MX2020006507A - Hoja de acero que tiene excelente tenacidad, ductilidad y resistencia, y metodo de fabricacion de la misma. - Google Patents

Hoja de acero que tiene excelente tenacidad, ductilidad y resistencia, y metodo de fabricacion de la misma.

Info

Publication number
MX2020006507A
MX2020006507A MX2020006507A MX2020006507A MX2020006507A MX 2020006507 A MX2020006507 A MX 2020006507A MX 2020006507 A MX2020006507 A MX 2020006507A MX 2020006507 A MX2020006507 A MX 2020006507A MX 2020006507 A MX2020006507 A MX 2020006507A
Authority
MX
Mexico
Prior art keywords
steel sheet
ductility
resistance
manufacturing
same
Prior art date
Application number
MX2020006507A
Other languages
English (en)
Inventor
Astrid Perlade
Kangying Zhu
Coralie Jung
Frédéric Kegel
Original Assignee
Arcelormittal
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Arcelormittal filed Critical Arcelormittal
Publication of MX2020006507A publication Critical patent/MX2020006507A/es

Abstract

Una hoja de acero laminada en frío y tratada térmicamente, que tiene una composición que comprende 0.1 % = C = 0.4 %, 3.5 % = Mn = 8.0 %, 0.1 % = Si = 1.5 %, Al = 3 %, Mo = 0.5 %, Cr = 1 %, Nb = 0.1 %, Ti = 0.1 %, V = 0.2 %, B = 0.004 %, 0.002 % = N = 0.013 %, S = 0.003 %, P = 0.015 %. La estructura consiste de, en fracción superficial: entre el 8 y 50 % de austenita retenida, máximo el 80 % de ferrita intercrítica, los granos de ferrita, si los hay, tienen un tamaño promedio de máximo 1.5 µm, y máximo 1 % de cementita, las partículas de cementita tienen un tamaño promedio inferior a 50 nm, martensita y/o bainita.
MX2020006507A 2017-12-19 2018-12-18 Hoja de acero que tiene excelente tenacidad, ductilidad y resistencia, y metodo de fabricacion de la misma. MX2020006507A (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
PCT/IB2017/058129 WO2019122964A1 (en) 2017-12-19 2017-12-19 Steel sheet having excellent toughness, ductility and strength, and manufacturing method thereof
PCT/IB2018/060242 WO2019123240A2 (en) 2017-12-19 2018-12-18 Steel sheet having excellent toughness, ductility and strength, and manufacturing method thereof

Publications (1)

Publication Number Publication Date
MX2020006507A true MX2020006507A (es) 2020-09-17

Family

ID=60972277

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2020006507A MX2020006507A (es) 2017-12-19 2018-12-18 Hoja de acero que tiene excelente tenacidad, ductilidad y resistencia, y metodo de fabricacion de la misma.

Country Status (13)

Country Link
US (2) US11591665B2 (es)
EP (1) EP3728655A2 (es)
JP (3) JP7275137B2 (es)
KR (2) KR102470965B1 (es)
CN (4) CN120400705A (es)
BR (1) BR112020011672B1 (es)
CA (2) CA3085539C (es)
MA (1) MA50091A (es)
MX (1) MX2020006507A (es)
RU (1) RU2747730C1 (es)
UA (1) UA125358C2 (es)
WO (2) WO2019122964A1 (es)
ZA (1) ZA202003349B (es)

Families Citing this family (27)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019122964A1 (en) 2017-12-19 2019-06-27 Arcelormittal Steel sheet having excellent toughness, ductility and strength, and manufacturing method thereof
WO2021009543A1 (en) * 2019-07-16 2021-01-21 Arcelormittal Method for producing a steel part and steel part
WO2021089851A1 (en) * 2019-11-08 2021-05-14 Ssab Technology Ab Medium manganese steel product and method of manufacturing the same
WO2021123887A1 (en) * 2019-12-19 2021-06-24 Arcelormittal High toughness hot rolled steel sheet and method of manufacturing the same
WO2021123886A1 (en) * 2019-12-19 2021-06-24 Arcelormittal High toughness hot rolled and annealed steel sheet and method of manufacturing the same
WO2021123888A1 (en) 2019-12-19 2021-06-24 Arcelormittal Cold rolled and heat-treated steel sheet and method of manufacturing the same
WO2021123889A1 (en) * 2019-12-19 2021-06-24 Arcelormittal Hot rolled and heat-treated steel sheet and method of manufacturing the same
KR102823033B1 (ko) * 2020-02-28 2025-06-20 제이에프이 스틸 가부시키가이샤 강판, 부재 및 그들의 제조 방법
WO2022018503A1 (en) * 2020-07-24 2022-01-27 Arcelormittal Cold rolled and annealed steel sheet
WO2022018502A1 (en) * 2020-07-24 2022-01-27 Arcelormittal Cold rolled and annealed steel sheet
WO2022018499A1 (en) * 2020-07-24 2022-01-27 Arcelormittal Cold rolled and annealed steel sheet
WO2022018498A1 (en) * 2020-07-24 2022-01-27 Arcelormittal Cold rolled and annealed steel sheet and method of manufacturing the same
WO2022018497A1 (en) * 2020-07-24 2022-01-27 Arcelormittal Cold rolled and annealed steel sheet and method of manufacturing the same
MX2023003307A (es) * 2020-09-23 2023-04-13 Arcelormittal Hoja de acero laminada en frio y recubierta y un metodo de fabricacion de la misma.
CN112375990B (zh) * 2020-10-30 2021-10-19 东北大学 一种屈服强度大于2000MPa的超高强度钢及其制备方法
CN112779465A (zh) * 2020-11-30 2021-05-11 江苏联峰能源装备有限公司 一种微合金车轴钢的制备方法
CN116917519B (zh) * 2021-03-25 2025-11-07 日本制铁株式会社 钢板
CN115181887B (zh) * 2021-04-02 2023-08-11 宝山钢铁股份有限公司 一种1180MPa级别低碳低合金Q＆P钢及其快速热处理制造方法
JP7215646B1 (ja) * 2021-06-11 2023-01-31 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
CN117337338B (zh) * 2021-07-16 2026-03-27 安赛乐米塔尔公司 制造钢部件的方法
TWI795076B (zh) * 2021-11-15 2023-03-01 中國鋼鐵股份有限公司 鋼材之熱處理方法
WO2023094856A1 (en) * 2021-11-24 2023-06-01 Arcelormittal Zinc coated mn-containing advanced high strength steel and method of manufacturing the same
CN116144887B (zh) * 2022-09-09 2024-01-16 北京理工大学 一种实现无硅、无铝中锰钢的淬火-配分热处理方法
CN116752048A (zh) * 2023-06-12 2023-09-15 北京科技大学 一种强塑积大于90GPa%的超高强韧中锰钢及制备方法
CN117265430B (zh) * 2023-06-29 2024-12-10 鞍钢股份有限公司 一种抗氧化温成形高强钢、制造方法及成形方法
CN116926421B (zh) * 2023-07-11 2026-02-06 鞍钢集团北京研究院有限公司 低Si1600MPa级免涂层温成形中锰钢及制备方法
CN118222943B (zh) * 2024-04-26 2024-10-22 武汉科技大学 一种超高冲击韧性热轧中锰钢及其热处理方法

Family Cites Families (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE19936151A1 (de) 1999-07-31 2001-02-08 Thyssenkrupp Stahl Ag Höherfestes Stahlband oder -blech und Verfahren zu seiner Herstellung
EP3421634A1 (en) * 2007-02-23 2019-01-02 Tata Steel IJmuiden B.V. Cold rolled and continuously annealed high strength steel strip and method for producing said steel
JP5440672B2 (ja) * 2011-09-16 2014-03-12 Ｊｆｅスチール株式会社 加工性に優れた高強度鋼板およびその製造方法
US9976203B2 (en) * 2012-01-19 2018-05-22 Arcelormittal Ultra fine-grained advanced high strength steel sheet having superior formability
WO2015001367A1 (en) * 2013-07-04 2015-01-08 Arcelormittal Investigación Y Desarrollo Sl Cold rolled steel sheet, method of manufacturing and vehicle
WO2015011510A1 (en) * 2013-07-25 2015-01-29 Arcelormittal Investigación Y Desarrollo Sl Spot welded joint using high strength and high forming and its production method
ES2745428T3 (es) * 2014-01-06 2020-03-02 Nippon Steel Corp Acero y método para fabricar el mismo
WO2016001703A1 (en) * 2014-07-03 2016-01-07 Arcelormittal Method for manufacturing a high strength steel sheet and sheet obtained by the method
WO2016001705A1 (en) * 2014-07-03 2016-01-07 Arcelormittal Method for manufacturing a high strength steel sheet having improved formability and ductility and sheet obtained
KR101915917B1 (ko) * 2014-10-30 2018-11-06 제이에프이 스틸 가부시키가이샤 고강도 강판, 고강도 용융 아연 도금 강판, 고강도 용융 알루미늄 도금 강판 및 고강도 전기 아연 도금 강판, 그리고 그것들의 제조 방법
EP3219821B1 (en) 2015-01-15 2019-11-13 JFE Steel Corporation High-strength galvanized steel sheet and method for producing the same
AU2016264749C1 (en) * 2015-05-20 2019-10-03 Ak Steel Properties, Inc. Low alloy third generation advanced high strength steel
CN104988391A (zh) * 2015-07-07 2015-10-21 河北钢铁股份有限公司 一种1200MPa级冷轧Q&P钢及其制造方法
KR101677396B1 (ko) 2015-11-02 2016-11-18 주식회사 포스코 성형성 및 구멍확장성이 우수한 초고강도 강판 및 이의 제조방법
WO2017109538A1 (en) * 2015-12-21 2017-06-29 Arcelormittal Method for producing a steel sheet having improved strength, ductility and formability
WO2017109541A1 (en) * 2015-12-21 2017-06-29 Arcelormittal Method for producing a high strength coated steel sheet having improved ductility and formability, and obtained coated steel sheet
WO2017131053A1 (ja) * 2016-01-29 2017-08-03 Ｊｆｅスチール株式会社 温間加工用高強度鋼板およびその製造方法
WO2019122964A1 (en) 2017-12-19 2019-06-27 Arcelormittal Steel sheet having excellent toughness, ductility and strength, and manufacturing method thereof

Also Published As

Publication number Publication date
BR112020011672B1 (pt) 2023-05-09
US11591665B2 (en) 2023-02-28
JP2023065520A (ja) 2023-05-12
CN120400705A (zh) 2025-08-01
EP3728655A2 (en) 2020-10-28
CA3135015C (en) 2023-06-13
CA3085539C (en) 2022-08-30
US20200362432A1 (en) 2020-11-19
KR102470965B1 (ko) 2022-11-28
US20230151452A1 (en) 2023-05-18
WO2019122964A1 (en) 2019-06-27
WO2019123240A3 (en) 2019-08-01
ZA202003349B (en) 2021-06-30
KR20200083600A (ko) 2020-07-08
CN111511933A (zh) 2020-08-07
MA50091A (fr) 2021-03-31
JP2021508769A (ja) 2021-03-11
CA3135015A1 (en) 2019-06-27
CN114891961A (zh) 2022-08-12
CN120400704A (zh) 2025-08-01
JP2025063203A (ja) 2025-04-15
CA3085539A1 (en) 2019-06-27
JP7275137B2 (ja) 2023-05-17
KR102401886B1 (ko) 2022-05-24
WO2019123240A2 (en) 2019-06-27
KR20220030308A (ko) 2022-03-10
BR112020011672A2 (pt) 2020-11-17
US11965225B2 (en) 2024-04-23
UA125358C2 (uk) 2022-02-23
RU2747730C1 (ru) 2021-05-13

Similar Documents

Publication Publication Date Title
WO2019123240A3 (en) Steel sheet having excellent toughness, ductility and strength, and manufacturing method thereof
MX2020006342A (es) Hoja de acero de alta resistencia y alta formabilidad y metodo de fabricacion.
MX2019003282A (es) Lamina de acero de alta resistencia y alta conformabilidad laminada en frio y tratada termicamente y metodo de fabricacion.
MX2016009745A (es) Lamina de acero laminada en frio de alta resistencia y metodo para la fabricacion de la misma.
MX391301B (es) Acero para conformado en caliente y pieza conformada en caliente fabricada de tal acero.
MX2021004933A (es) Lamina de acero de alta resistencia y metodo para la fabricacion de la misma.
MX2024000436A (es) Lamina de acero para fabricar partes endurecidas por presion, parte endurecida por presion que tiene una combinacion de alta resistencia y ductilidad al choque, y metodos de fabricacion de las mismas.
MX385708B (es) Lámina de acero laminada en caliente de alta resistencia y método para la fabricación de la misma.
MX2018008561A (es) Lamina de acero de alta resistencia que tiene excelente conformabilidad y un metodo de fabricacion de la misma.
MX388381B (es) Acero de elevada resistencia y procedimiento de fabricacion.
MX374819B (es) Hoja de acero laminada en caliente de alta resistencia, que tiene endurecimiento de recocido y dureza a baja temperatura excelentes, con resistencia a la tension maxima de 980 mpa o mas.
MX2018009735A (es) Lamina de acero de alta resistencia y metodo para fabricar la misma.
MX2022007459A (es) Hoja de acero laminada en frio y tratada termicamente y metodo de fabricacion de la misma.
MX2018010467A (es) Hoja de acero de alta resistencia y metodo para fabricar la misma.
MX2017009200A (es) Lamina de acero galvanizada de alta resistencia y metodo para producir la misma.
MX2020005586A (es) Hoja de acero laminada en frio y recocida y metodo de fabricacion de la misma.
MX385499B (es) Metodo para producir una lamina de acero de alta resistencia que tiene resistencia y formabilidad mejoradas, y la lamina de acero de alta resistencia obtenida.
MX2019011709A (es) Lamina de acero laminada en caliente, pieza forjada de acero y metodo de produccion para la misma.
MX2012000872A (es) Hoja de acero de alta resistencia y proceso de fabricacion.
MX2020010211A (es) Lamina de acero de alta resistencia y metodo para fabricar la misma.
MX2021004105A (es) Lamina de acero laminada en caliente y metodo para fabricar la misma.
MX2016014884A (es) Elemento placa de acero laminada en caliente.
MX367060B (es) Lamina de acero laminada en frio y proceso para fabricar la misma.
MX2017012196A (es) Lamina de acero de alta resistencia y metodo para la produccion de la misma.
MX2021007215A (es) Hoja de acero laminada en frio y tratada termicamente y metodo de fabricacion de la misma.