MA35820B1 - Aciers martensitiques à limite élastique de 1 700 à 2 200 mpa - Google Patents

Aciers martensitiques à limite élastique de 1 700 à 2 200 mpa

Info

Publication number
MA35820B1
MA35820B1 MA37078A MA37078A MA35820B1 MA 35820 B1 MA35820 B1 MA 35820B1 MA 37078 A MA37078 A MA 37078A MA 37078 A MA37078 A MA 37078A MA 35820 B1 MA35820 B1 MA 35820B1
Authority
MA
Morocco
Prior art keywords
mpa
yield strength
martensitic steels
steels
martensitic
Prior art date
Application number
MA37078A
Other languages
English (en)
Inventor
Narayan S Pottore
Rongjie Song
Original Assignee
Arcelormittal Lnvestigacion Y Desarrollo S L
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Arcelormittal Lnvestigacion Y Desarrollo S L filed Critical Arcelormittal Lnvestigacion Y Desarrollo S L
Publication of MA35820B1 publication Critical patent/MA35820B1/fr

Abstract

L'invention concerne des compositions d'acier martensitique et des procédés de production de celles-ci. Plus particulièrement, les aciers martensitiques présentent une limite élastique allant de 1 700 à 2 200 mpa. Plus particulièrement, l'invention concerne des aciers à ultra-haute rigidité de faible calibre (épaisseur de 1 mm) présentant une résistance à la traction de 1 700 à 2 200 mpa et leurs procédés de production.
MA37078A 2011-11-28 2014-05-27 Aciers martensitiques à limite élastique de 1 700 à 2 200 mpa MA35820B1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US201161629762P 2011-11-28 2011-11-28
PCT/US2012/066895 WO2013082188A1 (fr) 2011-11-28 2012-11-28 Aciers martensitiques à limite élastique de 1 700 à 2 200 mpa

Publications (1)

Publication Number Publication Date
MA35820B1 true MA35820B1 (fr) 2014-12-01

Family

ID=48536024

Family Applications (1)

Application Number Title Priority Date Filing Date
MA37078A MA35820B1 (fr) 2011-11-28 2014-05-27 Aciers martensitiques à limite élastique de 1 700 à 2 200 mpa

Country Status (18)

Country Link
US (4) US20150023835A1 (fr)
EP (1) EP2785888B1 (fr)
JP (1) JP6181065B2 (fr)
KR (3) KR102117176B1 (fr)
CN (1) CN104126022B (fr)
BR (1) BR112014012758B1 (fr)
CA (1) CA2858507C (fr)
ES (1) ES2731472T3 (fr)
HU (1) HUE044254T2 (fr)
IN (1) IN2014CN04908A (fr)
MA (1) MA35820B1 (fr)
MX (1) MX377143B (fr)
PL (1) PL2785888T3 (fr)
RU (1) RU2660482C2 (fr)
TR (1) TR201909721T4 (fr)
UA (1) UA113529C2 (fr)
WO (1) WO2013082188A1 (fr)
ZA (1) ZA201403826B (fr)

Families Citing this family (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP6181065B2 (ja) * 2011-11-28 2017-08-16 アルセロルミタル・インベステイガシオン・イ・デサロジヨ・エセ・エレ １７００から２２００ｍｐａの引張強度を有するマルテンサイト鋼
WO2014143702A2 (fr) * 2013-03-15 2014-09-18 Am/Ns Calvert Llc Aciers pour tube de canalisation et procédé de fabrication
JP6327737B2 (ja) 2013-07-09 2018-05-23 国立研究開発法人物質・材料研究機構 マルテンサイト鋼及びその製造方法
PL3080322T3 (pl) * 2013-12-11 2020-03-31 Arcelormittal Stal martenzytrowa z odpornością na opóźnione pękanie i sposób wytwarzania
GB2548049B (en) 2014-12-19 2021-12-29 Nucor Corp Hot rolled light-gauge martensitic steel sheet and method for making the same
KR101999019B1 (ko) * 2017-12-24 2019-07-10 주식회사 포스코 초고강도 냉연강판 및 그 제조방법
WO2020109851A1 (fr) 2018-11-30 2020-06-04 Arcelormittal Procédé de fabrication d'acier martensitique et acier martensitique ainsi obtenu
ES2939457T3 (es) * 2018-11-30 2023-04-24 Arcelormittal Lámina de acero recocida laminada en frío con alta relación de expansión de orificios y procedimiento de fabricación de la misma
WO2020250009A1 (fr) * 2019-06-12 2020-12-17 Arcelormittal Acier martensitique laminé à froid et procédé d'acier martensitique s'y rapportant
TWI811081B (zh) * 2022-08-26 2023-08-01 中國鋼鐵股份有限公司 一種錳硼鋼材及其製造方法
CN117418212A (zh) * 2023-10-18 2024-01-19 钢铁研究总院有限公司 一种低碳当量超高强度钢板及其制备方法

Family Cites Families (25)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN1039034C (zh) 1993-01-14 1998-07-08 日本钢管株式会社 抗延迟断裂性优良的超高强度冷轧薄钢板及其制造方法
JP3494799B2 (ja) * 1996-03-29 2004-02-09 新日本製鐵株式会社 遅れ破壊特性の優れた高強度ボルトおよびその製造方法
US6284063B1 (en) * 1996-07-12 2001-09-04 Thyssen Stahl Ag Hot-rolled steel strip and method of making it
RU2238332C1 (ru) * 2003-11-03 2004-10-20 Закрытое акционерное общество "Инструмент" Способ изготовления полосы из стали, сталь конструкционная и изделия из нее
JP4476863B2 (ja) * 2005-04-11 2010-06-09 株式会社神戸製鋼所 耐食性に優れた冷間成形ばね用鋼線
DE112006003169B4 (de) 2005-12-01 2013-03-21 Posco Stahlbleche zum Warmpressformen mit ausgezeichneten Wärmebehandlungs- und Schlageigenschaften, daraus hergestellte Warmpressteile und Verfahren zu deren Herstellung
CN101316942A (zh) * 2005-12-01 2008-12-03 Posco公司 用于热压成形的具有优良的热处理和冲击性质的钢板，由该钢板制造的热压部件及其制造方法
JP5365216B2 (ja) * 2008-01-31 2013-12-11 Ｊｆｅスチール株式会社 高強度鋼板とその製造方法
US20090242086A1 (en) * 2008-03-31 2009-10-01 Honda Motor Co., Ltd. Microstructural optimization of automotive structures
JP2009263876A (ja) 2008-04-22 2009-11-12 Hitachi Constr Mach Co Ltd 建設機械の昇降装置および建設機械
DE102008022400B4 (de) * 2008-05-06 2013-08-01 Thyssenkrupp Steel Europe Ag Verfahren zum Herstellen eines Stahlformteils mit einem überwiegend martensitischen Gefüge
KR101027285B1 (ko) * 2008-05-29 2011-04-06 주식회사 포스코 열처리성이 우수한 초고강도 열간성형 가공용 강판, 열처리경화형 부재 및 이들의 제조방법
CN101363099A (zh) * 2008-09-11 2009-02-11 北京科技大学 一种抗拉强度1000MPa级冷轧双相钢板及制备方法
JP5637342B2 (ja) 2008-09-18 2014-12-10 国立大学法人 岡山大学 ホットプレス加工を施した鋼板部材及びその製造方法
CN101775545B (zh) * 2009-01-14 2011-10-12 宝山钢铁股份有限公司 一种低合金高强度高韧性耐磨钢板及其制造方法
US8460800B2 (en) * 2009-03-31 2013-06-11 Kobe Steel, Ltd. High-strength cold-rolled steel sheet excellent in bending workability
JP5402191B2 (ja) 2009-04-15 2014-01-29 Ｊｆｅスチール株式会社 伸びフランジ性に優れた超高強度冷延鋼板およびその製造方法
JP4766186B2 (ja) 2009-08-21 2011-09-07 Ｊｆｅスチール株式会社 ホットプレス部材、ホットプレス部材用鋼板、ホットプレス部材の製造方法
CN101713046B (zh) * 2009-12-14 2013-09-18 钢铁研究总院 纳米析出相强化及控制的超细晶粒马氏体钢的制备方法
JP4947176B2 (ja) * 2010-03-24 2012-06-06 Ｊｆｅスチール株式会社 超高強度冷延鋼板の製造方法
JP5466576B2 (ja) * 2010-05-24 2014-04-09 株式会社神戸製鋼所 曲げ加工性に優れた高強度冷延鋼板
CN102230129A (zh) * 2011-07-12 2011-11-02 内蒙古包钢钢联股份有限公司 一种含稀土高强度钢板及其热处理工艺
JP5704721B2 (ja) * 2011-08-10 2015-04-22 株式会社神戸製鋼所 シーム溶接性に優れた高強度鋼板
JP6181065B2 (ja) * 2011-11-28 2017-08-16 アルセロルミタル・インベステイガシオン・イ・デサロジヨ・エセ・エレ １７００から２２００ｍｐａの引張強度を有するマルテンサイト鋼
GB201708662D0 (en) 2017-05-31 2017-07-12 Tropic Biosciences Uk Ltd Compositions and methods for increasing shelf-life of banana

Also Published As

Publication number Publication date
RU2014126350A (ru) 2016-02-10
KR20140117366A (ko) 2014-10-07
ZA201403826B (en) 2015-07-29
EP2785888B1 (fr) 2019-04-17
US20150023835A1 (en) 2015-01-22
CA2858507A1 (fr) 2013-06-06
WO2013082188A1 (fr) 2013-06-06
MX377143B (es) 2025-03-07
EP2785888A4 (fr) 2015-09-02
HUE044254T2 (hu) 2019-10-28
US20220220596A1 (en) 2022-07-14
ES2731472T3 (es) 2019-11-15
BR112014012758A2 (pt) 2017-07-04
CN104126022B (zh) 2016-11-09
CN104126022A (zh) 2014-10-29
KR102117176B1 (ko) 2020-06-01
US11319620B2 (en) 2022-05-03
PL2785888T3 (pl) 2019-09-30
BR112014012758B1 (pt) 2019-02-05
BR112014012758A8 (pt) 2018-12-18
CA2858507C (fr) 2020-07-07
MX2014006416A (es) 2015-04-08
IN2014CN04908A (fr) 2015-09-18
JP2015504486A (ja) 2015-02-12
KR20170026490A (ko) 2017-03-08
UA113529C2 (xx) 2017-02-10
JP6181065B2 (ja) 2017-08-16
KR20180080360A (ko) 2018-07-11
TR201909721T4 (tr) 2019-07-22
US20200140980A1 (en) 2020-05-07
RU2660482C2 (ru) 2018-07-06
EP2785888A1 (fr) 2014-10-08
US20150267281A1 (en) 2015-09-24

Similar Documents

Publication Publication Date Title
MA35820B1 (fr) Aciers martensitiques à limite élastique de 1 700 à 2 200 mpa
GB201210376D0 (en) High Strength steel sheet excellent in workability and cold brittleness resistance, and manufacturing method thereof
MA45115B1 (fr) Procédé de fabrication d'une tôle d'acier twip à microstructure austénitique
MX2020006442A (es) Lamina de acero de alta resistencia que tiene excelente procesabilidad y metodo para manufacturarla.
MX380415B (es) Lamina de acero de alta resistencia y metodo para la produccion de la misma.
MX387894B (es) Lamina de acero de alta resistencia y metodo de produccion para la misma, y metodo de produccion para lamina de acero galvanizada de alta resistencia.
WO2013099235A8 (fr) Fine tôle d'acier à haute résistance et son procédé de fabrication
EP3279363A4 (fr) TÔLE D'ACIER LAMINÉE À FROID À HAUTE RÉSISTANCE PRÉSENTANT D'EXCELLENTES CARACTÉRISTIQUES D'APTITUDE AU FAÇONNAGE ET DE COLLISION ET PRÉSENTANT UNE RÉSISTANCE À LA TRACTION SUPÉRIEURE OU ÉGALE À 980 MPa, ET SON PROCÉDÉ DE PRODUCTION
EP3279362A4 (fr) TÔLE D'ACIER LAMINÉE À FROID HAUTE RÉSISTANCE, AYANT UNE EXCELLENTE APTITUDE AU FAÇONNAGE, DE TRÈS BONNES CARACTÉRISTIQUES DE COLLISION ET UNE RÉSISTANCE À LA TRACTION DE 980 MPa OU PLUS, ET PROCÉDÉ DE PRODUCTION
MY186913A (en) Aluminium-zinc-hot-dipped and colour-coated steel plate having a 500 mpa yield strength grade and a high elongation and a manufacturing method thereof
MX383870B (es) Lamina de acero de alta resistencia, metodo de produccion para la misma y metodo de produccion para lamina de acero galvanizada de alta resistencia.
MY186509A (en) Aluminium-zinc-hot-dipped and colour-coated steel plate having a 600 mpa yield strength grade and a high elongation and manufacturing method thereof
MX2017010273A (es) Lamina de acero de ultra alta resistencia que tiene excelente resistencia de fractura retardada en extremo cortado de la misma.
BR112013028931A2 (pt) processo de fabricação de uma chapa e de uma peça de aço com estrutura totalmente martensítica e chapa com limite de elasticidade superior a 1300 mpa de aço
EP2762594A4 (fr) Tôle d'acier à haute résistance et haute ténacité présentant une limite d'élasticité de 700 mpa et son procédé de fabrication
UA117656C2 (uk) Сплави на основі заліза з високою твердістю, високою міцністю і способи їхнього виробництва
MX2018000576A (es) Un componente de perforacion.
MA40194A (fr) Procédé de fabrication d'une tôle d'acier à haute résistance avec formabilité et ductilité ameliorées et la tôle obtenue
PH12017500557A1 (en) Steel sheet for cans and method for manufacturing steel sheet for cans
MA49613A (fr) Procédé pour la production d'une tôle d'acier à haute résistance ayant une ductilité, une aptitude au formage et une soudabilité élevées et tôle d'acier ainsi obtenue
EP2799582A4 (fr) Acier austénitique résistant à l'usure et présentant une usinabilité et une ductilité améliorées, et procédé de production correspondant
MX2024005459A (es) Lamina de acero de alta resistencia que tiene excelente resistencia al choque y formabilidad, y metodo para fabricar la misma.
MX2016011337A (es) Lamina de acero laminada en frio, metodo para la produccion de la misma, lamina de acero galvanizada por inmersion en caliente de alta resistencia, y lamina de acero galvano-recocida por inmersion en caliente de alta resistencia.
FI20115832A7 (fi) Menetelmä erinomaisilla mekaanisilla ominaisuuksilla varustetun terästuotteen valmistamiseksi, menetelmällä valmistettu terästuote ja muokkauslujitetun teräksen käyttö
MX2018011735A (es) Componente de union con remache mecanico y metodo de fabricacion del mismo.