by the description of the claims of the present invention.

[제조예][Production example]

50㎛ 두께의 투명 PET 필름 일면에 무기안료를 포함한 자외선 경화형 수지 조성물을 15㎛ 두께로 도포한 후, 성형롤러를 통해 미세 패턴(요철)을 형성하고, UV 조사를 통해 자외선 경화를 시켜 유색의 패턴층을 형성하였다.After applying a UV-curable resin composition containing an inorganic pigment to a surface of 50 μm thick transparent PET film to a thickness of 15 μm, a fine pattern (irregularity) is formed through a molding roller, and UV curing is performed through UV irradiation to give a colored pattern. A layer was formed.

다음으로, 유기안료를 포함한 자외선 경화형 수지 조성물을 15㎛ 두께로 상기 유색의 패턴층 일면(상기 투명 PET 필름과 마주하지 않는 면)에 도포한 후, UV 조사를 통해 자외선 경화를 시켜 유색의 코팅층을 형성하였다.Next, an ultraviolet curable resin composition containing an organic pigment is applied to one surface of the colored pattern layer (a surface that does not face the transparent PET film) to a thickness of 15 μm, followed by ultraviolet curing through UV irradiation to obtain a colored coating layer. Formed.

이 후, 웨트 코팅 방식으로 알루미늄을 상기 코팅층 일면(상기 패턴층과 마주하지 않는 면)에 분사시켜 1㎛ 두께로 반사층을 형성하여, 데코레이션 필름을 제조하였다. Thereafter, aluminum was sprayed on one surface of the coating layer (a surface not facing the pattern layer) by a wet coating method to form a reflective layer with a thickness of 1 μm, thereby preparing a decoration film.

이상과 같이, 첨부한 도면을 참고로 본 발명에 따른 데코레이션 필름의 실시예를 설명하였으나, 본 발명은 상기 설명된 실시예에 한정되는 것이 아니라 본 발명이 속하는 기술적 사상의 범위 내에서 다양한 형태로 변형될 수 있음은 자명하다 할 것이다.As described above, the embodiment of the decoration film according to the present invention has been described with reference to the accompanying drawings, but the present invention is not limited to the above-described embodiments but is modified in various forms within the scope of the technical spirit to which the present invention pertains. It is obvious that it can be done.

10 : 데코레이션 필름 100 : 기재층
110 : 유색의 패턴층 120 : 코팅층
130 : 반사층10: decoration film 100: base layer
110: colored pattern layer 120: coating layer
130: reflective layer

Claims (11)

기재층;
상기 기재층 하부에 위치하는 유색의 패턴층;
상기 패턴층 하부에 위치하는 유색 또는 투명 코팅층; 및
상기 코팅층 하부에 위치하는 반사층;
을 포함하고,
상기 반사층은 상기 코팅층 일면에 금속을 웨트(wet) 코팅 방식으로 분사하여 제조되는 데코레이션 필름.
Base layer;
A colored pattern layer located under the base layer;
A colored or transparent coating layer located under the pattern layer; And
A reflective layer located under the coating layer;
Including,
The reflective layer is a decoration film produced by spraying a metal on one surface of the coating layer by a wet coating method.
제1항에서,
상기 금속은 알루미늄인 데코레이션 필름.
In claim 1,
The metal is an aluminum decorative film.
제1항에서,
상기 반사층은 20nm 내지 5㎛의 두께를 가지는 데코레이션 필름.
In claim 1,
The reflective layer is a decoration film having a thickness of 20nm to 5㎛.
제1항에서,
상기 코팅층은 무색의 자외선 경화형 수지인 데코레이션 필름.
In claim 1,
The coating layer is a colorless UV curable resin decoration film.
제1항에서,
상기 코팅층 및 패턴층은 각각 독립적으로 유색의 자외선 경화형 수지인 데코레이션 필름.
In claim 1,
The coating layer and the pattern layer are each independently colored ultraviolet curing resin decorative film.
제5항에서,
상기 코팅층 및 패턴층은 각각 독립적으로 착색제가 혼합된 자외선 경화형 수지 조성물에 의해 형성되며,
상기 착색제는 나노 입자를 가지는 무기 안료, 유기 안료, 염료 또는 잉크를 포함하는 데코리이션 필름.
In claim 5,
Each of the coating layer and the pattern layer is independently formed by an ultraviolet curable resin composition in which a colorant is mixed,
The coloring agent is a decorative film comprising an inorganic pigment, an organic pigment, a dye or ink having nanoparticles.
제6항에서,
상기 자외선 경화형 수지 조성물은 아크릴레이트 올리고머와 모노머, 광개시제 및 첨가제를 포함하는 데코레이션 필름.
In claim 6,
The UV curable resin composition is a decoration film comprising an acrylate oligomer and a monomer, a photoinitiator and additives.
제6항에서,
상기 유기 안료는 페릴렌, 프탈로시아닌 안료, 시아닌 안료, 나프탈로시아닌 안료, 니트로소 안료, 모노-아조 안료, 디-아조 안료, 디-아조 축합 안료, 염기성 안료, 알칼리 블루 안료, 블루 레이크 안료, 프록신 안료, 퀴나크리돈 안료, 이소-인돌리논 안료, 디-옥사진 안료, 카바졸 디-옥사진 바이올렛 안료, 알리자린 레이크 안료, 프탈록시 아민 안료, 카민 레이크 안료, 테트라클로로이소인돌리논 안료, 페리논 안료, 티오-인디고 안료, 안트라퀴논 안료, 퀴노프탈론 안료 또는 이들의 조합을 포함하는 데코레이션 필름.
In claim 6,
The organic pigment is perylene, phthalocyanine pigment, cyanine pigment, naphthalocyanine pigment, nitroso pigment, mono-azo pigment, di-azo pigment, di-azo condensation pigment, basic pigment, alkali blue pigment, blue lake pigment, proxine Pigment, quinacridone pigment, iso-indolinone pigment, di-oxazine pigment, carbazole di-oxazine violet pigment, alizarin lake pigment, phthaloxyamine pigment, carmine lake pigment, tetrachloroisoindolinone pigment, perinone Decoration film comprising a pigment, thio-indigo pigment, anthraquinone pigment, quinophthalone pigment, or combinations thereof.
제6항에서,
상기 무기 안료는 금속 산화물, 카본블랙 안료, 금속 황화물, 금속 염화물 또는 이들의 조합을 포함하는 데코레이션 필름.
In claim 6,
The inorganic pigment is a decoration film comprising a metal oxide, a carbon black pigment, a metal sulfide, a metal chloride, or a combination thereof.
제1항에서,
상기 기재층은 PET(polyethylene terephthalate), TPU(Thermoplastic Poly Urethane), PBT(polybutylene terephthalate), PP(polypropylene), PE(polyethylene), PVC(poly vinyl chloride), PMMA(poly methyl methacrylate), ABS(acrylonitrile-butadiene-styrene), PC(polycarbonate), SAN(styrene-acrylonitrile copolymer) 또는 이들의 조합인 데코레이션 필름.
In claim 1,
The substrate layer is PET (polyethylene terephthalate), TPU (Thermoplastic Poly Urethane), PBT (polybutylene terephthalate), PP (polypropylene), PE (polyethylene), PVC (poly vinyl chloride), PMMA (poly methyl methacrylate), ABS (acrylonitrile) -Deadiene-styrene (PC), polycarbonate (PC), styrene-acrylonitrile copolymer (SAN), or a combination film of these.
기재층을 형성하는 단계;
상기 기재층의 배면에 유색의 자외선 경화형 수지에 미세 패턴이 형성된 마스터 몰드를 압착한 후 자외선을 투사함으로써 경화시켜 입체적인 미세 패턴을 구비하는 유색의 패턴층을 형성하는 단계;
상기 패턴층의 배면에 유색 또는 무색의 자외선 경화형 수지를 코팅한 후 자외선을 투사함으로써 경화시킨 코팅층을 형성하는 단계; 및
상기 코팅층의 배면에 금속을 웨트(wet) 코팅 방식으로 분사하여 반사층을 형성하는 단계
로 이루어지는 데코레이션 필름의 제조방법.Forming a base layer;
Forming a colored pattern layer having a three-dimensional fine pattern by pressing a master mold on which a fine pattern is formed on a colored ultraviolet curable resin on the back surface of the base layer and then projecting ultraviolet rays;
Coating a colored or colorless UV curable resin on the back surface of the pattern layer and then forming a cured coating layer by projecting UV light; And
Forming a reflective layer by spraying a metal on the back surface of the coating layer by a wet coating method
Method of manufacturing a decoration film consisting of.
KR1020180138317A 2018-11-12 2018-11-12 Decoration film expressing metalic appearance and manufacturing method of the same Ceased KR20200055837A (en)