PL157798B2 - Method of dehumidifying masonry saturated with moisture

Info

Publication number: PL157798B2
Application number: PL27123288A
Authority: PL
Inventors: Tadeusz Domin
Original assignee: Politechnika Krakowska
Priority date: 1988-03-15
Filing date: 1988-03-15
Publication date: 1992-07-31
Also published as: PL271232A2

Abstract

The invention concerns a method of damp wall drying by creating hydrophobic membrane, consisting in execution of a series of holes in wall and driving under pressure into those holes hydrophobic agents including methyl silicone resin, ethyl alcohol and organic solvent, characterised in that at the first stage into holes in wall is forced insulating agent in form of sodium water-glass mixed with water in proportion 1:1 to 1:0.5 with addition of sodium fluosilicate in amount 5-15 % per mass in proportion to amount of water-glass, next is introduced hydrophobic agent being a composition of in percent per mass: methyl silicone resin 10-15, ethyl alcohol 50-60% and organic solvent 30-35%.

Description

Przedmiotem wynalazku jest sposób osuszania murów zawilgoconych wodą podciąganą kapilarnie .The subject of the invention is a method of drying walls moistened with capillary water.

Zawilgocone z powodu braku izolacji poziomej mury ulegają przyspieszonemu niszczeniu a ponadto pomieszczenia, w których mury wykazują zawilgocenie przekraczające 3-4% nie mogą byó użytkowane zgodnie z ich przeznaczeniem.The damp walls due to the lack of horizontal insulation are subject to accelerated deterioration and, moreover, the rooms in which the walls show moisture exceeding 3-4% cannot be used in accordance with their intended use.

W technice budowlanej są znane metody osuszania murów, w których stosuje się wprowadzenie do murów różnych środków chemicznych, także hydrofobowych. Wprowadzone do wilgotnego materiału murów środki hydrofobowe z trudnością mogą penetrować. Powoduje to, iż skuteczność metody jest zadawalająca.There are known methods of drying masonry in building technology, in which various chemicals, including hydrophobic, are applied to the walls. The hydrophobic agents introduced into the wet wall material can penetrate with difficulty. As a result, the effectiveness of the method is satisfactory.

Ponadto znane są metody wykorzystujące zjawisko elektroosmozy do osuszania murów takie jak na przykład metodą elektroiniekcji lub metodą aerodrenażu i elektrodrenażu w połączeniu z wytworzeniem przepony hydrofobowej. Ideą wyżej wymienionych metod jest wstępne podsuszenie murów do stanu zawilgocenia umożliwiającego wystarczająco dobrą penetrację preparatu hydrofobowego w materiale.In addition, there are known methods that use the phenomenon of electroosmosis to drain walls, such as, for example, by electroinjection or by the method of aerodrainage and electrode-drainage in combination with the production of a hydrophobic membrane. The idea of the above-mentioned methods is to pre-dry the walls to a damp state that allows a sufficiently good penetration of the hydrophobic preparation in the material.

Wytworzona przepona hydrofobowa powinna uniemożliwiać kapilarne wznoszenie nią wody w murze.The created hydrophobic diaphragm should prevent capillary rise of water in the wall.

W polskim opisie patentowym nr 126 351 przedstawiony jest sposób zabezpieczenia przed wilgocią murów, polegający na jednoczesnym wstępnym osuszaniu muru metodą elektrodrenażu z wykorzystaniem elektrod rurowych i swobodnego aerodrenażu przez te same elektrody rurowe. Następnie w trakcie dalszego osuszania elektroosmotycznego przez te same elektrody rurowe wprowadza się do muru w obszar objęty działaniem pola elektrycznego środek hydrofobowy w postaci roztworu w benzynie lakowej, ksylenie i chlorku metylu - żywicy metylosilikonowej. Znane jest również z polskiego zgłoszenia patentowego nr P-269498 rozwiązanie, w którym mieszanka do hydrofobizacji materiałów zawiera Silak M-ll i/lub Silak M-114 bądź M-50, ewentualnie w mieszaninie z rozpuszczalnikiem węglowodorowym typu nitro oraz etanol, ewentualnie skażony przykładowo 3% dodatkiem benzyny lakowej w stosunku 1:8 do 1:9. Niedogodnością znanych metod osuszania i izolowania murów jest ich duża pracochłonność lub też niewystarczająca skuteczność działania.The Polish patent description No. 126 351 describes a method of protecting walls against moisture, consisting in the simultaneous preliminary drying of the wall by means of electrode drainage with the use of tubular electrodes and free aerodrainage by the same tubular electrodes. Then, during further electroosmotic drying through the same tubular electrodes, a hydrophobic agent in the form of a solution in white spirit, xylene and methyl chloride - methyl silicone resin is introduced into the wall in the area covered by the electric field. There is also known from the Polish patent application No. P-269498 a solution in which the mixture for the hydrophobization of materials contains Silak M-II and / or Silak M-114 or M-50, possibly in a mixture with a nitro-type hydrocarbon solvent and ethanol, possibly contaminated, for example 3% mineral spirits in a ratio of 1: 8 to 1: 9. The disadvantage of the known methods of drying and insulating walls is their high labor consumption or insufficient effectiveness.

Celem wynalazku jest sposób osuszania i zabezpieczania murów przed kapilarnym wznoszeniem wody, tańszy od obecnie stosowanych a jednocześnie skuteczniejszy.The object of the invention is a method of drying and protecting walls against capillary rise of water, cheaper than those currently used and at the same time more effective.

Sposób według wynalazku polega na tym, że w pierwszym etapie w otwory w murze wtłacza się pod ciśnieniem środek uszczelniający w postaci szkła wodnego sodowego zmieszanego z wodą w stosunku 1:1 do 1:0,5, a następnie środek hydrofobowy stanowiący kompozycję o składzie w procentach masowych: żywica metylosilikonowa 10-15%, alkohol etylowy 50-60% oraz rozpuszczalnik organiczny 30-35%. Środek uszczelniający zawiera dodatek fluorokrzemianu sodowego w ilości 5-15% masowych w stosunku do ilości szkła wodnego sodowego, który przyspiesza twardnienie szkła wodnego.The method according to the invention consists in that, in the first step, a sealing agent in the form of sodium water glass mixed with water mixed with water in a ratio of 1: 1 to 1: 0.5 is forced into the wall openings under pressure, and then a hydrophobic agent consisting of a composition of percentages by mass: methyl silicone resin 10-15%, ethyl alcohol 50-60% and organic solvent 30-35%. The sealant contains an addition of sodium fluorosilicate in the amount of 5-15% by mass in relation to the amount of sodium water glass, which accelerates the hardening of the water glass.

157 798157 798

Wprowadzony środek hydrofobowy po wtłoczeniu go do muru w wyniku zhydrofobizowania warstwy materiału muru wytwarza przeponę przecinającą drogę dla kapilarnego wznoszenia się wody, w wyniku czego mur ponad przeponą odsycha. Wprowadzenie ciśnieniowe preparatu hydrofobowego stwarza warunki maksymalnego zhydrofobizowania materiału muru. Wtłoczenie do wilgotnego muru kolejno środka uszczelniającego a następnie środka hydrofobowego daje synergiczny efekt wytwarzania skutecznej przepony przeciw wznoszeniu wody. Zetknięcie ze sobą w kapilarach muru dwu preparatów powoduje, iż w wyniku odciągania przez alkohol wody od szkła wodnego, następuje żelowanie a następnie krystalizacja krzemianu sodowego tworzącego korki w kapilarach. Obecność preparatu hydrofobowego dodatkowo przyczynia się do zhydrofobizowania ścianek kapilar. Ujawnia się efekt synergiczny wzmacniający działanie poszczególnych środków co gwarantuje skuteczność i trwałość tak wytworzonej przepony.The introduced hydrophobic agent, after it is forced into the wall, as a result of the hydrophobization of the layer of the wall material, creates a diaphragm that cuts the way for the capillary rise of water, as a result of which the wall dries above the diaphragm. The pressure introduction of a hydrophobic preparation creates conditions for the maximum hydrophobization of the wall material. The injection of a sealing agent into the damp masonry successively followed by a hydrophobic agent has a synergistic effect to produce an effective anti-rising diaphragm. If two preparations come into contact with each other in the wall capillaries, as a result of the alcohol drawing water from the water glass, gelation takes place and then crystallization of sodium silicate forming plugs in the capillaries. The presence of the hydrophobic preparation additionally contributes to the hydrophobization of the capillary walls. A synergistic effect is revealed, enhancing the action of individual agents, which guarantees the effectiveness and durability of the diaphragm produced in this way.

Z uwagi na fakt, że iniekcję wykonuje się zazwyczaj w przypadku murów o wilgotności przekraczającej 12-15%, zastosowane ciśnienie, niezależnie od lepkości preparatu posiada decydujący wpływ na promień rozchodzenia się preparatu w murach. Rozchodzenie się preparatu w materiale zachodzi nie tylko dzięki występującym tu kapilarom, ale także poprzez wszelkie spękania materiału i inne nieciągłości a także pomiędzy zaprawą a cegłami.Due to the fact that the injection is usually performed in the case of walls with a moisture content exceeding 12-15%, the applied pressure, regardless of the viscosity of the preparation, has a decisive influence on the radius of the preparation in the walls. The spreading of the preparation in the material takes place not only due to the capillaries present here, but also through any cracks in the material and other discontinuities, as well as between the mortar and bricks.

Sposób osuszenia i zabezpieczenia przed zawilgoceniem murów jest sposobem wymagającym mniejszych nakładów w robociżnie i kosztach, gdyż nie wymaga stosowania dodatkowych zabiegów związanych ze wstępnym osuszaniem murów, na przykład przez elektroosmozę, dającym jednak większą gwarancję skuteczności zabiegu osuszania.The method of drying and protecting the walls against dampness is a method that requires less labor and costs, as it does not require the use of additional procedures related to the initial drying of the walls, for example by electroosmosis, which, however, guarantees the effectiveness of the drying procedure.

Przakład. Do zawilgoconego muru (15% wilgotności masowej) przez nawiercone otwory wtłoczono pod ciśnieniem 1,0 MPa szkło wodne zmieszane z wodą w stosunku 1:1 z dodatkiem 5% fluorokrzemianu sodowego. Następnie do tych otworów wtłoczono przy stałym mieszaniu pod ciśnieniem 1,0 MPa środek hydrofobowy o następującym składzie podanym w procentach masowych: żywica metylosilikonowa 10% benzyna lakowa 30% alkohol etylowy 10%For example. Water glass mixed with water in the ratio 1: 1 with the addition of 5% sodium fluorosilicate was forced through the drilled holes into the damp wall (15% by mass) through the drilled holes. Then, a hydrophobic agent with the following composition given as a percentage by mass was forced into these holes under constant stirring under a pressure of 1.0 MPa: methyl silicone resin 10% white spirit 30% ethyl alcohol 10%

W ten sposób uzyskano przeponę hydrofobową, która spowodowała obniżenie się zawilgocenia muru nad przeponą.In this way, a hydrophobic diaphragm was obtained, which reduced the moisture content in the wall above the diaphragm.

157 798157 798

Zakład Wydawnictw UP RP. Nakład 90 egz Cena 5000 zł.Department of Publishing of the UP RP. Circulation of 90 copies Price PLN 5,000.

Claims

Patent claim

A method of drying damp walls by creating a hydrophobic membrane, consisting in making a series of holes in the wall and introducing hydrophobic agents containing methyl silicon resin, ethyl alcohol and an organic solvent under pressure into these holes, characterized in that in the first stage, the holes in the wall are forced under pressure Sealing agent in the form of sodium water glass mixed with water in a ratio of 1: 1 to 1: 0.5 with the addition of sodium fluorosilicate in the amount of 5-15% by weight in relation to the amount of water glass, and then a hydrophobic agent is introduced, which is a composition with a percentage composition by mass: methyl silicone resin 10-15%, ethyl alcohol 50-60% and organic solvent 30-35%.

* * *