PL2762583T3 - Blacha stalowa o dużej wytrzymałości cynkowana zanurzeniowo na gorąco mająca doskonałą odporność na opóźnione pękanie i sposób jej wytwarzania - Google Patents

Blacha stalowa o dużej wytrzymałości cynkowana zanurzeniowo na gorąco mająca doskonałą odporność na opóźnione pękanie i sposób jej wytwarzania

Info

Publication number
PL2762583T3
PL2762583T3 PL12835699T PL12835699T PL2762583T3 PL 2762583 T3 PL2762583 T3 PL 2762583T3 PL 12835699 T PL12835699 T PL 12835699T PL 12835699 T PL12835699 T PL 12835699T PL 2762583 T3 PL2762583 T3 PL 2762583T3
Authority
PL
Poland
Prior art keywords
manufacturing
steel sheet
galvanized steel
dip galvanized
fracture resistance
Prior art date
Application number
PL12835699T
Other languages
English (en)
Inventor
Hiroyuki Kawata
Naoki Maruyama
Akinobu Murasato
Akinobu MINAMI
Takeshi Yasui
Takuya Kuwayama
Hiroyuki Ban
Kaoru HIRAMATSU
Original Assignee
Nippon Steel & Sumitomo Metal Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel & Sumitomo Metal Corp filed Critical Nippon Steel & Sumitomo Metal Corp
Publication of PL2762583T3 publication Critical patent/PL2762583T3/pl

Links

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21B—ROLLING OF METAL
    • B21B1/00—Metal-rolling methods or mills for making semi-finished products of solid or profiled cross-section; Sequence of operations in milling trains; Layout of rolling-mill plant, e.g. grouping of stands; Succession of passes or of sectional pass alternations
    • B21B1/22—Metal-rolling methods or mills for making semi-finished products of solid or profiled cross-section; Sequence of operations in milling trains; Layout of rolling-mill plant, e.g. grouping of stands; Succession of passes or of sectional pass alternations for rolling plates, strips, bands or sheets of indefinite length
    • B21B1/24—Metal-rolling methods or mills for making semi-finished products of solid or profiled cross-section; Sequence of operations in milling trains; Layout of rolling-mill plant, e.g. grouping of stands; Succession of passes or of sectional pass alternations for rolling plates, strips, bands or sheets of indefinite length in a continuous or semi-continuous process
    • B21B1/26—Metal-rolling methods or mills for making semi-finished products of solid or profiled cross-section; Sequence of operations in milling trains; Layout of rolling-mill plant, e.g. grouping of stands; Succession of passes or of sectional pass alternations for rolling plates, strips, bands or sheets of indefinite length in a continuous or semi-continuous process by hot-rolling, e.g. Steckel hot mill
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21B—ROLLING OF METAL
    • B21B3/00—Rolling materials of special alloys so far as the composition of the alloy requires or permits special rolling methods or sequences ; Rolling of aluminium, copper, zinc or other non-ferrous metals
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/013—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/12—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties
    • C21D8/1244—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties characterised by the heat treatment
    • C21D8/1255—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties characterised by the heat treatment with diffusion of elements, e.g. decarburising, nitriding
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/12—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties
    • C21D8/1277—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties involving a particular surface treatment
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C18/00—Alloys based on zinc
    • C22C18/04—Alloys based on zinc with aluminium as the next major constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/58—Ferrous alloys, e.g. steel alloys containing chromium with nickel with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0222—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating in a reactive atmosphere, e.g. oxidising or reducing atmosphere
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0224—Two or more thermal pretreatments
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C23C2/29—Cooling or quenching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C23C2/36—Elongated material
    • C23C2/40—Plates; Strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/005—Ferrite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/12—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties
    • C21D8/1216—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties characterised by the working steps
    • C21D8/1222—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/12—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties
    • C21D8/1216—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties characterised by the working steps
    • C21D8/1233—Cold rolling
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12535—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.] with additional, spatially distinct nonmetal component
    • Y10T428/12611—Oxide-containing component
    • Y10T428/12618—Plural oxides
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12785—Group IIB metal-base component
    • Y10T428/12792—Zn-base component
    • Y10T428/12799—Next to Fe-base component [e.g., galvanized]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12861—Group VIII or IB metal-base component
    • Y10T428/12951—Fe-base component
    • Y10T428/12972—Containing 0.01-1.7% carbon [i.e., steel]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/26—Web or sheet containing structurally defined element or component, the element or component having a specified physical dimension
    • Y10T428/263—Coating layer not in excess of 5 mils thick or equivalent
    • Y10T428/264—Up to 3 mils
    • Y10T428/265—1 mil or less

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Electromagnetism (AREA)
  • Manufacturing & Machinery (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Coating With Molten Metal (AREA)
PL12835699T 2011-09-30 2012-09-28 Blacha stalowa o dużej wytrzymałości cynkowana zanurzeniowo na gorąco mająca doskonałą odporność na opóźnione pękanie i sposób jej wytwarzania PL2762583T3 (pl)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2011218776 2011-09-30
PCT/JP2012/075108 WO2013047760A1 (ja) 2011-09-30 2012-09-28 耐遅れ破壊特性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
EP12835699.5A EP2762583B1 (en) 2011-09-30 2012-09-28 High-strength hot-dip galvanized steel sheet having excellent delayed fracture resistance and manufacturing method thereof

Publications (1)

Publication Number Publication Date
PL2762583T3 true PL2762583T3 (pl) 2019-04-30

Family

ID=47995785

Family Applications (1)

Application Number Title Priority Date Filing Date
PL12835699T PL2762583T3 (pl) 2011-09-30 2012-09-28 Blacha stalowa o dużej wytrzymałości cynkowana zanurzeniowo na gorąco mająca doskonałą odporność na opóźnione pękanie i sposób jej wytwarzania

Country Status (14)

Country Link
US (1) US8993120B2 (pl)
EP (1) EP2762583B1 (pl)
JP (1) JP5352793B2 (pl)
KR (1) KR101605980B1 (pl)
CN (1) CN103842543B (pl)
BR (1) BR112014007483B1 (pl)
CA (1) CA2850462C (pl)
ES (1) ES2706996T3 (pl)
MX (1) MX360510B (pl)
PL (1) PL2762583T3 (pl)
RU (1) RU2585889C2 (pl)
TW (1) TWI499675B (pl)
WO (1) WO2013047760A1 (pl)
ZA (1) ZA201402351B (pl)

Families Citing this family (63)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
PL2762585T3 (pl) * 2011-09-30 2020-01-31 Nippon Steel Corporation Blacha stalowa cienka o dużej wytrzymałości cynkowana zanurzeniowo na gorąco o doskonałych właściwościach skrawania mechanicznego, stopowa blacha stalowa cienka o dużej wytrzymałości cynkowana zanurzeniowo na gorąco oraz sposób wytwarzania wspomnianych blach cienkich
JP5304924B2 (ja) * 2011-12-27 2013-10-02 Ｊｆｅスチール株式会社 脆性亀裂伝播停止特性に優れた構造用高強度厚鋼板およびその製造方法
CN105102653B (zh) * 2013-03-29 2018-05-08 杰富意钢铁株式会社 氢用钢结构物、储氢容器及氢用管道的制造方法
EP3040440B1 (en) * 2013-08-26 2019-03-06 JFE Steel Corporation High-strength hot-dip galvanized steel sheet and method for manufacturing same
JP5799997B2 (ja) * 2013-09-12 2015-10-28 Ｊｆｅスチール株式会社 外観性とめっき密着性に優れる溶融亜鉛めっき鋼板および合金化溶融亜鉛めっき鋼板ならびにそれらの製造方法
JP5817805B2 (ja) * 2013-10-22 2015-11-18 Ｊｆｅスチール株式会社 伸びの面内異方性が小さい高強度鋼板およびその製造方法
JP5817804B2 (ja) * 2013-10-22 2015-11-18 Ｊｆｅスチール株式会社 伸びの面内異方性が小さい高強度鋼板およびその製造方法
KR101585744B1 (ko) 2013-12-26 2016-01-14 주식회사 포스코 표면품질 및 내지연파괴 특성이 우수한 아연도금강판 및 그 제조방법
JP5888471B1 (ja) * 2014-03-31 2016-03-22 Ｊｆｅスチール株式会社 高降伏比高強度冷延鋼板及びその製造方法
CN106661690B (zh) * 2014-07-14 2018-09-07 新日铁住金株式会社 热轧钢板
JP6179674B2 (ja) 2014-10-30 2017-08-16 Ｊｆｅスチール株式会社 高強度鋼板、高強度溶融亜鉛めっき鋼板、高強度溶融アルミニウムめっき鋼板および高強度電気亜鉛めっき鋼板、ならびに、それらの製造方法
US10113223B2 (en) 2014-11-05 2018-10-30 Nippon Steel & Sumitomo Metal Corporation Hot-dip galvanized steel sheet
WO2016072475A1 (ja) * 2014-11-05 2016-05-12 新日鐵住金株式会社 溶融亜鉛めっき鋼板
TWI564404B (zh) * 2014-11-05 2017-01-01 新日鐵住金股份有限公司 熔融鍍鋅鋼板
CN104532126B (zh) * 2014-12-19 2017-06-06 宝山钢铁股份有限公司 一种低屈强比超高强度热轧q&p钢及其制造方法
KR101569508B1 (ko) 2014-12-24 2015-11-17 주식회사 포스코 굽힘 특성이 우수한 hpf 성형부재 및 그 제조방법
ES2769086T3 (es) 2015-04-22 2020-06-24 Nippon Steel Corp Lámina de acero chapada
EP3323906B1 (en) * 2015-07-13 2020-09-30 Nippon Steel Corporation Steel sheet, hot-dip galvanized steel sheet, alloyed hot-dip galvanized steel sheet, and production methods therefor
MX2018000329A (es) * 2015-07-13 2018-03-14 Nippon Steel & Sumitomo Metal Corp Lamina de acero, lamina de acero galvanizado por inmersion en caliente, lamina de acero recocido y galvanizado y metodos de fabricacion.
JP6536294B2 (ja) * 2015-08-31 2019-07-03 日本製鉄株式会社 溶融亜鉛めっき鋼板、合金化溶融亜鉛めっき鋼板、およびそれらの製造方法
KR101696121B1 (ko) 2015-12-23 2017-01-13 주식회사 포스코 내수소지연파괴특성, 내박리성 및 용접성이 우수한 열간성형용 알루미늄-철 합금 도금강판 및 이를 이용한 열간성형 부재
BR112018012606A2 (pt) * 2016-02-25 2018-12-04 Nippon Steel & Sumitomo Metal Corporation chapa de aço galvanizada por imersão a quente de alta resistência com excelente resistência ao destacamento por impacto e resistência à corrosão em seção trabalhada
US11560606B2 (en) 2016-05-10 2023-01-24 United States Steel Corporation Methods of producing continuously cast hot rolled high strength steel sheet products
MX2018013869A (es) 2016-05-10 2019-03-21 United States Steel Corp Productos de acero de alta resistencia y procesos de recocido para fabricar los mismos.
US11993823B2 (en) 2016-05-10 2024-05-28 United States Steel Corporation High strength annealed steel products and annealing processes for making the same
US11377708B2 (en) 2016-12-27 2022-07-05 Jfe Steel Corporation High-strength galvanized steel sheet and method for producing the same
MX2019009599A (es) 2017-02-13 2019-10-14 Jfe Steel Corp Lamina de acero de alta resistencia y metodo para producir la misma.
MX2019010816A (es) 2017-03-13 2019-10-30 Jfe Steel Corp Lamina de acero laminado en frio de alta resistencia y metodo para fabricar la misma.
JP6384703B1 (ja) * 2017-03-13 2018-09-05 Ｊｆｅスチール株式会社 高強度冷延鋼板とその製造方法
CN108977726B (zh) * 2017-05-31 2020-07-28 宝山钢铁股份有限公司 一种抗延迟开裂的马氏体超高强度冷轧钢带及其制造方法
KR102010048B1 (ko) 2017-06-01 2019-10-21 주식회사 포스코 도장 밀착성과 도장 후 내식성이 우수한 열간 프레스 성형 부재용 강판 및 그 제조방법
RU2650951C1 (ru) * 2017-11-27 2018-04-18 Юлия Алексеевна Щепочкина Сталь
EP3725904B1 (en) 2017-12-15 2024-03-06 Nippon Steel Corporation Steel sheet, hot-dip zinc-coated steel sheet, and alloyed hot-dip zinc-coated steel sheet
WO2019122965A1 (en) * 2017-12-19 2019-06-27 Arcelormittal Cold rolled and coated steel sheet and a method of manufacturing thereof
WO2019122957A1 (en) 2017-12-19 2019-06-27 Arcelormittal A coated steel substrate
MX2020006763A (es) * 2017-12-27 2020-08-24 Jfe Steel Corp Lamina de acero de alta resistencia y metodo para la produccion de la misma.
CN111902554B (zh) * 2018-03-30 2022-03-29 日本制铁株式会社 钢板及其制造方法
WO2019189842A1 (ja) 2018-03-30 2019-10-03 Ｊｆｅスチール株式会社 高強度亜鉛めっき鋼板、高強度部材およびそれらの製造方法
TWI651418B (zh) * 2018-03-30 2019-02-21 日商新日鐵住金股份有限公司 合金化熔融鍍鋅鋼板
EP3828299A1 (en) 2018-10-18 2021-06-02 JFE Steel Corporation High-ductility, high-strength electro-galvanized steel sheet and manufacturing method thereof
KR102153197B1 (ko) * 2018-12-18 2020-09-08 주식회사 포스코 가공성이 우수한 냉연강판, 용융아연도금강판 및 이들의 제조방법
MX2021007759A (es) 2018-12-26 2021-08-05 Jfe Steel Corp Lamina de acero galvanizada por inmersion en caliente de alta resistencia y metodo para producir la misma.
EP3936628A4 (en) 2019-03-06 2022-10-26 Nippon Steel Corporation HOT ROLLED STEEL SHEET
MX2021010854A (es) * 2019-03-11 2021-10-22 Jfe Steel Corp Lamina de acero de alta resistencia y metodo para producir la misma.
CN110057650B (zh) * 2019-05-20 2022-03-15 常德力元新材料有限责任公司 钢带晶粒的评价方法
DE102019130381A1 (de) * 2019-11-11 2021-05-12 Benteler Automobiltechnik Gmbh Kraftfahrzeugbauteil mit gesteigerter Festigkeit
KR102305748B1 (ko) * 2019-12-18 2021-09-27 주식회사 포스코 내부식성이 우수한 용융 합금도금 강재 및 그 제조방법
CN115244203B (zh) 2020-03-11 2023-11-21 日本制铁株式会社 热轧钢板
WO2021205943A1 (ja) * 2020-04-07 2021-10-14 日本製鉄株式会社 鋼板
WO2022097734A1 (ja) * 2020-11-06 2022-05-12 Ｊｆｅスチール株式会社 Ｆｅ系電気めっき鋼板，電着塗装鋼板，自動車部品，電着塗装鋼板の製造方法，及びＦｅ系電気めっき鋼板の製造方法
KR20220084651A (ko) * 2020-12-14 2022-06-21 주식회사 포스코 굽힘성 및 성형성이 우수한 고강도 강판 및 이의 제조방법
US20240240278A1 (en) * 2021-04-27 2024-07-18 Nippon Steel Corporation Steel sheet and plated steel sheet
CN115537681B (zh) * 2021-06-30 2023-10-17 宝山钢铁股份有限公司 高韧性、低屈强比及低纵横向强度各向异性500MPa级钢板及其制造方法
CN116657033A (zh) * 2022-02-17 2023-08-29 宝山钢铁股份有限公司 抗点焊lme裂纹的高强钢复合镀锌板及其制备方法
CN115029630B (zh) * 2022-05-23 2023-06-02 武汉钢铁有限公司 一种提高1800MPa级抗延迟开裂热成形钢及生产方法
CN117286396A (zh) * 2022-06-17 2023-12-26 宝山钢铁股份有限公司 一种耐氢致开裂冷轧热镀锌超高强双相钢及其制造方法
JP7736042B2 (ja) * 2022-07-22 2025-09-09 Ｊｆｅスチール株式会社 鋼板およびその製造方法
CN118326251A (zh) * 2023-01-10 2024-07-12 通用汽车环球科技运作有限责任公司 具有高平整度的热浸镀锌超高强度钢板
EP4663801A1 (en) 2023-03-31 2025-12-17 JFE Steel Corporation Steel sheet, member, and production methods for these
EP4663800A1 (en) 2023-03-31 2025-12-17 JFE Steel Corporation Steel sheet, member, and method for manufacturing same
WO2025075095A1 (ja) 2023-10-04 2025-04-10 Ｊｆｅスチール株式会社 鋼板、部材およびそれらの製造方法
CN121941787A (zh) 2023-10-04 2026-04-28 杰富意钢铁株式会社 钢板、构件和它们的制造方法
CN119243050B (zh) * 2024-09-30 2025-12-19 宁波星科金属材料有限公司 一种耐盐雾钢材、制备方法及其应用

Family Cites Families (24)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3247907B2 (ja) 1992-11-05 2002-01-21 川崎製鉄株式会社 延性と耐遅れ破壊特性に優れた高強度冷延鋼板およびその製造方法
JP3477955B2 (ja) * 1995-11-17 2003-12-10 Ｊｆｅスチール株式会社 極微細組織を有する高張力熱延鋼板の製造方法
EP1498507B1 (en) * 2000-05-26 2006-06-28 JFE Steel Corporation Cold-rolled steel sheet and galvanized steel sheet having excellent strain age hardenability and method of producing the same
FR2844281B1 (fr) * 2002-09-06 2005-04-29 Usinor Acier a tres haute resistance mecanique et procede de fabrication d'une feuille de cet acier revetue de zinc ou d'alliage de zinc
JP4317384B2 (ja) 2003-04-28 2009-08-19 新日本製鐵株式会社 耐水素脆化、溶接性および穴拡げ性に優れた高強度亜鉛めっき鋼板とその製造方法
JP4384523B2 (ja) 2004-03-09 2009-12-16 新日本製鐵株式会社 形状凍結性に極めて優れた低降伏比型高強度冷延鋼板およびその製造方法
JP4555694B2 (ja) * 2005-01-18 2010-10-06 新日本製鐵株式会社 加工性に優れる焼付け硬化型熱延鋼板およびその製造方法
JP4741376B2 (ja) 2005-01-31 2011-08-03 新日本製鐵株式会社 外観が良好な高強度合金化溶融亜鉛めっき鋼板及びその製造方法と製造設備
CN101336308B (zh) 2006-01-30 2012-08-29 新日本制铁株式会社 成形性及镀覆性优良的高强度热浸镀锌钢板和高强度合金化热浸镀锌钢板及其制造方法和制造装置
JP4781836B2 (ja) * 2006-02-08 2011-09-28 新日本製鐵株式会社 耐水素脆性に優れた超高強度鋼板とその製造方法及び超高強度溶融亜鉛めっき鋼板の製造方法並びに超高強度合金化溶融亜鉛めっき鋼板の製造方法
JP5194878B2 (ja) * 2007-04-13 2013-05-08 Ｊｆｅスチール株式会社 加工性および溶接性に優れる高強度溶融亜鉛めっき鋼板およびその製造方法
CA2718304C (en) * 2008-03-27 2012-03-06 Nippon Steel Corporation High-strength cold-rolled steel sheet, high-strength galvanized steel sheet, and high-strength alloyed hot-dip galvanized steel sheet having excellent formability and weldability,and methods for manufacturing the same
JP4712882B2 (ja) 2008-07-11 2011-06-29 株式会社神戸製鋼所 耐水素脆化特性および加工性に優れた高強度冷延鋼板
JP5131844B2 (ja) * 2008-08-12 2013-01-30 新日鐵住金株式会社 熱間プレス用熱延鋼板およびその製造方法ならびに熱間プレス鋼板部材の製造方法
JP5195413B2 (ja) 2008-12-26 2013-05-08 新日鐵住金株式会社 曲げ加工性及び靭性の異方性に優れた高強度熱延鋼板及びその製造方法
JP2010168651A (ja) 2008-12-26 2010-08-05 Nakayama Steel Works Ltd 高強度熱延鋼板およびその製造方法
JP5740847B2 (ja) * 2009-06-26 2015-07-01 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板およびその製造方法
JP5696359B2 (ja) * 2009-07-08 2015-04-08 新日鐵住金株式会社 高強度鋼板およびその溶鋼の溶製方法
JP5370104B2 (ja) * 2009-11-30 2013-12-18 新日鐵住金株式会社 耐水素脆化特性に優れた引張最大強度９００ＭＰａ以上の高強度鋼板および高強度冷延鋼板の製造方法、高強度亜鉛めっき鋼板の製造方法
JP5499663B2 (ja) * 2009-11-30 2014-05-21 新日鐵住金株式会社 機械切断特性に優れた引張最大強度９００ＭＰａ以上の高強度冷延鋼板及びその製造方法、並びに、高強度亜鉛めっき鋼板及びその製造方法
JP5644095B2 (ja) 2009-11-30 2014-12-24 新日鐵住金株式会社 延性及び耐遅れ破壊特性の良好な引張最大強度９００ＭＰａ以上を有する高強度鋼板および高強度冷延鋼板の製造方法、高強度亜鉛めっき鋼板の製造方法
JP5434537B2 (ja) * 2009-12-03 2014-03-05 新日鐵住金株式会社 溶接性に優れた高Ｓｉ含有合金化溶融めっき鋼板およびその製造方法
JP5786317B2 (ja) * 2010-01-22 2015-09-30 Ｊｆｅスチール株式会社 材質安定性と加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP2011153349A (ja) * 2010-01-27 2011-08-11 Sumitomo Metal Ind Ltd 外観特性に優れた合金化溶融亜鉛めっき鋼板およびその製造方法

Also Published As

Publication number Publication date
CN103842543A (zh) 2014-06-04
CN103842543B (zh) 2016-01-27
TWI499675B (zh) 2015-09-11
MX360510B (es) 2018-11-05
RU2585889C2 (ru) 2016-06-10
US20140234659A1 (en) 2014-08-21
ES2706996T3 (es) 2019-04-02
KR20140052070A (ko) 2014-05-02
BR112014007483B1 (pt) 2019-12-31
BR112014007483A2 (pt) 2017-04-04
MX2014003793A (es) 2014-07-10
EP2762583B1 (en) 2018-11-07
JPWO2013047760A1 (ja) 2015-03-30
EP2762583A4 (en) 2015-12-02
EP2762583A1 (en) 2014-08-06
TW201331383A (zh) 2013-08-01
JP5352793B2 (ja) 2013-11-27
RU2014117668A (ru) 2015-11-10
US8993120B2 (en) 2015-03-31
WO2013047760A1 (ja) 2013-04-04
ZA201402351B (en) 2015-03-25
CA2850462A1 (en) 2013-04-04
KR101605980B1 (ko) 2016-03-23
CA2850462C (en) 2016-10-11

Similar Documents

Publication Publication Date Title
ZA201402351B (en) High-strength hot-dip galvanized steel sheet having excellent delayed fracture resistance and manufacturing method thereof
ZA201402259B (en) Hot-dip galvanized steel sheet and manufacturing method thereof
EP2762589B8 (en) High-strength hot-dip galvanized steel sheet excellent in impact resistance property and manufacturing method thereof, and high-strength alloyed hot-dip galvanized steel sheet and manufacturing method thereof
ZA201401401B (en) High-strength steel sheet excellent in impact resistance and manufacturing method thereof,and high-strength galvanized steel sheet and manufacturing method thereof
ZA201402355B (en) High-strength hot-dip galvanized steel sheet and high-strength alloyed hot-dip galvanized steel sheet excellent in mechanical cutting property,and manufacturing method thereof
ZA201402256B (en) High-strength hot-dip galvanized steel sheet
ZA201402216B (en) Galvanized steel sheet and method of manufacturing the same
PL2738280T3 (pl) Blacha stalowa cienka ocynkowana o dużej wytrzymałości mająca doskonałą zginalność oraz sposób jej wytwarzania
ZA201401402B (en) High-strength steel sheet and high-strength galvanized steel sheet excellent in shape fixability,and manufacturing method thereof
PL2738276T3 (pl) Blacha stalowa cienka ocynkowana o dużej wytrzymałości i blacha stalowa cienka o dużej wytrzymałości mająca doskonałą formowalność oraz sposób ich wytwarzania
EP2811047A4 (en) FIREPLATED STEEL PLATE AND METHOD OF MANUFACTURING THEREOF
PL2653582T3 (pl) Blacha stalowa cienka cynkowana zanurzeniowo na gorąco i sposób jej wytwarzania
PL2762579T3 (pl) Blacha stalowa cienka cynkowana na gorąco o dużej wytrzymałości i sposób jej wytwarzania
EP2634281A4 (en) HIGH-RESISTANCE FIRE-GRAINED STEEL PLATE WITH EXCELLENT EVEN STRENGTH AND EXCELLENT PLATING CHARACTERISTICS, AND METHOD OF MANUFACTURING THEREOF
PL3034644T3 (pl) Blacha stalowa o dużej wytrzymałości i ocynkowana blacha stalowa o dużej wytrzymałości z doskonałą ciągliwością i podatnością na wywijanie kołnierza oraz sposób ich wytwarzania
EP2644736A4 (en) Al-Zn HOT DIP-PLATED STEEL SHEET AND METHOD FOR MANUFACTURING THE SAME
AU2012276644A1 (en) High-corrosion-resistance hot-dip galvanized steel sheet having excellent appearance uniformity and manufacturing method thereof
ZA201306547B (en) High-strength cold-rolled steel sheet with excellent local formability,and manufacturing method therefor
ZA201503075B (en) Alloyed hot-dip galvanized steel sheet and method of manufacturing the same
ZA201401348B (en) High-strength cold-rolled steel sheet having excellent stretch flangeability and precision punchability,and manufacturing method thereof
PL2692894T3 (pl) Zawierająca bainit blacha stalowa cienka walcowana na gorąco o wysokiej wytrzymałości oraz doskonałej obrabialności izotropowej i sposób jej wytwarzania
PL2944705T3 (pl) Stopowa blacha stalowa cynkowana zanurzeniowo na gorąco i sposób jej wytwarzania
EP3257962A4 (en) High-strength hot-dip galvanized steel sheet and manufacturing method therefor
EP2749667A4 (en) HIGH MANGANIC STEEL STEEL OF EXCELLENT WELDABILITY AND METHOD FOR PRODUCING A FIREPLATED GALVANIZED STEEL PLATE THEREOF
EP2412842A4 (en) HOT-GALVANIZED STEEL PLATE AND MANUFACTURING METHOD THEREFOR