TWI488978B - Molten galvanized steel sheet and method of manufacturing the same - Google Patents

Molten galvanized steel sheet and method of manufacturing the same Download PDF

Info

Publication number
TWI488978B
TWI488978B TW102127806A TW102127806A TWI488978B TW I488978 B TWI488978 B TW I488978B TW 102127806 A TW102127806 A TW 102127806A TW 102127806 A TW102127806 A TW 102127806A TW I488978 B TWI488978 B TW I488978B
Authority
TW
Taiwan
Prior art keywords
steel sheet
hot
less
base steel
mass
Prior art date
Application number
TW102127806A
Other languages
English (en)
Chinese (zh)
Other versions
TW201413005A (zh
Inventor
Soshi Fujita
Shintaro Yamanaka
Original Assignee
Nippon Steel & Sumitomo Metal Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel & Sumitomo Metal Corp filed Critical Nippon Steel & Sumitomo Metal Corp
Publication of TW201413005A publication Critical patent/TW201413005A/zh
Application granted granted Critical
Publication of TWI488978B publication Critical patent/TWI488978B/zh

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/013—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/001—Heat treatment of ferrous alloys containing Ni
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/002—Heat treatment of ferrous alloys containing Cr
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/005—Heat treatment of ferrous alloys containing Mn
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/008—Heat treatment of ferrous alloys containing Si
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/021—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips involving particular fabrication steps or treatments of ingots or slabs
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0226—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0236—Cold rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0263—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment following hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0278—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips involving a particular surface treatment 
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/005—Ferrous alloys, e.g. steel alloys containing rare earths, i.e. Sc, Y, Lanthanides
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/08—Ferrous alloys, e.g. steel alloys containing nickel
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/16—Ferrous alloys, e.g. steel alloys containing copper
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/22—Ferrous alloys, e.g. steel alloys containing chromium with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/26—Ferrous alloys, e.g. steel alloys containing chromium with niobium or tantalum
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/28—Ferrous alloys, e.g. steel alloys containing chromium with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/32—Ferrous alloys, e.g. steel alloys containing chromium with boron
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/38—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/58—Ferrous alloys, e.g. steel alloys containing chromium with nickel with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0222—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating in a reactive atmosphere, e.g. oxidising or reducing atmosphere
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0224—Two or more thermal pretreatments
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/024—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by cleaning or etching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/261—After-treatment in a gas atmosphere, e.g. inert or reducing atmosphere
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C23C2/36—Elongated material
    • C23C2/40—Plates; Strips
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12785—Group IIB metal-base component
    • Y10T428/12792—Zn-base component
    • Y10T428/12799—Next to Fe-base component [e.g., galvanized]

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Thermal Sciences (AREA)
  • Physics & Mathematics (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Coating With Molten Metal (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Electroplating Methods And Accessories (AREA)
TW102127806A 2012-08-03 2013-08-02 Molten galvanized steel sheet and method of manufacturing the same TWI488978B (zh)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
JP2012172739 2012-08-03

Publications (2)

Publication Number Publication Date
TW201413005A TW201413005A (zh) 2014-04-01
TWI488978B true TWI488978B (zh) 2015-06-21

Family

ID=50028115

Family Applications (1)

Application Number Title Priority Date Filing Date
TW102127806A TWI488978B (zh) 2012-08-03 2013-08-02 Molten galvanized steel sheet and method of manufacturing the same

Country Status (9)

Country Link
US (1) US10131981B2 (2)
JP (1) JP5648755B2 (2)
KR (1) KR101653510B1 (2)
CN (1) CN104508169B (2)
BR (1) BR112015001809B1 (2)
IN (1) IN2015DN01525A (2)
MX (1) MX370268B (2)
TW (1) TWI488978B (2)
WO (1) WO2014021452A1 (2)

Families Citing this family (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9713823B2 (en) * 2012-04-06 2017-07-25 Jfe Steel Corporation Continuous galvanizing line having an annealing furnace
WO2015181581A1 (fr) * 2014-05-28 2015-12-03 ArcelorMittal Investigación y Desarrollo, S.L. Tôle d'acier munie d'un revêtement à protection cathodique sacrificielle comprenant du lanthane
CN104342603A (zh) * 2014-10-21 2015-02-11 大丰市南亚阀门有限公司 一种提高阀门耐腐蚀性能的合金材料及其处理工艺
KR101561008B1 (ko) 2014-12-19 2015-10-16 주식회사 포스코 구멍확장능이 우수한 용융아연도금강판, 합금화 용융아연도금강판 및 그 제조방법
MX2017009017A (es) * 2015-01-09 2018-04-13 Kobe Steel Ltd Lamina de acero chapada de alta resistencia y metodo para su produccion.
WO2016111273A1 (ja) * 2015-01-09 2016-07-14 株式会社神戸製鋼所 高強度めっき鋼板、並びにその製造方法
JP6085348B2 (ja) * 2015-01-09 2017-02-22 株式会社神戸製鋼所 高強度めっき鋼板、並びにその製造方法
WO2016111272A1 (ja) * 2015-01-09 2016-07-14 株式会社神戸製鋼所 高強度めっき鋼板、並びにその製造方法
KR101746996B1 (ko) * 2015-12-24 2017-06-28 주식회사 포스코 도금 밀착성이 우수한 고망간 용융 알루미늄계 도금강판
CN105734425A (zh) * 2016-05-09 2016-07-06 周常 一种海洋钻井平台结构材料
CN105970080A (zh) * 2016-05-18 2016-09-28 安徽合矿机械股份有限公司 一种加工性能方便的汽车零部件制备方法
CN105970089A (zh) * 2016-05-18 2016-09-28 安徽合矿机械股份有限公司 一种易加工减磨型汽车零部件用合金钢材料
JP6455544B2 (ja) * 2017-05-11 2019-01-23 Ｊｆｅスチール株式会社 溶融亜鉛めっき鋼板の製造方法
CN107815614A (zh) * 2017-10-29 2018-03-20 江苏鼎荣电气集团有限公司 一种抗拉型电缆桥架及其生产工艺
CN110273111B (zh) * 2019-07-30 2020-11-24 马鞍山钢铁股份有限公司 一种宽热成形加热工艺窗口的锌基镀层热成形钢及其制备方法

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN101649415A (zh) * 2008-08-12 2010-02-17 株式会社神户制钢所 加工性优异的高强度钢板
CN101646797B (zh) * 2007-03-30 2012-05-09 杰富意钢铁株式会社 高强度热镀锌钢板

Family Cites Families (21)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS55122865A (en) 1979-03-12 1980-09-20 Nippon Steel Corp Molten zinc plating method for difficult plating steel sheet
JP2932701B2 (ja) * 1991-01-09 1999-08-09 住友金属工業株式会社 合金化溶融亜鉛めっき鋼板
JPH11343551A (ja) * 1998-05-28 1999-12-14 Nkk Corp 耐食性に優れた溶融Ａｌ−Ｚｎ系合金めっき鋼板
KR100595947B1 (ko) * 1998-09-29 2006-07-03 제이에프이 스틸 가부시키가이샤 고강도 박강판, 고강도 합금화 용융아연도금 강판 및이들의 제조방법
JP3606102B2 (ja) 1999-04-20 2005-01-05 Ｊｆｅスチール株式会社 熱延鋼板、溶融めっき熱延鋼板およびそれらの製造方法
JP2001279412A (ja) 2000-03-29 2001-10-10 Nippon Steel Corp 耐食性の良好なＳｉ含有高強度合金化溶融亜鉛めっき鋼板とその製造方法
JP2001323355A (ja) 2000-05-11 2001-11-22 Nippon Steel Corp めっき密着性と塗装後耐食性の良好なＳｉ含有高強度溶融亜鉛めっき鋼板と塗装鋼板およびその製造方法
US6797410B2 (en) * 2000-09-11 2004-09-28 Jfe Steel Corporation High tensile strength hot dip plated steel and method for production thereof
JP4192051B2 (ja) 2003-08-19 2008-12-03 新日本製鐵株式会社 高強度合金化溶融亜鉛めっき鋼板の製造方法と製造設備
CN101048527A (zh) * 2004-10-07 2007-10-03 杰富意钢铁株式会社 热镀锌钢板及其制造方法
JP4741376B2 (ja) 2005-01-31 2011-08-03 新日本製鐵株式会社 外観が良好な高強度合金化溶融亜鉛めっき鋼板及びその製造方法と製造設備
BRPI0610540B1 (pt) * 2005-04-20 2017-01-17 Nippon Steel & Sumitomo Metal Corp método de produção de chapa de aço recozida após galvanização de imersão a quente
JP4837459B2 (ja) 2006-06-30 2011-12-14 新日本製鐵株式会社 外観が良好な耐食性に優れた高強度溶融亜鉛めっき鋼板及びその製造方法
JP5338087B2 (ja) 2008-03-03 2013-11-13 Ｊｆｅスチール株式会社 めっき性に優れる溶融亜鉛めっき鋼板の製造方法および連続溶融亜鉛めっき設備
JP2010126757A (ja) * 2008-11-27 2010-06-10 Jfe Steel Corp 高強度溶融亜鉛めっき鋼板およびその製造方法
JP5564784B2 (ja) 2008-12-05 2014-08-06 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板及び高強度合金化溶融亜鉛めっき鋼板の製造方法
JP5444752B2 (ja) 2009-02-23 2014-03-19 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板の製造方法および高強度合金化溶融亜鉛めっき鋼板の製造方法
ES2730891T3 (es) 2009-08-31 2019-11-13 Nippon Steel Corp Lámina de acero recocido y galvanizado de alta resistencia
JP5644094B2 (ja) 2009-11-30 2014-12-24 新日鐵住金株式会社 延性及び曲げ性の良好な引張最大応力９００ＭＰａ以上を有する高強度鋼板および高強度冷延鋼板の製造方法、高強度亜鉛めっき鋼板の製造方法
MX2012011280A (es) * 2010-03-31 2012-11-06 Nippon Steel Corp Placa de acero galvanizado por inmersion en caliente de alta resitencia con excelente maleabilidad y proceso para producirla.
WO2013047804A1 (ja) 2011-09-30 2013-04-04 新日鐵住金株式会社 めっき濡れ性及びめっき密着性に優れた溶融亜鉛めっき層を備えた鋼板とその製造方法

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN101646797B (zh) * 2007-03-30 2012-05-09 杰富意钢铁株式会社 高强度热镀锌钢板
CN101649415A (zh) * 2008-08-12 2010-02-17 株式会社神户制钢所 加工性优异的高强度钢板

Also Published As

Publication number Publication date
TW201413005A (zh) 2014-04-01
BR112015001809A2 (pt) 2017-07-04
JPWO2014021452A1 (ja) 2016-07-21
KR101653510B1 (ko) 2016-09-01
CN104508169B (zh) 2017-02-22
WO2014021452A1 (ja) 2014-02-06
MX2015001224A (es) 2015-04-10
US10131981B2 (en) 2018-11-20
US20150225829A1 (en) 2015-08-13
JP5648755B2 (ja) 2015-01-07
BR112015001809B1 (pt) 2020-11-10
CN104508169A (zh) 2015-04-08
IN2015DN01525A (2) 2015-07-03
MX370268B (es) 2019-12-09
KR20150036681A (ko) 2015-04-07

Similar Documents

Publication Publication Date Title
TWI488978B (zh) Molten galvanized steel sheet and method of manufacturing the same
TWI464297B (zh) 熔融鍍鋅鋼板及其製造方法
KR101431317B1 (ko) 고강도 용융 아연 도금 강판 및 그 제조 방법
JP5218703B2 (ja) 耐加熱黒変性に優れた溶融Ａｌめっき鋼板及びその製造方法
JP5708884B2 (ja) 合金化溶融亜鉛めっき鋼板とその製造方法
CN103582717B (zh) 镀覆密合性优异的高强度热浸镀锌钢板及其制造方法
JP3997931B2 (ja) 高張力溶融亜鉛めっき鋼板の製造方法
JP5513216B2 (ja) 合金化溶融亜鉛めっき鋼板の製造方法
KR101752077B1 (ko) 고강도 용융 아연 도금 강판 및 그 제조 방법
JP2013136809A (ja) Ｓｉ含有高強度溶融亜鉛めっき鋼板、及びＳｉ含有高強度合金化溶融亜鉛めっき鋼板の製造方法
WO2015079699A1 (ja) 焼付け硬化型溶融亜鉛めっき鋼板
EP3396005B1 (en) Mn-containing hot-dip galvannealed steel sheet and manufacturing method therefor
EP4667607A1 (en) Steel sheet and method for manufacturing steel sheet
EP4296385A1 (en) Method for manufacturing steel sheet
JP2024500721A (ja) めっき密着性及び溶接性に優れた高強度溶融亜鉛めっき鋼板及びその製造方法
JP7696817B2 (ja) 鋼板の製造方法
JP2011026674A (ja) 耐めっき剥離性に優れる高強度溶融亜鉛めっき鋼板
KR20250092386A (ko) 도금강판 및 그 제조방법
JP2024144148A (ja) 鋼板および鋼板の製造方法

Legal Events

Date Code Title Description
MM4A Annulment or lapse of patent due to non-payment of fees