TH10100A3 - Sheet material containing rice husk ash and manufacturing process - Google Patents

Abstract

DC60 (February 9, 2015) A sheet material containing rice husk ash powder and a manufacturing process. The mixture consists of rice husk ash powder mixed with Portland cement, fine sand, and water. This mixture is then molded into the desired shape using a mold and cured for a specified period. The resulting product has a naturally dark color without the need for added or coated synthetic dyes. It can be used in products requiring high strength, such as roof tiles, floor tiles, or wall bricks. (Revised Invention Summary February 16, 2015 (February 9, 2015)) A sheet material containing rice husk ash powder and a manufacturing process. The mixture consists of rice husk ash powder mixed with Portland cement, fine sand, and water. This mixture is then molded into the desired shape using a mold and cured for a specified period. The resulting product has a naturally dark color without the need for added or coated synthetic dyes. It can be used in products requiring high strength, such as roof tiles, floor tiles, or wall bricks. ------------------------------------------------------------- A sheet material containing rice husk ash powder and a manufacturing process. The mixture consists of rice husk ash powder mixed with Portland cement, fine sand, and water. This mixture is then molded into the desired shape and cured. The resulting product has a naturally dark color without the need for added synthetic dyes or coatings. It can be used to create high-strength products such as roof tiles, floor tiles, or wall bricks.

Claims (2)

1. Claims (all) which will not appear on the advertising page: Revised 16/02/2015 (9/02/2015) 1. The rice husk ash composite material contains the following components: a. Fine sand, 80 percent by weight of the dry mixture. b. Portland cement, 14-19 percent by weight of the dry mixture. c. Finely ground rice husk ash, 1-6 percent by weight of the dry mixture. d. Water, 16-25 percent by weight of the total dry mixture. 2. The manufacturing process of the rice husk ash composite material as per claim 1 involves the following steps: a. The rice husk ash is sieved using a No. 35 sieve to remove impurities. It is then dry-ground for 1.5-3 hours, and the resulting rice husk ash powder can pass through a standard No. 325 sieve. b. The sand is sieved through a standard No. 35 sieve. c. Fine sand and Portland cement are mixed in. 1. Mix the finely ground rice husk ash powder thoroughly for 10-30 minutes. 2. Add water to the mixture and mix well for 1-5 minutes. 3. Mold the mixture using a mold. 4. Allow the mixture to harden for 12-24 hours at room temperature. 5. Cure under 90-100% relative humidity for 7-14 days. ---------------------------------------------------------- 1. A sheet of material containing rice husk ash has the following components: a. Fine sand, 80 percent by weight of the dry mixture. b. Portland cement, 14-19 percent by weight of the dry mixture. c. Finely ground rice husk ash powder, 1-6 percent by weight of the dry mixture. d. Water, 16-25 percent by weight of the total dry mixture. 2. The manufacturing process of rice husk ash composite sheets, as per claim 1, involves the following steps: a. Sift the rice husk ash using a No. 35 sieve to remove impurities. It is then dry-ground for 1.5-3 hours, and the resulting powder should pass through a standard No. 325 sieve. b. Sift the sand through a standard No. 35 sieve. c. Mix the fine sand, Portland cement, and finely ground rice husk ash for 10-30 minutes. d. Add water to the mixture and mix thoroughly for 1-5 minutes. e. Mold the mixture using a mold. f. Cure the mixture under a relative humidity of 90-100% for 7-14 days.