PL150896B1 - The specific for washing and activating of metal surfaces before the process of phosphate coating - Google Patents
The specific for washing and activating of metal surfaces before the process of phosphate coatingInfo
- Publication number
- PL150896B1 PL150896B1 PL26870487A PL26870487A PL150896B1 PL 150896 B1 PL150896 B1 PL 150896B1 PL 26870487 A PL26870487 A PL 26870487A PL 26870487 A PL26870487 A PL 26870487A PL 150896 B1 PL150896 B1 PL 150896B1
- Authority
- PL
- Poland
- Prior art keywords
- weight
- parts
- amount
- mixture
- alkali metal
- Prior art date
Description
OPIS PATENTOWYPATENT DESCRIPTION
Patent dodatkowy do patentu nrZgłoszono: 87 11 10 /P. 268704/Additional patent to patent no. Applied for: 87 11 10 / P. 268704 /
Pierwszeństwo —Zgłoszenie ogłoszono: 88 θθPriority — Application announced: 88 θθ
Opis patentowy opublikowano: 1990 11 30Patent description published: 1990 11 30
CZYTELNIAREADING ROOM
Urzędu Pnientoweęo K BR' ?· .·· «!Pnientoweęo K BR '? ·. ·· «!
Int. Cl.8 C23C 22/78 C11D 1/825 C23G 1/24Int. Cl. 8 C23C 22/78 C11D 1/825 C23G 1/24
Twórcy wynalazku: Elżbieta Błachowicz, Helena Białostocka, Hanna Kolankowa, Ewa Radomska, Jerzy Kucharski, Krzysztof Robakiewicz,Creators of the invention: Elżbieta Błachowicz, Helena Białostocka, Hanna Kolankowa, Ewa Radomska, Jerzy Kucharski, Krzysztof Robakiewicz,
Anna Szczepańska-Rozdział, Irmina KazubskaAnna Szczepańska-Chapter, Irmina Kazubska
Uprawniony z patentu: Instytut Mechaniki Precyzyjnej, Warszawa /Polska/Authorized by the patent: Institute of Precision Mechanics, Warsaw / Poland /
ŚRODEK DO MYCIA I AKTYWOWANIA POWIERZCHNI METALOWYCH PRZED FOSFORANOWANIEMAGENT FOR CLEANING AND ACTIVATING METAL SURFACES BEFORE PHOSPHATICATION
Przedmiotem wynalazku jest środek do mycia i aktywowania powierzchni metalowych przed fosforanowaniem. Środek przeznaczony jest do stosowania metodą natryskowo-zanurzeniową przed procesem forforanowania niskocynkowego, w wyniku którego otrzymuje się cienkowarstwowe, drobnokrystaliczne powłoki o masie jednostkowej około 2 g/m2, zawierające jako główny składnik fosforany cynkowo-źelazowe. Proces mycia, aktywowania i fosforanowania przewidziany jest do stosowania w agregatach przelotowych, jako przygotowanie powierzchni pod malowanie kataforetyczne, zwłaszcza nadwozi samochodowych.The present invention relates to an agent for cleaning and activating metal surfaces prior to phosphating. The agent is intended for use with the spray-dipping method before the low-zinc phosphating process, which produces thin-layer, fine-crystalline coatings with a unit weight of about 2 g / m 2 , containing zinc iron phosphates as the main component. The process of washing, activating and phosphating is intended for use in continuous aggregates as a preparation of surfaces for cataphoretic painting, especially of car bodies.
Znany jest z polskiego opisu patentowego nr 120 499 środek do sporządzania kąpieli do odtłuszczania i aktywowania powierzchni detali stalowych, zwłaszcza przed fosforanowaniem natryskowym, zawierający fosforan trój sodowy w ilości 0-30% wagowych, czteroboran sodowy w ilości 0-50% wagowych, trój polifosforan sodowy w ilości 15-40% wagowych, pirofosforan sodowy w ilości 20-30% wagowych, aktywny ortofosforan tytanu w ilości 0,1-0,7% wagowych oraz mieszaninę środków powierzchniowo-czynnych w ilości 5-15% wagowych,którą stanowi w ilości 50-90% wagowych produkt addycji tlenku etylenu do estru d-sorbitu kwasu tłuszczowego i w ilości 20-50% wagowych kompozycja myjąca.It is known from Polish patent specification No. 120,499 an agent for preparing a bath for degreasing and activating the surface of steel details, especially before spray phosphating, containing trisodium phosphate in the amount of 0-30% by weight, sodium tetraborate in the amount of 0-50% by weight, tripolyphosphate sodium in an amount of 15-40% by weight, sodium pyrophosphate in an amount of 20-30% by weight, active titanium orthophosphate in an amount of 0.1-0.7% by weight and a mixture of surfactants in an amount of 5-15% by weight, which is an amount of 50-90% by weight of the addition product of ethylene oxide to the fatty acid ester of d-sorbitol and an amount of 20-50% by weight of the washing composition.
□ako kompozycję myjącą znany środek zawiera 15-45% wagowych soli sodowej siarczanu dwuetylenowego nonylofenolu, 0-25% wagowych alkilobenzenosulfanianu sodu o łańcuchu alkilowym Cn-13· 20-30% wagowych mydła trójetanoloaminowego nienasyconych kwasów tłuszczowych, 15-30% wagowych soli sodowej siarczanu oksypropylenowanego metanolu, 15 - 30% wagowych oksyetylenowanego nonylefenolu i/lub oksyetylenowanego alkoholu tłuszczowego oraz 0-2,5% wagowych wersenianu dwusodowego.□ As a washing composition, the known agent contains 15-45% by weight of sodium nonylphenol diethylene sulfate, 0-25% by weight of sodium Cn-13 alkylbenzenesulfanate 20-30% by weight of unsaturated fatty acid triethanolamine soap, 15-30% by weight of sodium salt Methanol ethoxylate, 15-30 wt% nonylphenol ethoxylate and / or fatty alcohol ethoxylate and 0-2.5 wt% disodium edetate.
150 896150 896
150 896150 896
Znany środek posiada następujące wady:The known agent has the following disadvantages:
- krótki okres żywotności aktywatora tytanowego w kąpieli sporządzonej na bazie tego środka,- short service life of the titanium activator in a bath prepared on the basis of this agent,
- wysoka pienistość przy stosowaniu ciśnień rzędu 0,6 - 1,0 MPa,- high foaming when using pressures of 0.6 - 1.0 MPa,
- mierne właściwości myjące przy stosowaniu technologii zanurzeniowej·- moderate cleaning properties when using the immersion technology
Znany Jest z polskiego opisu patentowego nr 143 176 środek do mycia powierzchni metalowych oparty na wodorotlenkach lub węglanach metali alkalicznych, metakrzemianach lub trój polifosforanach metali alkalicznych i związkach powierzchniowo-czynnych. Jako związki powierzchniowo-czynne znany środek zawiera mieszaniną czterech związków powierzchniowo czynnych w stosunkach ilościowych w mieszaninie związku pierwszego do drugiego do trzeciego do czwartego wynoszących wagowo 5:3 : 1:1· Pierwszym związkiem powierzchniowo czynnym w mieszaninie są addukty tlenku etylenu do alkilofenolu o temperaturze zmętnienia około + 35°C, drugim związkiem powierzchniowo czynnym w mieszaninie są oksyetylenowe amidy kwasów tłuszczowych o temperaturze zmętnienia około 4* 30°C, trzecim związkiem powierzchniowo czynnym w mieszaninie są addukty tlenku etylenu i propylenu do alkilofenolu o temperaturze zmętnienia około * 22°C i czwartym związkiem powierzchniowo czynnym w mieszaninie są blokowe polimery tlenku etylenu i propylenu o temperaturze zmętnienia około + 29°C· Ponadto znany środek zawiera glukonian metalu alkalicznego lub glukoniany metali alkalicznych w ilości od 5 do 12 części wagowych i czterosodową i/lub czteropotasową i/lub inną sól metalu alkalicznego i/lub sól amonową kwasu etylenodwuaminoczterooctowego w ilości do 3 części wagowych· Wprowadzenie tego znanego środka do mycia, jako składnika myjącego, do kompozycji zawartej w składzie znanego środka do sporządzania kąpieli do odtłuszczania i aktywowania powierzchni stalowych przed fosforanowaniem nie dało dobrych wyników ani w zakresie jakości mycia, ani poprawy żywotności aktywatora tytanowego· Znany środek do mycia największą efektywność działania wykazuje w zakresie temperatur 20-40°C, a zwłaszcza 35°C, podczas gdy środek według wynalazku musi osiągać największą aktywność w zakresie temperatur 55 - 65°C, gdyż w tym zakresie temperatur działa zarówno strefa natrysku jak i zanurzania w przelotowych myjniach komorowych· Ponadto znany środek do mycia daje dobre efekty myjące głównie w środowisku o wysokim pH, powyżej 11, bowiem jednym ze składników kąpieli jest zwykle wodorotlenek sodowy·It is known from the Polish patent description No. 143 176 an agent for cleaning metal surfaces, based on alkali metal hydroxides or carbonates, alkali metal metasilicates or tripolyphosphates and surfactants. As surfactants, the known agent contains a mixture of four surfactants in 5: 3: 1: 1 weight ratios in the mixture of the first to second to third to fourth compounds. The first surfactant in the mixture are adducts of ethylene oxide to alkylphenol at a temperature of turbidity about + 35 ° C, the second surfactant in the mixture are oxyethylene fatty acid amides with a cloud point of about 4 * 30 ° C, the third surfactant in the mixture are adducts of ethylene and propylene oxide to alkylphenol with a cloud point of about * 22 ° C and the fourth surfactant in the mixture are block polymers of ethylene and propylene oxide with a cloud point of about + 29 ° C or another alkali metal salt and / or ammonium salt of ethylenediaminetetraacetic acid in an amount of up to 3 parts by weight. Incorporation of this known detergent as a washing component into the composition of the known detergent for degreasing and activating steel surfaces before phosphating did not give good results, neither in in terms of cleaning quality or improvement of the service life of the titanium activator. , because in this temperature range, both the spray zone and the immersion zone in continuous chamber washes works
Celem wynalazku jest opracowanie składu środka do mycia i aktywowania powierzchni metalowych o wysokiej efektywności mycia i odtłuszczania z jednoczesnym długim okresem aktywnej pracy aktywatora tytanowego, a więc długim okresie pracy kąpieli sporządzonej ne podstawie tego środka·The aim of the invention is to develop the composition of an agent for washing and activating metal surfaces with high cleaning and degreasing efficiency, with a simultaneous long period of active work of the titanium activator, i.e. a long period of operation of the bath prepared on the basis of this agent.
Celem wynalazku jest opracowanie środka do jednoczesnego mycia i aktywowania powierzchni metalowych przed fosforanowaniem, który będzie dobrze pracował przy pH poniżej 10, zwłaszcza 7,0 - 9,0 i w temperaturze 55 - 65°C·The aim of the invention is to provide an agent for simultaneous washing and activating metal surfaces prior to phosphating, which will work well at a pH below 10, especially 7.0 - 9.0 and at a temperature of 55 - 65 ° C.
Zadaniem do rozwiązania okazało się zasadniczo opracowanie mieszaniny związków powierzchniowo czynnych spełniającej założone wymagania oraz takiej, w której dezaktywacja aktywatora tytanowego przebiega najwolniej·The task to be solved was basically the development of a mixture of surfactants meeting the assumed requirements and the one in which the deactivation of the titanium activator is slowest
Środek do mycia i aktywowania powierzchni metalowych przed fosforanowaniem oparty na fosforanach i polifosforanach metali alkalicznych, czteroboranie metalu alkalicznego, mieszaninie niejonowych związków powierzchniowo czynnych i zawierający aktywny ortofosforan tytanu i ewentualnie zawierający sól metalu alkalicznego lub sól amonową kwasu wersenowego, według istoty wynalazku charakteryzuje się tym, że zawiera trój polifosforan metalu alkalicznego w ilości od 5 do 40 części wagowych, fosforany metali alkalicznych w ilości od 5 do 48 części wagowych, czteroboran metalu alkalicznego w ilości od 18 do 75 części wagowych, przy czym łączna ilość polifosforanów, fosforanów i boranów wynosi od 70 do 95 części wagowych, aktywny ortofosforan tytanu w ilości od 0,1 do 0,7 części wagowych i ewentualnie sól metalu alkalicznego lub sól amonową kwasu wersenowego w ilości do 5 części wagowych i zawiera mieszaninę trzech związków powierzchniowo czynnych z tego samego szeregu homologicznego w łącznej ilości od 3 do 30 części wagowych, w której pierwszy związek stanowią addukty 7 moli tlenku etylenu do alkilofenolu o temperaturze zmętnienia około 20°C, drugi związek mieszaniny stanowią addukty 8 moli tlenku etylenu do alkilofenolu o temperaturze zmętnienia około 40°C i trzeci związek stanowią addukty 9 moli tlenku etylenu do alkilofenolu o temperaturze zmętnienia około 60°C, przy czym stosunek ilościowy związku pierwszego do drugiego do trzeciego wAn agent for washing and activating metal surfaces prior to phosphating based on alkali metal phosphates and polyphosphates, alkali metal tetraborate, mixture of non-ionic surfactants and containing active titanium orthophosphate and optionally containing an alkali metal salt or an ammonium salt of edetic acid, according to the essence of the invention is characterized by: that it contains an alkali metal triphosphate in an amount of 5 to 40 parts by weight, an alkali metal phosphate in an amount of 5 to 48 parts by weight, an alkali metal tetraborate in an amount of 18 to 75 parts by weight, the total amount of polyphosphates, phosphates and borates is from 70 to 95 parts by weight, active titanium orthophosphate in an amount of 0.1 to 0.7 parts by weight, and optionally an alkali metal salt or ammonium salt of edetic acid in an amount of up to 5 parts by weight and contains a mixture of three surfactants of the same homologous series combined and from 3 to 30 parts by weight, in which the first compound is adducts of 7 moles of ethylene oxide to an alkylphenol with a cloud point of about 20 ° C, the second compound of the mixture is adducts of 8 moles of ethylene oxide to an alkylphenol with a cloud point of about 40 ° C, and the third compound is adducts of 9 moles of ethylene oxide to an alkylphenol with a cloud point of about 60 ° C, the ratio of the amount of the first to the second to the third compound in
150 896 mieszaninie trzech związków powierzchniowo czynnych wynosi odpowiednio: 0,5 : 4 do 0,5 : 8 do 0,5 : 8, korzystnie 1:3:6· Wskazane jest aby środek według wynalazku zawierał ponadto w ilości od 0,1 do 3 części wagowych mieszaninę produktów przyłączania tlenku etylenu i tlenku propylenu do alkilofenolu o temperaturze zmętnienia około 25°C oraz w ilości od 0,1 do 1 części wagowej mieszaninę produktów przyłączania tlenku etylenu do kwasów tłuszczowych o temperaturze zmętnienia około 85°C·150 896 in a mixture of three surfactants is respectively: 0.5: 4 to 0.5: 8 to 0.5: 8, preferably 1: 3: 6. It is advisable that the agent according to the invention also contains 0.1 to 3 parts by weight a mixture of ethylene oxide and propylene oxide addition products to an alkylphenol with a cloud point of about 25 ° C, and a mixture of 0.1 to 1 part by weight of a mixture of ethylene oxide and fatty acid addition products with a cloud point of about 85 ° C
Okazało się, że środek według wynalazku posiada tak wysoką aktywność, że skutecznie myje, odtłuszcza i aktywuje zarówno w procesie mycia natryskowego w szerokim zakresie ciśnień od 0,2 do 1,0 MPa, nie wywołując przy tym nadmiernego pienienia,zwłaszcza przy ciśnieniu 0,6 - 1,0 MPa,jak i w procesie mycia zanurzeniowego· Jest to bardzo Istotna zaleta środka według wynalazku ze względu na fakt, że przeznaczony jest on głównie do mycia i aktywowania karoserii samochodowych, prowadzonego w przelotowych agregatach, w których karoserie przechodzą kolejno przez poszczególne strefy natrysku i zanurzenia· W strefie natrysku podlegają obróbce chemicznej, przede wszystkim zewnętrzne powierzchnie karoserii, natomiast powierzchnie trudno dostępne, takie jak części wnętrza karoserii, zagłębienia, przestrzenie zamknięte z trzech stron itp· myte sę dopiero w strefie zanurzania·It turned out that the agent according to the invention has such a high activity that it effectively cleans, degreases and activates both in the spray washing process in a wide range of pressures from 0.2 to 1.0 MPa, without causing excessive foaming, especially at pressure 0, 6 - 1.0 MPa, as well as in the immersion washing process.This is a very significant advantage of the agent according to the invention due to the fact that it is intended mainly for washing and activating car bodies, carried out in through-going aggregates in which the car bodies pass successively through individual spraying and immersion zones In the spraying zone, the external surfaces of the car body are chemically treated, while surfaces that are difficult to access, such as parts of the inside of the car body, depressions, spaces closed on three sides, etc., are only cleaned in the immersion zone
W powszechnie stosowanych agregatach natryskowych powierzchnia trudno dostępne w ogóle nie były myte ani fosforanowane, co uniemożliwiało osadzanie się na tych powierzchniach farby elektroforetycznej· Następstwem takiego sposobu prowadzenia procesu było przenoszenie do farby elektroforetycznej zabrudzeń z niedomytych części nadwozia, która w tego typu procesie jest całkowicie zanurzane do farby· Problem właściwego mycia całej karoserii, w tym także miejsc trudno dostępnych nabiera szczególnej wagi w przypadku stosowania farb kataforetycznych, charakteryzujących się dużą wgłębnościę· środek będący przedmiotem wynalazku, przeznaczony do mycia i aktywowania powierzchni przed procesem drobnokrystalicznego fosforanowania niskocynkowego, a następnie malowania kataforetycznego zapewnia spełnienie stawianych w tym zakresie wymagań· Istotną zaletę środka według wynalazku jest ponadto wysoka trwałość zwięzków powierzchniowo czynnych zastosowanych w określonym zestawie soli nieorganicznych.In commonly used spraying units, the surfaces that are difficult to access were not washed or phosphated at all, which prevented the deposition of electrophoretic paint on these surfaces. The result of this method of conducting the process was the transfer of dirt from unwashed body parts to the electrophoretic paint, which in this type of process is completely immersed for paint · The problem of proper washing of the entire body, including hard-to-reach places, becomes particularly important when using cataphoretic paints, characterized by a large depth · the agent being the subject of the invention, intended for washing and activating the surface before the process of fine-crystalline low-zinc phosphating and then cataphoretic painting ensures that the requirements set forth in this respect are met. A significant advantage of the agent according to the invention is also the high stability of surfactants used in a specific set of inorganic salts.
Problem jest ważny, ponieważ wymiana kąpieli w strefie zanurzeniowej przelotowego agregatu do mycia i aktywowania powierzchni karoserii samochodowych ze względu na znaczną * 3 pojemność wanny, wynoszącą około 100 m przewidziana jest nie częściej niż 4 krotnie w roku, z uwagi na znaczne koszty związane ze sporządzaniem tak dużej ilości kąpieli oraz na odprowadzanie takiej ilości kąpieli do ścieków.The problem is important, because the replacement of the bath in the immersion zone of the through unit for washing and activating the surface of car bodies due to the considerable * 3 capacity of the bath, amounting to about 100 m, is planned not more often than 4 times a year, due to the significant costs associated with the preparation such a large number of baths and the discharge of such a number of baths into the waste water.
środek według wynalazku pokazany jest w przykładach wykonania·the agent according to the invention is shown in the following examples
Przykład I· Skład środka w procentach wagowych:Example I: Composition of the agent in percent by weight:
1/ czteroboran sodu 69,5 2/ trój polifosforan sodu 5,0 3/ pirofosforan sodu 5,0 4/ ortofosforan tytanu 0,2 5/ fosforan dwusodowy 10,01 / sodium tetraborate 69.5 2 / sodium tri-polyphosphate 5.0 3 / sodium pyrophosphate 5.0 4 / titanium orthophosphate 0.2 5 / disodium phosphate 10.0
6/ mieszanina związków powierzchniowo czynnych - 10,0 Mieszanina związków powierzchniowo czynnych zawiera:6 / mixture of surfactants - 10.0 The mixture of surfactants contains:
części wagowych·parts by weight
Przykład II· Skład środka w procentach wagowych: 1/ czteroboran sodu - 27Example II · The composition of the agent in percent by weight: 1 / sodium tetraborate - 27
2/ trój polifosforan sodu - 382 / sodium triphosphate - 38
3/ fosforan trój sodowy - 53 / trisodium phosphate - 5
150 896150 896
4/ wersenian czterosodowy - 4,54 / tetrasodium edetate - 4.5
5/ ortofosforan tytanu - 0,55 / titanium orthophosphate - 0.5
6/ mieszanina związków powierzchniowo czynnych - 20,0 Mieszanina związków powierzchniowo czynnych zawiera:6 / mixture of surfactants - 20.0 The mixture of surfactants contains:
- addukty 7 moli tlenku etylenu do oktylofenolu o temperaturze zmętnienia ♦ 20°C - 20 części wagowych,- adducts of 7 moles of ethylene oxide to octylphenol with a cloud point of ♦ 20 ° C - 20 parts by weight,
- addukty 8 moli tlenku etylenu do heptylofenolu o temperaturze zmętnienia ♦ 40°C - 20 części wagowych,- adducts of 8 moles of ethylene oxide to heptylphenol with a cloud point of ♦ 40 ° C - 20 parts by weight,
- addukty 9 moli tlenku etylenu do nonylofenolu o temperaturze zmętnienia ♦ 62°C - 20 części wagowych,- adducts of 9 moles of ethylene oxide to nonylphenol with a cloud point of ♦ 62 ° C - 20 parts by weight,
7/ inne związki powierzchniowo czynne 5,0 Inne związki powierzchniowo czynne zawierają:7 / other surfactants 5.0 Other surfactants include:
- mieszaninę produktów przyłączania 8 moli tlenku etylenu i 7 moli tlenku propylenu do nonylofenolu o temperaturze zmętnienia 4 26°C - 4 części wagowe,- mixture of the products of adding 8 moles of ethylene oxide and 7 moles of propylene oxide to nonylphenol with a cloud point of 4–26 ° C - 4 parts by weight,
- mieszaninę produktów przyłączania 6 moli tlenku etylenu do nasyconych kwasów tłuszczowych o długości łańcucha węglowego 0 temperaturze zmętnienia * 83°C - 5 części wagowych·- product mixture attachment 6 moles of ethylene oxide to saturated fatty acids of carbon chain length of 0 * cloud point of 83 ° C - 5 parts by weight ·
Sporządza się kąpiel do mycia i aktywowania, rozpuszczając środek według przykładu I w proporcji 20-50 g na 1 litr wody· Kąpielą tą prowadzi się mycia i aktywowanie próbek stalowych z blachy zimnowalcowanej niskowęglowej karoseryjnej kategorii la SSB, sposobem natryskowym przy ciśnieniu 0,3 MPa, a następnie w tej samej kąpieli poddaje się myciu i aktywowaniu takie same próbki, sposobem zanurzeniowym w kąpieli mieszanej za pomocą mieszadła laboratoryjnego o prędkości obrotów 1/s· Po 5 min· mycia zarówno sposobem natryskowym jak i zanurzeniowym stwierdzono obecność ciągłego filmu wodnego podczas płukania próbek wodą, co świadczyło o usunięciu zatłuszczeń z powierzchni· Następnie próbki poddano fosforanowaniu w kąpieli do fosforanowania niskocynkowego, uzyskując drobnokrystaliczne, równomierne powłoki spełniające wymagania PN-81/H-97016· Mycie i aktywowanie kąpielą przygotowaną na bazie środka według przykładu I prowadzono z intensywnością 0,54 m /1 kąpieli przy niezmiennym poziomie aktywności aktywatora tytanowego· Dla porównania prowadzono mycie i aktywowanie w kąpieli znanej z polskiego opisu patentowego nr 120 499· Aktywator tytanowy obniżył swoją aktywność do 60% aktywności w świeżo sporządzonej kąpieli po przepracowaniu 0,25 m2 w 1 1 kąpieli· Dla porównania zastąpiono mieszaniną czterech związków powierzchniowo czynnych, znaną z polskiego opisu patentowego nr 143 176 związki powierzchniowo czynne stosowane w składzie środka znanego z polskiego opisu patentowego nr 120 499. Trwałość kąpieli z aktywatorem tytanowym wzrosła do 0,31 m2 w 1 1 kąpieli·A washing and activation bath is prepared, dissolving the agent according to example 1 in a proportion of 20-50 g per 1 liter of water. and then in the same bath, the same samples are washed and activated by immersion in a mixed bath using a laboratory stirrer with a speed of 1 / s.After 5 minutes of washing, both by spraying and immersing, a continuous water film was found during rinsing samples with water, which indicated that the grease was removed from the surface. 0.54 m / 1 bath with constant activity level titanium activator properties · For comparison, washing and activation were carried out in the bath known from Polish patent specification No. 120 499 · The titanium activator decreased its activity to 60% of the activity in a freshly prepared bath after working with 0.25 m 2 in 1 bath · For comparison, it was replaced with a mixture four surfactants, known from Polish patent description No. 143 176 surfactants used in the composition of the agent known from Polish patent description No. 120 499. Durability of the bath with titanium activator increased to 0.31 m 2 in 1 bath
Claims (2)